JPH05331581A - Aluminum alloy expanded material for surface roughening and its production - Google Patents

Abstract

PURPOSE:To provide an expanded material of Al alloy having a fine and uniform rough surface with sharp pits by performing chemical surface roughening treatment by alkali etching. CONSTITUTION:This material has a composition which consists of 1-1.5% Mn, <=0.15% Si, <=0.3% Fe, and the balance essentially Al and where Mn/Si>=10 and Mn/Fe>=5 are satisfied. Further, it can contain 0.05-5% Mg. Moreover, an Al6Mn precipitate and/or an Al6(MnFe) precipitate (where Fe/(Fe+Mn)<=0.5 is satisfied) is dispersed in a grain size of 0.01-3mum by >=1X10<5>/mm<2>. This material can be produced by performing precipitation treatment at 300-600 deg.C for 0.5-24hr in an arbitrary stage after casting.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an aluminum alloy wrought material having a surface roughened and used, in particular, an aluminum alloy wrought material having a surface roughened by alkali etching. The present invention relates to a material and a manufacturing method thereof.

[0002]

2. Description of the Related Art Depending on the intended use of an wrought aluminum alloy material, it may be necessary to perform a treatment for imparting uniform and fine unevenness to the surface, that is, a roughening treatment. For example, in applications such as building materials that are coated and used, or in applications that require adhesion such as composite boards or printed circuit boards,
In order to improve the adhesion of the coating film and the adhesive layer by the anchor effect on the surface of the base, a roughening treatment is often performed as a base treatment before coating or before adhesion. In addition, in applications such as optical parts and electronic parts, it may be required to have no gloss. In such a case, it is necessary to apply a roughening treatment to make the surface non-reflective and matte. is there. Further, when a functional film is formed on the surface like a PS plate for a printing plate to be used, it may be subjected to a roughening treatment in order to improve its function and increase the surface area of the base.

Conventionally, JIS R 1100 alloy or 5 has been mainly used for the purpose of using such a surface-roughening treatment.
There were many 052 alloys.

By the way, the above-mentioned methods for surface roughening are roughly classified into the following three methods A, B and C.

A: Mechanical surface roughening method A method for physically and mechanically forming irregularities on the surface,
Shot blasting method, hairline processing, mechanical graining method, roll roughening method, etc.

B: Chemical surface roughening method A method of chemically etching the surface to form pits, which is an acidic etching solution such as an HCl-based etching solution, an acidic ammonium fluoride-based etching solution, or a phosphoric acid-based etching solution. And a method of etching using an alkaline etching solution such as a NaF-based etching solution or a NaOH-based etching solution.

C: Electrochemical surface roughening method This is a method in which a surface is electrolyzed by an alternating current, a direct current or a composite waveform thereof using an HCl type electrolytic bath, an HNO ₃ type electrolytic bath or the like.

Among these surface roughening methods, in the mechanical surface roughening method of A, it is difficult to stably form a uniform rough surface, there is a problem in mass productivity, and the final process is performed. In addition to problems such as the need for cleaning in, there is a problem that the cost is inevitably high. On the other hand, the chemical roughening method of B generally has the advantages of low cost and excellent mass productivity. Among these chemical surface roughening methods, the method using an acidic etching solution can form deep and fine pits, but lacks uniformity of pits, and the etching surface becomes sharp and the convex portions fall off. There is a risk that Further, among the chemical surface roughening methods, the method using an alkaline etching solution can form uniform and smooth irregularities, but in the conventional aluminum alloy wrought material, the pits are shallow and large, and it is difficult to obtain a fine rough surface. there were. Further, in the electrochemical roughening method of C, if the bath and electrolysis conditions are appropriately selected, a relatively good rough surface can be obtained, but the equipment cost and running cost are high, and the target material is There is also the problem of being limited to coils or small ones.

[0009]

As described above, each of the conventional roughening methods has advantages and disadvantages. Among them, the chemical roughening method is advantageous in view of cost and mass productivity. it is conceivable that. Among the chemical surface-roughening methods, the method using an alkaline etching solution (alkali etching) is excellent in the uniformity of pits, and therefore fine and sharp pits are formed by this surface-roughening method by alkali etching. If it becomes possible, it will be advantageous not only in terms of cost and mass productivity but also in terms of the obtained rough surface property. However, as already mentioned,
In conventional general aluminum alloy wrought materials, the pits must be shallow and large when subjected to alkali etching, so it cannot be said that the surface is sufficiently roughened, and the adhesion of the coating film and adhesive In reality, it has not been possible to sufficiently meet the purpose of roughening such as enhancing the property.

