JPH01210500A - Material capable of removing foreign matter adhering to vehicle outside plate - Google Patents
Material capable of removing foreign matter adhering to vehicle outside plateInfo
- Publication number
- JPH01210500A JPH01210500A JP3596888A JP3596888A JPH01210500A JP H01210500 A JPH01210500 A JP H01210500A JP 3596888 A JP3596888 A JP 3596888A JP 3596888 A JP3596888 A JP 3596888A JP H01210500 A JPH01210500 A JP H01210500A
- Authority
- JP
- Japan
- Prior art keywords
- foreign matter
- asbestos
- weight
- vehicle
- synthetic rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、自動車、自動二輪車等の塗装された外板に付
着した塗装粉末、鉄粉、火山灰等の異物を取除くために
用いる異物除去材に関する。[Detailed Description of the Invention] [Field of Industrial Application] The present invention is a foreign matter removal method used to remove foreign matter such as paint powder, iron powder, volcanic ash, etc. adhering to the painted outer panels of automobiles, motorcycles, etc. Regarding materials.
従来、車輌外板の塗装面には、塗装粉末、鉄粉。 Traditionally, paint powder and iron powder were applied to the painted surfaces of vehicle exterior panels.
火山灰等の異物が付着し易い。そして、異物の付着が少
ない場合は洗車するか、市販の専用ワックスを塗布して
除去していた。このように、洗車かワックスの塗布作業
ですむ場合は、車輌外板は問題なく綺麗になっていた。Foreign matter such as volcanic ash easily adheres to it. If there was only a small amount of foreign matter adhering to it, it was removed by washing the car or applying a commercially available special wax. In this way, if all you had to do was wash the car or apply wax, the exterior of the vehicle would be clean without any problems.
しかし、車輌外板に対する異物の付着が多い場合は異物
が簡単に落ち難く、全面を塗装置しするか、あるいは、
回転ポリラシャと称する機械と異物を削るためのコンパ
ウンドによって除去するしかなく、作業も長時間を要し
ていた。そして、コンパウンドを使用する作業の場合は
、塗装面を削って異物を取るため塗装面を痛め光沢をな
くし、車輌外板の老化を早める原因となっていた。However, if there is a lot of foreign matter adhering to the exterior of the vehicle, it is difficult to remove the foreign matter easily, so it is necessary to paint the entire surface, or
The only way to remove the foreign matter was with a machine called a rotary polisher and a compound for scraping the foreign matter, which took a long time. In the case of work using compounds, the painted surface is scraped to remove foreign matter, which damages the painted surface and causes it to lose its luster, causing accelerated aging of the vehicle's exterior panels.
本発明は、車輌外板の全面塗装置しや塗装面の削り取り
を要せずに、これらの問題点を解消できる異物除去材を
提供すること番目的とする。It is an object of the present invention to provide a foreign matter removal material that can solve these problems without requiring painting the entire surface of a vehicle exterior panel or scraping off the painted surface.
本発明の車輌外板に付着した異物除去材は、その目的を
達成するため、合成ゴム１５．０〜５５．０重量％、石
綿１５．０〜４５．０重量％、滑石１．０〜２．５重量
％、老化防止剤０．５〜１２．０重量％、着色剤０．４
〜１．５重量％、炭酸カルシウム０〜２８．０重量％、
クレー０〜２８．０重量％からなることを特徴とする特
〔作用〕
本発明の異物除去材は、合成ゴム、石綿、滑石。In order to achieve the purpose, the material for removing foreign matter attached to the vehicle outer panel of the present invention is composed of 15.0 to 55.0% by weight of synthetic rubber, 15.0 to 45.0% by weight of asbestos, and 1.0 to 2% of talc. .5% by weight, anti-aging agent 0.5-12.0% by weight, colorant 0.4
~1.5% by weight, calcium carbonate 0-28.0% by weight,
Features [Function] The foreign matter removing material of the present invention is composed of 0 to 28.0% by weight of clay.
老化防止剤及び着色剤を必須成分とする可塑性をもった
粘土状の固形物である。It is a clay-like solid substance with plasticity that contains an anti-aging agent and a coloring agent as essential ingredients.
