JPH03121183A - Composition capable of facilitating bonding - Google Patents
Composition capable of facilitating bondingInfo
- Publication number
- JPH03121183A JPH03121183A JP25804489A JP25804489A JPH03121183A JP H03121183 A JPH03121183 A JP H03121183A JP 25804489 A JP25804489 A JP 25804489A JP 25804489 A JP25804489 A JP 25804489A JP H03121183 A JPH03121183 A JP H03121183A
- Authority
- JP
- Japan
- Prior art keywords
- polyester film
- component
- easily adhesive
- solvent
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、易接着性組成物に関し、特に、延伸ポリエス
テルフィルムと、その上に設けられる回路パターン層な
どの紫外線硬化樹脂層や、タッチパネル用の透明シート
などとの両者を接合するのに優れた易接着性組成物に関
する。Detailed Description of the Invention (Industrial Field of Application) The present invention relates to an easily adhesive composition, and particularly to a stretched polyester film, an ultraviolet curing resin layer such as a circuit pattern layer provided thereon, and a composition for use in touch panels. This invention relates to an easily adhesive composition that is excellent for bonding transparent sheets and the like.
(従来の技術及びその解決すべき課題)ポリエステルフ
ィルムは、機械的強度や透明性などの諸性能が良好であ
るために、従来より可撓性印刷回路板や、タッチパネル
板などに多用されている。このような回路板などにおい
ては、ポリエステルフィルムの表面エネルギーが比較的
小さく、そのため印刷回路層や、タッチパネル用透明シ
ートなどとの接着性に劣るために、従来よりポリエステ
ルフィルムと、これら印刷回路層や透明シート層などと
の間の接着力を向上させるための易接着性層を形成させ
ることが行われている。(Conventional technology and problems to be solved) Polyester film has been widely used for flexible printed circuit boards, touch panel boards, etc. due to its good properties such as mechanical strength and transparency. . In such circuit boards, polyester film has a relatively low surface energy, and therefore has poor adhesion to printed circuit layers and transparent sheets for touch panels. Formation of an easily adhesive layer to improve the adhesive strength between the transparent sheet layer and the like has been carried out.
このような易接着性層としては、例えば、主成分として
溶媒可溶性の飽和ポリエステルを含有する塗料に、(1
)イソシアネートアダクトを添加したり、(2)ウレタ
ンポリマーを添加したり、(3)ウレタンポリマーと、
イソシアネートアダクトとを添加したり、更に(4)ア
クリルポリマーを添加した塗料から形成することが提案
されている。As such an easily adhesive layer, for example, a paint containing a solvent-soluble saturated polyester as a main component (1
) adding an isocyanate adduct, (2) adding a urethane polymer, (3) adding a urethane polymer,
It has been proposed to form the coating material by adding an isocyanate adduct or (4) adding an acrylic polymer.
しかしながら、これらの塗料を使用して形成された易接
着性層との接着力は必ずしも十分ではなく、更に接着力
の優れた易接着性組成物が強く要望されていた。However, the adhesive strength with the easily adhesive layer formed using these paints is not necessarily sufficient, and there has been a strong demand for an easily adhesive composition with even better adhesive strength.
(発明の目的)
従って、本発明は、ポリエステルフィルムと、その上に
設けられる層との間の接着力を向上する易接着性組成物
を提供することを目的とする。(Objective of the Invention) Therefore, an object of the present invention is to provide an easily adhesive composition that improves the adhesive strength between a polyester film and a layer provided thereon.
(課題を達成するために手段)
本発明者は、上記目的を達成するために鋭意検討した結
果、以下の成分:
(a) 溶媒可溶性飽和ポリエステル樹脂、ら)ポリ
イソシアネート、及び
(c)2以上のビニル基又はイソプロペニル基を有する
アクリレート、
を含有する組成物により、上記目的が達成できることを
見出し、本発明に到達したものである。(Means for Achieving the Object) As a result of intensive studies to achieve the above object, the inventor of the present invention found the following components: (a) solvent-soluble saturated polyester resin, et al. polyisocyanate, and (c) 2 or more. The inventors have discovered that the above object can be achieved by a composition containing an acrylate having a vinyl group or an isopropenyl group, and have arrived at the present invention.
