JPH01315045A - Optical disk - Google Patents
Optical diskInfo
- Publication number
- JPH01315045A JPH01315045A JP63163444A JP16344488A JPH01315045A JP H01315045 A JPH01315045 A JP H01315045A JP 63163444 A JP63163444 A JP 63163444A JP 16344488 A JP16344488 A JP 16344488A JP H01315045 A JPH01315045 A JP H01315045A
- Authority
- JP
- Japan
- Prior art keywords
- protective film
- film
- coupling agent
- silane coupling
- inorganic protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、レーザ光を照射して記録情報の再生を図る
ことができる光ディスクに関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to an optical disc that can reproduce recorded information by irradiating it with laser light.
従来より、レーザ光を照射して記録された情報の再生を
図ることができる記録媒体としての光ディスクが知られ
ている。この光ディスクは、例えば第５図に示すように
、ポリカーボネイト（ＰＣ）等の基板１００上に無機系
保護膜１０１として酸化イツトリウム（ＹｚＯ３）、そ
の上に磁性［１０２としてテルビウム・鉄・コバルト磁
性膜（ＴｂＦｅＣｏ）さらにその上に無機系保護膜１０
３として酸化イツトリウム（ＹｚＯｉ）あるいは窒化ケ
イ素（Ｓ ｉ Ｎ）等を成膜し、さらにその上から樹脂
によりコーティングして樹脂膜１０４を形成した構成の
ものが知られている。2. Description of the Related Art Optical discs have been known as recording media that can reproduce recorded information by irradiating laser light. For example, as shown in FIG. 5, this optical disk is made of yttrium oxide (YzO3) as an inorganic protective film 101 on a substrate 100 made of polycarbonate (PC), and a terbium-iron-cobalt magnetic film (102) thereon. TbFeCo) Furthermore, an inorganic protective film 10 is applied thereon.
As No. 3, a structure is known in which a film of yttrium oxide (YzOi) or silicon nitride (S i N) or the like is formed and then coated with resin to form a resin film 104 .
ところで、このような構成の光ディスクにあっては、無
機系保護膜１０３と樹脂膜１０４とはもともと密着性の
悪い無機物と有機物であるため、温度や湿度によって、
或いは物理的な衝撃力によって剥離し易く、大きな問題
となっている。By the way, in the optical disc having such a structure, since the inorganic protective film 103 and the resin film 104 are made of inorganic and organic materials that have poor adhesion, they may deteriorate depending on the temperature or humidity.
Alternatively, it is easy to peel off due to physical impact force, which is a big problem.
そこで、この発明は、上記した従来の欠点に鑑み、コー
ティングした樹脂膜と無機系保護膜との密着性を高め、
耐候性の大きな光ディスクを提供することを目的とする
ものである。Therefore, in view of the above-mentioned conventional drawbacks, this invention improves the adhesion between the coated resin film and the inorganic protective film,
The purpose is to provide an optical disc with high weather resistance.
（課題を解決するための手段〕
この発明の光ディスクは、レーザ光を照射して記録情報
の再生を図る光ディスクにおいて、無機系保Ｉ１ｍと樹
脂膜との間にシランカップリング剤を介在させたもので
ある。(Means for Solving the Problems) The optical disc of the present invention is an optical disc in which recorded information is reproduced by irradiating laser light, in which a silane coupling agent is interposed between an inorganic adhesive I1m and a resin film. It is.
以下この発明の実施例について添付図面を参照しながら
説明する。Embodiments of the present invention will be described below with reference to the accompanying drawings.
第１図及び第２図はこの発明にかかる光ディスクを示す
ものであり、この光ディスクは、基板１と、無機系保護
膜２と、磁性膜３と、無機系保護膜４と、シランカップ
リング剤５と、樹脂膜６とをＱＦｊＪしたものから形成
されている。1 and 2 show an optical disk according to the present invention, which includes a substrate 1, an inorganic protective film 2, a magnetic film 3, an inorganic protective film 4, and a silane coupling agent. 5 and the resin film 6 are formed by QFjJ.
