JPH01153471A - Easily unsealable sterilized package - Google Patents
Easily unsealable sterilized packageInfo
- Publication number
- JPH01153471A JPH01153471A JP30967687A JP30967687A JPH01153471A JP H01153471 A JPH01153471 A JP H01153471A JP 30967687 A JP30967687 A JP 30967687A JP 30967687 A JP30967687 A JP 30967687A JP H01153471 A JPH01153471 A JP H01153471A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- parts
- air
- weight
- polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は易開封性滅菌包装体に関し、特にポリエチレン
系不織布、紙基材等からなる透気性基材を使用した易開
封性滅菌包装体に関する。Detailed Description of the Invention (Industrial Application Field) The present invention relates to an easy-to-open sterilized package, and more particularly to an easy-to-open sterile package using an air-permeable base material made of polyethylene nonwoven fabric, paper base material, etc. .
（従来の技術）
従来より合成樹脂系不織布等からなる透気性基材を用い
た易開封性滅菌袋は知られており、これらの製造方法と
しては上記の合成樹脂系不織布に溶剤系の易開封性接着
剤を塗布、接着して製造されているが、このような方法
では接着剤が通気性基材中に滲み込んで透気度を低下さ
せる原因となり、これを防］トするために通気性基材に
アンカー剤層を施したり、或は接着剤を格子状、点状に
塗布しなければならないという欠点があった。(Prior Art) Easy-to-open sterilization bags using an air-permeable base material made of a synthetic resin non-woven fabric have been known for a long time, and the manufacturing method for these bags is to use a solvent-based easy-to-open bag on the above-mentioned synthetic resin non-woven fabric. However, in this method, the adhesive seeps into the breathable base material and causes a decrease in air permeability. This method has the disadvantage that it is necessary to apply an anchoring agent layer to the adhesive base material, or to apply the adhesive in a grid or dotted manner.
（解決すべき問題点）
本発明者は上記の欠点を改善し、通気性基材の透気度を
害することなく、容易に易開封性滅菌包装体をイ＾く種
々検討した結果本発明を完成したもので、本発明の目的
は通気性基材の透気度を害ねない易開封性滅菌包装体を
提供するにある。(Problems to be Solved) The present inventor has developed the present invention as a result of various studies to improve the above-mentioned drawbacks and create an easily openable sterilized package without impairing the air permeability of the breathable base material. The object of the present invention is to provide an easy-to-open sterilized package that does not impair the air permeability of the air-permeable base material.
（問題点を解決するための手段）
すなわち１本発明は、一方の包装材に合成樹脂フィルム
基材を用い、他方に合成樹脂系不織布、紙基材等からな
る透気性基材を用い、両者の必要部相互を熱接着してな
る、滅菌用包装体において、透気性基材全面に易開封性
接着材１００重量部に対し、低分子量ポリエチレン系を
１００〜１０００重斌部、ポリエチレン系微粒状熱接着
剤５０〜５００重量部を混合した水溶性の易開封性接着
剤を塗布成層し、最低製膜温度以下の温度で接着層を形
成したことを特徴とする易開封性滅菌用包装体である。(Means for Solving the Problems) That is, one aspect of the present invention is to use a synthetic resin film base material for one packaging material, and use an air-permeable base material made of a synthetic resin nonwoven fabric, paper base material, etc. for the other packaging material, and to combine both packaging materials. In a sterilization package formed by thermally bonding the necessary parts of each other, 100 parts by weight of an easy-to-open adhesive is applied to the entire surface of an air-permeable base, 100 to 1000 parts by weight of low-molecular-weight polyethylene, and polyethylene fine particles. An easy-open sterilization package characterized by coating and layering a water-soluble easy-open adhesive mixed with 50 to 500 parts by weight of a thermal adhesive, and forming an adhesive layer at a temperature below the minimum film forming temperature. be.
