JPH02162815A - Manufacture of hermetic seal for crystal resonator - Google Patents
Manufacture of hermetic seal for crystal resonatorInfo
- Publication number
- JPH02162815A JPH02162815A JP31500488A JP31500488A JPH02162815A JP H02162815 A JPH02162815 A JP H02162815A JP 31500488 A JP31500488 A JP 31500488A JP 31500488 A JP31500488 A JP 31500488A JP H02162815 A JPH02162815 A JP H02162815A
- Authority
- JP
- Japan
- Prior art keywords
- base body
- ground wire
- lead wires
- fixing
- hermetic seal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
２明の目的
（産業上の利用分野）
本発明は、電気的な基準周波数の発生や、周波数の選択
に利用される水晶振動子用ハーメチックシールの製造方
法の改良に関するものである。DETAILED DESCRIPTION OF THE INVENTION 2.Objective (Industrial Application Field) The present invention relates to an improvement in a method for manufacturing a hermetic seal for a crystal resonator used for generating an electrical reference frequency and selecting a frequency. It is something.
（従来の技術）
近年使用されるアースリード付きの水晶振動子用ハーメ
チックシールの基本構造は、振動子のベース体に対して
、２本のリード線と該リード線間に配される１本のセン
ターアース線を設ける構成となっているが、具体的構造
において大別する２種類のものが存在する。(Prior art) The basic structure of a hermetic seal for a crystal resonator with an earth lead used in recent years is that the base body of the resonator has two lead wires and one lead wire placed between the lead wires. Although the structure is such that a center ground wire is provided, there are two types that can be broadly classified in terms of specific structure.
その一つは、第６図Ａに示す如く、ベース体１に上記リ
ード線を固定する筒状の絶縁性ガラス材３を装着する２
個の取付孔２ａを穿設して、該各取付孔２ａ内にガラス
材３の溶融固化により２本のリード線４ａ・４ｂを夫々
固定する一方、ベース体１の裏面に１本のセンターアー
ス、５ＩＳ５をスポット溶接６で直接固定し、且つ必要
に応じて、ベース体１の表面側に上記アース線５と対応
するＬ字状の端子７を、同じくスポット溶接６で固定す
る構成となっている。One of them is, as shown in FIG. 6A, a cylindrical insulating glass material 3 for fixing the lead wires to the base body 1.
Mounting holes 2a are formed, and two lead wires 4a and 4b are fixed in each mounting hole 2a by melting and solidifying the glass material 3, while one center ground wire is connected to the back surface of the base body 1. , 5IS5 are directly fixed by spot welding 6, and if necessary, an L-shaped terminal 7 corresponding to the ground wire 5 is fixed to the surface side of the base body 1 by spot welding 6 as well. There is.
又、もう一つのものは、同図Ｂに示す如く、ベース体１
を裏側が開口するリング状に成形して。Another one is the base body 1 as shown in figure B.
Form it into a ring shape with an opening on the back side.
ベース体ｌの表面側に２本のリード線４ａ・４ｂと１本
のセンターアース線５を挿通する挿通孔２ｂを形成する
一方、上記裏側の開口部内に装着される絶縁性ガラス材
３にも対応する３個の挿通孔３ａを形成して、該ガラス
材３の溶融固化により、２本のリード線４ａ・４ｂを夫
々固定すると共に。An insertion hole 2b is formed on the front surface side of the base body l, through which two lead wires 4a and 4b and one center ground wire 5 are inserted, and an insulating glass material 3 installed in the opening on the back side is also formed. Three corresponding insertion holes 3a are formed, and the two lead wires 4a and 4b are respectively fixed by melting and solidifying the glass material 3.
センターアース線５については、ガラス材３の他にスポ
ット溶接６でベース体１に固定する構成となっている。The center earth wire 5 is fixed to the base body 1 by spot welding 6 in addition to the glass material 3.
