JPH0691797A - Non-slip sheet - Google Patents
Non-slip sheetInfo
- Publication number
- JPH0691797A JPH0691797A JP24186092A JP24186092A JPH0691797A JP H0691797 A JPH0691797 A JP H0691797A JP 24186092 A JP24186092 A JP 24186092A JP 24186092 A JP24186092 A JP 24186092A JP H0691797 A JPH0691797 A JP H0691797A
- Authority
- JP
- Japan
- Prior art keywords
- slip
- sheet
- weight
- parts
- slip sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、たとえば、浴室出入口
に置かれる足拭きマットや玄関フロアーに置かれる玄関
マット等の敷物と、平滑な床との間に載置され、敷物が
滑って位置がずれたりすることがないようにする滑り止
めシートに関する。INDUSTRIAL APPLICABILITY The present invention is placed between a rug such as a foot wipe mat placed at a doorway of a bathroom or an entrance mat placed on an entrance floor and a smooth floor so that the rug slips to a position. The present invention relates to a non-slip sheet that prevents slippage.
【０００２】[0002]
【従来の技術】平滑な床に玄関マットや座布団などの敷
物を直接置いた場合、床が非常に滑りやすいため、足を
不用意に敷物に載せると敷物が滑りバランスを崩して怪
我をしたりする。そこで、このように滑りやすい床に玄
関マットや足拭きマットなどを敷く場合、図１に示すよ
うに、床１にまず滑り止めシート２を敷き、その上に玄
関マット等のマット３を敷くようにしている。2. Description of the Related Art When a rug such as a front door mat or cushion is directly placed on a smooth floor, the floor is very slippery, so if the foot is carelessly placed on the rug, the rug will slip and lose its balance, resulting in injury. To do. Therefore, when laying a front door mat or a foot wipe mat on such a slippery floor, as shown in FIG. 1, first lay a non-slip sheet 2 on the floor 1 and then lay a mat 3 such as a front door mat thereon. I have to.
【０００３】すなわち、滑り止めシート２は、図２に示
すように網目状に形成された芯材シート２１が芯材シー
ト２１を構成するフィラメント２２の表面を滑り止め効
果を有する樹脂材料２３によって被覆することで得られ
るようになっている。そして、被覆樹脂材料２３の摩擦
抵抗によってマット３の滑りを防止するようにしてい
る。また、被覆樹脂材料２３の厚みは、網目２４が残る
程度にしてある。That is, in the non-slip sheet 2, a core material sheet 21 formed in a mesh shape as shown in FIG. 2 covers the surface of filaments 22 constituting the core material sheet 21 with a resin material 23 having an anti-slip effect. You can get it by doing. The friction resistance of the coating resin material 23 prevents the mat 3 from slipping. The thickness of the coating resin material 23 is set so that the mesh 24 remains.
【０００４】[0004]
【発明が解決しようとする課題】ところで、従来の滑り
止めシート２は、樹脂として塩化ビニル樹脂が一般に使
用されているが、この滑り止めシート２には、次のよう
な問題がある。すなわち、滑り止めシート２を廃棄処理
すると、通常焼却されるが、塩化ビニル樹脂は焼却時に
塩素ガスが発生し、環境保護の面で非常に問題がある。
しかも、焼却時に発熱が大きく、焼却炉を傷めると言う
問題、さらに、塩化ビニル樹脂に一般的に含まれるフタ
ル酸ジオクチル等の可塑剤が滑り止めシート２に接触し
ている床１やマット３等に移行して汚染したり、可塑剤
が抜けて滑り止めシート２の風合いが変わったり、滑り
止め効果が薄れたりしやすいと言う問題などもある。By the way, a vinyl chloride resin is generally used as a resin in the conventional anti-slip sheet 2, but the anti-slip sheet 2 has the following problems. That is, when the anti-slip sheet 2 is disposed of, it is normally incinerated, but the vinyl chloride resin generates chlorine gas during incineration, which is very problematic in terms of environmental protection.
Moreover, the heat generated during incineration is large and damages the incinerator. Furthermore, a plasticizer such as dioctyl phthalate, which is generally contained in vinyl chloride resin, is in contact with the anti-slip sheet 2, floor 3, mat 3, etc. There is also a problem in that the anti-slip effect tends to be weakened, or the texture of the anti-slip sheet 2 is changed due to the plasticizer being removed, and the anti-slip effect tends to be weakened.