基板１は、透明なポリカーボネイト（ＰＣ）を用いて略
円板状に形成されており、その基板１の表面側には所定
幅のレーザ光のガイド用の溝が所定ピッチでスパイラル
に設けである。なお、この基板としては、ポリカーボネ
イト（ＰＣ）に特に限定されるものではな（、例えばこ
れ以外にも透明なアクリル（ＰＭＭＡ）、ガラス等のよ
うなものでも可能である。The substrate 1 is formed into a substantially disk shape using transparent polycarbonate (PC), and grooves for guiding laser light of a predetermined width are spirally provided at a predetermined pitch on the front side of the substrate 1. . Note that this substrate is not particularly limited to polycarbonate (PC); for example, other materials such as transparent acrylic (PMMA), glass, etc. may also be used.
無機系保護膜２は、入射するレーザ光を基板１との界面
α側及び磁性ＩＩ ３との界面β側との間で多重反射さ
せてエンハンス効果を起こしカー回転角を増大させるよ
うになっており、この実施例では窒化ケイ素（ＳｉＮ）
をスパッタリングによって成膜させている。The inorganic protective film 2 multiple-reflects the incident laser light between the interface α side with the substrate 1 and the interface β side with the magnetic II 3, causing an enhancement effect and increasing the Kerr rotation angle. In this example, silicon nitride (SiN) is used.
The film is formed by sputtering.
磁性膜３は、入射するレーザ光を表面で反射する際にそ
のレーザ光の偏光面を回転する、いわゆるカー効果を発
生するようになっており、この実施例ではアモルファス
合金であるテリビウム・鉄・コバル） （ＴｂＦｅＣｏ
）が用いられており、スパッタリングによって成膜され
ている。なお、この磁性膜としては、先のテルビウム・
鉄・コバルト以外に例えばガドリニウム・テルビウム・
鉄（ＧｄＴｂＦｅ）等であってもよい。The magnetic film 3 rotates the plane of polarization of the laser beam when it reflects the incident laser beam on its surface, producing the so-called Kerr effect. Kobal) (TbFeCo
) is used, and the film is formed by sputtering. Note that this magnetic film is made of the previously mentioned terbium.
In addition to iron and cobalt, for example, gadolinium, terbium,
It may also be iron (GdTbFe) or the like.
無機系保護膜４は、磁性膜３を保護するためのものであ
り、この実施例では窒化ケイ素（ＳｉＮ）をスパッタリ
ング等によって成膜されている。The inorganic protective film 4 is for protecting the magnetic film 3, and in this embodiment, silicon nitride (SiN) is formed by sputtering or the like.
シランカップリング剤５は、分子中に２種以上の異なっ
た官能基を持つ有機ケイ素化合物であり、無機質及び有
機質の双方に対して作用するという特有の性質を有して
いる。そして、このシランカップリング剤５は、無機系
保護膜４と樹脂膜６との密着性を高めるために用いられ
ており、この実施例では原２シリコーン社製の商品名Ｔ
ＳＬ８３７０（３−メタクリロキシトリメトキシシラン
）が用いられており、これをスピンコード法あるいはス
プレー法等によって無機系保護膜４の上から薄く塗布さ
せている。なお、このＴＳＬ８３７０を有しており、次
のように加水分解する。The silane coupling agent 5 is an organosilicon compound having two or more different functional groups in its molecule, and has the unique property of acting on both inorganic and organic materials. The silane coupling agent 5 is used to improve the adhesion between the inorganic protective film 4 and the resin film 6, and in this embodiment, it is manufactured by Hara 2 Silicone Co., Ltd. under the trade name T.
SL8370 (3-methacryloxytrimethoxysilane) is used, and is applied thinly onto the inorganic protective film 4 by a spin code method, a spray method, or the like. Note that this TSL8370 is included and is hydrolyzed as follows.
Ｘ−３ｉ （ＯＣＨｚ ）：ｌ ＋３Ｈｚ Ｏ
→Ｘ Ｓ ｉ （ＯＨ）！ ＋ ３ ＣＨｓ
ＯＨよってシラノール（Ｓｔ−ＯＨ）が生成される
が、このシラノールは無機系保護膜４上の表面水酸基（
−ＯＨ）と水素結合して吸着するようになっている。X-3i (OCHz):l +3Hz O
→X Si (OH)! +3 CHs
Silanol (St-OH) is generated by OH, and this silanol is formed by the surface hydroxyl group (St-OH) on the inorganic protective film 4.
