JPH06340483A - Fertilizer and its preparation - Google Patents
Fertilizer and its preparationInfo
- Publication number
- JPH06340483A JPH06340483A JP3359161A JP35916191A JPH06340483A JP H06340483 A JPH06340483 A JP H06340483A JP 3359161 A JP3359161 A JP 3359161A JP 35916191 A JP35916191 A JP 35916191A JP H06340483 A JPH06340483 A JP H06340483A
- Authority
- JP
- Japan
- Prior art keywords
- chemical fertilizer
- salt
- compound
- soluble
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】この発明は、化学肥料の組成に関
するもので、特に高い溶解性を有するとともに、高い機
械強度及び非凝固特性を有する化学肥料の組成に関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a chemical fertilizer composition, and more particularly to a chemical fertilizer composition having high solubility, high mechanical strength and non-coagulating properties.
【０００２】[0002]
【従来の技術】化学肥料の取扱い、運搬及び貯蔵におい
て生じる主要な問題の一つは、化学肥料が凝固して凝塊
を形成し易いことである。さらに、周知の化学肥料の組
成は、許容可能な硬度または耐破壊性を有していない。
一般的な従来技術においては、化学肥料に添加剤を加え
て、化学肥料を所望の最終製品とする工程において化学
肥料の結晶方法を変化させるようにしている。アメリカ
特許第３，１１２，３４３号、第４，１６０，７８２号
及び第４，２０４，０５３号には、上記の問題を解消す
るために、ホルムアルデヒド等の添加剤により化学肥料
を処理するための種々の方法が開示されている。ホルム
アルデヒドは、アメリカ環境保護局(U.S.Environmental
Protection Aency)によって有毒で発ガン性のある化学
物質として指定されている。従って、化学肥料の脆弱さ
及び凝結性を改善するために他の添加剤が用いられて来
ている。アメリカ特許第４，５８７，３５８号には、化
学肥料の上記した特性を改良するための添加剤としてリ
グノスルホン酸塩を使用した化学肥料の組成が示されて
いる。またアメリカ特許第４，７４３，２８９号及び第
４，８４６，８７１号には同様に、機械強度及び非凝結
性を改善する添加剤を含む化学肥料の組成が示されてい
る。BACKGROUND OF THE INVENTION One of the major problems encountered in handling, transporting and storing chemical fertilizers is the tendency of chemical fertilizers to solidify and form agglomerates. Moreover, known chemical fertilizer compositions do not have an acceptable hardness or puncture resistance.
In the general prior art, additives are added to the chemical fertilizer to change the method of crystallization of the chemical fertilizer in the process of making the chemical fertilizer the desired end product. U.S. Pat. Nos. 3,112,343, 4,160,782 and 4,204,053 disclose treatment of chemical fertilizers with an additive such as formaldehyde in order to solve the above problems. Various methods have been disclosed. Formaldehyde is used by the US Environmental Protection Agency (USEn environmental
Designated by the Protection Aency as a toxic and carcinogenic chemical. Therefore, other additives have been used to improve the fragility and caking properties of chemical fertilizers. U.S. Pat. No. 4,587,358 shows the composition of chemical fertilizers using lignosulfonate as an additive to improve the above-mentioned properties of chemical fertilizers. Also, U.S. Pat. Nos. 4,743,289 and 4,846,871 similarly show the composition of chemical fertilizers containing additives that improve mechanical strength and non-caking properties.
【０００３】[0003]
【発明が解決しようとする課題】当然のことながら、高
い機械強度及び非凝固特性を持つ化学肥料は、毒性がな
く、非発ガン性であることが望ましく、またその製造方
法は製造コストが安価であることが望ましい。As a matter of course, it is desirable that the chemical fertilizer having high mechanical strength and non-coagulation properties is non-toxic and non-carcinogenic, and the production method thereof is low in production cost. Is desirable.
【０００４】そこで、本発明の目的は、高い機械強度と
非凝結性を持つ化学肥料組成及びその製造方法を提供す
ることにある。Therefore, an object of the present invention is to provide a chemical fertilizer composition having high mechanical strength and non-caking properties, and a method for producing the same.
