JPH0525901Y2 - - Google Patents
Info
- Publication number
- JPH0525901Y2 JPH0525901Y2 JP1989032710U JP3271089U JPH0525901Y2 JP H0525901 Y2 JPH0525901 Y2 JP H0525901Y2 JP 1989032710 U JP1989032710 U JP 1989032710U JP 3271089 U JP3271089 U JP 3271089U JP H0525901 Y2 JPH0525901 Y2 JP H0525901Y2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- transparent
- layer
- ohp
- image forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】
〈産業上の利用分野〉
本考案はスクリーン上に文字や図形等を投影す
るオーバーヘツドプロジエクター（以下OHPと
略記する）に使用するOHP用シートに関するも
のである。[Detailed Description of the Invention] <Industrial Application Field> The present invention relates to an OHP sheet used in an overhead projector (hereinafter abbreviated as OHP) that projects characters, figures, etc. onto a screen.
〈従来の技術〉
近年、会議や講演会等においてOHPが盛んに
使用されるようになつてきた。従来のOHP用シ
ートは、手書き、複写機による複写、ワープロ等
による感熱転写記録、インクジエツト記録等によ
つて画像を透明性基材上に形成し、OHPに使用
されるものである。<Prior Art> In recent years, overhead projectors have come to be widely used at conferences, lectures, etc. Conventional overhead projector sheets are used for overhead projectors, with images formed on a transparent base material by handwriting, copying with a copying machine, thermal transfer recording with a word processor or the like, inkjet recording, or the like.
しかし最近OHP用シートの用途の多様化が望
まれており、例えばOHPで画像形成して会議等
で使用された後、書類としてそのまま保存した
り、一部を報告書等に添付したり掲示板に貼着し
て展示することが提案されている。しかしなが
ら、従来のOHP用シートは透明性が必要とされ
るので通常透明プラスチツクフイルムが用いられ
ているため、書類として見る際に透明で読みにく
く、従つて一旦画像形成したOHP用シートを他
の用途に転用することは困難であつた。また、
OHP用シートに画像形成する際にもプラスチツ
クフイルムのため、画像の定着が悪く、画像部を
こすると汚れたり画像がとれて消えてしまつたり
という問題を有するものである。 However, recently there has been a desire to diversify the uses of OHP sheets. For example, after forming an OHP image and using it at a meeting, it can be saved as a document, attached to a report, etc., or posted on a bulletin board. It is proposed to be pasted and displayed. However, since conventional OHP sheets require transparency, transparent plastic film is usually used, which makes it difficult to read when viewed as a document. It was difficult to convert it to other uses. Also,
When an image is formed on an OHP sheet, since the plastic film is used, the image does not fix well, and if the image area is rubbed, it becomes smudged or the image is removed and erased.
〈考案が解決しようとする課題〉
本考案は上記の事情に鑑み、画像形成特性に優
れ、しかもOHP用シートとして使用した後に保
存したり、その一部を他の用途に転用する場合に
取扱い性の良好なOHP用シートを提供するもの
である。<Problems to be solved by the invention> In view of the above circumstances, the present invention has excellent image forming properties and is easy to handle when stored after being used as an OHP sheet or when a part of the sheet is to be used for other purposes. This provides a good quality OHP sheet.
〈課題を解決するための手段〉
本考案は、透明支持体上の一方の面にウレタン
系樹脂を含有する画像形成層を設け、他方の面に
粘着層を設け、更に該粘着層上に透明離型性シー
トが貼り合わされている構成よりなるOHP用シ
ートである。<Means for Solving the Problems> The present invention provides an image forming layer containing a urethane resin on one side of a transparent support, an adhesive layer on the other side, and a transparent support on the other side. This is an OHP sheet consisting of a releasable sheet pasted together.
本考案に使用される透明支持体としては、ポリ
エステル、ポリエチレン、ポリプロピレン、ポリ
塩化ビニル、セルローストリアセテート等の透明
フイルムが挙げられるが、これらに限定されるこ
となく透明性を有し、実用上支障のない程度の強
度と柔軟性を有するシート状物であれば使用する
ことができる。 Transparent supports used in the present invention include, but are not limited to, transparent films such as polyester, polyethylene, polypropylene, polyvinyl chloride, and cellulose triacetate. Any sheet-like material having a certain degree of strength and flexibility can be used.
画像形成層は、上記透明支持体上の一方の面に
設けられるものであり、複写機、感熱転写、イン
クジエツト等の各種記録方式により透明支持体上
に直接記録すると記録画像の定着性が充分に得ら
れず、こすると汚れたり画像がとれてしまつたり
するという欠点を解消するために設けられるもの
で、画像の定着・保持という機能を有するもので
ある。画像形成層は、ウレタン系樹脂を含有する
ものであり、かかる樹脂と、必要に応じてシリコ
ーン樹脂、ポリエステル系樹脂、塩化ビニル−酢
酸ビニル系樹脂等の各種樹脂と、透明性を損わな
い範囲でシリカ、クレー、タルク、カオリン、炭
酸カルシウム、ケイ酸アルミニウム、酸化アルミ
ニウム、酸化亜鉛等の顔料とを水、アルコール、
トルエン、メチルエチルケトン、シクロヘキサン
等の溶媒に分散または溶解した塗液をエアーナイ
フコーテイング法、ロールコーテイング法、ワイ
ヤバーコーテイング法、スプレーコーテイング
法、フアウンテンコーテイング法等の塗工方式に
よつて透明支持体上に塗布・乾燥して設けられ
る。 The image forming layer is provided on one side of the transparent support, and when directly recorded on the transparent support by various recording methods such as a copying machine, thermal transfer, or inkjet, the recorded image has sufficient fixing properties. It is provided in order to solve the problem that the image cannot be obtained and the image gets dirty or comes off when rubbed, and has the function of fixing and retaining the image. The image forming layer contains a urethane resin, and if necessary, various resins such as silicone resin, polyester resin, vinyl chloride-vinyl acetate resin, etc. are mixed in a range that does not impair transparency. Pigments such as silica, clay, talc, kaolin, calcium carbonate, aluminum silicate, aluminum oxide, and zinc oxide are mixed with water, alcohol,
A coating liquid dispersed or dissolved in a solvent such as toluene, methyl ethyl ketone, or cyclohexane is coated on a transparent support by a coating method such as an air knife coating method, a roll coating method, a wire bar coating method, a spray coating method, or a fountain coating method. It is applied and dried.
粘着層は、透明支持体の画像形成層とは反対側
の面上に設けられるもので、常温で粘着性を有す
る粘着剤よりなるものである。粘着剤としては、
例えばアクリル系、シリコン系、ゴム系等の粘着
剤が用いられ、これら粘着剤を水、アルコール、
トルエン、メチルエチルケトン、酢酸エチル等の
溶媒に分散または溶解した塗液を、前記画像形成
層と同様にして設けられる。 The adhesive layer is provided on the surface of the transparent support opposite to the image forming layer, and is made of an adhesive that is adhesive at room temperature. As an adhesive,
For example, acrylic, silicone, and rubber adhesives are used, and these adhesives can be mixed with water, alcohol,
A coating liquid dispersed or dissolved in a solvent such as toluene, methyl ethyl ketone, or ethyl acetate is provided in the same manner as the image forming layer.
透明離型性シートは、前記粘着層に貼り合わせ
て設けられるもので、本考案のOHP用シートが
OHPで使用された後、保存されたり、一部分を
カツトして他の用途に転用したりする際に粘着層
によつて容易に貼着されるべく剥離して取除かれ
るものである。従つて、少なくとも粘着層に貼り
合わされる面が離型性を有していることが必要で
ある。透明離型性シートとしては、前記透明支持
体の如きシート状物の少なくとも片面に離型剤を
塗布・乾燥して離型層を設けたシートや、離型層
を設けることなくシートそのものに離型性を有す
る材料よりなる透明シートを用いることができ
る。なお、離型剤としては、エマルジヨン型、溶
剤型、無溶剤型の各種シリコーン系、フツ素系等
の公知の離型剤を使用することができる。 The transparent release sheet is attached to the adhesive layer, and the OHP sheet of the present invention is
After being used in an OHP, it can be peeled off and removed so that it can be easily attached with an adhesive layer when stored or when a portion is cut and used for other purposes. Therefore, it is necessary that at least the surface to be bonded to the adhesive layer has releasability. Examples of the transparent release sheet include a sheet in which a release layer is provided by coating and drying a release agent on at least one side of a sheet-like material such as the transparent support, and a release layer formed on the sheet itself without providing a release layer. A transparent sheet made of a moldable material can be used. As the mold release agent, known mold release agents such as emulsion type, solvent type, and non-solvent type silicone type, fluorine type, etc. can be used.
