JPH04281098A - Wallpaper having projector screen function and its production - Google Patents
Wallpaper having projector screen function and its productionInfo
- Publication number
- JPH04281098A JPH04281098A JP3065531A JP6553191A JPH04281098A JP H04281098 A JPH04281098 A JP H04281098A JP 3065531 A JP3065531 A JP 3065531A JP 6553191 A JP6553191 A JP 6553191A JP H04281098 A JPH04281098 A JP H04281098A
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- wallpaper
- thermoplastic resin
- projector screen
- screen function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】0001
【産業上の利用分野】本発明は、プロジェクタースクリ
ーンとしての機能を併せ持った壁紙およびその製造方法
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wallpaper that also functions as a projector screen and a method for manufacturing the same.
【0002】0002
【従来の技術】オーバーヘッドプロジェクター(OHP
)が普及し、学校、会社、あるいは講演会等で幅広く使
用されているが、投写するスクリーンとしては従来表面
の白い塩ビ製のスクリーンが多く用いられている。また
、近年、液晶パネル等を用いた投写形テレビジョンシス
テムが市場に現われてきた。これらOHPや投写形テレ
ビジョンはスクリーンを用いることを常とし、仮にスク
リーンがない場合に、白壁でも画像、文字等を一応見る
ことはできたが、そもそも壁材適性とスクリーン適性と
は根本的に異なるため、画像が暗すぎて明瞭に見えない
などの問題がある。特に投写形テレビジョンは光源の明
るさを高くすることが出来ず、明るい画像を得るために
は、むしろ従来より反射特性の良い明るいスクリーンの
要望が強まっている。[Prior art] Overhead projector (OHP)
) has become popular and is widely used in schools, companies, lectures, etc., but conventionally, PVC screens with white surfaces are often used as projection screens. Furthermore, in recent years, projection television systems using liquid crystal panels and the like have appeared on the market. These OHPs and projection televisions usually use a screen, and even if there was no screen, it was possible to see images, text, etc. even on a white wall, but in the first place, the suitability of wall materials and the suitability of screens are fundamentally different. Since the images are different, there are problems such as images being too dark to be seen clearly. In particular, in projection televisions, the brightness of the light source cannot be increased, and in order to obtain bright images, there is a growing demand for a brighter screen with better reflective properties than before.
【0003】しかし、スクリーンを使用することは、そ
れを設置するスペースが必要であり、あらかじめ用意す
る手間もかかる。また、移動設置を考えるとスクリーン
の大きさにも限度がある。そこで、スクリーンを用意し
ていなくとも、会議等でOHP等を使用したいと思うと
きにすぐに対応できるような手段が要望されている。[0003] However, using a screen requires space to install it, and it takes time and effort to prepare it in advance. Furthermore, there is a limit to the size of the screen when considering mobile installation. Therefore, there is a need for a means that can be used immediately when a user wants to use an OHP or the like in a meeting, etc., even if a screen is not prepared.
【0004】0004
【発明が解決しようとする課題】本発明は上記従来の課
題に鑑みなされたもので、その目的は、スクリーンをい
ちいち用意しなくとも、OHP等を使用したいという要
求に瞬時に応えるべく、プロジェクタースクリーンとし
ての機能を併せ持った壁紙およびその製造方法を提供す
ることにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned conventional problems, and its purpose is to provide a projector screen in order to instantly meet the demand for using OHP, etc., without having to prepare a screen each time. The purpose of the present invention is to provide wallpaper that has both the functions of
【0005】[0005]
【課題を解決するための手段】上記目的を達成するため
に、本発明の壁紙は、着色基材上に、少なくとも一層の
発泡樹脂層を有し、その上にパール顔料等を混入した少
なくとも一層の熱可塑性樹脂層を有し、該熱可塑性樹脂
層の最上層の表面に透明ビーズを一面に並べてなる、あ
るいは該熱可塑性樹脂層の最上層の表面に砂目模様のエ
ンボスが施されていることを特徴とするものである。[Means for Solving the Problems] In order to achieve the above object, the wallpaper of the present invention has at least one foamed resin layer on a colored base material, and at least one layer containing a pearl pigment or the like thereon. The thermoplastic resin layer has a thermoplastic resin layer with transparent beads arranged all over the surface of the uppermost layer, or the uppermost layer of the thermoplastic resin layer has an embossed grain pattern on the surface. It is characterized by this.