-OH) and is adsorbed through hydrogen bonding.
また、これに含まれるメタクリロキシ基は、樹脂膜６と
して用いであるアクリル系樹脂と共重合するため強い密
着力が得られる。Further, the methacryloxy group contained therein copolymerizes with the acrylic resin used as the resin film 6, so that strong adhesion can be obtained.
樹脂膜６は、光磁気ディスクとしての信頼性を高めるた
め、シランカップリング剤５の外側にコーティングする
ものであり、アクリル系のもの、叩ちこの実施例では大
日本インキ社習の高品名５Ｄ−１７が用いられており、
先のシランカップリング剤５を塗布した後充分乾燥させ
てから、コーティングさせるようになっている。なお、
８０℃〜１００ ”Ｃの熱風を用いて乾燥させるとより
効果的である。The resin film 6 is coated on the outside of the silane coupling agent 5 in order to improve reliability as a magneto-optical disk, and is made of acrylic material, and in this embodiment, Dainippon Ink Co., Ltd.'s high quality 5D. -17 is used,
After applying the silane coupling agent 5, it is sufficiently dried before coating. In addition,
Drying using hot air at 80°C to 100″C is more effective.
この実施例の光ディスクによれば、この発明者によって
スコッチテープを用いて剥離テストの実験を行ってみた
ところ、その無機系保護膜４と樹脂膜６との間に介在す
るシランカップリング剤５の結合作用によってこれら双
方には全く剥離現象の発生が見られなかった。According to the optical disc of this embodiment, when the inventor conducted a peel test using Scotch tape, it was found that the silane coupling agent 5 interposed between the inorganic protective film 4 and the resin film 6 was removed. Due to the bonding action, no peeling phenomenon was observed in either of these.
さらに、この実施例の光ディス゛りに対して冷熱サイク
ルテストや耐湿性テストの実験を行ってみたが、同様に
剥離現象が発生せず、これによって耐候性についても充
分であることが実証された。Furthermore, when the optical disk of this example was subjected to a thermal cycle test and a moisture resistance test, no peeling phenomenon occurred, which demonstrated that the optical disk had sufficient weather resistance. .
次に、この発明にかかる光ディスクの第２実施例につい
て、第３図を参照しながら説明する。なお、この実施例
において先の第１実施例と同一部分には同一符号を付し
て重複説明を避ける。Next, a second embodiment of the optical disc according to the present invention will be described with reference to FIG. In this embodiment, the same parts as in the first embodiment are given the same reference numerals to avoid redundant explanation.
この実施例の光ディスクは、基板ｌ、無機系保護膜２、
磁性膜３、シランカップリング剤５及び樹脂膜６は第１
実施例と同様のもので形成されているが、第１実施例で
の無機系０！護膜４が、窒化物膜８と酸化物膜９の２Ｆ
ｌによって構成されている。The optical disc of this embodiment includes a substrate 1, an inorganic protective film 2,
The magnetic film 3, the silane coupling agent 5 and the resin film 6 are the first
Although it is made of the same material as in the embodiment, it is made of the inorganic material used in the first embodiment. The protective film 4 consists of 2F of the nitride film 8 and the oxide film 9.
It is composed of l.
無機系保護膜８は、酸化物、例えば酸化イツトリウム（
ｙｚ Ｏ，）が用いられているが、これ以外にも例えば
酸化タンタル、酸化シリコン等でも可能である。The inorganic protective film 8 is made of an oxide such as yttrium oxide (
yz O, ) is used, but other materials such as tantalum oxide, silicon oxide, etc. may also be used.
無機系保護膜９は、窒化物、即ち窒化シリコン（ＳｉＮ
）が用いられている。なお、この実施例の無機系保護膜
は、窒化物８と酸化物９との積層物で構成したが、窒化
物と酸化物との適当な組み合わせのものでもよい。The inorganic protective film 9 is made of nitride, that is, silicon nitride (SiN
) is used. Although the inorganic protective film in this embodiment is made of a laminate of nitride 8 and oxide 9, it may be made of a suitable combination of nitride and oxide.
そして、この実施例の光ディスク・に対して先の第１実
施例と同様のテストを行い実験してみたところ、先の第
１実施例のものと同様に大きな密着力及びに磁性を有す
ることがわかった。When the optical disk of this example was subjected to the same test as in the first example, it was found that it had the same great adhesion and magnetism as the first example. Understood.
