JPH0420034Y2 - - Google Patents
Info
- Publication number
- JPH0420034Y2 JPH0420034Y2 JP1985108731U JP10873185U JPH0420034Y2 JP H0420034 Y2 JPH0420034 Y2 JP H0420034Y2 JP 1985108731 U JP1985108731 U JP 1985108731U JP 10873185 U JP10873185 U JP 10873185U JP H0420034 Y2 JPH0420034 Y2 JP H0420034Y2
- Authority
- JP
- Japan
- Prior art keywords
- film
- sheet
- resistance
- polycarbonate
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
〔産業上の利用分野〕
本考案は、片面に耐紫外線性を有し、かつ必要
に応じて熱線遮断性、耐擦傷性又は耐汚染性から
なる群から選択された１種もしくは２種以上の機
能を付加してなるフイルムを、その反対面に少な
くとも防曇性を有するフイルムを積層接着してな
り、高度の透明性、耐衝撃性を持つポリカーボネ
ートシートであり、特に正弦波状もしくは角波状
の波形状に賦形してなる該シートは、明り取り屋
根材、窓などの外装材に好適な構造部材として利
用されるものである。[Detailed description of the invention] [Industrial application field] The present invention has ultraviolet resistance on one side and, if necessary, a material selected from the group consisting of heat ray blocking properties, scratch resistance, or stain resistance. It is a polycarbonate sheet with a high degree of transparency and impact resistance, which is made by laminating and adhering a film with one or more functions added, and a film with at least an anti-fog property on the opposite side. The sheet formed into a sinusoidal or square wave shape is used as a structural member suitable for exterior materials such as roofing materials and windows.
従来、金属薄板を角波状に賦形した構造部材が
折版波板と呼称されて主に屋根材を中心に広く使
用されて来た。この金属の折版波板は不透明なの
で、例えば、採光といつた目的のためには別途に
明り取り部分を設計、施工する必要があつた。
BACKGROUND ART Conventionally, a structural member made of a thin metal plate shaped into a rectangular wave shape is called a folded corrugated plate and has been widely used mainly for roofing materials. Since this metal folded corrugated plate is opaque, for example, it was necessary to design and construct a separate lighting section for purposes such as daylighting.
最近、FRPを素材とする折版波板が上市され、
明り取り部分の施工が金属の施工と同様の方法で
簡易に行えると言われているが、FRPは、透明
性、耐紫外線性、及び耐衝撃性において尚不充分
であり、美観や構造状からより高度の透明性、耐
紫外線性、及び耐衝撃性に優れた材料が必要とさ
れている。 Recently, folded corrugated plates made of FRP have been put on the market.
It is said that the construction of lighted areas can be easily done using the same method as metal construction, but FRP is still insufficient in terms of transparency, UV resistance, and impact resistance, and it is not suitable for aesthetics and structure. There is a need for materials with a high degree of transparency, UV resistance, and impact resistance.
この要求を満足する素材として、本考案者らは
ポリカーボネートシートを素材とする折版波板を
先に考案し出願した（実開昭58−128019号）。こ
のポリカーボネート折版波板は、耐紫外線性、透
明性、耐衝撃性に優れたものであるが、傷や汚れ
により透明性が劣化すること（表面硬度、耐汚染
性）、夏場の直射日光等による内部の温度上昇
（熱線遮断性）などの面で不充分な場合があり、
更に、高湿下や温度差に基づいて内面が曇る（防
曇性）という不充分点があつた。 As a material that satisfies this requirement, the inventors of the present invention have previously devised and filed an application for a folded corrugated plate made of polycarbonate sheet (Utility Model Application No. 128019/1983). This polycarbonate folded corrugated plate has excellent UV resistance, transparency, and impact resistance, but the transparency may deteriorate due to scratches or dirt (surface hardness, stain resistance), and it may be affected by direct sunlight in summer. may be insufficient in terms of internal temperature rise (heat ray insulation), etc.
Furthermore, there was an unsatisfactory point in that the inner surface became foggy (anti-fogging properties) under high humidity conditions or due to temperature differences.
本考案は、上記の不充分点を解決したポリカー
ボネートシートを提供するために鋭意検討した結
果完成したものである。
The present invention was completed as a result of intensive studies to provide a polycarbonate sheet that solves the above-mentioned inadequacies.
