JPH01283791A - Film type el panel - Google Patents
Film type el panelInfo
- Publication number
- JPH01283791A JPH01283791A JP63115067A JP11506788A JPH01283791A JP H01283791 A JPH01283791 A JP H01283791A JP 63115067 A JP63115067 A JP 63115067A JP 11506788 A JP11506788 A JP 11506788A JP H01283791 A JPH01283791 A JP H01283791A
- Authority
- JP
- Japan
- Prior art keywords
- moisture
- resin film
- organic resin
- black
- metal foil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（イ）産業上の利用分野
この発明は、パーソナルコンピュータやワードプロセッ
サ等のデイスプレィ装置に使用される薄膜ＥＬパネルに
関する。DETAILED DESCRIPTION OF THE INVENTION (a) Field of Industrial Application This invention relates to a thin film EL panel used in display devices such as personal computers and word processors.
（ロ）従来の技術
従来のｆｖＩＱＥＬパネルは、第４図に示すように、ガ
ラス基板！の上に下部透明電極２、下部絶縁層３、発光
Ｆ！１４、上部絶縁層５および上部電極６を順次積層し
てＥＬ素子を構成し、ＥＬ素子への湿気の侵入を防止す
るため裏躍りガラス７をエポキシ樹脂の接着剤８によっ
て固定し、更にその信頼性を高く保つために裏張りガラ
ス７の穴９を通してシリカゲル粉末及び黒色粉末を分散
させたシリコンオイルを空間ｌＯに封入し、穴９をトー
ルシール１１で密封するようにしている。また、特開昭
６１−２９０６９３号公報にみられるようにラミネート
フィルムを用いて湿気の侵入を防止するようにしたもの
ら提案されている。(b) Conventional technology The conventional fvIQEL panel, as shown in Fig. 4, uses a glass substrate! A lower transparent electrode 2, a lower insulating layer 3, and a light emitting F! 14. The upper insulating layer 5 and the upper electrode 6 are sequentially laminated to form an EL element, and the backing glass 7 is fixed with an epoxy resin adhesive 8 to prevent moisture from entering the EL element. In order to maintain high performance, silicone oil in which silica gel powder and black powder are dispersed is filled into the space IO through the hole 9 of the lining glass 7, and the hole 9 is sealed with a tall seal 11. Furthermore, as seen in Japanese Patent Application Laid-Open No. 61-290693, a laminate film has been proposed to prevent moisture from entering.
（ハ）発明が解決しようとする課題
しかしながら、面金においては、裏張りガラス及び封入
するシリコンオイルが高価であり、またシリコンオイル
を空間に封入する作業が長時間を要するため、薄膜ＥＬ
パネルの工数低減及び低コスト化が難しい。さらに、裏
張りガラス自体の厚みや重量のために薄膜ＥＬパネルの
薄型、軽量化が難しいという問題点がある。また、後者
のＥＴ、パネルでは、高コントラスト化に対する配慮が
なされていないので、高いコントラストが得られないと
いう問題点がある。(c) Problems to be Solved by the Invention However, in the case of metal plates, the lining glass and the silicone oil to be sealed are expensive, and the work of sealing the silicone oil into the space takes a long time.
It is difficult to reduce panel man-hours and costs. Furthermore, there is a problem in that it is difficult to make thin film EL panels thinner and lighter due to the thickness and weight of the lining glass itself. Furthermore, the latter ET panel does not take into consideration high contrast, so there is a problem in that high contrast cannot be obtained.
この発明は、このような事情を考慮してなされたもので
、ＥＬパネルの薄型軽量化を図り更に高コントラスト化
を実現すると共に、工数低減及び低価格化が可能な薄膜
ＥＬパネルを提供するものである。This invention was made in consideration of these circumstances, and provides a thin-film EL panel that can be made thinner and lighter, achieve higher contrast, and reduce man-hours and cost. It is.
（ニ）課題を解決するための手段
この発明は、透光性基板上に形成された薄膜ＥＬ素子と
、薄膜ＥＬ素子を被覆する防湿性シートを備え、防湿シ
ートが、黒色または黒色に近い色で着色した有機樹脂フ
ィルムをＥＬ素子側の而に積層した金属箔からなること
を特徴とする薄膜ＥＬパネルである。(d) Means for Solving the Problems This invention comprises a thin film EL element formed on a light-transmitting substrate and a moisture-proof sheet covering the thin-film EL element, and the moisture-proof sheet is black or has a color close to black. This is a thin-film EL panel characterized by comprising a metal foil in which a colored organic resin film is laminated on the EL element side.