【０００５】特に、本発明の目的は、水溶性のリグニン
化(lignate)塩の添加剤を含有する前述の化学肥料を提
供することにある。In particular, it is an object of the present invention to provide the aforesaid chemical fertilizer containing an additive of a water-soluble lignate salt.
【０００６】さらに、本発明の目的は、紙パルプ工場で
発生する廃棄物から生成される水溶性リグニン化塩を添
加物として使用した化学肥料及びその製造方法を提供す
ることにある。Further, it is an object of the present invention to provide a chemical fertilizer using as an additive a water-soluble ligninating salt produced from a waste produced in a paper pulp mill, and a method for producing the same.
【０００７】また、本発明のもう一つの目的は、安価
で、無毒性で且つ非発ガン性の化学肥料及びその製造方
法を提供することにある。Another object of the present invention is to provide an inexpensive, non-toxic and non-carcinogenic chemical fertilizer and a method for producing the same.
【０００８】[0008]
【課題を解決するための手段】本発明によれば、上記の
目的及び利点が達成される。According to the present invention, the above objects and advantages are achieved.
【０００９】本発明は、化学肥料の組成及びその製造方
法に係るもので、本発明による化学肥料は、高い機械強
度と非凝結性を有している。本発明によれば、化学肥料
組成は、尿素、硫酸アンモニウム、窒素−カリウム−リ
ン粒状物、リン酸−アンモニウム、リン酸二アンモニウ
ム、塩化カリウム及びそれらの混合物の群より選択され
る化合物、及びリグニン化ナトリウム(sodium lignate
s)、リグニン化アルカリ金属(alkaline metal lignate
s)、リグニン化アンモニウム(ammonium lignated)及び
その混合物より成る群より選択される硫黄分を含有しな
い水溶性リグニン化塩によって形成され、水溶性リグニ
ン化塩は最終化学肥料組成に０．１乃至５．０ｗｔ％の
量で添加されて、化学肥料の溶解性を低下させることな
く高い機械強度及び低い凝結性を達成する。本発明の好
適実施例によれば、水溶性リグニン化塩は、硫黄分を含
有しないリグニン化ナトリウムであり、このリグニン化
ナトリウムは紙パルプ工場より発生する廃棄物から生成
される。好適な化学肥料組成は、尿素を共通の窒素担体
とする尿素、硫酸アンモニウム、塩化カリウム、リン酸
−アンモニウム、リン酸二アンモニウムである。リグニ
ン化塩の添加によって、化学肥料には大きな耐圧縮性、
耐衝撃性及び非凝結性が与えられる。The present invention relates to the composition of a chemical fertilizer and a method for producing the same, and the chemical fertilizer according to the present invention has high mechanical strength and non-caking property. According to the invention, the chemical fertilizer composition comprises a compound selected from the group of urea, ammonium sulphate, nitrogen-potassium-phosphorus granulate, phosphate-ammonium phosphate, diammonium phosphate, potassium chloride and mixtures thereof, and lignination. Sodium lignate
s), alkali metal lignate
s), ammonium lignated and a mixture thereof, which is formed by a sulfur-free water-soluble ligninating salt, the water-soluble ligninating salt having a final fertilizer composition of 0.1 to 5 It is added in an amount of 0.0 wt% to achieve high mechanical strength and low cohesiveness without reducing the solubility of chemical fertilizers. According to a preferred embodiment of the present invention, the water-soluble ligninated salt is sulfur-free sodium ligninated salt, which is produced from waste produced by pulp and paper mills. A preferred chemical fertilizer composition is urea with urea as a common nitrogen carrier, ammonium sulphate, potassium chloride, phosphate-ammonium, diammonium phosphate. With the addition of ligninized salt, chemical fertilizers have great compression resistance,
It provides impact resistance and non-caking properties.
【００１０】本発明による化学肥料を製造する方法は、
化合物とリグニン化塩を混合して均一な混合物を形成
し、次いで混合物を炉内で１２０゜Ｃ乃至１６０゜Ｃの
温度で加熱して所望の微粒子状の材料を得る構成と成っ
ている。好適実施例による方法においては、リグニン化
ナトリウムは、紙パルプ製造処理工程から得られる。The method for producing a chemical fertilizer according to the present invention comprises:
The compound and the ligninating salt are mixed to form a uniform mixture, and then the mixture is heated in a furnace at a temperature of 120 ° C. to 160 ° C. to obtain a desired particulate material. In the method according to the preferred embodiment, sodium ligninide is obtained from a paper pulp manufacturing process.
【００１１】本発明の化学肥料及びその製造方法によれ
ば、無毒性、非発ガン性の化学肥料組成が得られ、この
化学肥料は高い機械強度と良好な非凝固特性を有してい
る。According to the chemical fertilizer and the method for producing the same of the present invention, a non-toxic and non-carcinogenic chemical fertilizer composition is obtained, and this chemical fertilizer has high mechanical strength and good non-coagulating properties.
【００１２】[0012]
【実施例】紙パルプ工場で発生する廃棄物は、「ソーダ
液」と呼ばれ、実質的にリグニン化物で構成されてい
る。紙パルプ工場における処理工程においては、原材料
が水酸化ナトリウムによって処理されて、「ソーダ液」
が生成される。このソーダ液に含まれるリグニン化合物
は、主にリグニン化ナトリウムである。EXAMPLE Waste generated at a pulp and paper mill is called "soda liquid" and is substantially composed of lignin compounds. In the process of processing at a pulp and paper mill, raw materials are treated with sodium hydroxide to produce "soda solution".
Is generated. The lignin compound contained in this soda solution is mainly sodium lignin.
【００１３】本発明による化学肥料組成に使用される水
溶性リグニン化塩添加物を得るために、「ソーダ液」
は、リグニン化ナトリウム濃度が４８乃至５５ｗｔ％の
水溶液または水分を含有しないリグニン化合物粉末を得
るために脱水される。To obtain the water-soluble ligninating salt additive used in the chemical fertilizer composition according to the present invention, a "soda solution" is used.
Is dehydrated to obtain an aqueous solution or a water-free lignin compound powder having a sodium lignination concentration of 48 to 55 wt%.
【００１４】リグニン化ナトリウムは、本発明の化学肥
料の添加剤として適当なものではあるが、例えばアルカ
リ金属のリグニン化合物、アンモニウムのリグニン化合
物も同様に使用することが出来るものである。さらに、
リグニン化合物は、例えば多糖及び／または単糖及びま
たはパルプ製造作業中に炭水化物の滅成により含有され
る酸から生成される塩を含んでいる。これらの物質は、
機械強度及び非凝結性に関してその特性を変化させるこ
となくリグニン化合物中に存在している。本発明の好適
実施例によれば、リグニン化合物塩は、紙パルプの製造
に用いられる原材料から生成され、この原材料は例えば
薯糖のしぼりかす(suger cane bagasse)を使用すること
が好適であるが、他の少なくとも１５ｗｔ％のリグニン
を含有する植物材料を使用することも可能である。Sodium lignination is suitable as an additive for the chemical fertilizer of the present invention, but, for example, alkali metal lignin compounds and ammonium lignin compounds can also be used. further,
Lignin compounds include, for example, polysaccharides and / or monosaccharides and / or salts formed from acids contained by the destruction of carbohydrates during pulp making operations. These substances are
It is present in the lignin compound without changing its properties with respect to mechanical strength and non-caking properties. According to a preferred embodiment of the present invention, the lignin compound salt is produced from a raw material used for the production of paper pulp, which raw material is preferably a sugar cane bagasse, for example. It is also possible to use other plant materials containing at least 15 wt% lignin.
