JPH03272996A - Manufacture of designed hand rail - Google Patents
Manufacture of designed hand railInfo
- Publication number
- JPH03272996A JPH03272996A JP7194290A JP7194290A JPH03272996A JP H03272996 A JPH03272996 A JP H03272996A JP 7194290 A JP7194290 A JP 7194290A JP 7194290 A JP7194290 A JP 7194290A JP H03272996 A JPH03272996 A JP H03272996A
- Authority
- JP
- Japan
- Prior art keywords
- display
- sheet
- urethane resin
- handrail
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は既設の乗客コンベアにおけるハンドレールに表
示を施して成るデザインハンドレールの製造方法に関す
る。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a method of manufacturing a designed handrail in which a handrail of an existing passenger conveyor is marked.
、従来のこの種のデザインハンドレールとしては、炙
着開昭５１−６１６８９号公報に記載のようにハンドレ
ールの表面に、その色とは異なる色の標識を施し、その
上に吹付けにより透明ウレタンゴム層を設けたものが知
られている。Conventional handrails with this type of design include markings of a different color from the handrail surface, as described in Aburiku Kaitoku Publication No. 51-61689, and transparent markings are sprayed onto the surface of the handrail. One with a urethane rubber layer is known.
しかしながら従来のデザインハンドレールは、走行中に
屈曲を受けると、標識にひび割れが生じてしまい十分な
耐久性を得るのが難しく、しかも既設の乗客コンベアに
適用しようとすると、この傾向はより顕著になる。However, when conventionally designed handrails are bent while running, the sign cracks, making it difficult to obtain sufficient durability.Moreover, this tendency becomes even more pronounced when applying it to an existing passenger conveyor. Become.
本発明の目的は、走行中に屈曲を受けても表示がひび割
れすることなく十分な耐久性を有するデザインハンドレ
ールの製造方法を提供するにある。An object of the present invention is to provide a method for manufacturing a handrail with a design that has sufficient durability without causing cracks in the display even if the rail is bent during travel.
本発明は上記目的を達成するために、ハンドレールの研
磨し、た表面に表示に対応する切抜きを有するシートを
貼付する通して上記切抜きを通して上記ハンドレールの
表面に着色ウレタン樹脂を用いて表示する通して上記シ
ートを剥す通して上記ハンドレールの近傍に着色ウレタ
ン樹脂を用いて表示する工程と、上記シートを剥す工程
とを有することを特徴とする。In order to achieve the above object, the present invention applies a sheet having a cutout corresponding to the display to the polished surface of the handrail, and displays the surface of the handrail through the cutout using a colored urethane resin. The handrail is characterized by comprising the steps of: peeling off the sheet through the handrail to display an area near the handrail using a colored urethane resin; and peeling off the sheet.
本発明によるデザインハンドレールの製造方法は上述の
如き工程を有するものであるから、研磨されたハンドレ
ールの表面に切抜きを有するシートを用いることによっ
て表示を所望の膜厚にすることができると共に、着色ウ
レタン樹脂と透明ウレタン樹脂とはハンドレールと同様
あるいはそれ以上の伸び率をもつよう設定するのが容易
であり、しかも劣化していた表面を整えて表示を行って
いるので走行中に屈曲や伸縮を受けてもこれに対応させ
て屈曲および伸縮させることができ、既設の乗客コンベ
アであっても、ひび割れが発生することのない十分な耐
久性を有するデザインハンドレールが得られる。Since the method for manufacturing a designed handrail according to the present invention includes the steps described above, by using a sheet having cutouts on the surface of the polished handrail, the display can be made to have a desired thickness, and Colored urethane resin and transparent urethane resin can be easily set to have the same or higher elongation rate than the handrail, and since the deteriorated surface is smoothed and displayed, there is no possibility of bending or bending while driving. A designed handrail that can be bent and expanded/contracted in response to expansion/contraction and has sufficient durability without cracking even on an existing passenger conveyor can be obtained.
以下本発明の実施例を図面によって説明する。 Embodiments of the present invention will be described below with reference to the drawings.
第１図はデザインハンドレールの製造工程を示す流れ図
である。この実施例では既納品の乗客コンベア用ハンド
レールを加工してデザインハンドレールにする場合につ
いて説明する。FIG. 1 is a flowchart showing the manufacturing process of the designed handrail. In this embodiment, a case will be described in which a handrail for a passenger conveyor that has already been delivered is processed into a designed handrail.