そして、従来にあって、斯る構成の水晶振動子用ハーメ
チックシールを製造する場合には１通常上治具と下治具
が使用されており、具体的には図示しないが、該上下の
治具中、下治具側に上記ベース体１を収納する多数のキ
ャビティーを列設すると共に、２本のリード線４ａ・４
ｂを挿入する２個の貫通孔を該各キャビティー毎に形成
する一方、上治具側に下治具の貫通孔に対応する部位夫
々に、各リード線４ａ・４ｂの先端部を収納する凹部を
形成する構成になっている。Conventionally, when manufacturing a hermetic seal for a crystal resonator with such a configuration, an upper jig and a lower jig are usually used, and although they are not specifically shown, the upper and lower jigs are In the tool, a number of cavities for storing the base body 1 are arranged in a row on the lower jig side, and two lead wires 4a and 4 are arranged in a row on the lower jig side.
Two through-holes into which the lead wires 4a and 4b are inserted are formed in each cavity, while the tips of the lead wires 4a and 4b are housed in the upper jig side at positions corresponding to the through-holes of the lower jig. The structure is such that a recess is formed.
依って、斯る上下の治具を用いて、既述した前者の水晶
振動子用ハーメチックシールを製造する場合には、ます
下治具の各キャビティー内に、予め取付孔２ａに絶縁性
ガラス材３を装着したベース体１をセットして、下治具
と上治具とを重ね合わせた後、該重合状態にある上下の
治具を逆さまとして、各キャビティーの貫通孔からリー
ド線４ａ・４ｂを挿入した状態を得て、加熱炉等におい
て約１，０００℃の雰囲気温度で加熱すると、絶縁性ガ
ラス材３が溶融固化して、２本のリード線４ａ・４ｂが
夫々ベース体１に対して固定される。Therefore, when manufacturing the former hermetic seal for a crystal resonator mentioned above using such upper and lower jigs, insulating glass is inserted into the mounting hole 2a in each cavity of the lower jig in advance. After setting the base body 1 with the material 3 attached and overlapping the lower jig and the upper jig, turn the overlapping upper and lower jigs upside down and insert the lead wire 4a from the through hole of each cavity.・When the state in which 4b is inserted is heated in a heating furnace or the like at an ambient temperature of approximately 1,000°C, the insulating glass material 3 is melted and solidified, and the two lead wires 4a and 4b are connected to the base body 1, respectively. Fixed to .
そこで、今度は２本のリード線４ａ・４ｂが固定された
ベース体１を上下の治具から取り出して。Therefore, this time, I took out the base body 1 to which the two lead wires 4a and 4b were fixed from the upper and lower jigs.
ベース体１の裏面所定個所にセンターアース線５とＬ字
状端子７を夫々スポット溶接６で固定すれば良い。The center earth wire 5 and the L-shaped terminal 7 may be fixed to predetermined locations on the back surface of the base body 1 by spot welding 6, respectively.
又、後者の水晶振動子用ハーメチックシールを製造する
場合には、前記とは逆に、先にセンターアース線５をベ
ース体１の対応する挿通孔２ｂにスポット溶接６で固定
してから、上記上下の治具を使用することにより、絶縁
性ガラス材３の溶融固化を得て、後から２本のリード線
４ａ・４ｂをベース体１に固定することとなる。In addition, when manufacturing the latter hermetic seal for a crystal resonator, contrary to the above, first fix the center earth wire 5 to the corresponding insertion hole 2b of the base body 1 by spot welding 6, and then By using the upper and lower jigs, the insulating glass material 3 is melted and solidified, and the two lead wires 4a and 4b are then fixed to the base body 1.
（発明が解決しようとする課題）
然し乍ら、従来の製造方法にあっては、いずれの構成の
水晶振動子用ハーメチックシールを製造する場合でも、
時間的な相違はあるが、２本のリード線４ａ・４ｂをガ
ラス材３の溶融固化を得てベース体１に固定する工程と
、１本のセンターアース線５をスポット溶接６を得てベ
ース体１に固定する工程とが、夫々独立して要求される
こととなるので、生産効率が著しく悪くなってしまうと
言う大きな問題点を有していた。(Problem to be Solved by the Invention) However, in the conventional manufacturing method, no matter which configuration of the hermetic seal for a crystal resonator is manufactured,
Although there are differences in time, there is a process of fixing the two lead wires 4a and 4b to the base body 1 by melting and solidifying the glass material 3, and spot welding 6 of one center earth wire 5 to the base body. Since each step of fixing the material to the body 1 is required independently, there is a major problem in that the production efficiency is significantly reduced.
しかも、通常は、多数のベース体１を上下の治具内にセ
ットして製造するものであるから、この生産効率の問題
点は、水晶振動子用ハーメチックシールの製造において
は極めて重大であった。Moreover, since manufacturing is usually done by setting a large number of base bodies 1 in upper and lower jigs, this problem of production efficiency is extremely serious in the manufacture of hermetic seals for crystal resonators. .
見見ｑ盪底
（課題を解決するための手段）
本発明は、斯る従来製造方法の問題点を有効に解決する
ために開発されたもので、ベース体に２本のリード線と
１本のアース線を固定する水晶振動子用ハーメチックシ
ールを、上下の治具を用いて製造する製造方法において
、下治具側にベース体を収納するキャビティーを設ける
と共に、該各キャビティーに２本のリード線と１本のア
ース線を挿入する３個の貫通孔を形成し、リード線を固
定する絶縁性ガラス材とアース線を固定する導電性固着
材とが付与されたベース体を、上記下治具に形成された
キャビティー内に収納して、上下の治具同士を重ね合わ
せた後、上記３個の貫通孔内に２本のリード線と１本の
アース線を挿入して、所定温度で加熱することにより、
上記絶縁性ガラス材の溶融固化でリード線をベース体に
固定し。The present invention was developed in order to effectively solve the problems of the conventional manufacturing method, and includes two lead wires and one wire on the base body. In a manufacturing method that uses upper and lower jigs to manufacture a hermetic seal for a crystal resonator that fixes the ground wire of the The above-mentioned base body has three through holes into which the lead wire and one ground wire are inserted, and is provided with an insulating glass material for fixing the lead wire and a conductive adhesive material for fixing the ground wire. After storing it in the cavity formed in the lower jig and overlapping the upper and lower jigs, insert two lead wires and one ground wire into the three through holes, By heating at a predetermined temperature,
The lead wire is fixed to the base body by melting and solidifying the above insulating glass material.
導電性固着材の溶融固化でアース線をベース体に同時に
固定する構成を採用した。We adopted a structure in which the ground wire is simultaneously fixed to the base body by melting and solidifying the conductive fixing material.
又、斯ろ水晶振動子用ハーメチックシールの製造方法に
おいて、導電性固着材に銀ロー材を使用する構成を採用
した。In addition, in the method for manufacturing a hermetic seal for a crystal resonator, a structure is adopted in which a silver brazing material is used as the conductive fixing material.
（作 用）
依って１本発明にあっては、予めベース体に絶縁性ガラ
ス材と導電性固着材を付与する状態を得て、該ベース体
を下治具のキャビティー内にセットした後、下治具と上
治具とを重ね合わせ、次いで、該重合状態にある上下の
治具を逆さまとして、各キャビティーの貫通孔から２本
のリード線と１本アース線を一緒に挿入して、所定の雰
囲気温度下で加熱すると、絶縁性ガラス材が溶融固化し
て、２本のリード線がベース体に対して確実に固定され
ると同時に、導電性固着材も同様に溶融固化して、１本
のアース線がベース体に確実に固定されることとなる。(Function) Accordingly, in the present invention, after obtaining a state in which the insulating glass material and the conductive fixing material are applied to the base body in advance and setting the base body in the cavity of the lower jig, , overlap the lower jig and the upper jig, then turn the overlapping upper and lower jigs upside down, and insert two lead wires and one ground wire together from the through hole of each cavity. When heated at a predetermined ambient temperature, the insulating glass material melts and solidifies, and the two lead wires are securely fixed to the base, and at the same time, the conductive adhesive material also melts and solidifies. Thus, one ground wire is securely fixed to the base body.
従って、後は、リード線とアース線とが同時に固定され
たベース体を上下の治具から取り出せばよいので、従来
の製造方法と比較すると、生産効率が頗る向上する。Therefore, all that is left to do is to take out the base body to which the lead wire and the ground wire are fixed at the same time from the upper and lower jigs, so the production efficiency is significantly improved compared to conventional manufacturing methods.
