JPH0582431B2 - - Google Patents
Info
- Publication number
- JPH0582431B2 JPH0582431B2 JP59074387A JP7438784A JPH0582431B2 JP H0582431 B2 JPH0582431 B2 JP H0582431B2 JP 59074387 A JP59074387 A JP 59074387A JP 7438784 A JP7438784 A JP 7438784A JP H0582431 B2 JPH0582431 B2 JP H0582431B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- present
- adhesive tape
- rubber
- newspaper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
〔発明の技術分野〕
本発明は新聞、雑誌等に印刷された記事、特に
新聞インキ(JIS K 5703)で印刷された記事を
写しとつて、スクラツプブツク、ノート等に容易
に複写することができる簡易複写用粘着テープも
しくはシートに関する。[Detailed Description of the Invention] [Technical Field of the Invention] The present invention allows articles printed in newspapers, magazines, etc., especially articles printed with newspaper ink (JIS K 5703), to be easily copied into scrapbooks, notebooks, etc. This invention relates to an adhesive tape or sheet for simple duplication that can be used to make copies.
従来新聞記事等を記録保存するには複写機で複
写したり、はさみで切り抜いてスクラツプブツ
ク、ノート等の貼着していたが、複写するのは経
費が高くつき、はさみで切り抜くのは、裏面が利
用できず、切り抜いた残りが利用できないという
欠点があつた。
Conventionally, newspaper articles, etc., have been recorded and preserved by copying them with a copy machine, cutting them out with scissors, and pasting them on scrapbooks, notebooks, etc., but copying them is expensive, and cutting them out with scissors means that the back side is The disadvantage was that it was not possible to use the cutout, and the remaining parts after cutting it out could not be used.
上記欠点を解消するために特開昭58−3897号公
報には透明フイルム上に液状可塑剤を含む透明な
感圧接着組成物(対ベークライト板接着力30〜
4000g/25mm)を塗設した転着体をインキ面に貼
り合せた後剥離することを特徴とする印刷物から
インキ層を転写する方法が記載されている。 In order to eliminate the above-mentioned drawbacks, Japanese Patent Application Laid-Open No. 58-3897 discloses a transparent pressure-sensitive adhesive composition containing a liquid plasticizer on a transparent film (adhesive strength to Bakelite plate of 30 to 30).
A method for transferring an ink layer from a printed matter is described, which is characterized in that a transfer body coated with 4,000 g/25 mm) is attached to an ink surface and then peeled off.
しかしながら上記方法では感圧接着組成物とし
てアクリル系粘着物・ポリビニルエーテル粘着
物、ゴム系粘着物等の粘着物を使用しているの
で、明瞭な複写物を得るには感圧接着組成物層を
厚くし、強く圧着する必要があり、そのため剥離
する際に紙むしり現象が発生し、複写された新聞
等が使用できなくなるという欠点があつた。 However, in the above method, adhesives such as acrylic adhesives, polyvinyl ether adhesives, rubber adhesives, etc. are used as pressure-sensitive adhesive compositions, so in order to obtain clear copies, the pressure-sensitive adhesive composition layer is required. It is necessary to make the paper thick and press it strongly, which has the disadvantage that paper tearing occurs when it is peeled off, making the copied newspapers etc. unusable.
本発明の目的は新聞、雑誌等に印刷された記
事、特に新聞インキ(JIS K 5703)で印刷され
た記事を、紙むしり現象を発生することなく写し
とつて、スクラツプブツク、ノート等に容易に複
写することのできる簡易複写用粘着テープもしく
はシートを提供することにある。
The purpose of the present invention is to copy articles printed in newspapers, magazines, etc., especially articles printed with newsprint ink (JIS K 5703), without causing paper tearing, and to easily copy articles into scrapbooks, notebooks, etc. An object of the present invention is to provide an adhesive tape or sheet for simple copying that can be used for copying.
本発明の要旨は実質的に粘着性を有さない熱可
塑性樹脂もしくはゴムと液状可塑剤が重量比で
1:1〜5の範囲で混合された混合物100重量部
と粘着付与樹脂1〜40重量部よりなる透明微粘着
性組成物が透明フイルムの一面に積層されてなる
簡易複写用粘着テープもしくはシートに存する。
The gist of the present invention is to combine 100 parts by weight of a mixture of a thermoplastic resin or rubber having substantially no tackiness and a liquid plasticizer in a weight ratio of 1:1 to 5, and 1 to 40 parts by weight of a tackifying resin. The adhesive tape or sheet for simple copying comprises a transparent slightly adhesive composition laminated on one side of a transparent film.
本発明で使用する熱可塑性樹脂もしくはゴム
は、実質的に粘着性を有さないものであつて、た
とえば塩化ビニル樹脂、塩化ビニルを主体とし、
エチレン、プロピレン等の塩化ビニルと共重合し
うる重合性モノマーとの共重合体、エチルアクリ
レート、メチルメタアクリレート、ブチルアクリ
レート等のアクリレート系重合体及び共重合体、
エチレン−プロピレンゴム、スチレンとイソプレ
ン、ブタジエン、イソブチレン等のブロツク共重
合ゴムなどがあげられる。 The thermoplastic resin or rubber used in the present invention has substantially no tackiness, and includes, for example, vinyl chloride resin, vinyl chloride as a main component,
Copolymers with polymerizable monomers copolymerizable with vinyl chloride such as ethylene and propylene; acrylate polymers and copolymers such as ethyl acrylate, methyl methacrylate, and butyl acrylate;
Examples include ethylene-propylene rubber, block copolymer rubber of styrene and isoprene, butadiene, isobutylene, etc.
本発明で使用する液状可塑剤としてはたとえば
ジオクチルフタレート、ジブチルフタレート、ジ
オクチルアジペート、トリクレジルホスフエート
等のエステル類、軽油、スピンドル油、マシン油
等の鉱物油、アマニ油、ゴマ油、ヒマシ油、ツバ
キ油等の植物油、合成油などがあげられる。 Examples of liquid plasticizers used in the present invention include esters such as dioctyl phthalate, dibutyl phthalate, dioctyl adipate, and tricresyl phosphate; mineral oils such as light oil, spindle oil, and machine oil; linseed oil, sesame oil, and castor oil; Examples include vegetable oils such as camellia oil, and synthetic oils.
本発明で使用する粘着付与樹脂としては、一般
に粘着剤に使用されているものであつて、たとえ
ばロジン樹脂、水添ロジン樹脂、テルペン樹脂、
テルペン−フエノール樹脂、アルキルフエノール
樹脂、クマロンインデン樹脂、アリサイクリツク
樹脂等があげられる。 The tackifier resin used in the present invention is one commonly used in adhesives, such as rosin resin, hydrogenated rosin resin, terpene resin,
Examples include terpene-phenol resin, alkylphenol resin, coumaron indene resin, and alicyclic resin.
本発明における微粘着性組成物は上記熱可塑性
樹脂もしくはゴムと液状可塑剤と粘着付与樹脂よ
りなる透明なものであり、熱可塑性樹脂もしくは
ゴムと液状可塑剤の混合比率は、液状可塑剤の量
が少ないと混合物が硬くて紙になじみにくく、多
くなるとベタベタして粘着力が高くなるので重量
比で1:1〜5の範囲であり、又粘着付与樹脂の
添加量は少なくなると組成物の粘着性が小さくな
り、多くなると粘着性が向上して紙むしり現象を
おこすようになるので、上記混合物100重量部に
対し1〜40重量部添加される。 The slightly adhesive composition in the present invention is a transparent composition consisting of the above-mentioned thermoplastic resin or rubber, a liquid plasticizer, and a tackifier resin, and the mixing ratio of the thermoplastic resin or rubber and liquid plasticizer is determined by the amount of liquid plasticizer. If the amount of tackifying resin is too low, the mixture will be hard and difficult to adapt to the paper, and if it is too large, it will become sticky and have high adhesive strength.The weight ratio should be in the range of 1:1 to 5. If the adhesiveness is increased, the adhesiveness will be increased and the paper peeling phenomenon will occur.
尚上記組成物の粘着力は、特に限定されるもの
ではないが、被着体としてベークライト板を使用
し、JIS Z 1522に準拠して測定した際に10〜
200g/25mm巾であるのが好ましい。 The adhesive strength of the above composition is not particularly limited, but when measured in accordance with JIS Z 1522 using a Bakelite plate as an adherend, the adhesive strength is 10 to 10.
Preferably it is 200g/25mm width.
本発明で使用する透明フイルムは実質的に透明
であれば良く、たとえばポリプロピレンフイル
ム、ポリ塩化ビニルフイルム、酢酸繊維素フイル
ム、ポリエステルフイルム、ポリスチレンフイル
ム、セロハンフイルム、硫酸紙等があげられ、酢
酸繊維素フイルムが好適に使用される。 The transparent film used in the present invention may be substantially transparent, and examples thereof include polypropylene film, polyvinyl chloride film, cellulose acetate film, polyester film, polystyrene film, cellophane film, parchment paper, etc. Films are preferably used.