The present invention has been made in view of the above circumstances, and it is possible to form fine and sharp pits uniformly and densely when performing the chemical surface roughening treatment by alkali etching. It is an object of the present invention to provide an aluminum alloy wrought material with which a roughened surface having excellent surface performance can be obtained.

[0011]

Means for Solving the Problems The inventors of the present application have conducted an earnest experiment and study to achieve the above-mentioned object, and as a result,
The amount of each component in the Mn-based (or Al-Mn-Mg-based) alloy, the Mn / Si ratio, and the Mn / Fe ratio are appropriately adjusted, and thus the type of Mn-based precipitate is appropriately adjusted.
Furthermore, they have found that an aluminum alloy wrought material having a good surface roughening property by alkali etching can be obtained by appropriately adjusting the size and density of precipitates, and completed the present invention.

Specifically, the aluminum alloy wrought material of the invention of claim 1 contains 1 to 1.5 wt% of Mn, and Si
Is regulated to 0.15 wt% or less and Fe to 0.3 wt% or less, and the ratio of Mn (wt%) / Si (wt%) is 1 or less.
It is characterized in that it is 0 or more, the ratio of Mn (wt%) / Fe (wt%) is 5 or more, and the balance is Al and inevitable impurities.

Further, the aluminum alloy wrought material of the invention of claim 2 further contains 0.05 to 5 wt% of Mg in addition to the respective components defined in the invention of claim 1.

Furthermore, the aluminum alloy wrought product of the invention of claim 3 defines the precipitate (Mn-based intermetallic compound precipitate), and the aluminum alloy wrought product of claim 1 or 2. in wood, the Mn-based intermetallic compound precipitates, Al ₆ Mn precipitates, and / or Fe (wt%) / {Fe (wt%) + Mn (wt%)} Al 6 ratio of 0.5 or less ( MnFe) precipitate is 0.01
It is characterized in that it is dispersed in a size of ˜3 μm and a distribution density of 1 × 10 ⁵ pieces / mm ² or more.

Further, the invention of claim 4 defines a method for producing an aluminum alloy wrought material excellent in roughening property by alkali etching, wherein Mn
1 to 1.5 wt%, Si is regulated to 0.15 wt% or less, Fe is regulated to 0.3 wt% or less, and the ratio of Mn (wt%) / Si (wt%) is 10 or more. Moreover, the ratio of Mn (wt%) / Fe (wt%) is 5 or more,
Further, if necessary, 0.05 to 5 wt% of Mg is contained, and an alloy having the balance of Al and unavoidable impurities is cast,
Further, in performing hot working and / or cold working to obtain an wrought material having a predetermined plate thickness, after the casting, or after hot working, or during or after cold working, 3
Heat to a temperature of 00 to 600 ° C. for 0.5 to 24 hours to give M
As an n-based intermetallic compound precipitate, an Al ₆ Mn precipitate and / or Fe (wt%) / {Fe (wt%) + Mn (wt
%)} Of Al ₆ (MnFe) precipitates having a ratio of 0.5 or less, having a size of 0.01 to 3 μm and 1 × 10 ⁵ pieces / mm
^The feature is to obtain a wrought material dispersed with a distribution density of ² or more.

[0016]

Function: The type of Mn-based intermetallic compound precipitate has a great influence on the rough surface properties of the wrought aluminum alloy material after the chemical roughening treatment by alkali etching. Therefore, by appropriately setting the ratio of the content of each alloying element and the content of each alloying element so that an appropriate Mn-based intermetallic compound precipitate can be obtained, the roughening property by alkali etching is significantly improved. Can be made

As the Mn-based intermetallic compound precipitates in aluminum alloys, generally, Al ₆ Mn and Al ₆ (Mn
Fe), αAlMn (Fe) Si, and even C
For example, a small amount of r, Ti, etc. forms a solid solution. These M
Of the n-based precipitates, Al ₆ Mn and Al ₆ (MnF
e) relates to roughening by alkali etching, and especially Al ₆ Mn contributes to obtain a good rough surface, but Al ₆ Mn
_As will be described later, ₆ (MnFe) may deteriorate the rough surface property after roughening by alkali etching depending on the amount of Fe in the intermetallic compound. Further αAlMn
(Fe) Si does not contribute to roughening by alkali etching. Therefore, especially among Mn-based precipitates, Al
₆ Mn-based precipitates are deposited, while αAlMn (Fe)
If Si is not deposited and Al ₆ (MnFe) is further deposited, the amount of Fe must be regulated.

