JPH04153255A - Unsaturated polyester resin molding material - Google Patents
Unsaturated polyester resin molding materialInfo
- Publication number
- JPH04153255A JPH04153255A JP27729390A JP27729390A JPH04153255A JP H04153255 A JPH04153255 A JP H04153255A JP 27729390 A JP27729390 A JP 27729390A JP 27729390 A JP27729390 A JP 27729390A JP H04153255 A JPH04153255 A JP H04153255A
- Authority
- JP
- Japan
- Prior art keywords
- polyester resin
- unsaturated polyester
- molding material
- resin molding
- additives
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
[発明の目的]
(産業上の利用分野)
本発明は、成形性、機械的強度、防錆性に優れた、不飽
和ポリエステル樹脂成形材料に関する。Detailed Description of the Invention [Object of the Invention] (Industrial Application Field) The present invention relates to an unsaturated polyester resin molding material that has excellent moldability, mechanical strength, and rust prevention properties.
(従来の技術]
従来、不飽和ポリエステル樹脂成形材料は、その優れた
特性から、電気機器部品、41I遣部品等に広く使用さ
れている。 また、特に好適な使用例として、密閉型ま
たは半密閉型の電動機の固定子コイルを成形することが
行われていた。(Prior Art) Conventionally, unsaturated polyester resin molding materials have been widely used for electrical equipment parts, 41I parts, etc. due to their excellent properties. molding of stator coils for electric motors.
しかし、これらの用途は金属と接する部分が多く、発錆
の問題があった。 すなわち、電気機器部品、構造部品
に使用した場合には金属部分の発錆によるmsを起こし
、また電動機部品に使用した場合には軸受(ボールベア
リング)に発錆し、回転不良やロックを起こす等の問題
があった。However, many of these applications come into contact with metal, which poses the problem of rust. In other words, when used in electrical equipment parts and structural parts, metal parts will rust and cause ms, and when used in electric motor parts, bearings (ball bearings) will rust, causing rotation failure and locking. There was a problem.
これらの問題を解決するため、種々の添加剤を配合する
ことが試みられたが、成形性や機械的強度とのバランス
が悪く満足すべきものではなく、成形性、機械的強度と
ともに防錆性に優れた成形材料の開発が要望されていた
。In order to solve these problems, attempts have been made to incorporate various additives, but the result is unsatisfactory due to poor balance with formability and mechanical strength, and the rust prevention properties are not good in addition to formability and mechanical strength. There was a demand for the development of superior molding materials.
(発明が解決しようとする課B)
本発明は、上記の事情にfみてなされたもので、成形性
、機械的強度に優れ、かっ発錆のない不飽和ポリエステ
ル樹脂成形材料を提供しようとするものである。(Problem B to be Solved by the Invention) The present invention has been made in view of the above circumstances, and aims to provide an unsaturated polyester resin molding material that has excellent moldability and mechanical strength and is free from rusting. It is something.
[発明の構成〕
(8題を解決するための手段)
本発明者らは、上記の目的を達成しようと鋭意研究を重
ねた結果、後述する成形材料が上記目的を達成すること
を見いだし、本発明を完成したものである。[Structure of the Invention] (Means for Solving the Eight Problems) As a result of intensive research to achieve the above object, the present inventors discovered that the molding material described below achieves the above object, and the present inventors have developed the present invention. It is a completed invention.
すなわち、本発明は、
不飽和ポリエステル樹脂、架橋剤、充填材および添加剤
を配合してなる不飽和ポリエステル樹脂成形材料におい
て、添加剤として気化防錆剤を、成形材料に対して0,
03〜1.0重1%含有してなることを特徴とする不飽
和ポリエステル樹脂成形材料である。That is, the present invention provides an unsaturated polyester resin molding material containing an unsaturated polyester resin, a crosslinking agent, a filler, and an additive.
This is an unsaturated polyester resin molding material characterized by containing 1% by weight of 03-1.0.
以下、本発明について説明する。The present invention will be explained below.