【０００５】本発明は、このような事情に鑑みて、耐候
性に優れ、可塑剤を含まないとともに、焼却して有毒ガ
スがでず、滑り止め効果の高い滑り止めシートを提供す
ることを目的としている。In view of such circumstances, an object of the present invention is to provide a non-slip sheet which is excellent in weather resistance, does not contain a plasticizer, does not emit toxic gas upon incineration, and has a high anti-slip effect. I am trying.
【０００６】[0006]
【課題を解決するための手段】本発明にかかる滑り止め
シートは、このような目的を達成するために、所望径の
フィラメントを網目に組んだ芯材シートを備え、この芯
材シートは、前記フィラメントが前記網目を潰さない程
度に滑り止め効果を有する樹脂材料によって被覆されて
いる滑り止めシートであって、前記樹脂材料がアクリル
系樹脂の発泡体である構成にした。In order to achieve such an object, a non-slip sheet according to the present invention comprises a core material sheet in which filaments of a desired diameter are assembled in a mesh, and the core material sheet is A non-slip sheet in which filaments are covered with a resin material having an anti-slip effect to the extent that the mesh is not crushed, and the resin material is a foam of acrylic resin.
【０００７】上記構成において、アクリル系樹脂として
は、アクリルエマルション、アクリル系エマルション
（アクリルースチレン共重合体、アクリルー酢酸ビニル
共重合体、エチレン−アクリル共重合体、エチレン−酢
酸ビニル−アクリル共重合体）等が挙げられ、これらに
滑り止め効果を低下させない程度にラテックス（天然、
ＳＢＲ，ＮＢＲ，ＭＢＲ，ＣＲ等）やエチレン−酢酸ビ
ニル共重合体、酢酸ビニル、ウレタン等のエマルション
を添加しても構わない。In the above constitution, as the acrylic resin, acrylic emulsion, acrylic emulsion (acrylic-styrene copolymer, acrylic-vinyl acetate copolymer, ethylene-acrylic copolymer, ethylene-vinyl acetate-acrylic copolymer ) Etc., and latex (natural,
SBR, NBR, MBR, CR, etc.) and ethylene-vinyl acetate copolymer, vinyl acetate, emulsions such as urethane may be added.
【０００８】芯材シートとしては、特に限定されず、
綿、麻、ナイロン糸などで織った織布が挙げられる。網
目の大きさは、特に限定されないが、一辺の長さを網目
を囲む樹脂被覆部の厚みと略同じ程度から１０倍程度と
なるようにすることが好ましい。この滑り止めシート
は、特に限定されないが、一般には、芯材シートに発泡
剤を含むアクリル系樹脂エマルションを含浸させたり塗
布したのち、加熱して発泡させることで得ることができ
る。The core sheet is not particularly limited,
Examples include woven fabrics woven from cotton, linen, nylon threads, and the like. The size of the mesh is not particularly limited, but it is preferable that the length of one side is approximately the same as the thickness of the resin coating portion surrounding the mesh to about 10 times. This non-slip sheet is not particularly limited, but generally, it can be obtained by impregnating or coating an acrylic resin emulsion containing a foaming agent on a core sheet, and then heating and foaming.
【０００９】発泡体の発泡倍率は、特に限定されない
が、３〜１５倍程度が好ましい。すなわち、発泡倍率が
３倍を下回ると被膜強度は強くなるのであるが、滑り止
め効果が悪くなる傾向がある。一方、発泡倍率が１５倍
を上回ると滑り止め効果は大きくなるのであるが、被膜
強度が弱くなる傾向がある。また、上記のように芯材シ
ートに含浸又は塗布するアクリル系樹脂エマルションに
は、滑り止め効果の調整のためワックスも適宜加えるこ
とができる。すなわち、アクリル系樹脂のみでは、滑り
止め効果が大きくなりすぎて、却ってシートの耐久性に
問題が出る虞がある。The expansion ratio of the foam is not particularly limited, but is preferably about 3 to 15 times. That is, when the expansion ratio is less than 3, the coating strength increases, but the anti-slip effect tends to deteriorate. On the other hand, when the expansion ratio exceeds 15 times, the anti-slip effect increases, but the coating strength tends to be weak. In addition, wax may be appropriately added to the acrylic resin emulsion to be impregnated or applied to the core sheet as described above for the purpose of adjusting the anti-slip effect. That is, if the acrylic resin alone is used, the anti-slip effect becomes too great, which may rather cause a problem in the durability of the sheet.
