JPH0686108B2 - Dew condensation prevention sheet - Google Patents
Dew condensation prevention sheetInfo
- Publication number
- JPH0686108B2 JPH0686108B2 JP1280141A JP28014189A JPH0686108B2 JP H0686108 B2 JPH0686108 B2 JP H0686108B2 JP 1280141 A JP1280141 A JP 1280141A JP 28014189 A JP28014189 A JP 28014189A JP H0686108 B2 JPH0686108 B2 JP H0686108B2
- Authority
- JP
- Japan
- Prior art keywords
- vinyl chloride
- chloride resin
- water
- dew condensation
- substance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、壁材、家具用レザー、床材などの内装材に使
用される結露防止性シート状物に関する。TECHNICAL FIELD The present invention relates to a dew condensation preventing sheet used for interior materials such as wall materials, leather for furniture and floor materials.
従来より、基材に非発泡塩化ビニル系樹脂を積層したシ
ート状物は、その表面に種々のプリントやエンボス模様
を形成し、建物内壁に貼着する壁材、ソファーの外張り
に使用する家具用レザー、建物床面に貼着する床材等の
広い分野に応用され多量に使用されてきた。Conventionally, a sheet-like material in which a non-foamed vinyl chloride resin is laminated on a base material has various prints and embossed patterns formed on the surface, and is a wall material to be attached to the inner wall of a building, and furniture used for covering the sofa. It has been used in large quantities in a wide range of fields such as leather for leather and floor materials attached to building floors.
しかしながら、このような基材に非発泡塩化ビニル系樹
脂を積層したシート状物を、建物内壁に貼着する壁材、
ソファーの外張りに使用する家具用レザー、建物床面に
貼着する床材に使用した場合、冬場においてこれら壁
材、レザー、床材の表面に空気中の湿気が水滴状に凝結
し、濡れてしまうという欠点があった。However, a sheet material obtained by laminating a non-foamed vinyl chloride resin on such a base material is a wall material to be attached to an inner wall of a building,
When used as furniture leather used for the outer covering of sofas and floor materials attached to the floor surface of buildings, in the winter, the surface moisture of these wall materials, leather, and floor materials condense in the form of water droplets and get wet. There was a drawback that it would end up.
これを改善するため、吸水性高分子物質や天然繊維質物
質を含有する塩化ビニル系樹脂層を基材表面に形成した
壁材が開発されている。このものは、塩化ビニル系樹脂
中の吸水性高分子物質や天然繊維質物質により、シート
状物表面に凝結する水分を直ちに吸収して結露を防止し
ようとするものであるが、現実には吸水性高分子物質や
天然繊維質物質を含有しないものと結露防止性の点にお
いてはほとんど差異がなものであった。In order to improve this, a wall material has been developed in which a vinyl chloride resin layer containing a water-absorbing polymer substance or a natural fiber substance is formed on the surface of a substrate. This is intended to prevent dew condensation by immediately absorbing the moisture condensed on the surface of the sheet-like material by the water-absorbing polymer substance or the natural fiber substance in the vinyl chloride resin, but in reality, it absorbs water. There was almost no difference in dew condensation prevention property from those containing no high-polymer material or natural fiber material.
本発明は、これらの欠点を改善し、結露防止性にすぐれ
たシート状物を提供することを目的とするものである。An object of the present invention is to improve these drawbacks and to provide a sheet-like material excellent in dew condensation prevention property.
すなわち、本発明は、 （１）基材表面全面に、吸水性高分子物質及び／又は天
然繊維質物質と浸透剤を含有する非発泡塩化ビニル系樹
脂層が形成されてなる結露防止性シート状物。That is, the present invention provides (1) a dew condensation-preventing sheet having a non-foamed vinyl chloride resin layer containing a water-absorbent polymer substance and / or a natural fiber substance and a penetrant formed on the entire surface of a substrate. object.
