JPH029791A - Production of blue rock crystal - Google Patents
Production of blue rock crystalInfo
- Publication number
- JPH029791A JPH029791A JP16233188A JP16233188A JPH029791A JP H029791 A JPH029791 A JP H029791A JP 16233188 A JP16233188 A JP 16233188A JP 16233188 A JP16233188 A JP 16233188A JP H029791 A JPH029791 A JP H029791A
- Authority
- JP
- Japan
- Prior art keywords
- crystal
- rock crystal
- blue
- crystals
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は装飾品としてよく知られているアメシスト(紫
水晶)と同質の水晶であり、同じく装飾品として価値の
ある青色水晶の製造方法に関するしのである。[Detailed Description of the Invention] [Industrial Application Field] The present invention relates to a method for producing blue crystal, which is a crystal similar to amethyst (amethyst), which is well known as an ornament, and is also valuable as an ornament. It's Shino.
本発明は、装飾品としてよく知られている着色水晶を人
工的に合成できる製造方法において、所定の温度、圧力
を与え、適当な溶媒中で種結晶上に結晶を育成する水熱
合成法により、着色添加剤としてFe(NO5)iを添
加し、結晶を育成し、育成した結晶を熱処理することに
よって青色水晶を製造する方法である。The present invention is a manufacturing method that can artificially synthesize colored crystals, which are well known as decorative items, using a hydrothermal synthesis method in which crystals are grown on seed crystals in an appropriate solvent while applying a predetermined temperature and pressure. , is a method of producing blue crystal by adding Fe(NO5)i as a coloring additive, growing crystals, and heat-treating the grown crystals.
従来、水熱合成法においては、人工水晶の育成について
の研究開発および量産化が最も盛んであり、水熱合成法
における結晶育成としては、鼓ら成功した例であるとい
える。現在までに人工水晶に関してはほとんど址産1ヒ
技術が確立している。Conventionally, in the hydrothermal synthesis method, research and development and mass production of artificial quartz crystals have been most active, and this can be said to be a successful example of crystal growth using the hydrothermal synthesis method. Until now, most of the techniques for producing artificial crystals have been established.
また、この製造技術を生かした着色水晶の製造方法につ
いても、紫水晶、黄水晶など各種着色水晶について研究
開発がなされている。現在の着色水晶は、溶媒として、
水酸化カリウム(K OIf )水溶液、あるいは炭酸
カリウム(K2 CO,)水溶液を使用し、温度範囲3
00〜400 ’C1圧力1000〜1500kg/a
llの条件で育成が行われている。また、着色添加剤と
しては、各種金属塩が使用されている。Furthermore, research and development is being carried out on various colored crystals such as amethyst and yellow quartz regarding methods for producing colored crystals that utilize this manufacturing technology. Current colored crystals use solvents such as
Using potassium hydroxide (K OIf ) aqueous solution or potassium carbonate (K2 CO,) aqueous solution, temperature range 3
00~400'C1 pressure 1000~1500kg/a
The cultivation is carried out under the following conditions. Furthermore, various metal salts are used as coloring additives.
従来の青色水晶の水熱合成においては、着色用添加剤と
しては、CoCj 2− COO3、CoCO3等か用
いられていた。これtlの着色用添加剤を使用しても青
色結晶が育成できる(、のの以下のような問題点があっ
た。In conventional hydrothermal synthesis of blue crystal, CoCj 2-COO3, CoCO3, etc. have been used as coloring additives. Even if this TL coloring additive is used, blue crystals can be grown (there were the following problems with Nono.
従来の着色用添加剤を使用した場合、育成結晶中に濃く
着色された部分と、薄く着色された部分ができてしまう
といった色むらの問題があった。When conventional coloring additives are used, there is a problem of color unevenness in which darkly colored parts and lightly colored parts are formed in the grown crystal.
また、育成部分の着色が不十分であるといった、色あい
の問題も生じていた。In addition, there was also a problem of color tone, such as insufficient coloring of the growing part.
従来の水熱合成法により着色水晶の育成についての、色
あい、色むら、透明度、あるいはクラックの発生といっ
た課題については、着色用添加剤の選択に起因している
0着色用添加剤については様々な種類があるか、L記課
題を解決するため最適な着色用添加剤としてF e (
NOx ) sを見出した。When growing colored crystals using conventional hydrothermal synthesis methods, problems such as color tone, color unevenness, transparency, or the occurrence of cracks are caused by the selection of coloring additives. There are various types of additives for coloring, and F e (
NOx)s was found.
また、育成結晶を青色にするために熱処理を行うことに
した。We also decided to perform heat treatment to turn the grown crystals blue.