しかも、アース線を固定する導電性固着材として銀ロー
材を使用すれば、該銀ロー材が絶縁性ガラス材と等しい
温度で溶融する性質を有する他に、スポット溶接と比し
引張強度に優れ、且つ電気的特性も良好となるので、ア
ース線の固定には頗る最適となる。Moreover, if a silver brazing material is used as a conductive fixing material for fixing the ground wire, the silver brazing material has the property of melting at the same temperature as the insulating glass material, and has superior tensile strength compared to spot welding. , and the electrical characteristics are also good, making it extremely suitable for fixing the ground wire.
（実施例） 以下、本発明を図示する実施例に基づいて詳述する。(Example) Hereinafter, the present invention will be described in detail based on illustrated embodiments.
まず、ベース体に２本のリード線と１本のセンターアー
ス線を固定する構成の水晶振動子用ハーメチックシール
において、ベース体１１に筒状の絶縁ガラス材１３を装
着する大径な取付孔１２ａを穿設して、該各地付孔１２
ａ内にガラス材１３の溶融固化により２本のリード線１
４ａ・１４ｂを夫々固定し、且つベース体１１の表面側
にＬ字状の端子１７を設ける構成の水晶振動子用ハーメ
チックシールを製造する場合について説明する。First, in a hermetic seal for a crystal resonator configured to fix two lead wires and one center ground wire to a base body, a large diameter mounting hole 12a is used to attach a cylindrical insulating glass material 13 to the base body 11. , and each attachment hole 12
Two lead wires 1 are formed in a by melting and solidifying the glass material 13.
A case will be described in which a hermetic seal for a crystal resonator is manufactured in which the L-shaped terminals 17 are provided on the surface side of the base body 11 while fixing the L-shaped terminals 4a and 14b, respectively.
この場合には、第１図に示す如く、ベース体１１に穿設
された取付孔１２ａの中間部に、アース１ｉＡ１５を固
定する小径な取付孔１８を形成すると共に、該取付孔１
２ａのベース体１１裏面側の開口部に、導電性固着材た
る銀ロー材を付与する空所１８ａを形成する。In this case, as shown in FIG.
A cavity 18a is formed in the opening on the back side of the base body 11 of 2a, in which a silver brazing material as a conductive fixing material is applied.
他方、上下の治具２１・２２に対しては、第２図に示す
如く、下治具２２側にベース体１１を収納するキャビテ
ィー２３を列設すると共に、該各キャビティー２３毎に
２本のリード線Ｌ４ａ・１４ｂと１本のアース線１５を
挿入する３個の貫通孔２４を形成し、且つアース線用貫
通孔２４の縁部に銀ロー材を付与する空所２５を形成す
る一方、上治具２１側の上記リード線用の貫通孔２４に
対応する部位夫々に、各リード線１４ａ・１４ｂの先端
部を収納する凹部２６を形成すると共に、アース線用の
貫通孔２４と対応する部位に、Ｌ字状の端子１７を収納
する凹部２７を形成する。On the other hand, for the upper and lower jigs 21 and 22, as shown in FIG. Three through holes 24 are formed into which book lead wires L4a and 14b and one ground wire 15 are inserted, and a cavity 25 is formed at the edge of the ground wire through hole 24 to apply silver brazing material. On the other hand, recesses 26 for accommodating the tips of the lead wires 14a and 14b are formed in the portions of the upper jig 21 corresponding to the through holes 24 for the lead wires, and the through holes 24 for the ground wires A recess 27 for accommodating the L-shaped terminal 17 is formed at a corresponding location.