【0006】また、本発明の壁紙の製造方法は、着色基
材上に、少なくとも一層の加熱発泡剤を含有する樹脂層
を塗設し、その上に少なくとも一層のパール顔料等を混
入した熱可塑性樹脂層を積層し、さらに該熱可塑性樹脂
層の最上層の表面に透明ビーズを一面に並べ必要に応じ
て上から軽く圧着した後、全体を加熱して前記発泡剤含
有樹脂層を発泡せしめることを特徴とするものである。[0006] Furthermore, the method for producing wallpaper of the present invention involves coating a colored base material with at least one resin layer containing a heat-foaming agent, and on top of that a thermoplastic resin layer containing at least one pearl pigment or the like. Laminating the resin layers, further arranging transparent beads on the surface of the uppermost layer of the thermoplastic resin layer and pressing lightly from above if necessary, then heating the whole to foam the foaming agent-containing resin layer. It is characterized by:
【0007】また、本発明の壁紙の製造方法は、着色基
材上に、少なくとも一層の加熱発泡剤を含有する樹脂層
を塗設し、その上に少なくとも一層のパール顔料等を混
入した熱可塑性樹脂層を積層した後、全体を加熱して前
記発泡剤含有樹脂層を発泡せしめ、さらに最上層の表面
に砂目模様のエンボスを施すことを特徴とするものであ
る。[0007] Furthermore, the method for producing wallpaper of the present invention involves coating a colored base material with at least one resin layer containing a heat-foaming agent, and on top of that a thermoplastic resin layer containing at least one pearl pigment or the like. After the resin layers are laminated, the entire layer is heated to foam the foaming agent-containing resin layer, and the surface of the uppermost layer is further embossed with a grain pattern.
【0008】以下、本発明を詳述する。図1は本発明の
壁紙の構成例を示す断面図である。本構成例によると、
着色基材1上に、発泡樹脂層2、第1の熱可塑性樹脂層
3a、および第2の熱可塑性樹脂層3bがこの順に積層
され、最上層である第2の熱可塑性樹脂層3bの表面に
透明ビーズ4を一面に並べた構成となっている。The present invention will be explained in detail below. FIG. 1 is a sectional view showing an example of the structure of the wallpaper of the present invention. According to this configuration example,
A foamed resin layer 2, a first thermoplastic resin layer 3a, and a second thermoplastic resin layer 3b are laminated in this order on the colored base material 1, and the surface of the second thermoplastic resin layer 3b, which is the uppermost layer, It has a structure in which transparent beads 4 are arranged on one side.
【0009】着色基材1としては、着色裏打紙あるいは
裏打紙の表面にベタ印刷を施したものが良い。着色ある
いはベタ印刷を施すことにより、光の乱反射性を低くし
、プロジェクタースクリーンとしての効果を高めること
ができる。また壁紙としての色もひかりすぎず、落ちつ
いた色となる。ベタ印刷の色はどの色でも良いが、黒ベ
タが最も好ましい。また、裏打紙は、壁紙貼り換え時に
裏打紙の層間で剥離する性質(ピーラブル性)を有して
おり、それゆえ貼り換え時の手間(凹凸をなくすための
パテ塗りやうまく貼れない場所の掃除等)が少なくて済
む。The colored base material 1 is preferably a colored backing paper or a backing paper with solid printing applied to the surface thereof. By coloring or solid printing, the diffused reflection of light can be reduced and the effect as a projector screen can be enhanced. Also, the color of the wallpaper is not too bright and has a calming color. Any color may be used for solid printing, but solid black is most preferable. In addition, the backing paper has a property (peelability) of peeling between the layers of the backing paper when re-pasting the wallpaper, which makes it difficult to apply putty to eliminate unevenness and cleaning areas where it cannot be properly pasted. etc.).
【0010】発泡樹脂層2は、塩化ビニル樹脂等の熱可
塑性樹脂のペースト中に発泡剤を含有し、これを着色基
材1上に塗設して発泡せしめることにより形成されるが
、この発泡樹脂層2を設けることにより壁の下地をひろ
わず凹凸をカバーすることができる。発泡剤としては、
通常の有機発泡体を使用するとガスが層間に残りシート
がふくれたり、再加熱でセルがつぶれる等の不都合が考
えられるため、本発明では加熱タイプのカプセル発泡剤
を使用することが望ましい。カプセル発泡剤の使用量は
ペースト樹脂に対し2〜20重量部程度である。発泡樹
脂層2は通常一層で十分であるが、厚みによっては二層
以上設けるようにしてもよい。The foamed resin layer 2 is formed by containing a foaming agent in a paste of thermoplastic resin such as vinyl chloride resin, and coating this on the colored base material 1 and causing it to foam. By providing the resin layer 2, unevenness can be covered without covering the base of the wall. As a foaming agent,
If a normal organic foam is used, gas may remain between the layers and the sheet may swell, or the cells may collapse upon reheating. Therefore, in the present invention, it is preferable to use a heating type capsule foaming agent. The amount of capsule foaming agent used is about 2 to 20 parts by weight based on the paste resin. Although one foamed resin layer 2 is usually sufficient, two or more layers may be provided depending on the thickness.