本発明に用いる不飽和ポリエステル樹脂は、特に限定さ
れるものではなく、通常成形材料として使用できる不飽
和ポリエステル樹脂であれば広く使用することができる
。The unsaturated polyester resin used in the present invention is not particularly limited, and a wide variety of unsaturated polyester resins that can be used as ordinary molding materials can be used.
本発明に用いる架橋剤としては、スチレンモノマー暮、
常温液状のもの又は常温固体のモノマーが用いられ、特
に限定されるものではない。The crosslinking agent used in the present invention includes styrene monomer,
Monomers that are liquid at room temperature or solid at room temperature are used, and are not particularly limited.
本発明に用いる充填材としては、炭酸カルシウム、クレ
ー、シリカ、タルク等であり、必要によリガラス繊維や
ビニロン繊維等も配合することができる。 これらの充
填材は特に限定されるものではなく、また単独、もしく
は2種以上混合して使用することができる。Fillers used in the present invention include calcium carbonate, clay, silica, talc, etc., and if necessary, glass fibers, vinylon fibers, etc. can also be blended. These fillers are not particularly limited and can be used alone or in combination of two or more.
本発明に用いる気化防錆剤としては、例えばキレスガー
ドC(日本化学産業社製、商品名)、タイアナ(菱江化
学社製、商品名)、T、V、1(キレスト化学社製、商
品名)、NP−20(日本石油社製、商品名)、フェロ
ガード100E(米国ロンコラボラトリーズ社製、商品
名)、ストアセイフ(大洋液化カス社製、商品名)、ゼ
ラスト(大洋液化カス社製、商品名)、更に気化防錆性
のある離形剤や気化防錆剤を含有した離型剤等が挙げら
れる。 気化防錆剤の配合割合は、成形材料に対して0
.03〜1.Ofi量%含有するように配合することが
望ましい、 配合割合が003重量%未溝では、十分な
防錆効果が得られず、また、 1.0重量%を超えると
成形性か悪<、mw的強度か低下し好ましくない。Examples of the vaporized rust preventive used in the present invention include Killesgard C (manufactured by Nihon Kagaku Sangyo Co., Ltd., trade name), Taiana (manufactured by Ryoe Chemical Co., Ltd., trade name), T, V, 1 (manufactured by Kirest Kagaku Co., Ltd., trade name). , NP-20 (manufactured by Nippon Oil Co., Ltd., trade name), Ferroguard 100E (manufactured by Ronco Laboratories, Inc., USA, trade name), Storesafe (manufactured by Taiyo Liquefaction Kass Co., Ltd., trade name), Zelast (manufactured by Taiyo Kasshu Co., Ltd., product name) Further examples include mold release agents with vaporization rust prevention properties and mold release agents containing vaporization rust prevention agents. The blending ratio of the vaporized rust preventive agent to the molding material is 0.
.. 03-1. It is preferable to mix it so that it contains 0.03% by weight.If the blending ratio is 0.3% by weight without grooves, a sufficient rust prevention effect cannot be obtained, and if it exceeds 1.0% by weight, the moldability will be poor. This is undesirable as it reduces the strength of the target.
気化防錆剤のほかの添加剤として、低収縮剤、硬化触媒
、離型剤、着色剤又は必要に応じて界面活性剤等を添加
配合するこ、とができる、 低収縮剤としては、ポリス
チレン、ポリメチルメタクリレート、飽和ポリエステル
等の一般的な熱可塑性樹脂が使用される。 また硬化触
媒としては、例えばアルデヒドパーオキサイド、ジアシ
ルパーオキサイド、ハイドロパーオキサイド、アルキル
パーエステル等が挙げられ、適宜選択して使用すること
ができる。As additives other than the vaporized rust preventive agent, low shrinkage agents, curing catalysts, mold release agents, coloring agents, surfactants, etc. can be added and blended as necessary.As low shrinkage agents, polystyrene Common thermoplastic resins such as , polymethyl methacrylate, and saturated polyester are used. Examples of the curing catalyst include aldehyde peroxide, diacyl peroxide, hydroperoxide, and alkyl perester, which can be appropriately selected and used.
