JPH02163304A - Manufacture of extrusion pipe made of aluminum base rapidly cooling solidified powder material - Google Patents
Manufacture of extrusion pipe made of aluminum base rapidly cooling solidified powder materialInfo
- Publication number
- JPH02163304A JPH02163304A JP31787488A JP31787488A JPH02163304A JP H02163304 A JPH02163304 A JP H02163304A JP 31787488 A JP31787488 A JP 31787488A JP 31787488 A JP31787488 A JP 31787488A JP H02163304 A JPH02163304 A JP H02163304A
- Authority
- JP
- Japan
- Prior art keywords
- solidified powder
- rapidly cooling
- core shaft
- manufacture
- cooling solidified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、アルミニウム基急冷凝固粉末材製の押出パイ
プの製造方法に関する。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to a method for manufacturing an extruded pipe made of aluminum-based rapidly solidified powder material.
(従来の技術)
従来、粉末金属材からパイプを押出成形するには、第2
図に示されるように、まず、ピレン目゛を製造し、この
押出ビレット1゛に貫通孔2”を形成し、そのビレット
1゛を中子軸3″が押出方向に沿って内装された成形型
4゛内に中子軸3゛を外嵌するように内装し、しかる後
にステムプラテン5°で圧縮してグイ本体6′から押出
すことでパイプ7”としていた。(Prior art) Conventionally, in order to extrude a pipe from powder metal material, a second
As shown in the figure, first, a pirene eye is manufactured, a through hole 2'' is formed in this extruded billet 1'', and the billet 1 is molded with a core shaft 3'' installed along the extrusion direction. The core shaft 3'' was placed inside the mold 4'' so as to be fitted onto the outside, and then compressed using a stem platen at 5° and extruded from the goo body 6' to form a pipe 7''.
(発明が解決しようとする課題)
従来の方法では、押出ビレット1゛の製造工程と、中子
軸3°のだめの貫通孔2″の成形工程とが必要でまた、
材料保留が悪く、製造コストの嵩む要因となっていた。(Problems to be Solved by the Invention) The conventional method requires a step of manufacturing an extrusion billet 1'' and a step of forming a through hole 2'' with a core axis of 3°, and
Material retention was poor and was a factor in increasing manufacturing costs.
本発明は上記課題を解決することを目的とする。The present invention aims to solve the above problems.
(課題を解決するための手段)
本発明の特徴とするところは、中子軸が押出方向に沿っ
て内装された成形型内に、アルミニウム基急冷凝固粉末
をその中子軸を囲むように充填し、この粉末を成形型か
ら押出成形してパイプとする点にある。(Means for Solving the Problems) The present invention is characterized by filling aluminum-based rapidly solidified powder into a mold in which a core shaft is arranged along the extrusion direction so as to surround the core shaft. This powder is then extruded from a mold to form a pipe.
(作 用)
本発明は、アルミニウム基(アルミニウム又はアルミニ
ウム合金をいう)の象、冷凝固粉末の押出tオは、結晶
粒が小さいので塑性変形能力が大きく、粉末から直接押
出されるものであっても所望形状を得ることができるこ
とに基づく。(Function) The present invention is based on the extrusion of aluminum-based (aluminum or aluminum alloy) cold-solidified powder, which has a large plastic deformation ability due to its small crystal grains, and is extruded directly from the powder. It is based on the fact that the desired shape can be obtained even if the
(実施例) 以下、本発明の詳細な説明する。(Example) The present invention will be explained in detail below.
第1図に示す押出用成形金型4は、ダイ本体6を囲む筒
状の成形コンテナ8と、このコンテナ8の下端を閉塞す
るシールブロック9と、ステムプラテン5とを備える。The extrusion mold 4 shown in FIG. 1 includes a cylindrical molding container 8 surrounding a die body 6, a seal block 9 closing the lower end of the container 8, and a stem platen 5.
この成形金型4には、押出方向(図中上下方向)に沿う
中子軸3が内装され、この中子軸3はシールブロック9
に取付けられている。This molding die 4 is equipped with a core shaft 3 that extends along the extrusion direction (vertical direction in the figure), and this core shaft 3 is attached to a seal block 9.
installed on.
そして、金型4内にはアルミニウム基急冷凝固粉末10
が中子軸3を囲むように充填される。本実施例で用いた
アルミニウム基急冷凝固粉末は、アトマイズ法により製
造され、その急例凝固速度は104〜106°C/se
cとした・
そして、粉末10の充填後に、ステムプラテンを圧下し
、ダイ本体6の押出口11の内周と中子軸3の外周との
間から粉末10を押出成形し、図中仮想線で示すように
パイプ7とする。ここで押出温度は480°Cとし、押
出比は40〜50とした。Inside the mold 4, there is aluminum-based rapidly solidified powder 10.
is filled so as to surround the core shaft 3. The aluminum-based rapidly solidified powder used in this example was manufactured by the atomization method, and its rapid solidification rate was 104 to 106°C/se.
After filling the powder 10, the stem platen is pressed down, and the powder 10 is extruded from between the inner periphery of the extrusion port 11 of the die body 6 and the outer periphery of the core shaft 3, and the imaginary line in the figure The pipe is designated as pipe 7 as shown in . Here, the extrusion temperature was 480°C, and the extrusion ratio was 40-50.
(発明の効果)
本発明によれば、アルミニウム基急冷凝固粉末をビレッ
トにすることはなく、直接押出成形してパイプを製造す
るものであるため、ビレットの製造工程、中子軸の貫通
孔の成形工程が不要で、また、材料保留もよく、製造コ
ストの低減を図れる。(Effects of the Invention) According to the present invention, pipes are manufactured by directly extruding the aluminum-based rapidly solidified powder without forming it into a billet. No molding process is required, and material can be easily stored, reducing manufacturing costs.
第1図は本発明方法の実施例装置の断面図、第2図は従
来例装置の断面図である。
3・・・中子軸、4・・・成形型、7・・・パイプ、l
O・・・アルミニウム基急例凝固粉末。FIG. 1 is a sectional view of an apparatus according to an embodiment of the present invention, and FIG. 2 is a sectional view of a conventional apparatus. 3... Core shaft, 4... Molding die, 7... Pipe, l
O: Aluminum-based rapidly solidified powder.
Claims (1)
、アルミニウム基急冷凝固粉末をその中子軸を囲むよう
に充填し、この粉末を成形型から押出成形してパイプと
することを特徴とするアルミニウム基急冷凝固粉末材製
押出パイプの製造方法。(1) Fill a mold with a core shaft inside along the extrusion direction with aluminum-based rapidly solidified powder so as to surround the core shaft, and extrude this powder from the mold to form a pipe. A method for manufacturing an extruded pipe made of aluminum-based rapidly solidified powder material, characterized by: