JPH01272692A - Method for preventing briquetted coal from powdering - Google Patents
Method for preventing briquetted coal from powderingInfo
- Publication number
- JPH01272692A JPH01272692A JP10129288A JP10129288A JPH01272692A JP H01272692 A JPH01272692 A JP H01272692A JP 10129288 A JP10129288 A JP 10129288A JP 10129288 A JP10129288 A JP 10129288A JP H01272692 A JPH01272692 A JP H01272692A
- Authority
- JP
- Japan
- Prior art keywords
- coal
- belt conveyor
- briquetted
- briquette
- briquetted coal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
この発明は成型炭槽からベルトコンベアを介して石炭塔
に供給される成型炭の粉化防止方法に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial Application Field) The present invention relates to a method for preventing pulverization of molded coal supplied from a molded coal tank to a coal tower via a belt conveyor.
(従来の技術及び発明が解決しようとする課題)成型炭
は、配合炭と混合されて石炭塔へベルトコンベアを乗り
継いで送給されるが、ベルトコンベアのジャンクション
にて落下する際に、その落下の衝撃により成型炭がかな
りの割合で粉化していた。(Prior art and problems to be solved by the invention) Molded coal is mixed with blended coal and sent to the coal tower via a belt conveyor, but when it falls at the junction of the belt conveyor, the A considerable proportion of the briquette coal was pulverized by the impact.
この発明は、かかる問題点を解決するためになされたも
ので、成型炭の粉化率を減少させることを可能にした成
型炭の粉化防止方法を得ることを目的とする。The present invention was made to solve this problem, and an object of the present invention is to provide a method for preventing pulverization of briquette coal, which makes it possible to reduce the pulverization rate of molten coal.
(課題を解決するための手段)
この発明に係る成型炭の粉化防止方法は、成型炭払出し
時に、ベルトコンベア争ジャンクションにおいて、ター
ル滓を成型炭にスプレー・コーティングする。(Means for Solving the Problems) A method for preventing pulverization of briquette coal according to the present invention sprays and coats briquette coal with tar slag at a belt conveyor junction when discharging briquette coal.
(作用)
この発明においては、ベルトコンベア・ジャンクション
において、成型炭をタール滓でスプレー−コーティング
するので、タール滓がクツションとなって成型炭の形状
が崩れる率が小さくなる。(Function) In this invention, since the briquette is spray-coated with the tar slag at the belt conveyor junction, the rate at which the tar slag becomes a cushion and the briquette loses its shape is reduced.
(実施例) 第1図はこの発明の一実施例を示す図である。(Example) FIG. 1 is a diagram showing an embodiment of the present invention.
図において、(1)は成型炭が貯蔵された成型炭槽、(
2)はタール滓が貯蔵されたタンク、(3) 、 (5
) 。In the figure, (1) is a briquette tank in which briquette coal is stored;
2) is a tank where tar slag is stored, (3), (5
).
(8) 、 (7)はベルトコンベア、(4)はタール
滓を成型炭にスプレーするスプレーガン、(8)は石炭
塔で、(9)はコークス炉である。(8) and (7) are belt conveyors, (4) is a spray gun that sprays tar slag onto briquette coal, (8) is a coal tower, and (9) is a coke oven.
上記のよう15、構成された設備において、成型炭槽(
1)から排Llされた成型炭は、ベルトコンベア(3)
からベル1コンベア(6)へと移送される。そのとき、
ベル1コンベア(3) (6)のジャンクションで、タ
ンク・、2)からのタール滓がスプレーガン(4)によ
り成型炭に下方から吹き付けられる。その後、配合ポ′
がベルトコンベア(5)によりベルトコンベア(6)上
に移送されてくる。このため、タール滓でツー−1イン
グされた成型炭は、タール滓に配合r?が付着し、て、
更に配合炭(23)でコーテングされる。In the equipment configured as above 15, the molten coal tank (
Molded coal discharged from 1) is transferred to a belt conveyor (3)
from there to the Bell 1 conveyor (6). then,
At the junction of Bell 1 conveyors (3) and (6), tar slag from tanks 2) is sprayed onto the briquette coal from below by a spray gun (4). After that, the blending point
is transferred onto the belt conveyor (6) by the belt conveyor (5). For this reason, briquette coal that has been mixed with tar slag is mixed with tar slag. is attached,
Furthermore, it is coated with a coal blend (23).
このように2手(7コーテイングされた成型炭は、更に
ベルトコンへ (7)を介して石炭t! (8)に移送
され、更に、そ、Sらコークス炉(9)に移送される。The briquette coated in this way is further transferred to a belt converter (7) to a coal t! (8), and further transferred to a coke oven (9).
従って、ベルトコンベア(6)以降の移送に際しては、
成型炭が2重のコーティングされているので、これらの
コーティングがクツションとなり、成型炭の形状が崩れ
る率が著しく小さくなっている。Therefore, when transferring after the belt conveyor (6),
Since the briquettes are coated in two layers, these coatings act as a cushion and the rate at which the briquettes lose their shape is significantly reduced.
第2図(A)は従来の成型炭(21)で、同図(B)は
成型炭(21)にタール滓(22)及び配合炭(23)
をつ・−テ・rングしたこの実施例の成型炭(20)で
あり、これらについてシャッター強度による比較は次の
とおりである。なお、下記の数値は原型保持率を示して
いる。Figure 2 (A) shows conventional briquette coal (21), and Figure 2 (B) shows briquette coal (21), tar slag (22) and blended coal (23).
This is the briquette coal (20) of this example which was subjected to the following process.A comparison of these in terms of shutter strength is as follows. The numbers below indicate the original shape retention rate.
(従来例) (実施例)
1回 99.6% 100.0%
3 97.3 97.8
5 95.6 9”1.7
7 93.3 97.6
10 90.1 96.8
上記の実験例から明らかなように、回数が増える程この
実施例の効果が顕著になっている。(Conventional example) (Example) 1 time 99.6% 100.0% 3 97.3 97.8 5 95.6 9”1.7 7 93.3 97.6 10 90.1 96.8 Above As is clear from the experimental examples, the effect of this example becomes more significant as the number of experiments increases.
(発明の効果)
以上のようにこの発明によれば、移送の途中で成型炭に
タール滓をコ・−ティングするようにしたので、それが
クツションとなって成型炭の粉化率が著しく減少してい
る。(Effects of the Invention) As described above, according to the present invention, tar slag is coated on the briquette coal during transportation, which acts as a cushion and significantly reduces the pulverization rate of the briquette coal. are doing.
第1図はこの発明の一実施例に係る方法を実施する装置
及び関連設備の説明図で、第2図は従来の成型炭と上記
実施例の成型炭の説明図である。
代理人 弁理士 佐 々 木 宗 治
第 1 図FIG. 1 is an explanatory diagram of an apparatus and related equipment for carrying out a method according to an embodiment of the present invention, and FIG. 2 is an explanatory diagram of conventional briquette coal and the briquette of the above embodiment. Agent Patent Attorney Souji Sasaki Figure 1
Claims (1)
おいて、タール滓を成型炭にスプレー・コーティングす
ることを特徴とする成型炭の粉化防止方法。A method for preventing pulverization of molded coal, characterized by spraying and coating the molded coal with tar slag at a belt conveyor junction when the molded coal is discharged.