JPH0651701A - Label for in-molding with coupon ticket - Google Patents
Label for in-molding with coupon ticketInfo
- Publication number
- JPH0651701A JPH0651701A JP6088491A JP6088491A JPH0651701A JP H0651701 A JPH0651701 A JP H0651701A JP 6088491 A JP6088491 A JP 6088491A JP 6088491 A JP6088491 A JP 6088491A JP H0651701 A JPH0651701 A JP H0651701A
- Authority
- JP
- Japan
- Prior art keywords
- label
- base material
- adhesive layer
- material layer
- coupon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、差圧成形、中空成形に
よって製造される合成樹脂製容器に容器成形と同時に貼
着されるクーポン券付インモールド用ラベルに関し、特
に、金型内に予めクーポン券を備えたラベルをセット
し、その上より熱可塑性樹脂を中空成形又は真空成形も
しくは圧空成形することによって、該ラベルを樹脂成形
容器と一体に成形させてクーポン券を備えた容器に加飾
することができるクーポン券付インモールド用ラベルに
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an in-mold label with a coupon ticket, which is attached to a synthetic resin container manufactured by differential pressure molding or hollow molding at the same time as the container is molded. A label with a coupon ticket is set, and the thermoplastic resin is blown or vacuum-molded or pressure-molded on the label to form the label integrally with the resin-molded container and decorate the container with the coupon ticket. The present invention relates to a label for in-mold coupon attachment.
【０００２】[0002]
【従来の技術】従来、金型内に予めラベルをインサート
させた後、該金型内で射出成形、中空成形、差圧成形、
発泡成形などによって容器を成形して、絵付けされた容
器が形成させている（特開昭５８−６９０１５号公報、
ヨーロッパ公開特許第２５４９２３号明細書参照）。こ
の様なラベル付きの樹脂成形容器の一部の商品としてク
ーポン券の付いたラベルが一体成形されたものがある
が、この様なインモールド用ラベルに用いられるクーポ
ン券付ラベルには、一般に天然紙又はプラスチックフィ
ルムを用いたラベルが使用されている。この様なクーポ
ン券の付いたラベルは、商品を買い上げた後で、使用者
がそのクーポン券の部分を剥離しなければならないの
で、該剥離を容易に行なうことができるように、その周
囲の切り取り部分にミシン目を入れ、更にそのクーポン
券の裏面側の部分に、前記容器とラベルとが一体成形の
際に接着させないように、該ラベルの接着剤塗布部分に
離型剤を塗工したり、或いは、その部分にだけ接着剤を
塗工しないようにしたものが使用されている。2. Description of the Related Art Conventionally, after inserting a label in a mold in advance, injection molding, hollow molding, differential pressure molding,
The container is molded by foam molding or the like to form a painted container (Japanese Patent Laid-Open No. 58-69015).
See European Published Patent No. 254923). As a part of such a resin molded container with a label, a label with a coupon ticket is integrally molded, but a label with a coupon ticket used for such an in-mold label is generally a natural product. Labels using paper or plastic film are used. Since such a label with a coupon ticket must be peeled off by the user after purchasing the product, the label around the label must be cut off so that the peeling can be performed easily. A perforation is made in the part, and a release agent is applied to the part of the back side of the coupon so that the container and the label are not adhered to each other when integrally molded. Alternatively, the one in which the adhesive is not applied only to that portion is used.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、このよ
うなクーポン券の付いたラベルでは、クーポン券部分が
大きくなったときには、ラベル貼着後の容器の収縮によ
りクーポン券部分が容器と未接着であるために浮き上が
り易く、ブリスター状態となって外観が悪くなったりす
るので、商品価値を著しく低下させてしまうといった欠
点があった。また、ラベルのクーポン券部分を切り離し
易くするためにミシン目を周囲に入れるミシン目加工を
施すことが必須であり、この様なミシン目加工はラベル
の製造コストを著しく高くさせている。しかも、該ミシ
ン目加工は安価に加工するため粗雑に加工すると切り離
しの際に横走りが生じて、目的のクーポン券が欠損して
しまったり、クーポン券の部分だけを切り離すことが困
難になるなどの欠点があった。However, in such a label with a coupon ticket, when the coupon ticket portion becomes large, the coupon ticket portion is not adhered to the container due to contraction of the container after the label is attached. As a result, the product tends to float up, and the appearance becomes poor in a blister state, which has a drawback that the product value is significantly reduced. Further, in order to make it easier to separate the coupon portion of the label, it is indispensable to perform perforation processing to insert perforations in the periphery, and such perforation processing makes the label manufacturing cost extremely high. Moreover, since the perforation processing is inexpensive, rough processing causes lateral running at the time of separation, resulting in loss of the intended coupon ticket, or difficulty in separating only the coupon ticket portion. There was a drawback.
【０００４】[0004]
［発明の概要］本発明者らは、上記問題点に鑑みて鋭意
研究を重ねた結果、基材層と接着層とからなるインモー
ルド用ラベルの基材層を二軸延伸配向フィルムにて形成
すると共に、前記接着層の一部に接着層の形成密度を５
０％以下とした帯状の引き剥がし部を形成して、該帯状
の引き剥がし部に相当する基材層の表面側にクーポン券
を印刷して、該ラベルの帯状の引き剥がし部の少なくと
も一端にノッチ部を形成すれば、切り離しのためのミシ
ン目を入れる工程が省略でき、ラベルを安価に製造する
ことができると共に、ラベルの切り離しの際にもミシン
目による横走りが生じなく、しかも、クーポン券の部分
が容器と一体成型された後でもラベルが容器より浮き上
がることがなく、外観の良好なミシン目の無いクーポン
券付インモールド用ラベルとすることができるとの知見
に基づき本発明を完成するに至ったものである。すなわ
ち、本発明のクーポン券付インモールド用ラベルは、基
材層と該基材層の容器に接着させる側の面に接着層を形
成したインモールド用ラベルにおいて、前記基材層が二
軸延伸配向フィルムにて形成すると共に、前記接着層の
一部に接着層の形成密度を５０％以下とした帯状の引き
剥がし部を形成して、該帯状の引き剥がし部に相当する
基材層の表面側にクーポン券が印刷されて、該ラベルの
引き剥がし部の少なくとも一端の２箇所にノッチ部を形
成させたことを特徴とするものである。[Summary of the Invention] The present inventors have conducted intensive studies in view of the above problems, and as a result, formed a base material layer of an in-mold label composed of a base material layer and an adhesive layer with a biaxially oriented film. In addition, the formation density of the adhesive layer is 5 in a part of the adhesive layer.