本発明の簡易複写用粘着テープもしくはシート
の製造方法は特に限定されるものではなく、任意
の方法が採用されてよいが、たとえば上記熱可塑
性樹脂もしくはゴムと液状可塑剤をロール等で加
熱混合し、ゾル状混合物とし、これに粘着付与樹
脂を添加混合して組成物を得、透明フイルムの一
面に塗布、冷却する方法があげられる。 The method for producing the adhesive tape or sheet for simple copying of the present invention is not particularly limited, and any method may be adopted, but for example, the above-mentioned thermoplastic resin or rubber and liquid plasticizer are heated and mixed using a roll or the like. The method includes a method in which a sol-like mixture is prepared, a tackifying resin is added and mixed to obtain a composition, and the composition is coated on one side of a transparent film and cooled.
本発明の簡易複写用粘着テープもしくはシート
の構成は上述の通りであり、新聞、雑誌等の被複
写物に貼付け、剥離して、スクラツプブツク、ノ
ート等に貼付けることによつて容易に必要な部分
を複写することができる。特に新聞インキはカー
ボンブラツクと、固着剤であるロジン、エステル
ゴム、ギルソナイト、石油樹脂等の鉱物油に可溶
性樹脂を軽油、スピンドル油、マシン油等の鉱物
油に溶解、分散したいわゆるコンポジシヨンワニ
スをビヒクルとし、粘度が3〜15ポイズという低
粘度のものであり、新聞は多孔質の繊維間隙の多
きな新聞に上記新聞インキで印刷したものである
から、本発明の粘着テープもしくはテープにより
新聞記事は紙むしり現象を生ずることなく、特に
鮮明に複数回複写することができる。
The structure of the adhesive tape or sheet for simple copying of the present invention is as described above, and it can be easily attached to a copying object such as a newspaper or magazine, peeled off, and attached to a scrapbook, notebook, etc. can be copied. Newspaper ink in particular uses carbon black and a so-called composite varnish, which is made by dissolving and dispersing a soluble resin in mineral oil such as rosin, ester rubber, gilsonite, or petroleum resin as a fixing agent in mineral oil such as diesel oil, spindle oil, or machine oil. The vehicle is one with a low viscosity of 3 to 15 poise, and the newspaper is a porous newspaper with many fiber gaps printed with the above newspaper ink, so newspaper articles can be printed using the adhesive tape or tape of the present invention. can be particularly clearly reproduced multiple times without causing the paper tearing phenomenon.
次に本発明の実施例を説明する。 Next, examples of the present invention will be described.
実施例
塩化ビニル樹脂(重合度1050) 20重量部
ポリメチルメタクリレート 10 〃
ジオクチルフタレート 70 〃
ジブチルチンジマレート 2 〃
ステアリン酸亜鉛 2 〃
上記組成よりなる配合物を160℃のロールに供
給して溶融混合し、ゾル状の混合物を得、次にロ
ジンを5重量部添加し、さらに混合して微粘着性
組成物を得、得られた組成物をパークコーター
で、厚さ45μ、裏面がマツト加工された透明なジ
アセテートフイルムに厚さ30μに塗布し冷却して
本発明の粘着テープを得た。得られた粘着テープ
の粘着力は60g/25mm巾であつた。又得られた粘
着テープを新聞紙に貼り付け、剥離したところ、
紙むしりすることなく容易に剥離でき、鮮明な画
像が粘着テープに転写できた。又新聞の同じ地点
で繰り返し複写を行つたところ8回まで鮮明な画
像が得られた。Example Vinyl chloride resin (degree of polymerization 1050) 20 parts by weight Polymethyl methacrylate 10 〃 Dioctyl phthalate 70 〃 Dibutyltin dimaleate 2 〃 Zinc stearate 2 〃 The blend having the above composition was fed to a roll at 160°C and melt mixed. Then, 5 parts by weight of rosin was added to obtain a sol-like mixture, and further mixed to obtain a slightly sticky composition. The adhesive tape of the present invention was obtained by coating it on a transparent diacetate film to a thickness of 30 μm and cooling it. The adhesive strength of the resulting adhesive tape was 60 g/25 mm width. In addition, when the obtained adhesive tape was pasted on newspaper and peeled off,
It could be easily peeled off without tearing the paper, and a clear image could be transferred to the adhesive tape. Also, when copying was repeated at the same spot on the newspaper, clear images were obtained up to 8 times.
Claims (1)
くはゴムと液状可塑剤が重量比で1:1〜5の範
囲で混合された混合物100重量部と粘着付与樹脂
1〜40重量部よりなる透明微粘着性組成物が透明
フイルムの一面に積層されてなる簡易複写用粘着
テープもしくはシート。1 A transparent product consisting of 100 parts by weight of a mixture of a thermoplastic resin or rubber that does not have substantially tackiness and a liquid plasticizer in a weight ratio of 1:1 to 5, and 1 to 40 parts by weight of a tackifying resin. An adhesive tape or sheet for simple copying comprising a slightly adhesive composition laminated on one side of a transparent film.