そして、実際に上記第１図に示す水晶振動子用ハーメチ
ックシールを製造する場合には、まず第３図Δに示す如
く、予めベース体１１のリード線取付孔１２ａに絶縁性
ガラス材１３を装着し、該ベース体１１を下治具２２の
各キャビティー２３内にセットする一方、下治具２２の
空所２５に銀ロー材２８を付与し、且つ上治具２１の空
所２７内にＬ字状の端子１７を収納した後、下治具２２
と上治具２１とを重ね合わせ１次いで同図Ｂに示す如く
、該重合状態にある上下の治具２１・２２を逆さまとし
て、各キャビティー２３の貫通孔２４から２本のリード
線１４ａ・１４ｂと１本のアース線１５を同時に挿入し
た状態を得て、加熱炉等において約１，０００℃の雰囲
気温度で加熱すると、ガラス材１３が溶融固化して、２
本のリード線１４ａ・１４ｂがベース体１１の取付孔１
２ａに対して固定される一方、銀ロー材２８も同様に溶
融固化して、センターアース線１５がベース体１１の取
付孔１８に固定される。When actually manufacturing the hermetic seal for a crystal resonator shown in FIG. 1 above, first, as shown in FIG. Then, the base body 11 is set in each cavity 23 of the lower jig 22, while a silver brazing material 28 is applied to the hollow space 25 of the lower jig 22, and a silver brazing material 28 is applied to the hollow space 27 of the upper jig 21. After storing the L-shaped terminal 17, the lower jig 22
and the upper jig 21, and as shown in FIG. 14b and one ground wire 15 are inserted at the same time, and when heated in a heating furnace or the like at an ambient temperature of about 1,000°C, the glass material 13 is melted and solidified, and the 2
The lead wires 14a and 14b of the book are attached to the mounting hole 1 of the base body 11.
While being fixed to 2a, the silver brazing material 28 is similarly melted and solidified, and the center ground wire 15 is fixed to the attachment hole 18 of the base body 11.
しかも、銀ロー材２８が溶融すると、取付孔１８を伝っ
て下流してＬ字状の端子１７をも同時に固定することと
なる。Moreover, when the silver brazing material 28 melts, it flows downstream along the attachment hole 18 and fixes the L-shaped terminal 17 at the same time.
従って１本実施例に製造方法にあっては、従来の如く、
ベース体１１の裏面にセンターアース線１５を、ベース
体１１の表面に端子１７をスポット溶接することなく、
−回の加熱工程のみで、リード線１４ａ・１４ｂとアー
ス線１５と端子１７が、同時に固定されたベース体１１
を製造できることとなる。尚、上記上下の治具２１・２
２を使用した製造過程において、Ｌ字状の端子１７を仮
止めするために、磁石やバキュームを使用することも実
施に応じ任意である。Therefore, in the manufacturing method of this embodiment, as in the conventional method,
Without spot welding the center ground wire 15 to the back surface of the base body 11 and the terminal 17 to the surface of the base body 11,
- The base body 11 has the lead wires 14a and 14b, the ground wire 15, and the terminal 17 fixed at the same time with only one heating process.
This means that it can be manufactured. In addition, the above-mentioned upper and lower jigs 21.2
In the manufacturing process using 2, it is optional to use a magnet or a vacuum to temporarily fix the L-shaped terminal 17, depending on the implementation.
次ぎに、Ｌ字状の端子１７を有しない水晶振動子用ハー
メチックシールを製造する場合には、第４図に示す如く
、ベース体１１に穿設された２本のリード線１４ａ−１
４ｂの取付孔１２ａの中間部に、１本のセンターアース
線１５の固定と銀ロー材２８の付与を兼用する取付凹部
１９を形成するものとする。尚、この場合にあっては、
上治具２１として既述したＬ字状の端子１７を収納する
凹部２７を形成したものを使用しても、何ら支障がない
ことは言うまでもないが、該凹部２７が形成されていな
い下治具２１を使用することが好ましい。Next, when manufacturing a hermetic seal for a crystal resonator that does not have an L-shaped terminal 17, two lead wires 14a-1 are bored through the base body 11, as shown in FIG.
A mounting recess 19 is formed in the middle of the mounting hole 12a of 4b, which serves both to fix one center earth wire 15 and to apply the silver brazing material 28. In this case,
It goes without saying that there is no problem in using the upper jig 21 that has the recess 27 for housing the L-shaped terminal 17 described above, but the lower jig does not have the recess 27 formed therein. Preferably, 21 is used.