先ず、工程１０としてハンドレールの表面を研磨し、表
面の劣化層や傷を取り除く０次いで、工程１１のように
ハンドレールに施す表示と同一形状のシートをハンドレ
ールの研磨済み表面に貼付する。First, in step 10, the surface of the handrail is polished to remove the deteriorated layer and scratches on the surface.Next, in step 11, a sheet having the same shape as the marking to be applied to the handrail is attached to the polished surface of the handrail.
このシートを貼付した部分を除く近傍に、工程１２の如
く後述する着色ウレタン樹脂で予備膜を剥す。その後、
このシートを剥すが、これら工程１１．１２は省略する
こともできる。工程１３では、表示に対応する部分を切
抜いたシートを貼付するが、工程１１．１２を行なった
場合は、前者のシートを剥した部分に後者のシートの切
抜きが対応するようにする。この状態で、切抜きを通し
てハンドレールの表面に着色ウレタン樹脂で表示する。In step 12, a preliminary film is peeled off using a colored urethane resin, which will be described later, in the vicinity of the area where this sheet is pasted. after that,
Although this sheet is peeled off, these steps 11 and 12 can also be omitted. In step 13, a sheet is pasted with a portion corresponding to the display cut out, but if step 11.12 is performed, the cutout of the latter sheet is made to correspond to the portion removed from the former sheet. In this state, the cutout is displayed on the surface of the handrail using colored urethane resin.
その後、工程１５でシートを剥し、工程１６で表示上お
よび周辺部に着色ウレタン樹脂を用いて表示する工程と
、上記シートを剥す。Thereafter, in step 15, the sheet is peeled off, and in step 16, a colored urethane resin is used for display on and around the display, and the sheet is peeled off.
更に、これら工程の詳細については第２図〜第５図を用
いて説明する。Furthermore, details of these steps will be explained using FIGS. 2 to 5.
第２図は第１図の工程１０に対応するもので、ハンドレ
ール３の化粧ゴム層３ａを研磨し、表面の劣化層や傷を
取り除く。研磨装置としてはベルトサンダーを用い、表
面の劣化および傷の深さに応してベルトサンダーのペー
パー粗さや、ペーパー粗さの種類数を選択し、粗さの大
きいペーパーから順次小さいペーパーのものを用いて研
磨する。FIG. 2 corresponds to step 10 in FIG. 1, and the decorative rubber layer 3a of the handrail 3 is polished to remove the deteriorated layer and scratches on the surface. A belt sander is used as the polishing device, and the paper roughness of the belt sander and the number of types of paper roughness are selected depending on the deterioration of the surface and the depth of the scratches. Polish using.
次いで、水洗いによって研磨粉を除去し、その後自然乾
燥する。Next, the polishing powder is removed by washing with water and then air drying.
次ぎに第１図の工程１３に対応する第３図に示す形状の
切抜き４ａを有するシート４を貼付する。Next, a sheet 4 having a cutout 4a in the shape shown in FIG. 3 corresponding to step 13 in FIG. 1 is attached.
このシート４は、厚さ１００ ミクロン（０，１ｍｍ
）のシート材に３０ミクロン（０，０３ｍｍ）の接着剤
層を形成したものである。また接着剤は、シート４を化
粧ゴム層３ａの表面から剥がしたとき接着剤が表面に残
存しない性質のもので、アクリルゴム、有機溶削および
トリクロルエタンガスを含有したものが適している。This sheet 4 has a thickness of 100 microns (0.1 mm).
) A 30 micron (0.03 mm) adhesive layer is formed on the sheet material. Further, the adhesive has such a property that it does not remain on the surface of the decorative rubber layer 3a when the sheet 4 is peeled off from the surface of the decorative rubber layer 3a, and an adhesive containing acrylic rubber, organic abrasion, and trichloroethane gas is suitable.
この状態で第１図に示した工程１４に対応して、シート
４の切抜き４ａを通してハンドレール３の表面に表示５
を剥す。この作業に際して、ハンドレール３の地色と異
なる色、例えば白色に着色された液状のウレタン樹脂を
塗布し、ハンドレール３の化粧ゴム層３ａの表面に、白
色のウレタン樹脂による表示５を剥す。ここで用いられ
る着色ウレタン樹脂は、純性ウレタンを主成分とし、白
色チタン、セロソルブアセテート、トルエン、メチルイ
ソブチルケトンおよびトリエチレンヂアミンを含存して
いる。標識形成用の着色ウレタン樹脂の塗布厚さはハン
ドレール３の地色が見えなくなる程度、すなわち１００
ミクロン（０，１ｍｍ ）とする。In this state, corresponding to step 14 shown in FIG.
