JPH03178387A - Method for disposal of harmful granular solid waste - Google Patents
Method for disposal of harmful granular solid wasteInfo
- Publication number
- JPH03178387A JPH03178387A JP2310099A JP31009990A JPH03178387A JP H03178387 A JPH03178387 A JP H03178387A JP 2310099 A JP2310099 A JP 2310099A JP 31009990 A JP31009990 A JP 31009990A JP H03178387 A JPH03178387 A JP H03178387A
- Authority
- JP
- Japan
- Prior art keywords
- waste
- asphalt
- asphalt emulsion
- slurry
- fly ash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、固型廃棄物質の分野に関し、より詳しくはア
スファルトのエマルジョン中での封入による毒性粒状物
質の処理方法に関する。DETAILED DESCRIPTION OF THE INVENTION Field of the Invention The present invention relates to the field of solid waste materials, and more particularly to a method for treating toxic particulate materials by encapsulation in an asphalt emulsion.
従来の技術
固型廃棄物の焼却のようなある種の工業的方法において
、鉛のような毒性成分が存在するために環境的に有害な
フライアシュ（ｆｌｙ ａｓｈ）が生ずる。そのよう
なフライアシュは、毒性成分が地下水面へ浸出するため
に、標準的な埋立地（１ａｎｄｆｉ ＩＩ）において処
分することはできない。BACKGROUND OF THE INVENTION Certain industrial processes, such as the incineration of solid waste, produce fly ash, which is environmentally hazardous due to the presence of toxic components such as lead. Such fly ash cannot be disposed of in standard landfills (1andfi II) due to the leaching of toxic components into the ground water table.
廃棄物に対し浸出抵抗性を与える物質のある場所でさえ
、埋立地は不足し、かつ、高価になってきている。Even where there are materials that provide leaching resistance to waste, landfills are becoming scarce and expensive.
フライアシュ中の毒性成分のレベルが十分に低い場合に
、過去に使用されたフライアシュ廃棄物の処理方法の一
つとして、アスファルトコンクリート舗装乃至アスファ
ルト道路（ｂｌａｃｋｔｏｐ） 中１：：充填剤（ｆｉ
ｌｔｅｒ）としてフライアシュを添加することが行われ
てきた。該処理方法は、フライアシュが高いレベルの毒
性成分を有している場合には、毒性成分の浸出が起こる
ために、不適当なものである。When the level of toxic components in fly ash is sufficiently low, one of the methods used in the past to dispose of fly ash waste is to use asphalt concrete pavement or asphalt road (blacktop) filler (fi).
It has been practiced to add fly ash as a filler. This treatment method is unsuitable when the fly ash has high levels of toxic components because leaching of the toxic components occurs.
ケムーテクニクス インコーホレイティラド（Ｃｈｅｍ
−Ｔ ｅｃｈｎｉｃｓ Ｉ ｎｃ、 ）に対して１９８
６年１１月１８日に発行された米国特許箱４．６２３゜
４６９号には、埋立地で処理できる疎水性固型物を生じ
るように液体廃棄物とアスファルトを混合することによ
り、親水性の液体及び半流動体の廃棄物を処理する方法
が開示されている。この方法によると、廃棄物カウンタ
ーイオンのイオン電荷が測定され、該廃棄物カウンター
イオンのイオン電荷と反対の粒子電荷を持つエマルジョ
ン化されたアスファルト懸濁液が選択される。十分量の
選択されたアスファルトエマルジョンが、疎水性固型物
へと合体するように液体廃棄物に加えられる。Chemu Technics Incophoretic Radiation (Chem
- 198 for Technics Inc.
U.S. Pat. A method of treating liquid and semi-liquid waste is disclosed. According to this method, the ionic charge of a waste counterion is measured and an emulsified asphalt suspension is selected that has a particle charge opposite to the ionic charge of the waste counterion. A sufficient amount of the selected asphalt emulsion is added to the liquid waste so that it coalesces into a hydrophobic solid.
その混合物は固体状態にまで固められる。、しかしなが
ら、この方法は高価な埋立空間を使用するものであり、
又最終生成物は商業的に有益ではない。The mixture is solidified to a solid state. However, this method uses expensive landfill space;
Also, the final product is not commercially useful.
アスファルトエマルジョン又はエマルジョン化されたア
スファルトは、水中にアスファルトセメント又はビチュ
ーメン（ｂＮｕｍｅｎ）の微小滴乃至微小粒が分散した
エマルジョンである。該エマルジョンは、界面活性剤の
ような乳化剤の存在により安定化される。使用される乳
化剤により、そのようなエマルジョンは、陰性に荷電し
たアスファルト小滴を有するアニオン性のもの又は陽性
に荷電したアスファルト小滴を有するカチオン性のもの
になる。そのようなエマルジョンは、多くの用途につい
て商業的に利用できる。そのような用途の一つは、スラ
リーを製造するために水とエマルジョン化アスファルト
、微小骨材（ｆｉｎｅ ａｇｇｒｅｇａｔｅ）及び鉱物
充填剤（ｍｉｎｅｒａｌ ｆｉｉｌｅｒ）を混合したア
スファルトエマルジョンスラリーシールを形成すること
である。水の留去により乾燥したとき、スラリーは厚い
、ゼリーのようなコーテイング物質となり、それは舗道
や車道等を塗装するための塗料のように湿った状態で適
用される。An asphalt emulsion or emulsified asphalt is an emulsion of microdroplets or microparticles of asphalt cement or bitumen (bNumen) dispersed in water. The emulsion is stabilized by the presence of emulsifiers such as surfactants. Depending on the emulsifier used, such emulsions can be anionic with negatively charged asphalt droplets or cationic with positively charged asphalt droplets. Such emulsions are commercially available for many applications. One such application is to form an asphalt emulsion slurry seal by mixing water with emulsified asphalt, fine aggregate, and mineral filler to produce a slurry. When dried by distillation of water, the slurry becomes a thick, jelly-like coating material that is applied wet as a paint for painting pavements, driveways, etc.
それゆえ、浸出に抵抗性であり、しかも高価な埋立空間
を要求することなく商業的に使用できる態様で、毒性粒
状廃棄物を安全に処理する方法が必要とされている。Therefore, there is a need for a method to safely dispose of toxic particulate waste in a manner that is resistant to leaching and yet can be used commercially without requiring expensive landfill space.
課題を解決するための手段
本発明は、アスファルトエマルジョンスラリーを形成し
、該スラリーを商業用のアスファルトエマルジョンスラ
リーシールとして使用することによる有害な廃棄物イオ
ンを含有する有害な粒状廃棄物の処理方法を提供する。SUMMARY OF THE INVENTION The present invention provides a method for treating hazardous particulate waste containing hazardous waste ions by forming an asphalt emulsion slurry and using the slurry as a commercial asphalt emulsion slurry seal. provide.
その方法は以下のａ）〜Ｃ）のステップを包含する。The method includes the following steps a) to C).
ａ）アスファルト、水及び前記粒状廃棄物の安定なエマ
ルジョンを形成するために適当な乳化剤を選択するステ
ップ、
ｂ）安全な浸出特性を有するアスファルトエマルジョン
スラリーを形成する比率で粒状廃棄物とアスファルトエ
マルジョンを混合するステップ、Ｃ）前記アスファルト
エマルジョンスラリーを現存する商業的な用途に利用す
るステップ。a) selecting a suitable emulsifier to form a stable emulsion of asphalt, water and said particulate waste; b) combining the particulate waste and asphalt emulsion in a ratio to form an asphalt emulsion slurry with safe leaching properties. C) Utilizing the asphalt emulsion slurry for existing commercial applications.
