JPH05278052A - Production of decorative sheet - Google Patents
Production of decorative sheetInfo
- Publication number
- JPH05278052A JPH05278052A JP4084139A JP8413992A JPH05278052A JP H05278052 A JPH05278052 A JP H05278052A JP 4084139 A JP4084139 A JP 4084139A JP 8413992 A JP8413992 A JP 8413992A JP H05278052 A JPH05278052 A JP H05278052A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- pearl pigment
- decorative sheet
- plastic
- irregularities
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、建材や成形品の装飾に
使用するための化粧シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative sheet for use in decorating building materials and molded articles.
【０００２】[0002]
【従来の技術】壁材、床材のような建材、家電製品のキ
ャビネット、机などの家具を製造するときに光沢のある
意匠を付与するための化粧シートとして、パール顔料を
練り込んだプラスチックシートまたは表面にパールイン
キをベタ印刷したプラスチックシートと、絵柄を印刷し
たプラスチックの印刷シートとの積層材が用いられてい
る。 しかしこれらの化粧シートは、光沢に変化がない
ために立体感をもたず意匠が単調である。2. Description of the Related Art A plastic sheet containing a pearl pigment as a decorative sheet for giving a glossy design when manufacturing furniture such as wall materials, flooring materials, cabinets for electric home appliances and desks. Alternatively, a laminated material of a plastic sheet having a solid printing of pearl ink on the surface and a plastic printing sheet having a pattern printed is used. However, since these decorative sheets have no change in gloss, they do not have a three-dimensional effect and have a monotonous design.
【０００３】化粧シートの表面にエンボスを施せば光沢
を変化させることができるはずであるが、化粧シートと
印刷シートとを積層するときの熱と圧力によってエンボ
スが消えてしまうから、結局は均一な光沢をもつ製品し
か得られない。Although it should be possible to change the gloss by embossing the surface of the decorative sheet, the embossing disappears due to heat and pressure when the decorative sheet and the printing sheet are laminated, so that it is eventually uniform. Only glossy products can be obtained.
【０００４】本発明者は、他の研究者らと共同で行なっ
た研究の成果として、鱗片状のパール顔料を使用して、
シート内部に立体感を生じさせた化粧シートを開発し、
すでに提案した（特願平４−２４０９３）。 この化粧
シートは、鱗片状のパール顔料を透明または半透明のプ
ラスチックに練り込んでシートに形成し、その裏面に絵
柄印刷、エンボス加工および金属薄膜形成の少なくとも
１種を施してなり、プラスチックシート中の鱗片状パー
ル顔料の分散の密度および（または）層面の配向方向が
部分によって異なることによって、上記の内部立体感を
生じさせたものである。As a result of research conducted in collaboration with other researchers, the present inventor has used flaky pearl pigments,
We developed a decorative sheet that creates a three-dimensional effect inside the sheet,
It has already been proposed (Japanese Patent Application No. 4-24093). This decorative sheet is formed by kneading a flaky pearl pigment into a transparent or translucent plastic to form a sheet, and at least one of pattern printing, embossing and metal thin film formation on the back side of the sheet. The density of dispersion of the flaky pearl pigment and / or the orientation direction of the layer surface is different depending on the part, so that the above internal stereoscopic effect is generated.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、上記
のような、パール顔料がもたらす光沢が部分によって異
なり、シートの内部に立体感を生じさせた化粧シートを
容易に製造する方法を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a method for easily producing a decorative sheet as described above, in which the pearlescent pigment brings about a different gloss depending on the part and gives a three-dimensional effect inside the sheet. To do.
【０００６】[0006]
【課題を解決するための手段】本発明のシート内部に立
体感を生じさせた化粧シートの製造方法は、基本的には
図１に示すように鱗片状のパール顔料（２）を透明また
は半透明のプラスチックに練り込み、少なくとも一方の
面に凹凸（３）を有するシート（１Ａ）に形成し、この
シートを加熱プレスして図２に示すようなシート表面の
凹凸をなくした平坦なシート（１Ｂ）とすることにより
パール顔料の分散の密度および（または）層面の配向の
方向が部分により異なるシートを得ることができる。The method for producing a decorative sheet having a three-dimensional effect inside the sheet according to the present invention is basically such that a scale-like pearl pigment (2) is transparent or semi-transparent as shown in FIG. It is kneaded into transparent plastic to form a sheet (1A) having irregularities (3) on at least one surface, and this sheet is hot-pressed to eliminate the irregularities on the sheet surface as shown in FIG. 1B) makes it possible to obtain a sheet in which the dispersion density of the pearl pigment and / or the orientation direction of the layer surface differs depending on the part.