依って、斯る第４図に示す水晶振動子用ハーメチックシ
ールを製造する場合には、具体的には図示しないが、前
記の場合と同様に、ベース体１１のリード線取付孔１２
ａに絶縁性ガラス材１３を装着し、アース線取付凹部１
９内に銀ロー材２８を付与して、該ベース体１１を下治
具２２の各キャビティー２３内にセットした後、下治具
２２と上治具２１とを重ね合わせ、次いで、該上下の治
具２１・２２を逆さまとして、各キャビティー２３の貫
通孔２４からリード線１４ａ・１４ｂとアース線１５を
同時に挿入した状態を得て、約１゜０００℃の雰囲気温
度で加熱すると、やはり、ガラス材１３が溶融固化して
、２本のリード線１４ａ・１４ｂがベース体１１の取付
孔１２ａに対して固定される一方、銀ロー材２８も同様
に溶融固化して、アース線１５がベース体１１の取付凹
部１９に固定されることとなる。Therefore, when manufacturing the hermetic seal for a crystal resonator shown in FIG.
Attach the insulating glass material 13 to a, and connect the ground wire attachment recess 1
After applying silver brazing material 28 in the inside of the base body 11 and setting the base body 11 in each cavity 23 of the lower jig 22, the lower jig 22 and the upper jig 21 are overlapped, and then the upper and lower When the jigs 21 and 22 are turned upside down and the lead wires 14a and 14b and the ground wire 15 are simultaneously inserted from the through holes 24 of each cavity 23, and heated at an ambient temperature of about 1°000°C, The glass material 13 is melted and solidified, and the two lead wires 14a and 14b are fixed to the mounting hole 12a of the base body 11, while the silver brazing material 28 is similarly melted and solidified, and the ground wire 15 is fixed. It will be fixed in the mounting recess 19 of the base body 11.
更に、ベース体１１を裏側が開口するリング状に成形し
て、該ベース体１１の表面側に２本のリード線１４ａ・
１４ｂと１本のセンターアース線１５を挿通する挿通孔
１２ｂを形成する一方、上記ベース体１１の裏面開口部
内に装着されるガラス材１３にも同様な３個の挿通孔１
３ａを形成して、該ガラス材１３の溶融固化によりリー
ド線１４ａ・１４ｂを固定する構成の水晶振動子用ハー
メチックシールを製造する場合には、第５図に示す如く
、上治具２１のアース線１５用の貫通孔２４に対応する
部位の縁部に銀ロー材２８を付与する空所２０を形成す
る一方、上治具２１のアース線１５用の貫通孔２４と対
応する部位に、アース線１５の上端部を収納する凹部（
図示せず）を形成するものとする。Furthermore, the base body 11 is formed into a ring shape with an open back side, and two lead wires 14a are attached to the front side of the base body 11.
14b and one center ground wire 15 are formed, and three similar insertion holes 1 are formed in the glass material 13 installed in the back opening of the base body 11.
3a and fixing the lead wires 14a and 14b by melting and solidifying the glass material 13, as shown in FIG. A space 20 for applying silver brazing material 28 is formed at the edge of a portion corresponding to the through hole 24 for the wire 15, and a ground hole 20 is formed at a portion of the upper jig 21 corresponding to the through hole 24 for the ground wire 15. A recess (
(not shown).
依って、斯る第５図に示す水晶振動子用ハーメチックシ
ールを製造する場合には、ベース体１１の裏面開口部に
、アース線用挿通孔１３ａの縁部に形成された絶縁性ガ
ラス材１３を装着して、該ベース体１１を下治具２２の
各キャビティー２３内にセットした後、下治具２２と空
所２０に銀ロー材２８が付与された上治具２１とを重ね
合わせ、次いで、該上下の治具２１・２２を逆さまとし
て、各キャビティー２３の貫通孔２４を介して、リード
線１４ａ・１４ｂとアース線１５をガラス材１３の各挿
通孔１３ａ内に同時に挿入した状態を得て、約ｉ、ｏｏ
ｏ℃の雰囲気温度で加熱すると。Therefore, when manufacturing the hermetic seal for a crystal resonator shown in FIG. After mounting the base body 11 in each cavity 23 of the lower jig 22, the lower jig 22 and the upper jig 21 with the silver brazing material 28 applied to the empty space 20 are placed on top of each other. Next, the upper and lower jigs 21 and 22 were turned upside down, and the lead wires 14a and 14b and the ground wire 15 were simultaneously inserted into each insertion hole 13a of the glass material 13 through the through hole 24 of each cavity 23. Get state, about i,oo
When heated at an ambient temperature of 0°C.
ガラス材１３が溶融固化して、２本のリード線１４ａ・
１４ｂがベース体１１の挿通孔１２ｂに対して固定され
る一方、銀ロー材２８も同様に溶融固化して、アース線
１５がベース体１１の挿通孔１２ｂに固定されることと
なる。The glass material 13 is melted and solidified, and the two lead wires 14a.
14b is fixed to the insertion hole 12b of the base body 11, while the silver brazing material 28 is similarly melted and solidified, and the ground wire 15 is fixed to the insertion hole 12b of the base body 11.
従って１本実施例に係る製造方法にあっては。Therefore, in the manufacturing method according to this embodiment.
いずれの水晶振動子用ハーメチックシールを製造する場
合であっても、２本のリード線１４ａ・１４ｂと１本の
アース線１５とを、−工程をもってベース体１１側に固
定できるので、従来と比し生産効率が頗る向上すること
となる。No matter which type of hermetic seal for a crystal oscillator is manufactured, the two lead wires 14a and 14b and one ground wire 15 can be fixed to the base body 11 side in the - process, compared to the conventional method. This will greatly improve production efficiency.
しかも、本実施例において、センターアース線１５を固
定する導電性固着材として銀ロー材２８を使用している
のは、該銀ロー材２８がガラス材１３と等しい温度で溶
融する性質を有する他に。Moreover, in this embodiment, the reason why the silver brazing material 28 is used as the conductive fixing material for fixing the center earth wire 15 is that the silver brazing material 28 has the property of melting at the same temperature as the glass material 13. To.
スポット溶接と比し引張強度に優れ、且つ電気的特性も
良好であることに起因するものであるが。This is due to its superior tensile strength and good electrical properties compared to spot welding.
本発明はこれに限定されるものではなく、導電性固着材
として、例えばリンとニッケルの合金材や銅と錫の合金
材等を使用することも実施に応じ任意である。The present invention is not limited thereto, and it is also possible to use, for example, an alloy material of phosphorus and nickel, an alloy material of copper and tin, etc. as the conductive fixing material depending on the implementation.
ｌ胛度然米
以上説明したように、本発明は、予めベース体に絶縁性
ガラス材と導電性固着材を付与する状態を得て、該ベー
ス体を下治具のキャビティー内にセットした後、下治具
と上治具とを重ね合わせ。As explained above, in the present invention, the insulating glass material and the conductive fixing material are applied to the base body in advance, and the base body is set in the cavity of the lower jig. After that, overlap the lower jig and upper jig.
次いで、該重合状態にある上下の治具を逆さまとして、
各キャビティーの貫通孔から２本のリード線と１本アー
ス線を同時に挿入して、所定の雰囲気温度下で加熱する
と、絶縁性ガラス材が溶融固化して、２本のリード線が
ベース体に対して確実に固定される一方、導電性固着材
も同様に溶融固化して、１本のアース線がベース体に確
実に固定されることとなる６
従って、後は、リード線とアース線とが同時に固定され
たベース体を上下の治具から取り出せばよいので、従来
の製造方法と比較すると、生産効率が頗る向上すること
が可能となった。Next, the upper and lower jigs in the polymerized state are turned upside down,
When two lead wires and one ground wire are simultaneously inserted through the through-hole of each cavity and heated under the specified atmospheric temperature, the insulating glass material melts and solidifies, and the two lead wires connect to the base body. While the conductive adhesive material is also melted and solidified, one ground wire is securely fixed to the base.6 Therefore, all that is left is to connect the lead wire and the ground wire. Since the fixed base body can be removed from the upper and lower jigs at the same time, production efficiency can be significantly improved compared to conventional manufacturing methods.
