JPH039292A - Dial plate for clock and its production - Google Patents
Dial plate for clock and its productionInfo
- Publication number
- JPH039292A JPH039292A JP14390789A JP14390789A JPH039292A JP H039292 A JPH039292 A JP H039292A JP 14390789 A JP14390789 A JP 14390789A JP 14390789 A JP14390789 A JP 14390789A JP H039292 A JPH039292 A JP H039292A
- Authority
- JP
- Japan
- Prior art keywords
- plating layer
- layer
- forming
- inorganic
- mask
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〈産業上の利用分野〉
本発明は時計用文字板とその製造方法に関するものであ
り、特にメッキにより形成された時字、マークあるいは
模様等のパターンを着色したものに関する。[Detailed Description of the Invention] <Industrial Application Field> The present invention relates to a watch dial and a method for manufacturing the same, and particularly relates to a watch dial with colored patterns such as hour letters, marks, or patterns formed by plating. .
〈従来の技術〉
近年、部分的にメッキを厚くすることにより、時字、マ
ーク、ブランド名、模様等のパターンを形成した時計用
文字板が提案されている。この手法による文字板は、微
細な表現ができ、又立体感があり、更に金属光沢を有す
る高級感のある文字板を提供することができる。<Prior Art> In recent years, clock dials have been proposed in which patterns such as hour characters, marks, brand names, patterns, etc. are formed by partially thickening the plating. The dial plate produced by this method can provide a fine expression, a three-dimensional effect, and a luxurious-looking dial plate with a metallic luster.
従来の文字板においては、ニッケルや銅等で肉盛りメッ
キをし、更に仕上げメッキを施してパターンを形成して
いた。In conventional dials, patterns were formed by overlaying with nickel, copper, etc., and then applying finishing plating.
〈発明が解決しようとする課題〉
上記従来の文字板における仕上げメッキに対しては、耐
候性や肉盛りメッキとの密着性等が要求される。特に表
面に保護被膜がない文字板においては、保護被膜がある
ものに比べて数段高い耐食性等が要求される。<Problems to be Solved by the Invention> Weather resistance, adhesion to overlay plating, etc. are required for the finish plating on the conventional dial plate. In particular, a dial without a protective coating on its surface is required to have much higher corrosion resistance than a dial with a protective coating.
このため、この仕上げメッキとしては物質的に安定し、
上記条件を満足させる金やロジウムに限定されていた。For this reason, this finish plating is materially stable,
It was limited to gold and rhodium that met the above conditions.
このように材質が限定されるのでその色調も限定されて
しまうという課題があった。Since the materials are limited in this way, there is a problem in that the color tone is also limited.
又、金、ロジウム以外の仕上げメッキで着色した場合に
は、色ムラが生じたり、経時変化による色調変化が起こ
る等安定性に欠け、文字板として商品化することができ
なかった。Furthermore, when colored with finish plating other than gold or rhodium, it lacks stability, such as color unevenness or color change due to aging, and cannot be commercialized as a dial.
本発明の目的は、耐候性が良く、色調変化や色ムラのな
い金属光沢を有する様々な色調のパターンを有する時計
用文字板及びその製造方法を提供することにある。An object of the present invention is to provide a timepiece dial plate having patterns in various tones, which has good weather resistance, has a metallic luster with no color change or color unevenness, and a method for manufacturing the same.
く課題を解決するための手段〉
本発明の時計用文字板は、透明塗膜上にパターンが形成
されるものと、パターンの上に透明層が形成されるもの
がある。前者は基板上の有色層の更に上に設けられた透
明塗膜上に導電膜を形成してパターンを厚メッキ層によ
り形成し、この厚メッキ層上に気相法により無機被膜を
形成してなるものである。Means for Solving the Problems The timepiece dials of the present invention include those in which a pattern is formed on a transparent coating film, and those in which a transparent layer is formed on the pattern. In the former method, a conductive film is formed on a transparent coating film provided above a colored layer on a substrate, a pattern is formed by a thick plating layer, and an inorganic film is formed on this thick plating layer by a vapor phase method. It is what it is.