【００１０】なお、ワックスの添加量は、特に限定され
ないが、エマルション中のアクリル系樹脂１００重量部
に対して１〜５（特に好ましくは２〜３）重量部程度が
好ましい。さらに、芯剤シートに含浸させるアクリル系
樹脂エマルションは、芯材シートのフィラメントに定着
しやすいように、メチルセルロース等の増粘剤を加えて
粘度調整を予め行って置くことが好ましい。なお、粘度
としては、８０００〜１００００cps （特に好ましくは
９０００cps 前後）程度にすることが好ましい。The amount of wax added is not particularly limited, but is preferably about 1 to 5 (particularly preferably 2 to 3) parts by weight per 100 parts by weight of the acrylic resin in the emulsion. Further, the acrylic resin emulsion to be impregnated into the core sheet is preferably adjusted in advance by adding a thickening agent such as methyl cellulose so that the acrylic resin emulsion is easily fixed to the filament of the core sheet. The viscosity is preferably about 8000 to 10000 cps (particularly preferably about 9000 cps).
【００１１】[0011]
【作用】上記構成によれば、焼却時に塩素などの有害ガ
スを発生することがなくなる。また、耐候性も向上する
ようになる。According to the above construction, no harmful gas such as chlorine is generated during incineration. Also, the weather resistance is improved.
【００１２】[0012]
【実施例】以下に、本発明を、その実施例を参照しつつ
詳しく説明する。 （実施例１）65ｇ／ｍ2 、網目の１マスの大きさが 5.5
mm× 6.５mmの綿布（ラッセル織り）を芯材シート２１
として用意し、この芯材シート２１に下記配合の配合液
を乾燥重量で50〜70ｇ／ｍ3 塗布した後、140 ℃で熱処
理して滑り止めシート２を得た。なお、発泡倍率は３〜
４倍であった。EXAMPLES The present invention will be described in detail below with reference to its examples. (Example 1) 65 g / m 2 , the size of one square of the mesh was 5.5
mm × 6.5mm cotton cloth (Russell weave) for the core sheet 21
The coating solution of the following composition was applied to the core sheet 21 at a dry weight of 50 to 70 g / m 3 and then heat treated at 140 ° C. to obtain a non-slip sheet 2. The expansion ratio is 3 ~
It was four times.
【００１３】 配合液（但し、各成分の重量部は乾燥時のものである） アクリルエマルション（新中村化学工業（株）製 ＴＳ９０５）１００重量部 発泡剤（スェーデン、エクスパンセル社製 ＷＵ４６１） ８重量部 ワックス（ヘキスト社製 パラフィンワックス） ２重量部 メチルセルロース 1.5 重量部 顔料 0.5重量部 (チタンホワイト 0.4重量部、シアニンブルー 0.1重量部) 固形分 ４３％ 粘度 ９０００cps Mixing liquid (however, the weight parts of the respective components are those when dried) Acrylic emulsion (TS905 manufactured by Shin-Nakamura Chemical Co., Ltd.) 100 weight parts Blowing agent (WU461 manufactured by Expancel Co., Sweden) 8 Parts by weight wax (paraffin wax manufactured by Hoechst) 2 parts by weight methyl cellulose 1.5 parts by weight pigment 0.5 parts by weight (titanium white 0.4 parts by weight, cyanine blue 0.1 parts by weight) solid content 43% viscosity 9000 cps
【００１４】（実施例２）93ｇ／ｍ2 、網目の１マスの
大きさが 2.5mm× 2.5mmの綿布（ラッセル織り）を芯材
シート２１として用意し、この芯材シート２１に下記配
合の配合液を乾燥重量で80〜100 ｇ／ｍ3 塗布した後、
140 ℃で熱処理して滑り止めシート２を得た。なお、発
泡倍率は７〜８倍であった。Example 2 A cotton cloth (Russell weave) having a size of 93 g / m 2 and a mesh size of 2.5 mm × 2.5 mm was prepared as a core material sheet 21. After applying the compounded liquid at a dry weight of 80 to 100 g / m 3 ,
It was heat treated at 140 ° C. to obtain a non-slip sheet 2. The expansion ratio was 7 to 8 times.