本発明の不飽和ポリエステル樹脂成形材料は、不飽和ポ
リエステル樹脂、架橋剤、充填材、それに気化防錆剤、
その他低収a荊、離型剤、硬化触媒等の添加剤を加えて
ニーダ−で混練して容易に製造することができる。 こ
うして得られた不飽和ポリエステル樹脂成形材料は圧縮
成形、押出成形、トランスファー成形、射出成形等によ
って加熱加圧成形し、電気機器部品、411遺部品、固
定子コイル等の成形品とすることができる4(作用)
本発明の不飽和ポリエステル樹脂成形材料は、一定量の
気化防錆剤を使用することによって優れた成形性、機械
的強度を損なうことなく防錆効果を付与することができ
たものである。The unsaturated polyester resin molding material of the present invention comprises an unsaturated polyester resin, a crosslinking agent, a filler, and a vaporized rust preventive agent.
It can be easily produced by adding other additives such as low-yield agar, mold release agent, curing catalyst, etc. and kneading in a kneader. The unsaturated polyester resin molding material thus obtained can be molded under heat and pressure by compression molding, extrusion molding, transfer molding, injection molding, etc., and can be made into molded products such as electrical equipment parts, 411 parts, stator coils, etc. 4 (Function) The unsaturated polyester resin molding material of the present invention is capable of imparting rust prevention effects without impairing excellent moldability and mechanical strength by using a certain amount of vaporized rust preventive agent. It is.
(実施例) 以下、本発明を実施例によって説明する。(Example) Hereinafter, the present invention will be explained by examples.
実施例 1〜3
第1表に示した組成の各材料を常法によりニーダ−で混
練して、実施例1〜3の不飽和ポリエステル樹脂成形材
料を製造した。Examples 1 to 3 Unsaturated polyester resin molding materials of Examples 1 to 3 were produced by kneading each material having the composition shown in Table 1 using a kneader in a conventional manner.
比較例 1〜2
実施例と同様にして第1表に示した組成の各材料をニー
ダ−で混練して、比較例1〜2の不飽和ポリエステル樹
脂成形材t4を製造した。Comparative Examples 1-2 Unsaturated polyester resin molded materials t4 of Comparative Examples 1-2 were produced by kneading each material having the composition shown in Table 1 in a kneader in the same manner as in Examples.
実施例1〜3及び比較例1〜2で製造した不飽和ポリエ
ステル樹脂成形材料を用いて成形性、曲げ強さ、発錆性
を試験したので、その結果を第1表に示した。 本発明
はいずれも優れており、本発明の効果を確認することが
できた。The unsaturated polyester resin molding materials produced in Examples 1 to 3 and Comparative Examples 1 to 2 were tested for moldability, bending strength, and rust resistance, and the results are shown in Table 1. The present invention was excellent in all cases, and the effects of the present invention could be confirmed.
[発明の効果]
以上の説明および第1表から明らかなように、本発明の
不飽和ポリエステル樹脂成形材料番よ、成形性、機械的
強度に優れており、かつ発錆のな髪)もので、電気機器
部品、III遣部品、密閉用モーlレドに好適なもので
ある。[Effects of the Invention] As is clear from the above explanation and Table 1, the unsaturated polyester resin molding material of the present invention has excellent moldability and mechanical strength, and is free from rust. It is suitable for electrical equipment parts, III parts, and sealing molds.
特許出願人 東芝ケミカル株式会社(p4.1□、代理
人 1”−t WEB i= )’+、1’、
G′ ダPatent applicant Toshiba Chemical Corporation (p4.1□, agent 1”-t WEB i= )'+, 1',
G' da
Claims (1)
加剤を配合してなる不飽和ポリエステル樹脂成形材料に
おいて、添加剤として気化防錆剤を、成形材料に対して
0.03〜1.0重量%含有してなることを特徴とする
不飽和ポリエステル樹脂成形材料。1. In an unsaturated polyester resin molding material containing an unsaturated polyester resin, a crosslinking agent, a filler, and an additive, a vaporized rust preventive agent is added as an additive in an amount of 0.03 to 1.0% by weight based on the molding material. An unsaturated polyester resin molding material characterized by containing: