JPH02232277A - Ink for marking pen - Google Patents
Ink for marking penInfo
- Publication number
- JPH02232277A JPH02232277A JP1053331A JP5333189A JPH02232277A JP H02232277 A JPH02232277 A JP H02232277A JP 1053331 A JP1053331 A JP 1053331A JP 5333189 A JP5333189 A JP 5333189A JP H02232277 A JPH02232277 A JP H02232277A
- Authority
- JP
- Japan
- Prior art keywords
- ink
- solvent
- org
- loading
- affinity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、マーキングベン用インキのペン先における耐
乾燥性の改善に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial Field of Application) The present invention relates to improving the drying resistance of the nib of a marking ben ink.
(従来の技術)
従来の一般的なマーキングベン用インキには、筆記面に
マーキングされた筆跡がほぼ瞬時に乾燥してインキ非浸
透面を含むあらゆる表面にマーキングが可能となるよう
に、低級脂肪族アルコール,エステル類,グリコールエ
ーテル類,ケトン類等の揮発性の有機溶剤が用いられて
いる。それ故、従来のマーキングペンはキャップを外し
たまま放置すると、これら有機溶剤が蒸発してペン先に
着色剤や樹脂等が析出してペン先の表面に被膜が形成さ
れ、これが筆跡のカスレや、ひどい場合は筆記不能をひ
き起すという弊害があった。(Prior art) Conventional general marking inks contain low-grade fat so that the handwriting marked on the writing surface dries almost instantly, making it possible to mark all surfaces including ink-impermeable surfaces. Volatile organic solvents such as group alcohols, esters, glycol ethers, and ketones are used. Therefore, if conventional marking pens are left with the cap removed, these organic solvents will evaporate and colorants and resins will precipitate on the pen tip, forming a film on the surface of the pen tip, which can cause blurred handwriting and In severe cases, this had the disadvantage of causing an inability to write.
(発明が解決しようとする課題)
そこで本発明は、筆記面にマーキングされた筆跡がほぼ
瞬時に乾燥してインキ非浸透面を含むあらゆる表面にマ
ーキングできるという性能を損なわず,且つマーキング
ベンのペン先の耐乾燥性を向上せしめるマーキングベン
用インキの提供を目的とする。(Problem to be Solved by the Invention) Therefore, the present invention provides a method that allows the handwriting marked on the writing surface to dry almost instantly, allowing marking to be performed on any surface including non-ink penetrating surfaces, and without impairing the performance of the marking pen. The purpose of the present invention is to provide a marking ink that improves the drying resistance of the tip.
(課厘を解決するための手段)
上記目的を達成するために、本発明におけるマーキング
ベン用インキは、着色剤,樹脂,水と親和性のある有機
溶剤、及び次の一般式n−0〜5
であらわされるヘキサグリセリルトリステアレートを少
なくとも含有してなるものであ.る。(Means for Solving Problems) In order to achieve the above object, the marking ink of the present invention contains a colorant, a resin, an organic solvent having an affinity for water, and the following general formula n-0 to It contains at least hexaglyceryl tristearate represented by 5. Ru.
本発明において含有する着色剤としては,一般に油性マ
ーキングベン用インキに用いられる油溶性染料や、酒精
溶性染料や、スピリットソルブル染料等のソルベント染
料や、アゾ,アンスラキノン,インジゴ,フタ口シアニ
ン,トリフエニルメタン,又はキタンサン系の有機顔料
や、カーボンブラック,チタン白等が使用可能で、その
含有量はインキ組成物中1〜20重量%とする。The coloring agents contained in the present invention include oil-soluble dyes generally used in oil-based marking inks, solvent dyes such as alcohol-soluble dyes and spirit-soluble dyes, azo, anthraquinone, indigo, lid cyanine, etc. Triphenylmethane or chitansan-based organic pigments, carbon black, titanium white, etc. can be used, and the content thereof is 1 to 20% by weight in the ink composition.
本発明において含有する樹脂としては、ロジン,エステ
ルガム,ロジン変性マレイン酸レジン等のロジン誘導体
,ケトン樹脂,可溶性フェノールレジン,メチル又はエ
チルセルロース,ヒドロキシアルキルセルロース誘導体
,スチレンーマレイン酸共重合体,ビニルブチラール,
酢酸ビニル,酢酸ビニルー塩化ビニル重合体,ビニルビ
ロリドン等のビニル系ボリマーなとの一般に油性マーキ
ングベン用インキに用いられる樹脂が使用可能で、その
含有量はインキ組成物中1〜30重量%とする。The resins contained in the present invention include rosin, ester gum, rosin derivatives such as rosin-modified maleic acid resin, ketone resin, soluble phenol resin, methyl or ethyl cellulose, hydroxyalkyl cellulose derivative, styrene-maleic acid copolymer, vinyl butyral. ,
Resins commonly used in oil-based marking inks, such as vinyl polymers such as vinyl acetate, vinyl acetate-vinyl chloride polymers, and vinyl pyrrolidone, can be used, and the content thereof is 1 to 30% by weight in the ink composition.
本発明において含有する溶剤は水との親和性が良いこと
が必要であり、メタノールやエタノール等の低級脂肪族
アルコール,酢酸メチルや酢酸エチル等のエステル類,
メチルセロソルブやエチルセロソルブやブロビレングリ
コールモノメチルエーテル等のグリコールエーテル類,
アセトンやMEK等のケトン類などの有機溶剤が使用可
能で、その含有量はインキ組成物中20〜98重量%と
する。The solvent contained in the present invention needs to have good affinity with water, such as lower aliphatic alcohols such as methanol and ethanol, esters such as methyl acetate and ethyl acetate, etc.
Glycol ethers such as methyl cellosolve, ethyl cellosolve, and brobylene glycol monomethyl ether,
Organic solvents such as ketones such as acetone and MEK can be used, and the content thereof is 20 to 98% by weight in the ink composition.
本発明において含有するヘキサグリセリルトリステアレ
ートは上記の水と親和性のある有機溶剤に対してのみ特
に効果を発揮するもので、その含有量はインキ組成物中
0.01〜1 0.0 0重量%とするが、好ましいの
は0.1〜2.0重景%である。The hexaglyceryl tristearate contained in the present invention is particularly effective only against the above-mentioned organic solvents that have an affinity for water, and its content is 0.01 to 10.00 in the ink composition. It is expressed as weight percent, but preferably 0.1 to 2.0 weight percent.
本発明では、その他、目的に応じて所要な添加剤を含有
可能である。例えばホワイトボード等の筆記板用として
は筆跡剥離剤などを含有する。In the present invention, other necessary additives can be included depending on the purpose. For example, for writing boards such as whiteboards, it contains a handwriting remover.
(作 用)
有機溶剤として水と親和性のあるものを用い、且つヘキ
サグリセリルトリステアレートを含有することにより、
ペン先表面に脆い薄膜が形成されて溶剤の蒸発を防ぎ,
マーキングする場合は容易にその薄膜が破壊されて筆跡
のカスレなどを発生させないように作用する。(Function) By using an organic solvent that has an affinity for water and containing hexaglyceryl tristearate,
A brittle thin film is formed on the surface of the pen tip to prevent solvent evaporation.
When marking, the thin film is easily destroyed and acts to prevent blurring of handwriting.
(実施例)
本発明実施例の配合例を以下に示す。尚、数字の単位は
重量%である。(Example) A formulation example of an example of the present invention is shown below. In addition, the unit of the number is weight %.
実施例1
着色剤(バリファストレッド1308)天然口ジン
エチルセロソルブ
メチルセロソルブ
ヘキサグリセリルトリステアレーl・
7.0
5.0
74.5
1 3.2
0.3
実施例2
着色剤(ニグロシンベース)
フェノール樹脂
エタノール
エチルセロソルブ
オレイン酸
ヘキサグリセリルトリステアレート
実施例3
着色剤(カーボンブラック)
塩ビー酢ビ共重合物
MI BK
酢酸エチル
ヘキサグリセリルトリステアレート
実施例4
着色剤(フタロシアニンブルー)
ポリビニルブチラール
エタノール
イソブロバノール
ポリオキシエチレンアルキルエーテル
セバシン酸ジオクチル
ヘキサグリセリルトリステアレート
1 0.0
2.0
60.0
2 2.7
5.0
0.3
3.0
4.0
7 8.0
1 4.8
0.2
3.5
4.0
6 6.4
1 6.6
4.0
5.0
0,5
上記の配合から調整された各実施例のインキと後記する
各比較例のインキをそれぞれ別個のマーキングペンの中
綿に充填し、各マーキングベンのキャップを外してその
繊維芯製のペン先を露出させた状態で温度25℃湿度6
5%の室内に放置して、筆跡がカスレを生じるまでの時
間を測定した.その結果は表−1の通りである.尚,比
較例1−1は実施例1におけるヘキサグリセリルトリス
テアレートの代わりに同量のへキサグリセリルジステア
レートを含有したもの、比較例1−2は比較例1−1の
ヘキサグリセリルジステアレートの代わりにその分(0
.3 重量%)だけエチルセロソルブを増やしたもの,
また比較例2,比較例3及び比較例4はそれぞれ実施例
2,実施例3及び実施例4における−へキサグリセリル
トリステアレートの代わりにそれぞれ同量のグリセリン
ジバルミテート,ヘキサグリセリルジバルミテート及び
ラウリン酸アミドを含有したものである.