【００１５】本発明の方法によれば、水溶性のリグニン
化合物塩は、尿素、硫酸アンモニウム、窒素−カリウム
−リン粒状物、リン酸−アンモニウム、リン酸二アンモ
ニウム、塩化カリウム及びそれらの混合物の群より選択
される化合物と混合される。上記したように、水溶性リ
グニン化合物塩は、アルカリ金属のリグニン化合物、ア
ンモニウムのリグニン化合物及びその混合物で構成され
る群より選択され、最終化学肥料組成中に０．１乃至
５．０ｗｔ％の量で含有されて、溶解性に影響を与える
ことなく、高い機械強度と低い凝結性を化学肥料に付与
する。本発明によれば、好適な水溶性リグニン化合物塩
は、硫黄分を含有しないリグニン化ナトリウムであり、
これを混合する好適な化合物は尿素である。尿素が化合
物として使用されると、リグニン化合物塩は、最終化学
肥料組成中に０．１乃至１．０ｗｔ％の量存在する。硫
酸アンモニウムを化合物として使用した場合、水溶性リ
グニン化合物塩は、最終化学肥料組成に２．６乃至４．
８ｗｔ％の量で存在する。According to the method of the present invention, the water-soluble lignin compound salt is selected from the group of urea, ammonium sulfate, nitrogen-potassium-phosphorus granules, phosphate-ammonium phosphate, diammonium phosphate, potassium chloride and mixtures thereof. It is mixed with the compound of choice. As described above, the water-soluble lignin compound salt is selected from the group consisting of alkali metal lignin compounds, ammonium lignin compounds and mixtures thereof, and has an amount of 0.1 to 5.0 wt% in the final chemical fertilizer composition. Contained in, it imparts high mechanical strength and low coagulation to chemical fertilizers without affecting solubility. According to the invention, the preferred water-soluble lignin compound salt is sulfur-free sodium ligninate,
The preferred compound with which to mix is urea. When urea is used as the compound, the lignin compound salt is present in the final fertilizer composition in an amount of 0.1 to 1.0 wt%. When ammonium sulfate is used as the compound, the water-soluble lignin compound salt is added to the final chemical fertilizer composition in the range of 2.6 to 4.
Present in an amount of 8 wt%.
【００１６】本発明によれば、化合物と水溶性リグニン
化合物塩は混合されて、均一な混合物を形成する。均一
な混合物は、その後に１２０゜Ｃ乃至１６０゜Ｃの温度
で加熱され、次いで周知の球状加工(prilling)されて最
終の微粒子形状となる。According to the present invention, the compound and the water-soluble lignin compound salt are mixed to form a uniform mixture. The homogenous mixture is then heated at a temperature of 120 ° C to 160 ° C and then well-known prilling to the final particulate form.
【００１７】前記のようにリグニン化合物塩は、紙パル
プ製造過程において廃棄物として生成されるもので、こ
の紙パルプ製造に使用される原材料は通常薯糖のしぼり
かすである。As described above, the lignin compound salt is produced as a waste in the paper pulp manufacturing process, and the raw material used for the paper pulp manufacturing is usually squeezed sugar powder.
【００１８】本発明の化学肥料の組成の特性は、周知の
化学肥料組成の特性と同等である。これに関して以下に
例を挙げて説明する、化学肥料において要求される機械
強度は、二つの要素を有していた。第一の要素は圧縮強
度であり、この時加えられる力は静的な力であり、第二
の要素は衝撃強度であり、この時加えられる力は動的な
力である。圧縮強度は、チャティロン硬度圧縮(Chatill
on Hardness Compression)によって決定され、国際化学
肥料開発センター規格Ｓ−１１５に従って製造されるジ
ョン チャティロン アンド サンズ(John Chatillon
& Sons)社製のモデルＮｏ．ＬＴＣＭ−３の装置を使用
して測定された。衝撃強度は、国際化学肥料開発センタ
ー規格Ｆ−１１８によって決定された。凝結性は、加速
された凝結試験によって評価された。こうした試験は、
所定量の球状粒子を中空管内部に収納し、この球状粒子
を二つのプラスチックガラス製ピストンの間に捕捉して
行われた。所定の時間経過後に小さな凝結塊が得られ
た。この凝結塊を破壊した、凝結塊の破壊に要した力
は、硬度計で測定された。小さな力ほど、より少ない凝
結が生じていることを示す。The compositional characteristics of the chemical fertilizer of the present invention are similar to those of known chemical fertilizer compositions. The mechanical strength required in chemical fertilizers, which is explained in the following by way of example, has two components. The first factor is compressive strength, the force applied at this time is static force, the second factor is impact strength, and the force applied at this time is dynamic force. The compressive strength is Chatillon hardness compression (Chatill
on Hardness Compression) and manufactured in accordance with International Chemical Fertilizer Development Center Standard S-115, John Chatillon and Sons (John Chatillon)
& Sons) model No. It was measured using the instrument of LTCM-3. Impact strength was determined by International Fertilizer Development Center Standard F-118. Settability was evaluated by an accelerated settling test. These tests are
A predetermined amount of spherical particles were housed inside a hollow tube, and the spherical particles were trapped between two plastic glass pistons. After a certain time, a small aggregate was obtained. The force required to break the clot, which broke the clot, was measured with a durometer. Smaller forces indicate less condensation is occurring.