（２）基材表面に模様状に、吸水性高分子物質及び／又
は天然繊維質物質と浸透剤を含有する非発泡塩化ビニル
系樹脂層が形成されてなる結露防止性シート状物。(2) A dew condensation-preventing sheet-like product, comprising a non-foaming vinyl chloride resin layer containing a water-absorbing polymer substance and / or a natural fiber substance and a penetrant formed in a pattern on the surface of a substrate.
（３）塩化ビニル系樹脂100重量部に対して、吸水性高
分子物質及び／又は天然繊維質物質の含有量が３〜30重
量部であり、浸透剤の含有量が0.3〜５重量部である請
求項１〜２のいづれかに１項に記載の結露防止性シート
状物。(3) When the content of the water-absorbing polymer and / or the natural fiber material is 3 to 30 parts by weight and the content of the penetrant is 0.3 to 5 parts by weight with respect to 100 parts by weight of the vinyl chloride resin. The dew condensation preventing sheet material according to any one of claims 1 to 2.
（４）吸水性高分子物質が、ビニルアルコール−アクリ
ル酸共重合体、酢酸ビニル−アクリル酸エステル共重合
体ケン化物、イソブチレン−無水マレイン酸共重合体変
性物の架橋物、アクリル酸ソーダ重合体部分架橋物、ア
クリルニトリルグラフト化デンプンの加水分解物の群か
ら選ばれた１種以上の吸水性高分子物質である請求項１
〜３のいずれか１項記載の結露防止性シート状物。(4) Water-absorbing polymer substance is vinyl alcohol-acrylic acid copolymer, vinyl acetate-acrylic acid ester copolymer saponified product, crosslinked product of isobutylene-maleic anhydride copolymer modified product, sodium acrylate polymer 2. One or more water-absorbing polymer substances selected from the group of partially crosslinked products and hydrolyzed products of acrylonitrile-grafted starch.
4. A dew condensation preventing sheet material according to any one of 3 to 3.
を要旨とするものである。Is the gist.
本発明に使用できる吸水性高分子物質としては、ビニル
アルコール−アクリル酸共重合体、酢酸ビニル−アクリ
ル酸エステル共重合体ケン化物、イソブチレン−無水マ
レイン酸共重合体変性物の架橋物、アクリル酸ソーダ重
合体部分架橋物、アクリルニトリルグラフト化デンプン
の加水分解物などが挙げられる。天然繊維質物質として
は、木綿、スフ、麻などの天然繊維の短繊維や、木粉、
モミガラ粉などの植物体の粉末等を使用することができ
る。Examples of the water-absorbing polymer that can be used in the present invention include vinyl alcohol-acrylic acid copolymer, vinyl acetate-acrylic acid ester copolymer saponified product, crosslinked product of isobutylene-maleic anhydride copolymer modified product, acrylic acid. Examples include partially crosslinked soda polymers and hydrolyzates of acrylonitrile-grafted starch. Examples of natural fiber substances include short fibers of natural fibers such as cotton, soup, and hemp, and wood powder,
It is possible to use plant powders such as chaff powder.
吸水性高分子物質や天然繊維質物質は単独で使用しても
よいし、複数種を併用して使用してもよい。吸水性高分
子物質及び／又は天然繊維質物質の塩化ビニル系樹脂へ
の配合量は、塩化ビニル系樹脂100重量部に対して３〜3
0重量部、好ましくは５〜15重量部であり、３重量部未
満では充分な結露防止性能が得られず、30重量部を越え
て多量に用いると低下や、耐侯変色性、耐薬品性等の特
性を失うおそれがある。The water-absorbent polymer substance and the natural fiber substance may be used alone or in combination of two or more. The amount of the water-absorbent polymer substance and / or the natural fiber substance to be mixed with the vinyl chloride resin is 3 to 3 with respect to 100 parts by weight of the vinyl chloride resin.
0 parts by weight, preferably 5 to 15 parts by weight. If it is less than 3 parts by weight, sufficient dew condensation-preventing performance cannot be obtained, and if it is used in excess of 30 parts by weight, the deterioration, deterioration in weather resistance, chemical resistance, etc. There is a risk of losing the characteristics of.