この中、合成ゴムは石綿等の材料を保持するための基材
であると共に、適度の可塑性を持って車輌外板の塗装面
に対する接触を良くし、且つ塗装面に付着した異物に粘
着して異物を取除く粘着性を持った代用粘土とする材料
である。合成ゴムとしては、ポリイソブチレン、ポリオ
レフィンポリドール、ポリブタジェンゴム（ＢＲ）、
ブタジェンスチレンゴム（ＳＢＲ）、 ブタジェンアク
リロニトリルゴム（ＮＢＲ）、ポリクロロプレン（ＣＲ
）、 クロルスルホン化ポリエチレン（ＩＲ）、インブ
チレンイソプレンゴム（ＩＩＲ）等多数の種類がある。Among these, synthetic rubber is a base material for holding materials such as asbestos, and has appropriate plasticity to improve contact with the painted surface of the vehicle exterior panel, and also to prevent foreign matter adhering to the painted surface. This material is used as a clay substitute with adhesive properties to remove foreign substances. Synthetic rubbers include polyisobutylene, polyolefin polydol, polybutadiene rubber (BR),
Butadiene styrene rubber (SBR), butadiene acrylonitrile rubber (NBR), polychloroprene (CR)
), chlorosulfonated polyethylene (IR), and inbutylene isoprene rubber (IIR).
これらのうち、はとんどすべての合成ゴムを異物除去材
の基材として用い得るが、種々比較試験の結果、ブタジ
ェンスチレンゴム（ＳＢＲ）およびポリブタジェンゴム
（ＢＲ）の油入りゴム、すなわちオイルエキステンデッ
ドラバーが添加した油によりゴム特有の高い摩擦係数を
下げ、車輌外板に対する滑りをよくし、作業性がよく好
ましいことを見出した。Of these, almost all synthetic rubbers can be used as the base material for the foreign matter removal material, but as a result of various comparative tests, oil-filled rubbers such as butadiene styrene rubber (SBR) and polybutadiene rubber (BR), In other words, it has been found that oil extended rubber reduces the high coefficient of friction peculiar to rubber due to the added oil, improves the slippage on the vehicle outer panel, and is preferable for its workability.
特に、ブタジェンスチレンゴム（ＳＢＲ）では、合成ゴ
ム１００重量部当たり５０重量部の油を添加したものが
市販されており、人手し易く且つ安価なため、最も好ま
しい材料である。In particular, butadiene styrene rubber (SBR) is commercially available in which 50 parts by weight of oil is added per 100 parts by weight of synthetic rubber, and is the most preferred material because it is easy to handle and inexpensive.
天然ゴムも試験したが、粘着性、やわらかさの点から不
適である。Natural rubber was also tested, but it was not suitable due to its stickiness and softness.
本発明においては、異物除去材１００重量％当たり１５
．０〜４５．０重量％の石綿を添加する。石綿はアスベ
ストとも称し、繊維状の結晶からなる鉱物である。石綿
は車輌外板の塗装面上に付着した異物の突起をその繊維
で引掛けて取り除くために、合成ゴム中に混練する必須
成分である。異物除去材中の石綿量を４５．０重量％以
上にすることは、異物除去材の表面に表れる石綿が多く
なり、異物の突起に対する石綿の引掛かりをよくするが
、石綿の混練に時間を要し、合成ゴム中への分散が困難
となり、性能も殆ど改善されない。In the present invention, 15% per 100% by weight of the foreign matter removing material
．． 0-45.0% by weight of asbestos is added. Asbestos, also called asbestos, is a mineral consisting of fibrous crystals. Asbestos is an essential ingredient that is mixed into synthetic rubber in order to use its fibers to catch and remove foreign particles adhering to the painted surface of vehicle exterior panels. Setting the amount of asbestos in the foreign matter removal material to 45.0% by weight or more increases the amount of asbestos that appears on the surface of the foreign matter removal material, making it easier for the asbestos to catch foreign matter protrusions, but it takes time to knead the asbestos. Therefore, dispersion into synthetic rubber becomes difficult, and performance is hardly improved.
