JPH04159316A - Composition for shaping - Google Patents
Composition for shapingInfo
- Publication number
- JPH04159316A JPH04159316A JP28340490A JP28340490A JPH04159316A JP H04159316 A JPH04159316 A JP H04159316A JP 28340490 A JP28340490 A JP 28340490A JP 28340490 A JP28340490 A JP 28340490A JP H04159316 A JPH04159316 A JP H04159316A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- weight
- composition
- polyester resin
- marble powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は、彫塑、彫刻、レリーフ、その他の美術工芸品
等の造形物、或いは建築物の内装や外装に用いる各種の
造形部材、また、看板や標識等に利用される造形物など
を製造するに用いられる造形用組成物に関する。[Detailed Description of the Invention] [Industrial Field of Application] The present invention is applicable to sculptures, sculptures, reliefs, other arts and crafts, and various shaped members used for the interior and exterior of buildings. The present invention relates to a modeling composition that is used for producing shaped objects such as signboards and signs.
［従来の技術〕
従来、彫刻などの美術品を作成するための素材として大
理石などの石材、木材、硬質プラスチックス、ブロンズ
等が用いられているが、美麗で寸法の大きなものは極め
て高価である。[Conventional technology] Traditionally, stones such as marble, wood, hard plastics, bronze, etc. have been used as materials for creating works of art such as sculptures, but beautiful and large-sized items are extremely expensive. .
また、建築物の内装や外装に大理石の板を用いることも
行われているが、これまた産出量が限られていて高価で
ある。Marble plates are also used for the interior and exterior of buildings, but they are also expensive and produced in limited quantities.
そのため、この様な天然大理石に代わるものとして、大
理石粉を白色セメントで結合した人造大理石や、各種の
石粉や顔料などを不飽和ポリエステル樹脂で結合した模
造大理石などが提案され、用いられている。Therefore, as alternatives to such natural marble, artificial marble, which is made by bonding marble powder with white cement, and imitation marble, which is made by bonding various stone powders and pigments with unsaturated polyester resin, have been proposed and used.
これら従来の造形用素材を用いて作成した彫刻などの造
形物は、明るい環境下では鑑貰することができるが、暗
（なると照明をする必要がある。Sculptures and other objects created using these conventional modeling materials can be viewed in bright environments, but in the dark (when it is dark), they must be illuminated.
しかし、野外等では通常用いられている点光源による照
明は、造形物の微妙な凹凸を鑑賞することができず、ま
た、多数の面光源を用いた散光照明は設備費が嵩んで不
経済である。However, the point light source lighting that is commonly used outdoors does not allow you to appreciate the subtle unevenness of objects, and the diffused lighting that uses multiple surface light sources is uneconomical due to high equipment costs. be.
そこで本発明は、夜間などの暗い環境下でも容易に鑑賞
することができ、しかも極めて経済的な照明設備で足り
るような特殊な造形物を得ることを目的としたものであ
り、かかる造形物を作成するに通した新規な造形用組成
物を提供しようとするものである。Therefore, the purpose of the present invention is to obtain a special shaped object that can be easily viewed even in a dark environment such as at night, and that requires extremely economical lighting equipment. The present invention aims to provide a novel modeling composition that is easy to create.
本発明による造形用組成物は、大理石粉４０〜５５重量
部、蓄光性顔料５〜２５重量部、および不飽和ポリエス
テル樹脂３５〜５５重量部ならびに有効量の増粘剤を含
有するもの、または、大理石粉４５〜５０重量部、蓄光
性顔料２０〜４０重量部、および白色セメント２０〜４
０重量部ならびに有効量の照度調節剤と凝結用水を含有
するものである。The modeling composition according to the present invention contains 40 to 55 parts by weight of marble powder, 5 to 25 parts by weight of luminescent pigment, and 35 to 55 parts by weight of unsaturated polyester resin and an effective amount of a thickener, or 45-50 parts by weight of marble powder, 20-40 parts by weight of luminescent pigment, and 20-4 parts by weight of white cement
It contains 0 parts by weight as well as effective amounts of an illuminance control agent and water for coagulation.