なお、有機樹脂フィルムが透明である場合には、その表
面または裏面が黒色または黒色に近い着色層を備えるか
、もしくは金属箔がＥＬ素子側に黒色又は黒色に近い色
に着色されておればよい。In addition, when the organic resin film is transparent, it is sufficient that the front or back surface thereof is provided with a black or nearly black colored layer, or the metal foil is colored black or nearly black on the EL element side. .
（ホ）作用
ＥＬ素子は防湿シートによりシーリングされると共に、
防湿シートのＥし素子側表面が黒色又は黒色に近い色で
あるためＥＬ素子のコントラストが向上する。(E) The functioning EL element is sealed with a moisture-proof sheet, and
Since the surface of the moisture-proof sheet on the E element side is black or a color close to black, the contrast of the EL element is improved.
（へ）実施例
以下、図面に示す実施例に基づいて、この発明を詳述す
る。これによって、この発明が限定されるものではない
。(f) Examples The present invention will now be described in detail based on examples shown in the drawings. This invention is not limited by this.
第１図はこの発明の一実施例を示す構成説明図であり、
２１はガラス製の透光性基板、２２は透光性基板２１の
上に一定間隔で平行配列された帯状の下部透明電極、２
３は下部透明電極２２の上に形成された下部絶縁層、２
４は発光層、２５は発光層２４の上に積層された上部絶
縁層、２６は上部絶縁ＦＪ２５の上に下部透明電極２２
に直交する方向に一定間隔で平行配列された帯状の上部
電極であり、これらによってＥＬ素子が構成される。FIG. 1 is a configuration explanatory diagram showing one embodiment of the present invention,
21 is a transparent substrate made of glass; 22 is a band-shaped lower transparent electrode arranged in parallel at regular intervals on the transparent substrate 21;
3 is a lower insulating layer formed on the lower transparent electrode 22;
4 is a light emitting layer, 25 is an upper insulating layer laminated on the light emitting layer 24, and 26 is a lower transparent electrode 22 on the upper insulating FJ 25.
These are strip-shaped upper electrodes arranged in parallel at regular intervals in a direction perpendicular to the EL element.
２７ａは防湿シートであり、これは金属箔２８ａと有機
樹脂フィルム２９ａとが積層されて構成される。防湿シ
ート２７ａは有機樹脂フィルム２９λをＥＬ素子側に対
向させて空間３０を形成するようにＥＬ素子を被覆し、
その周辺部が透光性基板２１（場合によっては下部透明
電極２２あるいは上部透明電極２Ｇ）上に、エポキシ製
樹脂３■こよって接着されるか、あるいは防湿シート２
７λに予めコートされたホットメルト樹脂によって熱圧
着されることによって、ＥＬ素子は完全密封される。な
お、この実施例においては、金属箔２８ａには厚さ５〜
３０μ脂のアルミニウム箔を使用し、有機樹脂フィルム
２９ユには黒色または黒色に近い色に着色された厚さ５
〜５０μｌのポリエステルフィルムを使用している。27a is a moisture-proof sheet, which is constructed by laminating a metal foil 28a and an organic resin film 29a. The moisture-proof sheet 27a covers the EL element with the organic resin film 29λ facing the EL element side to form a space 30.
Its peripheral portion is adhered to the transparent substrate 21 (in some cases, the lower transparent electrode 22 or the upper transparent electrode 2G) using an epoxy resin 3 or a moisture-proof sheet 2
The EL element is completely sealed by thermocompression bonding with a hot melt resin pre-coated with 7λ. In this embodiment, the metal foil 28a has a thickness of 5 to
A 30μ thick aluminum foil is used, and the organic resin film has a thickness of 5 mm colored black or close to black.
~50 μl of polyester film is used.
第２図はこの発明の他の実施例を示す構成説明図であり
、防湿シート２７ｂにおいて、２８ｂは黒色または黒色
に近い色の金属箔、あるいはＥＬ素子側の表面が黒色ま
たは黒色に近い色に着色された金属箔、２９ｂは金属箔
２８ｂに積層された透明な有機樹脂フィルムである。そ
して、その他の構成は第１図と同等である。FIG. 2 is a configuration explanatory diagram showing another embodiment of the present invention. In the moisture-proof sheet 27b, 28b is a metal foil of black or near-black color, or the surface on the EL element side is black or near-black. The colored metal foil 29b is a transparent organic resin film laminated on the metal foil 28b. The other configurations are the same as in FIG. 1.