しかも、アース線を固定するための導電性固着材として
銀ロー材を使用すれば、該銀ロー材が絶縁性ガラス材と
等しい温度で溶融する性質を有する他に、スポット溶接
と比し引張強度に優れ、且つ電気的特性も良好となるの
で、アース線の固定には頗る最適となる。Moreover, if silver brazing material is used as a conductive fixing material for fixing the ground wire, not only does the silver brazing material have the property of melting at the same temperature as the insulating glass material, but it also has a tensile strength that is higher than that of spot welding. Since it has excellent electrical properties and excellent electrical characteristics, it is extremely suitable for fixing the ground wire.
第１図は本発明の実施例に係る製造方法により製造され
た水晶振動子用ハーメチックシールを示す断面図、第２
図は同製造方法に供される上治具と下治具を断面して示
す要部斜視図、第３図Ａ・Ｂは水晶振動子用ハーメチッ
クシールの製造過程を示す要部断面図、第４図・第５図
は実施例に係る製造方法により製造された別の水晶振動
子用ハーメチックシールを示す断面図、第６図Ａ−８は
従来の製造方法により製造された水晶振動子用ハーメチ
ックシールを示す断面図である。
１１・・・ベース体、１３・・・絶縁性ガラス材、１４
ａ・１４ｂ・・・リード線、１５・・・アース線、２１
・・・下治具、２２・・・下治具、２３・・・キャビテ
ィー ２４・・・貫通孔、２８・・・銀ロー材。
第１図
第２図FIG. 1 is a sectional view showing a hermetic seal for a crystal resonator manufactured by a manufacturing method according to an embodiment of the present invention, and FIG.
3A and 3B are cross-sectional views of essential parts showing the manufacturing process of a hermetic seal for a crystal resonator; 4 and 5 are cross-sectional views showing another hermetic seal for a crystal resonator manufactured by the manufacturing method according to the embodiment, and FIG. 6A-8 is a hermetic seal for a crystal resonator manufactured by the conventional manufacturing method. FIG. 3 is a sectional view showing a seal. 11... Base body, 13... Insulating glass material, 14
a・14b...Lead wire, 15...Ground wire, 21
...Lower jig, 22...Lower jig, 23...Cavity 24...Through hole, 28...Silver brazing material. Figure 1 Figure 2
Claims (2)
定する水晶振動子用ハーメチックシールを、上下の治具
を用いて製造する製造方法において、下治具側にベース
体を収納するキャビティーを設けると共に、該各キャビ
ティーに２本のリード線と１本のアース線を挿入する３
個の貫通孔を形成し、リード線を固定する絶縁性ガラス
材とアース線を固定する導電性固着材とが付与されたベ
ース体を、上記下治具に形成されたキャビティー内に収
納して、上下の治具同士を重ね合わせた後、上記３個の
貫通孔内に２本のリード線と１本のアース線を挿入して
、所定温度で加熱することにより、上記絶縁性ガラス材
の溶融固化でリード線をベース体に固定し、導電性固着
材の溶融固化でアース線をベース体に同時に固定するこ
とを特徴とする水晶振動子用ハーメチックシールの製造
方法。(1) In a manufacturing method that uses upper and lower jigs to manufacture a hermetic seal for a crystal resonator that fixes two lead wires and one ground wire to the base body, the base body is stored on the lower jig side. 3. Insert two lead wires and one ground wire into each cavity.
The base body, which has several through holes formed therein and is provided with an insulating glass material for fixing the lead wire and a conductive fixing material for fixing the ground wire, is housed in the cavity formed in the lower jig. After overlapping the upper and lower jigs, two lead wires and one ground wire are inserted into the three through holes and heated to a predetermined temperature to form the insulating glass material. A method for manufacturing a hermetic seal for a crystal resonator, characterized in that a lead wire is fixed to a base body by melting and solidifying a conductive adhesive, and a ground wire is simultaneously fixed to a base body by melting and solidifying a conductive adhesive.
項記載の水晶振動子用ハーメチックシールの製造方法。(2) Claim 1, wherein a silver brazing material is used as the conductive fixing material.
A method for manufacturing a hermetic seal for a crystal resonator as described in .