一方、石綿の添加量を１５．０重量％以下にすると、合
成ゴムに対する混練は容易であるが、異物除去材の表面
に表れる石綿が相対的に少なくなり、異物の突起に対す
る石綿の引掛かりが少なくなり、性能が悪くなる。On the other hand, when the amount of asbestos added is 15.0% by weight or less, it is easy to knead into synthetic rubber, but the amount of asbestos appearing on the surface of the foreign material removal material is relatively small, and asbestos is less likely to get caught on foreign material protrusions. The performance will deteriorate.
また、本発明においては、必須成分として１．０〜２．
５重量％の滑石を添加する。滑石は硬度１〜１．５で甚
だ軟らかく、滑らかな触感をもち、細粉として減摩剤等
に用いられる。本発明では滑石を異物除去剤の車輌外板
に対する滑りをよくするために用いる。In addition, in the present invention, 1.0 to 2.
Add 5% by weight of talcum. Talc has a hardness of 1 to 1.5 and is extremely soft and smooth to the touch, and is used as a fine powder in anti-friction agents. In the present invention, talc is used to improve the slippage of the foreign matter remover on the vehicle outer panel.
しかし、２．５重量％以上を添加しても滑りはそれほど
改善されなくなる。また、１．０重量％以下では滑りは
ほとんど改善されない。However, even if 2.5% by weight or more is added, the slippage will not be improved so much. Moreover, if it is less than 1.0% by weight, slippage is hardly improved.
異物除去材の製造後における硬化、亀裂発生等の老化を
防止するために、０．５〜１２．０重量％の老化防止剤
を添加する。老化防止剤としては、ポリオレフィン系の
合成樹脂であるＰＥ、ＰＰやＡＢＳ樹脂を用いる。老化
防止剤の添加は車輌外板の酸化防止作用を改善する。す
なわち、車輌外板の塗装面の引掛けや剥離を生じた部分
に付着して、発錆を防止すると共に、生じた錆の進行を
阻止するのを助ける。しかし、１２．０重量％以上添加
しても、酸化防止効果はあまり改善されない。In order to prevent aging such as hardening and cracking after production of the foreign matter removal material, 0.5 to 12.0% by weight of an anti-aging agent is added. As the anti-aging agent, polyolefin-based synthetic resins such as PE, PP, and ABS resin are used. The addition of anti-aging agents improves the antioxidant properties of the vehicle skin. That is, it adheres to parts of the painted surface of a vehicle's outer panel that have caught or peeled off, thereby preventing rust and helping to inhibit the progress of the rust that has formed. However, even if 12.0% by weight or more is added, the antioxidant effect is not improved much.
異物除去材は、加硫されることなく可塑性をもった粘土
状の固形物として使用するので、合成ゴム中の不飽和二
重結合は架橋されないまま残っており、酸化を受けて変
質して硬化し易い。このため、相対的に老化防止剤の添
加量を多くした。しかし、１２．０重量％以上を添加し
ても老化による硬化はほとんど改善されなくなる。また
、０．５重量％以下の添加量では老化防止にはほとんど
役立たない。The foreign matter removal material is used as a clay-like solid with plasticity without being vulcanized, so the unsaturated double bonds in the synthetic rubber remain uncrosslinked and undergo oxidation, deterioration and hardening. Easy to do. For this reason, the amount of anti-aging agent added was relatively increased. However, even if 12.0% by weight or more is added, hardening due to aging will hardly be improved. Further, if the amount added is less than 0.5% by weight, it is hardly useful for preventing aging.
更に、本発明にふいては異物除去材に０．４〜１．５重
量％の着色剤を使用して綺麗な色に着色する。Furthermore, in the present invention, the foreign matter removing material is colored with a beautiful color by using a coloring agent of 0.4 to 1.5% by weight.
着色剤は異物除去材に対する異物の付着程度を測定する
ための一種のスケールであると共に、異物除去材の外観
をよくし商品価値を高めるものである。The coloring agent is a kind of scale for measuring the degree of adhesion of foreign matter to the foreign matter removal material, and also improves the appearance of the foreign matter removal material and increases its commercial value.
本発明の異物除去材は、必須成分のみによって満足な製
品を製造することができる。しかし、上記の必須成分と
しての石綿、滑石、老化防止剤及び着色剤に加えて、下
記の炭酸カルシウム、クレーを任意成分として添加する
ことができる。With the foreign matter removing material of the present invention, a satisfactory product can be manufactured using only essential ingredients. However, in addition to the above-mentioned essential ingredients such as asbestos, talc, anti-aging agent, and coloring agent, the following calcium carbonate and clay can be added as optional ingredients.