以上述べたとおり、本考案のOHP用シートは
第１図および第２図に示す構成を有するものであ
る。すなわち、第１図は透明支持体１の一方の面
に画像形成層２が設けられ、他方の面に粘着層３
が設けられ、更に透明シート５に離型層４が設け
られた透明離型性シート６が粘着層に貼り合わせ
られたものである。また第２図は、第１図の離型
層が設けられた透明離型性シートの代わりに、シ
ート自体に離型性を有する材料よりなる透明離型
性シート６が粘着層に貼り合わされたものであ
る。 As described above, the OHP sheet of the present invention has the structure shown in FIGS. 1 and 2. That is, in FIG. 1, an image forming layer 2 is provided on one side of a transparent support 1, and an adhesive layer 3 is provided on the other side.
is provided, and a transparent release sheet 6 in which a release layer 4 is provided on a transparent sheet 5 is bonded to an adhesive layer. In addition, in FIG. 2, instead of the transparent release sheet provided with the release layer shown in FIG. 1, a transparent release sheet 6 made of a material that itself has release properties is laminated to the adhesive layer. It is something.
なお、本考案のOHP用シートは帯電防止処理
が施されていることが好ましい。帯電防止処理を
施すには、透明支持体や透明離型性シートにおい
てはシート自体に帯電防止剤を含有させたり、透
明支持体や透明離型性シートの表面に帯電防止剤
を塗工することによつて、また画像形成層や粘着
層においては、各層形成用塗液に帯電防止剤を配
合することによつてなされる。ここで帯電防止剤
としては、例えばリン酸エステル系、脂肪酸エス
テル系等が挙げられ、カチオン系、アニオン系、
ノニオン系の各種帯電防止剤を適宜選択して使用
することができる。 Note that the OHP sheet of the present invention is preferably subjected to antistatic treatment. To perform antistatic treatment, it is necessary to incorporate an antistatic agent into the transparent support or transparent release sheet, or to coat the surface of the transparent support or transparent release sheet with an antistatic agent. In addition, in the image forming layer and the adhesive layer, an antistatic agent is added to the coating liquid for forming each layer. Here, examples of the antistatic agent include phosphoric acid ester type, fatty acid ester type, etc., and cationic type, anionic type,
Various nonionic antistatic agents can be appropriately selected and used.
また、本考案のOHP用シートにおいては、全
体が透明体であるため、画像形成に際して画像形
成層側の面が容易に識別できる様に、例えば、記
号、文字、図形等によるマークをOHP用シート
の画像形成層、透明支持体、粘着層、透明離型シ
ートの一部に、画像に影響を及ぼさない様に印刷
したり、OHP用シートの一部に例えば切欠部の
如き形態上の目印を設けたりして画像形成面とそ
の反対側の面である離型性を有する透明シート面
との識別手段を施しておくことが実用上有効であ
る。 In addition, since the OHP sheet of the present invention is entirely transparent, marks such as symbols, letters, figures, etc. are placed on the OHP sheet so that the surface on the image forming layer side can be easily identified during image formation. The image forming layer, transparent support, adhesive layer, and transparent release sheet may be printed in a manner that does not affect the image, or a part of the OHP sheet may be marked with a morphological mark such as a notch. It is practically effective to provide means for distinguishing between the image forming surface and the surface of the transparent sheet having releasability, which is the surface on the opposite side.
〈実施例〉
次に本考案を実施例により説明する。なお、配
合を示す部数は全て重量部を表わす。<Example> Next, the present invention will be explained with reference to an example. Note that all parts indicating formulations represent parts by weight.