Peel off. During this work, a liquid urethane resin colored in a color different from the ground color of the handrail 3, for example, white, is applied, and the display 5 made of white urethane resin is peeled off on the surface of the decorative rubber layer 3a of the handrail 3. The colored urethane resin used here has pure urethane as its main component, and contains white titanium, cellosolve acetate, toluene, methyl isobutyl ketone, and triethylenediamine. The coating thickness of the colored urethane resin for sign formation is such that the base color of the handrail 3 is not visible, that is, 100%.
Micron (0.1 mm).
−回の塗布で１００ ミクロン（０，１ｍｍ ）の膜厚
が得られないときは、自然乾燥後再度着色ウレタン樹脂
を塗布する。また１、この着色ウレタン樹脂の乾燥後の
伸び率は、ハンドレール３の伸び率と同等またはそれ以
上である。その後、第１図の工程１５に対応してシート
４を剥がすと共に、工程１６に従って白色ウレタン樹脂
による表示５を付したハンドレール３の表面全体に、着
色ウレタン樹脂を、表示５以外の部分の膜厚が２００
ミクロン（０，２＋ｗ ）程度となるように塗布する。- If a film thickness of 100 microns (0.1 mm) cannot be obtained in the first coating, apply the colored urethane resin again after air drying. Further, 1. The elongation rate of this colored urethane resin after drying is equal to or higher than the elongation rate of the handrail 3. Thereafter, the sheet 4 is peeled off in accordance with step 15 in FIG. Thickness is 200
Apply to a thickness of about microns (0.2+w).
回の塗布で所定の膜厚さにならないので、塗布と自然乾
燥とを数回繰返し、所定の膜厚のコーテイング膜６を得
、その後コーテイング膜６を自然乾燥する。ここで用い
られる着色ウレタン樹脂は、純性ウレタンを主成分とし
、セロソルブアセテ−１・、トルエン、キシレン、酢酸
エチル、フリーイソシアネートおよびトリエチレンヂア
ミンを含有している。また、この透明ウレタン樹脂の乾
燥後の伸び率は、ハンドレール３の伸び率と同等または
それ以上である。Since the predetermined film thickness cannot be achieved with one coating, the coating and air drying are repeated several times to obtain the coating film 6 with a predetermined thickness, and then the coating film 6 is air dried. The colored urethane resin used here is mainly composed of pure urethane and contains cellosolve acetate-1., toluene, xylene, ethyl acetate, free isocyanate, and triethylenediamine. Further, the elongation rate of this transparent urethane resin after drying is equal to or higher than the elongation rate of the handrail 3.
以上の手順により、ハンドレール３の露出している範囲
の表面の再生と表示５の形成が完了し、残りの範囲につ
いても前記と同じ手順を経て表面の再生と表糸５の形成
を行なう。By the above procedure, the surface regeneration of the exposed range of the handrail 3 and the formation of the display 5 are completed, and the surface regeneration and the formation of the front thread 5 are performed for the remaining range through the same procedure as described above.
しかしながら上述の手順によれば、着色ウレタン樹脂に
よる表示５の上に透明ウレタン樹脂によるコーテイング
膜６が積層されるため、表示５の部分が少し盛り上がる
が、次ぎの手順によれば盛り上がりを無くすることがで
きる。これは第１図における工程１１．１２を追加した
場合に相当する。However, according to the above procedure, since the coating film 6 made of transparent urethane resin is laminated on the display 5 made of colored urethane resin, the part of the display 5 is slightly raised, but according to the following procedure, the raisedness can be eliminated. I can do it. This corresponds to the case where steps 11 and 12 in FIG. 1 are added.
つまり第６図は先の実施例における第２図と同様にして
第１図の工程１０を行なうが、その後、第１図の工程１
１に対応して第７図に示すように、前述した表示５に全
く対応した形状のシート４を貼付する。先の実施例では
表示に対応する部分を切抜いていたが、本実施例では表
示に対応する形状のシート４となっている。このシート
４は厚さ１００ミクロンのシート材に３０ミクロンの接
着側層を形成したものであり、この接着剤は、シート４
を化粧ゴム層３ａの表面から剥がしたとき、そこに残存
しない性質のもので５．アクリルゴム、有機溶剤および
トリクロエタンガスを含有したものが通している。In other words, in FIG. 6, step 10 in FIG. 1 is performed in the same manner as in FIG. 2 in the previous embodiment, but after that, step 1 in FIG.
