JPH05271677A - Silicone grease composition - Google Patents
Silicone grease compositionInfo
- Publication number
- JPH05271677A JPH05271677A JP10356592A JP10356592A JPH05271677A JP H05271677 A JPH05271677 A JP H05271677A JP 10356592 A JP10356592 A JP 10356592A JP 10356592 A JP10356592 A JP 10356592A JP H05271677 A JPH05271677 A JP H05271677A
- Authority
- JP
- Japan
- Prior art keywords
- group
- grease
- sio
- parts
- units
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はシリコーングリース組成
物、特には増稠剤を用いなくても粘着力にすぐれ、潤滑
性の良好なグリースを与えるシリコーングリース組成物
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a silicone grease composition, and more particularly to a silicone grease composition which gives a grease having excellent tackiness and good lubricity without using a thickener.
【０００２】[0002]
【従来の技術】シリコーングリースはシリコーンオイル
と増稠剤とからなるものが基本とされているが、これに
ついてはジオルガノポリシロキサン、Ｒ3 3ＳｉＯ1/2 単
位（以下Ｍ単位と略記する）、Ｒ2 ＳｉＯ単位（以下Ｄ
単位と略記する）およびＳｉＯ2 単位（以下Ｑ単位と略
記する）からなるオルガノポリシロキサン組成物と増稠
剤からなるもの（特公昭53-776号広報参照）、ジオルガ
ノポリシロキサン、Ｍ単位、ＲＳｉＯ3/2 単価（以下Ｔ
単位と略記する）およびＱ単位とからなるオルガノポリ
シロキサン組成物と増稠剤からなるもの（特公昭60-452
40号広報参照）、分岐状オルガノポリシロキサン、Ｍ単
位とＱ単位とからなるオルガノポリシロキサン組成物と
増稠剤からなるもの（特公平3-76359 号広報参照）など
が提案されている。2. Description of the Related Art Silicone grease is basically composed of a silicone oil and a thickening agent. For this, diorganopolysiloxane, R 3 3 SiO 1/2 unit (hereinafter abbreviated as M unit). , R 2 SiO unit (hereinafter D
Unit) and an SiO 2 unit (hereinafter abbreviated as Q unit) and an organopolysiloxane composition and a thickener (see Japanese Patent Publication No. 53-776), diorganopolysiloxane, M unit, RSiO 3/2 unit price (hereinafter T
Abbreviated as "unit") and a Q unit, and a thickener (Japanese Patent Publication No. 60-452).
No. 40), branched organopolysiloxanes, organopolysiloxane compositions composed of M units and Q units and thickeners (see Japanese Patent Publication No. 3-76359).
【０００３】[0003]
【発明が解決しようとする課題】しかし、ＭＤＱ単位、
ＭＴＱ単位、ＭＱ単位からなるオルガノポリシロキサン
組成物はジオルガノポリシロキサンまたは分岐状オルガ
ノポリシロキサンに溶解するため、この組成物をグリー
ス状とするためにはアルミニウム、鉛、亜鉛、マンガ
ン、リチウム、ナトリム、カリウム、カルシウム、バリ
ウム、ストロンチウム、銅、水銀、ビスマス、クロム、
鉄、ニッケルなどの金属を含有する炭素数が少なくとも
８個の脂肪酸の金属石けん、シリカ、アルミナ、酸化
鉄、酸化チタン、酸化亜鉛、ガラス繊維、粘土などの無
機質元素の微粒子不活性酸化物、窒化ほう素、アリ−ル
尿素、フタロシアニン、インダスレン、ポリ四ふっ化エ
チレン粉末、グラファイト、カ−ボンブラックなどの増
稠剤の添加が必須とされる。そのため、これについては
増稠剤を添加しないオルガノポリシロキサンとＭ単位で
表わされるオルガノポリシルセスキオキサンとからなる
ものも提案されているが（特公平2-22797 号広報参
照）、このものは増稠剤が必須成分でないために増稠効
果が弱く、稠度の大きい（軟らかい）グリースしか与え
ないので、稠度の安定したものを得るにはやはり増稠剤
を加える必要がある。However, the MDQ unit,
An organopolysiloxane composition comprising MTQ units and MQ units dissolves in a diorganopolysiloxane or a branched organopolysiloxane, and therefore aluminum, lead, zinc, manganese, lithium, sodium and sodium are required to make the composition a grease. , Potassium, calcium, barium, strontium, copper, mercury, bismuth, chromium,
Metallic soaps of fatty acids containing metals such as iron and nickel and having at least 8 carbon atoms, silica, alumina, iron oxide, titanium oxide, zinc oxide, fine particles of inorganic elements such as glass fiber and clay, nitriding It is essential to add a thickening agent such as boron, aryl urea, phthalocyanine, indusulene, polytetrafluoroethylene powder, graphite or carbon black. For this reason, there has been proposed a composition comprising an organopolysiloxane containing no thickening agent and an organopolysilsesquioxane represented by M units (see Japanese Patent Publication No. 2-22797). Since the thickener is not an essential component, the thickening effect is weak, and it gives only a thick (soft) grease. Therefore, it is necessary to add a thickener to obtain a stable consistency.