【0011】熱可塑性樹脂層3は、塩化ビニル樹脂など
の熱可塑性樹脂中にプロジェクタースクリーン機能を持
たせるためにパール顔料等を含有したもので、図1に示
す構成では第1及び第2の二層(3a及び3b)からな
る積層構成であるが、一層構成でもよいし、また三層以
上の多層構成でもよい。使用するパール顔料としては、
雲母に二酸化チタンをコーティングしたタイプのフィラ
ーで、チタンの被覆率28%、粒径5〜60μm(平均
粒径30μm)の鱗片状のものが、コーティング適性か
ら好ましい。パール顔料は、通常樹脂に対し30重量部
以下程度の添加量で使用される。The thermoplastic resin layer 3 is made of a thermoplastic resin such as vinyl chloride resin containing a pearl pigment or the like in order to provide a projector screen function, and in the configuration shown in FIG. Although it has a laminated structure consisting of layers (3a and 3b), it may have a single layer structure or a multilayer structure of three or more layers. The pearl pigment used is
A type of filler in which mica is coated with titanium dioxide, and a scale-like filler with a titanium coverage of 28% and a particle size of 5 to 60 μm (average particle size of 30 μm) is preferable from the viewpoint of coating suitability. The pearl pigment is usually used in an amount of about 30 parts by weight or less based on the resin.
【0012】また、熱可塑性樹脂層3は、透明ペースト
中に所望の色のインキ(使用量は通常樹脂に対し3重量
部以下程度)を混入して着色ペースト層とすることもで
きる。例えば、図1に示す構成で、第1の層3aを着色
ペースト層、第2の層3bをパール顔料含有層とするこ
とができる。The thermoplastic resin layer 3 can also be made into a colored paste layer by mixing ink of a desired color into a transparent paste (the amount used is usually about 3 parts by weight or less based on the resin). For example, in the configuration shown in FIG. 1, the first layer 3a can be a colored paste layer and the second layer 3b can be a pearl pigment-containing layer.
【0013】上記熱可塑性樹脂層3、および前記発泡樹
脂層2の形成にあたっては、公知のコーティング手段を
用いることができる。また、上記熱可塑性樹脂層3はペ
ースト層として形成するほか、フィルムとして形成して
も構わない。[0013] In forming the thermoplastic resin layer 3 and the foamed resin layer 2, known coating means can be used. In addition to forming the thermoplastic resin layer 3 as a paste layer, it may also be formed as a film.
【0014】熱可塑性樹脂層3の最上層(図1では3b
)の表面には透明ビーズ4を一面に並べることにより、
効果的なプロジェクタースクリーン機能を持たせる。す
なわち、光の収束する方向からは鮮明であるが見る角度
を変えると見にくくなるといった事のないように、広範
な角度から見て画像が鮮明に写し出される。透明ビーズ
の施工方法としては、例えばガラス接着用の接着剤(ペ
ーストでも可)を塗布し、公知のサンドペーパー製造法
と同様に透明ビーズをふきつけて製造することができる
。透明ビーズとしては、ガラスビーズが使用され、効果
的なプロジェクタースクリーン機能を持たせるためにガ
ラスビーズの屈折率は1.0〜2.5、特に1.9程度
が好ましく、また壁紙としての施工性の点からガラスビ
ーズの粒径は100μm以下のものが好ましい。The uppermost layer of the thermoplastic resin layer 3 (3b in FIG. 1)
) By arranging transparent beads 4 all over the surface,
To provide an effective projector screen function. That is, the image is clearly projected from a wide range of angles, so that the image is clear from the direction in which the light converges, but becomes difficult to see when the viewing angle is changed. The transparent beads can be manufactured by, for example, applying an adhesive for adhering glass (paste is also acceptable) and then wiping the transparent beads in the same manner as in the known sandpaper manufacturing method. As the transparent beads, glass beads are used, and in order to have an effective projector screen function, the refractive index of the glass beads is preferably 1.0 to 2.5, particularly about 1.9, and also has good workability as wallpaper. From this point of view, the particle size of the glass beads is preferably 100 μm or less.
【0015】熱可塑性樹脂層3の最上層の表面に透明ビ
ーズを並べるかわりに、エンボスを施すことによりプロ
ジェクタースクリーン機能を持たせることができる。こ
の場合は透過型から反射型スクリーンとなる。エンボス
を施すことにより、光の反射を分散させ、まぶしさをな
くすことができる。この場合のエンボスはモアレを起こ
さない砂目模様が良い。透明ビーズを使用の時に比べ、
価格や汚れ防止、安全性に有利である。[0015] Instead of arranging transparent beads on the surface of the uppermost layer of thermoplastic resin layer 3, it can be provided with a projector screen function by embossing it. In this case, the screen changes from a transmissive type to a reflective type. By applying embossing, it is possible to disperse the reflection of light and eliminate glare. In this case, the embossing should be a grain pattern that does not cause moiré. Compared to when using transparent beads,
It is advantageous in terms of price, stain prevention, and safety.
【0016】また、壁紙の配合中に防カビ剤を入れるこ
とにより防カビ性能を付加することができる。防カビ剤
としてはビオサイト(台商(株)製,商品名)等を使用
できる。また、トップコートを施すことにより耐汚染性
能を付加することができる。トップコートの材質として
は自己架橋タイプのアクリル樹脂等である。このような
防カビ性能、耐汚染性能によって壁紙の製品としての付
加価値を高めることができる。[0016]Furthermore, anti-mold performance can be added by adding a fungicide to the formulation of the wallpaper. As a fungicidal agent, Biosite (manufactured by Taisho Co., Ltd., trade name) or the like can be used. Furthermore, stain resistance can be added by applying a top coat. The material of the top coat is a self-crosslinking type acrylic resin or the like. Such anti-mold and anti-stain properties can increase the added value of wallpaper as a product.
【0017】[0017]
【実施例】以下、実施例を示して本発明をさらに具体的
に説明する。EXAMPLES The present invention will be explained in more detail below with reference to Examples.
【0018】裏打紙(坪量75g/m2)に200線−
42μmのベタ版で黒インキ(通常壁紙で使用のVDイ
ンキ,東洋インキ製造(株)製,vis #3ザーンカ
ップ 16秒±1秒)をベタ刷した。その上に下記ペー
ストAを厚み約0.15m/mで塗布しゲル化させたの
ち、下記ペーストBを厚み約0.08m/mで積層しゲ
ル化させた。さらにその上に下記ペーストCを厚み約0
.04m/mで積層し、全体を加熱して発泡せしめたの
ち、表面にガラス接着用の接着剤を塗布し、屈折率1.
9、粒径100μのガラスビーズをふきつけて、本発明
の壁紙を得た。得られた壁紙は、壁紙として必要な適性
はもちろんのこと、広範な角度から画像が鮮明に見える
優れたプロジェクタースクリーン機能をも有するもので
あった。200 wires on backing paper (basis weight 75g/m2)
Black ink (VD ink normally used for wallpaper, manufactured by Toyo Ink Mfg. Co., Ltd., vis #3 Zahn Cup 16 seconds ± 1 second) was printed on a 42 μm solid plate. Paste A below was applied thereon to a thickness of about 0.15 m/m and gelled, and then paste B below was laminated to a thickness of about 0.08 m/m and gelled. Then apply paste C below to a thickness of about 0.
.. After laminating them at a thickness of 0.4 m/m and heating the whole to foam, an adhesive for adhering glass is applied to the surface to give a refractive index of 1.04 m/m.
9. The wallpaper of the present invention was obtained by spraying glass beads with a particle size of 100 μm. The resulting wallpaper not only had the necessary suitability for wallpaper, but also had an excellent projector screen function that allowed images to be clearly seen from a wide range of angles.
【0019】各ペースト層の配合を以下に示す。なお、
部は重量部を表わす。The composition of each paste layer is shown below. In addition,
Parts represent parts by weight.