すなわち、本考案は、ポリカーボネート樹脂の
シートの片面に少なくとも耐紫外線性を有するフ
イルムを、反対面に防曇性を有するフイルムを積
層接着してなるポリカーボネート樹脂シートであ
り、好ましい実施態様においては、該ポリカーボ
ネートシートが正弦波状もしくは角波状の波形状
に、積層工程等で賦形してなるものである。 That is, the present invention is a polycarbonate resin sheet formed by laminating and adhering a film having at least ultraviolet ray resistance on one side of a polycarbonate resin sheet and a film having antifogging properties on the other side. A polycarbonate sheet is shaped into a sinusoidal or angular waveform through a lamination process or the like.
まず、本考案の理解を容易にするために、本考
案の一例を図面により説明する。 First, in order to facilitate understanding of the present invention, an example of the present invention will be explained with reference to drawings.
第１図は、本考案のポリカーボネートシートの
層構成を示す断面図であり、第２図乃至第５図は
本考案シートによる種々の波形状の例を示す断面
図である。 FIG. 1 is a cross-sectional view showing the layer structure of the polycarbonate sheet of the present invention, and FIGS. 2 to 5 are cross-sectional views showing examples of various wave shapes formed by the sheet of the present invention.
第１図において、ポリカーボネート樹脂シート
１の上面には、表面に耐汚染性の層３を形成した
耐紫外線性のアクリレート系樹脂フイルム２が積
層され、その反対面には表面に防曇性層５を形成
したアクリレート系樹脂フイルム４が積層された
ものであり、上面を外側とし下側を内側として、
通常は正弦波状又は角波状に賦形した後、使用さ
れ、耐紫外線性、耐汚染性並びに防曇性を有する
ものとして好適に使用されるものである。このよ
うな賦形したシートの一例が第２図である。第２
図は、押し出し工程で上記した２種類のフイルム
をラミネートし、次いで波付ロールを使用して正
弦波板に賦形したものの断面図であり、第３図〜
第５図は、該ラミネートされたポリカーボネート
シートを所望の長さに切断した後、冷間折り曲げ
加工してなる角波板に賦形したものの断面図であ
る。 In FIG. 1, a UV-resistant acrylate resin film 2 with a stain-resistant layer 3 formed on its surface is laminated on the upper surface of a polycarbonate resin sheet 1, and an anti-fog layer 5 on its opposite surface. acrylate resin films 4 are laminated, with the top surface on the outside and the bottom side on the inside.
It is usually used after being shaped into a sinusoidal or angular waveform, and is suitably used as it has ultraviolet ray resistance, stain resistance, and antifogging properties. An example of such a shaped sheet is shown in FIG. Second
The figure is a cross-sectional view of the two types of films described above laminated in an extrusion process and then shaped into a sine wave board using a corrugated roll.
FIG. 5 is a cross-sectional view of the laminated polycarbonate sheet cut into a desired length and cold-folded to form a rectangular corrugated sheet.
以上、本考案を図面を使用して説明したが、本
考案の表面に形成される機能性の層、及び波の形
状は図面に限定されるものではない。 Although the present invention has been described above using the drawings, the functional layer formed on the surface of the present invention and the shape of the waves are not limited to the drawings.
本考案のポリカーボネートシートの素材となる
ポリカーボネート樹脂とは、２，２ビス（４−ヒ
ドロキシフエニル）アルカンや２，２ビス（４−
ヒドロキシ−３，５−ジハロゲノフエニル）アル
カンで代表されるビスフエノール化合物から周知
の方法で製造されたポリカーボネート樹脂を言
い、その重合体骨格中に樹脂族ジオールに由来す
る構造単位、エステル結合を持つ構造単位等がふ
くまれていてもよい。また、厚みは特に制限され
ないが、通常は0.5〜４mm範囲が好適である。 The polycarbonate resin that is the material of the polycarbonate sheet of the present invention is 2,2 bis (4-hydroxyphenyl) alkane or 2,2 bis (4-hydroxyphenyl) alkane.
A polycarbonate resin produced by a well-known method from a bisphenol compound represented by hydroxy-3,5-dihalogenophenyl)alkane, and has structural units derived from resin group diols and ester bonds in its polymer skeleton. It may also include structural units, etc. Further, the thickness is not particularly limited, but a range of 0.5 to 4 mm is usually suitable.
次に、本考案に使用する耐紫外線性を有するフ
イルムは、耐紫外線性に優れた樹脂に紫外線吸収
剤を添加して押し出し法、Ｔダイ法、溶液流延法
その他の方法でフイルムとし、所望により、その
片面に熱線遮断性、耐擦傷性又は耐汚染性からな
る群から選択された１種もしくは２種以上の機能
を付加してなる層を塗装その他の手段で形成して
なるものである。ここに、熱線遮断性の付与は、
赤外線吸収剤を含有する塗料を塗布する方法、赤
外線吸収剤を含有するフイルムをラミネートする
方法その他により；耐擦傷性の付与は、従来公知
の例えば、エポキシ樹脂系、アクリル樹脂系、ア
ミノ樹脂系、ウレタン系、ポリシロキサン系等の
ハードコーテイング剤をコートし、ついで熱また
は紫外線等の手段により硬化することにより；耐
汚染性の付与は、ポリメチルメタクリレート系、
フツ素樹脂系などの塗料やフイルムを塗布もしく
はラミネートする方法によつて各々製造する。 Next, the ultraviolet-resistant film used in the present invention is obtained by adding an ultraviolet absorber to a resin with excellent ultraviolet resistance and making it into a film by an extrusion method, T-die method, solution casting method, or other method. A layer having one or more functions selected from the group consisting of heat ray blocking properties, scratch resistance, and stain resistance is formed on one side by painting or other means. . Here, the provision of heat ray blocking properties is
Scratch resistance can be imparted by applying a paint containing an infrared absorber, laminating a film containing an infrared absorber, or other methods; conventionally known methods such as epoxy resins, acrylic resins, amino resins, etc. By coating with a hard coating agent such as urethane type or polysiloxane type, and then curing by means such as heat or ultraviolet rays;
Each is manufactured by applying or laminating a fluororesin-based paint or film.
また、本考案に使用する防曇性を有するフイル
ムは、界面活性剤及びその他の添加剤類を含有す
る樹脂のフイルム、又はこれをポリカーボネート
樹脂と接着性を有するフイルムに接着もしくはラ
ミネートしたフイルムを使用する方法、ポリカー
ボネート樹脂と積層接着性を有するフイルムに、
ポリビニルアルコール、水溶性アクリレート樹脂
などの塗膜形成性の熱可塑性や熱硬化性樹脂に界
面活性剤などの防曇剤を添加してなる防曇性の塗
料の塗布層を形成する方法などによる。 In addition, the antifogging film used in this invention is a resin film containing surfactants and other additives, or a film in which this is adhered or laminated to a polycarbonate resin and an adhesive film. A method of laminating polycarbonate resin and a film with adhesive properties,
A method of forming a coating layer of an antifogging paint made by adding an antifogging agent such as a surfactant to a film-forming thermoplastic or thermosetting resin such as polyvinyl alcohol or water-soluble acrylate resin.
なお、本考案の好ましい態様においては、平板
であるシートを積層直後の熱曲げ加工乃至積層後
冷間加工により賦形して正弦波板や角波板にする
ものであるので、上記の機能性を付与してなるフ
イルムは、熱曲げ加工や冷間曲げ加工において白
化などの不良が発生しないものが好ましい。この
ようなものとしては、例えば、耐紫外線性を有す
るフイルムとしては、メチルメタクリレートとブ
チルアクリレートの共重合体からなるアクリル系
フイルムに紫外線吸収剤を添加したものが例示さ
れ、市販品としては日本カーバイド(株)製の「ハイ
エス」、鐘淵化学(株)製の「サンジユレン」、三菱レ
ーヨン(株)製の「アクリプレン」等が例示され、防
曇製を有するフイルムとしては、トリアセテート
フイルムを鹸化処理して防曇性を付与し、これと
アクリル系フイルムを積層したものやアクリル系
フイルムに防曇塗料を塗布したものがある。 In a preferred embodiment of the present invention, flat sheets are shaped into sinusoidal or square corrugated plates by heat bending immediately after lamination or cold working after lamination, so that the above functionality is achieved. It is preferable that the film provided with the above-mentioned properties is one that does not cause defects such as whitening during hot bending or cold bending. For example, an example of such a film having UV resistance is an acrylic film made of a copolymer of methyl methacrylate and butyl acrylate to which a UV absorber is added, and a commercially available product is Nippon Carbide. Examples of films with anti-fog properties include ``HiS'' manufactured by Kaneka Co., Ltd., ``Sanjiyuren'' manufactured by Kanekabuchi Chemical Co., Ltd., and ``Acryprene'' manufactured by Mitsubishi Rayon Co., Ltd.; There are some types in which an acrylic film is laminated with an acrylic film, and an acrylic film coated with an anti-fog coating.
