JPH05178646A - Artificial marble - Google Patents
Artificial marbleInfo
- Publication number
- JPH05178646A JPH05178646A JP34618591A JP34618591A JPH05178646A JP H05178646 A JPH05178646 A JP H05178646A JP 34618591 A JP34618591 A JP 34618591A JP 34618591 A JP34618591 A JP 34618591A JP H05178646 A JPH05178646 A JP H05178646A
- Authority
- JP
- Japan
- Prior art keywords
- artificial marble
- glass filler
- polyester resin
- refractive index
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は浴槽等に用いるに適した
耐熱水性と透明感に優れた人造大理石に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to artificial marble suitable for use in bathtubs and the like and having excellent hot water resistance and transparency.
【０００２】[0002]
【従来の技術】ポリエステル樹脂中にガラスフィラーを
分散させた人造大理石は従来から広く知られており、こ
のためのガラスフィラーとしては、例えば次の通りの組
成を持つものが普通である。 SiO2 40〜65％ （本明細書では全て重量％で表示） B2O3 10〜30％ Al2O3 0〜15％ R2O 5〜20％ MO 5〜30％ TiO2 0〜10％ ZrO2 0〜10％2. Description of the Related Art Artificial marble in which a glass filler is dispersed in a polyester resin has been widely known, and a glass filler for this purpose has, for example, the following composition. SiO 2 40 to 65% (indicated by all herein wt%) B 2 O 3 10~30% Al 2 O 3 0~15% R 2 O 5~20% MO 5~30% TiO 2 0~10 % ZrO 2 0~10%
【０００３】ところが上記のような従来の人造大理石
は、耐熱水性が不十分であって長期間使用すると次第に
ブリスターや白化が生じ易く、またガラスフィラー自体
は透明であるにもかかわらず、人造大理石としたときに
十分な透明感を得られないという問題を残していた。However, the conventional artificial marbles as described above have insufficient hot water resistance, and gradually become blistered or whitened when they are used for a long period of time. I was left with the problem that I could not get a sufficient transparency when I did.
【０００４】[0004]
【発明が解決しようとする課題】本発明は上記した従来
の問題点を解決して、従来品よりも耐熱水性と透明感に
優れた人造大理石を提供するために完成されたものであ
る。本発明者はこの課題を解決するために従来品におけ
る問題の原因を追求した結果、ガラスフィラーの組成中
に多量に含有されているB2O3およびR2O 成分が耐熱水性
を低下させている原因であることを知った。The present invention has been completed in order to solve the above-mentioned conventional problems and provide an artificial marble which is more excellent in hot water resistance and transparency than conventional products. As a result of pursuing the cause of problems in conventional products in order to solve this problem, the present inventor reduced the hot water resistance of the B 2 O 3 and R 2 O components contained in a large amount in the composition of the glass filler. I knew it was the cause.
【０００５】[0005]
【課題を解決するための手段】本発明は上記の知見に基
づいてなされたものであり、SiO2 50 〜65％、Al2O3 10
〜20％、CaO 20〜30％、B2O3 0.1％以下、R2O ３％以下
の組成を持つ３成分系のガラスフィラーを、ポリエステ
ル樹脂中に分散させたことを特徴とする人造大理石を要
旨とするものである。The present invention has been made on the basis of the above findings, and SiO 2 50 to 65%, Al 2 O 3 10
〜20%, CaO 20〜30%, B 2 O 3 0.1% or less, R 2 O 3% or less composition of the three-component glass filler dispersed in polyester resin, artificial marble Is the gist.
【０００６】上記のように本発明はガラスフィラーの組
成に特徴を持つものであり、従来の組成とは異なり、B2
O3およびR2O 成分をほとんど含有しないSiO2−Al2O3 −
CaOの３成分系の組成とした。ここでB2O3を 0.1％以
下、R2O を３％以下としたのは、耐熱水性を大幅に向上
させるためであり、このような特殊な組成のガラスフィ
ラーを分散させた人造大理石は従来は知られていない。As described above, the present invention is characterized by the composition of the glass filler, and unlike the conventional composition, B 2
SiO 2 − Al 2 O 3 − containing almost no O 3 and R 2 O components
The composition is a three-component system of CaO. The reason why B 2 O 3 is 0.1% or less and R 2 O is 3% or less is to significantly improve the hot water resistance, and artificial marble in which glass filler having such a special composition is dispersed is Previously unknown.
【０００７】またB2O3およびR2O を含有しないSiO2−Al
2O3 −CaO の３成分系のガラス組成においてポリエステ
ル樹脂との屈折率の一致を図るため、本発明においては
図１に示されるSiO2 50 〜65％、Al2O3 10〜20％、CaO
20〜30％の組成範囲を選択した。ここでSiO2を50〜60％
としたのは、50％未満ではガラスフィラーの屈折率がポ
リエステル樹脂の屈折率（1.54〜1.55) と一致せず、ま
た65％を越えるとこの成分系では溶融しにくくなるため
である。Al2O3 を10〜20％としたのは、10％未満ではや
はりガラスフィラーの屈折率がポリエステル樹脂と合わ
ず、20％を越えると溶融しにくくなるためである。さら
にCaO を20〜30％としたのは、20％未満ではガラスフィ
ラーの屈折率が合わず、30％を越えるとガラスフィラー
中に結晶が生じ易くなって透明感が失われるおそれがあ
るためである。Further, SiO 2 -Al containing no B 2 O 3 and R 2 O
In order to match the refractive index with the polyester resin in the three-component glass composition of 2 O 3 —CaO, in the present invention, SiO 2 50 to 65%, Al 2 O 3 10 to 20% shown in FIG. CaO
A composition range of 20-30% was selected. Where SiO 2 is 50-60%
The reason is that if it is less than 50%, the refractive index of the glass filler does not match the refractive index of the polyester resin (1.54 to 1.55), and if it exceeds 65%, it becomes difficult to melt in this component system. The reason why Al 2 O 3 is set to 10 to 20% is that when the content is less than 10%, the refractive index of the glass filler still does not match the polyester resin, and when it exceeds 20%, it becomes difficult to melt. Further, CaO is set to 20 to 30% because if it is less than 20%, the refractive index of the glass filler does not match, and if it exceeds 30%, crystals may easily occur in the glass filler and the transparency may be lost. is there.
