JPH05265365A - Production of diffraction grating sheet - Google Patents
Production of diffraction grating sheetInfo
- Publication number
- JPH05265365A JPH05265365A JP4065057A JP6505792A JPH05265365A JP H05265365 A JPH05265365 A JP H05265365A JP 4065057 A JP4065057 A JP 4065057A JP 6505792 A JP6505792 A JP 6505792A JP H05265365 A JPH05265365 A JP H05265365A
- Authority
- JP
- Japan
- Prior art keywords
- diffraction grating
- resin
- sheet
- ethylene
- extrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、回折格子シートの製造
方法に関する。さらに詳しくは、本発明は、押出成形機
から押し出された溶融状態の樹脂に、ホログラムスタン
パ等の回折格子スタンパを装着したロールを押しつけて
樹脂表面に回折格子をエンボスして得られる回折格子シ
ートの製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a diffraction grating sheet. More specifically, the present invention relates to a resin in a molten state extruded from an extrusion molding machine, a roll equipped with a diffraction grating stamper such as a hologram stamper is pressed, and a diffraction grating sheet obtained by embossing a diffraction grating on the resin surface is provided. The present invention relates to a manufacturing method.
【０００２】[0002]
【従来の技術】ホログラムスタンパ等の回折格子スタン
パは薄い金属製のものであり、その製造工程の一例を以
下に説明する。2. Description of the Related Art A diffraction grating stamper such as a hologram stamper is made of a thin metal, and an example of its manufacturing process will be described below.
【０００３】まず、レーザー光による二光束干渉など既
知の方法により、感光性樹脂上に干渉縞を凹凸形状で記
録する。次いで、前記凹凸表面にAu、Ag、Ni等を蒸着
し、これを電極としてNiメッキを行なって、厚さ数百μ
ｍ程度のNiメッキ層を形成した後、剥離することにより
原版を得る。次いで、前記原版の表面に剥離処理を施
し、この原版を基にして、複数回Niメッキの形成・剥離
を繰り返すことによって、スタンパが得られる。First, interference fringes are recorded in an uneven shape on a photosensitive resin by a known method such as two-beam interference with laser light. Then, Au, Ag, Ni, etc. are vapor-deposited on the uneven surface, and Ni plating is performed by using this as an electrode, and the thickness is several hundred μ.
After forming a Ni plating layer of about m, the original plate is obtained by peeling. Next, the stamper is obtained by subjecting the surface of the original plate to a peeling treatment and repeating the formation and peeling of the Ni plating a plurality of times based on this original plate.
【０００４】このスタンパを樹脂の押出成形機の冷却ロ
ールに装着し、押し出された溶融状態の樹脂に押しつけ
て回折格子シートを製造する方法は公知である（特開昭
６２−１９１８７２号公報、特開昭６２−１９２７７９
号公報）。この方法によれば、極めて高速度で能率良く
回折格子シートを製造することが可能である。A method for manufacturing a diffraction grating sheet by mounting this stamper on a cooling roll of a resin extrusion molding machine and pressing it against the extruded molten resin is known (Japanese Patent Laid-Open No. 191872/1987). Kaisho 62-192779
Publication). According to this method, it is possible to manufacture a diffraction grating sheet efficiently at an extremely high speed.
【０００５】得られた回折格子シートは、その回折格子
形成面に金属蒸着膜や高屈折率透明材料の蒸着膜等の光
反射層を設けて、より明るい回折格子シートとすること
ができる。The obtained diffraction grating sheet can be made a brighter diffraction grating sheet by providing a light reflecting layer such as a metal vapor deposition film or a vapor deposition film of a high refractive index transparent material on the diffraction grating forming surface.
【０００６】しかしながら、この押出成形技術を利用し
た回折格子シートの製造方法に用いる樹脂の特性とし
て、回折格子スタンパの、約７００〜１５００本／mm、
深さ約０．１〜１．０μｍ程度の微細な凹凸パターンを
再現性良くエンボス加工するエンボス加工性が悪いと、
樹脂表面に形成されたレリーフ型回折格子の回折光が暗
くなってしまい、回折格子特有の虹色に光る装飾効果
や、ホログラムにあっては３次元情報を記録したことに
よるその立体感を損ね、見栄えの悪いものとなってしま
うという問題があった。However, as a characteristic of the resin used in the method of manufacturing a diffraction grating sheet using this extrusion molding technique, the diffraction grating stamper has a characteristic of about 700 to 1500 pieces / mm.
Embossing a fine concavo-convex pattern with a depth of about 0.1 to 1.0 μm with good reproducibility.
The diffracted light of the relief type diffraction grating formed on the resin surface becomes dark, and the rainbow-colored decorative effect peculiar to the diffraction grating and the three-dimensional effect due to the recording of three-dimensional information in the hologram are impaired. There was a problem that it looked bad.
【０００７】また、エンボス後、その表面に光反射層と
して金属蒸着膜を設ける場合、樹脂と金属との接着が弱
かったり、またこの接着を向上させるためのプライマー
コーティング、化学薬品処理等の湿式処理は、回折格子
の微細な凹凸を消失させるため行うことができず、さら
に樹脂表面にコロナ放電処理、グロー放電処理、オゾン
処理、プラズマ処理等の乾式の表面処理を行う方法で
は、接着性の経時劣化や、蒸着後に印刷等の後工程を行
った場合に接着性が劣化する恐れがあるという問題があ
った。When a metal vapor deposition film is provided on the surface after embossing as a light reflecting layer, the adhesion between the resin and the metal is weak, and the primer coating for improving this adhesion, wet treatment such as chemical treatment, etc. Cannot be performed because the fine irregularities of the diffraction grating disappear, and the resin surface is subjected to dry surface treatment such as corona discharge treatment, glow discharge treatment, ozone treatment, and plasma treatment. There is a problem that there is a possibility that the adhesiveness may be deteriorated when deterioration or a post-process such as printing is performed after vapor deposition.