【０００４】[0004]
【課題を解決するための手段】本発明はこのような不利
を解決したシリコーングリース組成物に関するものであ
り、これはＡ）一般式SUMMARY OF THE INVENTION The present invention relates to a silicone grease composition which has solved such disadvantages, which is represented by A) the general formula
【化２】 （ここにＲ1 は炭素数４〜18の飽和１価炭化水素基、Ｒ
2 は炭素数１〜12のアルキル基、アルケニル基および非
置換または置換のアリール基から選ばれる１価の炭化水
素基、ａ、ｂは０または１、ｍは０〜500 、ｎは５〜50
0 、ｍ＋ｎは５〜500 の正数）で示され、Ｒ1 が全置換
基中の10〜50モル％であり、25℃での粘度が50〜5,000
cSである長鎖アルキル変性シリコーンオイル100 重量
部、Ｂ）Ｒ3 3ＳｉＯ1/2 単位（Ｒ3 はアルキル基、アル
ケニル基、アリール基から選ばれる基）とＳｉＯ2 単位
とからなり、Ｒ3 3ＳｉＯ1/2 単位とＳｉＯ2 単位とのモ
ル比が0.5 〜0.95であるパウダー状のオルガノポリシロ
キサン20〜300 重量部、とからなることを特徴とするも
のである。[Chemical 2] (Here, R 1 is a saturated monovalent hydrocarbon group having 4 to 18 carbon atoms, R 1
2 is a monovalent hydrocarbon group selected from an alkyl group having 1 to 12 carbon atoms, an alkenyl group and an unsubstituted or substituted aryl group, a and b are 0 or 1, m is 0 to 500, and n is 5 to 50.
0, m + n are positive numbers of 5 to 500), R 1 is 10 to 50 mol% of all the substituents, and the viscosity at 25 ° C. is 50 to 5,000.
100 parts by weight of a long-chain alkyl-modified silicone oil of cS, B) R 3 3 SiO 1/2 unit (R 3 is a group selected from an alkyl group, an alkenyl group, and an aryl group) and a SiO 2 unit, and R 3 3 20 to 300 parts by weight of a powdery organopolysiloxane having a molar ratio of SiO 1/2 unit to SiO 2 unit of 0.5 to 0.95.
【０００５】すなわち、本発明者らは増稠剤を添加しな
くても良好な粘着性グリースとなり得るシリコーングリ
ース組成物を開発すべく種々検討した結果、ここに使用
するオルガノポリシロキサンを前記した一般式（１）で
示される長鎖アルキル変性シリコーンオイルとし、これ
に添加するＭ単位とＱ単位とからなるオルガノポリシロ
キサン組成物をパウダー状のものとしてこれらを混合
し、三本ロールで混練りすると、これが増稠剤を添加し
なくても潤滑性の良好な粘着性グリースとなることを見
出し、これによれば製造時間を大巾に短縮できるし、コ
ストも低減できることを確認して本発明を完成させた。
以下にこれを詳述する。That is, as a result of various investigations by the present inventors to develop a silicone grease composition capable of forming a good tacky grease without adding a thickener, the organopolysiloxane used here is generally described above. When the long-chain alkyl-modified silicone oil represented by the formula (1) is used, and the organopolysiloxane composition comprising M units and Q units to be added thereto is made into a powder form, these are mixed and kneaded with a three-roll mill. However, it was found that this can be an adhesive grease with good lubricity even without adding a thickener, and according to this, it was confirmed that the production time can be greatly shortened and the cost can be reduced, and thus the present invention can be realized. Completed
This will be described in detail below.
【０００６】[0006]
【作用】本発明はシリコーングリース組成物に関するも
のであり、これはＡ）前記した一般式（１）で示される
長鎖アルキル変性シリコーンオイル100 重量部と、Ｂ）
Ｍ単位とＱ単位からなり、Ｍ／Ｑのモル比が 0.5〜0.95
であるパウダー状のオルガノポリシロキサン20〜300 重
量部よりなることを特徴とするものであるが、このもの
は増稠剤を添加しなくても潤滑性のある良好な増稠剤グ
リースを与えるので、シリコーングリース組成物を効率
よく、安価に得ることができるという有利性が与えられ
る。The present invention relates to a silicone grease composition, which comprises A) 100 parts by weight of a long-chain alkyl-modified silicone oil represented by the general formula (1) and B).
Consists of M unit and Q unit, M / Q molar ratio is 0.5 to 0.95
It is characterized by comprising 20 to 300 parts by weight of powdery organopolysiloxane, which gives a good thickener grease with lubricity without adding a thickener. The advantage that the silicone grease composition can be obtained efficiently and inexpensively is provided.
【０００７】本発明のシリコーングリース組成物は前記
したようにＡ）一般式（１）で示される長鎖アルキル変
性シリコーンオイルと、Ｂ）Ｍ単位とＱ単位とからな
り、Ｍ／Ｑのモル比が 0.5〜0.95であるパウダー状のオ
ルガノポリシロキサンとを混合してなるものである。こ
のシリコーングリース組成物を構成するＡ）成分として
の長鎖アルキル変性シリコーンオイルは一般式（１）で
示されるものであり、このＲ1 はブチル基、ヘキシル
基、ヘプチル基、オクチル基、ノニル基、デシル基など
の炭素数が４〜18の、好ましくは６〜14の飽和１価炭化
水素基、Ｒ2 はメチル基、エチル基、プロピル基、ブチ
ル基、オクチル基などのアルキル基、ビニル基、アリル
基などのアルケニル基、フェニル基、トリル基などのア
リール基から選ばれる炭素数１〜12の１価の炭化水素基
で、好ましくはメチル基とされる基、ａ、ｂは０または
１でｍは０〜500 、ｎは５〜500 、ｍ＋ｎは５〜500 の
正数とされるものである。As described above, the silicone grease composition of the present invention comprises A) a long-chain alkyl-modified silicone oil represented by the general formula (1) and B) M units and Q units, and has a molar ratio of M / Q. Is a mixture of powdery organopolysiloxane having a ratio of 0.5 to 0.95. The long-chain alkyl-modified silicone oil as the component A) constituting this silicone grease composition is represented by the general formula (1), and R 1 is a butyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group. A saturated monovalent hydrocarbon group having 4 to 18 carbon atoms, preferably 6 to 14 such as decyl group, R 2 is an alkyl group such as methyl group, ethyl group, propyl group, butyl group, octyl group, or vinyl group , An alkenyl group such as an allyl group, a phenyl group, a monovalent hydrocarbon group having 1 to 12 carbon atoms selected from an aryl group such as a tolyl group, preferably a methyl group, and a and b are 0 or 1 Here, m is 0 to 500, n is 5 to 500, and m + n is a positive number of 5 to 500.
