JPH0593336A - Monofilament and polishing tool using monofilament - Google Patents
Monofilament and polishing tool using monofilamentInfo
- Publication number
- JPH0593336A JPH0593336A JP3248954A JP24895491A JPH0593336A JP H0593336 A JPH0593336 A JP H0593336A JP 3248954 A JP3248954 A JP 3248954A JP 24895491 A JP24895491 A JP 24895491A JP H0593336 A JPH0593336 A JP H0593336A
- Authority
- JP
- Japan
- Prior art keywords
- polishing
- monofilament
- synthetic resin
- fiber
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、モノフィラメントおよ
び該モノフィラメントを用いた研磨具の構造に関するも
のである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a monofilament and a structure of a polishing tool using the monofilament.
【０００２】[0002]
【従来の技術】従来、自動車の車体水研用ブラシなどの
研磨具に使用されるモノフィラメントとしては、例えば
実開昭５６−７８８８５号公報に開示されているよう
に、研磨材として粒状の砥粒を用い、該砥粒を合成樹脂
等のバインダ内に含有させてなるものが知られている。2. Description of the Related Art Conventionally, as a monofilament used for a polishing tool such as a brush for water car body of an automobile, for example, as disclosed in Japanese Utility Model Laid-Open No. 56-78885, granular abrasive grains are used as an abrasive. It is known that the abrasive grains are contained in a binder such as a synthetic resin.
【０００３】ところが、このような砥粒を研磨材として
用いたモノフィラメントの場合、モノフィラメントの研
磨断面ごとに砥粒の出現率が異なったり、また研磨断面
に出現した砥粒がとれ落ちてしまうなどの問題があり、
各研磨断面ごとが略均一な研磨力を有する構造とするこ
とが困難であった。However, in the case of a monofilament using such abrasive grains as an abrasive, the appearance rate of the abrasive grains differs depending on the polished cross section of the monofilament, and the abrasive grains appearing on the polished cross section may fall off. There is a problem,
It has been difficult to obtain a structure in which each polished cross section has a substantially uniform polishing force.
【０００４】最近、上記砥粒の代わりに繊維状の研磨用
繊維（例えばアルミナ繊維や炭化ケイ素繊維）を研磨材
として用い、該研磨用繊維をモノフィラメントの長さ方
向に略平行な状態で含有させることによって、各研磨断
面ごとの研磨用繊維の出現率を略等しくすることが可能
となり、モノフィラメントとしての各研磨断面ごとの研
磨力を均一化できることがわかってきた。Recently, fibrous polishing fibers (for example, alumina fibers and silicon carbide fibers) have been used as abrasives instead of the above-mentioned abrasive grains, and the polishing fibers are contained in a state substantially parallel to the length direction of the monofilament. As a result, it has been found that it is possible to make the appearance ratio of the polishing fibers in each polishing section substantially equal, and to make the polishing force uniform in each polishing section as a monofilament.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、上記研
磨用繊維を用いたモノフィラメントにおいては、例えば
バインダとして熱硬化性樹脂を用いた場合には耐熱性、
耐溶剤性には優れたものができる反面、もろく折れ易い
ものになるなどの問題が生じる。一方、熱可塑性樹脂は
延伸させることにより強度がいちじるしく増大する性質
があるので、熱硬化性樹脂の代わりに熱可塑性樹脂をバ
インダとして用いることも考えられるが、研磨用繊維の
ように繊維状物を含有させた熱可塑性樹脂を延伸させる
ことは困難である。したがってバインダとして熱可塑性
樹脂を用いたとしても延伸できないため、モノフィラメ
ントとしての弾性および強度が不足してしまう。However, in the monofilament using the above-mentioned polishing fiber, for example, when a thermosetting resin is used as the binder, heat resistance,
Although excellent solvent resistance can be obtained, there arises a problem that it becomes brittle and easily broken. On the other hand, since the thermoplastic resin has a property that the strength remarkably increases by stretching, it is possible to use a thermoplastic resin as a binder instead of the thermosetting resin, but a fibrous material such as a polishing fiber is used. It is difficult to stretch the contained thermoplastic resin. Therefore, even if a thermoplastic resin is used as a binder, it cannot be stretched, resulting in insufficient elasticity and strength as a monofilament.
【０００６】本発明は、上記課題に鑑み、モノフィラメ
ントとしての弾性、折れにくさを向上させて研磨力とと
もに耐久性にも優れた高い研磨性能を有するモノフィラ
メント、および研磨力、耐久性に優れた研磨具を提供す
ることを目的とするものである。In view of the above problems, the present invention provides a monofilament having high polishing performance which is improved in elasticity as a monofilament and is hard to break and is excellent in polishing power and durability as well as polishing power and durability. The purpose is to provide a tool.
【０００７】[0007]
【課題を解決するための手段】上記課題を解決するため
に本発明によるモノフィラメントは、請求項１に記載し
たように、合成樹脂内に所定長の研磨用繊維を含有させ
てなるモノフィラメントであって、前記所定長の研磨用
繊維が含有された合成樹脂の外周に、該外周を囲繞する
補強材が設けられていることを特徴とするものである。In order to solve the above problems, the monofilament according to the present invention is a monofilament comprising a synthetic resin containing polishing fibers of a predetermined length as described in claim 1. A reinforcing material surrounding the outer circumference of the synthetic resin containing the polishing fiber of the predetermined length is provided.