本発明において、好適なアスファルトエマルジョンスラ
リーは、構成要素としてフライアシュを用いて調製され
る。好適なスラリーを得るために、まず最初にエマルジ
ョン中のアスファルト小滴がフライアシュ粒子を封入す
るように適当な乳化剤を選択しなければならない。この
ことは、フライアシュ、アスファルト、水及び商業的に
入手可能な乳化剤を含むサンプル混合物を調製し、どの
組合せが適切に混合するかを視覚的に決定することによ
り行うことができる。もし、エマルジョンに加えるとき
の廃棄フライアシュ物質のイオン電荷が測定できる場合
には、廃棄物イオンと反対の電荷をもつ適切な乳化剤が
選択される。アニオン性又はカチオン性のいずれかのア
スファルトエマルジョンが、粒状廃棄物の性質により要
求される。In the present invention, a suitable asphalt emulsion slurry is prepared using fly ash as a component. To obtain a suitable slurry, a suitable emulsifier must first be selected so that the asphalt droplets in the emulsion encapsulate the fly ash particles. This can be done by preparing a sample mixture containing fly ash, asphalt, water and a commercially available emulsifier and visually determining which combinations mix properly. If the ionic charge of the waste fly ash material when added to the emulsion can be determined, an appropriate emulsifier with an opposite charge to the waste ions is selected. Either anionic or cationic asphalt emulsions are required depending on the nature of the particulate waste.
適切な乳化剤を決定した後、浸出の程度をテストするた
め及び環境的に許容できる範囲内の浸出に抑えるフライ
アシュの含有率を選択するために、混合物中のフライア
シュの含有率の一定の範囲をカバーするようフライアシ
ュ及びアスファルトエマルジョンのサンプル混合物を調
製する。望ましい結果は、アスファルト小滴によりフラ
イアシュ粒子を完全に封入したときに最も効果的に達成
される。その上、アスファルトエマルジョンとフライア
シュの相対的な比率は、混合物が固型物というよりはむ
しろアスファルトエマルジョンスラリーを調製するよう
に選択される。After determining a suitable emulsifier, a range of fly ash contents in the mixture is used to test the extent of leaching and to select a fly ash content that keeps leaching within an environmentally acceptable range. Prepare a sample mixture of fly ash and asphalt emulsion to cover. The desired results are most effectively achieved when the fly ash particles are completely encapsulated by the asphalt droplets. Additionally, the relative proportions of asphalt emulsion and fly ash are selected such that the mixture forms an asphalt emulsion slurry rather than a solid.
調製された最終的なアスファルトエマルジョンスラリー
は、例えば道路用又は商業上／工業上の敷地用のスラリ
ーコート舗装用材（ｐａｖｅｍｅｎｔ）又は地面を被う
シーラー（ｓｅａｌｅｒ）のような、スラリーコート舗
装用材（ｐａｖｅｍｅｎｔ）乃至シーラー（ｓｅａｌｅ
ｒ）として通常の方法により商業的に使用できる。これ
ら適用の場合の重量／面積比は、皿型的には有害な廃棄
物の濃度を最小限にするために低くするのが好ましいが
、毒性廃棄物のタイプ及び濃度によっても変わり得る。The final asphalt emulsion slurry prepared can be used as a slurry coated pavement, such as a slurry coated pavement or a ground covering sealer, for example for roads or commercial/industrial sites. ) to sealer
r) can be used commercially by conventional methods. The weight/area ratio for these applications is preferably low in order to minimize the concentration of hazardous waste in a dish format, but may also vary depending on the type and concentration of toxic waste.
この方法で、有害なフライアシュは商業的に有用な方法
で安全に処理され、廃棄物を貯えるための埋立用地の必
要性は最小限となる。In this way, hazardous fly ash is safely disposed of in a commercially useful manner and the need for landfill space to store the waste is minimized.
実施例
危険なレベルの鉛を含む有害なフライアシュを使用した
。特に、フライアシュは、バグハウス濾過空気放出シス
テム（ｂａｇ ｈｏｕｓｅ ｆｉＨｒａｊｉｏｎ ａｉ
ｒｅｍｉｓｓｉｏｎ ｓｙｓｔｅｍ）及び焼却した都市
の廃棄物の収集装置から得た。該フライアシュは、ブリ
ティッシュ コロンビア ウェイスト マネージメント
アクト（ＢｒＮｉｓｈ Ｃｏｌｕｍｂｉａ Ｗａｓ
ｔｅＭａｎａｇｅｍｅｎｔ Ａｃ＋） ″リーシーｊ
”７ト イクストラクション プロシージャー−スペシ
ャル ウェイスト、スケジュール４” （’Ｌ ｅａｃ
ｈａｔｅＥ ｘｊｒａｃｊｉｏｎ Ｐ ｒｏｃｅｄｕｒ
ｅｓ −５ｐｅｃｉａｌ−Ｗａｓｔｅ。Example: Hazardous fly ash containing dangerous levels of lead was used. In particular, flyash is a bag house filtered air release system.
remission system) and incinerated municipal waste collection equipment. The flyash is subject to the British Columbia Waste Management Act.
teManagement Ac+)
``7 Extraction Procedures - Special Waste, Schedule 4''('L eac
HateE xjracjion Procedur
es-5special-Waste.
５ｃｈｅｄｕｌｅ ４“）の許容浸出液試験限界を越え
る鉛を含んでいた。換言すると、調製された浸出液は、
５ ｐｐｍを越える鉛を含んでいた。In other words, the prepared leachate contained lead in excess of the permissible leachate test limits for
It contained more than 5 ppm of lead.
適当なエマルジョンを得るために、種々の乳化剤が、フ
ライアシュ、アスファルト及び水の混合物について試験
された。その結果、このフライアシュの場合には、アル
マーク ケミカル カンパ＝ −（Ａｒｍａｋ Ｃｈ
ｅｍｉｃａｌ Ｃｏ、）により製造されたＲＥＤＩ−Ｋ
ＯＴＥ Ｅ−５７６２（商標）が好適な安定エマルジ
ョンを与えることを見出した。Various emulsifiers were tested on fly ash, asphalt and water mixtures to obtain suitable emulsions. As a result, in the case of this flyash, Armak Chemical Campa = -(Armak Ch
REDI-K manufactured by chemical Co.)
It has been found that OTE E-5762(TM) provides a suitable stable emulsion.
５重量％、１０重量％、１５重量％、２０重量％及び２
５重量％の比率でフライアシュを含む、アスファルトエ
マルジョンの種々のサンプル混合物が調製された。“ス
ペシャル ウェイスト−スケジュール ４“ （“Ｓ
ｐｅｃｉａｌ Ｗａｓｔｅ −８ｃｈｅｄｕｌｅ ４
”）中に規定され、ブリティッシュコロンビア ウェイ
スト マネージメント アクト （Ｂｒｉｔｉｓｈ
Ｃｏｌｕｍｂｉａ Ｗａｓｔｅ Ｍａｎ
ａｇｅｍｅｎｔＡｃ＋）（１９８８年２月２９日）によ
り規定された水浸出試験を、上記サンプルについて行っ
た。5% by weight, 10% by weight, 15% by weight, 20% by weight and 2
Various sample mixtures of asphalt emulsions were prepared containing fly ash in a proportion of 5% by weight. “Special Waste Schedule 4” (“S
special waste -8chedule 4
”) and the British Columbia Waste Management Act (British
Columbia Waste Man
A water leaching test as specified by J. Co., Ltd. (February 29, 1988) was performed on the above samples.
各サンプルからの浸出液が調製され分析された。Leachate from each sample was prepared and analyzed.
侵出液中に見出された鉛のレベルは、例えばフライアシ
ュが１５重量％のサンプルで４． Ｏ２ｐｐｍ及び２
５重量％のサンプルで３． ３９ｐｐｍであり、許容で
きるものであることがわかった。The level of lead found in the leachate was, for example, 4.5% in a sample with 15% fly ash by weight. O2 ppm and 2
3. with 5% by weight sample. 39 ppm, which was found to be acceptable.
２５重量％のサンプルを除き、種々のサンプルがアスフ
ァルトエマルジョンスラリーとしての使用のために適当
な組成物であることが見出された。With the exception of the 25% by weight sample, various samples were found to be suitable compositions for use as asphalt emulsion slurries.
２５重量％のサンプルは、舗道のコーティング又は同様
な用途のための実用的なスラリーとしては通常許容でき
るものではないように思われる。A 25% by weight sample would not normally appear to be acceptable as a practical slurry for pavement coatings or similar applications.
当業者には明らかであるが、上記構成の種々の修飾及び
調節が、本発明の精神及び特許請求の範囲に従って解釈
される範囲から離れることなくなされ得る。As will be apparent to those skilled in the art, various modifications and adjustments to the above configurations may be made without departing from the spirit of the invention and its scope as construed in accordance with the scope of the claims.