【００１９】上記の例は、本発明による化学肥料の品質
が、従来の化学肥料の組成に較べて優れていることを示
している。The above examples show that the quality of the chemical fertilizers according to the invention is superior to the composition of conventional chemical fertilizers.
【００２０】例１ ８ｗｔ％の全固形成分を含有する「ソーダ液」を脱水し
て、固形成分５１ｗｔ％を持つ溶液を得た。濃縮された
ソーダ液は、０．５ｗｔ％のリグニン化合物塩を含む試
験サンプル１と０．７ｗｔ％のリグニン化合物塩を含む
試験サンプル２の二つのサンプルを得るために、二つの
異なるバッチで固相の尿素と混合された。各化学肥料試
験サンプルは、その後に混合され、均一にブレンドされ
た後１４０゜Ｃの温度に炉内で加熱されて溶解された。
リグニン化合物が、溶融された尿素に対して非常に高い
溶解性を有し、尿素とリグニン化合物の溶融物は、全く
懸濁を示さなかった。その後に、混合物が冷却され、周
知の要領で球状の微粒子に形成され、種々の径を持った
微粒子となった。球状加工後に、粒子を１０メッシュ、
１２メッシュ、１４メッシュにふるい分けた。Example 1 A "soda solution" containing 8 wt% of all solid components was dehydrated to obtain a solution having 51 wt% of solid components. The concentrated soda solution was used as a solid phase in two different batches to obtain two samples, a test sample 1 containing 0.5 wt% lignin compound salt and a test sample 2 containing 0.7 wt% lignin compound salt. Mixed with urea. Each fertilizer test sample was then mixed, uniformly blended and then heated in a furnace to a temperature of 140 ° C. to dissolve.
The lignin compound had a very high solubility in the melted urea and the melt of urea and lignin compound showed no suspension. After that, the mixture was cooled and formed into spherical fine particles in a well-known manner into fine particles having various diameters. After spheroidizing, the particles are 10 mesh,
It was sieved to 12 mesh and 14 mesh.
【００２１】第三番目の試験サンプル３の化学肥料組成
が、リグニン化合物の固相粉末を、最終化学肥料組成中
のリグニン化合物成分が０．５ｗｔ％と成るように、尿
素に添加した。混合物はその後ブレンドされて均一な混
合物を形成し、次いで加熱され、球状粒子に加工され、
試験サンプル１，２と同様にふるい分けされた。本発明
の化学肥料組成の機能を示すために、これらの試験サン
プルのチャティロン硬度圧縮による圧縮強度の測定が行
われ、二つの周知の尿素と添加剤を含む比較例化学肥料
組成及び尿素単独の化学肥料と比較された。二つの周知
の化学肥料組成は、アライド ケミカル社（米国）のＵ
Ｆ−８５（登録商標）とダイショウワケミカル（米国）
のノーリン −ＨＰ（登録商標）とした。圧縮試験の結
果は以下の表１に示す。For the chemical fertilizer composition of the third test sample 3, solid phase powder of lignin compound was added to urea so that the lignin compound component in the final chemical fertilizer composition would be 0.5 wt%. The mixture is then blended to form a uniform mixture, then heated and processed into spherical particles,
It screened similarly to the test samples 1 and 2. In order to demonstrate the function of the chemical fertilizer composition of the present invention, the compressive strength of these test samples was measured by Chatillon hardness compression, a comparative chemical fertilizer composition containing two well-known urea and additives, and the chemistry of urea alone. Compared to fertilizer. Two well-known chemical fertilizer compositions are U of Allied Chemical Company (USA).