このうち、炭酸カルシウムは表面処理をしたものを加硫
ゴムの引張り強さ、伸びを改善する補強剤として用いる
が、本発明においては加硫されない異物除去材の滑りを
よくするため、０〜２８重量％添加することができる。Of these, surface-treated calcium carbonate is used as a reinforcing agent to improve the tensile strength and elongation of vulcanized rubber. % by weight can be added.
但し、２８重量％以上の量を添加しても滑りは殆ど改善
されない上、品質を低下する。However, even if it is added in an amount of 28% by weight or more, the slippage is hardly improved and the quality is deteriorated.
クレー、即ち粘土は湿っているとき粘性をもち玉状を呈
し、土壌の重要成分を構成するが、異物除去剤の車輌外
板に対する密着性を良くし、それ自体の固化を増す固化
剤として、０〜２８重量％添加することができる。しか
し、２８重量％以上の量を添加しても密着性又は固化は
それほど改善されない。加えて、異物除去剤の品質を低
下する。Clay, which is viscous and ball-shaped when wet, constitutes an important component of soil, but it is used as a solidifying agent that improves the adhesion of the foreign matter remover to the vehicle exterior plate and increases the solidification of itself. It can be added in an amount of 0 to 28% by weight. However, adding more than 28% by weight does not significantly improve adhesion or solidification. In addition, the quality of the foreign material remover is reduced.
以下に、本発明の特徴を実施例によって具体的に説明す
る。Hereinafter, the features of the present invention will be specifically explained using examples.
着色剤を石綿に添加して予め着色させておき、２本ロー
ル、パンバリミキサ又は撹拌機のいずれかにより、合成
ゴムを可塑化しながら着色剤を混入した石綿、滑石、老
化防止剤を添加して均一に混練した。混練を終わり可塑
性をもち粘土状となった混練物を加熱した型に入れて加
圧成形した後冷却すると、六面体小ブロツク状の異物除
去材が得られた。A coloring agent is added to asbestos to color it in advance, and asbestos mixed with a coloring agent, talc, and an anti-aging agent are added while plasticizing the synthetic rubber using either a two-roll machine, a panburi mixer, or a stirrer to uniformly color the asbestos. It was kneaded. After kneading, the kneaded material, which had plasticity and became clay-like, was put into a heated mold, pressure-molded, and then cooled to obtain a foreign matter removal material in the form of hexahedral small blocks.
必須成分に対して任意成分を添加して異物除去材を製造
する場合にも、混練して可塑化しながら炭酸カルシウム
、クレー、酸化防止剤等の添加剤を順次添加しながら均
一な配合物が得られるまで混練した。配合物を加熱成形
して異物除去材の製品とした。Even when manufacturing a foreign matter removal material by adding optional ingredients to the essential ingredients, a uniform mixture can be obtained by sequentially adding additives such as calcium carbonate, clay, and antioxidants while kneading and plasticizing. Knead until smooth. The mixture was heat-molded to make a foreign material removal material product.
第１表は異物除去材の配合表を示すもので、実施例１の
配合を基嘩配合としてこれに炭酸カルシウム、クレーの
任意成分を添加して各種の配合の異物除去材を製造した
例を示すものである。Table 1 shows a formulation table for foreign matter removal materials, and shows examples in which foreign matter removal materials with various formulations were manufactured by adding optional ingredients such as calcium carbonate and clay to the formulation of Example 1 as the basic formulation. It shows.
炭酸カルシウム及びクレーの添加は異物除去材が安価に
できるが、製品が硬くなる傾向がある。Addition of calcium carbonate and clay makes the foreign material removal material inexpensive, but tends to make the product hard.
本１：油含有量５０重量部
以下、本発明に係る異物除去材の使用方法について、具
体的に説明する。Book 1: The method of using the foreign matter removing material according to the present invention, which has an oil content of 50 parts by weight or less, will be specifically explained.