第３図はこの発明の更に他の実施例を示す構成説明図で
あり、防湿シート２７ｃは、金属箔２８ｃと、透明な有
機樹脂フィルム２９ｃと、両者を接着する黒色または黒
色に近い色を有する接着剤層３２から構成され、その他
の構成は第１図に示す実施例と同等である。FIG. 3 is a configuration explanatory diagram showing still another embodiment of the present invention, in which a moisture-proof sheet 27c has a metal foil 28c, a transparent organic resin film 29c, and a black or near-black color that adheres the two. It consists of an adhesive layer 32, and the other configurations are the same as the embodiment shown in FIG.
上記各実施例において、防湿シートと透光性基板とを貼
り合わせる場合には、それらを真空中で２００℃以上に
加熱し、ＥＬ素子の残留水分を充分に除去した後、乾燥
Ｎ、ガス雰囲気中で速やかに貼り合わせる。それによっ
て、ＥＬ素子と防湿シートで形成される空間に乾燥Ｎ、
ガスが封入される。なお、Ｎ、ガスが封入される空間に
、防湿性をさらに高めるために、黒色または黒色に近い
色に着色されたシリカゲルのような吸湿剤や、あるいは
吸湿剤を分散させた吸湿シートを挿入してもよい。また
、上記各実施例においては、ドツトマトリックス型°の
ＥＬ素子について説明したが、セグメント型のＥＬ素子
であってもよい。In each of the above embodiments, when bonding the moisture-proof sheet and the transparent substrate, they are heated in a vacuum to 200°C or higher to sufficiently remove residual moisture from the EL element, and then heated in a dry N, gas atmosphere. Glue them together quickly inside. As a result, dry N,
Gas is sealed. In addition, in order to further improve moisture resistance, a moisture absorbent such as silica gel colored black or close to black, or a moisture absorption sheet containing a moisture absorbent dispersed therein, is inserted into the space where N and gas are sealed. You can. Further, in each of the above embodiments, a dot matrix type EL element has been described, but a segment type EL element may also be used.
このようにして、ＥＬ素子は防湿シートによりシーリン
グが行われると共に、防湿シートのＥＬ素子側の表面が
黒色であるため、ＥＬ索子の表示においてコントラスト
が大きく向上する。また、従来のようにシリコンオイル
を封入する必要がないためＥＬ表示パネルの製介工程が
単純化され工数が低減される。In this way, the EL element is sealed by the moisture-proof sheet, and since the surface of the moisture-proof sheet on the EL element side is black, the contrast in the display of the EL element is greatly improved. Further, since there is no need to seal in silicone oil as in the conventional case, the manufacturing process of the EL display panel is simplified and the number of man-hours is reduced.
（ト）発明の効果
この発明によれば、ＥＬ表示パネルの高コントラスト化
が図られると共に、も■成が簡単で製作が容易となる。(G) Effects of the Invention According to the present invention, the contrast of the EL display panel can be increased, and the structure is simple and easy to manufacture.
第１図はこの発明の一実施例を示す構成説明図、第２図
はこの発明の池の実施例を示す第１図対応図、第３図は
この発明の更に他の実施例を示す第１図対応図、第４図
は従来例を示す第１図対応図である。
２１・・・・・・透光性基板、２２・・・・・・下部透
明電極、２３・・・・・・下部絶縁層、２４・・・・・
・発光層、２５・・・・・・上部絶縁層、２６・・・・
・・上部電極、２７ａ・・・・・・防湿シート、 ２
８ａ・・・・・・金属箔、２９ａ・・・・・・有機樹脂
フィルム、３０・・・・・・空間、３Ｉ・・・・・・接
着剤。
第１図
第２図FIG. 1 is a configuration explanatory diagram showing one embodiment of this invention, FIG. 2 is a diagram corresponding to FIG. 1 showing an embodiment of a pond of this invention, and FIG. 3 is a diagram showing still another embodiment of this invention. FIG. 1 is a diagram corresponding to FIG. 1, and FIG. 4 is a diagram corresponding to FIG. 1 showing a conventional example. 21... Transparent substrate, 22... Lower transparent electrode, 23... Lower insulating layer, 24...
- Light emitting layer, 25... Upper insulating layer, 26...
...Top electrode, 27a...Moisture-proof sheet, 2
8a...Metal foil, 29a...Organic resin film, 30...Space, 3I...Adhesive. Figure 1 Figure 2
Claims (1)
ＥＬ素子を被覆する防湿性シートを備え、防湿シートが
、黒色または黒色に近い色で着色した有機樹脂フィルム
をＥＬ素子側の面に積層した金属箔からなることを特徴
とする薄膜ＥＬパネル。1. It comprises a thin film EL element formed on a transparent substrate and a moisture-proof sheet covering the thin-film EL element, and the moisture-proof sheet has an organic resin film colored black or close to black laminated on the surface on the EL element side. A thin film EL panel characterized by being made of metal foil.