As shown in FIG. 7, a sheet 4 having a shape completely corresponding to the display 5 described above is pasted in correspondence with the display 5. In the previous embodiment, the portion corresponding to the display was cut out, but in this embodiment, the sheet 4 has a shape corresponding to the display. This sheet 4 is made by forming an adhesive side layer of 30 microns on a sheet material of 100 microns thick, and this adhesive is
When it is peeled off from the surface of the decorative rubber layer 3a, it does not remain on the surface of the decorative rubber layer 3a. Contains acrylic rubber, organic solvent, and tricloethane gas.
次ぎに、この状態で第８図に示すようにシート４の周辺
に、着色ウレタン樹脂を厚さ１００ミクロン程度となる
ように塗布して予ｒｉＩＩ１６ ａを形成し工程１２を
実施する。−回の塗布で所定の膜厚さにならない場合は
、塗布と自然乾燥とを数回繰返し、所定の膜厚さを得る
６その後、これを自然乾燥する。ここで用いられる着色
ウレタン樹脂は、純性ウレタンを主成分とし、セロソル
ブアセテート、トルエン、キシレン、酢酸エチル、
フリーイソシアネートおよびトリエチレンヂ７ミンを含
有している。また、この透明ウレタン樹脂の乾燥後の伸
び率は、ハンドレール３の伸び率と同等またはそれ以上
である。Next, in this state, as shown in FIG. 8, a colored urethane resin is applied to the periphery of the sheet 4 to a thickness of about 100 microns to form a preliminary riII 16a, and step 12 is carried out. - If the predetermined film thickness is not achieved after several coats, repeat the coating and air drying several times to obtain the predetermined film thickness.6 Then, air dry the film. The colored urethane resin used here is mainly composed of pure urethane and contains cellosolve acetate, toluene, xylene, ethyl acetate, free isocyanate, and triethylenedi7mine. Further, the elongation rate of this transparent urethane resin after drying is equal to or higher than the elongation rate of the handrail 3.
次ぎに、第９図に示ずようにシ・−ト４を剥がすと共に
、第１図の工程１３に対応してシート４あるいは表示に
対応する形状の切欠き７ａを有するシート７を先のシー
ト４の位置に合わせて貼付する。Next, as shown in FIG. 9, the sheet 4 is peeled off, and the sheet 4 or the sheet 7 having the notch 7a of the shape corresponding to the display is removed from the previous sheet in accordance with step 13 of FIG. Paste it according to position 4.
従って、シート７によって予備層６ａは被われ、この予
備層がない部分が切抜き７ａに対応している。このシー
ト７の先のシーｉ−４と同様に構成されたものである。Therefore, the preliminary layer 6a is covered by the sheet 7, and the portion where this preliminary layer is not provided corresponds to the cutout 7a. This seat 7 is constructed in the same way as the seat i-4.
この状態で、第１０図に示すようにハンドレール３に貼
付されたシート４の切抜き４ａに、ハンドレール３の地
色と異なる色、例えば白色に着色された液状のウレタン
樹脂を塗布し、ハンドレール３の化粧ゼム層３ａの表面
に白色のウレタン樹脂全塗布し、ハンドレール３の化粧
ゼムＮ ３ ａの表面に白色のウレタン樹脂による表示
５を形成して工程１４を実施する。ここで用いられる着
色ウレタン樹脂は、先の実施例と同様に純性ウレタンを
主成分とし、白色チタン、セロソルブアセテート、トル
エン、メチルイソブチルケントおよびトリエチレンヂア
ミンを含有している。着色ウレタン樹脂による表示５の
塗布厚さは予備層６ａと同じにする。−回の塗布で１０
０ ミクロンの表示５の膜厚が得られないときは、自然
乾燥後再度着色ウレタン樹脂の乾燥後の伸び率は、ハン
ドレール３の伸び率と同等またはそれ以上である。In this state, as shown in FIG. 10, liquid urethane resin colored in a color different from the ground color of the handrail 3, for example, white, is applied to the cutout 4a of the sheet 4 attached to the handrail 3, and the A white urethane resin is completely applied to the surface of the decorative gem layer 3a of the rail 3, a display 5 made of white urethane resin is formed on the surface of the decorative gem N 3 a of the handrail 3, and step 14 is carried out. The colored urethane resin used here has pure urethane as its main component, as in the previous example, and contains white titanium, cellosolve acetate, toluene, methyl isobutyl Kent, and triethylenediamine. The coating thickness of the display 5 made of colored urethane resin is the same as that of the preliminary layer 6a. -10 times in one application
When a film thickness of 0 microns is not obtained, the elongation rate of the colored urethane resin after drying is equal to or greater than the elongation rate of the handrail 3.