次にこの発明にかかる光ディスクの第３実施例について
、第４図を参照しながら説明する。なお、この実施例に
おいて第１．第２実施例と同一部分には同一符号を付し
て重複説明を避ける。Next, a third embodiment of the optical disc according to the present invention will be described with reference to FIG. Note that in this embodiment, the first. The same parts as in the second embodiment are given the same reference numerals to avoid redundant explanation.
この実施例の光ディスクは、基板１と、無機系保護膜１
０と、磁性１ｆＪ ３と、無機系保護膜１１と、シラン
カップリング剤１２と、樹脂膜６とから構成されており
、このうち基板１、磁性膜３及び樹脂膜６は第１実施例
と同じものが使用されている。The optical disc of this embodiment includes a substrate 1 and an inorganic protective film 1.
0, magnetic 1fJ 3, an inorganic protective film 11, a silane coupling agent 12, and a resin film 6. Of these, the substrate 1, magnetic film 3, and resin film 6 are the same as those in the first embodiment. the same one is used.
無機系保護１１ｉＪ１０には、この実施例では酸化イツ
トリウム（Ｙｚ Ｏｘ ）が用いられているが、他の酸
化物又は窒化物でもよい。In this embodiment, yttrium oxide (YzOx) is used for the inorganic protection 11iJ10, but other oxides or nitrides may be used.
シランカップリング剤１２には、この実施例ではＮ−（
２−アミノエチル）−３−アミノプロピルトリメトキシ
シランが用いられており、このＮ−（弐−アミノエチル
）−３−アミノプロピルトリメトキシシランをエタノー
ル等のアルコールで希釈し、１０〜１重量％濃度とした
溶液に、そのＮ−（２−アミノエチル）−３−アミノプ
ロピルトリメトキシシランの６〜１５倍のモル数の水を
加え攪拌・混合したものを用いており、これを無機系保
護膜１１の上からスピンコード法によって薄く塗布して
いる。In this example, the silane coupling agent 12 contains N-(
2-Aminoethyl)-3-aminopropyltrimethoxysilane is used, and this N-(2-aminoethyl)-3-aminopropyltrimethoxysilane is diluted with alcohol such as ethanol to give a concentration of 10 to 1% by weight. A concentrated solution is mixed with water in an amount 6 to 15 times the number of moles of N-(2-aminoethyl)-3-aminopropyltrimethoxysilane, and then stirred and mixed. A thin layer is applied onto the film 11 by a spin code method.
そして、この実施例の光ディスクによれば、アミノ系の
シランカップリング剤１２として用いたＮ−（２−アミ
ノエチル）−３−アミノプロピルトリメトキシシラン溶
液で処理したことにより、処理面上にスリガラス状の微
細な凹凸が形成され、これによって無機系保護膜１１と
シランカップリング剤１２との間には大きな密着力が形
成されることがわかった。According to the optical disc of this example, by treating with the N-(2-aminoethyl)-3-aminopropyltrimethoxysilane solution used as the amino-based silane coupling agent 12, ground glass was formed on the treated surface. It was found that fine irregularities of the shape were formed, and thereby a large adhesion force was formed between the inorganic protective film 11 and the silane coupling agent 12.
以上説明してきたように、この発明にかかる光ディスク
によれば、無機系保護膜と樹脂膜との間にこれら双方に
対して反応し化学結合力を発生するシランカップリング
剤によって密着性が高められており、その結果ディスク
としての耐候性が格段と向上すると共に物理的な衝撃等
に対する尉剥離性も改善させる等の潰れた効果が得られ
る。As explained above, according to the optical disc according to the present invention, the adhesion between the inorganic protective film and the resin film is enhanced by the silane coupling agent that reacts with both of them and generates a chemical bonding force. As a result, the weather resistance of the disk is significantly improved, and the peelability against physical impact and the like is also improved.