【０００８】あるいは、回折格子を成形した樹脂シート
の表面に光沢がないと、蒸着による金属光沢が低く、見
方によっては白化したように見え、前述のような装飾効
果等を損なうといった問題があった。Alternatively, if the surface of the resin sheet on which the diffraction grating is molded is not glossy, the metallic luster due to vapor deposition is low, and it looks like whitening depending on the viewpoint, and there is a problem that the above-mentioned decorative effect is impaired. ..
【０００９】さらに、回折格子シートに用いた樹脂の透
明性が低い場合、形成された回折格子が見えにくく、特
に回折格子シートが回折格子形成面とは反対側の面から
回折格子を見るような構成の場合に問題となった。Further, when the resin used for the diffraction grating sheet is low in transparency, the formed diffraction grating is hard to see, and in particular, the diffraction grating sheet sees the diffraction grating from the surface opposite to the diffraction grating forming surface. It was a problem with the configuration.
【００１０】[0010]
【発明が解決しようとする課題】そこで、本発明は、溶
融押出成形された樹脂に回折格子を押しつけて、レリー
フ型回折格子をエンボスする回折格子の製造方法におい
て、生産効率が格段に優れ、安価で、経済的であるだけ
でなく、極めて回折格子の装飾効果が高く、ホログラム
にあってはその立体感を損なうことがなく、また、金属
蒸着適性や押出加工適性等に優れた回折格子シートの製
造方法を提供することを目的とする。Therefore, the present invention is a method for manufacturing a diffraction grating in which a relief type diffraction grating is embossed by pressing a diffraction grating against a resin that has been melt-extruded, and the production efficiency is remarkably excellent and the cost is low. Therefore, not only is it economical, but the decoration effect of the diffraction grating is extremely high, and the hologram does not impair the three-dimensional effect, and it is also suitable for metal deposition suitability and extrusion suitability. It is intended to provide a manufacturing method.
【００１１】[0011]
【課題を解決するための手段】この目的を達成するため
に、本発明は、押出成形機からシート状に押し出された
溶融状態の樹脂、または押出成形機から基材シート上に
押し出された樹脂に回折格子スタンパを押しつけて、シ
ート成形または積層シート成形を行うと共に樹脂表面に
レリーフ型回折格子をエンボスし、次いでエンボス表面
に光反射層を設けて成る回折格子シートの製造方法にお
いて、この樹脂として、エンボス加工適性、金属接着
性、透明性、表面光沢等に優れたエチレンーメタクリル
酸共重合樹脂を用いたことを特徴とする回折格子シート
の製造方法を提供する。In order to achieve this object, the present invention provides a resin in a molten state extruded in a sheet form from an extruder or a resin extruded on a base material sheet from an extruder. In the method for manufacturing a diffraction grating sheet, which comprises pressing a diffraction grating stamper onto a sheet to form a sheet or a laminated sheet, embossing a relief type diffraction grating on the resin surface, and then providing a light reflection layer on the embossed surface Provided is a method for producing a diffraction grating sheet, which comprises using an ethylene-methacrylic acid copolymer resin excellent in embossing suitability, metal adhesion, transparency, surface gloss, and the like.
【００１２】以下、本発明の詳細を図面を参照して説明
する。図１は本発明にかかる回折格子シートの製造方法
を説明するための説明図である。本発明にかかる回折格
子シート１０は、押出成形機１から押し出されたエチレ
ン−メタクリル酸共重合樹脂１１ａに回折格子スタンパ
を押圧することにより容易に形成することができる。The details of the present invention will be described below with reference to the drawings. FIG. 1 is an explanatory diagram for explaining a method of manufacturing a diffraction grating sheet according to the present invention. The diffraction grating sheet 10 according to the present invention can be easily formed by pressing the diffraction grating stamper against the ethylene-methacrylic acid copolymer resin 11a extruded from the extrusion molding machine 1.
【００１３】すなわち、図１において、１は押出成形機
本体、２はＴ−ダイ、３は冷却ロール、４はニップロー
ル、５は冷却ロール３の表面に装着された回折格子スタ
ンパ、１１ａは押し出された溶融状態のエチレン−メタ
クリル酸共重合樹脂、６は引き取りロール、７は巻き取
りロールをそれぞれ示す。That is, in FIG. 1, 1 is an extruder main body, 2 is a T-die, 3 is a cooling roll, 4 is a nip roll, 5 is a diffraction grating stamper mounted on the surface of the cooling roll 3, and 11a is extruded. The molten ethylene-methacrylic acid copolymer resin, 6 is a take-up roll, and 7 is a take-up roll.
【００１４】押出成形機１のＴ−ダイ２からシート状に
押し出されたエチレン−メタクリル酸共重合樹脂１１ａ
を冷却ロール３とニップロール４の間で、シート成形す
ると同時に、冷却ロール３に装着された回折格子スタン
パ５を押圧して、エチレンーメタクリル酸共重合樹脂１
１ａの表面に回折格子をエンボスする。得られた回折格
子シート１０は、引き取りロール６を介して巻き取りロ
ール７に巻き取られる。An ethylene-methacrylic acid copolymer resin 11a extruded in a sheet form from the T-die 2 of the extruder 1.
A sheet is molded between the cooling roll 3 and the nip roll 4 and at the same time, the diffraction grating stamper 5 mounted on the cooling roll 3 is pressed to remove the ethylene-methacrylic acid copolymer resin 1
Emboss a diffraction grating on the surface of 1a. The obtained diffraction grating sheet 10 is taken up by the take-up roll 7 via the take-up roll 6.
【００１５】この結果、図２に示すような、表面にレリ
ーフ型回折格子を形成した樹脂シート１１を連続的に得
ることができる。図３は、更にこの回折格子形成面に、
光反射層１２を設けることにより、本発明に述べる回折
格子シート１０の構成を示す説明図である。As a result, the resin sheet 11 having the relief type diffraction grating formed on the surface thereof as shown in FIG. 2 can be continuously obtained. FIG. 3 further shows that the surface on which the diffraction grating is formed,
It is explanatory drawing which shows the structure of the diffraction grating sheet 10 described in this invention by providing the light reflection layer 12. FIG.
【００１６】本発明では次のようなことも可能である。
すなわち、図４に示すように、基材シート１３上に押出
成形機１のＴ−ダイ２から押し出されたエチレン−メタ
クリル酸共重合樹脂１１ａを、表面に回折格子スタンパ
５を装着した冷却ロール３とニップロール４の間で押出
コーティングすることにより、表面に回折格子を形成し
た積層シートを連続的に得ることができる。以下、同様
に回折格子形成面に光反射層１２を設けることにより、
図５に示すような回折格子形成シート２０を得ることが
できる。The present invention can also do the following.
That is, as shown in FIG. 4, the ethylene-methacrylic acid copolymer resin 11a extruded from the T-die 2 of the extruder 1 on the base material sheet 13 and the cooling roll 3 having the diffraction grating stamper 5 mounted on the surface thereof. By performing extrusion coating between the nip roll 4 and the nip roll 4, a laminated sheet having a diffraction grating formed on the surface can be continuously obtained. Hereinafter, similarly, by providing the light reflection layer 12 on the diffraction grating formation surface,
The diffraction grating forming sheet 20 as shown in FIG. 5 can be obtained.
【００１７】以上のように、本発明は樹脂シートの製造
方法を利用して、極めて効率的に、安価で、経済的であ
るだけでなく、樹脂としてエンボス加工性、金属接着
性、透明性、表面光沢等に優れたエチレン−メタクリル
酸共重合樹脂を用いることで、回折格子スタンパからの
エンボス再現性も良好で、極めて外観上優れた回折格子
シートの製造方法を提供するものであり、実用性の高い
ものである。As described above, the present invention utilizes the method for producing a resin sheet, and is not only extremely efficient, inexpensive and economical, but also embossable as a resin, metal adhesion, transparency, By using an ethylene-methacrylic acid copolymer resin having excellent surface gloss and the like, emboss reproducibility from a diffraction grating stamper is also good, and it provides a method of manufacturing a diffraction grating sheet having an extremely excellent appearance, which is practical. It is expensive.
【００１８】本発明に利用できる押出成形機１、Ｔ−ダ
イ２は特に制限はなく、エチレンーメタクリル酸共重合
樹脂は通常の樹脂シート成形用押出機にて押し出し加工
可能である。The extrusion molding machine 1 and the T-die 2 which can be used in the present invention are not particularly limited, and the ethylene-methacrylic acid copolymer resin can be extruded by a usual resin sheet molding extruder.
【００１９】本発明に述べる冷却ロール３に回折格子ス
タンパ５を装着させる方法としては、耐熱性の接着剤で
固定する方法、物理的にビス止めで固定する方法、磁石
を利用し固定する方法、真空吸着による固定する方法
等、いずれの方法でも可能である。As a method of mounting the diffraction grating stamper 5 on the cooling roll 3 described in the present invention, a method of fixing with a heat-resistant adhesive, a method of physically fixing with a screw, a method of fixing with a magnet, Any method such as a method of fixing by vacuum adsorption is possible.
【００２０】なお、スタンパ５は凹凸により回折格子を
形成した周知のスタンパで良く、ニッケル等の金属板か
ら成るスタンパが例示できる。また、回折格子は、ホロ
グラムであっても良い。The stamper 5 may be a known stamper having a diffraction grating formed by unevenness, and a stamper made of a metal plate such as nickel can be exemplified. Further, the diffraction grating may be a hologram.
【００２１】また、冷却ロール３は、回折格子をエンボ
スしたエチレン−メタクリル酸共重合樹脂１１ａを速や
かに冷却して、エンボスの消失と歪みを防ぐ機能を有す
る必要がある。例えば、冷却水を内部に循環する流路を
有する金属性のロールが使用できる。Further, the cooling roll 3 needs to have a function of rapidly cooling the ethylene-methacrylic acid copolymer resin 11a having the embossed diffraction grating to prevent disappearance and distortion of the emboss. For example, a metallic roll having a flow path for circulating cooling water therein can be used.
【００２２】ニップロール４は、溶融状態のエチレン−
メタクリル酸樹脂１１ａに十分な圧力で押圧するため
に、表面がウレタンまたはシリコン等の弾性体から成る
ロールが望ましい。The nip roll 4 is made of ethylene in a molten state.
In order to press the methacrylic acid resin 11a with a sufficient pressure, a roll whose surface is made of an elastic material such as urethane or silicon is desirable.
【００２３】押出成形機より押し出され、深さ１μｍ以
下、７００〜１５００本／ｍｍの凹凸で構成されている
レリーフ型回折格子を表面にエンボス成形するエチレン
−メタクリル酸共重合樹脂１１ａとしては、押し出しコ
ーティング用のものであれば使用可能であるが、特に、
エンボス加工適性、押し出し加工適性の点でＭＦＲの高
いもの（ＭＦＲ５〜１２ｇ／１０ｍｉｎ）が望ましく、
また金属接着性の点でメタクリル酸含有量が多いこと
（メタクリル酸含有量９〜１２重量％）が望ましい。The ethylene-methacrylic acid copolymer resin 11a is extruded from an extrusion molding machine and is embossed on the surface with a relief-type diffraction grating having a depth of 1 μm or less and unevenness of 700 to 1500 lines / mm. It can be used if it is for coating, but especially
In terms of suitability for embossing and extrusion, those with high MFR (MFR5-12g / 10min) are desirable,
Further, it is desirable that the content of methacrylic acid is large (methacrylic acid content 9 to 12% by weight) from the viewpoint of metal adhesion.