A strip-shaped peeling portion of 0% or less is formed, a coupon is printed on the surface side of the base material layer corresponding to the strip-shaped peeling portion, and at least one end of the strip-shaped peeling portion of the label is printed. If the notch is formed, the step of inserting perforations for separation can be omitted, the label can be manufactured at a low cost, the lateral running due to the perforations does not occur even when separating the label, and the coupon The present invention was completed based on the finding that the label does not float up from the container even after the ticket portion is integrally molded with the container, and that it can be a label for in-mold coupon coupons with a good perforation with a good appearance. It has come to do. That is, the label for in-mold with coupon according to the present invention is a label for in-mold in which an adhesive layer is formed on a surface of a base material layer and a side of the base material layer to be adhered to a container, wherein the base material layer is biaxially stretched. The surface of the base material layer corresponding to the strip-shaped peeling portion is formed with an oriented film, and a strip-shaped peeling portion having a formation density of the adhesive layer of 50% or less is formed on a part of the adhesive layer. It is characterized in that a coupon ticket is printed on the side, and notch portions are formed at at least one end of the peeling portion of the label.
【０００５】［発明の具体的説明］ [I] インモールド用ラベル （１）構 造 本発明のクーポン券付インモールド用ラベル１は、差圧
成形又は中空成形によって合成樹脂製容器が製造される
際に、金型内で容器に貼着されて、容器と一体になって
容器を加飾するためのラベルであって、その構造が、図
１及び図２に示すように、基材層２に二軸延伸配向フィ
ルムを使用して、該基材層２の容器と接着させる側に接
着層３を形成させたものから基本的に構成されたもの
で、該接着層３の一部分に接着層３の形成密度が５０％
以下とした帯状の引き剥がし部４を設けて、該帯状の引
き剥がし部４に相当する部分の基材層２側の表面にクー
ポン券５が印刷されていると共に、該帯状の引き剥がし
部４の少なくとも一端にノッチ部６を形成させたもので
ある。従って、インモールド成形により、容器に被着さ
れた本発明のクーポン券付インモールド用ラベル１は、
該ラベル１の帯状の引き剥がし部の末端４ａを指により
引き上げて、前記ノッチ部６よりラベル１のクーポン券
部分を引き裂けば、帯状の引き剥がし部４に相当する部
分をラベルより切り離してクーポン券５とすることがで
きるような構造になっている。[Detailed Description of the Invention] [I] In-Mold Label (1) Structure In the in-mold label 1 with a coupon ticket of the present invention, a synthetic resin container is manufactured by differential pressure molding or hollow molding. At this time, the label is attached to the container in the mold to decorate the container integrally with the container, the structure of which is as shown in FIG. 1 and FIG. A biaxially stretched oriented film is used to form an adhesive layer 3 on the side of the base material layer 2 to be adhered to the container, and the adhesive layer is formed on a part of the adhesive layer 3. Forming density of 3 is 50%
The strip-shaped peeling section 4 described below is provided, the coupon ticket 5 is printed on the surface of the base layer 2 side of the portion corresponding to the strip-shaped peeling section 4, and the strip-shaped peeling section 4 is provided. Is formed with a notch portion 6 at least at one end thereof. Therefore, the in-mold label with coupon 1 of the present invention, which is adhered to the container by in-mold molding, is
By pulling up the end 4a of the strip-shaped peeling portion of the label 1 with a finger and tearing the coupon ticket portion of the label 1 from the notch portion 6, the portion corresponding to the strip-shaped peeling portion 4 is cut off from the label. It has a structure that can be set to 5.
【０００６】（２）構成層 （ａ）基材層 本発明のクーポン券付インモールド用ラベル１において
基材層２として用いられる二軸延伸配向フィルムとして
は、ポリプロピレン、高密度ポリチレン、ポリ塩化ビニ
ル、ポリエチレンテレフタレート、ポリアミドなどの融
点が１３５〜２６４℃の熱可塑性樹脂の２軸延伸フィル
ム、或いはこれら樹脂に、炭酸カルシウム、硫酸カルシ
ウム、焼成クレイ、酸化チタン、タルクなどの無機微細
粉末を通常８〜５５重量％含有させた樹脂フィルムの２
軸延伸物、或いは、該延伸樹脂フィルムの表面上に炭酸
カルシウム、硫酸カルシウム、クレイ、酸化チタン、タ
ルクなどの無機充填剤含有ラテックス（塗工剤）を塗工
させたフィルム、或いは、前記延伸樹脂フィルムにアル
ミニウムなどの金属を蒸着させた金属泊積層フィルム、
或いは、前記無機微細粉末含有延伸樹脂フィルムの片面
または両面に無機微細粉末を８〜６５重量％含有する樹
脂フィルムの一軸延伸物を積層した積層合成紙（特公昭
４６−４０７９４号公報）などを挙げることができる。
このような基材層２は単層であっても、或いは、二層以
上の積層された構造のもの、或いは、これら基材層２に
更に表面層を積層したものであっても良い。該基材層２
は本発明のクーポン券付インモールド用ラベル１におい
て、該ラベル１のクーポン券部分５を帯状の引き剥がし
部４の末端のノッチ部６よりラベル１を切り裂いた際
に、前記ノッチ部６より帯状の引き剥がし部４の両側端
部４ｂに沿って切り離されてクーポン券５とすることが
できるように、配向された熱可塑性樹脂フィルムとする
ために、前記熱可塑性樹脂フィルムを二軸延伸すること
が重要である。クーポン券５の切り離し方向は、二軸延
伸配向フィルムの延伸方向と一致するので、クーポン部
分の印刷は基材フィルムの配向方向を考慮して行うべき
である。延伸倍率は切り離し方向が３〜１０倍であり、
該切り離し方向と直角の方向が通常３〜１０倍にて行な
われる。(2) Constituent layers (a) Base material layer The biaxially stretched oriented film used as the base material layer 2 in the label 1 for in-mold coupon coupons of the present invention includes polypropylene, high density polyethylene, and polyvinyl chloride. , Polyethylene terephthalate, polyamide and the like, biaxially stretched films of thermoplastic resins having a melting point of 135 to 264 ° C., or inorganic fine powders such as calcium carbonate, calcium sulfate, calcined clay, titanium oxide and talc are usually added to these resins. 2 of resin film containing 55% by weight
Axial stretched product, or a film obtained by coating the surface of the stretched resin film with a latex (coating agent) containing an inorganic filler such as calcium carbonate, calcium sulfate, clay, titanium oxide, talc, or the stretched resin. Metal foil laminated film in which metal such as aluminum is deposited on the film,
Alternatively, mention may be made of a laminated synthetic paper (Japanese Patent Publication No. 46-40794) in which a uniaxially stretched resin film containing 8 to 65% by weight of inorganic fine powder is laminated on one side or both sides of the inorganic fine powder-containing stretched resin film. be able to.
Such a base material layer 2 may be a single layer, may have a laminated structure of two or more layers, or may have a surface layer further laminated on these base material layers 2. The base material layer 2
In the in-mold label 1 with a coupon ticket of the present invention, when the label 1 is torn from the notch portion 6 at the end of the strip-shaped peeling portion 4 of the coupon ticket portion 5 of the label 1, the strip portion is formed from the notch portion 6. Biaxially stretching the thermoplastic resin film in order to obtain an oriented thermoplastic resin film so that the coupon voucher 5 can be separated along both end portions 4b of the peeling portion 4 of FIG. is important. Since the separating direction of the coupon ticket 5 coincides with the stretching direction of the biaxially stretched oriented film, the coupon portion should be printed in consideration of the orientation direction of the base film. The stretching ratio is 3 to 10 times in the separating direction,
The direction perpendicular to the separating direction is usually 3 to 10 times.
【０００７】（ｂ）接着層 本発明のクーポン券付インモールド用ラベル１におい
て、前記基材層２の二軸延伸配向フィルムの裏面側（樹
脂容器と接する側）に樹脂容器と融着してラベルを容器
に一体化させるために用いられる接着層３としては、一
般に低密度ポリエチレン、酢酸ビニル・エチレン共重合
体、エチレン・アクリル酸共重合体、エチレン・メタク
リル酸共重合体の金属塩などの、融点が８５〜１３５℃
のヒートシール性樹脂よりなるフィルム層が用いられ
る。これらヒートシール性樹脂は溶融してフィルム積層
する場合の肉厚は１〜３０μｍ、好ましくは１〜１０μ
ｍである。或いは、塗布して積層する場合には、該ヒー
トシール性樹脂のエマルジョンやヒートシール性樹脂を
トルエン、エチルセロソルブ等の溶剤に溶かした樹脂溶
液を基材層に塗布した後に乾燥させて接着層を形成す
る。しかし、本発明のクーポン券付インモールド用ラベ
ルにおいては、これら基材層である二軸延伸配向フィル
ムの裏面側全体に接着層３を形成させるものではなく、
該二軸延伸配向フィルムの裏面側の一部分に、接着層３
の形成密度が５０％以下、好ましくは５〜５０％とした
帯状の引き剥がし部４が設けられていて、この帯状の引
き剥がし部４に相当する部分に基材層２側の表面部分に
クーポン券５が印刷されて、この帯状の引き剥がし部４
を切り離してクーポン券５とすることができるように形
成されている。従って、帯状の引き剥がし部４の両端部
４ａがラベルの両端部１ａにまで達して、接着層３は帯
状の引き剥がし部４によって分断されている。また、該
引き剥がし部４の少なくとも一端のラベル１の端部１ａ
には１対のノッチ部６が形成されていて容易にクーポン
部分のラベル１を引き裂くことができるように形成され
ている。このヒートシール性樹脂フィルム層の存在によ
って、インモールド用ラベル１と樹脂容器との接着をよ
り強固にさせることができる。但し、成形される樹脂と
ラベル素材の樹脂とが同一のときは、接着層３を省略す
ることもできる。従って、容器に被着された本発明のク
ーポン券付インモールド用ラベル１は、該ラベル１の帯
状の引き剥がし部４の末端４ａを引き上げて前記ノッチ
部６よりラベル１を引き裂けば、帯状の引き剥がし部４
に相当する部分をラベル１より切り離してクーポン券５
とすることができるようになっている。また、引き剥が
し部４の占める面積はラベル１全体の面積の１０〜７０
％、好ましくは３０〜５０％である。ラベル１の裏面側
の帯状の引き剥がし部４の接着剤３ａは点状、水玉状、
帯状又は市松模様状に形成されることが好ましい。(B) Adhesive Layer In the in-mold label 1 with a coupon ticket of the present invention, the back side of the biaxially stretched oriented film of the base material layer 2 (the side in contact with the resin container) is fused with the resin container. The adhesive layer 3 used to integrate the label into the container is generally made of low density polyethylene, vinyl acetate / ethylene copolymer, ethylene / acrylic acid copolymer, metal salt of ethylene / methacrylic acid copolymer, or the like. , Melting point 85-135 ° C
A film layer made of the heat-sealable resin is used. The thickness of these heat-sealable resins when melted to form a film is 1 to 30 μm, preferably 1 to 10 μm.
m. Alternatively, when applied and laminated, an emulsion of the heat-sealable resin or a resin solution obtained by dissolving the heat-sealable resin in a solvent such as toluene or ethyl cellosolve is applied to the base material layer and then dried to form an adhesive layer. Form. However, in the in-mold label with a coupon ticket of the present invention, the adhesive layer 3 is not formed on the entire back surface side of the biaxially stretched and oriented film that is the base material layer,
The adhesive layer 3 is formed on a part of the back surface side of the biaxially oriented film.
The strip-shaped peeling portion 4 having a formation density of 50% or less, preferably 5 to 50% is provided, and the coupon corresponding to the surface portion on the base material layer 2 side corresponds to the strip-shaped peeling portion 4. A ticket 5 is printed, and this strip-shaped peeling portion 4
Is formed so that the coupon ticket 5 can be separated. Therefore, both ends 4a of the strip-shaped peeling portion 4 reach the both ends 1a of the label, and the adhesive layer 3 is divided by the strip-shaped peeling portion 4. In addition, the end portion 1a of the label 1 on at least one end of the peeling portion 4
Is formed with a pair of notches 6 so that the label 1 of the coupon portion can be easily torn. Due to the presence of this heat-sealable resin film layer, the bond between the in-mold label 1 and the resin container can be made stronger. However, when the resin to be molded and the resin of the label material are the same, the adhesive layer 3 can be omitted. Therefore, the label 1 for in-mold with coupon of the present invention attached to the container has a strip-like shape by pulling up the end 4a of the strip-shaped peeling portion 4 of the label 1 and tearing the label 1 from the notch portion 6. Peeling off part 4
Coupon voucher 5
And can be. The area occupied by the peeling section 4 is 10 to 70 of the total area of the label 1.