F-85 (registered trademark) and Daishowa Chemical (US)
Norin-HP (registered trademark). The results of the compression test are shown in Table 1 below.
【００２２】[0022]
【表１】 [Table 1]
【００２３】上記の表１よりわかるように、本発明の化
学肥料はいずれの周知の化学肥料よりも格段に優れた圧
縮強度を示した。さらに、上述したように衝撃強度がＦ
ＤＣ−１１８規格によって測定された。測定結果を、以
下の表２に示す。As can be seen from Table 1 above, the chemical fertilizer of the present invention showed significantly superior compressive strength to any known chemical fertilizer. Further, as described above, the impact strength is F
Measured according to the DC-118 standard. The measurement results are shown in Table 2 below.
【００２４】[0024]
【表２】 [Table 2]
【００２５】上記の表２より明かなように、本発明の化
学肥料の衝撃強度は、周知の化学肥料の衝撃強度と同等
であった。As is clear from Table 2 above, the impact strength of the chemical fertilizer of the present invention was equivalent to that of known chemical fertilizers.
【００２６】例２ 例１において使用した化学肥料を、上述した方法により
凝結試験した。試験結果は、以下の表３に示す。Example 2 The chemical fertilizer used in Example 1 was tested for coagulation by the method described above. The test results are shown in Table 3 below.
【００２７】[0027]
【表３】 [Table 3]
【００２８】本発明による化学肥料組成における凝結性
は、最も悪い結果においても周知の化学肥料と同等であ
り、多くの場合非凝結性において周知の化学肥料よりも
優れていた。The setting properties of the chemical fertilizer compositions according to the invention were comparable to the known chemical fertilizers with the worst results and in many cases were superior to the known chemical fertilizers in the non-setting properties.
【００２９】例３ 本発明の他の組成の化学肥料の有効性を調べるために、
リグニン化ナトリウム粉末１５−１５−１５固相の構造
式を持つ窒素−カリウム−リン粒状物に混合して、最終
生成物中のリグニン組成を５ｗｔ％として調整した。ま
た１３−２６−０６の構造式を持つ窒素−カリウム−リ
ン粒状物にリグニン化ナトリウムを混合して最終生成物
中のリグニン組成を２．８ｗｔ％とした。これらのサン
プルに関して凝結試験を行い、本発明による添加剤のこ
れらの化学肥料に対する効果を比較した。この結果は、
以下の表４に示されている。Example 3 To determine the effectiveness of chemical fertilizers of other composition of the present invention,
Sodium lignin powder 15-15-15 It was mixed with nitrogen-potassium-phosphorus granular material having a structural formula of solid phase to adjust the lignin composition in the final product to 5 wt%. The nitrogen-potassium-phosphorus granular material having the structural formula of 13-26-06 was mixed with sodium lignin to adjust the lignin composition in the final product to 2.8 wt%. A setting test was carried out on these samples to compare the effect of the additives according to the invention on these chemical fertilizers. This result is
It is shown in Table 4 below.
【００３０】[0030]
【表４】 [Table 4]
【００３１】表４より明かなように、本発明によるリグ
ニン化合物塩の添加剤化合物は、周知の化学肥料の凝結
性を大幅に改善した。As is clear from Table 4, the additive compound of the lignin compound salt according to the present invention significantly improved the coagulability of known chemical fertilizers.