【００２４】更に、押し出し加工によって連続的に安定
した品質の高い回折格子シートを得るために、エチレン
−メタクリル酸共重合樹脂１１ａには添加剤を含有しな
いものが好ましい。添加剤が含まれていると、高温加工
により添加剤が蒸発し冷却ロール３に装着したスタンパ
５に付着して、成形された回折格子シート１０の透明
性、表面光沢や、後工程である光反射層１２を設ける際
の接着性を劣化させる原因になるためである。Further, in order to obtain a continuously stable and high quality diffraction grating sheet by extrusion processing, it is preferable that the ethylene-methacrylic acid copolymer resin 11a contains no additive. When the additive is included, the additive evaporates due to high temperature processing and adheres to the stamper 5 mounted on the cooling roll 3 to cause transparency and surface gloss of the molded diffraction grating sheet 10 and light as a post-process. This is because it becomes a cause of deteriorating the adhesiveness when the reflective layer 12 is provided.
【００２５】また、本発明に用いる樹脂として、エチレ
ン−メタクリル酸共重合体の分子間を金属イオンで架橋
した樹脂、すなわち、アイオノマー樹脂も使用可能であ
り、エチレンーメタクリル酸共重合樹脂と同等の性能を
示す。この押し出されたエチレン−メタクリル酸共重合
樹脂層１１ａの厚みは、透明性の点で１〜２００μｍが
最も好ましい。Further, as the resin used in the present invention, a resin obtained by crosslinking the ethylene-methacrylic acid copolymer between the molecules with a metal ion, that is, an ionomer resin can also be used, which is equivalent to the ethylene-methacrylic acid copolymer resin. Show performance. The thickness of the extruded ethylene-methacrylic acid copolymer resin layer 11a is most preferably 1 to 200 μm in terms of transparency.
【００２６】光反射層１２としては、金属蒸着膜や透明
材料による蒸着膜から構成することができる。この光反
射層１２は、エチレン−メタクリル酸共重合樹脂１１ａ
の表面に形成された回折格子を、より明るいものとする
ために形成するものである。エチレン−メタクリル酸共
重合樹脂１１ａの特徴である金属接着性を活かすことを
考慮すれば、光反射層１２として金属蒸着膜を用いるこ
とが望ましい。この金属としては、表面反射率の高いも
のが望ましく、例えば、アルミニウム、金、銀、銅、錫
等およびこれらの金属を含む合金が使用できる。透明材
料としては、屈折率の高いものが望ましく、例えば、酸
化珪素、酸化チタン等が使用できる。この光反射層１２
を設ける方法としては、真空蒸着法、スパッタリング
法、イオンプレーティング法等の方法により設けること
ができる。厚みは、１００〜１００００Åの範囲が適当
である。The light reflection layer 12 can be composed of a metal vapor deposition film or a vapor deposition film of a transparent material. The light reflecting layer 12 is made of an ethylene-methacrylic acid copolymer resin 11a.
The diffraction grating formed on the surface of is formed in order to make it brighter. Considering that the metal adhesiveness, which is a characteristic of the ethylene-methacrylic acid copolymer resin 11a, is utilized, it is desirable to use a metal vapor deposition film as the light reflecting layer 12. As this metal, one having a high surface reflectance is desirable, and for example, aluminum, gold, silver, copper, tin and the like and alloys containing these metals can be used. As the transparent material, one having a high refractive index is desirable, and for example, silicon oxide, titanium oxide or the like can be used. This light reflection layer 12
As a method of providing the film, a method such as a vacuum vapor deposition method, a sputtering method, an ion plating method or the like can be provided. A suitable thickness is in the range of 100 to 10000Å.
【００２７】また、光反射層１２は、回折格子形成面に
密着して形成する必要があり、樹脂層１１と光反射層１
２との間に他の物質が介在してはならない。本発明で
は、樹脂としてエチレン−メタクリル酸共重合樹脂１１
を用いているため、光反射層１２が樹脂１１に強く密着
して形成される結果、この光反射層１２は樹脂表面のエ
ンボスにしたがって凹凸に形成され、それ自体で反射型
回折格子を構成する。Further, the light reflection layer 12 needs to be formed in close contact with the diffraction grating formation surface, and the resin layer 11 and the light reflection layer 1 are formed.
No other substance should intervene between the two. In the present invention, ethylene-methacrylic acid copolymer resin 11 is used as the resin.
As a result, the light reflection layer 12 is strongly adhered to the resin 11, and as a result, the light reflection layer 12 is unevenly formed according to the embossing of the resin surface, and the light reflection layer 12 itself constitutes the reflection type diffraction grating. ..
【００２８】図４に示した方法により、回折格子シート
１０を製造する場合に必要となる基材シート１３として
は、樹脂シート、紙、金属箔、もしくはこれらの積層材
料が使用できる。また、基材シート１３は押出成形機か
ら押出成形されたエチレン−メタクリル酸共重合樹脂１
１ａと積層するため、長尺のシートであることが望まし
い。A resin sheet, paper, a metal foil, or a laminated material of these can be used as the base sheet 13 required when the diffraction grating sheet 10 is manufactured by the method shown in FIG. The substrate sheet 13 is an ethylene-methacrylic acid copolymer resin 1 extruded from an extrusion molding machine.
Since it is laminated with 1a, a long sheet is preferable.
【００２９】基材シート１３として、金属箔、またはこ
れを用いた積層材料等を用いた場合、基材シート１３自
体が光反射層としての働きを成す光反射性基材シート１
３ａとすることが可能である。すなわち、金属箔に表面
反射率の高い金属を用い、さらに金属箔側に押出成形機
１から押し出されたエチレン−メタクリル酸共重合樹脂
１１ａを押出コーティングすることにより、シート成形
と回折格子形成、さらに光反射層積層を同時に行うこと
ができる。これにより、回折格子形成面に光反射層１２
を新たに積層する必要がなくなり、一工程削減により効
率的かつ経済的に回折格子シート３０の生産が可能とな
る。また、エチレン−メタクリル酸共重合樹脂１１は金
属接着性が良いので、光反射性基材シート１３ａとの接
着性を向上させるためのアンカーコート剤を塗布する必
要がない。図７は、このようにして成形された回折格子
シート３０の断面図である。When a metal foil or a laminated material using the same is used as the base sheet 13, the base sheet 13 itself functions as a light reflecting layer.