【0020】
ペーストA 塩化ビニル樹脂
100部
ジオクチルフタレート(D
OP) 55部
安定剤(亜鉛−スズ系)
2部
炭酸カルシウム
100部
カプセル発泡剤
7部
チタン
10部
希釈剤(ミネラルスピ
リット(商品名)) 適量 ペーストB 塩
化ビニル樹脂
100部
DOP
50部
安定剤(前出)
2部
青インキ
0.1部
希釈剤(前出)
適量
ペーストC 塩化ビニル樹脂
100部
DOP
5
0部 安定剤(前出)
2部 パール顔料
20部 希
釈剤(前出)
適量Paste A Vinyl chloride resin
100 copies
Dioctyl phthalate (D
OP) 55 copies
Stabilizer (zinc-tin type)
2nd part
calcium carbonate
100 copies
capsule blowing agent
7th part
Titanium
10 copies
Diluent (mineral spirit (product name)) Appropriate amount Paste B Vinyl chloride resin
100 copies
DOP
50 copies
Stabilizer (mentioned above)
2nd part
blue ink
0.1 part
Diluent (mentioned above)
Appropriate amount
Paste C Vinyl chloride resin
100 copies
DOP
5
0 parts Stabilizer (mentioned above)
Part 2 Pearl pigment
20 parts diluent (mentioned above)
Appropriate amount
【0021】[0021]
【発明の効果】以上詳細に説明したように、本発明によ
れば、壁紙としての適性は勿論のこと、優れたプロジェ
クタースクリーン機能をも併せ持った壁紙が得られ、O
HP等を使用したいときに、わざわざスクリーンを用意
しなくてもすぐにその場で壁材に画像を写し出すことが
でき、その簡単便利であること、効果大なるものである
。[Effects of the Invention] As explained above in detail, according to the present invention, it is possible to obtain a wallpaper that is not only suitable as wallpaper but also has an excellent projector screen function, and
When you want to use a homepage or the like, you can immediately project an image onto the wall material on the spot without having to prepare a screen, which is simple, convenient, and highly effective.
【図1】本発明の壁紙の構成例を示す断面図である。FIG. 1 is a sectional view showing an example of the structure of wallpaper of the present invention.
1 着色基材 2 発泡樹脂層 3 熱可塑性樹脂層 4 透明ビーズ 1 Colored base material 2 Foamed resin layer 3 Thermoplastic resin layer 4 Transparent beads
Claims (4)
樹脂層を有し、その上にパール顔料等を混入した少なく
とも一層の熱可塑性樹脂層を有し、該熱可塑性樹脂層の
最上層の表面に透明ビーズを一面に並べてなることを特
徴とするプロジェクタースクリーン機能を有する壁紙。Claim 1: On a colored base material, there is at least one foamed resin layer, on which there is at least one thermoplastic resin layer mixed with a pearl pigment, etc., and the uppermost layer of the thermoplastic resin layer is A wallpaper with a projector screen function, characterized by transparent beads arranged all over the surface.
樹脂層を有し、その上にパール顔料等を混入した少なく
とも一層の熱可塑性樹脂層を有し、該熱可塑性樹脂層の
最上層の表面に砂目模様のエンボスが施されていること
を特徴とするプロジェクタースクリーン機能を有する壁
紙。2. On a colored base material, there is at least one foamed resin layer, on which there is at least one thermoplastic resin layer mixed with a pearl pigment, etc., and the uppermost layer of the thermoplastic resin layer is A wallpaper that has a projector screen function and is characterized by an embossed grain pattern on its surface.
発泡剤を含有する樹脂層を塗設し、その上に少なくとも
一層のパール顔料等を混入した熱可塑性樹脂層を積層し
、さらに該熱可塑性樹脂層の最上層の表面に透明ビーズ
を一面に並べ必要に応じて上から軽く圧着した後、全体
を加熱して前記発泡剤含有樹脂層を発泡せしめることを
特徴とするプロジェクタースクリーン機能を有する壁紙
の製造方法。3. On a colored base material, at least one resin layer containing a thermal foaming agent is coated, and on top of that, at least one thermoplastic resin layer containing a pearl pigment or the like is laminated, and then the thermal foaming agent is applied. It has a projector screen function characterized in that transparent beads are arranged all over the surface of the uppermost layer of the plastic resin layer and are lightly pressed from above if necessary, and then the whole is heated to foam the foaming agent-containing resin layer. How to make wallpaper.
発泡剤を含有する樹脂層を塗設し、その上に少なくとも
一層のパール顔料等を混入した熱可塑性樹脂層を積層し
た後、全体を加熱して前記発泡剤含有樹脂層を発泡せし
め、さらに最上層の表面に砂目模様のエンボスを施すこ
とを特徴とするプロジェクタースクリーン機能を有する
壁紙の製造方法。4. After coating at least one resin layer containing a heat-foaming agent on a colored base material and laminating thereon at least one thermoplastic resin layer containing a pearl pigment or the like, the whole is coated. A method for producing wallpaper having a projector screen function, which comprises heating the foaming agent-containing resin layer to foam it, and further embossing the surface of the uppermost layer with a grain pattern.