【０００８】請求項２に記載したように、上記構成にお
いて前記補強材は前記合成樹脂の外周に配された繊維か
らなるものとすることができる。According to the second aspect of the present invention, in the above structure, the reinforcing material may be made of fibers arranged on the outer periphery of the synthetic resin.
【０００９】また上記課題を解決するために本発明によ
るモノフィラメントは、請求項３に記載したように、合
成樹脂内に所定長の研磨用繊維を含有させてなるモノフ
ィラメントであって、前記所定長の研磨用繊維が含有さ
れた合成樹脂内にさらに補強用金属繊維が含有されてい
ることを特徴とするものである。In order to solve the above-mentioned problems, the monofilament according to the present invention is, as described in claim 3, a monofilament in which a predetermined length of polishing fiber is contained in a synthetic resin. It is characterized in that a reinforcing metal fiber is further contained in the synthetic resin containing the polishing fiber.
【００１０】また上記課題を解決するために本発明によ
るモノフィラメントは、請求項４に記載したように、合
成樹脂内に所定長の研磨用繊維を含有させてなるモノフ
ィラメントであって、前記研磨用繊維の外周に、該外周
を囲繞する補強体が設けられていることを特徴とするも
のである。In order to solve the above-mentioned problems, the monofilament according to the present invention is, as described in claim 4, a monofilament in which a predetermined length of polishing fiber is contained in a synthetic resin. A reinforcing body surrounding the outer circumference is provided on the outer circumference.
【００１１】請求項５に記載したように、上記構成にお
いて前記合成樹脂を熱硬化性樹脂とし、前記補強材を高
弾性ゴム系材とすることができる。In the above structure, the synthetic resin may be a thermosetting resin, and the reinforcing material may be a high elastic rubber material.
【００１２】また上記課題を解決するために本発明によ
るモノフィラメントは、請求項６に記載したように、金
属内に所定長の研磨用繊維を含有させてなることを特徴
とするものである。In order to solve the above-mentioned problems, the monofilament according to the present invention is characterized in that, as described in claim 6, a metal contains a predetermined length of polishing fiber.
【００１３】請求項７に記載したように、上記構成にお
いて前記金属を焼結合金とすることができる。As described in claim 7, in the above structure, the metal can be a sintered alloy.
【００１４】また上記課題を解決するために本発明によ
る研磨具は、請求項８に記載したように、請求項１，
２，３，４，５，６または７記載のモノフィラメントを
複数本集合させてなることを特徴とするものである。Further, in order to solve the above-mentioned problems, the polishing tool according to the present invention is, as described in claim 8, claim 1,
It is characterized in that a plurality of monofilaments described in 2, 3, 4, 5, 6 or 7 are collected.
【００１５】上記「研磨用繊維」としては、例えばアル
ミナ繊維や炭化ケイ素繊維を挙げることができる。Examples of the above-mentioned "polishing fibers" include alumina fibers and silicon carbide fibers.
【００１６】[0016]
【作用および効果】上記したように請求項１記載の本発
明によるモノフィラメントによれば、所定長の研磨用繊
維を合成樹脂内に含有させることにより形成されている
ので、研磨材として砥粒を用いた場合に比較して研磨用
繊維の分布を均一化でき、また研磨用繊維は砥粒と異な
り研磨断面において合成樹脂材からとれてしまうことも
ほとんど無く、したがって研磨力に優れており、また上
記所定長の研磨用繊維が含有された合成樹脂の外周に該
外周を囲繞する補強材を設けているので、これによりバ
インダとして合成樹脂を用いてもモノフィラメントとし
ての弾性および折れにくさを向上させることができ耐久
性の向上を図れる。As described above, according to the monofilament of the present invention as set forth in claim 1, since it is formed by incorporating a predetermined length of polishing fiber in a synthetic resin, abrasive grains are used as an abrasive. The distribution of the polishing fibers can be made uniform as compared with the case where the polishing fibers are not present, and the polishing fibers unlike the abrasive grains are hardly detached from the synthetic resin material in the polishing cross section, and therefore have excellent polishing power, and Since a reinforcing material surrounding the outer circumference of the synthetic resin containing a predetermined length of polishing fiber is provided, the elasticity and the fragility of the monofilament can be improved even if the synthetic resin is used as the binder. It is possible to improve durability.
【００１７】また、上記したように請求項２記載の本発
明によるモノフィラメントによれば、上記請求項１記載
の本発明によるモノフィラメントの構成において、上記
補強材を上記合成樹脂の外周に配された繊維からなるも
のとして、これにより補強材を簡便に構成することが可
能となるので、耐久性の向上を容易に図ることが可能と
なる。Further, as described above, according to the monofilament according to the present invention described in claim 2, in the constitution of the monofilament according to the present invention described in claim 1, the reinforcing material is arranged on the outer periphery of the synthetic resin. As a result, the reinforcing material can be easily configured, and thus the durability can be easily improved.