3a is possible. That is, a metal having a high surface reflectance is used for the metal foil, and the ethylene-methacrylic acid copolymer resin 11a extruded from the extrusion molding machine 1 is extrusion-coated on the metal foil side to form a sheet and a diffraction grating. Light reflection layer lamination can be performed simultaneously. As a result, the light reflection layer 12 is formed on the diffraction grating formation surface.
Since it is not necessary to newly laminate the above, it is possible to efficiently and economically produce the diffraction grating sheet 30 by reducing one step. Further, since the ethylene-methacrylic acid copolymer resin 11 has good metal adhesiveness, it is not necessary to apply an anchor coating agent for improving the adhesiveness with the light-reflecting base material sheet 13a. FIG. 7 is a cross-sectional view of the diffraction grating sheet 30 thus formed.
【００３０】基材シート１３として用いる樹脂シートと
しては、ポリエチレン樹脂、ポリプロピレン樹脂、ポリ
アミド樹脂、ポリ塩化ビニル樹脂、ポリエステル樹脂、
ポリカーボネート樹脂、ポリメタクリル酸メチル樹脂、
ポリスチレン樹脂、セロファン等のシートが使用でき、
樹脂シート側から回折格子を見る構成（図６）と成った
場合でも対応可能であるように透明なものであることが
望ましい。The resin sheet used as the base sheet 13 includes polyethylene resin, polypropylene resin, polyamide resin, polyvinyl chloride resin, polyester resin,
Polycarbonate resin, polymethylmethacrylate resin,
Sheets of polystyrene resin, cellophane, etc. can be used,
It is preferable that the resin sheet is transparent so that the diffraction grating can be viewed from the resin sheet side (FIG. 6).
【００３１】基材シート１３として用いる紙質基材とし
ては、用途に応じて幅広い範囲での選択が可能である
が、基材の平滑性が悪い場合、回折格子のエンボス成形
性に影響を与える可能性があるため、コート紙、アート
紙、キャストコート紙等平滑性の良い紙の使用が望まし
い。The paper base material used as the base sheet 13 can be selected in a wide range according to the application, but if the base material has poor smoothness, it may affect the embossing formability of the diffraction grating. Therefore, it is desirable to use coated paper, art paper, cast coated paper or the like with good smoothness.
【００３２】基材シート１３として用いる金属箔として
は、任意であるが、光反射性基材シート１３ａとして用
いることを考慮すると、アルミニウム箔、金箔、銀箔、
銅箔等の表面反射率の高い金属箔が望ましい。The metal foil used as the base sheet 13 is optional, but considering that it is used as the light-reflecting base sheet 13a, aluminum foil, gold foil, silver foil,
A metal foil having a high surface reflectance such as copper foil is desirable.
【００３３】また、基材シート１３として用いる積層基
材としては、上記金属箔と樹脂シートの積層材料、紙と
樹脂シートの積層材料や金属箔と紙との積層材料のいず
れもが使用でき、また、金属箔の代わりに上記金属箔と
同じ材質の金属薄膜を設けた樹脂シートあるいは紙質基
材を使用しても良い。As the laminated base material used as the base material sheet 13, any of the above-mentioned laminated material of metal foil and resin sheet, laminated material of paper and resin sheet and laminated material of metal foil and paper can be used. Further, instead of the metal foil, a resin sheet or a paper base material provided with a metal thin film made of the same material as the metal foil may be used.
【００３４】金属薄膜を設ける場合は、真空蒸着、スパ
ッタリング、イオンプレーティング等の方法によれば良
い。薄膜形成に先だって、樹脂シートあるいは紙質基材
にアンカーコート剤を塗布しても良い。薄膜は、１００
〜１００００Åの厚さが適当である。When the metal thin film is provided, a method such as vacuum vapor deposition, sputtering or ion plating may be used. Prior to forming the thin film, the anchor coating agent may be applied to the resin sheet or the paper base material. Thin film is 100
A thickness of ~ 10000Å is suitable.
【００３５】なお、基材シート１３は、任意の厚さでよ
いが、汎用性および樹脂シートの場合は透明性の点で、
通常１０〜２００μｍがもっとも適当である。また、必
要に応じて、光反射性基材シート１３ａを除く他の基材
シート１３にエチレン−メタクリル酸共重合樹脂１１を
積層するに先立って、基材シート１３の積層面側にアン
カーコート処理、コロナ放電処理等の表面活性化処理
や、または基材シート１３の積層面側に予め、エチレン
−メタクリル酸共重合樹脂１１と接着性の良いポリエチ
レンフィルムを押し出しコーティング、ドライラミネー
ション等の方法により施しても良い。The base sheet 13 may be of any thickness, but in the case of versatility and a resin sheet, it is transparent.
Usually, 10 to 200 μm is the most suitable. In addition, if necessary, prior to laminating the ethylene-methacrylic acid copolymer resin 11 on the other base sheet 13 excluding the light-reflecting base sheet 13a, an anchor coat treatment is performed on the laminated surface side of the base sheet 13. , A surface activation treatment such as corona discharge treatment, or a polyethylene film having good adhesiveness with the ethylene-methacrylic acid copolymer resin 11 is extruded on the laminated surface side of the base material sheet 13 in advance by a method such as extrusion coating or dry lamination. May be.
【００３６】以下、本発明をさらにわかり易くするため
に実施例をもって説明する。Hereinafter, the present invention will be described with reference to examples in order to make it easier to understand.
【００３７】[0037]
＜実施例１＞図１に示した装置を用い、下記のエチレン
−メタクリル酸共重合体樹脂を、下記の加工条件にて押
し出しコーティングを行うと共に回折格子をエンボス
し、図２に示すようなシートを連続して得た。次いで、
この回折格子形成面にアルミニウム蒸着層を設け、光反
射層を得、図３に示すような回折格子シートを得た。<Example 1> Using the apparatus shown in FIG. 1, the following ethylene-methacrylic acid copolymer resin was extrusion coated under the following processing conditions and the diffraction grating was embossed, and a sheet as shown in FIG. Was continuously obtained. Then
An aluminum vapor deposition layer was provided on this diffraction grating formation surface to obtain a light reflection layer, and a diffraction grating sheet as shown in FIG. 3 was obtained.