本発明の組成物は、骨材として大理石粉と蓄光性顔料と
を用い、結合剤として不飽和ポリエステル樹脂または白
色セメントを配合したことを基本とするものであり、こ
れに有効量の増粘剤または照度調節剤を配合してなるも
のである。The composition of the present invention is based on marble powder and a luminescent pigment as aggregates, unsaturated polyester resin or white cement as a binder, and an effective amount of a thickener. Alternatively, it may contain an illuminance control agent.
これらの組成物のうち、白色セメントを結合剤とし７た
ものには当然にセメント凝結用の水が配合されるが、こ
の水は配合物の可塑性を調節するために理論量よりも多
めに配合されることが望ましい。Of these compositions, water for cement setting is naturally added to those using white cement as a binder, but this water is added in a larger amount than the theoretical amount in order to adjust the plasticity of the mixture. It is desirable that
本発明の組成物中で用いられる大理石粉の配合量は、少
な過ぎると造形物の質感が失われ、また配合量が多すぎ
ると蓄光性顔料の効果を滅するので好ましくない。If the amount of marble powder used in the composition of the present invention is too small, the texture of the object will be lost, and if it is too large, the effect of the luminescent pigment will be lost, so it is not preferable.
一方、蓄光性顔料の配合量は、不飽和ポリエステル樹脂
と共に用いる場合は最低５重量部以上で美しい発光が得
られるが、多過ぎては経済的でないから２５重量部程度
までで充分である。On the other hand, when using the luminous pigment in combination with an unsaturated polyester resin, beautiful luminescence can be obtained with a minimum of 5 parts by weight or more, but too much is not economical, so it is sufficient to use up to about 25 parts by weight.
これに対し、白色セメントと共に用いる場合は最低２０
重量部以上４０重量部程度が望ましい。In contrast, when used with white cement, the minimum
The amount is desirably at least 40 parts by weight.
このような本発明の組成物は、上記のような基本配合成
分の他に、必要に応じて着色のための顔料や抗酸化側、
或いは、紫外線吸収剤などの配合剤を含有していてもよ
い。In addition to the above-mentioned basic ingredients, the composition of the present invention may optionally contain pigments for coloring, antioxidants,
Alternatively, it may contain a compounding agent such as an ultraviolet absorber.
本発明の造形用組成物を用いて成形し、また、適宜に彫
刻等の加工をした造形物は、外部から、または、その内
部もしくはその裏側などから適宜の光線で照射した後消
灯すると、全体が透明感のある発光をするので、暗い環
境下においても造形物が浮かび上がって見え、極めて美
しい。A model that has been molded using the modeling composition of the present invention and has been appropriately processed, such as engraving, is irradiated with an appropriate light beam from the outside, inside, or from the back side of the object, and then the light is turned off. Because it emits a transparent light, the objects stand out even in dark environments, making them extremely beautiful.
〔実施例１〕
白色大理石粉４０重量部、硫化亜鉛系蓄光性顔料（シン
ロイヒ、ＬＣ−ＣＩＡ）８重量部、増粘剤（ヱロジール
）２重量部、バリウム系安定剤０゜２重量部を、不飽和
ポリエステル樹脂４０重量部と配合して流動性の組成物
を得た。[Example 1] 40 parts by weight of white marble powder, 8 parts by weight of zinc sulfide luminous pigment (Shinroihi, LC-CIA), 2 parts by weight of thickener (Erosil), 0.2 parts by weight of barium stabilizer, A fluid composition was obtained by blending with 40 parts by weight of an unsaturated polyester resin.
次いで、筒状の型の中央に空洞形状の芯材を固定し、前
記の組成物を型と空洞形状の芯材の間に流し込んで硬化
させた。Next, a hollow core material was fixed in the center of a cylindrical mold, and the composition was poured between the mold and the hollow core material and cured.
こうして成形した硬化物は、型から取り出した後外面に
彫刻を施すが、この造形物の壁の厚さは５０〜８０厘程
度であった。After the cured product thus molded was taken out of the mold, the outer surface was engraved, and the wall thickness of this molded product was approximately 50 to 80 rin.