【０００８】この長鎖アルキル変性シリコーンオイルと
しては下記のものThe long chain alkyl modified silicone oil is as follows:
【化３】 [Chemical 3]
【化４】 [Chemical 4]
【化５】 [Chemical 5]
【化６】 が例示されるが、このものは25℃における粘度が50cS未
満では得られるグリースが安定性の悪いものになるし、
5,000 cSよりも粘度の高いものはその製造が非常に困難
であるので、これは25℃における粘度が50〜5,000 cSの
範囲のものとすることが必要とされるが、この好ましい
範囲は、100 〜2,000 cSとされる。[Chemical 6] However, if the viscosity at 25 ° C is less than 50 cS, the resulting grease will have poor stability,
Since those with a viscosity higher than 5,000 cS are very difficult to produce, it is necessary that the viscosity at 25 ° C be in the range of 50 to 5,000 cS, but this preferable range is 100 ~ 2,000 cS
【０００９】また、本発明のシリコーングリース組成物
を構成するＢ）成分はＭ単位とＱ単位とからなるＭＱシ
ロキサンとされるが、このものはＭ／Ｑのモル比が0.5
未満では製造が困難で、パウダ−化が難しくなり、0.95
より大きいものとすると十分な粘着性能を得ることがで
きなくなるので、Ｍ／Ｑのモル比が 0.5〜0.95であるも
のとすることが必要とされる。Further, the component B) which constitutes the silicone grease composition of the present invention is an MQ siloxane comprising M units and Q units, which has an M / Q molar ratio of 0.5.
If it is less than 0.95, it is difficult to manufacture and powdering becomes difficult.
If it is larger than this, sufficient adhesiveness cannot be obtained, so that it is necessary to set the molar ratio of M / Q to 0.5 to 0.95.
【００１０】しかして、このＭＱシロキサン自体は前記
したＡ）成分としての長鎖アルキル変性シリコーンオイ
ルには溶解しないので、この混合物を溶媒ストリップす
ると長鎖アルキル変性シリコーンオイルとＭＱシロキサ
ンの２層に分離してしまい、これをグリース化しても粘
着力や稠度の安定したグリースは得られないのである
が、このＭＱシロキサンはこれをパウダー状にして長鎖
アルキル変性シリコーンオイルに加えて混合後、三本ロ
ールなどで混練りすると増稠剤を添加しなくても潤滑性
のすぐれた粘着力をもつグリースとなることが本発明者
らによって発見されたので、このものはパウダー状で供
給することが必要とされる。However, since the MQ siloxane itself does not dissolve in the long-chain alkyl-modified silicone oil as the component A), when the mixture is solvent stripped, it is separated into two layers of the long-chain alkyl-modified silicone oil and the MQ siloxane. However, even if it is made into grease, it is not possible to obtain a grease with stable adhesive strength and consistency, but this MQ siloxane is powdered and added to a long-chain alkyl-modified silicone oil, and then mixed with three bottles. It was discovered by the present inventors that kneading with a roll or the like provides a grease having excellent lubricity and adhesiveness without adding a thickener, and therefore it is necessary to supply this in powder form. It is said that.
【００１１】したがって、このＭＱシロキサンはＭ単位
シランとＱ単位シランを混合したのち、加水分解、重縮
合し生成した固体をパウダー状のものとすることが必要
とされる。なお、このパウダー状のＭＱシロキサンの配
合量は、Ａ）成分としての長鎖アルキル変性シリコーン
オイル100 重量部に対して、20重量部未満では得られる
グリースが粘着力が弱く、稠度も大きくて軟らかいもの
となってグリースとしての目的を達成することができな
いものとなり、300 重量部より多くすると稠度の小さい
もの（硬い）ものとなって使用目的に合わないものとな
るため、20〜300 重量部の範囲とすることが必要とされ
るが、この好ましい範囲は30〜270 の重量部とされる。Therefore, it is necessary to mix the M unit silane and the Q unit silane, and then hydrolyze and polycondense the MQ siloxane to obtain a powdery solid. If the amount of this powdery MQ siloxane is less than 20 parts by weight with respect to 100 parts by weight of the long-chain alkyl-modified silicone oil as the component A), the grease obtained has a weak adhesive force and a large consistency and is soft. If the amount is more than 300 parts by weight, the product will have a low consistency (hard) and will not meet the intended purpose. A preferred range is 30 to 270 parts by weight, although a range is required.
【００１２】本発明のシリコーングリース組成物は、上
記したＡ）成分としての長鎖アルキル変性シリコーンオ
イルと、Ｂ）成分としてのパウダー状のＭＱシロキサン
との所定量を混合したものであるが、このものはプラネ
タリウムミキサーなどの混合機でよく混合したのち、三
本ロールなどで再び混練りするとグリース状物となる
が、このものは増稠剤を添加しなくても潤滑性、接着性
のすぐれたグリースとすることができるという有利性を
もつものである。The silicone grease composition of the present invention is a mixture of the above-mentioned long-chain alkyl-modified silicone oil as the component A) and a powdered MQ siloxane as the component B) in a predetermined amount. After mixing well with a mixer such as a planetarium mixer and kneading again with a three-roll mill, it becomes a grease-like product, but this product has excellent lubricity and adhesiveness even without adding a thickener. It has the advantage that it can be a grease.
