JPH07112517A - Heating container with fluororesin coating film and manufacture thereof - Google Patents
Heating container with fluororesin coating film and manufacture thereofInfo
- Publication number
- JPH07112517A JPH07112517A JP5259925A JP25992593A JPH07112517A JP H07112517 A JPH07112517 A JP H07112517A JP 5259925 A JP5259925 A JP 5259925A JP 25992593 A JP25992593 A JP 25992593A JP H07112517 A JPH07112517 A JP H07112517A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- coating film
- heating container
- ptfe
- pfa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、各種厨房器用加熱容器
に有用なフッ素樹脂積層を有する加熱容器及びその製造
方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heating container having a fluororesin laminate which is useful as a heating container for various kitchen appliances, and a method for producing the heating container.
【0002】[0002]
【従来の技術】ガス炊飯器又は電力を熱源とする炊飯
器、鍋等には、こげつき防止や撥水性を向上させるた
め、フッ素樹脂被膜を有するものが用いられている。フ
ッ素樹脂塗膜への印刷層の作成は種々の方法が提案され
ている。例えば、特開平5−116260号公報には、
基材上のプライマー層の上に特定の耐熱インクで印刷層
を形成し、その上にフッ素樹脂層を設けることが提案さ
れている。また特開平4−331150号公報には、基
材表面をあらかじめ凹凸処理し、次にフッ素樹脂ベース
層を設け、その上にインクで印刷層を形成し、その上に
フッ素樹脂層を設け、これをプレス成形して炊飯器や鍋
にすることが提案されている。さらに特開平4−144
41号公報には、基材上の不透明着色層の上にインクで
印刷層を形成し、その上にクリヤー系フッ素樹脂層を設
けることが提案されている。また、容器に文字等を表示
する手段として刻印のかわりに、最近はプライマー層と
トップ層の間に印刷されるものも多くなっている。2. Description of the Related Art Gas cookers, rice cookers using electric power as a heat source, pots, and the like have a fluororesin coating in order to prevent sticking and improve water repellency. Various methods have been proposed for forming a printing layer on a fluororesin coating film. For example, in Japanese Patent Laid-Open No. 5-116260,
It has been proposed to form a printing layer with a specific heat-resistant ink on a primer layer on a substrate, and provide a fluororesin layer on the printing layer. Further, in Japanese Unexamined Patent Publication No. 4-331150, the surface of a base material is subjected to an uneven treatment in advance, then a fluororesin base layer is provided, a print layer is formed with ink on the base layer, and a fluororesin layer is provided thereon. It has been proposed to press-mold into a rice cooker or pot. Further, JP-A-4-144
Japanese Patent Laid-Open No. 41 proposes to form a printing layer with ink on an opaque colored layer on a base material, and to provide a clear fluororesin layer thereon. Further, instead of engraving as a means for displaying characters or the like on a container, recently, more and more things are printed between the primer layer and the top layer.
【0003】[0003]
【発明が解決しようとする課題】しかし、前記従来技術
は、実際の量産性が良いものとは言えなかった。例え
ば、容器製作時に使用する切削油や潤滑油による汚染の
除去が完全で無いために発生する、プライマー塗膜のシ
ミ、ハジキによる外観欠点や、プライマー塗膜厚みのバ
ラツキによる色調変化が、トップ層のフッ素樹脂塗膜が
透明であるため、そのまま透けて見え外観不良品となる
という問題があった。特に鋳物の場合は巣が発生しやす
くこの巣の部分に切削油等が浸透し、塗膜欠点の原因と
なることが多い。However, the above-mentioned prior art cannot be said to have good actual mass productivity. For example, appearance defects due to stains and cissing of the primer coating film caused by incomplete removal of cutting oil and lubricating oil used during container production, and changes in color tone due to variations in primer coating film thickness Since the fluororesin coating film of No. 1 is transparent, there is a problem in that it can be seen through as it is and becomes a defective appearance product. Especially in the case of casting, cavities are likely to occur, and cutting oil or the like permeates into the cavities, which often causes coating film defects.