【００３２】[0032]
【発明の効果】上記のように本発明によれば、高い機械
強度と非凝結性を持つ化学肥料組成及びその製造方法を
提供することが出来る。また、本発明によれば、水溶性
のリグニン化合物(lignate)塩の添加剤を含有する前述
の化学肥料を提供することが出来る。さらに、本発明に
よれば、紙パルプ工場で発生する廃棄物から生成される
水溶性リグニン化塩を添加物として使用した化学肥料及
びその製造方法を提供することが出来る。また、本発明
によれば、安価で、無毒性で且つ非発ガン性の化学肥料
及びその製造方法を提供することが可能となる。As described above, according to the present invention, it is possible to provide a chemical fertilizer composition having high mechanical strength and non-caking property, and a method for producing the same. Further, according to the present invention, it is possible to provide the above-mentioned chemical fertilizer containing an additive for a water-soluble lignin compound (lignate) salt. Further, according to the present invention, it is possible to provide a chemical fertilizer using a water-soluble ligninating salt produced from waste generated in a pulp and paper factory as an additive and a method for producing the same. Further, according to the present invention, it is possible to provide an inexpensive, non-toxic, non-carcinogenic chemical fertilizer and a method for producing the same.
【００３３】なお、本発明は、他の形式においても本発
明の趣旨を逸脱することなく実施可能である。従って、
上記の実施例は、単に説明に供するものであって、本発
明を限定するものではなく、本発明の範囲は、特許請求
の範囲及びその均等範囲に属する全ての変形、変更を包
含するものである。The present invention can be implemented in other forms without departing from the spirit of the present invention. Therefore,
The above-mentioned embodiments are merely provided for the purpose of explanation, and do not limit the present invention. The scope of the present invention includes all modifications and changes belonging to the scope of claims and their equivalents. is there.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０５Ｄ 1/02 7537−4Ｈ Ｃ０５Ｇ 1/00 Ｆ 7537−4Ｈ Ｈ 7537−4Ｈ (72)発明者 マリル エス．デ リエンド ベネズエラ，エスタド ミランダ，ロス テケス，アパルタメント 42，エディフィ シオ アマポーラ，レジデンシャル ラス フローレス，コンジュント，ウルバニザ チオン ラ ポンデロサ （番地なし)─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI Technical indication C05D 1/02 7537-4H C05G 1/00 F 7537-4H H 7537-4H (72) Inventor Marill S. Deli End Venezuela, Estad Miranda, Los Teques, Apartament 42, Edificio Amapola, Residential Las Flores, Conjunto, Urbaniza Zionla Ponderosa (no address)
Claims (10)
カリウム−リン粒状物、リン酸−アンモニウム、リン酸
二アンモニウム、塩化カリウム及びそれらの混合物の群
より選択される化合物と、 （ｂ）リグニン化ナトリウム、リグニン化アルカリ金
属、リグニン化アンモニウム及びその混合物より成る群
より選択される硫黄分を含有しない水溶性リグニン化塩
によって形成され、前記水溶性リグニン化塩は最終化学
肥料組成に０．１乃至５．０ｗｔ％の量で添加されて、
化学肥料の溶解性を低下させることなく高い機械強度及
び低い凝結性を達成することを特徴とする高い機械強度
及び非凝結性を有する化学肥料組成。1. (a) Urea, ammonium sulfate, nitrogen-
A compound selected from the group consisting of potassium-phosphorus granules, phosphoric acid-ammonium phosphate, diammonium phosphate, potassium chloride and mixtures thereof; and (b) sodium lignonate, alkali metal ligninate, ammonium ligninide and mixtures thereof. Formed by a sulfur-free water-soluble ligninating salt selected from the group consisting of: the water-soluble ligninating salt is added to the final chemical fertilizer composition in an amount of 0.1 to 5.0 wt%,
A chemical fertilizer composition having high mechanical strength and non-caking properties, which is characterized by achieving a high mechanical strength and a low setting property without decreasing the solubility of the chemical fertilizer.
有しないリグニン化ナトリウムである請求項１の化学肥
料組成。2. The chemical fertilizer composition according to claim 1, wherein the water-soluble ligninated salt is sodium ligninated salt containing no sulfur content.