実施例 １
透明支持体として厚さ100μmの熱処理済ポリエ
ステルフイルム（富士写真フイルム社製、PT−
100AG）を使用して、この一方の面に下記組成
よりなる塗液を塗布・乾燥して層厚2μmの画像形
成層を設けた。Example 1 A heat-treated polyester film with a thickness of 100 μm (manufactured by Fuji Photo Film Co., Ltd., PT-
100AG), a coating liquid having the following composition was coated on one side and dried to form an image forming layer with a layer thickness of 2 μm.
ポリエステル系樹脂（東洋紡社製、バイロン
200、固形分40％） 20部
ポリウレタン系樹脂（日本ポリウレタン社製、
ニツポラン3124、固形分50％） ６部
硬化剤（日本ポリウレタン社製、コロネート
Ｌ、固形分75％） １部
シリカ（ワツカー社製、HDK−H2F） 0.03部
帯電防止剤（ドデシルリン酸ナトリウム） ５部
トルエン 22部
メチルエチルケトン 14部
次に、透明支持体の他方の面に下記組成よりな
る塗液を塗布・乾燥して層厚2μmの粘着層を設け
た。Polyester resin (manufactured by Toyobo Co., Ltd., Byron)
200, solid content 40%) 20 parts polyurethane resin (manufactured by Nippon Polyurethane Co., Ltd.)
Nitsuporan 3124, solid content 50%) 6 parts Hardening agent (Japan Polyurethane Co., Ltd., Coronate L, solid content 75%) 1 part Silica (Watzker Co., Ltd., HDK-H2F) 0.03 parts Antistatic agent (sodium dodecyl phosphate) 5 parts Toluene 22 parts Methyl ethyl ketone 14 parts Next, a coating liquid having the following composition was applied to the other side of the transparent support and dried to form an adhesive layer with a layer thickness of 2 μm.
アクリル系共重合体粘着剤（昭和高分子社製、
OLX−1724、固形分75％） 20部
水 50部
一方、厚さ38μmのポリエステルフイルム（帝
人社製、Ｓ−38）を用いて、この片面に下記組成
よりなる塗液を塗布・乾燥して層厚1μmの離型層
を設けて透明離型製シートを得た。この透明離型
性シートの離型層面と前記粘着層面とを貼り合わ
せて、透明支持体と透明離型性シートとを一体化
して本発明のOHP用シートを作製した。Acrylic copolymer adhesive (manufactured by Showa Kobunshi Co., Ltd.)
OLX-1724, solid content 75%) 20 parts Water 50 parts On the other hand, using a 38 μm thick polyester film (manufactured by Teijin Corporation, S-38), a coating liquid with the following composition was applied to one side and dried. A transparent release sheet was obtained by providing a release layer with a layer thickness of 1 μm. The release layer surface of this transparent release sheet and the adhesive layer surface were bonded together to integrate the transparent support and the transparent release sheet to produce an OHP sheet of the present invention.
シリコーン系離型剤（信越化学工業社製、Ｘ−
62−2087、固形分30％） 100部
触媒（信越化学工業社製、CAT PL−８）
１部
ドデシルリン酸ナトリウム ２部
実施例 ２
画像形成層用塗液として下記組成よりなる塗液
を使用した以外は、全て実施例１と同様にして本
発明のOHP用シートを作製した。Silicone mold release agent (manufactured by Shin-Etsu Chemical Co., Ltd., X-
62-2087, solid content 30%) 100 parts catalyst (manufactured by Shin-Etsu Chemical Co., Ltd., CAT PL-8)
1 part Sodium dodecyl phosphate 2 parts Example 2 An OHP sheet of the present invention was prepared in the same manner as in Example 1, except that a coating liquid having the following composition was used as the coating liquid for the image forming layer.