【００１５】 配合液（但し、各成分の重量部は乾燥時のものである） アクリルエマルション（新中村化学工業（株）製 ＴＳ９０５）１００重量部 発泡剤（スェーデン、エクスパンセル社製 ＷＵ４６１） １６重量部 ワックス（ヘキスト社製 パラフィンワックス） ２重量部 メチルセルロース 1.5 重量部 顔料 0.5重量部 (チタンホワイト 0.4重量部、シアニンブルー 0.1重量部) 固形分 ４３％ 粘度 ９０００cps Blended liquid (however, each part by weight is a dry component) Acrylic emulsion (TS905 manufactured by Shin-Nakamura Chemical Co., Ltd.) 100 parts by weight Blowing agent (WU461, Sweden, Expancel) 16 Parts by weight wax (paraffin wax manufactured by Hoechst) 2 parts by weight methyl cellulose 1.5 parts by weight pigment 0.5 parts by weight (titanium white 0.4 parts by weight, cyanine blue 0.1 parts by weight) solid content 43% viscosity 9000 cps
【００１６】（実施例３）50ｇ／ｍ2 、網目の１マスの
大きさが 9.5mm×10.0mmの綿布（ラッセル織り）を芯材
シート２１として用意し、この芯材シート２１に下記配
合の配合液を乾燥重量で30〜50ｇ／ｍ3 塗布した後、14
0 ℃で熱処理して滑り止めシート２を得た。なお、発泡
倍率は１４〜１５倍であった。Example 3 A cotton cloth (Russell weave) having a size of 50 g / m 2 and a mesh size of 9.5 mm × 10.0 mm is prepared as a core material sheet 21. After applying 30-50g / m 3 dry weight of compounded liquid,
Heat treatment was performed at 0 ° C. to obtain a non-slip sheet 2. The expansion ratio was 14 to 15 times.
【００１７】 配合液（但し、各成分の重量部は乾燥時のものである） アクリルエマルション（新中村化学工業（株）製 ＴＳ９０５）１００重量部 発泡剤（スェーデン、エクスパンセル社製 ＷＵ４６１） ２４重量部 ワックス（ヘキスト社製 パラフィンワックス） ２重量部 メチルセルロース 1.5 重量部 顔料 0.5重量部 (チタンホワイト 0.4重量部、シアニンブルー 0.1重量部) 固形分 ４３％ 粘度 ９０００cps 上記実施例１〜３で得た滑り止めシート２を風呂の足拭
きマットの下側においたところ、いずれも床が濡れてい
ても充分な滑り止め効果を発揮した。Mixing liquid (however, each part by weight is a dry component) Acrylic emulsion (TS905 manufactured by Shin-Nakamura Chemical Co., Ltd.) 100 parts by weight Blowing agent (WU461, Sweden, Expancel) 24 Parts by weight wax (paraffin wax manufactured by Hoechst) 2 parts by weight methyl cellulose 1.5 parts by weight pigment 0.5 parts by weight (titanium white 0.4 parts by weight, cyanine blue 0.1 parts by weight) solid content 43% viscosity 9000 cps slip obtained in Examples 1 to 3 above When the retaining sheet 2 was placed under the foot wiping mat in the bath, both exhibited sufficient anti-slip effect even when the floor was wet.
【００１８】[0018]
【発明の効果】本発明にかかる滑り止めシートは、以上
のように、滑り止め効果を有する樹脂材料にアクリル樹
脂系材料の発泡体を用いたので、廃棄物として焼却して
も有毒なガスが発生せず、環境汚染を無くすことができ
る。しかも、従来の塩化ビニル樹脂を用いたものに比べ
耐候性、耐久性も向上する。As described above, the non-slip sheet according to the present invention uses the foamed material of the acrylic resin material as the resin material having the anti-slip effect. It does not occur, and environmental pollution can be eliminated. In addition, weather resistance and durability are improved as compared with those using conventional vinyl chloride resin.
【００１９】また、樹脂材料中に可塑剤を含まないの
で、可塑剤による床やマット等の敷物への汚染と言う問
題も解決できる。Further, since the resin material does not contain a plasticizer, it is possible to solve the problem of the plasticizer contaminating the rug such as floors and mats.
【図１】滑り止めシートの使用例をあらわす斜視図であ
る。FIG. 1 is a perspective view showing an example of use of a non-slip sheet.
【図２】滑り止めシートの断面図である。FIG. 2 is a cross-sectional view of a non-slip sheet.
２ 滑り止めシート ２１ 芯材シート ２２ フィラメント ２３ 樹脂材料 ２４ 網目 2 Non-slip sheet 21 Core sheet 22 Filament 23 Resin material 24 Mesh
Claims (1)
シートを備え、この芯材シートは、前記フィラメントが
前記網目を潰さない程度に滑り止め効果を有する樹脂材
料によって被覆されている滑り止めシートであって、前
記樹脂材料がアクリル系樹脂の発泡体であることを特徴
とする滑り止めシート。1. A non-slip material comprising a core material sheet in which filaments having a desired diameter are assembled in a mesh, and the core material sheet is covered with a resin material having a slip-resisting effect to the extent that the filament does not crush the mesh. A non-slip sheet, wherein the resin material is a foam of acrylic resin.