%, Preferably 30 to 50%. The adhesive 3a of the strip-shaped peeling portion 4 on the back surface side of the label 1 has a dot shape, a dot shape,
It is preferably formed in a strip shape or a checkered pattern.
【０００８】[II] インモールド用ラベルの製造 （１）基材層（二軸延伸配向フィルム）の形成 （ａ）延 伸 本発明のクーポン券付インモールド用ラベル１を製造す
るには、先ず前記融点が１３５〜２６４℃の熱可塑性樹
脂、或いは、該熱可塑性樹脂に前記無機微細粉末を通常
８〜５５重量％含有させて形成した無機微細粉末含有樹
脂、或いは、これら樹脂に後記接着層３となるヒートシ
ール性樹脂を積層させた積層体を、インフレーションフ
ィルム成形やマンドレルを用いた同時二軸延伸フィルム
成形、或いは、Ｔダイにて押し出し、ロールにて縦方向
に延伸させた後、両側端をクリップにて掴んで横方向に
延伸させる逐次二軸延伸フィルム成形などにより二軸延
伸して二軸延伸配向フィルムを製造する。上記基材層２
となる二軸延伸配向フィルムを製造する際に行なわれる
延伸は、該フィルムの押出方向に通常３〜１０倍、好ま
しくは４〜８倍に延伸される。また該フィルムの幅方向
に通常３〜１０倍、好ましくは４〜１０倍に延伸され
る。該延伸は基材層２の樹脂の融点よりも低い温度で行
なわれる。また、前記延伸が基材層２と接着層３との積
層後に行なわれる場合には、接着層３のヒートシール性
樹脂の融点以上の温度で行われる。それ故、基材層２は
配向されるが、ヒートシール層は配向されることがな
い。[II] Production of in-mold label (1) Formation of base material layer (biaxially stretched oriented film) (a) Elongation In order to produce the in-mold label 1 with a coupon according to the present invention, first, A thermoplastic resin having a melting point of 135 to 264 ° C., or an inorganic fine powder-containing resin formed by adding 8 to 55% by weight of the inorganic fine powder to the thermoplastic resin, or an adhesive layer 3 to be described later. The heat-sealable resin is laminated on the laminate to form a biaxially stretched film using an inflation film or a mandrel, or it is extruded with a T-die and stretched in the longitudinal direction with a roll. Is gripped with a clip and stretched in the transverse direction by biaxial stretching such as sequential biaxial stretching film molding to produce a biaxially oriented film. The base material layer 2
The stretching performed when producing the biaxially stretched oriented film is usually 3 to 10 times, preferably 4 to 8 times in the extrusion direction of the film. The film is usually stretched 3 to 10 times, preferably 4 to 10 times in the width direction. The stretching is performed at a temperature lower than the melting point of the resin of the base material layer 2. When the stretching is performed after the base material layer 2 and the adhesive layer 3 are laminated, the stretching is performed at a temperature equal to or higher than the melting point of the heat-sealing resin of the adhesive layer 3. Therefore, the base material layer 2 is oriented, but the heat seal layer is not oriented.
【０００９】（ｂ）積 層 前記基材層２の二軸延伸配向フィルムの表面上には、更
に、前記無機充填剤を含有するラテックス（塗工剤）を
塗工させて塗工層を形成したり、アルミニウムなどの金
属を蒸着させて金属箔を形成したり、前記無機微細粉末
含有樹脂フィルムの一軸延伸物を積層させた積層体とす
ることもできる。(B) Laminated layer On the surface of the biaxially stretched oriented film of the base material layer 2, a latex (coating agent) containing the inorganic filler is further applied to form a coating layer. Alternatively, a metal foil such as aluminum may be vapor-deposited to form a metal foil, or a uniaxially stretched resin film containing the inorganic fine powder may be laminated to form a laminate.
【００１０】（２）接着層の形成 （ａ）接着層 本発明のクーポン券付インモールド用ラベル１の製造に
おいて、前記基材層２の二軸延伸配向フィルムの裏面側
（樹脂容器と接する側）に樹脂容器と融着してラベル１
を接着させるために接着層３が積層される。該接着層３
は、前記融点が８５〜１３５℃のヒートシール性樹脂よ
りなる素材が用いられ、該ヒートシール性樹脂よりなる
フィルム層を融着により基材層２の裏面側に積層させた
り、或いは、該ヒートシール性樹脂のエマルジョンや、
ヒートシール性樹脂を溶剤に溶かした溶液を塗布した後
に乾燥させて基材層２の裏面側に積層させる。しかし、
本発明のクーポン券付インモールド用ラベル１において
は、これら接着層３を基材層２である二軸延伸配向フィ
ルムの裏面側全体に形成させるのではなく、該二軸延伸
配向フィルムの裏面側に、接着層３の形成密度が５０％
以下とした帯状の引き剥がし部４を形成するように、該
帯状の引き剥がし部４を除く部分に接着層３が設けられ
る。ここで接着層の形成密度とは、クーポン部分４の占
める面積に対し、接着層３ａが占める面積割合をいう。(2) Formation of Adhesive Layer (a) Adhesive Layer In the production of the in-mold label 1 with a coupon according to the present invention, the back side of the biaxially stretched oriented film of the base material layer 2 (the side in contact with the resin container). ) Label 1 by fusion with resin container
An adhesive layer 3 is laminated to bond the two. The adhesive layer 3
Is made of a material made of a heat-sealable resin having a melting point of 85 to 135 ° C., a film layer made of the heat-sealable resin is laminated on the back surface side of the base material layer 2 by fusion bonding, or the heat is used. Emulsion of sealing resin,
A solution in which a heat-sealable resin is dissolved in a solvent is applied and then dried to be laminated on the back surface side of the base material layer 2. But,
In the in-mold label 1 with a coupon ticket of the present invention, these adhesive layers 3 are not formed on the entire back surface side of the biaxially stretched oriented film that is the base material layer 2, but the back surface side of the biaxially stretched oriented film. And the formation density of the adhesive layer 3 is 50%
The adhesive layer 3 is provided on the portion excluding the strip-shaped peeling portion 4 so as to form the strip-shaped peeling portion 4 described below. Here, the formation density of the adhesive layer means the ratio of the area occupied by the adhesive layer 3a to the area occupied by the coupon portion 4.