以下、本発明について詳述する。The present invention will be explained in detail below.
本発明で使用される飽和ポリエステル樹脂(成分(a)
)は溶媒可溶性であり、易接着性組成物用の塗料におい
て溶解するものである。このような溶媒可溶性飽和ポリ
エステル樹脂は公知であり、例えば特公昭51−102
73号公報に記載されているように、飽和ポリエステル
樹脂、例えばポリエチレンテレフタレート樹脂を製造す
る場合、その製造原料であるテレフタル酸とエチレング
リコールとともに第3成分として、他の酸成分、例えば
、アジピン酸やセバシン酸などの他の脂肪族二塩基酸、
イソフタル酸やオルソフタル酸、ジフェニルジカルボン
酸などの芳香族二塩基酸又は、他のアルコール成分、例
えば、■、2−プロピレングリコール、1.3−プロピ
レングリコール、1゜4−プロピレングリコール、1,
3−ブタンジオール、ジエチレングリコール、トリエチ
レングリコール等のグリコール類を配合して反応させる
ことによって得ることができる。このような第3成分を
配合することにより、飽和ポリエステル樹脂の結晶性を
減少させ、飽和ポリエステル樹脂の溶媒への溶解性を高
めたものである。Saturated polyester resin used in the present invention (component (a)
) is solvent soluble and dissolves in paints for easily adhesive compositions. Such solvent-soluble saturated polyester resins are known, for example, as disclosed in Japanese Patent Publication No. 51-102
As described in Publication No. 73, when producing a saturated polyester resin such as a polyethylene terephthalate resin, other acid components such as adipic acid or other aliphatic dibasic acids such as sebacic acid,
Aromatic dibasic acids such as isophthalic acid, orthophthalic acid, diphenyldicarboxylic acid, or other alcohol components, such as ■, 2-propylene glycol, 1,3-propylene glycol, 1°4-propylene glycol, 1,
It can be obtained by blending and reacting glycols such as 3-butanediol, diethylene glycol, and triethylene glycol. By blending such a third component, the crystallinity of the saturated polyester resin is reduced and the solubility of the saturated polyester resin in a solvent is increased.
本発明で使用されるポリイソシアネート(成分(b))
は、1分子中にイソシアネート基を2個以上有する化合
物である。ポリイソシアネートとしては、例えばトリメ
チロールプロパンアダクト型や、ビューレット型、更に
はトリマー型など種々のポリイソシアネートが挙げられ
る。具体的には、例えば以下のポリイソシアネートを挙
げることができる。Polyisocyanate used in the present invention (component (b))
is a compound having two or more isocyanate groups in one molecule. Examples of the polyisocyanate include various polyisocyanates such as trimethylolpropane adduct type, biuret type, and even trimer type. Specifically, the following polyisocyanates can be mentioned, for example.
1、トリメチロールプロパンアダクト型1
(1) C113C1(2−C+C1(20−[ニー
NH(cH2)6NCD)32、ビューレフト型
3、トリマー型
(cH2) 6NCO
本発明で使用される2以上のビニル基又はインプロペニ
ル基を有するアクリレート(成分(c))としては、以
下のアクリレートを挙げることができきる。1. Trimethylolpropane adduct type 1 (1) C113C1 (2-C+C1 (20-[nee NH(cH2)6NCD) 32, Beauleft type 3, trimer type (cH2) 6NCO Two or more vinyls used in the present invention As the acrylate (component (c)) having an impropenyl group or an impropenyl group, the following acrylates can be mentioned.
1、 CL=CHCO+ 0CH2CH辻TOCOCH
=CH2(n =4〜9)2、 (cH,=CHCOO
CH2す、 C−CH2CH3、(cH,=CHC00
C)+2 +rC’CH,CH。1, CL=CHCO+ 0CH2CH TsujiTOCOCH
=CH2(n =4~9)2, (cH,=CHCOO
CH2S, C-CH2CH3, (cH,=CHC00
C)+2 +rC'CH,CH.
1 CH2C1120COCH=C)I。1 CH2C1120COCH=C)I.
5、 [(c’)I2=(’H−CDΩCH2→丁[
ニーCH,→2D6、 CH,=[:HCoo−R−
00CNII−4−R−NHCOO−(ボリト)い−0
0CNII +−R−NHCO[]−R’−[1[:D
C)I=CH。5, [(c')I2=('H-CDΩCH2→D[
Knee CH,→2D6, CH,=[:HCoo-R-
00CNII-4-R-NHCOO-(borito)i-0
0CNII +-R-NHCO[]-R'-[1[:D
C) I=CH.
(ただし、R及びR′はそれぞれアルキル基又はアリー
ル基を示す。)
上記各成分の配合割合としては、成分(a):成分ら)
:成分(c)の重量割合は、100:10〜30:5〜
50が好ましい。成分(b)の量が上限より多くなると
、被膜が硬くなりすぎ、接着力が低下し、一方、下限よ
りも少なくなると、硬化性が劣る傾向にある。成分(c
)の量が上限よりも多くなると、被膜のブロッキング性
が大きくなって塗布フィルムの巻取りが困難となり、下
限よりも少なくなると接着性能が小さ(なる傾向にあり
、好ましくない。(However, R and R' each represent an alkyl group or an aryl group.) The blending ratio of each of the above components is component (a):component etc.)
:The weight ratio of component (c) is 100:10~30:5~
50 is preferred. When the amount of component (b) is more than the upper limit, the film becomes too hard and the adhesive strength is reduced, while when it is less than the lower limit, the curability tends to be poor. Component (c
) If the amount exceeds the upper limit, the blocking property of the coating increases, making it difficult to wind up the coated film, and if it decreases below the lower limit, the adhesive performance tends to be low, which is not preferable.
易接着性組成物には、必要に応じて、上記成分の他に、
例えば、ジブチル錫ジラウレートや、ジブチル錫ジオク
テートなどのイソシアネート反応促進剤、ベンゾフェノ
ンや、ベンゾイルアルキルエーテル、ヒドロキシメチル
フェニルプロパノンなどの紫外線開始剤、シリカ微粉末
や、タルク微粉末、炭酸カルシウム微粉末などのブロッ
キング防止剤等を配合することもできる。In addition to the above components, the easily adhesive composition may contain, if necessary,
For example, isocyanate reaction promoters such as dibutyltin dilaurate and dibutyltin dioctate, ultraviolet initiators such as benzophenone, benzoyl alkyl ether, and hydroxymethylphenylpropanone, fine silica powder, fine talc powder, fine calcium carbonate powder, etc. An antiblocking agent or the like may also be added.
易接着性組成物塗料を調製する場合において、上記成分
(a)〜(c)を、トルエン、メチルエチルケトン(M
EK)、酢酸エチルなどの適当な溶媒に溶解し、必要に
応じて紫外線開始剤などの添加剤を配合することによっ
て、易接着性組成物塗料が調製される。塗料の濃度は、
一般に3〜30重量%である。When preparing an easily adhesive composition paint, the above components (a) to (c) are combined with toluene, methyl ethyl ketone (M
EK), ethyl acetate, or other appropriate solvent, and optionally blending additives such as an ultraviolet initiator to prepare an easily adhesive composition paint. The concentration of the paint is
Generally from 3 to 30% by weight.
このようにして得られた塗料は、ポリエステルフィルム
の少なくとも片面に塗布し、90〜130℃で15〜6
0秒乾燥した後、例えば45〜80℃で1〜6日間エー
ジングすることによって、易接着性層を形成する。塗料
は、ポリエステルフィルム上で乾燥後の厚みが0.2〜
10g/m″となるような量で塗布される。The paint thus obtained is applied to at least one side of a polyester film and heated to 15 to 60°C at 90 to 130°C.