【００１３】また、このシリコーングリース組成物には
これに必要に応じて防錆剤や酸化防止剤などを加えても
よく、この防錆剤としてはベンゾトリアゾールなどが、
酸化防止剤としては4.4'−メチレンビス−2.6 −ジター
シャリーブチルフェノールなどが例示される。なお、こ
のシリコーングリース組成物が作られたシリコーングリ
ースはトルク値が小さく、ランニング後のトルク値ダウ
ン率が小さく、潤滑性もすぐれているので、例えばロー
タリーボリウムの軸、軸受のフィーリングアップ潤滑
剤、ドアーヒンジ部のダンパー潤滑剤として、またオー
トメ化ラインやロボットアームのダンパー用などに使用
することができる。If desired, a rust preventive or an antioxidant may be added to the silicone grease composition. As the rust preventive, benzotriazole or the like may be added.
Antioxidants 4.4 '- methylenebis -2.6 - such as ditertiary-butylphenol and the like. Since the silicone grease made from this silicone grease composition has a small torque value, a small torque value reduction rate after running, and excellent lubricity, for example, a rotary volume shaft, bearing feel-up lubricant It can be used as a damper lubricant for door hinges, as well as for automation lines and robot arm dampers.
【００１４】実施例 ８つぎに本発明の実施例、比較例をあげるが、例中の部
は重量部を、粘度は25℃における測定値を示したもので
あり、例中のグリースの物性は下記による測定値を示し
たものである。 〔物性測定〕 ＪＩＳ-K-2220 に準じて測定した。 〔粘着力〕 ４mmφ×８mmＬの軸、軸受を用い、ク
リアランス35μｍで測定した。 〔潤滑性〕 高速四球試験機を用いて1,500rpm、荷
重40Kg、時間１分、1/2インチ鋼球による摩耗痕直径で
示したが、これは摩耗痕直径の小さい程潤滑性の良いこ
とを示す。Example 8 Next, examples of the present invention and comparative examples will be given. Parts in the examples are parts by weight and viscosity is a measured value at 25 ° C., and the physical properties of the grease in the examples are The measured values are shown below. [Measurement of Physical Properties] Measurement was performed according to JIS-K-2220. [Adhesive strength] The adhesion was measured using a 4 mmφ × 8 mmL shaft and bearing with a clearance of 35 μm. [Lubricity] Using a high-speed four-ball tester, 1,500 rpm, load 40 Kg, time 1 minute, wear mark diameter by 1/2 inch steel ball was shown, but the smaller the wear mark diameter, the better the lubricity Show.
【００１５】実施例１〜４ 長鎖アルキル基がＣ14のテトラデシル基でその含有量が
37.5モル％であり、Examples 1 to 4 The long-chain alkyl group is a C 14 tetradecyl group and its content is
37.5 mol%,
【化７】 で示される粘度が400 cSである長鎖アルキル変性シリコ
ーンオイル100 部に、（ＣＨ3 ）3 ＳｉＯ1/2 単位とＳ
ｉＯ2 単位とのモル比が0.85であるＭＱレジンパウダー
を表１に示した量で添加し、プラネタリウムミキサーで
よく混合したのち、三本ロールで混練りしてシリコーン
グリース組成物を作り、このもののグリース特性をしら
べたところ、表２に併記したとおりの結果が得られた。[Chemical 7] In 100 parts of a long chain alkyl-modified silicone oil having a viscosity of 400 cS, (CH 3 ) 3 SiO 1/2 units and S
MQ resin powder with a molar ratio of 0.85 to iO 2 unit was added in the amount shown in Table 1, mixed well with a planetarium mixer, and then kneaded with a three-roll to prepare a silicone grease composition. When the grease characteristics were examined, the results shown in Table 2 were obtained.
【００１６】実施例５ 長鎖アルキル基がＣ16のヘキサデシル基でその含有量が
25モル％であるExample 5 The long-chain alkyl group is a C 16 hexadecyl group and the content thereof is
25 mol%
【化８】 で示され、粘度が450 cSである長鎖アルキル変性シリコ
ーンオイル100 部に、（ＣＨ3 ）3 ＳｉＯ1/2 単位とＳ
ｉＯ2 単位とのモル比が0.67であるＭＱレジンパウダー
150 部を加え、実施例１と同じように処理してシリコー
ングリース組成物を作り、このもののグリース特性をし
らべたところ、表２に示したとおりの結果が得られた。[Chemical 8] In 100 parts of a long chain alkyl-modified silicone oil having a viscosity of 450 cS, (CH 3 ) 3 SiO 1/2 units and S
MQ resin powder with a molar ratio of 0.67 to iO 2 unit
When 150 parts were added and treated in the same manner as in Example 1 to prepare a silicone grease composition, and the grease characteristics of this composition were examined, the results shown in Table 2 were obtained.
【００１７】実施例６ 長鎖アルキル基がＣ10のデシル基でその含有量が35モル
％であるExample 6 The long-chain alkyl group is a C 10 decyl group and its content is 35 mol%.
【化９】 で示され、粘度が2,000cS である長鎖アルキル変性シリ
コーンオイル100 部に、（ＣＨ2 ＝ＣＨ）（ＣＨ3 ）2
ＳｉＯ1/2 単位とＳｉＯ2 単位とのモル比が0.85である
ＭＱレジンパウダー150 部を加え、実施例１と同じよう
に処理してシリコーングリース組成物を作り、このもの
のグリース特性をしらべたところ、表２に示したとおり
の結果が得られた。[Chemical 9] In 100 parts of a long chain alkyl-modified silicone oil having a viscosity of 2,000 cS, (CH 2 = CH) (CH 3 ) 2
When 150 parts of MQ resin powder having a molar ratio of SiO 1/2 unit to SiO 2 unit of 0.85 was added and treated in the same manner as in Example 1 to prepare a silicone grease composition, the grease characteristics of this product were examined. The results shown in Table 2 were obtained.