【００１１】（ｂ）塗 布 該帯状の引き剥がし部４の形成は、図３に示されるよう
な塗布装置を用いて、ヒートシール性樹脂のエマルジョ
ンや、該樹脂を溶剤に溶かした溶液７を貯蔵する貯槽８
の樹脂溶液７中に一部分を浸漬したロール９と接触して
回転するグラビアロール１０によって基材層２の裏面側
に塗布し、乾燥させて接着層３を形成させる。上記グラ
ビアロール１０の表面は、図４に示されるように、両端
に接着層３ｂ，３ｂを形成する帯状凸部１０ｂを形成
し、その中央部に接着層３の形成密度が％以下の帯状の
引き剥がし部４が形成されている。該帯状の引き剥がし
部４を形成する部分はロール１０の表面に分散された点
状の接着層塗布部分１０ａにより、図１にて示されるよ
うな模様に、すなわち、点状の接着層３ａとして部分的
に塗布される。しかしながら、クーポン券付インモール
ド用ラベル１において帯状の引き剥がし部４でないラベ
ル１の裏面側の剥離しない部分の接着層３ｂには５０％
以上の高面積率にて、好ましくは全面に接着層３ｂが塗
布される。従って、この様にして塗布されたラベル１の
裏面側の接着層３の一部には、図１に示すように、クー
ポン券５部分が引き剥がし可能なように接着層３が余り
塗布されていない引き剥がし部４が帯状に形成されてい
る。他の方法としては、基材層の２軸延伸フィルムに押
出ラミネートされたヒートシール層の表面に、エンボス
ロール等を用い、シリコーン樹脂等の剥離剤をドット状
にクーポン部分４の面積に対して５０〜９５％の割合で
塗布する方法である。該ラベル１の断面は、図２に示す
ように、クーポン券５部分として引き剥がされる部分４
には接着層３の形成密度が前記値に示すように少なく形
成することが重要である。(B) Coating Fabric The strip-shaped peeling portion 4 is formed by using a coating device as shown in FIG. 3 and using an emulsion of a heat-sealable resin or a solution 7 obtained by dissolving the resin in a solvent. Storage tank 8
The back side of the base material layer 2 is coated with a gravure roll 10 that rotates by contacting a roll 9 partially immersed in the resin solution 7 and dried to form an adhesive layer 3. As shown in FIG. 4, the surface of the gravure roll 10 has a strip-shaped convex portion 10b forming the adhesive layers 3b, 3b at both ends, and a strip-shaped convex portion 10b in which the formation density of the adhesive layer 3 is not more than%. A peeling portion 4 is formed. The portion forming the strip-shaped peeling portion 4 is formed by the dot-shaped adhesive layer application portion 10a dispersed on the surface of the roll 10 into a pattern as shown in FIG. 1, that is, as the dot-shaped adhesive layer 3a. Partially applied. However, in the label 1 for in-mold with coupon ticket, the adhesive layer 3b in the non-peeling portion of the back side of the label 1 which is not the strip-shaped peeling portion 4 is 50%.
With the above high area ratio, the adhesive layer 3b is preferably applied over the entire surface. Therefore, as shown in FIG. 1, a part of the adhesive layer 3 on the back surface side of the label 1 applied in this way is coated with an excessive amount of the adhesive layer 3 so that the coupon ticket 5 portion can be peeled off. The peeling part 4 which is not formed is formed in a strip shape. As another method, an embossing roll or the like is used on the surface of the heat-sealing layer extrusion-laminated on the biaxially stretched film of the base material layer, and a release agent such as a silicone resin is dot-shaped with respect to the area of the coupon portion 4. It is a method of applying at a ratio of 50 to 95%. As shown in FIG. 2, the cross section of the label 1 is a portion 4 to be peeled off as a coupon 5 portion.
It is important that the formation density of the adhesive layer 3 is small as shown in the above value.
【００１２】（ｃ）その他の処理 前記延伸後の積層構造フィルムは、必要であれば、コロ
ナ放電加工、火炎処理、プラズマ処理などを施すことに
よって、表面の印刷性、接着性を改善しておくことがで
きる。(C) Other Treatments The stretched laminated structure film is subjected to corona discharge machining, flame treatment, plasma treatment, etc., if necessary, to improve the surface printability and adhesiveness. be able to.
【００１３】（３）印 刷 前記基材層２の表面側、例えば紙状層には、前記帯状の
引き剥がし部４に相当する部分にグラビア印刷、オフセ
ット印刷、フレキソ印刷、スクリーン印刷などの各種の
印刷方法によりクーポン券５が印刷され、その他の部分
に商品名、製造元、販売会社名、キャラクター、バーコ
ード、使用方法などが印刷される。このようなインモー
ルド用ラベル１は、容器表面の一部に貼着される部分的
なものであっても良いが、通常は差圧成形ではカップ状
容器の側面を取り巻くブランクとして、中空成形では瓶
状容器の表及び裏に貼着されるラベル１として製造され
る。(3) Printing Various kinds of gravure printing, offset printing, flexographic printing, screen printing, etc. are applied to the surface side of the base material layer 2, for example, the paper-like layer, in the portion corresponding to the strip-shaped peeling portion 4. The coupon ticket 5 is printed by the printing method of No. 3, and the product name, manufacturer, sales company name, character, bar code, usage method, etc. are printed on the other portions. Such an in-mold label 1 may be a partial label which is attached to a part of the container surface, but is usually used as a blank surrounding the side surface of the cup-shaped container in differential pressure molding, and in hollow molding. It is manufactured as the label 1 attached to the front and back of the bottle-shaped container.
【００１４】（４）抜打加工及びノッチの形成 上記印刷が施されたインモールド用ラベル１は、抜打加
工により必要な形状、寸法のラベル１に分離されが、こ
の時、前記接着層を印刷した引き剥がし部分４の少なく
とも一端には、Ｖ型、Ｉ型などの各種形状のノッチ部６
が形成される。(4) Stamping and Notch Formation The in-mold label 1 printed as above is separated into the label 1 having the required shape and dimensions by stamping. At this time, the adhesive layer is removed. At least one end of the printed peeling portion 4 has a notch portion 6 of various shapes such as V-shape and I-shape.