【0004】また、前記従来技術のプライマー層の上に
印刷を行い、その上に透明フッ素樹脂を被覆する方法で
は、プライマー層に発生した微細な欠点であっても、ト
ップ層が透明であるため外観上問題が発生するという問
題があった。Further, in the method of printing on the primer layer of the prior art and coating the transparent fluororesin on the primer layer, the top layer is transparent even if there are minute defects in the primer layer. There was a problem in that there was a problem in appearance.
【0005】本発明は前記従来の問題を解決するため、
塗膜欠点が少なく、外観に優れ、かつ量産性に優れたフ
ッ素樹脂塗膜を有する加熱容器及びその製造方法を提供
することを目的とする。In order to solve the above-mentioned conventional problems, the present invention provides
An object of the present invention is to provide a heating container having a fluororesin coating film having few coating film defects, excellent appearance, and excellent mass productivity, and a method for producing the heating container.
【0006】[0006]
【課題を解決するための手段】前記目的を達成するた
め、本発明のフッ素樹脂塗膜を有する加熱容器は、基材
上のプライマー層の上に、印刷表示層が施され、その上
に光輝性成分を含む薄膜のポリテトラフルオロエチレン
(PTFE)層が設けられ、かつその上に4フッ化エチ
レン−パーフルオロアルコキシエチレン共重合樹脂(P
FA)層が設けられているという構成を備えたものであ
る。In order to achieve the above-mentioned object, a heating container having a fluororesin coating film of the present invention is provided with a print display layer on a primer layer on a substrate, and a bright display is formed thereon. A thin film polytetrafluoroethylene (PTFE) layer containing an organic component is provided, and a tetrafluoroethylene-perfluoroalkoxyethylene copolymer resin (P
(FA) layer is provided.
【0007】前記構成においては、光輝性成分を有する
薄膜のポリテトラフルオロエチレン(PTFE)層の厚
さが、1〜20μmの範囲であることが好ましい。また
前記構成においては、光輝性成分がマイカ又は金属粉体
から選ばれることが好ましい。In the above structure, the thickness of the polytetrafluoroethylene (PTFE) layer of the thin film containing the glittering component is preferably in the range of 1 to 20 μm. Further, in the above-mentioned constitution, the glitter component is preferably selected from mica or metal powder.
【0008】また前記構成においては、加熱容器が、ガ
ス炊飯器又は電力を熱源とする炊飯器であることが好ま
しい。次に本発明のフッ素樹脂塗膜を有する加熱容器の
製造方法は、基材表面にプライマー層を形成し、その上
に文字、図面等の印刷を行い、その上に光輝性成分を含
む薄膜のポリテトラフルオロエチレン(PTFE)層を
ディスパージョンでスプレーコーティングした後、4フ
ッ化エチレン−パーフルオロアルコキシエチレン共重合
樹脂(PFA)を含む粉体塗料を静電塗装し、しかる後
焼成するという構成を備えたものである。In the above construction, it is preferable that the heating container is a gas rice cooker or a rice cooker using electric power as a heat source. Next, the method for producing a heating container having a fluororesin coating film of the present invention comprises forming a primer layer on the surface of a substrate, printing letters, drawings, etc. on the primer layer, and forming a thin film containing a glittering component on it. After spray-coating a polytetrafluoroethylene (PTFE) layer with a dispersion, a powder coating containing a tetrafluoroethylene-perfluoroalkoxyethylene copolymer resin (PFA) is electrostatically coated, and then baked. Be prepared.