【００１８】実施例７ 長鎖アルキル基がＣ8 のオクチル基でその含有量が50モ
ル％であるExample 7 The long-chain alkyl group is a C 8 octyl group and its content is 50 mol%.
【化10】 で示され、粘度が100 cSである長鎖アルキル変性シリコ
ーンオイル100 部に、（ＣＨ3 ）3 ＳｉＯ1/2 単位とＳ
ｉＯ2 単位とのモル比が0.74であるＭＱレジンパウダー
150 部を加え、実施例１と同じように処理してシリコー
ングリース組成物を作り、このもののグリース特性をし
らべたところ、表２に示したとおりの結果が得られた。[Chemical 10] In 100 parts of a long-chain alkyl-modified silicone oil having a viscosity of 100 cS, (CH 3 ) 3 SiO 1/2 units and S
MQ resin powder with a molar ratio of 0.74 to iO 2 unit
When 150 parts were added and treated in the same manner as in Example 1 to prepare a silicone grease composition, and the grease characteristics of this composition were examined, the results shown in Table 2 were obtained.
【００１９】比較例１ 粘度が500 cSのジメチルシリコーンオイル100 部に、
（ＣＨ3 ）3 ＳｉＯ1/2単位とＳｉＯ2 単位とのモル比
が0.85であるＭＱレジンパウダー67部を加え、プラネタ
リウムミキサーでよく混合してから三本ロールで混練り
したところ、ＭＱレジンパウダーがジメチルシリコーン
オイルに溶解してしまってオイル状となってしまったの
で、これに（Ｃ6 Ｈ5 ）2 Ｓｉ（ＯＨ）2 で表面処理し
たシリカ25部を加えて再び三本ロールで混練りしたとこ
ろグリースが得られたので、このもののグリース特性を
しらべたところ、表２に示したとおりの結果が得られ
た。Comparative Example 1 100 parts of dimethyl silicone oil having a viscosity of 500 cS,
When 67 parts of MQ resin powder having a molar ratio of (CH 3 ) 3 SiO 1/2 units to SiO 2 units of 0.85 was added, mixed well with a planetarium mixer and then kneaded with a three-roll mill, MQ resin powder was obtained. Was dissolved in dimethyl silicone oil and turned into an oily form. Add 25 parts of silica surface-treated with (C 6 H 5 ) 2 Si (OH) 2 and knead again with a three-roll mill. Since grease was obtained as a result, the grease characteristics of this product were examined and the results shown in Table 2 were obtained.
【００２０】比較例２ 粘度が3,000 cSでフェニル基含有量が５モル％であるメ
チルフェニルシリコーンオイル100 部に、（ＣＨ3 ）3
ＳｉＯ1/2 単位とＳｉＯ2 単位とのモル比が0.67である
ＭＱレジンパウダー107 部を加え、プラネタリウムミキ
サーでよく混合したのち、三本ロールで混練りしたとこ
ろ、ＭＱレジンパウダーがメチルフェニルシリコーンオ
イルに溶解してしまったので、これに（Ｃ6 Ｈ5 ）2 Ｓ
ｉ（ＯＨ）2 で表面処理したシリカ25部を加えて再び三
本ロールで混練りしたところグリースが得られたので、
このもののグリース特性をしらべたところ、表２に示し
たとおりの結果が得られた。Comparative Example 2 (CH 3 ) 3 was added to 100 parts of methylphenyl silicone oil having a viscosity of 3,000 cS and a phenyl group content of 5 mol%.
After adding 107 parts of MQ resin powder with a molar ratio of SiO 1/2 unit to SiO 2 unit of 0.67, thoroughly mixing with a planetarium mixer and kneading with a three-roll mill, the MQ resin powder was methylphenyl silicone oil. It has dissolved in (C 6 H 5 ) 2 S
When 25 parts of silica surface-treated with i (OH) 2 was added and kneaded again with a three-roll mill, a grease was obtained.
When the grease characteristics of this product were examined, the results shown in Table 2 were obtained.
【００２１】比較例３ 粘度が15,000 cS でフェニル基含有量が５モル％である
メチルフェニルシリコーンオイル100 部に、（ＣＨ3 ）
3 ＳｉＯ1/2 単位とＳｉＯ2 単位とのモル比が0.85であ
るＭＱレジンパウダー91部を加え、プラネタリウムミキ
サーでよく混合したのち三本ロールで混練りしたとこ
ろ、ＭＱレジンパウダーがメチルフェニルシリコーンオ
イルに溶解してしまったので、これに比較例１で用いた
ものと同じシリカを31部を加えて再び三本ロールで混練
りしたところグリースが得られたので、このもののグリ
ース特性をしらべたところ、表２に示したとおりの結果
が得られた。Comparative Example 3 (CH 3 ) was added to 100 parts of methylphenyl silicone oil having a viscosity of 15,000 cS and a phenyl group content of 5 mol%.
3 91 parts of MQ resin powder with a molar ratio of SiO 1/2 unit to SiO 2 unit of 0.85 was added, mixed well with a planetarium mixer, and then kneaded with a three-roll mill. The MQ resin powder was methylphenyl silicone oil. Since 31 parts of the same silica as that used in Comparative Example 1 was added and kneaded again with a three-roll mill, a grease was obtained, and the grease characteristics of this product were examined. The results shown in Table 2 were obtained.