Is formed.
【００１５】[III] 貼着 本発明のクーポン券付インモールド用ラベル１は、真空
成形、圧空成形などの差圧成形や、パリソンを圧空によ
り金型内壁に圧着する中空成形などの金型のキャビティ
内に印刷側が金型壁面に接するように設置した後、金型
の吸引により金型内壁に固定され、次いで容器成形材料
樹脂のシートの溶融物が金型に導かれ、常法により成形
され、ラベル１が容器外壁に一帯に融着された容器が成
形される。この様にして成形された容器は、ラベル１が
金型内で固定された後に、ラベル１と樹脂容器が一体に
成形されるので、ラベル１の変形もなく、容器本体とラ
ベル１の密着強度が強固であり、ブリスターも無く、ラ
ベルにより加飾された外観が良好な容器である。しかし
ながら、前記帯状の引き剥がし部４に相当する部分には
クーポン券５が印刷されており、その端部１ａを指によ
り摘まんで引っ張れば、前記ノッチ部６より帯状の引き
剥がし部４に沿って切り離されて、クーポン券５とする
ことができる。[III] Adhesion The label 1 for in-mold with coupon according to the present invention is applied to a differential pressure molding such as vacuum molding or pressure molding, or a mold such as hollow molding in which a parison is pressure-bonded to the inner wall of the mold. After the printing side is installed in the cavity so that it touches the wall surface of the mold, it is fixed to the inner wall of the mold by suction of the mold, and then the molten material of the resin sheet for the container molding material is guided to the mold and molded by the usual method. A container in which the label 1 is fused on the outer wall of the container is formed. In the container thus molded, since the label 1 and the resin container are integrally molded after the label 1 is fixed in the mold, the label 1 is not deformed and the adhesion strength between the container body and the label 1 is high. Is strong, has no blister, and has a good appearance decorated with a label. However, a coupon voucher 5 is printed on a portion corresponding to the strip-shaped peeling portion 4, and if the end portion 1a is grasped by a finger and pulled, the notch portion 6 extends along the strip-shaped peeling portion 4. It can be separated to form a coupon 5.
【００１６】[0016]
実施例１基材層（三層構造）の製造 三菱油化（株）製ポリプロピレン「三菱ノーブレン Ｍ
Ａ−６」（商品名）６９部、三菱油化（株）製高密度ポ
リエチレン「ユカロンハード ＥＹ−４０」（商品名）
８部、耐候性改良剤として平均粒径１μｍの酸化チタン
０．８部、三共（株）製ビス（２，２，６，６−テトラ
メチル−４−ピペリジル）セバケート「サノール ＬＳ
−７７０」（商品名）０．０６部、クレイ２２．２部、
酸化防止剤０．３部及び分散剤としてオレイン酸０．１
部よりなる組成物を、押出機を用いて溶融・混練させた
後、ダイより２００℃の温度でシート状に押し出し、該
シートを約５０℃の温度にまで冷却した。次いで、この
シートを１５０℃の温度にまで再度加熱した後、ロール
群の周速差を利用して、縦方向に４倍に延伸した。一
方、ポリプロピレン（三菱ノーブレン ＭＡ−６）５５
部、平均粒径０．８μｍの重質炭酸カルシウム４２部、
平均粒径１μｍの酸化チタン３部、ビス（２，２，６，
６−テトラメチル−４−ピペリジル）セバケート０．４
部、坑酸化剤としてヨシノックスＢＨＴ、マーク３２９
及びイルガノックス−１０７６をそれぞれ０．１部、及
び、オレイン酸０．１部の割合にて配合した組成物を、
２台の押出機を用いてそれぞれ溶融混練して、２台のダ
イより２００℃の温度でシート状に押し出した。そし
て、このダイより押し出したシート状物を、前記縦軸延
伸されたシートの両側面にラミネートし、一旦、室温よ
り２０℃高い温度にまで冷却させた後、約１５５℃の温
度にまで再加熱して、テンターを用いて横方向に８倍延
伸しさせた後、１６０℃のオーブン中を通過させて熱セ
ットし、更に、コロナ放電処理して、中間層（基材層）
の二軸延伸フィルムの肉厚が７０μｍ、表面・裏面層の
一軸延伸フィルムの肉厚が各々１０μｍの三層構造の印
刷、筆記性の優れた合成紙を得た。この合成紙の各層に
は微細なミクロボイドを多数有したものであり、合成紙
全体の比重は０．７１２であった。Example 1 Production of base material layer (three-layer structure) Polypropylene "Mitsubishi Noblen M" manufactured by Mitsubishi Yuka Co., Ltd.
A-6 "(trade name) 69 parts, Mitsubishi Petrochemical Co., Ltd. high density polyethylene" Yukaron Hard EY-40 "(trade name)
8 parts, 0.8 part of titanium oxide having an average particle size of 1 μm as a weather resistance improver, bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate “Sanol LS” manufactured by Sankyo Co., Ltd.
-770 "(trade name) 0.06 parts, clay 22.2 parts,
Antioxidant 0.3 parts and oleic acid 0.1 as dispersant
The composition consisting of parts was melted and kneaded using an extruder, and then extruded into a sheet form at a temperature of 200 ° C. from a die, and the sheet was cooled to a temperature of about 50 ° C. Next, this sheet was heated again to a temperature of 150 ° C. and then stretched 4 times in the machine direction by utilizing the peripheral speed difference of the roll group. On the other hand, polypropylene (Mitsubishi Noblen MA-6) 55
Parts, 42 parts of ground calcium carbonate having an average particle size of 0.8 μm,
3 parts of titanium oxide having an average particle diameter of 1 μm, bis (2, 2, 6,
6-tetramethyl-4-piperidyl) sebacate 0.4
Part, Yoshinox BHT, Mark 329 as anti-oxidant
And Irganox-1076 at a ratio of 0.1 part and 0.1 part of oleic acid, respectively,
Each of them was melt-kneaded by using two extruders and extruded into a sheet shape from two dies at a temperature of 200 ° C. Then, the sheet-like material extruded from this die is laminated on both sides of the longitudinally stretched sheet, cooled once to a temperature 20 ° C. higher than room temperature, and then reheated to a temperature of about 155 ° C. Then, it was stretched 8 times in the transverse direction using a tenter, passed through an oven at 160 ° C. for heat setting, and further subjected to corona discharge treatment to form an intermediate layer (base material layer).