本発明で使用する易開封性接着材とはポリエチレン、或
はエチレン−酢酸ビニル共重合体等を主成分として種々
の変性処理を行った水性ディスバージョンであって、該
易開封性接着材１００重量部に対し、低分子量のポリエ
チレン１００〜１ 、０００重量部、エチレン系微粒状
熱接着剤５０〜５００重量部の割合で混合したものであ
って低分量のポリエチレンとは分子量約ｓ、ｏｏｏ〜２
０，０００程度のワックス状のポリエチレンであって、
これを易開封性接着材１００重量部に対し、１００重景
重量下では易開封性を生ぜず、また、１ 、０００重量
部以上を使用すると接着が弱くなり、また、塗布膜をは
じく傾向が生ずる。エチレン系微粒状熱接着剤とはエチ
レン−酢酸ビニル共重合体変性物、エチレンーマクリル
酸エステル共重合体変性物、塩素化ポリプロピレン等の
混合物であり、その配合量が５０屯量部以ドでは接着が
弱くなり、他方５００重量部以上では接着が強くなりす
ぎ、易開封性が得られないものである。そして特に好ま
しい組成としては低分子、）ｌｋポリエチレン１００〜
５００重量部、エチレン系微オヘγ状熱接着剤５０〜２
００重量部である。この水分散性易開封性接着剤は５〜
１５ｇ／ｍ２程度のｔ（で塗布することが好ましく、余
り多量に塗布すると透気性を損なう。そして接着剤の最
低製膜温度より低い温度で加熱して接着層を形成して他
方の合成樹脂フィルムの必要部位と接着するものである
。The easy-open adhesive used in the present invention is an aqueous dispersion made of polyethylene or ethylene-vinyl acetate copolymer, etc., which has been subjected to various modification treatments. 100 to 1,000 parts by weight of low molecular weight polyethylene and 50 to 500 parts by weight of ethylene-based fine particulate thermal adhesive.
0,000 wax-like polyethylene,
If this is applied to 100 parts by weight of the easy-open adhesive, easy-opening will not occur if the weight is 100 parts by weight or more, and if more than 1,000 parts by weight is used, the adhesion will become weak and the coating film will tend to be repelled. arise. Ethylene-based fine particulate thermal adhesive is a mixture of modified ethylene-vinyl acetate copolymer, modified ethylene-macrylic acid ester copolymer, chlorinated polypropylene, etc., and the blending amount is 50 parts by weight or less. If the amount is more than 500 parts by weight, the adhesion becomes too strong and easy opening cannot be obtained. A particularly preferable composition is low molecular weight polyethylene ()lk polyethylene 100~
500 parts by weight, ethylene-based fine-gamma gamma adhesive 50-2
00 parts by weight. This water-dispersible, easy-to-open adhesive has a
It is preferable to apply the coating at a temperature of about 15 g/m2 (t); if too much is applied, the air permeability will be impaired.Then, the adhesive layer is formed by heating at a temperature lower than the minimum film forming temperature of the adhesive, and then the other synthetic resin film is coated. It is attached to the required part of the body.
本発明で使用される合成樹脂フィルムとしてはポリスチ
レン、ポリエチレン、ポリプロピレン、ポリ塩化ビニル
、ポリカーボネート、ポリエステル等であり、また、透
気性ノル材としては、ポリエチレン、ポリプロピレン等
からなる合成樹脂；トラ不織布、クラフト紙、和紙等の
紙よ１（材等が用いられ、ポリエチレン不織布としては
タイベックとして市販されているものが好ましい。Synthetic resin films used in the present invention include polystyrene, polyethylene, polypropylene, polyvinyl chloride, polycarbonate, polyester, etc., and air-permeable materials include synthetic resins such as polyethylene and polypropylene; nonwoven fabric, and kraft. Materials such as paper and Japanese paper are used, and the polyethylene nonwoven fabric commercially available as Tyvek is preferred.
本発明の包装体は、包装材同志を重ね合せて。The packaging body of the present invention is made by overlapping packaging materials.
必要部位を熱接着した包装袋や、蓋材を容器本体からな
る容器等に用いられるものである。It is used for packaging bags whose necessary parts are thermally bonded, containers whose lid is made of the container body, and the like.
次に実施例をもって本発明を更に詳細に説明する。Next, the present invention will be explained in more detail with reference to Examples.
実施例１
厚さ０．５ｍｍのポリスチレンシートとポリエチレン系
不織布（商品名：タイベック）とより易開封性滅菌包装
体を製造した。すなわち、エチレン相互重合体よりなる
水性分散体（東洋モートン（株）″ｍＡＤ−３７ＪＤ１
１９８固形分３７％）１００重景重量対し、低分子量ポ
リエチレン（三井石油化学（株）製ケミパールＷ−１０
０固形分４０％）２００重量部及びポリエチレン系微粒
状接着剤（東洋モートン（株）ｊＪｌｌｊＡＤ−３７Ｒ
３４５固形分４０％） １００重量部を添加して得られ
た易開封性接着剤をポリエチレン系不織布の一面の全面
に約１０ｇ／ｍ２塗布成層し、約１００℃の最低製膜以
下の温度で乾燥し接着層を形成し、この接着層の上にポ
リスチレンシートをのせ加熱加圧して両者の必要部を圧
着して包装袋とした。Example 1 An easily openable sterilized package was manufactured from a polystyrene sheet with a thickness of 0.5 mm and a polyethylene nonwoven fabric (trade name: Tyvek). That is, an aqueous dispersion of ethylene interpolymer (Toyo Morton Co., Ltd. mAD-37JD1)
Low molecular weight polyethylene (Chemipearl W-10 manufactured by Mitsui Petrochemical Co., Ltd.)
0 solids content 40%) and 200 parts by weight of polyethylene fine particle adhesive (Toyo Morton Co., Ltd. jJlljAD-37R)
Approximately 10 g/m2 of the easy-open adhesive obtained by adding 100 parts by weight of 345 (solid content: 40%) was applied to the entire surface of a polyethylene nonwoven fabric, and dried at a temperature below the minimum film forming temperature of approximately 100°C. An adhesive layer was formed, and a polystyrene sheet was placed on the adhesive layer and the necessary parts of the two were pressed together by heating and pressing to obtain a packaging bag.
実施例２
厚さ３．０ｍｍのポリエチレンシートと坪Ｊ４７０’ｇ
／ｍ２、透気度１００秒の紙基材とより易開封性滅菌包
装体を下記の接着剤を使用した点以外は実施例１と全く
同じ手順によって製造した。Example 2 3.0mm thick polyethylene sheet and Tsubo J470'g
/m2, and a paper base with an air permeability of 100 seconds and an easier-to-open sterile package were manufactured by the same procedure as in Example 1, except that the following adhesive was used.
接着剤
水性分散体（ＡＤ−３７ＪＤ１１９ｇ） １０
０重量部低分子量ポリエチレン
（ケミバールト１００） ２００重量部（ケミパー
ルＡ−１００） ２００重量部ポリエチレン系微粒
状接着剤
（Ａｎ−３７Ｒ３４５） １００重量部ケミ
パー／ｌ／Ａ−１００はケミパー／Ｌ／Ｗ−１００と同
様、固形分４部である。Adhesive aqueous dispersion (AD-37JD119g) 10
0 parts by weight Low molecular weight polyethylene (Chemivart 100) 200 parts by weight (Chemipard A-100) 200 parts by weight Polyethylene fine particle adhesive (An-37R345) 100 parts by weight Chemiper/L/A-100 is Chemiper/L/W- Similar to 100, the solid content is 4 parts.
（効果）
以上述べたように、本発明では合成樹脂フィルムと透気
性基材を赴滅菌用包装体において、前記のような特定の
配合から成る水性易開封性接着剤であるので取扱が容易
であり、且つ、該接着剤から成る被覆層を設けることに
よって透気性を損なうことなく易開封性を付与すること
がでる等の効果を奏するのである。(Effects) As described above, in the present invention, a synthetic resin film and an air-permeable base material are used in a sterilization package, and since the water-based easy-to-open adhesive is made of the above-mentioned specific formulation, it is easy to handle. Moreover, by providing a coating layer made of the adhesive, it is possible to impart easy-openability without impairing air permeability.
Claims (1)
気性基材を用いて、両者の必要部相互を熱接着してなる
滅菌用包装体において、透気性基材全面に易開封性接着
材１００重量部に対し、低分子量ポリエチレンを１００
〜１０００重量部、ポリエチレン系微粒状熱接着剤５０
〜５００重量部を混合した水溶性の易開封性接着剤を塗
布成層し、最低製膜温度以下の温度で接着層を形成した
ことを特徴とする易開封性滅菌用包装体。In a sterilization package that uses a synthetic resin film base material for one packaging material and an air-permeable base material for the other, the necessary parts of both are thermally bonded to each other, with easy-to-open adhesive bonded to the entire surface of the air-permeable base material. 100 parts by weight of low molecular weight polyethylene
~1000 parts by weight, polyethylene fine granule thermal adhesive 50
1. An easy-open sterilization package characterized by coating and layering a water-soluble easy-open adhesive mixed with ~500 parts by weight to form an adhesive layer at a temperature below the lowest film forming temperature.