【００２２】[0022]
【表１】 [Table 1]
【表２】 [Table 2]
【００２３】（実験結果の評価）実施例のものはいずれ
も増稠剤を用いなくても充分にグリース状を維持してお
り、これは離油度も小さいことからも証明されている。
また、このものはいずれもトルク値が小さくランニング
後のトルク値のダウン率も小さく安定しており、これは
また摩耗痕も小さく、潤滑性のよいことが確認された。
しかし、比較例のものはいずれも増稠剤を用いないとグ
リース状を維持することができないことが確認された
し、これらのグリースはトルク値が比較的高い値を示し
ているし、ランニング後のダウン率も大きく、さらには
摩耗痕も大きく、潤滑性のわるいものであることを示し
てる。(Evaluation of Experimental Results) In all of the examples, the grease state was maintained sufficiently even without using a thickener, which is also proved from the small oil separation degree.
It was also confirmed that all of these had a small torque value and a small reduction rate of the torque value after running and were stable, and that they also had small wear marks and good lubricity.
However, it was confirmed that none of the comparative examples could maintain a grease state unless a thickener was used.These greases show relatively high torque values, and after running, The rate of down is large and the wear scar is also large, indicating that the lubricity is poor.
【００２４】[0024]
【発明の効果】本発明はシリコーングリース組成物に関
するものであり、これは前記したようにＡ）一般式
（１）で示される長鎖アルキル変性シリコーンオイル10
0 重量部とＢ）Ｒ3 3ＳｉＯ1/2 単位（Ｍ単位）とＳｉＯ
2 単位（Ｑ単位）からなり、Ｍ／Ｑのモル比が 0.5〜0.
95であるパウダー状のオルガノポリシロキサン20〜300
重量部とからなることを特徴とするものであるが、この
長鎖アルキル変性シリコーンオイルとパウダー状のＭＱ
オルガノポリシロキサンとは三本ロールなどで混練りす
ると増稠剤の添加なしで容易に潤滑性、粘着性のよいグ
リースとなるので、これによればシリコーングリース組
成物を短時間で容易に、かつ安価に得ることができると
いう有利性が与えられる。The present invention relates to a silicone grease composition, which is, as mentioned above, A) a long-chain alkyl-modified silicone oil 10 represented by the general formula (1).
0 parts by weight and B) R 3 3 SiO 1/2 unit (M unit) and SiO
It consists of 2 units (Q units) and the molar ratio of M / Q is 0.5-0.
95-powdered organopolysiloxane 20-300
The long-chain alkyl-modified silicone oil and powdered MQ
When kneaded with an organopolysiloxane using a three-roll mill or the like, a grease having good lubricity and tackiness can be easily obtained without addition of a thickener. Therefore, according to this, the silicone grease composition can be easily and quickly obtained. It offers the advantage of being cheap to obtain.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成４年８月１４日[Submission date] August 14, 1992
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００６[Correction target item name] 0006
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【０００６】[0006]
【作用】本発明はシリコ−ングリ−ス組成物に関するも
のであり、これはＡ）前記した一般式（１）で示される
長鎖アルキル変性シリコ−ンオイル１００重量部と、
Ｂ）Ｍ単位とＱ単位からなり、Ｍ／Ｑのモル比が０．５
〜０．９５であるパウダ−状のオルガノポリシロキサン
２０〜３００重量部よりなることを特徴とするものであ
るが、このものは増稠剤を添加しなくても潤滑性のある
良好な粘着性グリ−スを与えるので、シリコ−ングリ−
ス組成物を効率よく、安価に得ることができるという有
利性が与えられる。The present invention relates to a silicone grease composition, which comprises A) 100 parts by weight of a long-chain alkyl-modified silicone oil represented by the general formula (1) above.
B) Consists of M unit and Q unit, and the M / Q molar ratio is 0.5.
It is characterized by comprising 20 to 300 parts by weight of a powdery organopolysiloxane having a content of ˜0.95, which has good tackiness with lubricity without addition of a thickener . Gives grease, so silicone
The advantage of being able to obtain the composition of the invention efficiently and cheaply is given.
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１２[Correction target item name] 0012
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１２】本発明はシリコ−ングリ−ス組成物は、上
記したＡ）成分として長鎖アルキル変性シリコ−ンオイ
ルと、Ｂ）成分としてのパウダ−状のＭＱシロキサンと
の所定量を混合したものであるが、このものはプラネタ
リ−ミキサ−などの混合機でよく混合したのち、三本ロ
−ルなどで再び混練りするとグリ−ス状物となるが、こ
のものは増稠剤を添加しなくても潤滑性、粘着性のすぐ
れたグリ−スとすることができるという有利性をもつも
のである。In the present invention, a silicone grease composition is a mixture of a predetermined amount of a long-chain alkyl-modified silicone oil as the component A) and a powdery MQ siloxane as the component B). some, but this compound planetary - were mixed well by a mixer such as a three roller type - - mixer benefit again kneaded like Le when glyceraldehyde - becomes a scan-like material, without adding thickener this thing lubricity even, viscosity adhesion of excellent grease - those having the advantage of being able to scan.
【手続補正３】[Procedure 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１３[Correction target item name] 0013
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１３】また、このシリコ−ングリ−ス組成物には
これに必要に応じて防錆剤や酸化防止剤などを加えても
よく、この防錆剤としてはベンゾトリアゾ−ルなどが、
酸化防止剤としては４．４' −メチレンビス−２．６−
ジタ−シャリ−ブチルフェノ−ルなどが例示される。な
お、このシリコ−ングリ−ス組成物で作られたシリコ−
ングリ−スは安定したトルク値が得られ、ランニング後
のトルク値ダウン率が小さく、潤滑性もすぐれているの
で、例えばロ−タリ−ボリウムの軸、軸受のフィ−リン
グアップ潤滑剤、ドア−ヒンジ部のダンパ−潤滑剤とし
て、またオ−トメ化ラインやロボットア−ムのダンパ−
用などに使用することができる。If desired, a rust preventive or an antioxidant may be added to the silicone grease composition. Benzotriazole may be used as the rust preventive.