車輌外板の落ち易い埃を箒等で落とした後、異物除去材
を持って外板の塗装面を擦る。粘土状の可塑性を有する
異物除去材は、外板の曲面になじみ、合成ゴムによる油
分、滑石及び炭酸カルシウムの助けにより塗装面上を滑
りながら塗装面の異物による突起に異物除去材中の合成
ゴムを粘着させて除去すると共に、異物除去材中に分散
している繊維状の石綿が異物の突起を引掛けて除去する
。After removing easily removed dust from the vehicle's exterior panels with a broom, etc., rub the painted surface of the vehicle's exterior panels with a foreign object remover. The foreign matter removal material, which has clay-like plasticity, conforms to the curved surface of the outer panel and slides on the painted surface with the help of oil, talc, and calcium carbonate from the synthetic rubber. At the same time, the fibrous asbestos dispersed in the foreign material remover catches the protrusions of the foreign material and removes it.
使用中に、異物除去材の表面付近は異物が付着して次第
に変色する。During use, foreign matter adheres to the vicinity of the surface of the foreign matter removal material and the material gradually changes color.
異物除去材の一面の着色が汚くなったら、他の新しい面
で車輌外板の塗装面を擦る。車輌外板の異物は石綿や滑
石、クレー等の鉱物材料により除去されると共に、これ
らの材料は塗装面をほとんど傷付けることなく研磨する
作用をし、且つ合成ゴム中の鉱物油分が表面を被覆する
ので光沢を有し、老化防止剤による防錆をも兼ねた綺麗
な仕上りとなり、異物付着前の状態に復元される。When the color on one side of the foreign object removal material becomes dirty, rub the painted surface of the vehicle's exterior with another new side. Foreign matter on the exterior of the vehicle is removed by mineral materials such as asbestos, talcum, and clay. These materials also work to polish the painted surface without damaging it, and the mineral oil in the synthetic rubber coats the surface. As a result, it has a glossy finish and is also rust-proofed by the anti-aging agent, giving it a beautiful finish and restoring it to its state before foreign matter was attached.
本発明の異物除去材は、車輌外板の塗装面をほとんど傷
付けず、従来のコンパウンド使用にょる作業が約３時間
を要するのに比べ、約１７３の時間で作業を終えること
ができる。The foreign matter removal material of the present invention hardly damages the painted surface of the vehicle exterior panel, and can complete the work in about 173 hours, compared to about 3 hours using conventional compounds.
本発明の車輌外板に付着した異物除去材によれば、油性
の合成ゴムを基材として粘土状に可塑化し、これに異物
を引掛ける石綿、滑りをよくする滑石及び老化防止剤を
分散した混練物とした。このため、塗装面上の異物を石
綿で引掛けて除去すると共に含有する油分で被覆し、異
物の付着しない元の状態に近い車輌外板に仕上げること
ができる。異物除去材には、硬化を防ぐ老化防止剤を配
合してあり、且つ粘土状の固形物であるため、手でこね
直して長く使用することができる。According to the material for removing foreign matter adhering to a vehicle outer panel of the present invention, oil-based synthetic rubber is plasticized into a clay-like base material, and asbestos that traps foreign matter, talc that improves slippage, and an anti-aging agent are dispersed therein. It was made into a kneaded product. For this reason, foreign matter on the painted surface can be removed by catching it with asbestos and coated with the oil contained therein, making it possible to finish the vehicle exterior panel in a state close to its original state without any foreign matter adhering to it. The foreign matter removal material contains an anti-aging agent to prevent hardening, and since it is a clay-like solid, it can be kneaded by hand and used for a long time.
Claims (1)
〜４５．０重量％、滑石１．０〜２．５重量％、老化防
止剤０．５〜１２．０重量％、着色剤０．４〜１．５重
量％、炭酸カルシウム０〜２８．０重量％、クレー０〜
２８．０重量％からなることを特徴とする車輌外板に付
着した異物除去材。1. Synthetic rubber 15.0-55.0% by weight, asbestos 15.0%
~45.0% by weight, talc 1.0-2.5% by weight, anti-aging agent 0.5-12.0% by weight, colorant 0.4-1.5% by weight, calcium carbonate 0-28.0 Weight%, clay 0~
A foreign matter removal material attached to a vehicle outer panel, characterized by comprising 28.0% by weight.