第１図はこの発明にかかる光ディスクを示す部分断面図
、第２図は第１図におけるＡ部拡大図、第３図及び第４
図は夫々この発明にかかる光ディスクの他の実施例の構
成を示す断面図、第５図は従来用いられている光ディス
クの構成を示す断面図である。
１．１００・・・・・・透明基板。
３．１０２・・・・・・磁性膜。
２．４，８，９．１０，１１，１０１゜１０３・・・・
・・無機系保護膜。
６．１０４・・・・・・樹脂膜。
５．１２・・・・・・シランカップリング剤。
出願人 日本電気ホームエレクトロ
ニクス株式会社
代理人 弁理士 増 １）竹 夫
暑 ２ 砺
肩 ３ ！
鷹４．・FIG. 1 is a partial sectional view showing an optical disc according to the present invention, FIG. 2 is an enlarged view of section A in FIG. 1, and FIGS.
Each figure is a cross-sectional view showing the structure of another embodiment of the optical disk according to the present invention, and FIG. 5 is a cross-sectional view showing the structure of a conventionally used optical disk. 1.100...Transparent substrate. 3.102...Magnetic film. 2.4,8,9.10,11,101゜103...
...Inorganic protective film. 6.104...Resin film. 5.12... Silane coupling agent. Applicant: NEC Home Electronics Co., Ltd. Representative: Patent Attorney Masu 1) Takeo Atsushi 2 Tokonata 3! Hawk 4.・
Claims (1)
クにおいて、 無機系保護膜と樹脂膜との間にシランカップリング剤を
介在させたことを特徴とする光ディスク。 ２、無機系保護膜として窒化物又は酸化物を用いた請求
項１に記載の光ディスク。 ３、無機系保護膜を窒化物と酸化物との組み合わせ又は
これらを積層したもので構成した請求項１に記載の光デ
ィスク。 ４、無機系保護膜の窒化物が窒化ケイ素で構成された請
求項１〜３に記載の光ディスク。５、無機系保護膜の酸
化物が酸化ケイ素、酸化タンタル若しくは酸化イットリ
ウムの中から選択された１種以上のもので構成された請
求項１〜３に記載の光ディスク。 ６、無機系保護膜の窒化物を窒化ケイ素で形成すると共
に樹脂膜をアクリル系のもので形成し、かつシランカッ
プリング剤としてメタクリロキシ系のものを用いた請求
項１〜５に記載の光ディスク。 ７、アルコールで希釈した０．１〜１．０重量％濃度の
３−メタクリロキシトリメトキシシラン溶液とその３−
メタクリロキシトリメトキシシランの６〜１５倍のモル
数の水との混合物で構成した物をシランカップリング剤
とする請求項６に記載の光ディスク。 ８、シランカップリング剤としてアミノ系のものを用い
た請求項１〜５に記載の光ディスク。 ９、アルコールで希釈した１〜１０重量％濃度のＮ−（
２−アミノエチル）−３−アミノプロピルトリメトキシ
シラン溶液で構成した物をシランカップリング剤とする
請求項８に記載の光ディスク。[Claims] 1. An optical disc for reproducing recorded information by irradiating laser light, characterized in that a silane coupling agent is interposed between an inorganic protective film and a resin film. 2. The optical disc according to claim 1, wherein a nitride or an oxide is used as the inorganic protective film. 3. The optical disc according to claim 1, wherein the inorganic protective film is composed of a combination of nitride and oxide or a stack of these. 4. The optical disk according to any one of claims 1 to 3, wherein the nitride of the inorganic protective film is composed of silicon nitride. 5. The optical disc according to claim 1, wherein the oxide of the inorganic protective film is composed of one or more selected from silicon oxide, tantalum oxide, and yttrium oxide. 6. The optical disk according to any one of claims 1 to 5, wherein the nitride of the inorganic protective film is formed of silicon nitride, the resin film is formed of an acrylic type, and the silane coupling agent is a methacryloxy type. 7. 3-methacryloxytrimethoxysilane solution diluted with alcohol and having a concentration of 0.1 to 1.0% by weight and its 3-
7. The optical disk according to claim 6, wherein the silane coupling agent is a mixture of methacryloxytrimethoxysilane and water in an amount of 6 to 15 times the number of moles. 8. The optical disc according to claims 1 to 5, wherein an amino-based silane coupling agent is used. 9. N-( at a concentration of 1 to 10% by weight diluted with alcohol)
9. The optical disc according to claim 8, wherein the silane coupling agent is composed of a solution of 2-aminoethyl)-3-aminopropyltrimethoxysilane.