The relationship between the type of Mn-based precipitate and the surface roughening property by alkali etching will be described in more detail.

According to the detailed experiments and examinations by the present inventors,
Among the Mn-based intermetallic compound deposits, it was found that particularly Al ₆ Mn and Al ₆ (MnFe) dissolve the intermetallic compound itself by an alkaline etching solution such as caustic soda to form pits. Regarding this point, conventionally, there was an idea that the Al ₆ Mn phase is cathodic with respect to an alkaline etching solution such as caustic soda, and therefore the matrix around the intermetallic compound is dissolved to form pits. However, such a conventional idea is wrong, and as described above, it was newly found that the intermetallic compound itself is dissolved to form a pit. This is supported also by the microstructure photograph (FIG. 1) of the surface of the rolled material of Alloy No. 1 in Example 1 which will be described later, in the state of being subjected to the mild alkali etching. That is, FIG. 1 shows the surface of the rolled material obtained under the same conditions as in Example 1 with respect to the alloy No. 1 material of Example 1, after the surface was polished and then etched with a 5% NaOH aqueous solution at 60 ° C. for 10 seconds. In this surface, Al ₆ Mn crystallized substances as coarse particles and Al ₆ Mn precipitates as fine particles were dispersed, but these crystallized substances and precipitates were dissolved. It is shown as a pit. Where Al ₆ Mn
A part of the crystallized substance remains black due to the reaction,
It can be seen that the crystallized substance itself melts and a pit having a clear shape corresponding to the contour is generated. Note that the crystallized substances remaining after reacting in black are also dissolved and removed by further progressing the etching. Here, it was confirmed that no trace of melting around the crystallized substance was found, and thus the conventional idea was incorrect.

The Al ₆ Mn precipitate is also much smaller than the crystallized product, but it can be seen that, like the crystallized product, the precipitate itself melts to form pits. In actual surface roughening, finer A than fine Al ₆ Mn crystallization product
The l ₆ Mn precipitate is important, and fine and evenly dispersed Al ₆ Mn precipitate can be dissolved to form fine and sharp pits uniformly and densely.

On the other hand, Al ₆ (MnFe) becomes cathodic with respect to the alkaline etching solution if the proportion of Fe in each element constituting the intermetallic compound becomes large, and it becomes difficult to dissolve Al ₆ (MnFe) in the alkaline etching solution. The surface treatment property deteriorates. Specifically, Al ₆ (MnFe)
Fe (wt%) / {Fe (wt%) + Mn (wt
%)} Exceeds 0.5, Al ₆ (MnFe) precipitates are less likely to be dissolved by the alkaline etching solution. Therefore, it is preferable to control the value of the above ratio to 0.5 or less. Thus, the Fe of the Al ₆ (MnFe) compound is
In order to adjust the amount, it is necessary to regulate the ratio of Mn (wt%) / Fe (wt%) to 5 or more for the alloy as a whole as described later.

Further, since αAlMn (Fe) Si is not dissolved by an alkaline etching solution such as caustic soda and therefore does not form pits, it has no effect on roughening, and if αAlMn (Fe) Si is present, rather. Adversely affect the formation of a uniform and fine rough surface.
In other words, αAlMn (Fe) Si becomes cathodic than the Al matrix and does not dissolve itself, but rather the surrounding aluminum matrix is corroded, so that the desired sharp pit cannot be obtained. The precipitation of αAlMn (Fe) Si is related to the amount of Si in the alloy and the ratio of the amount of Mn to the amount of Si. Therefore, in the present invention, the amount of Si in the alloy is set to 0.15 wt% or less as described later. Regulation and Mn (wt%) /
The ratio of Si (wt%) is regulated to 10 or more.