グニン化合物塩は、最終化学肥料組成中に０．１乃至
１．０ｗｔ％の範囲で含有される請求項１の化学肥料組
成。3. The chemical fertilizer composition according to claim 1, wherein the compound is urea, and the water-soluble lignin compound salt is contained in the final chemical fertilizer composition in a range of 0.1 to 1.0 wt%.
前記水溶性リグニン化合物塩は、最終化学肥料組成中に
２．６乃至４．８ｗｔ％の範囲で含有される請求項１の
化学肥料組成。4. The compound is ammonium sulfate,
The chemical fertilizer composition according to claim 1, wherein the water-soluble lignin compound salt is contained in the final chemical fertilizer composition in a range of 2.6 to 4.8 wt%.
カリウム−リン粒状物、リン酸−アンモニウム、リン酸
二アンモニウム、塩化カリウム及びそれらの混合物の群
より選択される化合物供給し、 （ｂ）リグニン化ナトリウム、リグニン化アルカリ金
属、リグニン化アンモニウム及びその混合物より成る群
より選択される硫黄分を含有しない水溶性リグニン化塩
によって形成され、前記水溶性リグニン化塩は最終化学
肥料組成に対して０．１乃至５．０ｗｔ％の量で添加
し、 （ｃ）化合物とリグニン化塩とを混合して均一な混合物
を形成し、 （ｄ）該混合物を処理して所望の粒状物を得ることを特
徴とする高い機械強度及び非凝結性を有する化学肥料の
製造方法。5. (a) Urea, ammonium sulfate, nitrogen-
Supplying a compound selected from the group of potassium-phosphorus granules, phosphate-ammonium phosphate, diammonium phosphate, potassium chloride and mixtures thereof, (b) sodium ligninate, alkali metal ligninate, ammonium ligninide and mixtures thereof Formed by a sulfur-free water-soluble ligninating salt selected from the group consisting of: said water-soluble ligninating salt being added in an amount of 0.1 to 5.0 wt% with respect to the final chemical fertilizer composition; chemical fertilizer with high mechanical strength and non-caking properties, characterized in that c) the compound and the ligninating salt are mixed to form a uniform mixture, and (d) the mixture is treated to obtain the desired granulate. Manufacturing method.
有しないリグニン化ナトリウムを供給する工程を含む請
求項５の方法。6. The method according to claim 5, which comprises the step of supplying a sulfur-free sodium ligninide salt as the lignin compound salt.
合物と前記リグニン化合物塩の混合物を加熱する工程を
含んでいる請求項５の方法。7. The method of claim 5 including the step of heating the mixture of said compound and said lignin compound salt prior to processing to the desired granular shape.
ダ液を処理する工程を含んでいる請求項５の方法。8. The method of claim 5 including the step of treating soda liquor to obtain said lignin compound salt.
水酸化ナトリウムにより薯糖しぼりかすを処理において
生成される廃液である請求項８の方法。9. The method according to claim 8, wherein the soda liquor is a waste liquor produced in the treatment of sucrose squeezed residue with sodium hydroxide to obtain paper pulp.
ルカリ金属、リグニン化アンモニウム及びその混合物よ
り成る群より選択される硫黄分を含有しない水溶性リグ
ニン化塩によって形成され、前記水溶性リグニン化塩は
最終化学肥料組成に０．１乃至５．０ｗｔ％の量で添加
されて、化学肥料の溶解性を低下させることなく高い機
械強度及び低い凝結性を達成することを特徴とする化学
肥料の機械強度及び凝結性を改善するための添加剤。10. Formed by a sulfur-free water-soluble lignination salt selected from the group consisting of sodium ligninate, alkali metal ligninate, ammonium ligninide and mixtures thereof, said water-soluble lignination salt being the final chemical compound. Mechanical strength and coagulation of chemical fertilizer characterized by being added to fertilizer composition in an amount of 0.1 to 5.0 wt% to achieve high mechanical strength and low coagulation without reducing the solubility of chemical fertilizer. Additives to improve sex.