Antioxidants 4.4 '- methylenebis-2,6
Examples include di-tert-butylphenol and the like. Incidentally, the silicone - Nguri - silico made of scan composition -
Nguri - scan is obtained stable torque value, the torque value down rate after the running is small, so that superior to lubricity, for example, Russia - Tali - axis volume, bearing Fi - ring up lubricant door - As a damper for the hinge part, as well as a damper for automatization lines and robot arms
It can be used for applications.
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１４[Correction target item name] 0014
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１４】実施例 つぎに本発明の実施例、比較例をあげるが、例中の部は
重量部を、粘度は２５℃における測定値を示したもので
あり、例中のグリ−スの物性は下記による測定値を示し
たものである。 ［物性測定］ ＪＩＳ−Ｋ−２２２０に準じて測定し
た。 ［粘着力］ ４mmφ×８mmＬの軸、軸受を用い、クリ
アランス３５μm で測定した。 ［潤滑性］ 高速四球試験機を用いて 1，５００rpm、
荷重４０ｋｇ、時間１分、１／２インチ鋼球による摩耗
痕直径で示したが、これは摩耗痕直径の小さい程潤滑性
の良いことを示す。Example Next, examples of the present invention and comparative examples will be given.
Parts by weight, the viscosity is the value measured at 25 ° C.
Yes, the physical properties of grease in the examples show the measured values according to the following.
It is a thing. [Measurement of physical properties] Measured according to JIS-K-2220
It was [Adhesive strength] Using a 4 mmφ x 8 mmL shaft and bearing,
It was measured at Alance 35 μm. [Lubricity] 1,500 rpm using a high-speed four-ball tester,
40kg load, 1 minute time, 1/2 inch steel ball wear
The trace diameter is shown, but the smaller the wear trace diameter, the better the lubricity.
Show the good things.
【手続補正５】[Procedure Amendment 5]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１５[Correction target item name] 0015
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１５】実施例１〜４ 長鎖アルキル基がＣ14のテトラデシル基でその含有量が
３７．５モル％であり、Examples 1 to 4 The long-chain alkyl group is a C 14 tetradecyl group and its content is 37.5 mol%,
【化７】 で示される粘度が４００ｃＳである長鎖アルキル変性シ
リコ−ンオイル１００部に、（ＣＨ3 ）3 ＳｉＯ1/2 単
位とＳｉＯ2 単位とのモル比が０．８５であるＭＱレジ
ンパウダ−を表１に示した量で添加し、プラネタリ−ミ
キサ−でよく混合したのち、三本ロ−ルで混練りしてシ
リコ−ングリ−ス組成物を作り、このもののグリ−ス特
性をしらべたところ、表２に併記したとおりの結果が得
られた。[Chemical 7] Table 1 shows an MQ resin powder in which 100 parts of a long chain alkyl-modified silicone oil having a viscosity of 400 cS and a molar ratio of (CH 3 ) 3 SiO 1/2 units to SiO 2 units of 0.85. was added in the amounts shown, planetary - mixers - After mixing well, the three b - kneaded Le to silico - Nguri - nest composition, glyceryl the ones - was examined scan characteristics, Table 2 The results are as described in the above.
【手続補正６】[Procedure Amendment 6]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１９[Name of item to be corrected] 0019
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００１９】比較例１ 粘度が５００ｃＳのジメチルシリコ−ンオイル１００部
に、（ＣＨ3 ）3 ＳｉＯ1/2 単位とＳｉＯ2 単位とのモ
ル比が０．８５であるＭＱレジンパウダ−６７部を加
え、プラネタリ−ミキサ−でよく混合してから三本ロ−
ルで混練りしたところ、ＭＱレジンパウダ−がジメチル
シリコ−ンオイルに溶解してしまってオイル状となって
しまったので、これに（Ｃ6 Ｈ5 ）2 Ｓｉ（ＯＨ）2 で
表面処理したシリカ２５部を加えて再び三本ロ−ルで混
練りしたところグリ−スが得られたので、このもののグ
リ−ス特性を調べたところ、表２に示したとおりの結果
が得られた。Comparative Example 1 To 100 parts of dimethyl silicone oil having a viscosity of 500 cS was added 67 parts of MQ resin powder having a molar ratio of (CH 3 ) 3 SiO 1/2 units to SiO 2 units of 0.85, planetary - mixer - mixed well three from at Russia -
After kneading, the MQ resin powder was dissolved in dimethylsilicone oil and turned into an oily state. Therefore, the silica resin 25 surface-treated with (C 6 H 5 ) 2 Si (OH) 2 was used. When the mixture was added and kneaded again with three rolls, a grease was obtained. Therefore, when the grease characteristics of this product were examined, the results shown in Table 2 were obtained.
【手続補正７】[Procedure Amendment 7]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２０[Correction target item name] 0020
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２０】粘度が３，０００ｃＳでフェニル基含有量
が５モル％であるメチルフェニルシリコ−ンオイル１０
０部に、（ＣＨ3 ）3 ＳｉＯ1/2 単位とＳｉＯ2 単位と
のモル比が０．６７であるＭＱレジンパウダ−１０７部
を加え、プラネタリ−ミキサ−でよく混合したのち、三
本ロ−ルで混練りしたところ、ＭＱレジンパウダ−がメ
チルフェニルシリコ−ンオイルに溶解してしまったの
で、これに（Ｃ6 Ｈ5 ）2 Ｓｉ（ＯＨ）2 で表面処理し
たシリカ２５部を加えて再び三本ロ−ルで混練りしたと
ころグリ−スが得られたので、このもののグリ−ス特性
を調べたところ、表２に示したとおりの結果が得られ
た。Methyl phenyl silicone oil 10 having a viscosity of 3,000 cS and a phenyl group content of 5 mol%.