After drying for 0 seconds, an easily adhesive layer is formed by aging, for example, at 45 to 80°C for 1 to 6 days. The paint has a thickness of 0.2~ after drying on the polyester film.
It is applied in an amount of 10 g/m''.
本発明の易接着性層が設けられるポリエステルフィルム
としては、従来よりこの種の可撓性印刷回路板やタッチ
パネル等において使用されているものは何でも使用する
こができる。ポリエステルフィルムの厚みは一般に25
〜250μmが好ましい。As the polyester film on which the easily adhesive layer of the present invention is provided, any film conventionally used in flexible printed circuit boards, touch panels, etc. of this type can be used. The thickness of polyester film is generally 25
~250 μm is preferred.
(実施例)
以下、本発明について実施例により更に詳細に説明する
。(Example) Hereinafter, the present invention will be explained in more detail with reference to Examples.
実施例1〜2、比較例1〜2
可撓性印刷板の用途に使用するために、以下の第1表に
記載した配合割合で、固形分濃度が5重量%の塗料を調
製し、厚み125μmのポリエステルフィルム(東し■
製ルミラー1253)に乾燥塗布量が0.3g/m’と
なるように塗布、乾燥し、次いで60℃で3日間エージ
ングして、易接着性層を有するポリエステルフィルムを
製造した。Examples 1-2, Comparative Examples 1-2 In order to use it for flexible printing plates, paints with a solid content concentration of 5% by weight were prepared at the blending ratios listed in Table 1 below. 125 μm polyester film (Toshi ■
Lumirror 1253) manufactured by Co., Ltd. was coated to a dry coating weight of 0.3 g/m', dried, and then aged at 60° C. for 3 days to produce a polyester film having an easily adhesive layer.
第1表
* I 5TAFIX−PLC(富士写真フィルム■
)*2 バイロン−200(東洋紡績■)1
*3 C1(、CH2−C−+CH,[]−C−Nl
((cH2)6NCO)3*4 [(cH2=CH−
[’DOC)12+rIl’−[’)12→r−D*5
C!(、=CHC00−R’−00CNL4−R
−NHCOO−(ポリトル)−0OCNH÷、 R−N
HCO[]−R′−DC[]CH=CH2*6 V
MCI(U、C,C,) VCC/V八c10へ=8
6/13/1*7 アエロジル200 (日本アエロジ
ル@)* 8 MEK/ )ルエン=1/1実施例及
び比較例で得られたポリエステルフィルムを、160℃
で1時間アニールした後、ゴバン目試験及び180度剥
離試験を行った。ゴバン目試験は、常態試験については
、アチソン社製紫外線樹脂ED450SSを厚さ約20
μmに塗布し、紫外線で硬化した後の試料で、一方、耐
湿試験については、同試料を60℃、95%RHの雰囲
気中に6日間放置した後の試料で、JISK5400に
従って紫外線硬化フィルムをゴバン目にカットし、次い
でJISC5012に従ってテープを貼り、テープを剥
がすことによって行った。Table 1 * I 5TAFIX-PLC (Fuji Photo Film■
) *2 Byron-200 (Toyobo ■) 1 *3 C1 (, CH2-C-+CH, []-C-Nl
((cH2)6NCO)3*4 [(cH2=CH-
['DOC)12+rIl'-[')12→r-D*5
C! (,=CHC00-R'-00CNL4-R
-NHCOO- (Polytle) -0OCNH÷, R-N
HCO[]-R'-DC[]CH=CH2*6 V
MCI (U, C, C,) VCC/V8c10=8
6/13/1 *7 Aerosil 200 (Japan Aerosil @) * 8 MEK/ ) Luene = 1/1 The polyester films obtained in the examples and comparative examples were heated at 160°C.
After annealing for 1 hour, a cross-cut test and a 180 degree peel test were conducted. For the eye test, for the normal test, ultraviolet resin ED450SS manufactured by Acheson was used with a thickness of approximately 20 mm.