A biaxially stretched film having a thickness of 70 μm and a uniaxially stretched film for the front and back layers each having a thickness of 10 μm were obtained. Each layer of this synthetic paper had many fine microvoids, and the specific gravity of the entire synthetic paper was 0.712.
【００１７】接着層の積層 次いで、この三層構造の合成紙の裏面側に、エチレン・
酢酸ビニル共重合体樹脂（酢酸ビニル含量１４重量％）
５５重量％のトルエン溶液よりなる接着剤を、図４に示
すようなグラビアロールを用いて図３に示すような塗布
装置を用いて、帯状の引き剥がし部の接着部のパターン
が、 接着層の直径 ２ｍｍφ ピッチ間隔 ８ｍｍ 引き剥がし部の幅 ２５ｍｍ の図１に示すようなパターンの接着層の印刷を施した。 Lamination of Adhesive Layer Next, ethylene.
Vinyl acetate copolymer resin (vinyl acetate content 14% by weight)
An adhesive composed of a 55 wt% toluene solution was used to apply a gravure roll as shown in FIG. 4 and an applicator as shown in FIG. It was subjected to printing of the adhesive layer of the pattern shown in Figure 1 having a diameter of 2 mm phi pitch 8mm peeling unit width 25mm of.
【００１８】印 刷 次いで、このようにして得られたインモールド用ラベル
をコロナ放電加工した後、基材層の表面側の紙状層に印
刷が施され、これによって、前記帯状の引き剥がし部に
相当する部分にクーポン券を印刷し、その他の部分に商
品名、製造元、販売会社名、キャラクター、バーコー
ド、使用方法などを印刷した。 Printing, then, the in-mold label thus obtained is subjected to corona discharge machining, and then printed on the paper-like layer on the front surface side of the base material layer, whereby the strip-shaped peeling portion is formed. The coupon ticket was printed on the part corresponding to, and the product name, manufacturer, sales company name, character, bar code, usage etc. were printed on the other parts.
【００１９】抜打加工及びノッチの形成 このようにして印刷されたインモールド用ラベルを、抜
打加工により長さ７ｃｍ、幅９ｃｍの図１に示すような
形状、寸法のラベルに分離した。この時、該点模様にヒ
ートシール樹脂を印刷した引き剥がし部分の両末端に
は、ラベルに一対のＶ型のノッチを形成させた。 Stamping and Notch Formation The in-mold label thus printed was separated by stamping into a label having a length of 7 cm and a width of 9 cm as shown in FIG. At this time, a pair of V-shaped notches were formed on the label at both ends of the peeled-off portion where the heat seal resin was printed on the dot pattern.
【００２０】貼 着 このインモールド用ラベル１をブロー成形用割型の一方
に真空を利用して印刷面側（Ｂ層）が金型と接するよう
に固定した後、高密度ポリエチレン（融点１３４℃）の
パリソンを１５５℃（低温パリソン）及び２０５℃（高
温パリソン）で溶融押出し、次いで割型を型締めした
後、４．２kg／cm2 の圧空をパリソン内に供給し、パリ
ソンを膨脹させて容器状とすると共にインモールド用ラ
ベルと融着させ、次いで該型を冷却した後、型開きをし
て中空容器を取り出した。この中空容器は、印刷の退色
もなく、ラベルの収縮やブリスターの発生も見受けられ
なかった。また、クーポン券部分の容器からの浮き上が
りも無かった。このラベルのＶ型ノッチ部分を指により
引き裂いたところ、クーポン券の部分は用意に引き裂く
ことができた。自動ラベル給紙装置によるブロー成形用
割型へのラベルの供給は１００枚連続で行ったがミス
（型よりラベルが落ちるなど）は１回も無かった。 Adhesion This in-mold label 1 was fixed to one of the blow molding split molds using vacuum so that the printing surface side (layer B) was in contact with the mold, and then high density polyethylene (melting point: 134 ° C.) was used. ) Is melt-extruded at 155 ° C (low temperature parison) and 205 ° C (high temperature parison), then the split mold is clamped, and 4.2 kg / cm 2 of compressed air is supplied into the parison to expand the parison. The container was formed into a container and was fused with an in-mold label, and then the mold was cooled, and then the mold was opened to take out a hollow container. In this hollow container, there was no discoloration of printing, and neither contraction of labels nor occurrence of blisters was observed. In addition, the coupon ticket part did not rise from the container. When the V-shaped notch part of this label was torn with a finger, the coupon part could be easily torn. 100 labels were continuously supplied to the split mold for blow molding by the automatic label feeding device, but there was no mistake (such as the label dropping from the mold).
【００２１】実施例２ 塗布面積を４５％とする他は実施例１と同様にしてラベ
ルを得た。結果を表１に示す。Example 2 A label was obtained in the same manner as in Example 1 except that the coating area was 45%. The results are shown in Table 1.
【００２２】実施例３〜４二軸単層構造フィルムの製造 ポリスチレン３２部、高密度ポリエチレン５５部、焼成
クレイ１０部及び酸化チタン３部よりなる混合物を、押
出機を用いて溶融混練した後、２００℃の温度にてダイ
よりシート状に押し出し、その後１２９℃の温度にまで
冷却させた。次いで、縦方向に４．５倍に延伸を行なっ
た後、その片面にエチレン・酢酸ビニル共重合体フィル
ムを２２０℃で押出ラミネートし、次いで横方向に５倍
延伸した。そして、これをコロナ放電処理した。次に、
この積層延伸フィルムの共重合体フィルム面に東洋イン
キ製造（株）の離型剤“ＯＰワニス”をグラビアロール
にてドット状に塗布し、その後耳部をカッティングし
て、肉厚が８０μｍのラベルを製造した。以下、実施例
１と同様にして容器を形成し、表１に示すラベル付き容
器を得た。Examples 3 to 4 Production of Biaxial Single Layer Structure Film A mixture of 32 parts of polystyrene, 55 parts of high density polyethylene, 10 parts of calcined clay and 3 parts of titanium oxide was melt-kneaded using an extruder, The sheet was extruded from the die at a temperature of 200 ° C., and then cooled to a temperature of 129 ° C. Then, the film was stretched 4.5 times in the machine direction, and an ethylene / vinyl acetate copolymer film was extrusion-laminated at 220 ° C. on one surface of the film, and then stretched 5 times in the cross direction. Then, this was subjected to corona discharge treatment. next,
A release agent "OP Varnish" from Toyo Ink Mfg. Co., Ltd. was applied to the copolymer film surface of this laminated stretched film in a dot shape with a gravure roll, and then the ears were cut to obtain a label having a thickness of 80 μm. Was manufactured. Hereinafter, a container was formed in the same manner as in Example 1 to obtain the labeled container shown in Table 1.