0 parts, (CH 3) 3 SiO 1/2 units and molar ratio of SiO 2 units of MQ Rejinpauda -107 parts 0.67 In addition, planetary - mixers - were mixed well, three B - MQ resin powder was dissolved in methylphenylsilicone oil after kneading with a solvent, so 25 parts of silica surface-treated with (C 6 H 5 ) 2 Si (OH) 2 was added to this and the mixture was mixed again. Since a grease was obtained by kneading with this roll, the grease characteristics of this product were examined, and the results shown in Table 2 were obtained.
【手続補正８】[Procedure Amendment 8]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２１[Correction target item name] 0021
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２１】比較例３ 粘度が１，５００ｃＳでフェニル基含有量が５モル％で
あるメチルフェニルシリコ−ンオイル１００部に、（Ｃ
Ｈ3 ）3 ＳｉＯ1/2 単位とＳｉＯ2 単位とのモル比が
０．８５であるＭＱレジンパウダ−９１部を加え、プラ
ネタリ−ミキサ−でよく混合したのち三本ロ−ルで混練
りしたところ、ＭＱレジンパウダ−がメチルフェニルシ
リコ−ンオイルに溶解してしまったので、これに比較例
１で用いたものと同じシリカ３１部を加えて再び三本ロ
−ルで混練りしたところグリ−スが得られたので、この
もののグリ−ス特性を調べたところ、表２に示したとお
りの結果が得られた。Comparative Example 3 100 parts of methylphenylsilicone oil having a viscosity of 1,500 cS and a phenyl group content of 5 mol% (C
H 3) 3 SiO 1/2 units and molar ratio of SiO 2 units of MQ Rejinpauda -91 parts of 0.85 was added, plastics <br/> Netari - Mixer - three After well mixed in Russia - Le After kneading, the MQ resin powder was dissolved in methylphenylsilicone oil, so 31 parts of the same silica as used in Comparative Example 1 was added and kneaded again with three rolls. Since a grease was obtained, the grease characteristics of this product were examined, and the results shown in Table 2 were obtained.
【手続補正９】[Procedure Amendment 9]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２３[Name of item to be corrected] 0023
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【００２３】（実験結果の評価）実施例のものはいずれ
も増稠剤を用いなくても充分にグリ−ス状を維持してお
り、これは離油度が小さいことからも証明されている。
また、このものはいずれも安定したトルク値が得られ、
ランニング後のトルク値のダウン率も小さく安定してお
り、これはまた摩耗痕も小さく、潤滑性のよいことが確
認された。しかし、比較例のものはいずれも増稠剤を用
いないとグリ−ス状を維持することができないことが確
認されたし、これらのグリ−スはトルク値が比較的高い
値を示しているが、ランニング後のダウン率も大きく、
さらには摩耗痕も大きく、潤滑性のわるいものであるこ
とを示している。[0023] (Experimental Evaluation of Results) is sufficiently even without using a thickening agent any grease that of Example - maintains a focal, which has been proven from the fact oil separation is small ..
In addition, a stable torque value is obtained for all of these ,
It was confirmed that the down rate of the torque value after running was small and stable, and this also had small wear marks and good lubricity. However, it was confirmed that none of the comparative examples could maintain the grease state unless a thickening agent was used, and these greases show relatively high torque values. However , the down rate after running is also large,
Furthermore, it shows that the wear marks are large and the lubricity is poor.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 津村 寛 群馬県安中市磯部２丁目13番１号 信越化 学工業株式 磯部工場内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Hiroshi Tsumura 2-13-1, Isobe, Annaka City, Gunma Shin-Etsu Chemical Co., Ltd. Isobe Factory
Claims (2)
2 は炭素数１〜12のアルキル基、アルケニル基および非
置換または置換のアリール基から選ばれる１価の炭化水
素基、ａ、ｂは０または１、ｍは０〜500 、ｎは５〜50
0 、ｍ＋ｎは５〜500 の正数）で示され、Ｒ1 が全置換
基中の10〜50モル％であり、25℃での粘度が50〜5,000
cSである長鎖アルキル変性シリコーンオイル100 重量
部、 Ｂ）Ｒ3 3ＳｉＯ1/2 単位（Ｒ3 はアルキル基、アルケニ
ル基、アリール基から選ばれる基）とＳｉＯ2 とからな
り、Ｒ3 3ＳｉＯ1/2 単位とＳｉＯ2 単位とのモル比が0.
5 〜0.95であるパウダー状のオルガノポリシロキサン20
〜300 重量部、とからなることを特徴とするシリコーン
グリース組成物。1. A) General formula: (Here, R 1 is a saturated monovalent hydrocarbon group having 4 to 18 carbon atoms, R 1
2 is a monovalent hydrocarbon group selected from an alkyl group having 1 to 12 carbon atoms, an alkenyl group and an unsubstituted or substituted aryl group, a and b are 0 or 1, m is 0 to 500, and n is 5 to 50.
0, m + n are positive numbers of 5 to 500), R 1 is 10 to 50 mol% of all the substituents, and the viscosity at 25 ° C. is 50 to 5,000.
100 parts by weight of a long-chain alkyl-modified silicone oil having cS, B) R 3 3 SiO 1/2 unit (R 3 is a group selected from an alkyl group, an alkenyl group, and an aryl group) and SiO 2, and R 3 3 The molar ratio of SiO 1/2 units to SiO 2 units is 0.
Powdered organopolysiloxane 20 with 5 to 0.95
~ 300 parts by weight, and a silicone grease composition.
シリコーングリース組成物。2. The silicone grease composition according to claim 1, wherein R 2 is a methyl group.