The sample was coated on a micrometer and cured with ultraviolet rays. On the other hand, for the moisture resistance test, the same sample was left in an atmosphere of 60°C and 95% RH for 6 days. This was done by making a cut, then applying tape according to JISC5012, and then peeling off the tape.
180度剥離試験は、常態試験については、アチソン社
製紫外線樹脂ED450SS/ML−25089=50
150を約75μmに塗布し、紫外線で硬化した後の試
料で、一方、耐湿試験については、同試料を60℃、9
5%RHの雰囲気中に6日間放置した後の試料で、紫外
線樹脂硬化フィルムとポリエステルフィルムとの間の接
着強度を測定した(180度剥離、引張速度200mm
Z分)。For the 180 degree peel test, for the normal test, ultraviolet resin ED450SS/ML-25089 made by Acheson Co., Ltd. = 50
150 was applied to a thickness of about 75 μm and cured with ultraviolet rays.On the other hand, for the moisture resistance test, the same sample was coated at 60°C and 90°C.
The adhesive strength between the ultraviolet resin cured film and the polyester film was measured using a sample that had been left in an atmosphere of 5% RH for 6 days (180 degree peeling, tensile speed 200 mm).
Z minutes).
結果を以下の第2表に示す。The results are shown in Table 2 below.
第2表から、易接着性層を介してポリエステルフィルム
に紫外線硬化樹脂層を設けることにより紫外線硬化樹脂
とポリエステルフィルムとの接着力を常態及び耐湿条件
の両方で優れていることが分かる。従って、本発明の易
接着性層を有するポリエステルフィルムは可撓性印刷回
路板として有用であることが分かる。From Table 2, it can be seen that by providing an ultraviolet curable resin layer on a polyester film via an easily adhesive layer, the adhesive force between the ultraviolet curable resin and the polyester film is excellent both under normal conditions and under moisture-resistant conditions. Therefore, it can be seen that the polyester film having the easily adhesive layer of the present invention is useful as a flexible printed circuit board.
第2表
実施例3、比較例3〜4
タッチパネル板の用途に使用するために、以下の第3表
に記載した配合割合で、固形分濃度が25重量%の塗料
を調製し、厚み100μmのボ、リエステルフィルム(
東し@製ルミラー100T)に乾燥塗布量が約5 g
/ m”となるように塗布し、次いで60℃で3日間乾
燥して、易接着性層を有するポリエステルフィルムを製
造した。Table 2 Example 3, Comparative Examples 3 to 4 In order to use it for touch panel board applications, a paint with a solid content concentration of 25% by weight was prepared using the blending ratios listed in Table 3 below. Bo, Lyester film (
The dry coating amount is approximately 5 g on Lumirror 100T manufactured by Toshi@.
/m'' and then dried at 60°C for 3 days to produce a polyester film having an easily adhesive layer.
第3表
*1 バイロン−200(東洋紡績@)*2 5TAF
IY−PLC(富士写真フィルム@)*3 第1表*3
と同じ
*4 第1表*4と同じ
*5 VMCH(U、C0C,) VCf/VAc1
0H=86/13/1*6 アエロジル200 (日本
アエロジル■)* 7 MBK/ )ルエンー1/1
実施例及び比較例で得られたポリエステルフィルムの易
接着性層に、紫外線樹脂として三菱レーヨン■製ダイヤ
ビームUR−6520を約10μmの厚みとなるように
塗布し、その上にポリエステルマットフィルムを貼り、
紫外線を照射し、紫外線樹脂を硬化した。ポリエステル
マットフィルムを剥がすと、紫外線樹脂層の表面に梨地
面が残った。この梨地面を爪で引っ掻くことにより、傷
の付き方の良否を判定したく梨地引っ掻き強度試験)。Table 3 *1 Byron-200 (Toyobo @) *2 5TAF
IY-PLC (Fuji Photo Film @) *3 Table 1 *3
Same as *4 Same as Table 1 *4 *5 VMCH (U, C0C,) VCf/VAc1
0H=86/13/1*6 Aerosil 200 (Japan Aerosil ■) * 7 MBK/ ) Ruen-1/1
Diabeam UR-6520 manufactured by Mitsubishi Rayon ■ was applied as an ultraviolet resin to the easily adhesive layer of the polyester film obtained in the Examples and Comparative Examples to a thickness of approximately 10 μm, and a polyester matte film was pasted on top of it. ,
The ultraviolet resin was cured by irradiation with ultraviolet light. When the polyester matte film was peeled off, a matte surface remained on the surface of the ultraviolet resin layer. The satin surface scratch strength test was conducted to judge whether the scratches are good or bad by scratching the satin surface with a fingernail.