表 1
(発明の効果)
本発明は叙上の通りであり、筆記面にマーキングされた
筆跡がほぼ瞬時に乾燥してインキ非浸透面を含むあらゆ
る表面にマーキングできるという性能を損なうことなく
、上記実施例及び比較例の試験結果からも明らかなよう
に、マーキングペンのペン先でのインキの乾燥防止能力
を極めて向上させ、よって筆跡のカスレを防止する効果
がある。Example 1 Coloring agent (Varifast Red 1308) Natural mouth zinc ethyl cellosolve methyl cellosolve hexaglyceryl tristearate 7.0 5.0 74.5 1 3.2 0.3 Example 2 Coloring agent (nigrosine base) Phenol Resin ethanol ethyl cellosolve oleate hexaglyceryl tristearate Example 3 Coloring agent (carbon black) Vinyl chloride vinyl acetate copolymer MI BK Ethyl acetate hexaglyceryl tristearate Example 4 Coloring agent (phthalocyanine blue) Polyvinyl butyral ethanol isobrobanol Polyoxyethylene alkyl ether sebacate dioctyl hexaglyceryl tristearate 1 0.0 2.0 60.0 2 2.7 5.0 0.3 3.0 4.0 7 8.0 1 4.8 0.2 3.5 4.0 6 6.4 1 6.6 4.0 5.0 0.5 The ink of each example prepared from the above formulation and the ink of each comparative example to be described later were mixed in separate marking pens. Fill the batting and remove the cap of each marking pen to expose the fiber core nib at a temperature of 25 degrees Celsius and a humidity of 6 degrees.
The handwriting was left in a room with 5% humidity, and the time it took for the handwriting to fade was measured. The results are shown in Table-1. In addition, Comparative Example 1-1 contained the same amount of hexaglyceryl distearate instead of hexaglyceryl tristearate in Example 1, and Comparative Example 1-2 contained the hexaglyceryl distearate of Comparative Example 1-1. Instead of the rate, the amount (0
.. 3% by weight) with increased ethyl cellosolve,
Comparative Example 2, Comparative Example 3, and Comparative Example 4 used the same amount of glycerin divalmitate and hexaglyceryl dibalmitate in place of -hexaglyceryl tristearate in Example 2, Example 3, and Example 4, respectively. and lauric acid amide. Table 1 (Effects of the Invention) The present invention is as described above, and achieves the above-mentioned characteristics without impairing the performance that handwriting marked on a writing surface dries almost instantly and can be marked on any surface including ink-impermeable surfaces. As is clear from the test results of Examples and Comparative Examples, this method greatly improves the ability to prevent ink from drying at the tip of a marking pen, and is therefore effective in preventing blurring of handwriting.
特許 出願人 三菱鉛筆株式会社Patent applicant: Mitsubishi Pencil Co., Ltd.
Claims (1)
般式 ▲数式、化学式、表等があります▼ m+n=5 m=0〜5 n=0〜5 であらわされるヘキサグリセリルトリステアレートを少
なくとも含有してなるマーキングペン用インキ。[Claims] Colorant, resin, organic solvent with affinity for water, and the following general formula ▲ Numerical formula, chemical formula, table, etc. ▼ Represented by m + n = 5 m = 0 to 5 n = 0 to 5 An ink for marking pens containing at least hexaglyceryl tristearate.