【0009】[0009]
【作用】前記した本発明の構成によれば、基材上のプラ
イマー層の上に、印刷表示層を施し、その上に光輝性成
分を含む薄膜のポリテトラフルオロエチレン(PTF
E)層を設け、かつその上に4フッ化エチレン−パーフ
ルオロアルコキシエチレン共重合樹脂(PFA)層を設
けたことにより、塗膜欠点が少なく、外観に優れ、かつ
量産性に優れたフッ素樹脂塗膜を有する加熱容器とする
ことができる。すなわち、プライマー層に発生しやすい
シミ、ハジキ等の塗膜外観欠点をカバーするため、プラ
イマー塗装し、乾燥後に文字等を印刷し、その後、光輝
成分を有するPTFEディスパージョン、PFA粉体の
順に塗装する。これを焼成し被膜とする。塗装欠点が目
立たず加工性、生産性の良い美しい塗膜を得る事が出来
る。According to the above-mentioned constitution of the present invention, a print display layer is formed on a primer layer on a substrate, and a thin film of polytetrafluoroethylene (PTF) containing a glittering component is formed thereon.
E) layer is provided, and a tetrafluoroethylene-perfluoroalkoxyethylene copolymer resin (PFA) layer is provided thereon, so that the fluororesin has few coating film defects, excellent appearance, and mass productivity. It can be a heating container having a coating film. That is, in order to cover the appearance defects such as stains and cissing that are likely to occur in the primer layer, a primer is applied, characters are printed after drying, and then PTFE dispersion having a glitter component and PFA powder are applied in that order. To do. This is fired to form a film. It is possible to obtain a beautiful coating film with good workability and productivity with no noticeable coating defects.
【0010】またFEP成分を含む印刷層を形成する場
合、その上に同じ溶融性樹脂であるPFAで被覆した場
合、温度上昇時に、FEPが最も先に軟化を始め、PF
A塗膜硬度が低下する。これを改善する為に、FEP印
刷層とPFAの間に同様の光輝成分を含むPTFE層を
狭む事により、印刷部塗膜硬度の低下を改善することが
できる。さらに、光輝性成分をマイカ又は金属粉体から
選定することにより、色彩の自由度を増大させることが
できる。When forming a printing layer containing an FEP component and coating it with PFA which is the same meltable resin, when the temperature rises, the FEP starts to soften first and then PF.
A coating film hardness decreases. In order to improve this, by narrowing the PTFE layer containing the same bright component between the FEP printing layer and the PFA, it is possible to improve the decrease in the coating film hardness of the printed part. Furthermore, the degree of freedom of color can be increased by selecting the glitter component from mica or metal powder.
【0011】また本発明方法によれば、前記塗膜欠点が
少なく、外観に優れ、かつ量産性に優れたフッ素樹脂塗
膜を有する加熱容器を効率よく合理的に製造できる。Further, according to the method of the present invention, it is possible to efficiently and rationally manufacture a heating container having a fluororesin coating film which has few coating film defects, is excellent in appearance, and is excellent in mass productivity.
【0012】[0012]
【実施例】以下図面を用いて本発明をさらに具体的に説
明する。図1は本発明の一実施例のガス炊飯器の部分拡
大断面図である。図1において、1はアルミニウム、ス
テンレスなどの金属基材、2はプライマー層、3は文
字、記号、図形等の印刷表示層(例えば炊飯器の場合、
米の量を示す「カップ」という文字及びカップの数、水
量などの文字・記号)、4は光輝性成分を含む薄膜のポ
リテトラフルオロエチレン(PTFE)層、5は4フッ
化エチレン−パーフルオロアルコキシエチレン共重合樹
脂(PFA)層である。プライマー層2は5〜20μm
程度の厚さが好ましい。印刷表示層3は10μm以下の
厚さが好ましい。光輝性成分を含む薄膜のポリテトラフ
ルオロエチレン(PTFE)層4(メタリック層)は1
〜20μm程度の厚さが好ましい。4フッ化エチレン−
パーフルオロアルコキシエチレン共重合樹脂(PFA)
層5は10〜100μm程度の厚さが好ましい。The present invention will be described more specifically with reference to the drawings. FIG. 1 is a partially enlarged sectional view of a gas rice cooker according to an embodiment of the present invention. In FIG. 1, 1 is a metal base material such as aluminum or stainless steel, 2 is a primer layer, 3 is a printed display layer of characters, symbols, figures, etc. (for example, in the case of a rice cooker,
The letter "cup" indicating the amount of rice and the letters / symbols such as the number of cups and the amount of water), 4 is a thin polytetrafluoroethylene (PTFE) layer containing a glitter component, and 5 is tetrafluoroethylene-perfluoro. It is an alkoxyethylene copolymer resin (PFA) layer. The primer layer 2 is 5 to 20 μm
A moderate thickness is preferred. The print display layer 3 preferably has a thickness of 10 μm or less. The thin polytetrafluoroethylene (PTFE) layer 4 (metallic layer) containing the glittering component is 1
A thickness of about 20 μm is preferable. Tetrafluoroethylene
Perfluoroalkoxyethylene copolymer resin (PFA)
The layer 5 preferably has a thickness of about 10 to 100 μm.
【0013】光輝性成分を含む薄膜のポリテトラフルオ
ロエチレン(PTFE)層4の光輝性成分としては、雲
母(マイカ)、合成雲母、金属粉体(例えばニッケル
粉、アルミニウム粉、銀粉、金粉、白金粉等)、合成樹
脂微粒子の表面に金属メッキしたものなどを一例として
挙げることができる。これら光輝性成分は、PTFE1
00重量部(固形重量)に対して、0.1〜15重量部
程度、好ましくは0.7〜11重量部添加するのが好ま
しい。Examples of the glittering component of the thin polytetrafluoroethylene (PTFE) layer 4 containing the glittering component include mica, synthetic mica, metal powder (eg nickel powder, aluminum powder, silver powder, gold powder, platinum). Examples thereof include powder, etc.), synthetic resin fine particles having metal surfaces plated, and the like. These glittering components are PTFE1
It is preferable to add about 0.1 to 15 parts by weight, preferably 0.7 to 11 parts by weight, relative to 00 parts by weight (solid weight).
【0014】以下具体的実施例を説明する。 (実施例1)アルミ容器を脱脂後、サンドプラスト処理
を行い表面を粗面化した。プライマーとしてダイキン工
業株式会社製プライマーEK−1959DGNを焼成後
膜厚10μmになるよう塗装し、120℃で10分間乾
燥した。その上に、ダイキン工業株式会社製FEPディ
スパージョンND−2と酸化チタンを主成分とするイン
キを用い、印刷層をタンポ印刷した。その後ダイキン工
業株式会社製PTFEディスパージョンEK−4300
CR(光輝性成分であるマイカを固形分に対して3重量
%添加)を焼成膜厚5μmになるようにスプレー塗装
し、乾燥後すぐその上に三井デュポンフロロケミカル株
式会社製PFA粉体MP−10を焼成後25μmになる
ように静電塗装した。これを380℃で20分間焼成分
した。このようにしてガス炊飯器用釜を作成した。Specific examples will be described below. (Example 1) After degreasing an aluminum container, a sand plast treatment was performed to roughen the surface. As a primer, primer EK-1959DGN manufactured by Daikin Industries, Ltd. was applied after firing to a film thickness of 10 μm, and dried at 120 ° C. for 10 minutes. A printing layer was tampo-printed thereon using FEP Dispersion ND-2 manufactured by Daikin Industries, Ltd. and an ink containing titanium oxide as a main component. After that, PTFE dispersion EK-4300 manufactured by Daikin Industries, Ltd.
CR (3% by weight of mica which is a glittering component is added to the solid content) is spray-coated to a baked film thickness of 5 μm, and immediately after drying, PFA powder MP- manufactured by Mitsui DuPont Fluorochemical Co., Ltd. After firing, 10 was electrostatically coated to a thickness of 25 μm. This was baked at 380 ° C. for 20 minutes. In this way, a gas cooker pot was prepared.
【0015】(比較例1)上記、実施例1よりPTFE
ディスパージョンを除いたものを比較例とした。すなわ
ち、アルミ容器を脱脂後、サンドプラスト処理を行い表
面を粗面化した。プライマーとしてダイキン工業株式会
社製プライマーEK−1959DGNを焼成後膜厚10
μmになるよう塗装し、120℃で10分間乾燥した。
その上に、ダイキン工業株式会社製FEPディスパージ
ョンND−2と酸化チタンを主成分とするインキを用
い、印刷層をタンポ印刷した。その後三井デュポンフロ
ロケミカル株式会社製PFA粉体MP−10を焼成後2
5μmになるように塗装した。これを380℃で20分
間焼成分した。このようにしてガス炊飯器用釜を作成し
た。(Comparative Example 1) From the above Example 1, PTFE was used.
The thing except the dispersion was made into the comparative example. That is, the aluminum container was degreased and then sandblasted to roughen the surface. As a primer, a film thickness of 10 after firing primer EK-1959DGN manufactured by Daikin Industries, Ltd.
It was coated to a thickness of μm and dried at 120 ° C. for 10 minutes.
A printing layer was tampo-printed thereon using FEP Dispersion ND-2 manufactured by Daikin Industries, Ltd. and an ink containing titanium oxide as a main component. After firing PFA powder MP-10 manufactured by Mitsui DuPont Fluorochemicals Co., Ltd. 2
It was coated so as to have a thickness of 5 μm. This was baked at 380 ° C. for 20 minutes. In this way, a gas cooker pot was prepared.
【0016】実施例1及び比較例1の外観及び鉛筆硬度
を比較した。表1に結果を示す。The appearance and pencil hardness of Example 1 and Comparative Example 1 were compared. The results are shown in Table 1.
【0017】[0017]
【表1】 [Table 1]
【0018】表1から明らかな通り、実施例1はプライ
マー表面のシミ、ハジキ等の欠点を隠蔽し、美しい外観
を得る事が出来た。これに対して比較例はプライマーの
ハジキが透けて見え、外観上の欠点となった。As is clear from Table 1, Example 1 was able to conceal defects such as spots and cissing on the primer surface and obtain a beautiful appearance. On the other hand, in the comparative example, the cissing of the primer was seen through, which was a defect in appearance.
【0019】(実施例2)マイカ/PTFE固形分比と
膜厚を表2に示すように変化させた以外は、実施例1と
同様な方法で実験を行った。その結果を表2に示す。表
2から明らかな通り、マイカ/PTFE固形分比が0.
71〜10.31重量%の範囲、及び膜厚が5〜15μ
mの範囲であれば、プライマー欠点が少なくて外観に優
れ、かつ文字も良く判別できた。Example 2 An experiment was conducted in the same manner as in Example 1 except that the mica / PTFE solid content ratio and the film thickness were changed as shown in Table 2. The results are shown in Table 2. As is clear from Table 2, the mica / PTFE solid content ratio is 0.
71 to 10.31 wt% range and film thickness 5 to 15 μ
Within the range of m, there were few primer defects, the appearance was excellent, and the characters could be distinguished well.
【0020】[0020]
【表2】 [Table 2]
【0021】また本発明の実施例においては、FEP成
分を含む印刷層を形成する場合、その上に同じ溶融性樹
脂であるPFAで被覆した場合、温度上昇時に、FEP
が最も先に軟化を始め、PFA塗膜硬度が低下する。こ
れを改善する為に、FEP印刷層とPFAの間に同様の
光輝成分を含むPTFE層を狭む事により、印刷部塗膜
硬度の低下を改善することができた。Further, in the embodiment of the present invention, when a printing layer containing an FEP component is formed, when it is coated with PFA which is the same meltable resin, when the temperature rises, FEP is applied.
Begins to soften, and the PFA coating film hardness decreases. In order to improve this, by narrowing the PTFE layer containing the same bright component between the FEP printing layer and PFA, it was possible to improve the decrease in the coating film hardness on the printed part.