（以 上）(that's all)
Claims (15)
ファルト、水及び前記粒状廃棄物の安定なエマルジョン
を形成するために適当な乳化剤を選択し、 ｂ）安全な浸出特性を有するアスファルトエマルジョン
スラリーを形成する比率で粒状廃棄物とアスファルトエ
マルジョンとを混合し、 ｃ）得られたアスファルトエマルジョンスラリーを現存
する商業的用途に利用すること を特徴とする方法。(1) A method for treating hazardous granular waste, comprising: a) selecting an appropriate emulsifier to form a stable emulsion of asphalt, water, and said granular waste; and b) asphalt having safe leaching properties. A method comprising: mixing particulate waste and an asphalt emulsion in proportions to form an emulsion slurry; c) utilizing the resulting asphalt emulsion slurry for existing commercial applications.
１）に記載の方法。(2) Claim (2) wherein the granular waste is fly ash.
The method described in 1).
ｎｔ）のコーティングである請求項（１）に記載の方法
。(3) Where the existing commercial use is
The method according to claim 1, which is a coating of nt).
ョンスラリーに３０重量％未満含まれる請求項（２）に
記載の方法。(4) The method according to claim 2, wherein the fly ash is contained in the asphalt emulsion slurry at less than 30% by weight.
理方法であって、 ａ）廃棄物イオンのイオン電荷を決定すること、ｂ）前
記粒状廃棄物と安定な混合物を形成するのに適したアス
ファルトエマルジョンを選択すること、 ｃ）アスファルトエマルジョンスラリーを形成する比率
で粒状廃棄物とアスファルトエマルジョンを混合するこ
と、 ｄ）現存する商業的用途に前記アスファルトエマルジョ
ンスラリーを利用すること を特徴とする方法。(5) A method for treating hazardous particulate waste containing hazardous waste ions, comprising: a) determining the ionic charge of the waste ions; and b) forming a stable mixture with said particulate waste. c) mixing particulate waste and asphalt emulsion in proportions to form an asphalt emulsion slurry; d) utilizing said asphalt emulsion slurry for existing commercial applications. Method.
５）に記載の方法。(6) Claim (6) wherein the granular waste is fly ash.
The method described in 5).
ｎｔ）のコーティングである請求項（５）に記載の方法
。(7) Where the existing commercial use is
The method according to claim 5, which is a coating of nt).
ョンスラリーに３０重量％未満含まれる請求項（５）に
記載の方法。(8) The method according to claim 5, wherein the asphalt emulsion slurry contains less than 30% by weight of the fly ash.
廃棄物がアスファルト中で完全に封入される状態で、ア
スファルト、水及び前記粒状廃棄物の安定なエマルジョ
ンを形成するのに適当な乳化剤を選択すること、 ｂ）安全な浸出特性を有するアスファルトエマルジョン
スラリーを形成する割合で粒状廃棄物とアスファルトエ
マルジョンを混合すること、ｃ）前記アスファルトエマ
ルジョンスラリーを現存する商業的用途で利用すること を特徴とする方法。(9) A method for treating hazardous granular waste, the method comprising: a) forming a stable emulsion of asphalt, water and said granular waste, with the granular waste completely encapsulated in the asphalt; b) mixing the granular waste and asphalt emulsion in proportions that form an asphalt emulsion slurry with safe leaching properties; c) utilizing said asphalt emulsion slurry in existing commercial applications. A method characterized by:
（９）に記載の方法。(10) The method according to claim 9, wherein the granular waste is fly ash.
ｅｎｔ）のコーティングである請求項（９）に記載の方
法。(11) The existing commercial use is for pavem.
10. The method according to claim 9, wherein the method is a coating of .ent).
０重量％未満の前記フライシュを含む請求項（９）に記
載の方法。(12) The asphalt emulsion slurry contains 3
10. A method according to claim 9, comprising less than 0% by weight of said flysch.
ョンスラリー。(13) Asphalt emulsion slurry containing hazardous particulate waste.
請求項（１３）に記載のアスファルトエマルジョンスラ
リー。(14) The asphalt emulsion slurry according to claim (13), wherein the hazardous granular waste is fly ash.
ュを含む請求項（１４）に記載のアスファルトエマルジ
ョンスラリー。(15) The asphalt emulsion slurry according to claim 14, wherein the slurry contains less than 30% by weight of fly ash.