本発明に使用できる浸透剤としては、スルホコハク酸ジ
−２−エチルヘキシルナトリウム等のスルホコハク酸ジ
アルキルエステル塩、ドデシルベンゼンスルホン酸ナト
リウム等のアルキルベンゼンスルホン酸塩、ラウリル硫
酸エステルナトリウム等のアルキル硫酸エステル塩、ブ
チルナフタレンスルホン酸ナトリウム等のアルキルナフ
タレンスルホン酸塩、オレイン酸ブチルスルホン酸ナト
リウム等のオレイン酸アルキル硫化物、ノニルフェノー
ルのエチレンオキサイド付加物やオクチルフェールのエ
チレンオキサイド付加物等のアルキルフェノールのエチ
レンオキサイド付加物、ラウリルアルコールのエチレン
オキサイド付加物等の高級アルコールのエチレンオキサ
イド付加物などが挙げられる。これらの浸透剤は単独で
使用してもよいし、複数種を併用して使用してもよい。Examples of penetrants that can be used in the present invention include sulfosuccinic acid dialkyl ester salts such as di-2-ethylhexyl sodium sulfosuccinate, alkylbenzene sulfonates such as sodium dodecylbenzenesulfonate, alkyl sulfate ester salts such as sodium lauryl sulfate, and butyl. Alkylnaphthalene sulfonates such as sodium naphthalene sulfonate, Alkyl sulfides such as sodium oleate butyl sulfonate, ethylene oxide adducts such as ethylene oxide adduct of nonylphenol and ethylene oxide adduct of octylfere, lauryl Examples thereof include ethylene oxide adducts of higher alcohols such as ethylene oxide adducts of alcohols. These penetrants may be used alone or in combination of two or more.
浸透剤の塩化ビニル系樹脂への配合量は、塩化ビニル系
樹脂100重量部に対して0.3〜５重量部、好ましくは0.5
から３重量部であり、0.3重量部未満では充分な結露防
止性能が得られず、５重量部を越えると浸透剤が塩化ビ
ニル系樹脂層の表面にブリードアウトし、表面がベタつ
くばかりでなく、汚れが付着し易くなり好ましくない。The amount of the penetrant added to the vinyl chloride resin is 0.3 to 5 parts by weight, preferably 0.5 to 100 parts by weight of the vinyl chloride resin.
If the amount is less than 0.3 parts by weight, sufficient dew condensation preventing performance cannot be obtained, and if it exceeds 5 parts by weight, the penetrant bleeds out onto the surface of the vinyl chloride resin layer, and the surface is not only sticky. It is not preferable because dirt easily adheres.
本発明で使用する塩化ビニル系樹脂としては、例えば一
般の懸濁、乳化重合により得られる塩化ビニル単独重合
体、あるいは塩化ビニルと、酢酸ビニル、エチレン、プ
ロピレン、マレイン酸エステル、メタクリル酸メチル、
メタクリル酸エステル、アクリル酸エステル、高級ビニ
ルエーテルなどとの共重合体のほか、これらと他のポリ
マーとの混合物を含むものからなる。As the vinyl chloride resin used in the present invention, for example, general suspension, vinyl chloride homopolymer obtained by emulsion polymerization, or vinyl chloride, vinyl acetate, ethylene, propylene, maleic acid ester, methyl methacrylate,
In addition to copolymers with methacrylic acid esters, acrylic acid esters, higher vinyl ethers, etc., they include those containing mixtures of these with other polymers.