次いで、上記で作成した梨地面をMEKで湿らせた布で
こすり、梨地に孔があくまでの回数を測定した。Next, the satin surface prepared above was rubbed with a cloth moistened with MEK, and the number of times until holes were formed in the satin surface was measured.
一方、凸部剪断強度試験を行った。この試験においては
、深さQ、 5 mm X幅3 mm X長さgm+n
の孔を9個形成したステンレス製平板金型に、ダイヤビ
ームUR−6520を塗布し、その上に易接着性層及び
ラミネートフィルムを積層し、その上から紫外線を照射
して易接着性層を硬化した後、ラミネートフィルムを取
り除いて、ステンレス製平板金型の孔に対応する凸部を
有する紫外線硬化樹脂層を得た。この凸部を剪断剥離す
ることにより、剪断剥離強度を測定した(9個の平均値
)。On the other hand, a convex shear strength test was conducted. In this test, depth Q, 5 mm x width 3 mm x length gm+n
Diabeam UR-6520 is applied to a flat stainless steel mold with 9 holes formed therein, an easily adhesive layer and a laminate film are laminated thereon, and ultraviolet rays are irradiated from above to form the easily adhesive layer. After curing, the laminate film was removed to obtain an ultraviolet curable resin layer having convex portions corresponding to the holes of the flat stainless steel mold. The shear peeling strength was measured by peeling off the convex portions by shearing (average value of 9 pieces).
上記各試験の結果を以下の第4表に示す。The results of each of the above tests are shown in Table 4 below.
第4表
*1評価
◎ : 全く傷つかず
○ : 僅か跡がつく
△ : 1部傷つきはがれる
× : 簡単に傷つきはがれる
第4表から、易接着性層の引っ掻き強度、耐溶剤性が優
れ、及び剪断剥離強度が優れていることが分かる。従っ
て、タッチパネル板として使用した場合に優れた効果を
発揮することが分かる。Table 4 *1 Evaluation ◎: Not scratched at all ○: Slight marks left △: Partially scratched and peeled off ×: Easily scratched and peeled off Table 4 shows that the easily adhesive layer has excellent scratch strength, solvent resistance, and shearing. It can be seen that the peel strength is excellent. Therefore, it can be seen that excellent effects are exhibited when used as a touch panel board.
なお、上記実施例において紫外線硬化樹脂塗料を使用す
る場合について示したが、本発明はこれら紫外線硬化樹
脂塗料のみに限定されるものではなく、その他の塗料に
ついても同様に効果を発揮するものである。In addition, although the case where an ultraviolet curable resin paint is used in the above example is shown, the present invention is not limited to these ultraviolet curable resin paints, and can similarly exhibit effects with other paints. .
Claims (3)
アクリレート、 を含むことを特徴とする易接着性組成物。(1) An easily adhesive composition comprising the following components: (a) a solvent-soluble saturated polyester resin, (b) a polyisocyanate, and (c) an acrylate having two or more vinyl groups or isopropenyl groups. thing.
)の重量比が100:10〜30:5〜50である請求
項1記載の易接着性組成物。(2) Component (a): Component (b): Component (c)
2. The easily adhesive composition according to claim 1, wherein the weight ratio of 100:10 to 30:5 to 50.
項1に記載の易接着性組成物の層を設けたことを特徴と
する易接着性ポリエステルフィルム。(3) An easily adhesive polyester film, characterized in that a layer of the easily adhesive composition according to claim 1 is provided on at least one side of the polyester film.