又、後者は基板上の基地メッキ層の上にパターンを厚メ
ッキ層で形成し、更にその上に気相法により無機被膜を
設け、これを透明層で被覆してなるものである。In the latter case, a pattern is formed as a thick plating layer on a base plating layer on a substrate, an inorganic coating is further provided on the thick plating layer by a vapor phase method, and this is covered with a transparent layer.
一方、前者の時計用文字板は基板上に有色層を形成する
工程と、その上に透明樹脂を塗布して透明塗膜を形成す
る工程と、その上に、導電層を蒸着にて形成する工程と
、この導電層をマスクにより部分的に被覆する工程と、
マスクされていない導電層上に厚メッキを施す工程と、
その上に気相法により無機被膜を形成する工程と、マス
クと被覆されている導電層とマスク上に形成された無機
被膜を除去する工程とを経て製造される。On the other hand, the former type of watch dial consists of a process of forming a colored layer on a substrate, a process of coating a transparent resin on it to form a transparent coating film, and a process of forming a conductive layer on top of it by vapor deposition. a step of partially covering the conductive layer with a mask;
A process of applying thick plating on the unmasked conductive layer,
It is manufactured through a step of forming an inorganic film thereon by a vapor phase method, and a step of removing the mask, the conductive layer covered thereon, and the inorganic film formed on the mask.
又、後者の時計用文字板は、基板上に基地メッキ層を形
成する工程と、この基地メッキ層をマスクにより部分的
に被覆する工程と、マスクされていない基地メッキ層上
に厚メッキを施す工程と、その上に気相法により無機被
膜を形成する工程と、マスク及びマスク上の無機被膜を
除去する工程と、透明層を形成する工程とを経て製造さ
れる。The latter type of watch face plate is produced by forming a base plating layer on a substrate, partially covering this base plating layer with a mask, and applying thick plating on the unmasked base plating layer. It is manufactured through a process of forming an inorganic film thereon by a vapor phase method, a process of removing the mask and the inorganic film on the mask, and a process of forming a transparent layer.
く作用〉
本発明における無機被膜は、それ自体による着色あるい
はこの無機被膜の光の干渉による着色作用がある。特に
、本発明におけるパターンは厚メッキにより盛り上がっ
て形成されているので、無機被膜による色がより強調さ
れて表現される。Effect> The inorganic coating in the present invention has a coloring effect by itself or by the interference of light of this inorganic coating. In particular, since the pattern in the present invention is formed by thick plating in a raised manner, the color of the inorganic coating is more emphasized and expressed.
〈実施例〉 以下図面に基づいて本発明の詳細な説明する。<Example> The present invention will be described in detail below based on the drawings.
第１図は本発明の一実施例に係る時計用文字板を示す断
面図である。FIG. 1 is a sectional view showing a timepiece dial according to an embodiment of the present invention.
１は基板であり、その表面には基板１を保護するＮｉ等
からなる基地メッキ層２が設けられている。Reference numeral 1 denotes a substrate, and a base plating layer 2 made of Ni or the like is provided on the surface of the substrate 1 to protect the substrate 1.
３は基地メッキ層２上に設けられている透明樹脂からな
る透明塗膜であり、その上面にはＡｕＣｕ等からなる導
電膜４が部分的に設けられている。3 is a transparent coating film made of a transparent resin provided on the base plating layer 2, and a conductive film 4 made of AuCu or the like is partially provided on its upper surface.
５は導電膜４上に設けられ時字、マーク、模様等のパタ
ーンを形成するＮｉ、Ｃｕ等からなる厚メッキ層である
。Reference numeral 5 denotes a thick plating layer made of Ni, Cu, etc., which is provided on the conductive film 4 and forms patterns such as hour characters, marks, patterns, etc.
６は厚メッキ層５上に設けられた無機被膜であり、金属
、酸化物、窒化物あるいはぶつ化物の単層又は無機被膜
の２以上の層からなるものである。Reference numeral 6 denotes an inorganic coating provided on the thick plating layer 5, which is composed of a single layer of metal, oxide, nitride, or hybrid, or two or more layers of inorganic coatings.