【０００７】プラスチックシートの材料は、パール顔料
の練り込みが容易なものであれば何でもよく、たとえば
ポリオレフィン、ビニル系樹脂、ポリエステル、アクリ
ル樹脂、スチレン系樹脂、ポリカーボネートなどからえ
らべばよい。 このプラスチックは、パール顔料の光沢
や色調が見えるように、透明ないし半透明であることを
要するが、この条件をみたせば、無色のもの、着色した
もの、どちらでもよい。Any material can be used for the plastic sheet as long as the pearl pigment can be easily kneaded therein. For example, polyolefin, vinyl resin, polyester, acrylic resin, styrene resin, polycarbonate or the like may be selected. This plastic needs to be transparent or semi-transparent so that the luster and color tone of the pearl pigment can be seen, but depending on this condition, it may be colorless or colored.
【０００８】パール顔料としては、二酸化チタン被覆雲
母、魚鱗箔、酸塩化ビスマスなど、真珠のような光沢を
もつ顔料であって、鱗片状のものを使用する。As the pearl pigment, pigments having a pearly luster, such as titanium dioxide-coated mica, fish scale foil, bismuth acid chloride, and the like, are used.
【０００９】パール顔料を練り込んだ、少なくとも一方
の面に凹凸を有するプラスチックシートを得るには、顔
料を練り込んだプラスチックを、加工温度やカレンダリ
ングロールの周速度などの条件を適切に選択することで
ある。 前記した、無機または有機質の繊維、たとえば
ガラス繊維やポリエステル繊維のような、パール顔料の
分散を阻害するものを混入させる手法は、この場合も有
効である。In order to obtain a plastic sheet in which pearl pigment is kneaded and which has irregularities on at least one surface, the plastic in which the pigment is kneaded is appropriately selected under conditions such as processing temperature and peripheral speed of the calendering roll. That is. The above-described method of mixing the inorganic or organic fibers, such as glass fibers and polyester fibers, which inhibits the dispersion of the pearl pigment, is also effective in this case.
【００１０】図３に示すように、上記の熱プレスによっ
て得たプラスチックシート（１Ｂ）の一方または両方の
面に、絵柄などの印刷層（４）および（または）着色ベ
タ印刷層（５）を設けてもよい。 絵柄は、木目や石目
など天然物を模したものや、文字、図形、縞模様、水玉
模様、抽象柄など任意である。 絵柄の印刷は、グラビ
ア法、スクリーン法などの既知の印刷法に従えばよく、
またホットスタンプ法のような転写法によって行なって
もよい。 所望であれば、図４に示すように、さらに一
方または両方の面に、プラスチックの保護層（６）を設
けてもよい。保護層の材料は、パール顔料を練り込んだ
プラスチックシートおよび化粧シートを積層する基材の
材料に応じて、上記したプラスチックのなかから選べば
よい。As shown in FIG. 3, a printing layer (4) such as a pattern and / or a colored solid printing layer (5) are provided on one or both surfaces of the plastic sheet (1B) obtained by the above heat pressing. It may be provided. The design is arbitrary such as imitation of natural products such as wood grain or stone grain, characters, figures, striped patterns, polka dots, and abstract patterns. The pattern may be printed by a known printing method such as a gravure method or a screen method.
Alternatively, a transfer method such as a hot stamp method may be used. If desired, a plastic protective layer (6) may also be provided on one or both sides, as shown in FIG. The material of the protective layer may be selected from the above-mentioned plastics according to the material of the base material on which the plastic sheet in which the pearl pigment is kneaded and the decorative sheet are laminated.
【００１１】保護層を設ける態様においては、シートに
印刷を施したものを使用し、このシートをパール顔料を
練り込んだプラスチックシートに積層してもよい。 パ
ール顔料を練り込んだプラスチックシートと保護層とす
るシートとの積層は、既知のラミネート法によればよ
く、必要であれば、接着シートを介して行なえばよい。
接着シートには、保護層とするシートよりも軟化温度が
低く透明なもの、たとえば軟質ポリ塩化ビニルシート、
アクリル樹脂系のシートを使用する。In the embodiment in which the protective layer is provided, a printed sheet may be used, and this sheet may be laminated on a plastic sheet in which a pearl pigment is kneaded. The laminating of the plastic sheet in which the pearl pigment is kneaded and the sheet serving as the protective layer may be carried out by a known laminating method, and if necessary, may be carried out via an adhesive sheet.
The adhesive sheet, which has a lower softening temperature than the sheet to be the protective layer and is transparent, such as a soft polyvinyl chloride sheet,
Use acrylic resin sheet.
【００１２】本発明の化粧シートの貼着面に隠蔽層を設
けると、被貼着材の表面を隠蔽するとともに奥行きのあ
る意匠を表現できる。 隠蔽層は、化粧シートの貼着面
に設けた印刷層や保護シートのほかに、新たな層として
設けてもよいし、パール顔料を練り込んだプラスチック
シートより貼着面側の印刷層を隠蔽インキのベタ印刷層
とすることにより設けてもよい。 ベタ印刷は、白色や
メタリックな色であってもよい。 ベタ印刷に代えて不
透明な着色シートを積層することもでき、この着色シー
トは、白色顔料を使用したものも含まれる。By providing a cover layer on the surface of the decorative sheet of the present invention, the surface of the adherend can be covered and a design with depth can be expressed. The hiding layer may be provided as a new layer in addition to the printing layer and protective sheet provided on the sticking surface of the decorative sheet, or the printing layer on the sticking surface side of the plastic sheet in which the pearl pigment is kneaded is hidden. It may be provided by forming a solid printing layer of ink. Solid printing may be white or metallic. Instead of solid printing, an opaque coloring sheet may be laminated, and this coloring sheet includes a sheet using a white pigment.
【００１３】上記の平坦化と保護層となるシートのラミ
ネートとは、どちらも熱プレス加工であるから、同時に
行なうことができる。 その場合は、パール顔料を練り
込んだプラスチックシートと保護フィルムとの間に、接
着シートを使用する必要がない。 平坦化とラミネート
を同時に行なう本発明の化粧シートの製造方法は、図１
に示したように、鱗片状のパール顔料（２）を透明また
は半透明のプラスチックに練り込み、少なくとも一方の
面に凹凸を有するシート（１Ａ）に形成し、続いて図５
に示すようにこのシートの一方または両方の面にプラス
チックの保護フィルム（７）を重ね、加熱プレスして、
図６に示すように、上記シートの凹凸（３）をなくした
もの（１Ｂ）とすると同時に保護フィルム（７）との熱
ラミネートをし、パール顔料の分散の密度および（また
は）層面の配向の方向が部分により異なるシート（１
Ｃ）を得ることからなる。 図示した例は、裏面に絵柄
印刷層（４）を設けた保護フィルム（６）を一方の面に
重ね、ベタ印刷層（５）を設けたフィルム（７）を他方
の面に重ねた場合を示す。Both the flattening and the laminating of the sheet to be the protective layer can be carried out at the same time because both are hot pressing. In that case, it is not necessary to use an adhesive sheet between the plastic sheet in which the pearl pigment is kneaded and the protective film. The method for producing a decorative sheet of the present invention in which flattening and laminating are performed at the same time is shown in FIG.
As shown in Fig. 5, the scale-like pearl pigment (2) is kneaded into a transparent or translucent plastic to form a sheet (1A) having irregularities on at least one surface, and then, as shown in FIG.
As shown in, the plastic protective film (7) is overlaid on one or both sides of this sheet, and hot pressed,
As shown in FIG. 6, the sheet (1B) without the unevenness (3) of the sheet was heat-laminated with the protective film (7) at the same time, and the density of the dispersion of the pearl pigment and / or the orientation of the layer surface was changed. Sheets with different directions (1
C). In the illustrated example, the case where the protective film (6) provided with the pattern printing layer (4) on the back surface is overlaid on one surface and the film (7) provided with the solid printing layer (5) is overlaid on the other surface is shown. Show.
【００１４】[0014]
【作用】さきに開示した発明に続く研究の結果、鱗片状
のパール顔料をプラスチックに練り込んでシートにした
とき、混練や製膜の条件によっては凹凸をもったシート
ができ、これを熱プレスによって平坦なシートにしたと
き、パール顔料の分散の密度および層面の配向方向、と
くに後者の不均一さが拡大されることを本発明者は見出
した。 その理由は主として、鱗片状パール顔料を練り
込んだプラスチックの流動性が低く、平坦化により凸部
がつぶされてその部分のパール顔料の層面の配向が行わ
れることにあると考えられる。[Function] As a result of the research following the invention disclosed above, when a scale-like pearl pigment is kneaded into a plastic to form a sheet, a sheet having irregularities is formed depending on the conditions of kneading and film formation. The present inventor has found that when a flat sheet is formed by the method, the dispersion density of the pearl pigment and the orientation direction of the layer surface, especially the non-uniformity of the latter are increased. It is considered that the reason is that the plastic in which the scale-like pearl pigment is kneaded has low fluidity, and the convex portion is crushed by flattening, and the layer surface of the pearl pigment in that portion is oriented.
【００１５】このようにして製造された化粧シートは、
プラスチックシート中にパール顔料が分散の密度が異な
るように、および（または）層面の配向の方向が異なる
ように存在しているので、光沢が不均一に見え、化粧シ
ート内部で立体感が生じたものとなる。The decorative sheet thus manufactured is
Since the pearl pigments are present in the plastic sheet with different dispersion densities and / or different orientations of the layer surfaces, the gloss looks uneven and a three-dimensional effect occurs inside the decorative sheet. Will be things.
【００１６】絵柄印刷層を設けた態様のものは、絵柄と
不均一な光沢とが重なり合って、変化に富んだ意匠をあ
らわすことができる。 とくに、絵柄を檜や欅などの木
目模様、またはトラバーチン、マーブルとよばれる大理
石の模様としたものは、光沢の変化がそれらの天然物の
もつ「照り」を再現して、本物とほとんど同じ外観を与
える。In the embodiment in which the pattern print layer is provided, the pattern and the non-uniform luster are overlapped with each other, so that a variety of designs can be represented. In particular, the designs with wood patterns such as cypress and keyaki, or the patterns of marble called travertine and marble, have a gloss change that reproduces the "shine" of those natural products, and the appearance is almost the same as the real thing. give.
【００１７】[0017]
【実施例】厚さ０．２ｍｍの透明なポリ塩化ビニルシー
ト「ＧＲクリヤ」（理研ビニル製）に、塩酢ビ−アクリ
ル系インキ「化Ｘ」（昭和インキ工業所製）で絵柄を印
刷した第一の保護フィルム、および厚さ０．０８ｍｍの
着色ポリ塩化ビニルシート「Ｂ−３００」（バンドー化
学製）に同じインキで絵柄を印刷した第二の保護フィル
ムを用意した。[Examples] A pattern was printed on a transparent polyvinyl chloride sheet "GR clear" (manufactured by Riken Vinyl) having a thickness of 0.2 mm with a vinyl chloride / acryl-based ink "Chemical X" (manufactured by Showa Ink Kogyo Co., Ltd.). A first protective film and a second protective film in which a pattern was printed with the same ink on a colored polyvinyl chloride sheet "B-300" (manufactured by Bando Kagaku) having a thickness of 0.08 mm were prepared.
【００１８】ポリ塩化ビニルに鱗片状のパール顔料を混
練し、カレンダリングにより、平均厚さ０．２ｍｍで一
方の面に、平均アラサ０．０５ｍｍのシートに成形し
た。A scaly pearl pigment was kneaded with polyvinyl chloride and calendered to form a sheet having an average thickness of 0.2 mm and an average surface of 0.05 mm on one surface.
【００１９】このプラスチックシートを第一の保護フィ
ルムと第二の保護フィルムとでサンドイッチし、熱圧ラ
ミネートした。 ラミネートの条件は、温度１６０℃、
圧力１０ｋｇ／ｃｍ2、プレス時間１０分間であった。This plastic sheet was sandwiched between a first protective film and a second protective film and laminated by heat and pressure. The lamination conditions are a temperature of 160 ° C,
The pressure was 10 kg / cm 2 , and the pressing time was 10 minutes.
【００２０】得られた化粧シートは、部分的に光沢が異
なり、立体感をもつ変化に富んだ意匠を有していた。The obtained decorative sheet had a partially different gloss and had a three-dimensional appearance and a varied design.
【００２１】[0021]
【発明の効果】本発明の方法により、部分によって光沢
が異なり、内部に立体感の生じた意匠を有する化粧シー
トが製造できる。 従って、本発明により製造した化粧
シートを使用して成形品の化粧を行なえば、光沢の変化
に富んだ立体感ある意匠をもった製品を製造できる。
表面に保護フィルムを設ける態様において、パール顔料
を練り込んだ凹凸シートの平坦化と保護フィルムの熱ラ
ミネートを同時に行なえば、間に接着シートを用いる必
要がない。According to the method of the present invention, it is possible to manufacture a decorative sheet having a design in which the gloss varies depending on the part and a three-dimensional effect is generated inside. Therefore, by applying makeup to a molded article using the decorative sheet produced by the present invention, a product having a three-dimensional design with a rich gloss change can be produced.
In the embodiment in which the protective film is provided on the surface, if the unevenness sheet in which the pearl pigment is kneaded is flattened and the protective film is thermally laminated, it is not necessary to use an adhesive sheet between them.
【図１】 本発明の化粧シートの製造方法について基本
的な態様を説明するための、第一の段階を示す模式的な
断面図。FIG. 1 is a schematic cross-sectional view showing a first step for explaining a basic aspect of the method for manufacturing a decorative sheet of the present invention.
【図２】 図１に続く第二の段階を示す同様な図。FIG. 2 is a similar view showing the second stage following FIG.
【図３】 本発明の化粧シ−トの製造方法の、基本的な
態様に付加的な工程を加えた態様によって製造した化粧
シートについて、構成の一例を示す断面図。FIG. 3 is a cross-sectional view showing an example of the structure of a decorative sheet manufactured by the basic mode of the cosmetic sheet manufacturing method according to the present invention with additional steps.
【図４】 本発明の化粧シ−トの製造方法の、基本的な
態様に別の付加的な工程を加えた態様によって製造した
化粧シートについて、構成の一例を示す断面図。FIG. 4 is a cross-sectional view showing an example of the structure of a decorative sheet manufactured by a basic mode of the cosmetic sheet manufacturing method of the present invention with another additional step added.
【図５】 本発明の化粧シ−トの製造方法の、異なる態
様を説明するための、第一の段階を示す摸式的な断面
図。FIG. 5 is a schematic cross-sectional view showing a first step for explaining a different aspect of the method for manufacturing a cosmetic sheet according to the present invention.
【図６】 図５に続く第二の段階を示す同様な図。FIG. 6 is a similar view showing the second stage following FIG. 5.
１Ａ，１Ｂ，１Ｃ パール顔料を練り込んだプラスチッ
クシート ２ パール顔料 ３ 凹凸 ４ 印刷層 ５ 着色ベタ印刷層 ６ 保護フィルム1A, 1B, 1C Plastic sheet in which pearl pigment is kneaded 2 Pearl pigment 3 Unevenness 4 Printing layer 5 Colored solid printing layer 6 Protective film
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 27/20 Ｚ 6122−4Ｆ 33/00 7141−4Ｆ // Ｂ２９Ｌ 31:10 4Ｆ 31:58 4Ｆ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI technical display location B32B 27/20 Z 6122-4F 33/00 7141-4F // B29L 31:10 4F 31:58 4F
Claims (5)
のプラスチックに練り込み、少なくとも一方の面に凹凸
を有するシートに形成し、このシートを加熱プレスして
表面の凹凸をなくした平坦なシートとすることにより、
パール顔料の分散の密度および（または）層面の配向の
方向が部分により異なるシートを得ることからなる、シ
ート内部に立体感を生じさせた化粧シートの製造方法。1. A flat sheet in which a flaky pearl pigment is kneaded into a transparent or translucent plastic to form a sheet having irregularities on at least one surface, and the sheet is hot-pressed to eliminate the irregularities on the surface. By
A method for producing a decorative sheet having a three-dimensional effect inside the sheet, which comprises obtaining a sheet in which the density of dispersion of the pearl pigment and / or the direction of orientation of the layer surface differs depending on the part.
繊維とともにプラスチックに練り込んで実施する、請求
項１の化粧シートの製造方法。2. The method for producing a decorative sheet according to claim 1, wherein the scale-like pearl pigment is kneaded into a plastic together with inorganic or organic fibers.
た平坦なシートの一方または両方の面に、絵柄印刷およ
び（または）ベタ印刷を施す工程を加えた化粧シートの
製造方法。3. A method for producing a decorative sheet, which comprises adding a step of performing pattern printing and / or solid printing to one or both surfaces of a flat sheet produced according to the method of claim 1 or 2.
製造した化粧シートの一方または両方の面に、プラスチ
ックの保護フィルムを熱ラミネートする工程を加えた化
粧シートの製造方法。4. A method for producing a decorative sheet, which comprises a step of thermally laminating a plastic protective film on one or both surfaces of the decorative sheet produced by the method according to claim 1.
のプラスチックに練り込み、少なくとも一方の面に凹凸
を有するシートに形成し、このシートの一方または両方
の面にプラスチックの保護フィルムを重ね、加熱プレス
して上記シートの凹凸をなくすと同時に熱ラミネートを
し、パール顔料の分散の密度および（または）層面の配
向の方向が部分により異なるシートを得ることからな
る、シート内部に立体感を生じさせた化粧シートの製造
方法。5. A scale-like pearl pigment is kneaded into a transparent or translucent plastic to form a sheet having irregularities on at least one side, and a plastic protective film is laminated on one or both sides of the sheet, A heat press is applied to eliminate the unevenness of the sheet and at the same time heat laminate to obtain a sheet in which the density of the dispersion of the pearl pigment and / or the direction of the orientation of the layer surface differs depending on the part. Method for manufacturing a decorative sheet.