また、この塩化ビニル系樹脂に含有される可塑剤として
は、例えばフタル酸ジ−２−エチルヘキシルエステル
（DOP）、フタル酸ジノニルエステル（DNP）、フタル酸
ジイソノニルエステル（DINP）、フタル酸ブチルベンジ
ルエステル（BBP）、フタル酸ジブチルエステル（DBP）
などに代表される一般のフタル酸エステル系可塑剤、ア
ジピン酸ジオクチルエステル（DOA）、セバシル酸ジオ
クチルエステル（DOS）、アゼライン酸ジオクチルエス
テル（DOZ）に代表される一般の脂肪酸エステル系可塑
剤、トリメリット酸トリオクチルエステル（TOTM）に代
表されるトリメリット酸エステル系可塑剤、トリクレジ
ルフォスフェート（TCP）、トリキシリルフォスフェー
ト（TXP）などに代表されるトリアリールフォスフェー
ト系可塑剤のほか、ポリエステル系可塑剤などの高分子
系可塑剤、塩素化パラフィンなどの一般の一次、二次可
塑剤が使用できるが、そのほか塩化ビニル系樹脂の可塑
剤として一般に使用できるものであれば特に制限はな
い。Examples of the plasticizer contained in this vinyl chloride resin include di-2-ethylhexyl phthalate (DOP), dinonyl phthalate (DNP), diisononyl phthalate (DINP), butylbenzyl phthalate. Ester (BBP), phthalic acid dibutyl ester (DBP)
Such as general phthalate ester plasticizer, adipic acid dioctyl ester (DOA), sebacyl acid dioctyl ester (DOS), azelaic acid dioctyl ester (DOZ), general fatty acid ester plasticizer, tri In addition to trimellitic acid ester plasticizers such as meritic acid trioctyl ester (TOTM), triaryl phosphate plasticizers such as tricresyl phosphate (TCP) and trixylyl phosphate (TXP) Polymeric plasticizers such as polyester plasticizers and general primary and secondary plasticizers such as chlorinated paraffin can be used, but there is no particular limitation as long as they can be generally used as plasticizers for vinyl chloride resin. Absent.
これらの可塑剤は、目的とする種々の用途に合わせて、
塩化ビニル系樹脂に適宜量添加される。These plasticizers are suitable for various intended applications.
It is added in an appropriate amount to the vinyl chloride resin.
一般に添加される量は、塩化ビニル系樹脂100重量部に
対して７〜150重量部程度であるが、本発明においては
これに限定されるものではない。Generally, the amount added is about 7 to 150 parts by weight with respect to 100 parts by weight of the vinyl chloride resin, but the present invention is not limited thereto.
また、本発明においては塩化ビニル系樹脂に、安定剤と
して、例えばPb系、Ba−Zn系、Ca−Zn系、Cd系、Cu系、
Na−Zn系、Sn系などの塩化ビニル系樹脂に使用される一
般的な安定剤が使用できる。Further, in the present invention, to the vinyl chloride resin, as a stabilizer, for example, Pb-based, Ba-Zn-based, Ca-Zn-based, Cd-based, Cu-based,
Common stabilizers used for vinyl chloride resins such as Na-Zn and Sn can be used.
この安定剤の添加量は、塩化ビニル系樹脂100重量部に
対して0.5から10重量部、好ましくは２〜５重量部程度
である。The stabilizer is added in an amount of 0.5 to 10 parts by weight, preferably 2 to 5 parts by weight, based on 100 parts by weight of the vinyl chloride resin.
さらに、この塩化ビニル系樹脂中には、充填剤を添加す
ることができる。この充填剤としては、一般に塩化ビニ
ル系樹脂に添加配合できるものであればどのようなもの
であってもよい。一例を挙げれば、炭酸カルシウム、タ
ルク、ハイドロタルサイト、炭酸マグネシウム、水酸化
アルミニウムなどが例示できる。Further, a filler can be added to the vinyl chloride resin. As the filler, any filler can be generally used as long as it can be added and blended with the vinyl chloride resin. As an example, calcium carbonate, talc, hydrotalcite, magnesium carbonate, aluminum hydroxide and the like can be exemplified.
さらに、この塩化ビニル系樹脂中には必要に応じて難燃
性、顔料、紫外線吸収剤、帯電防止剤、老化防止剤、防
黴剤なども併用することができる。Further, flame retardant, pigment, ultraviolet absorber, antistatic agent, antiaging agent, antifungal agent and the like can be used in combination in the vinyl chloride resin, if necessary.
