JPH03261587A - Method for applying display printing to laminated sheet - Google Patents
Method for applying display printing to laminated sheetInfo
- Publication number
- JPH03261587A JPH03261587A JP5900090A JP5900090A JPH03261587A JP H03261587 A JPH03261587 A JP H03261587A JP 5900090 A JP5900090 A JP 5900090A JP 5900090 A JP5900090 A JP 5900090A JP H03261587 A JPH03261587 A JP H03261587A
- Authority
- JP
- Japan
- Prior art keywords
- printing
- release
- prepregs
- film
- prepreg
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、積層板の生産効率向上に有用た積層板り表示
印刷方法に関する0
〔従来り波相〕
電子機器に使用される積層板は、紙基伺又はガラス布基
材にフェノール樹脂、エポキシ柄脂、不飽和ポリエステ
ル樹脂等kf&乾燥して得たプリプレグを複数枚重ね、
加熱加圧して底形製造する0紙基材には一般に木材バル
ブあるいはりンターバルブを原料とする紙を使用し、ガ
ラス布基@にをニガラス線維金織った布を使用する。[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to a method for printing a display on a laminate board that is useful for improving the production efficiency of laminate boards. , Layering multiple sheets of prepreg obtained by kf & drying such as phenol resin, epoxy pattern resin, unsaturated polyester resin, etc. on paper base or glass cloth base material,
The paper base material used to produce the bottom shape by heating and pressing is generally paper made from wood bulbs or linter bulbs, and a glass cloth base is woven with glass fiber gold.
これらり基@には製造時に生ずる方向性があるが、この
方向性は積層板り寸法、反り、振れ及び強度等に影響が
大きいのしたがって、使用する基材の方向性金明示する
ことにたっている0従来行なわハる方向性り表示手段は
、基411にメーカー塩と共に何らかの方向性表示を印
刷し、最終的には積層板面にこり印刷が残るようにする
0〔発明が解決しようとする課題〕
上記σノ表示印刷り方法會次に説明すると、熱硬化性樹
脂を含浸すべき繊維基祠りロール巻とは別に、同質り表
示印刷をしたm維基拐りa−ル巻を用意する。各ロール
巻り基@に樹脂金含浸乾燥してプリプレグを作る。さら
に前者り基@から得たプリプレグ1[数枚と後者の印刷
をした基材から得たプリプレグの1枚とkmねて加熱加
圧して積層板とする。こり従来り方法は1手数が多く効
率の悪い作業である。These substrates have a directionality that occurs during manufacturing, but this directionality has a large effect on the dimensions, warpage, runout, strength, etc. of the laminate, so it is important to specify the directionality of the substrate material used. The conventional directional display means prints some kind of directional display on the base 411 along with the manufacturer's salt, and ultimately leaves a lumpy print on the surface of the laminate.[Problems to be Solved by the Invention] ] The above-mentioned σ display printing method will now be described.Apart from the fiber-based roll roll to be impregnated with a thermosetting resin, a m-fiber-based a-roll roll with homogeneous display printing is prepared. A prepreg is made by impregnating each roll with gold resin and drying it. Furthermore, several sheets of prepreg obtained from the former substrate and one sheet of prepreg obtained from the latter printed substrate were heated and pressed to form a laminate. However, the conventional method requires many steps and is inefficient.
又、積層板り各製造工程において、印刷された基@は、
含浸基刺棟σ)増加、含浸工程における切替工数の増加
及び咎定な品種りみといった制約があって生産効率低下
り原因とたる○
不発FJ#は1以上の問題点Kかんがみ、槓贋敬り生産
効4cり向よに有用ftm層板り表示印刷方法を提供す
ることt−目的とする〇
c課mを解決するための手段〕
上記の目的を達成するために、不発明は、細紐基材に熱
硬化性捌脂t−含授乾燥して得たプリプレグt−複数枚
重ね、その片面と、JI!型材シート0)該プリプレグ
とiui性良き印刷拐による表示印刷−とを重ね合わせ
て加熱加圧した俊、該離型材シートを剥がして印刷を転
写する積層板Q表示印刷方法である。In addition, in each manufacturing process of laminated board, the printed base@
There are constraints such as an increase in the number of impregnated substrates (σ), an increase in the number of man-hours required for switching during the impregnation process, and a predetermined selection of varieties, which are the causes of a decline in production efficiency. To provide a production efficiency 4c and more useful ftm layered display printing method. A plurality of sheets of prepreg t obtained by impregnating and drying a thermosetting oil t into a base material, one side of the prepreg t, and JI! Shape material sheet 0) This is a laminate Q display printing method in which the prepreg and display printing by printing with good IUI properties are superimposed, heated and pressed, and the release material sheet is peeled off to transfer the printing.
シート状離型剃としては1wI型性Q良いポリプロピレ
ンフィルム、トリアセテートフィルム、テトラフルオロ
エチレンフィルム等りプラスチックフィルム、又は離型
剤を塗布しr:lI!型紙、あるいは金属量、離型剤金
塗布した金属箔とする0積層板り製造は、#I維基材に
熱硬化性樹脂k。As a sheet release shaver, apply a plastic film such as polypropylene film, triacetate film, tetrafluoroethylene film, etc. with good I type property Q, or a release agent. For the manufacture of laminated boards using pattern paper or metal foil coated with gold release agent, #I fiber base material is coated with thermosetting resin K.
含浸乾燥して得たプリプレグを複数枚重ね、さらに#4
箔を1ねる場合は銅陥り反対側に表示印刷をした#型駒
を電ね、銅箔上使用しrIい場合は片側に表示印hlJ
をした離型駒を重ねる0こσノようにして得た構成@を
加熱加圧成形した後、離型材を剥がして片面に表示印刷
が転写された積層板を得る。Layer multiple sheets of prepreg obtained by impregnating and drying, and then #4
When using one piece of foil, use a # type piece with a display printed on the opposite side of the copper foil, and when using it on copper foil, use a display stamp on one side.
After the structure obtained by stacking the mold release pieces in a manner of 0 x σ is molded under heat and pressure, the mold release material is peeled off to obtain a laminate with a display print transferred to one side.
′l11m初シートり片面に、プリプレグに含反するP
J硬化性樹脂と接漕性り艮い印刷狗を用いて印刷する。'l11m The first sheet was coated with P on one side of the prepreg.
Print using a J-curing resin and a contact printing machine.
このw1unシートり印刷面とプリプレグとを重ね合わ
せ加熱加圧すると、離型材シートを剥がして印刷をプリ
プレグ面に転写することができるO
〔実施例〕
エポキシ樹脂ワニスを秤量125 g/rn’0)リン
ター紙に含浸し160℃で加熱半硬化して樹脂分60%
り塗工紙Aを得た。塗工紙Aを8枚重ね、予め表示を印
刷したテドラフィルム(altrフィルム)をその片f
lllVC重ね、反対側に接着剤を塗布しr35μm厚
σノ銅陥を亘ねた0こσノ徊成t170”0.90kg
/atで60分間加熱加圧り、@mフィルムを剥離して
片面銅張積層板を得た。By overlapping the printed surface of this w1un sheet and the prepreg and applying heat and pressure, the release material sheet can be peeled off and the printing can be transferred to the prepreg surface. Impregnated with linter paper and semi-cured by heating at 160℃ to make resin content 60%
Coated paper A was obtained. Layer 8 sheets of coated paper A, and add Tedra film (altr film) with a pre-printed indication on one piece f.
Layered VC, applied adhesive on the other side, and crossed a 35 μm thick σ copper recess.
/at was heated and pressed for 60 minutes, and the @m film was peeled off to obtain a single-sided copper-clad laminate.
実施例で得た塗工紙Aと向じリンター紙に予め表示を印
刷し、さらにAと同じワニスに含浸乾燥して樹脂分60
%り塗工紙Bを得た。塗工紙Aχ7枚重ね、さらに塗工
紙Bを1枚重ね、その上にテドラフィルム(#Il型フ
ィルム)kNhた0その反対IIIに接着剤性き65μ
m厚0)鋼箔を血ね、実施例と同条件で1.6關厚り片
面銅彊槓鳩板を得た。A label was printed in advance on linter paper opposite to coated paper A obtained in Example, and the same varnish as A was impregnated and dried to obtain a resin content of 60.
% coated paper B was obtained. Layer 7 sheets of coated paper Ax, then layer one sheet of coated paper B, and on top of that, apply Tedra film (#Il type film) kNh0 and the opposite side III with adhesive 65μ.
A steel foil with a thickness of 0) was soaked under the same conditions as in the example to obtain a single-sided copper dovetail plate with a thickness of 1.6 mm.
従来法による比較例において、複数枚りプリプレグに別
り棚脂含f9り流れを経た表示印刷付きプリプレグを1
枚重ねることは非能率な作業であるが、さらにこり例の
ように離型フィルムを電ねる場合は猶更である。In a comparative example using the conventional method, one prepreg with an indication print that was separated into multiple sheets of prepreg and subjected to shelf fat-containing F9 flow.
Layering the sheets is inefficient work, but it is even more so when the release film is electrolyzed as in the example.
Claims (1)
レグを複数枚重ね、その片面と、該プリプレグと接着性
良き印刷材による離型材シートの表示印刷面とを重ね合
わせて加熱加圧した後、該離型材シートを剥がして表示
印刷を積層板面に転写することを特徴とする積層板の表
示印刷方法。1. A plurality of prepregs obtained by impregnating and drying a thermosetting resin into a fiber base material are stacked, and one side of the prepreg is overlapped with the display printed surface of a release material sheet made of a printing material with good adhesion to the prepreg, and heated. 1. A method for display printing on a laminate, which comprises the steps of: after pressing, the release material sheet is peeled off to transfer the display print onto the surface of the laminate.