【００３８】 （Ａ）エチレン−メタクリル酸共重合体樹脂 三井・デュポンポリケミカル株式会社製ニュクレルＮ−
０９０８Ｃ （メタクリル酸含有量 ９ｗｔ％、ＭＦＲ ８ｇ／１０
ｍｉｎ）(A) Ethylene-methacrylic acid copolymer resin Nucrel N- manufactured by Mitsui DuPont Polychemical Co., Ltd.
0908C (methacrylic acid content 9 wt%, MFR 8 g / 10
min)
【００３９】（Ｂ）押出加工条件 （ａ）装置・・図１の装置。 （ｂ）押出機・・φ＝６０ｍｍ、Ｌ／Ｄ＝２６ （ｃ）ニップロール・・シリコンゴムロール（ゴム硬度
８０度） （ｄ）押出機の温度設定 （イ）シリンダー１温度・・１８０℃ （ロ）シリンダー２温度・・２４０℃ （ハ）シリンダー３温度・・３００℃ （ニ）アダプター 温度・・３０５℃ （ホ）Ｔ−ダイ 温度・・３０５℃ （ｅ）冷却ロール温度・・１５℃ （ｆ）押し出し厚み・・４０μｍ （ｇ）エアーギャップ・・９０ｍｍ （ｈ）ニップ圧（エアーゲージ圧）・・４ｋｇ／cm2 (B) Extrusion processing conditions (a) Device ... Device of FIG. (B) Extruder: φ = 60 mm, L / D = 26 (c) Nip roll: Silicon rubber roll (rubber hardness 80 degrees) (d) Temperature setting of extruder (a) Cylinder 1 temperature: 180 ° C ) Cylinder 2 temperature ... 240C (C) Cylinder 3 temperature ... 300C (D) Adapter temperature ... 305C (E) T-die temperature ... 305C (e) Cooling roll temperature ... 15C (f) ) Extrusion thickness: 40 μm (g) Air gap: 90 mm (h) Nip pressure (air gauge pressure): 4 kg / cm 2
【００４０】（Ｃ）光反射層 （ａ）材料・・アルミニウム （ｂ）形成方法・・真空蒸着法 （ｃ）厚み・・５００Å(C) Light-reflecting layer (a) Material: Aluminum (b) Forming method: Vacuum deposition method (c) Thickness: 500Å
【００４１】得られた回折格子シートは、美しく鮮明な
回折格子像と金属光沢を有すると共に、樹脂とアルミニ
ウム蒸着膜との接着性も高く、極めて装飾効果の高いも
のであった。The obtained diffraction grating sheet had a beautiful and clear diffraction grating image and metallic luster, and also had high adhesiveness between the resin and the aluminum vapor deposition film, and had a very high decorative effect.
【００４２】＜実施例２＞図４に示したような装置に
て、下記のエチレン−メタクリル酸共重合体の分子間を
金属イオンで架橋した樹脂（アイオノマー樹脂）、基材
シートを用いて、下記の加工条件にて押し出しコーティ
ングすると共に回折格子をエンボスし、次いで実施例１
同様、この回折格子形成面にアルミニウム蒸着層を設
け、光反射層を得、図５に示す回折格子シートを得た。Example 2 Using a device as shown in FIG. 4, using a resin (ionomer resin) in which the intermolecular of the following ethylene-methacrylic acid copolymer was crosslinked with metal ions and a base sheet, Extrusion coating and embossing of the diffraction grating under the following processing conditions and then Example 1
Similarly, an aluminum vapor deposition layer was provided on this diffraction grating formation surface to obtain a light reflection layer, and the diffraction grating sheet shown in FIG. 5 was obtained.
【００４３】（Ａ）エチレン−メタクリル酸共重合体樹
脂 三井・デュポンポリケミカル株式会社製アイオノマー樹
脂 ハイミラン１６５２ （金属イオン 亜鉛タイプ、ＭＦＲ ５．０ｇ／１０ｍ
ｉｎ）(A) Ethylene-methacrylic acid copolymer resin Ionomer resin manufactured by Mitsui DuPont Polychemical Co., Ltd. High Milan 1652 (metal ion zinc type, MFR 5.0 g / 10 m)
in)
【００４４】（Ｂ）基材シート アート紙 （坪量 ８４．９ｇ／ｍ2 、積層面にコロナ
放電処理を予め実施したもの）(B) Base material sheet Art paper (basis weight of 84.9 g / m 2 , the laminated surface having been previously subjected to corona discharge treatment)
【００４５】（Ｃ）押出加工条件 （ａ）装置・・図５の装置。 （ｂ）押出機・・φ＝６０ｍｍ、Ｌ／Ｄ＝２６ （ｃ）ニップロール・・シリコンゴムロール（ゴム硬度
８０度） （ｄ）押出機の温度設定 （イ）シリンダー１温度・・１８０℃ （ロ）シリンダー２温度・・２４０℃ （ハ）シリンダー３温度・・３００℃ （ニ）アダプター 温度・・３０５℃ （ホ）Ｔ−ダイ 温度・・３０５℃ （ｅ）冷却ロール温度・・１５℃ （ｆ）押し出し厚み・・４０μｍ （ｇ）エアーギャップ・・９０ｍｍ （ｈ）ニップ圧（エアーゲージ圧）・・４ｋｇ／cm2 (C) Extrusion processing conditions (a) Device ... Device of FIG. (B) Extruder: φ = 60 mm, L / D = 26 (c) Nip roll: Silicon rubber roll (rubber hardness 80 degrees) (d) Temperature setting of extruder (a) Cylinder 1 temperature: 180 ° C ) Cylinder 2 temperature ... 240C (C) Cylinder 3 temperature ... 300C (D) Adapter temperature ... 305C (E) T-die temperature ... 305C (e) Cooling roll temperature ... 15C (f) ) Extrusion thickness: 40 μm (g) Air gap: 90 mm (h) Nip pressure (air gauge pressure): 4 kg / cm 2
【００４６】（Ｄ）光反射層 （ａ）材料・・アルミニウム （ｂ）形成方法・・真空蒸着法 （ｃ）厚み・・５００Å(D) Light reflection layer (a) Material: Aluminum (b) Forming method: Vacuum deposition method (c) Thickness: 500Å
【００４７】得られた回折格子シートは、実施例１同
様、美しく鮮明な回折格子像と金属光沢を有すると共
に、樹脂とアルミニウム蒸着膜との接着性も高く、極め
て装飾効果の高いものであった。As in Example 1, the obtained diffraction grating sheet had a beautiful and clear diffraction grating image and metallic luster, and also had a high adhesiveness between the resin and the aluminum vapor deposition film, and had an extremely high decorative effect. ..