また、この塩化ビニル系樹脂がペースト加工の場合に
は、ミネラルスピリットなどの希釈溶剤も使用すること
ができる。Further, when the vinyl chloride resin is used for paste processing, a diluting solvent such as mineral spirit can also be used.
本発明に使用される基材としては、紙、織布、編布、不
織布などのほか、これらに塩化ビニル樹脂等の合成樹脂
を積層したものも使用できる。本発明の結露防止性シー
ト状物は、この基材上に塩化ビニル系樹脂層を形成する
ものであるが、塩化ビニル系樹脂層を形成する手段とし
ては、カレンダー法により形成してもよいし、塩化ビニ
ルペースト組成物の公知のドクターナイフコート、ロー
ルコート等にて基材上の全面に塗布してもよいし、ロー
タリースクリーン等の手段により模様状の部分的に塗布
してもよい。塩化ビニル系樹脂層にはエンボスにより凹
凸模様を施すこともできる。As the base material used in the present invention, paper, woven cloth, knitted cloth, non-woven cloth and the like, and those obtained by laminating synthetic resin such as vinyl chloride resin on these can also be used. The dew condensation-preventing sheet material of the present invention forms a vinyl chloride resin layer on this substrate, but the means for forming the vinyl chloride resin layer may be a calender method. The vinyl chloride paste composition may be applied to the entire surface of the substrate by a known doctor knife coating, roll coating, or the like, or may be partially applied in a pattern by a means such as a rotary screen. The vinyl chloride resin layer may be embossed to provide an uneven pattern.
本発明では、基材上の塩化ビニル系樹脂層中には、吸水
性高分子物質および浸透剤が含有されているので、室内
の湿気（水分）は塩化ビニル系樹脂層表面に凝結すると
同時に、塩化ビニル系樹脂層中の浸透剤の作用により塩
化ビニル系樹脂中の吸水性高分子物質や天然繊維質物質
に吸収されるため、塩化ビニル系樹脂層の表面には水分
がほとんど残留することがない。吸水性高分子物質や天
然繊維質物質に吸収された水分は室内が乾燥状態になっ
たときに、自然に空気中に放出されるので結露防止作用
も長期に亘り保有される。In the present invention, the vinyl chloride resin layer on the substrate contains a water-absorbing polymer and a penetrating agent, so that indoor humidity (moisture) condenses on the vinyl chloride resin layer surface, Due to the action of the penetrant in the vinyl chloride resin layer, it is absorbed by the water-absorbing polymer substances and natural fiber substances in the vinyl chloride resin layer, so that almost all the water remains on the surface of the vinyl chloride resin layer. Absent. The water absorbed by the water-absorbent polymer or the natural fibrous substance is naturally released into the air when the room is in a dry state, so that the dew condensation preventing action is retained for a long time.
以下、本発明の実施例を具体的に説明するが、本発明は
これら実施例に限定されるものではない。Examples of the present invention will be specifically described below, but the present invention is not limited to these examples.
なお、実施例中、結露防止性の試験方法は、下記に従っ
た。In the examples, the test method for preventing dew condensation was as follows.
《結露防止性試験》 80℃の湯浴上で、10cm角の試料片の表面を蒸気に当て、
試料片の表面に結露を生じるまでの時間を測定する。こ
の時間が長いほど結露防止性が優れているものである。<< Condensation prevention test >> On a water bath at 80 ° C, expose the surface of a 10 cm square sample piece to steam,
Measure the time until dew condensation occurs on the surface of the sample piece. The longer this time, the better the dew condensation prevention property.
〇……30分以内に結露する。○: Dew condensation occurs within 30 minutes.
×……１時間30分〜２時間以内に結露する。×: Condensation occurs within 1 hour 30 minutes to 2 hours.
実施例１〜３、比較例１〜５ 第１表の各配合処方からなる塩化ビニル樹脂配合物を混
合撹拌してペーストを作成した。これらペーストを秤量
80g/m2の裏打紙に270g/m2となるようにドクターナイフ
を用いて塗布し、加熱炉で170℃で加熱ゲル化し壁紙を
得た。Examples 1 to 3 and Comparative Examples 1 to 5 Vinyl chloride resin formulations each having the formulation shown in Table 1 were mixed and stirred to prepare pastes. Weigh these pastes
A backing paper of 80 g / m 2 was coated with a doctor knife so as to be 270 g / m 2, and heated at 170 ° C. in a heating furnace to gel and obtain a wallpaper.
これらの壁紙の結露防止性の試験結果はそれぞれ第１表
に示す通りであった。The results of the dew condensation prevention test of these wallpapers are shown in Table 1.
本発明の結露防止性シート状物は塩化ビニル系樹脂層中
に、吸水性高分子物質および浸透剤を含有しているの
で、室内の湿気（水分）は塩化ビニル系樹脂層表面に凝
結すると同時に、塩化ビニル系樹脂中の浸透剤の作用に
より塩化ビニル系樹脂中の吸水性高分子物質や天然繊維
質物質に浸透吸収されるため、塩化ビニル系樹脂層の表
面には水分がほとんど残留することがない。吸水性高分
子物質や天然繊維質物質に吸収された水分は室内が乾燥
状態になったときに、自然に空気中に放出されるので結
露防止作用も長期に亘り保有されるという効果を奏す
る。Since the dew condensation-preventing sheet material of the present invention contains a water-absorbing polymer substance and a penetrant in the vinyl chloride resin layer, indoor humidity (moisture) simultaneously condenses on the vinyl chloride resin layer surface. Since the action of the penetrant in the vinyl chloride resin permeates and absorbs into the water-absorbing polymer substances and natural fiber substances in the vinyl chloride resin, most of the water remains on the surface of the vinyl chloride resin layer. There is no. The water absorbed by the water-absorbent polymer substance or the natural fiber substance is naturally released into the air when the room is in a dry state, so that the dew condensation preventing effect can be retained for a long time.
Claims (4)
又は天然繊維質物質と浸透剤を含有する非発泡塩化ビニ
ル系樹脂層が形成されてなる結露防止性シート状物。1. A water-absorbing polymeric substance and / or
Alternatively, a dew-condensation-preventing sheet-like product formed by forming a non-foaming vinyl chloride resin layer containing a natural fiber substance and a penetrant.
び／又は天然繊維質物質と浸透剤を含有する非発泡塩化
ビニル系樹脂層が形成されてなる結露防止性シート状
物。2. A dew condensation-preventing sheet-like product comprising a non-foaming vinyl chloride resin layer containing a water-absorbing polymer substance and / or a natural fiber substance and a penetrant formed in a pattern on the surface of a substrate.
水性高分子物質及び／又は天然繊維質物質の含有量が３
〜30重量部であり、浸透剤の含有量が0.3〜５重量部で
ある請求項１〜２のいづれかに１項に記載の結露防止性
シート状物。3. The content of the water-absorbing polymer substance and / or the natural fiber substance is 3 with respect to 100 parts by weight of the vinyl chloride resin.
To 30 parts by weight, and the content of the penetrant is 0.3 to 5 parts by weight, the dew condensation preventing sheet material according to any one of claims 1 and 2.
アクリル酸共重合体、酢酸ビニル−アクリル酸エステル
共重合体ケン化物、イソブチレン−無水マレイン酸共重
合体変性物の架橋物、アクリル酸ソーダ重合体部分架橋
物、アクリルニトリルグラフト化デンプンの加水分解物
の群から選ばれた１種以上の吸水性高分子物質である請
求項１〜３のいずれか１項記載の結露防止性シート状
物。4. The water-absorbing polymer is vinyl alcohol
Acrylic acid copolymer, saponified vinyl acetate-acrylic acid ester copolymer, crosslinked product of isobutylene-maleic anhydride copolymer modified product, partially crosslinked product of sodium acrylate polymer, hydrolyzate of acrylonitrile-grafted starch The dew condensation-preventing sheet-like article according to any one of claims 1 to 3, which is one or more water-absorbing polymer substances selected from the group of.