この無機被膜６を２層以上にしてその光の干渉を利用し
て着色する場合には、Ｃｒ−Ｃｒ２０３−Ｃｒ、Ａｕ−
ＭｇＦ２ 、Ｃｒ−３ｉ０２等の各組み合わせで積層す
る。例えば抵抗加熱によりＣｒ−Ｃｒ２０３−Ｃｒの３
層からなる無機被膜６を形成すると、第１層のＣｒと第
２層のＣｒ２Ｏ３により色を出し、第３ ＮＣｒにより
被膜の保護・色調整をする。これらの各層の厚さを変え
て組み合わせると様々な金属光沢のある色調を出すこと
ができる。When this inorganic coating 6 is made of two or more layers and colored using the interference of light, Cr-Cr203-Cr, Au-
Each combination of MgF2, Cr-3i02, etc. is laminated. For example, by resistance heating, 3 of Cr-Cr203-Cr
When the inorganic coating 6 consisting of layers is formed, the first layer of Cr and the second layer of Cr2O3 produce color, and the third NCr protects and adjusts the color of the coating. By changing the thickness of each of these layers and combining them, various metallic luster tones can be produced.
この文字板においては、パターンが盛り上がっているだ
けでなく、その表面が無機被膜６の色あるいはその干渉
による色に着色されている。This dial plate not only has a raised pattern, but also has its surface colored in the color of the inorganic coating 6 or its interference color.
次に第２図乃至第９図に基づいて第１図に示す時計用文
字板の製造方法を説明する。Next, a method for manufacturing the timepiece dial shown in FIG. 1 will be explained based on FIGS. 2 to 9.
はじめに、第２図に示す基板１の表面に目付けをして第
３図に示すようにする。First, the surface area of the substrate 1 shown in FIG. 2 is given a basis weight as shown in FIG. 3.
次に、この基板１の表面にＮｉメッキを施して第４図に
示すように基地メッキ層２を形成する。Next, the surface of this substrate 1 is plated with Ni to form a base plating layer 2 as shown in FIG.
更に第５図に示すように、基地メッキ２上に透明樹脂を
塗布して、これが硬化した後、その上面を研磨して透明
塗膜３を形成する。Further, as shown in FIG. 5, a transparent resin is applied onto the base plating 2, and after this is cured, the upper surface thereof is polished to form a transparent coating film 3.
その後、この透明塗膜３の上面全面にＡｕ、ＣＵ等を蒸
着させて第６図に示すような導電Ｍ４を形成する。Thereafter, Au, CU, etc. are deposited on the entire upper surface of the transparent coating film 3 to form a conductive layer M4 as shown in FIG.
次に第７図に示すようにこの導電Ｍ４上の所定の位置に
フォトレジスト等のマスク７を形成し、更に、Ｎｉ、Ｃ
ｕメッキ等により厚メッキ層５を形成する。このときに
、この厚メッキＮ５の上に更に仕上げメッキを施しても
良い。Next, as shown in FIG. 7, a mask 7 made of photoresist or the like is formed at a predetermined position on the conductive M4, and Ni, C
A thick plating layer 5 is formed by U plating or the like. At this time, finish plating may be further applied on this thick plating N5.
その後、第８図に示すように厚メッキ層らとマスク７の
上に真空蒸着、ＣＶＤ、イオンブレーティング、スパッ
タリング等の気相法により無機被膜６の単層又は多層を
形成する。Thereafter, as shown in FIG. 8, a single or multilayer inorganic coating 6 is formed on the thick plating layer and the mask 7 by a vapor phase method such as vacuum evaporation, CVD, ion blasting, or sputtering.
次に第９図に示すように、無機被膜６と共にマスク７を
ｌ（Ｉ ｍする。このときに厚メッキ層５上に付着して
いる無機被膜６は厚メッキ層５に密着しているため厚メ
ッキ層５上に残る。Next, as shown in FIG. 9, the mask 7 is coated with the inorganic coating 6. At this time, since the inorganic coating 6 adhering to the thick plating layer 5 is in close contact with the thick plating layer 5, It remains on the thick plating layer 5.
更に導電膜４をエツチングにより除去し、文字板は完成
する。Furthermore, the conductive film 4 is removed by etching, and the dial plate is completed.
尚、この無機被膜はエツチング液で溶解しないものであ
ることが必要である。Incidentally, it is necessary that this inorganic film is not dissolved by the etching solution.
第１０図は本発明の池の実施例に係る時計用文字板を示
す断面図である。FIG. 10 is a sectional view showing a timepiece dial according to an embodiment of the present invention.
１１は基板、１２はその表面に設けられた基地メッキ層
、１５はその上に設けられたパターンを形成する厚メッ
キ層、１６はその上に設けられた無機被膜、１３は基地
メッキ層１２と無機被膜１６を覆う透明層である。11 is a substrate, 12 is a base plating layer provided on the surface thereof, 15 is a thick plating layer provided thereon to form a pattern, 16 is an inorganic coating provided thereon, and 13 is a base plating layer 12. This is a transparent layer that covers the inorganic coating 16.
本実施例においては、直接基地メッキ１２の上に厚メッ
キ層１５を形成し、更にその上に形成される無機被膜１
６と基地メッキ１２を透明層１３で被覆している。In this embodiment, a thick plating layer 15 is formed directly on the base plating 12, and an inorganic coating 1 is further formed on the thick plating layer 15.
6 and base plating 12 are covered with a transparent layer 13.
次に第１１図乃至第１４図に基づいて第１０図に示す時
計用文字板の製造方法を説明する。Next, a method for manufacturing the timepiece dial shown in FIG. 10 will be explained based on FIGS. 11 to 14.
本実施例における文字板の基板１１の目付けや基地メッ
キ層１２の形成に関しては、前述した第１図に示す時計
用文字板の第２図乃至第４図に示す工程と同一であり、
このようにして形成された基地メッキ層１２の上面は第
１１図に示すように部分的にマスク１７により被覆され
る。The basis weight of the dial substrate 11 and the formation of the base plating layer 12 in this example are the same as the steps shown in FIGS. 2 to 4 for the watch dial shown in FIG. 1 described above.
The upper surface of the base plating layer 12 thus formed is partially covered with a mask 17 as shown in FIG.
その後、ＮｉあるいはＣｕメッキ等を施すことにより基
地メッキ層１２のマスクされてない部分に厚メッキ層１
５が形成される。更に第１２図に示すようにこの厚メッ
キ層１５及びマスク１７の上に前述した実施例と同じく
気相法により無機被膜１６の単層又は多層を形成する。Thereafter, a thick plating layer 1 is applied to the unmasked portion of the base plating layer 12 by applying Ni or Cu plating, etc.
5 is formed. Furthermore, as shown in FIG. 12, a single layer or multiple layers of an inorganic coating 16 is formed on the thick plating layer 15 and the mask 17 by the vapor phase method as in the embodiment described above.
ここで、マスク１７を無機被膜１６と共に剥離すると、
第１３図に示すように厚メッキ層１５の上だけに無機被
膜１６が残る。Here, when the mask 17 is peeled off together with the inorganic coating 16,
As shown in FIG. 13, the inorganic coating 16 remains only on the thick plating layer 15.
更にその上に透明樹脂を塗布し、それが硬化した後表面
を研磨して透明層１３を形成すると第１０図に示す文字
板が完成する。Further, a transparent resin is applied thereon, and after it has hardened, the surface is polished to form a transparent layer 13, thereby completing the dial plate shown in FIG.
又、この透明樹脂の塗布の代わりに、仕上げクリアー塗
装あるいは気相法により透明無機層を形成することによ
り、第１４図に示すような文字板を提供することもでき
る。Further, instead of coating this transparent resin, a dial plate as shown in FIG. 14 can be provided by forming a transparent inorganic layer by finishing clear coating or by a vapor phase method.
〈発明の効果〉
本発明によれば、立体感があり且つ金属光沢を有する所
望の色調を持つパターンを色ムラや耐候性の低下を招く
ことなく形成することができる。<Effects of the Invention> According to the present invention, a pattern with a desired color tone that has a three-dimensional effect and metallic luster can be formed without causing color unevenness or deterioration of weather resistance.