Further, the rough surface properties after the surface roughening treatment by alkali etching include Mn-based precipitates (particularly Al ₆ Mn precipitates and Al ₆ (MnFe with an atomic ratio of Fe / (Fe + Mn) of 0.5 or less). The size and distribution density of the precipitates) also have an effect. The size of these Mn-based precipitates is 0.01μ
If it is less than m, the precipitates are too small to form pits and 3μ
If it exceeds m, the pits are too large and a uniform and fine rough surface cannot be obtained. When the distribution density of these Mn-based precipitates is less than 1 × 10 ⁵ pieces / mm ² , the pits are sparse and the roughening is insufficient. Therefore, in the invention of claim 3,
Mn-based precipitates related to surface roughening, that is, Al ₆ Mn precipitates, and Fe (wt%) / {Fe (wt%) + Mn (wt
%)} Is 0.5 or less, the size of Al ₆ (MnFe) precipitates is within the range of 0.01 to 3 μm, and the distribution density is 1 × 10 ^5.
Specified as more than 1 piece / mm ² .

Further, the reasons for limiting the alloy component composition in the present invention will be described.

Mn: Mn is Al ₆ Mn that contributes to the formation of a fine and uniform rough surface by alkali etching.
It is an essential element for depositing precipitates. Mn amount is 1
If it is less than wt%, the amount of Al ₆ Mn precipitates deposited is insufficient and roughening is also insufficient. On the other hand, when Mn exceeds 1.5 wt%, the surface roughening property is good, but coarse intermetallic compounds are likely to be generated during DC casting and the castability is deteriorated. Especially when Mg coexists. The tendency becomes remarkable. Therefore, the amount of Mn is set within the range of 1 to 1.5 wt%.

Si: Si coexists with Mn and αAlMn
(Fe) Si precipitate is formed. This αAlMn (F
e) Since the Si phase does not dissolve in an alkaline etching solution such as caustic soda as described above, it becomes cathodic than the Al matrix, so that the Al matrix around the precipitate is eroded and the desired sharp pit is obtained. Absent. Therefore, the amount of Si is preferably as small as possible in order to suppress the precipitation of αAlMn (Fe) Si precipitates. Specifically, the Mn content is 1 to 1 as in the present invention.
In the case of 1.5 wt%, if the Si amount exceeds 0.15%, the surface roughening property due to alkali etching deteriorates, so the Si amount was restricted to 0.15 wt% or less. Even in this range, the amount of Si is preferably 0.10 wt% or less. In order to suppress the precipitation of αAlMn (Fe) Si precipitates, Fe (wt%) / Si (wt
%) Is also important, and by controlling the ratio to be 10 or more, the precipitation of αAlMn (Fe) Si precipitates can be suppressed and a good rough surface can be obtained by alkali etching.

Fe: Fe is Mn in Al ₆ Mn.
It exists as Al ₆ (MnFe) in a state where it is partially replaced with. The Al ₆ (MnFe) phase is dissolved by the alkaline etching solution, but becomes cathodic with respect to the alkaline etching solution such as caustic soda as the Fe content increases. As mentioned above, the tendency is Al
Fe (wt%) / {Fe (wt%) + M in ₆ (MnFe)
When the ratio of n (wt%)} exceeds 0.5, it becomes remarkable, the etching property by the caustic soda-based alkali etching solution becomes weak, and it becomes difficult to form the desired sharp, fine and uniform pits. Therefore, it is preferable to control the ratio of Fe (wt%) / {Fe (wt%) + Mn (wt%)} in Al ₆ (MnFe) to be 0.5 or less.
For that purpose, the absolute amount of Fe is restricted to 0.3 wt% or less, preferably 0.1 wt% or less, and the ratio of Mn (wt%) / Fe (wt%) in the entire alloy is 5 or more, preferably 10 or more. Regulate so that

Mg: Mg is not only effective for improving the strength, but also contributes to promoting the precipitation of Al ₆ Mn and improving the roughening property by alkali etching. Therefore, in the wrought aluminum alloy material of the present invention, Mg is positively added if necessary. When Mg is actively added, the above effect cannot be sufficiently obtained when the content is less than 0.05 wt%, while the castability is deteriorated when it exceeds 5 wt%. Within 5% by weight. Incidentally, Mg of less than 0.05 wt% is usually contained as an unavoidable impurity even if it is not positively added.