水熱合成法においては、適当な温度と圧力のもとで出発
原71を適当な溶媒の水溶液に溶解させ、徐冷するまた
は温度差を利用して養分を輸送することにより結晶を種
結晶上に育成する。この結晶育成の際に、着色用添加剤
を添加する。これにより、着色用添加剤は水溶液中で金
属イオンとなり、結晶中に取り込まれる。この着色用添
加剤としてFe<No5)3を用いた。育成された結晶
は、色に着色しているが、この育成結晶をさらに熱処理
することにより青色水晶を得ることかできる。In the hydrothermal synthesis method, the starting material 71 is dissolved in an aqueous solution of an appropriate solvent at an appropriate temperature and pressure, and crystals are grown on a seed crystal by slow cooling or by transporting nutrients using the temperature difference. to develop. A coloring additive is added during this crystal growth. As a result, the coloring additive becomes a metal ion in the aqueous solution and is incorporated into the crystal. Fe<No5)3 was used as the coloring additive. The grown crystals are colored, but blue crystals can be obtained by further heat-treating the grown crystals.
以下、実施例に従い詳しく説明する。Hereinafter, a detailed explanation will be given according to examples.
第1図に本実施例の構成を模式的に表す断面図を示す、
圧力容器本体1はシールリング2を介してカバー3によ
り圧力シールかされている。以Eの構成の圧力容器にお
いて圧力容器本体の底部に育成用原料4及び着色用添加
剤のFe (NOl)38を設置する。この育成用原料
4としては、天然水晶原石(ラス力)を適当な大きさに
砕いたものを使用した0次に種結晶支持枠5を介して種
結晶6が育成川原′f14の上に配置されている。FIG. 1 shows a cross-sectional view schematically showing the configuration of this embodiment.
The pressure vessel main body 1 is pressure-sealed by a cover 3 via a seal ring 2. In the pressure vessel having the following configuration E, the growth raw material 4 and the coloring additive Fe (NOl) 38 are installed at the bottom of the pressure vessel main body. The seed crystal 6 is placed on the growth riverbed 14 via the seed crystal support frame 5, which uses a natural crystal raw stone (lath force) crushed into an appropriate size as the raw material 4 for growth. has been done.
種結晶5としては、天然あるいは人工の水晶を用いる。As the seed crystal 5, natural or artificial crystal is used.
種結晶の結晶面としては各種の面(例えば、2面、Y面
、R面など)か用いられているが、今回は2面のもの(
Z板)を使用した。また、育成する単結晶の欠陥の原因
とならないように特に内部のインクルージヨン、クラッ
ク転位などの少ない種結晶が必要である。このように育
成用原料4および種結晶6を配置し、その間に同じく種
結晶支持枠5を介してバッフル板7が設置されている。Various types of crystal planes (for example, 2 planes, Y planes, R planes, etc.) are used as the crystal planes of the seed crystals, but this time we used 2 planes (2 planes, etc.).
Z plate) was used. In addition, a seed crystal with particularly few internal inclusions, crack dislocations, etc. is required so as not to cause defects in the single crystal to be grown. The growth raw material 4 and the seed crystal 6 are arranged in this way, and a baffle plate 7 is installed between them via the seed crystal support frame 5 as well.
このような構成の圧力容器中で着色水晶の育成を行った
。溶媒としては、K2CO3水溶液を用い、所定の温度
で所定の圧力が得られるような充填率で圧力容器中へ充
填した。Colored crystals were grown in a pressure vessel with such a configuration. A K2CO3 aqueous solution was used as the solvent, and the pressure vessel was filled at a filling rate such that a predetermined pressure was obtained at a predetermined temperature.
以上の設定で水熱合成を行った。このようにして得られ
た結晶は淡い褐色をしている。この結晶を所定の温度、
時間で、大気中で熱処理することによって青色水晶が得
られた。詳しい育成条件は以下の通りである。Hydrothermal synthesis was performed with the above settings. The crystals thus obtained have a light brown color. This crystal is heated to a specified temperature,
Blue crystals were obtained by heat treatment in air for an hour. The detailed growth conditions are as follows.
実施例1
種結晶6の温度・・・320°C
育成用原料4の温度・・・340°C
溶媒・・・0.5モルK 2COs水溶液着色用添加剤
量・・Fe(No3)s1重足%圧力・・・800kl
r/′−
育成期間・・・10日間
熱処理温度・・・400°C
熱処理時間・・・8時間
この結果、種結晶6の上に以下の様な青色水晶か育成さ
れた。Example 1 Temperature of seed crystal 6...320°C Temperature of growing raw material 4...340°C Solvent...0.5 mol K Amount of additive for coloring 2COs aqueous solution...Fe(No3)s 1 weight Foot % pressure...800kl
r/'- Growth period: 10 days Heat treatment temperature: 400°C Heat treatment time: 8 hours As a result, blue crystals as shown below were grown on the seed crystal 6.