【００２３】[0023]
【表１】 [Table 1]
【００２４】なお、評価方法は以下に示す基準で行なっ
た。 １） ブリスターの発生 ・クーポン券部分のラベルの浮き上りがないもの…○ ・クーポン券部分にラベルの浮き上りのあるもの…× ２） クーポン券部分のラベル接着強度 クーポン券部分の貼着されたラベル１５ｍ／ｍ幅の接着
強度（Ｔ字剥離）を測定した。 ３） クーポン券部の剥離状態 ・クーポン券部分のみ手剥離により横走りなく剥離出来
たもの…○ ・クーポン券部分の手剥離時に横走りが発生しクーポン
券部分だけを正常な形で剥離出来なかったもの又は剥離
が困難なもの…×The evaluation method was performed according to the following criteria. 1) Occurrence of blister ・ The label of the coupon ticket does not rise… ○ ・ The label of the coupon ticket has risen… × 2) The adhesive strength of the label on the coupon ticket The coupon ticket is attached The adhesive strength (T-shaped peeling) of the label having a width of 15 m / m was measured. 3) Peeling state of the coupon ticket part ・ Only the coupon ticket part could be peeled off without lateral running by hand peeling ... ○ ・ Horizontal running occurred when the coupon ticket part was manually peeled off, and only the coupon ticket part could not be peeled in a normal form Tacked or difficult to peel off ... ×
【００２５】[0025]
【発明の効果】この様に形成した本発明のクーポン券付
インモールド用ラベルは、基材層に二軸延伸配向フィル
ムを使用し、裏面側の容器に接着する側の一部に接着剤
の塗布率を５０％以下とした帯状の引き剥がし部を設け
て、その表面側の部分にクーポン券を印刷してあり、し
かも、該ラベルの帯状の引き剥がし部の少なくとも一端
にノッチ部が形成されているので、従来のラベルのよう
な切り離しのためのミシン目を入れる工程が省略でき、
ラベルを安価に製造することができると共に、ラベルの
切り離しの際にもミシン目による横走りが生じなく、目
的のクーポン券が欠損してしまったりすることが無く、
クーポン券の部分だけを切り離すことができる。しか
も、クーポン券の部分が容器と一体成型された後でもラ
ベルが容器より浮き上がることがなく、外観の良好なミ
シン目の無いクーポン券付インモールド用ラベルとする
ことができる。The label for coupon in-molding of the present invention thus formed uses a biaxially stretched oriented film for the base material layer, and a part of the adhesive side is adhered to the container on the back side. A strip-shaped peeling portion having an application rate of 50% or less is provided, and a coupon ticket is printed on the surface side portion thereof, and a notch portion is formed on at least one end of the strip-shaped peeling portion of the label. Therefore, it is possible to omit the step of inserting perforations for separation such as conventional labels,
Along with being able to manufacture the label at a low cost, there is no lateral running due to perforations even when the label is cut off, and the intended coupon will not be lost,
Only the coupon part can be separated. In addition, the label does not float up from the container even after the portion of the coupon ticket is integrally molded with the container, and the in-mold label with a coupon ticket having a good appearance and without perforations can be obtained.
【図１】本発明のクーポン券付インモールド用ラベルの
裏面図。FIG. 1 is a back view of a label for in-mold with coupon according to the present invention.
【図２】図１のＡ−Ａ線断面図。FIG. 2 is a sectional view taken along line AA of FIG.
【図３】ヒートシール性樹脂をグラビアロールを用いて
液状で塗布して接着層を形成するための塗布装置断面
図。FIG. 3 is a sectional view of a coating apparatus for coating a heat-sealable resin in a liquid form using a gravure roll to form an adhesive layer.
【図４】図３にて用いたグラビアロールの斜視図。FIG. 4 is a perspective view of the gravure roll used in FIG.
１ クーポン券付インモールド用ラベル １ａ ラベルの端部 ２ 基材層 ３ 接着層 ３ａ 接着層 ３ｂ ラベルの裏面側の剥離しない部分の接着層 ４ 引き剥がし部 ４ａ 引き剥がし部の末端 ４ｂ 引き剥がし部の側端部 ５ クーポン券 ６ ノッチ部 ７ ヒートシール性樹脂のエマルジョンや、該樹脂を溶
剤に溶かした樹脂溶液 ８ 貯槽 １０ グラビアロール １０ａ 点状の接着層塗布部分 １０ｂ 帯状凸部1 Label for in-mold with coupon ticket 1a Label edge 2 Base material layer 3 Adhesive layer 3a Adhesive layer 3b Adhesive layer on the back side of the label that does not peel off 4 Peel off part 4a Peel off end 4b Peel off part Side end part 5 Coupon voucher 6 Notch part 7 Emulsion of heat sealable resin or resin solution in which the resin is dissolved in a solvent 8 Storage tank 10 Gravure roll 10a Dot-shaped adhesive layer application part 10b Band-shaped convex part
Claims (1)
面に接着層を形成したインモールド用ラベルにおいて、
前記基材層が二軸延伸配向フィルムにて形成すると共
に、前記接着層の一部に接着層の形成密度を５０％以下
とした帯状の引き剥がし部を形成して、該帯状の引き剥
がし部に相当する基材層の表面側にクーポン券が印刷さ
れて、該ラベルの引き剥がし部の少なくとも一端の２箇
所にノッチ部を形成させたことを特徴とするクーポン券
付インモールド用ラベル。1. A label for in-mold comprising a base material layer and an adhesive layer formed on the surface of the base material layer on the side to be adhered to a container,
The base material layer is formed of a biaxially stretched oriented film, and a strip-shaped peeling portion having a formation density of the adhesive layer of 50% or less is formed in a part of the adhesive layer, and the strip-shaped peeling portion. A label for in-mold attachment with a coupon ticket, wherein a coupon ticket is printed on the surface side of the base material layer corresponding to, and notch portions are formed at at least two ends of the peeling portion of the label.