Other than the above elements, Al and unavoidable impurities may be basically used, but Cr, Zr, and V are essential to the effect of the present invention even if added to 0.3 wt% each. Since it has no effect, up to 0.3 wt% of each is allowed. If these elements exceed 0.3 wt%, coarse intermetallic compounds are formed, which is not preferable. In general Al alloys, a small amount of Ti is used in order to refine the ingot crystal structure and prevent the texture and streaks of the rolled plate.
May be added alone or in combination with a trace amount of B. In the aluminum alloy wrought product of the present invention, 0.15 wt% or less of Ti may be added alone or in combination with B of 100 ppm or less. Permissible. Ti is 0.
If it exceeds 15 wt%, TiAl ₃ coarse intermetallic compound will be formed and it will be unsuitable, and if B exceeds 100 ppm, it will become B.
Is saturated, and linear defects due to coarse TiB ₂ particles are generated, which is unsuitable. Further, when Mg is added, the molten metal is easily oxidized at the time of casting, but Be is generally added to prevent the oxidation of the molten metal in that case. Addition of Be does not adversely affect other performances, and therefore a small amount of B is added in the case of addition of Mg.
You may add e. In this case, the amount of Be added is 500 pp
m or less is common. In addition, if the Cu content is 1.0 wt% or less and the Zn content is 2.0 wt% or less, the effect of the present invention is not adversely affected.
% Or less and Zn of 2.0 wt% or less is allowed.

Next, a method for manufacturing the wrought aluminum alloy material of the present invention will be described.

First, an alloy having the above-described composition is cast by a conventional method. The casting method may be DC casting (semi-continuous casting method) or thin plate continuous casting method (continuous casting and rolling method). In the DC casting method, especially when the Mn content is high, M
If g coexists, a coarse intermetallic compound is likely to be formed, which adversely affects the surface roughening property and deteriorates the castability. However, in the present invention, the Mn content is 1.5 wt% or less. Therefore, the DC casting method is less likely to produce a coarse intermetallic compound, and the castability is good.

For the ingot obtained by DC casting,
It is usual to carry out homogenization treatment as necessary, hot rolling, and then cold rolling as necessary to obtain a rolled plate with a predetermined plate thickness, and hot forging and hot extrusion. Sometimes do. On the other hand, it is usual that the cast plate obtained by the thin plate continuous casting method is subjected to homogenization treatment if necessary and then cold-rolled to obtain a rolled plate having a predetermined plate thickness. In the case of the method of the present invention, at any of these stages after casting, heat treatment (precipitation treatment) is performed in order to disperse and precipitate the Mn dissolved during casting into the size and distribution density as described above. I need to do it. That is, when performing hot working such as hot rolling, hot forging, hot extrusion at the stage after casting, or after casting, at the stage after the hot working, and further at cold working such as cold rolling. When performing, precipitation treatment may be performed during or after cold working.

This precipitation treatment may be performed by heating to a temperature in the range of 300 to 600 ° C. for 0.5 to 24 hours. If the temperature of the precipitation treatment is less than 300 ° C, the precipitation of Mn-based precipitates will be insufficient, while if it exceeds 600 ° C, the Mn-based precipitates once precipitated will re-dissolve and the amount of precipitation will be insufficient, resulting in alkali etching. The roughening property deteriorates. If the heating time of the precipitation treatment is less than 0.5 hours, the precipitation of Mn-based precipitates will be insufficient, while if it exceeds 24 hours, the precipitation will be saturated and will be economically wasted.

Although such a precipitation treatment may be carried out independently for the purpose of precipitation, it is usually convenient to carry out it together with another heat treatment. That is, when performing a homogenizing treatment after casting, it can be combined with the homogenizing treatment, and when performing hot working after casting, it can be combined with heating for the hot working. Furthermore, when performing intermediate annealing between hot working and cold working or in the middle of cold working, or when performing final annealing after cold working, it may be performed also as the intermediate annealing or final annealing. .. In any case, the purpose of the precipitation treatment is achieved by performing these treatments within the range of the above-mentioned conditions.

The aluminum alloy wrought material of the present invention obtained as described above is applied to the purpose of applying a surface roughening treatment by alkali etching. This surface roughening treatment by alkali etching may be carried out according to a conventional method, and a material having a sharp and uniform pit with a fine pit can be obtained by using a normal alkali etching solution such as caustic soda. The aluminum alloy wrought product of the present invention is characterized in that fine and sharp pits are uniformly formed by alkali etching. However, depending on the purpose of roughening, relatively large pits and fine pits are formed. A complex surface roughness may be required. In that case, mechanical surface roughening treatment such as shot blasting or mechanical brushing, or chemical surface roughening with an etching solution such as ferric chloride solution other than the alkaline etching solution. It is sufficient to perform a chemical conversion treatment in advance to form coarse pits and then perform alkali etching to form fine pits.

In the above description, only the wrought material is explained, but in the case of a casting material such as a die casting material or a die casting material, the precipitation treatment under the above-mentioned conditions is carried out to obtain a good result by alkali etching. It is possible to obtain roughening properties.

[0037]

【Example】

Example 1: Each alloy No. 1 to No. 5 shown in Table 1 was 450 mm × 1200 mm × 4000 by DC casting method.
Cast into mm slabs. Each of the obtained slabs, 450 ℃
After heating for 2 hours, the hot rolling was started and the hot rolling was performed to a thickness of 4 mm. Then, cold rolling was performed to a thickness of 2 mm, intermediate annealing was performed at 400 ° C. for 2 hours, and further cold rolling was performed to a plate thickness of 1.5 mm.

As a roughening treatment by alkali etching, each of the obtained rolled plates was etched with a 10% NaOH aqueous solution at 60 ° C. for 3 minutes, washed with water and desmutted with nitric acid. The glossiness of the surface of each plate was measured, the lightness index L according to the Hunter color difference formula (see JIS Z8730) was measured, and the average pit diameter was examined by a scanning electron microscope. The results are shown in Table 2. Here, the L value of the lightness index is closer to white as the value is larger.

[0039]

[Table 1]

[0040]

[Table 2]

From Table 2, in the case of the rolled materials of alloys No. 1 and No. 2 within the compositional composition range and compositional ratio range of the present invention, the surface pits after etching with caustic soda are both fine. It can be seen that a rough surface having a low glossiness and a high L value, that is, a white rough surface having a fine rough surface shape and less reflection was obtained.

For each of the alloys shown in Table 1, hot rolling and cold rolling were performed as described above, and a photograph obtained by a transmission electron microscope was processed by an image analysis processor to obtain an average. The deposit size and the average deposit density were examined. As a result, in the alloys No. 1 and No. 2 of the present invention,
Among the Al ₆ Mn precipitates and the Al ₆ (MnFe) precipitates, the precipitates having a Fe (wt%) / {Fe (wt%) + Mn (wt%)} ratio of 0.5 or less have a size of 0. .05 to 1.2
μm, distribution density is 1 × 10 ⁹ to 1 × 10 ¹¹ pieces / mm
Turned out to be ² . In contrast, in the No. 3 comparative alloy, most of the precipitates are αAlMn (Fe) Si
As a phase, almost no precipitate of Al ₆ Mn phase was observed, and its density was less than 1 × 10 ⁵ pieces / mm ² . Also
In the case of No. 4 and No. 5 conventional alloys, Al ₆ Mn precipitates and Fe (wt%) / {Fe (wt%) + Mn (wt%)}
No Al ₆ (MnFe) precipitate having a ratio of 0.5 or less was observed at all.

Regarding the rolled material of Alloy No. 1, after surface polishing, mild caustic soda etching, that is, 5% Na
FIG. 1 shows a microstructure photograph of the surface after etching with an OH aqueous solution at 60 ° C. for 10 seconds. This is as described above.

Example 2: No. 6 and No. 7 shown in Table 3
Each alloy was cast into a 6-inch diameter billet by the DC casting method. For alloy No. 6 billet, 500 ° C ×
After carrying out a homogenizing treatment for 10 hours, hot extrusion was performed at 450 ° C. to obtain a plate having a cross-sectional shape of 6 mm × 120 mm. On the other hand, the alloy No. 7 billet was homogenized at 460 ° C. for 12 hours and then hot extruded at 420 ° C. to obtain a plate having the same size as described above. The alloy No. 7 extruded material was further solution-treated at 450 ° C for 30 minutes and water-quenched, and then aged at 120 ° C for 24 hours to obtain T.
6 materials were used.

As a roughening treatment by alkali etching, each of these materials was etched with a 10% NaOH aqueous solution at 50 ° C. for 5 minutes, washed with water and desmutted with nitric acid, and the surface glossiness and L value were examined. .. The results are shown in Table 4. For alloy No. 7 material, in addition to the alkali-etched samples described above, shot-blasted and then alkali-etched samples similar to the above, and acid ammonium fluoride instead of alkali etching Etched samples were prepared, and the glossiness and L value of these samples were also examined.

[0046]

[Table 3]

[0047]

[Table 4]

As is apparent from Table 4, the alloy of the present invention of No. 6 has a whiteness (L value) after alkali etching and a low glossiness, and therefore the conventional alloy No. 7 has an alkali etching material. Not only better, but better than the conventional alloy No. 7 shot blast + alkali etching material,
It is almost equivalent to the conventional acidic ammonium fluoride etching material of alloy No. 7. It can be seen that the alkali etching is much more advantageous in terms of cost than the acid ammonium fluoride etching, and therefore a good rough surface can be obtained at low cost.

Example 3 The alloy No. 8 in Table 5 was cast into a coil having a thickness of 7 mm and a width of 800 mm by a thin plate continuous casting method, and cold rolled to a thickness of 1 mm at 430 ° C.
After the intermediate annealing for 2 hours, the steel sheet was cold rolled to a thickness of 0.4 mm. Here, the above-mentioned intermediate annealing at 430 ° C. for 2 hours also serves as the precipitation treatment in the manufacturing method of the present invention. For comparison, with respect to the same alloy No. 8, a cold rolled sheet having a thickness of 0.4 mm was obtained in the same manner as the above process, except that the intermediate annealing (intermediate annealing also serving as precipitation treatment) was not performed. Each rolled plate of these alloys No. 8 was subjected to surface roughening treatment by alkali etching, etched with a 5% NaOH aqueous solution at 80 ° C. for 60 seconds, washed with water and desmutted with nitric acid. For further comparison, alloy No. in Table 5
Regarding the conventional alloy of No. 9 (JIS 1050 alloy), H18 material that was DC-cast, hot-rolled, and then cold-rolled to a thickness of 1.2 mm with intermediate annealing by continuous annealing at 500 ° C. for 0 seconds was also prepared. Current density 9 in 3% nitric acid solution
Electrochemical etching (electrochemical roughening treatment) was performed at 0 A / dm ² , followed by washing with water and desmutting with nitric acid.

Table 6 shows the results of examining the L value, glossiness, and pit size of each plate after the surface roughening treatment.

[0051]

[Table 5]

[0052]

[Table 6]

As is clear from Table 6, when the alloy No. 8 of the present invention was subjected to the precipitation treatment also as the intermediate annealing, the conventional alloy No. 9 was electrically treated by the roughening treatment by alkali etching. The same pit size, L value, and glossiness as those obtained by the chemical roughening treatment were obtained. Even with the alloy No. 8 of the present invention, it is clear that a good rough surface cannot be obtained if the treatment corresponding to the precipitation treatment is not performed.

Further, with respect to the No. 8 alloy, a rolled plate produced through intermediate annealing also serving as a precipitation treatment as described above,
FIG. 2 shows a rough surface in a state where etching was performed for 40 seconds at 50 ° C. using a 5% NaOH aqueous solution. From FIG.
It can be seen that a fine and uniform rough surface is formed.

As described above, the aluminum alloy wrought product of the present invention has a rough pit formed by forming a rough surface having relatively coarse pits and then forming a fine rough surface by alkali etching. It is possible to form a rough surface in which the above and fine pits are superposed, and an example in that case is shown in FIGS. These are all obtained by subjecting the rolled material of Alloy No. 8 used in FIG. 2 to surface roughening treatment. Here, FIG. 3 shows 20% FeCl ₃ (second chloride
(Iron) aqueous solution shows a state where the surface roughening treatment is performed only at 70 ° C. for 10 minutes. In this state, the rough surface of the coarse pit is formed, but 5% NaO is further added to the rough surface of FIG.
The rough surface of FIG. 4 is obtained by etching at 50 ° C. for 40 seconds using the H aqueous solution. In FIG. 4, it can be seen that the rough rough surface and the fine rough surface are superposed.