成長した層の厚み・・・7.4市
成長速度・・・740μm/日
育成、熱処理後の結晶の性質・・・α−水晶(X線回折
法により同定)、インクルージヨン、マイクロクラック
の非常に少ない色むらのない青色の結晶が得られた。Thickness of grown layer: 7.4 Growth rate: 740 μm/day Crystal properties after growth and heat treatment: α-quartz (identified by X-ray diffraction), inclusions, and microcracks. Blue crystals with little color unevenness were obtained.
実施例2
種結晶6の温度・・・320℃
育成用原料4の温度・・・340°C
溶媒・・・0.5モルに2 Co、水溶液若色用添加削
址・・Fe (NOs )31重量%J王力・・・50
0kf/J
育成期間・・・10日間
熱処理温度・・・1100℃
熱処理時間・・・8時間
この結果、種結晶6の上に以下の様な青色の水晶が育成
された。Example 2 Temperature of seed crystal 6: 320°C Temperature of growing raw material 4: 340°C Solvent: 0.5 mol of 2 Co, aqueous solution rejuvenation additive: Fe (NOs) 31% by weight J Royal Power...50
0 kf/J Growth period: 10 days Heat treatment temperature: 1100°C Heat treatment time: 8 hours As a result, blue crystals as shown below were grown on the seed crystal 6.
成長した層の厚み・・・5.81w11成長速度・・・
580μm/′日
育成、熱処理後の結晶の性質・・・α−水晶(X線回折
法により同定)、インクルージヨン、マイクロクラック
の非常に少ない色むらのない4色の結晶か得られた。実
施例aで得られた結晶とくらべて、淡い青色の結晶が得
られた。Thickness of grown layer...5.81w11 Growth rate...
Properties of crystals after growth at 580 μm/'day and heat treatment: Four-color crystals with very few α-quartz crystals (identified by X-ray diffraction), inclusions, and microcracks and no color unevenness were obtained. A pale blue crystal was obtained compared to the crystal obtained in Example a.
実施例3
種結晶6の温度・・・300″C
育成用原料4の温度・・・320℃
溶媒・・・0.5モルに2C03水溶液着色用添加剤量
・・・Fe(NOs )3 1.5重藍%圧力・・・1
000 k2./’aiff育成期間・・・10日間
熱処理温度・・・500℃
熱処理時間・・・8時間
この結果、種結晶6の上に以下の様な青色水晶が育成さ
れた。Example 3 Temperature of seed crystal 6: 300″C Temperature of growing raw material 4: 320°C Solvent: 0.5 mol 2C03 aqueous solution coloring additive amount: Fe(NOs)3 1 .5 heavy indigo% pressure...1
000 k2. /'aiff Growth period: 10 days Heat treatment temperature: 500° C. Heat treatment time: 8 hours As a result, blue crystals as shown below were grown on the seed crystal 6.
成長した層の厚み・・・7.1間
成長速度・・・710μ/m
育成、熱処理後の結晶の性質・・・α−水晶(X線回折
法により同定)、インクルージヨン、マイクロクラック
の非常に少ない色むらのない青色の結晶か得られた。Thickness of grown layer: 7.1 Growth rate: 710μ/m Properties of crystals after growth and heat treatment: α-quartz (identified by X-ray diffraction), inclusions, and microcracks. A blue crystal with little color unevenness was obtained.
以上詳述したように本発明によれば、着色用添加剤とし
てF e (NO3) 3を用いかつ熱処理を行うこと
により、色むらのほとんどない透明度の非常によい青色
水晶の育成が可能である。また、装飾品としての価値を
十分に持った青色水晶の育成が可能となり、その効果は
極めて大きい。As detailed above, according to the present invention, by using Fe (NO3) 3 as a coloring additive and performing heat treatment, it is possible to grow blue crystals with very good transparency and almost no color unevenness. . Furthermore, it becomes possible to grow blue crystals that have sufficient value as ornaments, and the effect is extremely large.
第1図は圧力容器の構造を表わす断面図である。
圧力容器本体
シールリング
カバー
育成用原料
種結晶支持枠
種結晶
バッフル板
着色用添加剤
以上
出願人 セイコー電子工業株式会社
代理人 弁理士 林 敬 之 動圧力客器の、構
凸Σ表)+−)す右面図第1図FIG. 1 is a sectional view showing the structure of a pressure vessel. Pressure vessel main body Seal ring cover Raw material for growing Seed crystal support frame Seed crystal baffle plate Additive for coloring Applicant Seiko Electronics Co., Ltd. Agent Patent attorney Takashi Hayashi Structure convex Σ table of dynamic pressure passenger equipment) +-) Right side view Figure 1
Claims (1)
おいて、着色用添加剤としてFe(NO_3)_3を加
え、水晶を育成した後に熱処理することを特徴とする青
色水晶の製造方法。A method for producing blue crystal, which is characterized by adding Fe(NO_3)_3 as a coloring additive in a hydrothermal synthesis method of growing a crystal by applying a predetermined temperature and pressure, and heat-treating the crystal after growing the crystal.