JPH0358786B2 - - Google Patents
Info
- Publication number
- JPH0358786B2 JPH0358786B2 JP3353388A JP3353388A JPH0358786B2 JP H0358786 B2 JPH0358786 B2 JP H0358786B2 JP 3353388 A JP3353388 A JP 3353388A JP 3353388 A JP3353388 A JP 3353388A JP H0358786 B2 JPH0358786 B2 JP H0358786B2
- Authority
- JP
- Japan
- Prior art keywords
- paint
- water droplets
- apply
- particles
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
（産業上の利用分野）
この発明な、缶表面にあたかも水滴や霜がつい
たような状態に塗布する缶表面の塗装方法に関す
る。DETAILED DESCRIPTION OF THE INVENTION (Industrial Field of Application) The present invention relates to a method for coating the surface of a can, in which the coating is applied to the surface of the can to give the appearance of water droplets or frost.
（従来の技術）
缶入飲料は、冷却して飲むと非常に美味である
ことが多い。(Prior Art) Canned beverages are often very delicious when cooled.
そのため、缶入飲料をよく冷すと、その缶の表
面に水滴や霜がつくこが多く、それを見るとよく
冷ているイメージがわき、それによつて飲欲がそ
そられる。 Therefore, when canned beverages are cooled down, water droplets and frost often form on the surface of the can, which gives the impression that the drink is cold, which arouses the desire to drink.
一方、缶入飲料は、自動販売機等により多数販
売されているが、その種類は非常に多い。 On the other hand, canned beverages are sold in large numbers through vending machines and the like, and there are many types of them.
そのため、自動販売機の上部等に陳列してある
商品見本の善し悪しによつて売れ行きが大幅に左
右されることがある。従つて、その商品見本の作
成にあつてはできるだけおいしそうに見えりよう
に最善の手段を講じている。 Therefore, sales can be greatly affected by the quality of the product samples displayed at the top of the vending machine. Therefore, when creating product samples, we take the best possible measures to make them look as delicious as possible.
そこで、この手段として、従来は、できるだけ
印刷を鮮明にしたり、照明に工夫をこらしたり、
その他デイスプレイに工夫をこらしたりしてい
た。 Therefore, as a means to achieve this, conventional methods include making the printing as clear as possible, making improvements to the lighting, etc.
Other improvements were made to the display.
（発明が解決しようとする問題点）
ところが、上記工夫等では、単に商品そのもの
の存在感しかなく、特に飲欲をそそることがな
い。そのため、他の陳列商品との差はあまり生れ
ず、商品自体の知名度等に影響されてしまうのが
現実であるという問題点があつた。(Problems to be Solved by the Invention) However, with the above-mentioned devices, there is only the presence of the product itself, and it does not particularly arouse the desire to drink. Therefore, there was a problem in that there was not much difference between the products and other products on display, and the reality was that they were influenced by the popularity of the product itself.
そこで、この発明は、上述した問題点等に鑑
み、陳列している商品見本を見るだけで飲欲がそ
そられるようにすべく缶表面に塗装できるように
することを課題として創出されたものである。 Therefore, in view of the above-mentioned problems, this invention was created with the aim of making it possible to paint the surface of a can so that the user's desire to drink can be aroused just by looking at the product samples on display. be.
（問題点を解決するための手段）
この発明は、缶表面に、シリコン系の透明塗料
を塗布して下塗りを行ない硬化させ、次に、その
上から、適宜水滴状となるように上記塗料と同様
の塗料を適数回吹付けそのまま硬化させることに
より、又、特に、シリコン系透明塗料として、紫
外線硬化型塗料を用いたことにより、上述した問
題点を解決するものである。(Means for Solving the Problems) This invention involves applying a silicone-based transparent paint to the surface of the can, applying an undercoat and curing it, and then applying the above-mentioned paint on top of the undercoat so that it forms water droplets. The above-mentioned problems can be solved by spraying a similar paint a suitable number of times and curing it as it is, and in particular by using an ultraviolet curable paint as the silicone-based transparent paint.
（作 用）
この発明に係る缶表面の塗装方法は、缶表面
に、シリコン系の透明塗料を塗布して下塗りを行
ない硬化させ、次に、その上から、適宜水滴状と
なるように上記塗料と同様の塗料を適数回吹付け
る。そうすると、シリコン系の塗料同士あ、下塗
りの方が硬化しているのではじく性質があり、そ
のまま硬化させることにより、そのまま水滴状の
状態で硬化して塗装される。(Function) The method for painting the can surface according to the present invention is to apply a silicone-based transparent paint to the can surface, apply an undercoat and cure it, and then apply the above paint onto the can surface so as to form water droplets as appropriate. Spray the same paint an appropriate number of times. In this case, silicone-based paints have the property of repelling each other because the undercoat is hardened, so by allowing it to harden as it is, it will harden and be painted in the form of water droplets.
その時に、最も適しているのが、シリコン系透
明塗料としての紫外線硬化型塗料であり、紫外線
を照射するだけで硬化し、加熱する必要がなくそ
のままの水滴状態を残すことができる。 At this time, the most suitable coating is an ultraviolet-curable silicone-based transparent coating, which cures simply by irradiating it with ultraviolet light and leaves water droplets as they are without the need for heating.
（実施例）
以下、図面を参考にしながらこの発明の実施例
を説明すると次の通りである。(Embodiments) Hereinafter, embodiments of the present invention will be described with reference to the drawings.
すなわち、図に示す符号１は陳列用缶であり、
その表面には、図示はしないが、適宜装飾用の模
様、図柄、文字等が印刷されている。 That is, the reference numeral 1 shown in the figure is a display can,
Although not shown, decorative patterns, designs, characters, etc. are appropriately printed on the surface.
先ず、Ａに示すこの陳列用缶１に、Ｂに示すよ
うに、塗料噴射装置２により全面にシリコン系の
透明の塗料３を吹付け下塗りを行う。そして、こ
の塗料３を硬化させた後、Ｃに示すように、その
上から、再び前記塗料と同様の塗料３を適数回吹
付け、陳列用缶１の表面に適宜水滴状に塗料粒４
が残るようにし、硬化させるものである。 First, as shown in B, this display can 1 shown in A is sprayed with a silicone-based transparent paint 3 over the entire surface using a paint spraying device 2 for undercoating. After this paint 3 is cured, as shown in C, the same paint 3 as the above paint is again sprayed several times to form paint particles 4 in the form of water droplets on the surface of the display can 1.
is left behind and cured.
この場合に、前記塗料３として紫外線硬化型塗
料を用いると最適である。 In this case, it is optimal to use an ultraviolet curing type paint as the paint 3.
これらの工程の具体的実施例を次に示す。 Specific examples of these steps are shown below.
以下の具体的な実施例は、下塗、中塗、上塗の
３工程を順次行ない実施する。 The following specific examples are carried out by sequentially performing three steps: undercoating, intermediate coating, and topcoating.
第１実施例
下 塗
塗料名：HO5800U紫外線硬化型塗料（藤倉化成
製）
塗布量：1.1mg／cm2
噴射圧力：４Kg／cm2
噴射距離：15cm
照射条件：４灯ランプ照射（I.R.70℃）
中 塗
塗料名：HO5800U紫外線硬化型塗料（藤倉化成
製）
塗布量：1.1mg／cm2
噴射圧力：４Kg／cm2
噴射距離：15cm
照射条件：４灯ランプ照射（I.R.なし）
塗装粒４が小粒となるように塗布。First example below Coating name: HO5800U ultraviolet curable paint (manufactured by Fujikura Kasei) Coating amount: 1.1 mg/cm 2 Injection pressure: 4 Kg/cm 2 Injection distance: 15 cm Irradiation conditions: 4 lamp irradiation (IR70℃) Medium Paint name: HO5800U ultraviolet curing paint (manufactured by Fujikura Kasei) Coating amount: 1.1mg/cm 2 Injection pressure: 4Kg/cm 2 Injection distance: 15cm Irradiation conditions: 4 lamp irradiation (no IR) Paint particles 4 are small particles Apply as desired.
上 塗
塗料名：UR4201紫外線硬化型塗料（三菱レーヨ
ン製）
塗布量：5.5mg／cm2
噴射圧力：0.1Kg／cm2
噴射距離：10cm
照射条件：６灯ランプ照射（I.R.なし）
塗装粒４が大粒となるように塗布。Top Paint name: UR4201 ultraviolet curing paint (Mitsubishi Rayon) Coating amount: 5.5 mg/cm 2 Spray pressure: 0.1 Kg/cm 2 Spray distance: 10 cm Irradiation conditions: 6 lamp irradiation (no IR) Paint particles 4 Apply in large particles.
その結果、小粒の上に大粒の塗料粒４が形成さ
れ、あたかも、適温に冷やされた状態の水滴の付
着と同様な外観を呈したものが得られた。 As a result, large paint particles 4 were formed on the small particles, giving an appearance similar to that of water droplets that had been cooled to an appropriate temperature.
第２実施例
下 塗
塗料名：HO5800U紫外線硬化型塗料（藤倉化成
製）
塗布量：1.1mg／cm2
噴射圧力：４Kg／cm2
噴射距離：15cm
照射条件：４灯ランプ照射（I.R.70℃）
中 塗
塗料名：HO5800U紫外線硬化型塗料（藤倉化成
製）
塗布量：3.3mg／cm2
噴射圧力：0.1Kg／cm2
噴射距離：10cm
照射条件：４灯ランプ照射（I.R.なし）
塗装粒４が大粒となるように塗布。Second Example Paint name: HO5800U ultraviolet curing paint (manufactured by Fujikura Kasei) Coating amount: 1.1 mg/cm 2 Injection pressure: 4 Kg/cm 2 Injection distance: 15 cm Irradiation conditions: 4 lamp irradiation (IR70℃) Medium Paint name: HO5800U ultraviolet curable paint (manufactured by Fujikura Kasei) Coating amount: 3.3 mg/cm 2 Injection pressure: 0.1 Kg/cm 2 Injection distance: 10 cm Irradiation conditions: 4 lamp irradiation (no IR) Paint particles 4 are large Apply so that.
上 塗
塗料名：UR4201紫外線硬化型塗料（三菱レーヨ
ン製）
塗布量：1.1mg／cm2
噴射圧力：３Kg／cm2
噴射距離：15cm
照射条件：６灯ランプ照射（I.R.なし）
塗装粒４が小粒となるように塗布。Top Coating name: UR4201 ultraviolet curing paint (manufactured by Mitsubishi Rayon) Coating amount: 1.1mg/cm 2 Injection pressure: 3Kg/cm 2 Injection distance: 15cm Irradiation conditions: 6 lamp irradiation (no IR) Paint particles 4 are small Apply so that.
その結果、大粒の上に小粒の塗料粒４が形成さ
れ、あたかも、適温に冷された状態の水滴の付着
と同様な外観を呈したものが得られた。 As a result, small paint particles 4 were formed on the large particles, giving an appearance similar to that of water droplets that had been cooled to an appropriate temperature.
第３実施例
下 塗
塗料名：HO5800U紫外線硬化型塗料（藤倉化成
製）にTRマツト材（東邦化研製）を３：１の
割合で混合したもの
塗布量：5.6mg／cm2
噴射圧力：３Kg／cm2
噴射距離：20cm
照射条件：４灯ランプ照射（I.R.70℃）
中 塗
塗料名：HO5800U紫外線硬化型塗料（藤倉化成
製）
塗布量：1.3mg／cm2
噴射圧力：３Kg／cm2
噴射距離：20cm
照射条件：４灯ランプ照射（I.R.なし）
塗装粒４が小粒となるように塗布。3rd Example Paint name: HO5800U ultraviolet curable paint (manufactured by Fujikura Kasei) mixed with TR pine material (manufactured by Toho Kaken) in a ratio of 3:1 Application amount: 5.6mg/cm 2 Injection pressure: 3Kg /cm 2 Spraying distance: 20cm Irradiation conditions: 4-lamp irradiation (IR70℃) Medium Paint name: HO5800U ultraviolet curing paint (manufactured by Fujikura Kasei) Coating amount: 1.3mg/cm 2 Spraying pressure: 3Kg/cm 2 Spraying distance :20cm Irradiation conditions: 4-lamp irradiation (no IR) Apply so that paint particles 4 are small.
上 塗
塗料名：UR4201紫外線硬化型塗料（三菱レーヨ
ン製）
塗布量：5.5mg／cm2
噴射圧力：0.1Kg／cm2
噴射距離：10cm
照射条件：６灯ランプ照射（I.R.なし）
塗装粒４が大粒となるように塗布。Top Paint name: UR4201 ultraviolet curing paint (Mitsubishi Rayon) Coating amount: 5.5 mg/cm 2 Spray pressure: 0.1 Kg/cm 2 Spray distance: 10 cm Irradiation conditions: 6 lamp irradiation (no IR) Paint particles 4 Apply in large particles.
その結果、細かい霜が着いたような状態の面の
上に、小粒、更に大粒の塗料粒４が形成され、あ
たかも、かなり定温にて冷却された状態と同様な
外観を呈したものが得られた。 As a result, small and even larger paint particles 4 are formed on the surface that has been covered with fine frost, giving an appearance similar to that of a state that has been cooled at a fairly constant temperature. Ta.
又、塗料としては、前記HO5800U紫外線硬化
型塗料の他に、HO5123U、HO5825紫外線硬化
型塗料（共に藤倉化成製）等も使用可能であり、
塗布量としては、0.7mg／cm2〜6.5mg／cm2、噴射圧
力は、0.05Kg／cm2〜6.5Kg／cm2の範囲で行えば十
分である。尚、この様な品位を越えても、前述し
たような状態に塗装できるのであれば、この様な
範囲も良いことは言うまでもない。 In addition to the above-mentioned HO5800U UV-curable paint, HO5123U and HO5825 UV-curable paints (both manufactured by Fujikura Kasei) can also be used as paints.
It is sufficient to apply the coating amount in the range of 0.7 mg/cm 2 to 6.5 mg/cm 2 and the injection pressure in the range of 0.05 Kg/cm 2 to 6.5 Kg/cm 2 . It goes without saying that such a range is good as long as the coating can be painted in the above-mentioned condition even if the quality is exceeded.
（発明の効果）
上述の如く構成したこの発明な、缶１表面に、
シリコン系の透明塗料３を塗布して下塗りを行な
い硬化させ、次に、その上から、適宜水滴状とな
るように上記塗料３を適数回吹付けそのまま硬化
させることにより、シリコン系の塗料３同士は、
下塗りの方が硬化しているのではじく性質があ
り、このまま硬化させることで、そのまま水滴状
の状態で硬化して塗装される。(Effect of the invention) In this invention configured as described above, on the surface of the can 1,
A silicone-based transparent paint 3 is applied, an undercoat is applied and cured, and then the above-mentioned paint 3 is sprayed an appropriate number of times in the form of water droplets and left to harden. They are
Since the undercoat is hardened, it has the property of being repellent, so if you let it harden as it is, it will harden and be painted in the form of water droplets.
従つて、そのまま水滴状の状態の硬化した透明
な塗料３は、外観上、あたかも水滴が缶１の表面
に付着しているように見える。そのため、缶１内
の飲料が適温に冷やされた状態に見えるので、飲
欲をそそるものである。 Therefore, the cured transparent paint 3 in the form of water droplets looks as if water droplets are attached to the surface of the can 1. Therefore, the beverage in the can 1 appears to be cooled to an appropriate temperature, which arouses the beverage's desire to drink.
その時に、最も適しているが、シリコン系透明
塗料３としての紫外線硬化型塗料であり、紫外線
を照射するだけで硬化し、加熱する必要がなくそ
のままの水滴状態を残すことができる。 At that time, the most suitable silicone-based transparent paint 3 is an ultraviolet curable paint, which cures simply by irradiating it with ultraviolet rays and can leave water droplets as they are without the need for heating.
その結果、自動販売機等の陳列用の缶１は陳列
ケース内にいれてあるのが一般的であるから直接
手等で触れることがないので、この様な缶１に上
記塗装を施せば、その陳列用缶１自体が冷却され
ているように見え、購買意欲をそそるものであ
る。 As a result, since cans 1 for display in vending machines and the like are generally kept in display cases and are not touched directly with hands, etc., if such cans 1 are coated with the above coating, The display can 1 itself appears to be cooled, which arouses the desire to purchase.
尚、この発明に係る缶表面の塗装方法は、陳列
用缶１に実施する以外に、実際の飲料用缶に実施
しても良く、その他の構成にあつても、前述した
実施例に限定されることがないことは言うまでも
ない。 The can surface coating method according to the present invention may be applied not only to the display can 1 but also to actual beverage cans, and even for other configurations, it is not limited to the above-mentioned embodiments. Needless to say, there is no such thing.
この様に、この発明によれば、表面に水滴、或
いは霜が付着しているように見えるから、非常に
良く冷やされているイメージが醸し出され、陳列
している商品見本を見るだけで飲欲がそそられる
等の種々優れた効果を奏するものである。 In this way, according to this invention, since it looks like water droplets or frost are attached to the surface, it creates an image that it is very well cooled, and just looking at the product samples on display increases the desire to drink. It has various excellent effects, such as being arousing.
第１図はこの発明の実施例を示す工程図であ
る。
１……陳列用缶、２……塗料噴射装置、３……
塗料、４……塗料粒。
FIG. 1 is a process diagram showing an embodiment of this invention. 1...Display can, 2...Paint injection device, 3...
Paint, 4...Paint particles.
Claims (1)
下塗りを行ない硬化させ、次に、その上から、適
宜水滴状となるように上記塗料と同様の塗料を適
数回吹付けそのまま硬化させることを特徴とした
缶表面の塗装方法。 ２ シリコン系透明塗料は、紫外線硬化型塗料を
用いた請求項１記載の缶表面の塗装方法。[Scope of Claims] 1. Apply a silicone-based transparent paint to the surface of the can, perform an undercoat and harden it, then apply a paint similar to the above paint an appropriate number of times on top of it so that it forms water droplets. A method for painting the surface of cans, which is characterized by curing the can surface as it is sprayed. 2. The method of painting a can surface according to claim 1, wherein the silicone-based transparent paint is an ultraviolet curable paint.