[0056]

According to the aluminum alloy wrought material for surface roughening of the present invention, it is possible to form a fine and uniform rough surface having sharp pits only by the chemical surface roughening treatment by alkali etching. it can. Then, even if the conventional method had to rely on mechanical surface roughening treatment, electrochemical surface roughening treatment, or chemical surface roughening treatment using an acid-based etching solution, chemical etching by alkali etching should be used instead. By applying the roughening treatment, it is possible to reduce the cost and improve the mass productivity. The purpose of the roughening applied to the aluminum alloy wrought material for surface roughening of the present invention is to improve the adhesiveness and the adhesion of the coating film or various functional coatings, and further for optical applications, electronic parts, etc. The purpose is to obtain a non-reflective material or a matting material for applications such as panels for various electric devices, but it goes without saying that it is not limited to them.

Further, according to the method for producing an aluminum alloy wrought material for surface roughening of the present invention, only a simple precipitation treatment is performed during the normal wrought material manufacturing process, or during the normal wrought material manufacturing process. As described above, a wrought material having a good surface roughening property by alkali etching can be obtained only by performing the precipitation treatment in combination with the heat treatment.

[Brief description of drawings]

FIG. 1 is a metallographic photograph (magnification: 860) showing an example of the surface texture of the wrought aluminum alloy material of the present invention that has been subjected to a slight alkali etching.

2 is a metallographic photograph (magnification: 3000 times) showing the surface condition of the rolled material of Alloy No. 8 of Example 3 which has been subjected to a surface roughening treatment by alkali etching.

[Fig. 3] Second chloride for the rolled material of alloy No. 8 in the example
It is a metallographic photograph (magnification: 3000 times) showing the surface condition in a state where etching is performed with an iron aqueous solution.

[Fig. 4] Fig. 4 is a diagram of the rolled material of alloy No. 8 of Example 3.
3 is a metallographic photograph (magnification: 3,000 times) showing the surface condition of a state in which the sample was etched with an aqueous solution of ferric chloride in the same manner as above, and then subjected to alkali etching.

Claims (4)

[Claims] 1. Containing 1 to 1.5 wt% of Mn and Si
Is regulated to 0.15 wt% or less and Fe to 0.3 wt% or less, and the ratio of Mn (wt%) / Si (wt%) is 1 or less.
An aluminum alloy wrought material for surface roughening, which is characterized by having a ratio of Mn (wt%) / Fe (wt%) of 5 or more, and the balance being Al and unavoidable impurities. 2. In addition to the above components, Mg0.05
The aluminum alloy wrought material for surface roughening according to claim 1, which contains -5 wt%. 3. An Mn-based intermetallic compound precipitate is Al
₆ Mn precipitate, and / or Fe (wt%) / {Fe
Al whose ratio of (wt%) + Mn (wt%)} is 0.5 or less
_{The 6} (MnFe) precipitates are dispersed in a size of 0.01 to 3 μm and with a distribution density of 1 × 10 ⁵ pieces / mm ² or more. Aluminum alloy wrought material for surface roughening. 4. Mn 1 to 1.5 wt% is contained and Si
Is regulated to 0.15 wt% or less and Fe to 0.3 wt% or less, and the ratio of Mn (wt%) / Si (wt%) is 1 or less.
0 or more, and the ratio of Mn (wt%) / Fe (wt%) is 5 or more, and if necessary, Mg 0.05 to 5
When casting an alloy containing wt% and the balance consisting of Al and unavoidable impurities, and further performing hot working and / or cold working to obtain an wrought material of a predetermined plate thickness, after the casting, Alternatively, after hot working, or during or after cold working, a temperature of 300 to 600 ° C. for 0.5 to 24
After heating for a time, Mn-based intermetallic compound precipitates as Al
₆ Mn precipitate, and / or Fe (wt%) / {Fe
Al whose ratio of (wt%) + Mn (wt%)} is 0.5 or less
Aluminum for roughening, characterized in that a wrought material having ₆ (MnFe) precipitates dispersed in a size of 0.01 to 3 μm and a distribution density of 1 × 10 ⁵ pieces / mm ² or more is obtained. Manufacturing method of alloy wrought material.