【００１８】また、上記したように請求項３記載の本発
明によるモノフィラメントによれば、所定長の研磨用繊
維を合成樹脂内に含有させることにより形成されている
ので、研磨材として砥粒を用いた場合に比較して研磨用
繊維の分布を均一化でき、また研磨用繊維は砥粒と異な
り研磨断面において合成樹脂材からとれてしまうことも
少なく、したがって研磨力に優れており、また上記所定
長の研磨用繊維が含有された合成樹脂内にさらに補強用
金属繊維を含有させているので、これによりバインダと
して合成樹脂を用いてもモノフィラメントとしての弾性
および折れにくさを向上させることができ耐久性の向上
を図れる。Further, as described above, according to the monofilament of the present invention as defined in claim 3, since it is formed by containing a predetermined length of polishing fiber in a synthetic resin, abrasive grains are used as an abrasive. Compared with the case where the polishing fiber is uniform, the distribution of the polishing fiber can be made uniform, and unlike the abrasive grain, the polishing fiber is less likely to come off from the synthetic resin material in the polishing cross section, and therefore has excellent polishing power, and the above-mentioned predetermined Since the reinforcing metal fiber is further contained in the synthetic resin containing long polishing fibers, this makes it possible to improve the elasticity and crease resistance as a monofilament even if a synthetic resin is used as a binder. It is possible to improve the sex.
【００１９】また、上記したように請求項４記載の本発
明によるモノフィラメントによれば、所定長の研磨用繊
維を合成樹脂内に含有させることにより形成されている
ので、研磨材として砥粒を用いた場合に比較して研磨用
繊維の分布を均一化でき、また研磨用繊維は砥粒と異な
り研磨断面において合成樹脂材からとれてしまうことも
少なく、したがって研磨力に優れており、また上記所定
長の研磨用繊維の外周に該外周を囲繞する補強材を設け
ているので、これによりバインダとして合成樹脂を用い
てもモノフィラメントとしての弾性および折れにくさを
向上させることができ耐久性の向上を図れる。Further, as described above, according to the monofilament of the present invention as defined in claim 4, since it is formed by containing a predetermined length of polishing fiber in the synthetic resin, abrasive grains are used as the abrasive. Compared with the case where the polishing fiber is uniform, the distribution of the polishing fiber can be made uniform, and unlike the abrasive grain, the polishing fiber is less likely to come off from the synthetic resin material in the polishing cross section, and therefore has excellent polishing power, and the above-mentioned predetermined Since the reinforcing material surrounding the outer periphery of the long polishing fiber is provided, the elasticity and the fragility of the monofilament can be improved and the durability can be improved even if the synthetic resin is used as the binder. Can be achieved.
【００２０】また、上記したように請求項５記載の本発
明によるモノフィラメントによれば、上記請求項４記載
の本発明によるモノフィラメントの構成において、上記
合成樹脂を熱硬化樹脂としているので、これにより耐熱
性、耐溶剤性を向上させることができ、また上記補強材
を高弾性ゴム系材として、これにより補強材を簡便に構
成することが可能となるので、耐久性の向上を容易に図
ることが可能となる。Further, as described above, according to the monofilament according to the present invention described in claim 5, in the constitution of the monofilament according to the present invention described in claim 4, the synthetic resin is a thermosetting resin. Property and solvent resistance can be improved, and since the reinforcing material is made of a high elastic rubber material, the reinforcing material can be easily configured, and thus the durability can be easily improved. It will be possible.
【００２１】また、上記したように請求項６記載の本発
明よるモノフィラメントによれば、所定長の研磨用繊維
を金属内に含有させることにより形成されているので、
研磨材として砥粒を用いた場合に比較して研磨用繊維の
分布を均一化でき、また研磨用繊維は砥粒と異なり研磨
断面において合成樹脂材からとれてしまうことも少な
く、したがって研磨力に優れており、またバインダとし
て金属を用いているので合成樹脂をバインダとして用い
たものに比較して折れにくくすることができ耐久性を向
上させることができる。Further, as described above, according to the monofilament according to the present invention as defined in claim 6, since it is formed by containing the polishing fiber of a predetermined length in the metal,
Compared to the case where abrasive grains are used as the abrasive, the distribution of the abrasive fibers can be made uniform, and unlike the abrasive grains, the abrasive fibers are less likely to come off from the synthetic resin material in the polishing cross section, and therefore the polishing force It is excellent, and since metal is used as the binder, it is less likely to be broken and durability can be improved as compared with the case where the synthetic resin is used as the binder.
【００２２】また、上記したように請求項７記載の本発
明によるモノフィラメントによれば、上記請求項６記載
の本発明によるモノフィラメントの構成において、上記
金属を焼結合金としているので、すなわち焼結合金は耐
熱性に優れ、また硬度も幅広い範囲で設定することがで
きるので、利用目的に適応した研磨性能を得ることがで
きる。また焼結合金は多孔性の組織を有するため保油性
も向上させることができる。According to the monofilament according to the present invention as set forth in claim 7 as described above, in the structure of the monofilament according to the present invention as set forth in claim 6, the metal is a sintered alloy, that is, the sintered alloy. Has excellent heat resistance and can be set in a wide range of hardness, so that polishing performance suitable for the intended purpose can be obtained. Further, since the sintered alloy has a porous structure, the oil retaining property can be improved.
【００２３】また、上記したように請求項８記載の本発
明による研磨具によれば、上記請求項１，２，３，４，
５，６または７記載のモノフィラメントを複数集合させ
て構成しているので、研磨力、耐久性を向上させること
が可能となる。Further, as described above, according to the polishing tool of the present invention according to claim 8, the above-mentioned claim 1, 2, 3, 4,
Since a plurality of monofilaments described in 5, 6, or 7 are assembled, the polishing power and durability can be improved.
【００２４】上述のように、本発明によれば、研磨力に
優れしかもモノフィラメントとしての弾性および折れに
くさを向上させて耐久性にも優れた高い研磨性能を有す
るモノフィラメント、および研磨力、耐久性に優れた研
磨具を提供することが可能となる。As described above, according to the present invention, a monofilament having excellent polishing power, improved elasticity and resistance to bending as a monofilament, and excellent polishing performance with excellent durability, and polishing power and durability. It is possible to provide an excellent polishing tool.
【００２５】[0025]
【実施例】以下、添付図面を参照しながら本発明による
モノフィラメントおよびモノフィラメントを使用した研
磨具の実施例について説明する。EXAMPLES Examples of a monofilament and a polishing tool using the monofilament according to the present invention will be described below with reference to the accompanying drawings.
【００２６】図１は本発明の第１実施例によるモノフィ
ラメントを示す図である。図１に示すように本実施例の
モノフィラメントＦ1 は、合成樹脂１内に複数本の所定
長の研磨用繊維２を所定間隔で軸方向に略平行な状態で
含有させ、その合成樹脂１の外周を、研磨用繊維２をク
ロス状に編んでなるシート状補強材３で囲繞してなるも
のである。FIG. 1 is a diagram showing a monofilament according to a first embodiment of the present invention. As shown in FIG. 1, the monofilament F 1 of this embodiment contains a plurality of polishing fibers 2 of a predetermined length in a synthetic resin 1 at a predetermined interval in a state substantially parallel to the axial direction. The outer periphery is surrounded by a sheet-like reinforcing material 3 formed by knitting the polishing fibers 2 in a cross shape.
【００２７】上記合成樹脂１は熱硬化性樹脂でも熱可塑
性樹脂でもよく、例としてナイロン樹脂を挙げることが
できる。また上記研磨用繊維２としては例えばアルミナ
繊維や炭化ケイ素繊維を挙げることができる。The synthetic resin 1 may be a thermosetting resin or a thermoplastic resin, and examples thereof include a nylon resin. Examples of the polishing fibers 2 include alumina fibers and silicon carbide fibers.
【００２８】また上記研磨用繊維２は、例えば直径５μ
ｍ〜１２０μｍ、また旧モース硬度８〜９、スープ硬度
１５００〜２０００以上のものが選択される。これらに
ついては以下に述べる他の実施例においても同様であ
る。The polishing fiber 2 has a diameter of 5 μm, for example.
m-120 m, old Mohs hardness 8-9, soup hardness 1500-2000 or more are selected. The same applies to other embodiments described below.
【００２９】本実施例によるモノフィラメントＦ1 によ
れば、研磨用繊維２を含有させた合成樹脂２の外周を、
研磨用繊維２をクロス状に編んだシート状補強材で囲繞
することにより、モノフィラメントとしての弾性や折れ
にくさを向上させているので耐久性に優れ、かつ砥材と
して研磨用繊維２を用いているので研磨力にも優れた構
造とすることができる。また補強材３が研磨用繊維２か
らなるので、補強材３を容易に構成することができ、ま
た補強材３自体にも研磨能力を持たすことができる。According to the monofilament F 1 according to this embodiment, the outer periphery of the synthetic resin 2 containing the polishing fiber 2 is
Since the polishing fiber 2 is surrounded by a sheet-shaped reinforcing material knitted in a cloth shape, the elasticity as a monofilament and the resistance to folding are improved, so that the durability is excellent and the polishing fiber 2 is used as an abrasive material. Therefore, the structure having excellent polishing power can be obtained. Further, since the reinforcing material 3 is composed of the polishing fibers 2, the reinforcing material 3 can be easily constructed, and the reinforcing material 3 itself can have polishing ability.
【００３０】次に、本発明によるモノフィラメントの第
２実施例について説明する。図２は本発明の第２実施例
によるモノフィラメントを示す図である。なお、前記第
１実施例と同様の部材については前記第１実施例と同じ
番号を付し、一部説明は省略する。このことは以下に述
べる他の実施例についても同様である。Next, a second embodiment of the monofilament according to the present invention will be described. FIG. 2 is a diagram showing a monofilament according to a second embodiment of the present invention. The same members as those in the first embodiment are designated by the same reference numerals as those in the first embodiment, and the description thereof is partially omitted. This also applies to other embodiments described below.