【0022】[0022]
【発明の効果】以上説明した通り、本発明によれば、基
材上のプライマー層の上に、印刷表示層を施し、その上
に光輝性成分を含む薄膜のポリテトラフルオロエチレン
(PTFE)層を設け、かつその上に4フッ化エチレン
−パーフルオロアルコキシエチレン共重合樹脂(PF
A)層を設けたことにより、塗膜欠点が少なく、外観に
優れ、かつ量産性に優れたフッ素樹脂塗膜を有する加熱
容器とすることができる。As described above, according to the present invention, a print display layer is formed on a primer layer on a substrate, and a thin polytetrafluoroethylene (PTFE) layer containing a glitter component is formed thereon. And a tetrafluoroethylene-perfluoroalkoxyethylene copolymer resin (PF
By providing the layer A), it is possible to obtain a heating container having a fluororesin coating film with few coating film defects, excellent appearance, and excellent mass productivity.
【0023】また本発明方法によれば、前記塗膜欠点が
少なく、外観に優れ、かつ量産性に優れたフッ素樹脂塗
膜を有する加熱容器を効率よく合理的に製造できる。Further, according to the method of the present invention, it is possible to efficiently and rationally manufacture a heating container having a fluororesin coating film which has few coating film defects, is excellent in appearance, and is excellent in mass productivity.
【図1】本発明の一実施例のガス炊飯器の部分拡大断面
図である。FIG. 1 is a partially enlarged cross-sectional view of a gas rice cooker according to an embodiment of the present invention.
1 基材 2 プライマー層 3 印刷表示層 4 光輝性成分を含む薄膜のポリテトラフルオロエチレ
ン(PTFE)層 5 4フッ化エチレン−パーフルオロアルコキシエチレ
ン共重合樹脂(PFA)層DESCRIPTION OF SYMBOLS 1 Base material 2 Primer layer 3 Print display layer 4 Polytetrafluoroethylene (PTFE) layer of a thin film containing a glitter component 5 4 Fluorinated ethylene-perfluoroalkoxyethylene copolymer resin (PFA) layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 B32B 27/06 8413−4F 27/20 Z 8413−4F ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location B32B 27/06 8413-4F 27/20 Z 8413-4F
Claims (5)
層が施され、その上に光輝性成分を含む薄膜のポリテト
ラフルオロエチレン(PTFE)層が設けられ、かつそ
の上に4フッ化エチレン−パーフルオロアルコキシエチ
レン共重合樹脂(PFA)層が設けられているフッ素樹
脂塗膜を有する加熱容器。1. A printed display layer is provided on a primer layer on a substrate, and a thin polytetrafluoroethylene (PTFE) layer containing a glittering component is provided on the printed display layer. Container having a fluororesin coating film provided with a fluorinated ethylene-perfluoroalkoxyethylene copolymer resin (PFA) layer.
ルオロエチレン(PTFE)層の厚さが、1〜20μm
の範囲である請求項1に記載のフッ素樹脂塗膜を有する
加熱容器。2. A polytetrafluoroethylene (PTFE) layer of a thin film having a glittering component has a thickness of 1 to 20 μm.
The heating container having the fluororesin coating film according to claim 1, which is in the range.
ばれる請求項1に記載のフッ素樹脂塗膜を有する加熱容
器。3. A heating container having a fluororesin coating film according to claim 1, wherein the glittering component is selected from mica and metal powder.
とする炊飯器である請求項1に記載のフッ素樹脂塗膜を
有する加熱容器。4. The heating container having the fluororesin coating film according to claim 1, wherein the heating container is a gas rice cooker or a rice cooker using electric power as a heat source.
上に文字、図面等の印刷を行い、その上に光輝性成分を
含む薄膜のポリテトラフルオロエチレン(PTFE)層
をディスパージョンでスプレーコーティングした後、4
フッ化エチレン−パーフルオロアルコキシエチレン共重
合樹脂(PFA)を含む粉体塗料を静電塗装し、しかる
後焼成するフッ素樹脂塗膜を有する加熱容器の製造方
法。5. A primer layer is formed on the surface of a substrate, characters, drawings, etc. are printed on the primer layer, and a thin polytetrafluoroethylene (PTFE) layer containing a glittering component is sprayed thereon by dispersion. After coating, 4
A method for producing a heating container having a fluororesin coating film, comprising electrostatically coating a powder coating material containing a fluoroethylene-perfluoroalkoxyethylene copolymer resin (PFA), and then firing the powder coating material.