【００４８】＜実施例３＞比較例として、図１に示した
装置において、押し出し加工樹脂を低密度ポリエチレン
（ＭＦＲ ５．１ｇ／１０ｍｉｎ）とし、下記の加工条
件にて、実施例１と同様にしてシート成形、回折格子形
成を行い、さらに同様にして光反射層を設け、図３に示
すような回折格子シートを得た。Example 3 As a comparative example, in the apparatus shown in FIG. 1, low density polyethylene (MFR 5.1 g / 10 min) was used as the extruded resin, and the same processing as in Example 1 was carried out under the following processing conditions. Sheet formation and diffraction grating formation were performed, and a light reflection layer was further provided in the same manner to obtain a diffraction grating sheet as shown in FIG.
【００４９】（Ａ）押出加工条件 （ａ）装置・・図１の装置。 （ｂ）押出機・・φ＝６０ｍｍ、Ｌ／Ｄ＝２６ （ｃ）ニップロール・・シリコンゴムロール（ゴム硬度
８０度） （ｄ）押出機の温度設定 （イ）シリンダー１温度・・１８０℃ （ロ）シリンダー２温度・・２４０℃ （ハ）シリンダー３温度・・３１０℃ （ニ）アダプター 温度・・３３０℃ （ホ）Ｔ−ダイ 温度・・３３０℃ （ｅ）冷却ロール温度・・１５℃ （ｆ）押し出し厚み・・４０μｍ （ｇ）エアーギャップ・・９０ｍｍ （ｈ）ニップ圧（エアーゲージ圧）・・４ｋｇ／cm2 (A) Extrusion processing conditions (a) Device ... Device of FIG. (B) Extruder: φ = 60 mm, L / D = 26 (c) Nip roll: Silicon rubber roll (rubber hardness 80 degrees) (d) Temperature setting of extruder (a) Cylinder 1 temperature: 180 ° C ) Cylinder 2 temperature ... 240C (c) Cylinder 3 temperature ... 310C (D) Adapter temperature ... 330C (E) T-die temperature ... 330C (e) Cooling roll temperature ... 15C (f) ) Extrusion thickness: 40 μm (g) Air gap: 90 mm (h) Nip pressure (air gauge pressure): 4 kg / cm 2
【００５０】（Ｃ）光反射層 （ａ）材料・・アルミニウム （ｂ）形成方法・・真空蒸着法 （ｃ）厚み・・５００Å(C) Light-reflecting layer (a) Material ... Aluminum (b) Forming method ... Vacuum deposition method (c) Thickness ... 500Å
【００５１】得られた回折格子シートは、実施例１およ
び２と比較して回折格子像が暗く、金属光沢も低く装飾
効果の劣るものとなった。また、樹脂とアルミニウム蒸
着膜との接着性も弱く、容易にアルミニウム蒸着膜が剥
離し、不満足な結果となった。The obtained diffraction grating sheet had a darker diffraction grating image as compared with Examples 1 and 2 and had a low metallic luster and a poor decorative effect. Further, the adhesion between the resin and the aluminum vapor deposition film was weak, and the aluminum vapor deposition film was easily peeled off, resulting in an unsatisfactory result.
【００５２】これらのエンボス加工性、アルミニウム蒸
着接着性、光沢性を比較評価した結果を表１に示す。Table 1 shows the results of comparative evaluation of these embossability, aluminum vapor deposition adhesiveness and glossiness.
【００５３】得られた回折格子シートの回折格子の成形
性（回折格子スタンパからのエンボス再現性）は、以下
の方法にて評価した。The formability of the diffraction grating of the obtained diffraction grating sheet (reproducibility of embossing from the diffraction grating stamper) was evaluated by the following method.
【００５４】・回折格子シートの回折格子の成形性 回折格子の成形性は、簡易的に回折効率によって評価を
行った。回折効率とは、回折格子において特定次数（こ
こでは１次）の回折光の強度と入射光との強度の比を百
分率で表したものであり、数値が高いほど成形性が良
い、すなわちスタンパからのエンボス再現性が良好であ
ることを示す。 回折効率（％）＝（１次回折光の強度）÷（入射光の強
度）×１００Formability of Diffraction Grating of Diffraction Grating Sheet The formability of the diffraction grating was evaluated simply by the diffraction efficiency. Diffraction efficiency is a ratio of the intensity of diffracted light of a specific order (first order here) to the intensity of incident light in a diffraction grating, and the higher the numerical value, the better the formability. Shows that the emboss reproducibility is good. Diffraction efficiency (%) = (strength of first-order diffracted light) / (strength of incident light) × 100
【００５５】今回、それぞれ得られた回折格子シートの
材質による差を一定とするため、回折格子形成面へ５０
０Å の厚さにアルミニウムを蒸着したのち、その蒸着
面にＨｅ−Ｎｅレーザーを照射し、回折してきた１次回
折光の強度と入射したレーザー光の強度を測定し、上記
式より成形性を判断した。回折効率の値は、評価に使用
した回折格子の形状により異なるが、今回用いた回折格
子の明るさを目視で評価した場合、約１０％でもある程
度明るい回折格子像を見ることができるが、判断基準と
しては、約２５％以上の回折効率が得られれば、ほぼ満
足のできるエンボス再現性であると判断した。This time, in order to make the difference due to the material of the diffraction grating sheet obtained respectively constant, 50
After aluminum was vapor-deposited to a thickness of 0Å, the vapor-deposited surface was irradiated with a He-Ne laser, the intensity of the diffracted first-order diffracted light and the intensity of the incident laser light were measured, and the formability was judged from the above formula. .. The value of the diffraction efficiency differs depending on the shape of the diffraction grating used for the evaluation, but when the brightness of the diffraction grating used this time is visually evaluated, it is possible to see a somewhat bright diffraction grating image even at about 10%. As a standard, it was judged that the emboss reproducibility was almost satisfactory if a diffraction efficiency of about 25% or more was obtained.