【００３１】図２に示すように本実施例によるモノフィ
ラメントＦ2 は、合成樹脂１内に複数本の所定長の研磨
用繊維２を所定間隔で軸方向に略平行な状態で含有さ
せ、その合成樹脂１の外周を、研磨用繊維２をらせん状
に巻回してなる補強材３で囲繞してなるものである。本
実施例が前記第１実施例と異なるのは補強材３の構成の
みであり、したがってその作用効果も前記第１実施例と
同様である。As shown in FIG. 2, the monofilament F 2 according to this embodiment contains a plurality of polishing fibers 2 of a predetermined length in a synthetic resin 1 at a predetermined interval in a state substantially parallel to the axial direction, and synthesizing the same. The outer periphery of the resin 1 is surrounded by a reinforcing material 3 formed by spirally winding the polishing fiber 2. The present embodiment is different from the first embodiment only in the constitution of the reinforcing member 3, and therefore the operation and effect thereof are also the same as in the first embodiment.
【００３２】次に、本発明によるモノフィラメントの第
３実施例について説明する。図３は本発明の第３実施例
によるモノフィラメントを示す図である。Next, a third embodiment of the monofilament according to the present invention will be described. FIG. 3 is a diagram showing a monofilament according to a third embodiment of the present invention.
【００３３】図３に示すように本実施例よるモノフィラ
メントＦ3 は、合成樹脂１内に複数本の所定長の研磨用
繊維２を所定間隔で軸方向に略平行な状態で含有させ、
その合成樹脂１の外周を、合成樹脂１′内に複数本の研
磨用繊維２を軸方向に対して斜めの（例えば軸方向に対
して略４５°傾いた）状態で含有させてなる補強材３で
囲繞してなるものである。As shown in FIG. 3, the monofilament F 3 according to this embodiment contains a plurality of polishing fibers 2 of a predetermined length in a synthetic resin 1 at a predetermined interval in a state substantially parallel to the axial direction,
Reinforcing material obtained by containing a plurality of polishing fibers 2 in the synthetic resin 1'in the outer periphery of the synthetic resin 1 in a state inclined with respect to the axial direction (for example, inclined by about 45 ° with respect to the axial direction). Surrounded by 3.
【００３４】本実施例によるモノフィラメントＦ3 によ
れば、補強材３の合成樹脂１′内に研磨用繊維２をモノ
フィラメントＦ3 の軸方向に対して斜めに配したことに
より、特にモノフィラメントとしての軸方向回りのねじ
り強度を高めることが可能となる。なお、合成樹脂１と
１′は同じ樹脂としても違う樹脂としてもよい。According to the monofilament F 3 of this embodiment, the polishing fiber 2 is disposed in the synthetic resin 1'of the reinforcing material 3 obliquely with respect to the axial direction of the monofilament F 3 , so that the axis of the monofilament F 3 is particularly effective. It is possible to increase the torsional strength around the direction. The synthetic resins 1 and 1'may be the same resin or different resins.
【００３５】なお、上記第１，第２および第３実施例で
は、研磨用繊維２としてモノフィラメントＦ1 ，Ｆ2 の
軸方向に延びる長繊維を用いているが、研磨用繊維２と
して短繊維を用いることも可能であり、また合成樹脂１
内に研磨用繊維２以外に砥粒を混入させることも可能で
ある。図４にその一例を示す。図４は上記第１，第２お
よび第３実施例の合成樹脂内の構造として適用可能な例
を一部を破断してを示す図である。図中４は砥粒を示
す。In the first, second and third embodiments, long fibers extending in the axial direction of the monofilaments F 1 and F 2 are used as the polishing fibers 2, but short fibers are used as the polishing fibers 2. It is also possible to use, and synthetic resin 1
It is also possible to mix abrasive grains in addition to the polishing fibers 2. FIG. 4 shows an example thereof. FIG. 4 is a view showing a partially cutaway example applicable as a structure in the synthetic resin of the first, second and third embodiments. Reference numeral 4 in the figure indicates an abrasive grain.
【００３６】また上記第１，第２および第３実施例にお
いては、補強材３は研磨用繊維２で構成されているが、
研磨用繊維２以外の他の繊維で構成した補強材を用いる
ことも可能であり、また補強材自体の構造もこのように
繊維で構成されたものに限定されるものではない。In the first, second and third embodiments, the reinforcing material 3 is composed of the abrasive fiber 2,
It is also possible to use a reinforcing material composed of a fiber other than the polishing fiber 2, and the structure of the reinforcing material itself is not limited to such a fiber structure.
【００３７】次に、本発明によるモノフィラメントの第
４実施例について説明する。図５は本発明の第４実施例
によるモノフィラメントを示す図で、同図（ａ）は斜視
図、同図（ｂ）は断面拡大図および同図（ｂ）は拡大断
面図である。Next, a fourth embodiment of the monofilament according to the present invention will be described. 5A and 5B are views showing a monofilament according to a fourth embodiment of the present invention. FIG. 5A is a perspective view, FIG. 5B is an enlarged sectional view, and FIG. 5B is an enlarged sectional view.
【００３８】図５（ａ），（ｂ）に示すように本実施例
によるモノフィラメントＦ4 は、合成樹脂１内に複数本
の所定長の研磨用繊維２を所定間隔で軸方向に略平行な
状態で含有させるとともに、さらに合成樹脂１内に複数
本の所定長の補強用金属繊維５を所定間隔で軸方向に略
平行な状態で含有させてなるものである。As shown in FIGS. 5 (a) and 5 (b), the monofilament F 4 according to the present embodiment has a plurality of polishing fibers 2 of a predetermined length in a synthetic resin 1 which are substantially parallel to the axial direction at predetermined intervals. In addition to being contained in a state, a plurality of reinforcing metal fibers 5 of a predetermined length are further contained in the synthetic resin 1 at a predetermined interval in a state substantially parallel to the axial direction.
【００３９】本実施例によるモノフィラメントＦ4 によ
れば、研磨用繊維２とともに補強用金属繊維５を合成樹
脂１内に含有させることにより、モノフィラメントとし
ての弾性や折れにくさを向上させているので耐久性に優
れ、かつ砥材として研磨用繊維を用いているので研磨力
にも優れた構造とすることができる。According to the monofilament F 4 according to this embodiment, the reinforcing metal fiber 5 is contained in the synthetic resin 1 together with the polishing fiber 2 to improve elasticity and breakage resistance of the monofilament, so that durability is improved. Since the polishing fiber is used as the abrasive, it is possible to obtain a structure having excellent polishing ability.
【００４０】なお上記第４実施例では、研磨用繊維２お
よび補強用金属繊維５としてモノフィラメントＦ4 の軸
方向に延びる長繊維を用いているが、これらを短繊維に
代えることも可能である。Although the long fibers extending in the axial direction of the monofilament F 4 are used as the polishing fibers 2 and the reinforcing metal fibers 5 in the fourth embodiment, they may be replaced by short fibers.
【００４１】次に、本発明によるモノフィラメントの第
５実施例について説明する。図６は本発明の第５実施例
によるモノフィラメントを示す図で、同図（ａ）は斜視
図、同図（ｂ）は拡大断面図、および同図（ｃ）は研磨
用繊維の斜視図である。Next, a fifth embodiment of the monofilament according to the present invention will be described. 6A and 6B are views showing a monofilament according to a fifth embodiment of the present invention. FIG. 6A is a perspective view, FIG. 6B is an enlarged sectional view, and FIG. 6C is a perspective view of a polishing fiber. is there.
【００４２】図６（ａ）に示すように本実施例によるモ
ノフィラメントＦ5は、合成樹脂１内に複数本の所定長
の研磨用繊維２を所定間隔で軸方向に略平行な状態で含
有させ、図６（ｂ），（ｃ）に示すように各研磨用繊維
２の外周を、補強体６で囲繞してなるものである。本実
施例では補強体６は高弾性ゴム系材から構成される。本
実施例によるモノフィラメントＦ5 によれば、合成樹脂
１内に含有させた各研磨用繊維２の外周を、高弾性ゴム
系材からなる補強体で囲繞することにより、モノフィラ
メントとしての弾性や折れにくさを向上させているので
耐久性に優れ、かつ砥材として研磨用繊維２を用いてい
るので研磨力にも優れた構造とすることができる。As shown in FIG. 6 (a), the monofilament F 5 according to this embodiment contains a plurality of polishing fibers 2 of a predetermined length in a synthetic resin 1 at a predetermined interval in a state substantially parallel to the axial direction. As shown in FIGS. 6B and 6C, the outer circumference of each polishing fiber 2 is surrounded by a reinforcing body 6. In this embodiment, the reinforcing member 6 is made of a highly elastic rubber material. According to the monofilament F 5 according to the present embodiment, by surrounding the outer periphery of each polishing fiber 2 contained in the synthetic resin 1 with a reinforcing body made of a highly elastic rubber material, elasticity and breakage as a monofilament can be obtained. Since the hardness is improved, the durability is excellent, and since the polishing fiber 2 is used as the abrasive material, the structure can also be excellent in the polishing power.
【００４３】なお上記第５実施例では、研磨用繊維２と
してモノフィラメントＦ5 の軸方向に延びる長繊維を用
いているが、これらを短繊維に代えることもできる。ま
た上記第５実施例では、全ての研磨用繊維２を補強体６
で囲繞しているが、モノフィラメントとしての必要な弾
性および折れにくさが得られれば研磨用繊維２全てを補
強体６で囲繞する必要はない。In the fifth embodiment, long fibers extending in the axial direction of the monofilament F 5 are used as the polishing fibers 2, but they may be replaced by short fibers. In addition, in the fifth embodiment described above, all the polishing fibers 2 are replaced by the reinforcing member 6.
However, it is not necessary to surround all of the polishing fibers 2 with the reinforcing member 6 as long as the elasticity and the bending resistance required as a monofilament are obtained.
【００４４】また上記第５実施例では、補強体６は高弾
性ゴム系材からなるものであるが、補強体６は上記構成
に限定されるものではない。図７にその一例を示す。図
７は研磨用繊維の外周を囲繞する補強体の他の例を示す
図である。図７に示す補強体６は研磨用繊維２の外周を
囲繞する合成樹脂１″内に粒状ゴム７を含有させてなる
ものである。In the fifth embodiment, the reinforcing member 6 is made of a high elastic rubber material, but the reinforcing member 6 is not limited to the above structure. FIG. 7 shows an example thereof. FIG. 7: is a figure which shows the other example of the reinforcement body which surrounds the outer periphery of the fiber for polishing. The reinforcing body 6 shown in FIG. 7 is formed by incorporating granular rubber 7 into a synthetic resin 1 ″ that surrounds the outer periphery of the polishing fiber 2.
【００４５】次に、本発明によるモノフィラメントの第
６実施例について説明する。図８は本発明の第６実施例
によるモノフィラメントを示す図である。Next, a sixth embodiment of the monofilament according to the present invention will be described. FIG. 8 shows a monofilament according to a sixth embodiment of the present invention.
【００４６】図８に示すように本実施例によるモノフィ
ラメントＦ6 は、金属８内に複数本の所定長の研磨用繊
維２を所定間隔で軸方向に略平行な状態で含有させてな
るものである。本実施例では金属８は焼結合金とされ
る。As shown in FIG. 8, the monofilament F 6 according to the present embodiment comprises a plurality of polishing fibers 2 of a predetermined length contained in a metal 8 at a predetermined interval in a state substantially parallel to the axial direction. is there. In this embodiment, the metal 8 is a sintered alloy.
【００４７】本実施例によるモノフィラメントＦ6 によ
れば、バインダとして合成樹脂ではなく焼結合金８を用
いたことにより、モノフィラメントとしての弾性や折れ
にくさを向上させているので耐久性に優れ、かつ砥材と
して研磨用繊維２を用いているので研磨力にも優れた構
造とすることができる。また焼結合金は耐熱性に優れ、
また硬度も幅広い範囲で設定することができるので、利
用目的に適応した研磨性能を得やすいとともに、焼結合
金は多孔性の組織を有するため保油性にも優れている。According to the monofilament F 6 according to the present embodiment, since the sintered alloy 8 is used as the binder instead of the synthetic resin, the elasticity and the breakage resistance of the monofilament are improved, and therefore the durability is excellent and Since the polishing fiber 2 is used as the abrasive material, the structure having excellent polishing power can be obtained. Also, the sintered alloy has excellent heat resistance,
Further, since the hardness can be set in a wide range, it is easy to obtain the polishing performance adapted to the purpose of use, and the sintered alloy has a porous structure and is excellent in oil retention.
【００４８】なお上記第６実施例ではバインダとして焼
結合金８を用いているが、これは焼結合金に限定される
ものではなく、また上記第６実施例では研磨用繊維２と
してモノフィラメントＦ6 の軸方向に延びる長繊維を用
いているが、研磨用繊維２として短繊維を用いることも
可能である。この短繊維の研磨用繊維２を金属８内に含
有させてなるモノフィラメントＦ7 を本発明によるモノ
フィラメントの第７実施例として図９に示す。図９は本
発明の第７実施例によるモノフィラメントを示す図であ
る。Although the sintered alloy 8 is used as the binder in the sixth embodiment, it is not limited to the sintered alloy, and the monofilament F 6 is used as the polishing fiber 2 in the sixth embodiment. Although long fibers extending in the axial direction of are used, short fibers can be used as the polishing fibers 2. FIG. 9 shows a monofilament F 7 in which the polishing fibers 2 of the short fibers are contained in the metal 8 as a seventh embodiment of the monofilament according to the present invention. FIG. 9 shows a monofilament according to a seventh embodiment of the present invention.
【００４９】次に本発明によるモノフィラメントを使用
した研磨具の実施例について説明する。図１０は本発明
の一実施例によるモノフィラメントを使用した研磨具を
示す側面図である。Next, examples of the polishing tool using the monofilament according to the present invention will be described. FIG. 10 is a side view showing a polishing tool using a monofilament according to an embodiment of the present invention.
【００５０】図１０に示すように本実施例による研磨具
１１は、板状の支持部材１２上に多数本のモノフィラメ
ントＦを所定間隔で植設集合させてなる研磨ブラシであ
る。使用するモノフィラメントＦとしては上記した本発
明の各実施例１〜７によるモノフィラメントＦ1 〜Ｆ7
を利用することが可能である。そして、本発明によるモ
ノフィラメントを使用した本実施例による研磨具１１
は、研磨力、耐久性ともに優れたものとなる。As shown in FIG. 10, the polishing tool 11 according to the present embodiment is a polishing brush in which a large number of monofilaments F are planted and assembled on a plate-shaped supporting member 12 at predetermined intervals. Monofilament F 1 to F 7 by each Examples 1 to 7 of the present invention as a monofilament F used the above-mentioned
Can be used. Then, the polishing tool 11 according to the present embodiment using the monofilament according to the present invention
Has excellent polishing power and durability.
【００５１】なお上記実施例の研磨具１１は、モノフィ
ラメントＦを板状の支持部材１２上に植設集合させてな
るものであるが、複数本のモノフィラメントＦを例えば
円柱状支持部材の周面上に植設集合させて回転ブラシと
して使用することができるなど研磨具の形状は使用目的
に応じて適宜変更が可能である。また本発明によるモノ
フィラメントを単独で研磨具として使用することも可能
である。The polishing tool 11 of the above embodiment is constructed by implanting and collecting monofilaments F on a plate-like support member 12. For example, a plurality of monofilaments F are provided on the peripheral surface of a cylindrical support member. The shape of the polishing tool can be appropriately changed according to the purpose of use, such as the fact that it can be planted and assembled in the above and used as a rotating brush. Further, the monofilament according to the present invention can be used alone as a polishing tool.
【図１】本発明の第１実施例によるモノフィラメントを
示す図FIG. 1 is a diagram showing a monofilament according to a first embodiment of the present invention.
【図２】本発明の第２実施例によるモノフィラメントを
示す図FIG. 2 is a diagram showing a monofilament according to a second embodiment of the present invention.
【図３】本発明の第３実施例によるモノフィラメントを
示す図FIG. 3 is a diagram showing a monofilament according to a third embodiment of the present invention.
【図４】上記第１，第２および第３実施例の合成樹脂内
の構造として適用可能な例を示す図。FIG. 4 is a diagram showing an example applicable as a structure in the synthetic resin of the first, second and third embodiments.
【図５】本発明の第４実施例によるモノフィラメントを
示す図FIG. 5 is a diagram showing a monofilament according to a fourth embodiment of the present invention.
【図６】本発明の第５実施例によるモノフィラメントを
示す図FIG. 6 is a diagram showing a monofilament according to a fifth embodiment of the present invention.
【図７】研磨用繊維の外周を囲繞する補強体の他の例を
示す図FIG. 7 is a view showing another example of the reinforcing body surrounding the outer periphery of the polishing fiber.
【図８】本発明の第６実施例によるモノフィラメントを
示す図FIG. 8 is a diagram showing a monofilament according to a sixth embodiment of the present invention.
【図９】本発明の第７実施例によるモノフィラメントを
示す図FIG. 9 is a diagram showing a monofilament according to a seventh embodiment of the present invention.
【図１０】本発明の一実施例によるモノフィラメントを
使用した研磨具を示す側面図FIG. 10 is a side view showing a polishing tool using a monofilament according to an embodiment of the present invention.
Ｆ，Ｆ1 〜Ｆ7 モノフィラメント １，１′，１″ 合成樹脂 ２ 研磨用繊維 ３ 補強材 ４ 砥粒 ５ 補強用金属繊維 ６ 補強体 ８ 金属（焼結合金） １１ 研磨具F, F 1 to F 7 monofilament 1, 1 ′, 1 ″ Synthetic resin 2 Polishing fiber 3 Reinforcing material 4 Abrasive grains 5 Reinforcing metal fiber 6 Reinforcing body 8 Metal (sintered alloy) 11 Polishing tool
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０２Ｇ 3/04 7199−3Ｂ 3/44 7199−3Ｂ Ｄ０６Ｍ 15/19 (72)発明者 槙前 辰己 広島県安芸郡府中町新地３番１号 マツダ 株式会社内─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI Technical display location D02G 3/04 7199-3B 3/44 7199-3B D06M 15/19 (72) Inventor Makimae Tatsumi 3-1, Shinchi, Fuchu-cho, Aki-gun, Hiroshima Prefecture Mazda Motor Corporation
Claims (8)
させてなるモノフィラメントであって、前記所定長の研
磨用繊維が含有された合成樹脂の外周に、該外周を囲繞
する補強材が設けられていることを特徴とするモノフィ
ラメント。1. A monofilament comprising a synthetic resin containing a predetermined length of polishing fiber, wherein a reinforcing material surrounding the outer periphery is provided on the outer periphery of the synthetic resin containing the predetermined length of polishing fiber. A monofilament characterized by being provided.
れた繊維からなることを特徴とする請求項１記載のモノ
フィラメント。2. The monofilament according to claim 1, wherein the reinforcing material is made of fibers arranged on the outer periphery of the synthetic resin.
させてなるモノフィラメントであって、前記所定長の研
磨用繊維が含有された合成樹脂内にさらに補強用金属繊
維が含有されていることを特徴とするモノフィラメン
ト。3. A monofilament in which a predetermined length of polishing fiber is contained in a synthetic resin, and a reinforcing metal fiber is further contained in the synthetic resin containing the predetermined length of polishing fiber. A monofilament characterized by that.
させてなるモノフィラメントであって、前記研磨用繊維
の外周に、該外周を囲繞する補強体が設けられているこ
とを特徴とするモノフィラメント。4. A monofilament in which a predetermined length of polishing fiber is contained in a synthetic resin, and a reinforcing body surrounding the outer periphery is provided on the outer periphery of the polishing fiber. Monofilament.
記補強体が高弾性ゴム系材からなることを特徴とする請
求項４記載のモノフィラメント。5. The monofilament according to claim 4, wherein the synthetic resin is a thermosetting resin, and the reinforcing body is made of a highly elastic rubber material.
てなることを特徴とするモノフィラメント。6. A monofilament comprising a metal containing a predetermined length of polishing fiber.
するモノフィラメント。7. A monofilament, wherein the metal is a sintered alloy.
記載のモノフィラメントを複数本集合させてなることを
特徴とする研磨具。8. The method of claim 1, 2, 3, 4, 5, 6 or 7.
A polishing tool comprising a plurality of the described monofilaments.