更に、この造形物の表面にシリコーン系防水塗料（例え
ば、東亜ペイント、トアハソスイシーラー）及び、弗素
樹脂塗料（例えば、東亜ペイント、ニューガーメッｌ−
＃７０００）を順次塗布した。Furthermore, the surface of this model is coated with a silicone-based waterproof paint (e.g. Toa Paint, Toa Hasosui Sealer) and a fluororesin paint (e.g. Toa Paint, New Garmell).
#7000) were applied sequentially.
この様にして作成した造形物は、昼間の太陽光及び明る
い散光の下では大理石と殆ど同様の外観を有しており、
また、暗い環境下では外部に設けた紫外線ランプを所望
時間点灯して照射した後消灯することによって、全体が
深みのある青白い発光をし、空間に浮かんでいるように
見えた。The objects created in this way have an appearance almost similar to marble under daytime sunlight and bright diffused light.
In addition, in a dark environment, by turning on an external ultraviolet lamp for a desired period of time, then turning off the light, the entire structure emitted a deep blue-white light, making it appear as if it was floating in space.
更に、この造形物を屋外におき、紫外線ランプによる間
欠的な繰り返し照明を行ったところ、息づくような周期
的な発光をし、幻想的な美しさが惑じられた。Furthermore, when this sculpture was placed outdoors and illuminated intermittently and repeatedly with an ultraviolet lamp, it emitted periodic light that seemed to be alive, giving it a mystical beauty.
また、この様な発光は、１年間の屋外曝露の後でも全く
変化が見られなかった。Moreover, no change was observed in such luminescence even after one year of outdoor exposure.
〔実施例２］
白色大理石粉５０重量部、硫化亜鉛系蓄光性顔料３５重
量部、白色セメント２５重量部、減水剤０．１重量部と
水１５重量部の混合液を配合して、流動性の組成物を得
た。[Example 2] A mixture of 50 parts by weight of white marble powder, 35 parts by weight of zinc sulfide luminous pigment, 25 parts by weight of white cement, 0.1 part by weight of water reducing agent and 15 parts by weight of water was blended to improve fluidity. A composition was obtained.
この組成物を実施例１と同様の手順で成形し、同様に直
付けして造形物を作った。This composition was molded in the same manner as in Example 1, and directly applied in the same manner to create a shaped article.
この造形物は重量感があり、高い強度を有するものであ
り、殆ど同様な発光性を示した。This shaped object had a heavy feel and high strength, and exhibited almost the same luminescence.
本発明の造形用組成物は、大理石粉と蓄光性顔料とを不
飽和ポリエステル樹脂又は白色セメントによって結合し
たものであるから、硬化造形して得た造形物は光エネル
ギーを吸収して柔らかな発光を継続するものであり、観
察者に幻想的な印象を与えるので芸術的な彫刻や工芸品
、或いは建築用その他構造物構築のだめの部材、その他
者板や標識など種々の用途に利用できる効果がある。Since the modeling composition of the present invention combines marble powder and luminescent pigment with unsaturated polyester resin or white cement, the shaped object obtained by hardening and modeling absorbs light energy and emits soft light. Since it gives a fantastic impression to the observer, it can be used for various purposes such as artistic sculptures and crafts, construction materials for architecture and other structures, and other purposes such as boards and signs. be.
Claims (2)
重量部、および不飽和ポリエステル樹脂３５〜５５重量
部ならびに有効量の増粘剤を含有することを特徴とする
造形用組成物。(1) Marble powder 40-55 parts by weight, luminous pigment 5-25 parts
and 35 to 55 parts by weight of an unsaturated polyester resin and an effective amount of a thickener.
０重量部、および白色セメント２０〜４０重量部ならび
に有効量の貼度調節剤と凝結用水を含有することを特徴
とする造形用組成物。(2) Marble powder 45-50 parts by weight, luminous pigment 20-4
1. A modeling composition comprising 0 parts by weight of white cement, 20 to 40 parts by weight of white cement, and effective amounts of a patchiness regulator and setting water.