ポリウレタンエラストマー（日本ポリウレタン
社製、パラプレン84） ８部
ポリエステル系樹脂（東洋紡社製、バイロン
300） ２部
帯電防止剤（三菱油化社製、STH3000） １部
フツ素系離型剤（三井フロロケミカル社製、
FC430） 0.1部
メチルエチルケトン 60部
トルエン 20部
シクロヘキサン 10部
上記実施例１および２で得たOHP用シートを
A4サイズにカツトした後、画像形成層面側から
見て「記録面」と読めるように、透明離型性シー
ト面側の右下コーナーに小さく逆文字で印刷を施
した。これらのOHP用シートの画像形成層面に、
市販の電子写真複写機にてトナー画像を形成して
市販のOHPにかけたところ良好な画像が得られ、
しかも指等によるこすれにも耐え、十分な耐摩耗
性が得られた。このOHPシートの透明離型性シ
ートを剥離して白紙を粘着層に貼着したところ、
一般の書類と同じように読みやすい書類が得られ
た。また、別のOHPシートの一部である図表を
切り取り透明離型性シートを剥離して白色のノー
トや掲示板に貼りつけることによつて容易に他の
書類としての用途に転用することができた。Polyurethane elastomer (manufactured by Nippon Polyurethane Co., Ltd., Paraprene 84) 8 parts polyester resin (manufactured by Toyobo Co., Ltd., Vylon
300) 2 parts antistatic agent (Mitsubishi Yuka Co., Ltd., STH3000) 1 part fluorine-based mold release agent (Mitsui Fluorochemical Co., Ltd.,
FC430) 0.1 part Methyl ethyl ketone 60 parts Toluene 20 parts Cyclohexane 10 parts The OHP sheets obtained in Examples 1 and 2 above were
After cutting it to A4 size, small inverted letters were printed on the lower right corner of the transparent release sheet side so that it could be read as "recording side" when viewed from the image forming layer side. On the image forming layer surface of these OHP sheets,
When a toner image was formed using a commercially available electrophotographic copying machine and applied to a commercially available OHP, a good image was obtained.
Furthermore, it was able to withstand rubbing by fingers, etc., and had sufficient abrasion resistance. When the transparent release sheet of this OHP sheet was peeled off and the white paper was attached to the adhesive layer,
The result was a document that was as easy to read as any other document. In addition, by cutting out the diagrams that were part of another OHP sheet, peeling off the transparent release sheet, and pasting them on a white notebook or bulletin board, it was possible to easily repurpose them for other documents. .
〈考案の効果〉
本考案のOHP用シートは、ウレタン系樹脂を
含有する画像形成層を有する透明支持体と粘着層
および透明離型性シートとを一体化して設けた構
成のため、鮮明でかつ耐摩耗性を有する良好な画
像が得られるのみでなく、透明離型性シートを剥
離するだけで白色系の紙とか掲示板等に簡易に貼
着できるので、この画像形成したOHP用シート
を書類として保存したり他の書類へ転用したりす
る新規な用途に適用することができる。<Effects of the invention> The OHP sheet of the invention has a structure in which a transparent support having an image forming layer containing a urethane resin, an adhesive layer, and a transparent release sheet are integrated, so it is clear and transparent. Not only can a good image with abrasion resistance be obtained, but also it can be easily pasted on white paper, bulletin boards, etc. by simply peeling off the transparent release sheet, so the OHP sheet with this image formed on it can be used as a document. It can be applied to new uses such as storage or reuse for other documents.
第１図および第２図は本考案のOHP用シート
の構成を示す断面図である。
１……透明支持体、２……画像形成層、３……
粘着層、４……離型層、５……透明シート、６…
…透明離型性シート。
FIGS. 1 and 2 are cross-sectional views showing the structure of the OHP sheet of the present invention. 1... Transparent support, 2... Image forming layer, 3...
Adhesive layer, 4... Release layer, 5... Transparent sheet, 6...
...Transparent release sheet.
Claims (1)
含有する画像形成層を設け、他方の面に粘着層
を設け、更に該粘着層上に透明離型性シートが
貼り合わされていることを特徴とするオーバー
ヘツドプロジエクター用シート。 ２ オーバーヘツドプロジエクター用シートの層
構成の任意の個所に、記号、文字、図形等の識
別手段が施されていることを特徴とする請求項
１記載のオーバーヘツドプロジエクター用シー
ト。[Claims for Utility Model Registration] 1. An image forming layer containing a urethane resin is provided on one side of a transparent support, an adhesive layer is provided on the other side, and a transparent release sheet is further provided on the adhesive layer. A sheet for an overhead projector, which is characterized by being laminated with. 2. The sheet for an overhead projector according to claim 1, wherein an identification means such as a symbol, a character, a figure, etc. is applied to any part of the layer structure of the sheet for an overhead projector.