ポリカーボネートシートに上記に説明した耐紫
外線性及び防曇性フイルムを積層する方法は、通
常、溶融押し出しした直後の160〜280℃の表面温
度を有するポリカーボネートシートに、上記のフ
イルムを熱圧着するインライン法が好ましいが、
熱プレス法による後積層法によつてもよい。更
に、賦形は、押し出しラミネート工程に引き続い
て熱曲げ加工をする方法、押し出しラミネートし
た後、冷間加工する方法、熱プレスでラミネート
する方法において同時に賦形する方法など、更
に、真空成形、加圧空気成形などでよい。 The method of laminating the UV-resistant and anti-fogging film described above on a polycarbonate sheet is usually an in-line method in which the above-mentioned film is thermocompression bonded to a polycarbonate sheet that has a surface temperature of 160 to 280°C immediately after being melt-extruded. is preferable, but
A post-lamination method using a hot press method may also be used. Furthermore, shaping includes a method of heat bending following the extrusion lamination process, a method of cold working after extrusion lamination, a method of simultaneously shaping during lamination with a hot press, and a method of vacuum forming and processing. Pressurized air molding etc. may be used.
以上の詳細な説明から明確な如く、本考案のポ
リカーボネートシートは、片面が耐紫外線性を他
面が防曇性を有するので、耐久性に優れ、結露防
止などの効果を奏するものであり、更に、熱線遮
断性、耐擦傷性、耐汚染性などの性質も適宜付与
されるので長期に使用に耐える外装材として実用
性の高く、且つ好ましい実施態様によれば、イン
ライン法によつてこのようなポリカーボネートシ
ートが製造されるものであり、生産性等の面から
も実用性のあるものである。
As is clear from the above detailed description, the polycarbonate sheet of the present invention has UV resistance on one side and antifogging property on the other side, so it has excellent durability and has effects such as preventing dew condensation. It is highly practical as an exterior material that can withstand long-term use because it is appropriately imparted with properties such as heat ray blocking properties, scratch resistance, and stain resistance. A polycarbonate sheet is manufactured, and it is practical in terms of productivity and the like.
第１図は本考案のポリカーボネートシートの機
能性層の構成を示す一例の断面図であり、第２
図、第３図、第４図及び第５図は該シートより得
られた賦形された波板、角波板の断面図である。
図中の番号は、それぞれ
１……ポリカーボネート樹脂、２……耐紫外線
性フイルム層、３……耐汚染性層、４……接着用
フイルム、５……防曇性塗膜層を示す。
FIG. 1 is a cross-sectional view of an example of the structure of the functional layer of the polycarbonate sheet of the present invention.
3, 4, and 5 are cross-sectional views of shaped corrugated sheets and square corrugated sheets obtained from the sheet.
The numbers in the figure indicate 1...polycarbonate resin, 2...ultraviolet-resistant film layer, 3...stain-resistant layer, 4...adhesive film, and 5...anti-fog coating layer.
Claims (1)
くとも耐紫外線性を有するフイルムを、反対面
に防曇性を有するフイルムを積層接着してなる
ポリカーボネートシート。 ２ 該ポリカーボネートシートが正弦波状もしく
は角波状の波形状に賦形してなるものであるこ
とを特徴とする実用新案登録請求の範囲第１項
記載のポリカーボネートシート。[Claims for Utility Model Registration] 1. A polycarbonate sheet formed by laminating and adhering at least a UV-resistant film on one side of a polycarbonate resin sheet and an anti-fogging film on the other side. 2. The polycarbonate sheet according to claim 1, wherein the polycarbonate sheet is shaped into a sinusoidal or angular waveform.