【０００８】上記した組成のガラスフィラーを常法によ
りポリエステル樹脂中に分散させれば、耐熱水性に優れ
また透明感のある人造大理石を得ることができる。以下
に本発明の実施例を示す。By dispersing the glass filler having the above composition in the polyester resin by a conventional method, it is possible to obtain an artificial marble having excellent hot water resistance and transparency. Examples of the present invention will be shown below.
【０００９】[0009]
【実施例】表１に示される各種の組成のガラスを1400〜
1500℃で溶融し、冷却・粉砕したうえシランカップリン
グ剤により表面処理してガラスフィラーとした。これら
のガラスフィラー（各200g）と不飽和ポリエステル樹脂
100gおよび硬化剤１ｇを混練し、真空脱泡した。次にゲ
ルコート樹脂を0.3 〜0.4mm の厚さとして60℃で60分間
加熱硬化させ、その上に上記の混練物をそれぞれ流し込
み、60℃で２時間加熱硬化させて人造大理石を得た。[Examples] Glasses of various compositions shown in Table 1
It was melted at 1500 ° C, cooled, pulverized, and surface-treated with a silane coupling agent to obtain a glass filler. These glass fillers (200g each) and unsaturated polyester resin
100 g and 1 g of curing agent were kneaded and degassed in vacuum. Next, the gel coat resin having a thickness of 0.3 to 0.4 mm was heat-cured at 60 ° C. for 60 minutes, and the above kneaded products were respectively poured into the gel-coated resin and heat-cured at 60 ° C. for 2 hours to obtain artificial marble.
【００１０】なお表１のNo.1〜No.3は本発明の組成範囲
内の実施例を示す。これに対してNo.4〜No.7は比較例を
示すものであり、No.4はR2O が３％を越え、No.5はSiO2
が65％を越え、No.6はAl2O3 が20％を越え、No.7はCaO
が30％を越えたものである。No. 1 to No. 3 in Table 1 show examples within the composition range of the present invention. On the other hand, No. 4 to No. 7 are comparative examples, R 2 O exceeds 3% in No. 4 and SiO 2 in No. 5
Is over 65%, No. 6 is over 2 % Al 2 O 3 , No. 7 is CaO
Is over 30%.
【００１１】この結果、No.1〜No.3のガラスフィラーを
分散させた人造大理石は透明感に優れかつ耐熱水性が良
好であったが、No.4のものは透明感は優れるものの耐熱
水性が悪く、ブリスターの発生が早かった。またNo.5と
No.6はガラス化が困難であった。さらにNo.7はやはりガ
ラスフィラーの屈折率が低く、良好な透明感が得られな
かった。As a result, the artificial marble in which the No. 1 to No. 3 glass fillers were dispersed had excellent transparency and hot water resistance, while the No. 4 material had excellent transparency but hot water resistance. It was bad, and the blister occurred quickly. Also with No. 5
No. 6 was difficult to vitrify. Further, in No. 7, the refractive index of the glass filler was also low, and good transparency was not obtained.
【００１２】[0012]
【表１】 [Table 1]
【００１３】[0013]
【発明の効果】以上に詳細に説明したように、本発明の
人造大理石は耐熱水性に優れたものであり、浴槽等に使
用した場合にもブリスター等を生ずることがない。また
本発明の人造大理石はガラスフィラーの屈折率がポリエ
ステルの屈折率と一致しているため、透明感に富んだ美
しい外観を呈するものである。よって本発明は従来の問
題点を解消した人造大理石として、産業の発展に寄与す
るところは極めて大きいものである。As described above in detail, the artificial marble of the present invention has excellent hot water resistance and does not cause blisters or the like when used in a bathtub or the like. Further, since the refractive index of the glass filler of the artificial marble of the present invention matches the refractive index of polyester, the artificial marble exhibits a beautiful appearance with a rich transparency. Therefore, the present invention contributes greatly to industrial development as an artificial marble that solves the conventional problems.
【図１】本発明におけるガラスフィラーの組成範囲を示
す３成分図である。FIG. 1 is a three-component diagram showing a composition range of a glass filler in the present invention.
Claims (1)
Al2O3 10〜20％、CaO 20〜30％、B2O3 0.1％以下、R2O
３％以下の組成を持つ３成分系のガラスフィラーを、ポ
リエステル樹脂中に分散させたことを特徴とする人造大
理石。1. SiO 2 50 to 65% (weight%, the same applies hereinafter),
Al 2 O 3 10-20%, CaO 20-30%, B 2 O 3 0.1% or less, R 2 O
Artificial marble characterized in that a three-component glass filler having a composition of 3% or less is dispersed in a polyester resin.