その後、第１図の工程１５および工程１６に従って第１
１図に示すようにシート７を剥がし、自然乾燥させた後
、表示５を含む周辺の表面に、着色ウレタン樹脂を塗布
し、膜厚１００ミクロン程度のコーテイング膜６を得る
。この着色ウレタン樹脂は第８図で説明した予（ｉｔ
Ｎ ６ ａを剥すために用いたものと同一である。Thereafter, the first step according to steps 15 and 16 of FIG.
As shown in FIG. 1, the sheet 7 is peeled off and dried naturally, and then a colored urethane resin is applied to the surrounding surface including the display 5 to obtain a coating film 6 with a thickness of about 100 microns. This colored urethane resin has the same color as described in FIG.
It is the same as that used to strip the N 6 a.
このような手順によって表示５とコーテイング膜６を得
れば、表示５の部分と、その周辺部分のウレタン樹脂に
よる膜厚は等しくなる。If the display 5 and the coating film 6 are obtained by such a procedure, the thickness of the urethane resin film on the display 5 and its surrounding area will be equal.
以上説明したように本発明は、既設のハンドレールの表
面を研磨した後、この表面に切抜きを有するシートを用
いることによって表示を所望の膜厚にすることができる
と共に、着色ウレタン樹脂と透明ウレタン樹脂とはハン
ドレールと同様あるいはそれ以上の伸び率をもつよう容
易に設定できるため、走行中に受ける屈曲や伸縮によっ
て表示にひび割れが発生するようなことがなくなり、既
設の乗客コンベアに対しても容易に設けることができる
。As explained above, the present invention enables display to have a desired film thickness by polishing the surface of an existing handrail and then using a sheet having cutouts on this surface. Since the resin can be easily set to have an elongation rate similar to or higher than that of the handrail, the display will not crack due to bending and expansion/contraction during travel, and will also be suitable for existing passenger conveyors. It can be easily installed.
第１図は本発明の一実施例によるデザインハンドレール
の製造方法を示す作業工程図、第２図乃至第５図は第１
図の各工程に対応する作業中のデザインハンドレールの
斜視図、第６図乃至第１１図は本発明の他の実施例によ
るデザインハンドレールの製造方法による各工程に対応
する作業中のデザインハンドレールの斜視図である。
３・・・ハンドレール、４・・・シート、４ａ・・・切
抜キ、５・・・表示、６・・・コーテイング膜、１０〜
１６・・・工程。
第１図
第２図
第３図
第４図
第５図
第
６
図
第
図FIG. 1 is a work process diagram showing a method for manufacturing a designed handrail according to an embodiment of the present invention, and FIGS.
FIGS. 6 to 11 are perspective views of the designed handrail during work corresponding to each process in the figure, and FIGS. It is a perspective view of a rail. 3...Handrail, 4...Sheet, 4a...Cutout, 5...Display, 6...Coating film, 10~
16...Process. Figure 1 Figure 2 Figure 3 Figure 4 Figure 5 Figure 6 Figure
Claims (1)
、上記踏み段とほぼ同一速度で走行するゴム製のハンド
レールを備え、このハンドレールの表面に表示を有して
成るデザインハンドレールの製造方法において、上記ハ
ンドレールの研磨した表面に上記表示に対応する切抜き
を有するシートを貼付する工程と、上記切抜きを通して
上記ハンドレールの表面に着色ウレタン樹脂を用いて表
示する工程と、上記シートを剥す工程と、上記表示およ
びその近傍に液状の透明ウレタン樹脂を塗布してコーテ
ィング膜を形成する工程とを有することを特徴とするデ
ザインハンドレールの製造方法。1. A design hand that is arranged on the side of a step that runs between two entrances and exits, and that is equipped with a rubber handrail that runs at approximately the same speed as the step, and that has a display on the surface of the handrail. In the rail manufacturing method, a step of pasting a sheet having a cutout corresponding to the display on the polished surface of the handrail, a step of displaying the surface of the handrail through the cutout using a colored urethane resin, A method for manufacturing a designed handrail, comprising the steps of peeling off the sheet, and applying a liquid transparent urethane resin to the display and its vicinity to form a coating film.