第１図は本発明の一実施例に係る時計用文字板を示す断
面図、
第２図乃至第９図は第１図に示す時計用文字板の製造工
程における状態を示す断面図、第１０図は本発明の他の
実施例に係る時計用文字板を示す断面図、
第１１図乃至第１４図は第１０図に示す時計用文字板の
製造工程における状態を示す断面図である。
１．１１・・・基板、
２．１２・・・基地メッキ層、
３・・・透明塗膜、
第 １ 図
第 ２ 図
第３図
４・・・導電膜、
５．１５・・・厚メッキ層、
６．１６・・・無機被膜、
７．１７・・・マスク、
１３・・・透明層。
第
１
図
６３３−1 is a cross-sectional view showing a timepiece dial according to an embodiment of the present invention; FIGS. 2 to 9 are cross-sectional views showing states in the manufacturing process of the timepiece dial shown in FIG. 1; FIG. The figure is a sectional view showing a timepiece dial according to another embodiment of the present invention, and FIGS. 11 to 14 are sectional views showing the state of the timepiece dial shown in FIG. 10 in the manufacturing process. 1.11... Substrate, 2.12... Base plating layer, 3... Transparent coating film, Figure 1, Figure 2, Figure 3, Figure 3, 4... Conductive film, 5.15... Thick plating. Layer, 6.16... Inorganic coating, 7.17... Mask, 13... Transparent layer. 1st Figure 633-
Claims (4)
該基地メッキ層上に設けられた透明塗膜と、該透明塗膜
上に設けられた導電膜と、該導電膜上に設けられ且つ時
字、マーク、模様等のパターンを形成する厚メッキ層と
、該厚メッキ層上に設けられた無機被膜とからなること
を特徴とする時計用文字板。(1) a substrate, a base plating layer provided on the substrate,
A transparent coating film provided on the base plating layer, a conductive film provided on the transparent coating film, and a thick plating layer provided on the conductive film and forming patterns such as hour characters, marks, patterns, etc. and an inorganic coating provided on the thick plating layer.
程と、該基地メッキ層上に透明樹脂を塗布することによ
り透明塗膜を形成する工程と、該透明塗膜上に導電膜を
蒸着にて形成する工程と、該導電膜をマスクにより部分
的に被覆する工程と、前記導電膜のマスクにより被覆さ
れていない部分上にメッキを施して厚メッキ層を形成す
る工程と、該厚メッキ層上に気相法により無機被膜を形
成する工程と、前記マスク、該マスクにより被覆されて
いた導電膜及び前記マスク上に形成された無機被膜を除
去する工程とからなることを特徴とする時計用文字板の
製造方法。(2) A step of plating on a substrate to form a base plating layer, a step of forming a transparent coating film by applying a transparent resin on the base plating layer, and a step of vapor depositing a conductive film on the transparent coating film. a step of partially covering the conductive film with a mask; a step of plating on the portion of the conductive film not covered by the mask to form a thick plating layer; A watch comprising the steps of forming an inorganic film on the layer by a vapor phase method, and removing the mask, the conductive film covered by the mask, and the inorganic film formed on the mask. Method of manufacturing a dial plate.
該基地メッキ層上に設けられ且つ時字、マーク、模様等
のパターンを形成する厚メッキ層と、該厚メッキ層上に
設けられた無機被膜と、該無機被膜と基地メッキ層上を
被覆する透明層とからなることを特徴とする時計用文字
板。(3) a substrate, a base plating layer provided on the substrate,
A thick plating layer provided on the base plating layer and forming a pattern such as hour characters, marks, patterns, etc., an inorganic coating provided on the thick plating layer, and coating the inorganic coating and the base plating layer. A watch dial comprising a transparent layer.
程と、該基地メッキ層をマスクにより部分的に被覆する
工程と、前記基地メッキ層のマスクにより被覆されてい
ない部分上にメッキを施して厚メッキ層を形成する工程
と、該厚メッキ層上に気相法により無機被膜を形成する
工程と、前記マスク及び該マスク上に形成された無機被
膜を除去する工程と、前記無機被膜と基地メッキ層上に
透明層を形成する工程とからなることを特徴とする時計
用文字板の製造方法。(4) forming a base plating layer on the substrate by plating, partially covering the base plating layer with a mask, and plating on the portions of the base plating layer not covered with the mask; a step of forming a thick plating layer, a step of forming an inorganic film on the thick plating layer by a vapor phase method, a step of removing the mask and the inorganic film formed on the mask, and a step of removing the inorganic film and the base. A method for manufacturing a watch dial, comprising the step of forming a transparent layer on a plating layer.