【００５６】[0056]
【表１】 [Table 1]
【００５７】以上の実施例から、本発明の効果が非常に
大きいことは明かである。From the above examples, it is clear that the effect of the present invention is very large.
【００５８】[0058]
【発明の効果】以上述べたように、本発明によれば、樹
脂シートの成形とレリーフ型回折格子の形成が同時に行
うことにより、回折格子シートを効率的に、安価で、経
済的に得られるばかりでなく、回折格子形成樹脂として
エチレン−メタクリル酸共重合樹脂を用いたことによ
り、装飾効果に優れたより明るい回折格子像が得られ、
かつ金属蒸着適性が良好なため、金属反射層との接着性
や金属光沢等に優れた回折格子を製造することが可能で
ある。As described above, according to the present invention, the molding of the resin sheet and the formation of the relief type diffraction grating are simultaneously performed, so that the diffraction grating sheet can be obtained efficiently, inexpensively and economically. Not only that, by using ethylene-methacrylic acid copolymer resin as the diffraction grating forming resin, a brighter diffraction grating image excellent in decorative effect can be obtained,
In addition, since the metal vapor deposition suitability is good, it is possible to manufacture a diffraction grating having excellent adhesiveness to the metal reflection layer and metal gloss.
【００５９】[0059]
【図１】本発明の回折格子シートの製造装置の説明図。FIG. 1 is an explanatory view of an apparatus for manufacturing a diffraction grating sheet of the present invention.
【図２】図１に示す製造装置により製造された回折格子
シートの断面図。FIG. 2 is a sectional view of a diffraction grating sheet manufactured by the manufacturing apparatus shown in FIG.
【図３】図２に示したシートの回折格子形成面に光反射
層を設けた、本発明の回折格子シートの断面図。FIG. 3 is a cross-sectional view of a diffraction grating sheet of the present invention in which a light reflection layer is provided on the diffraction grating formation surface of the sheet shown in FIG.
【図４】本発明の他の回折格子シートの製造装置の説明
図。FIG. 4 is an explanatory view of another diffraction grating sheet manufacturing apparatus of the invention.
【図５】図４に示す製造装置により製造され光反射層を
設けた、本発明の回折格子シートの断面図。5 is a sectional view of the diffraction grating sheet of the present invention, which is manufactured by the manufacturing apparatus shown in FIG. 4 and provided with a light reflection layer.
【図６】図５に示した回折格子シートを利用したステッ
カーを示す断面図。6 is a cross-sectional view showing a sticker using the diffraction grating sheet shown in FIG.
【図７】図４に示す製造方法により製造された、本発明
の回折格子シートの断面図。7 is a cross-sectional view of the diffraction grating sheet of the present invention manufactured by the manufacturing method shown in FIG.
１…押出機本体 ２…Ｔ−ダイ ３…冷却ロール ４…ニップロール ５…回折格子スタンパ ６…引き取りロール ７…巻き取りロール １０，２０，３０…回折格子シート １１…エチレン−メタクリル酸共重合樹脂 １１ａ…溶融押出しされたエチレン−メタクリル酸共重
合樹脂 １２…光反射層 １３…基材シート １３ａ…光反射性基材シート １４…感圧接着剤層 １５…離型紙DESCRIPTION OF SYMBOLS 1 ... Extruder main body 2 ... T-die 3 ... Cooling roll 4 ... Nip roll 5 ... Diffraction grating stamper 6 ... Take-up roll 7 ... Winding roll 10, 20, 30 ... Diffraction grating sheet 11 ... Ethylene-methacrylic acid copolymer resin 11a ... Melt-extruded ethylene-methacrylic acid copolymer resin 12 ... Light reflecting layer 13 ... Base sheet 13a ... Light reflecting base sheet 14 ... Pressure-sensitive adhesive layer 15 ... Release paper
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｇ０２Ｂ 5/18 9018−2Ｋ Ｇ０３Ｈ 1/18 8106−2Ｋ // Ｂ２９Ｋ 55:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification number Office reference number FI technical display location G02B 5/18 9018-2K G03H 1/18 8106-2K // B29K 55:00
Claims (1)
に押し出すとともに、または押出成形機から押し出され
た溶融状態の樹脂を基材シート上に押出コーティングす
るとともに、表面に回折格子スタンパを装着したロール
にて、この樹脂を押しつけて樹脂表面にレリーフ型回折
格子をエンボスし、次いでエンボス表面に光反射層を設
けて成る回折格子シートの製造方法において、この樹脂
がエチレン−メタクリル酸共重合樹脂であることを特徴
とする回折格子シートの製造方法。1. A resin in a molten state is extruded from an extrusion molding machine into a sheet shape, or a resin in a molten state extruded from the extrusion molding machine is extrusion-coated on a base material sheet, and a diffraction grating stamper is mounted on the surface. In a manufacturing method of a diffraction grating sheet comprising pressing the resin with a rolled roll to emboss a relief type diffraction grating on the resin surface and then providing a light reflection layer on the embossed surface, the resin is an ethylene-methacrylic acid copolymer resin. A method for manufacturing a diffraction grating sheet, characterized in that