JP7431524B2 - Water-based fluororesin coating composition - Google Patents
Water-based fluororesin coating composition Download PDFInfo
- Publication number
- JP7431524B2 JP7431524B2 JP2019138424A JP2019138424A JP7431524B2 JP 7431524 B2 JP7431524 B2 JP 7431524B2 JP 2019138424 A JP2019138424 A JP 2019138424A JP 2019138424 A JP2019138424 A JP 2019138424A JP 7431524 B2 JP7431524 B2 JP 7431524B2
- Authority
- JP
- Japan
- Prior art keywords
- fluororesin
- water
- coating composition
- resin
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、金属基材、特にステンレス(SUS)基材、と強固に接着し、耐水蒸気性・耐食性に優れた塗膜を形成できる水性フッ素樹脂塗料組成物、それを塗装してなる塗膜、その塗膜を有する物品に関する。 The present invention relates to a water-based fluororesin coating composition that can firmly adhere to metal substrates, particularly stainless steel (SUS) substrates, and form a coating film with excellent water vapor resistance and corrosion resistance, and a coating film formed using the composition. , relates to an article having the coating film.
フッ素樹脂は、優れた耐熱性、耐薬品性、電気的性質及び機械的性質を有し、また極めて低い摩擦係数、非粘着性、撥水撥油性も有しているため、化学、機械、電機などあらゆる工業分野において広く利用されている。 Fluororesins have excellent heat resistance, chemical resistance, electrical properties, and mechanical properties, as well as extremely low coefficients of friction, non-stick properties, and water and oil repellency, so they are used in chemical, mechanical, and electrical equipment. It is widely used in all industrial fields.
特に、フッ素樹脂の非粘着性、撥水撥油性を利用して、フッ素樹脂コーティングは、フライパン・炊飯器などの調理器具の塗装、OA機器のトナーを定着させる定着ロール・ベルトなど様々な分野で利用され、近年では、インクジェットノズル、化学プラントの設備など、利用分野はさらに広がっている。 In particular, by taking advantage of the non-adhesive, water and oil repellent properties of fluororesin, fluororesin coatings are used in various fields such as painting cooking utensils such as frying pans and rice cookers, and fixing rolls and belts that fix toner in OA equipment. In recent years, the field of use has expanded further, including inkjet nozzles and chemical plant equipment.
ところが、各種基材にフッ素樹脂をコーティングする場合、フッ素樹脂の特性である非粘着性のために、フッ素樹脂を直接基材に塗装することは接着不良が生じ、極めて困難である。そのため、フッ素樹脂コーティングを行なう場合には、基材に対する接着性を有し、かつその上に塗装されるフッ素樹脂コーティングとも接着性を有するプライマー塗料組成物が通常利用されてきた。 However, when coating various base materials with a fluororesin, it is extremely difficult to directly apply the fluororesin to the base material because of the non-adhesive properties of the fluororesin, as this will result in poor adhesion. Therefore, when applying a fluororesin coating, a primer coating composition that has adhesive properties to the base material and also to the fluororesin coating applied thereon has been commonly used.
このようなプライマー塗料組成物には、基材との接着性を有し、かつフッ素樹脂の融点以上の高温に耐えうる耐熱性樹脂(いわゆるエンジニアリングプラスチック)が用いられており、例えば、特許文献1には、ポリイミド、ポリアミドイミド、ポリエーテルスルホンなどのプレカーサー及びポリフェニレンサルファイドなどの微粒子が開示されている。このような耐熱性樹脂をバインダーと呼ぶ。 Such primer paint compositions use heat-resistant resins (so-called engineering plastics) that have adhesive properties with the base material and can withstand high temperatures higher than the melting point of the fluororesin; for example, Patent Document 1 discloses precursors such as polyimide, polyamideimide, polyethersulfone, and fine particles such as polyphenylene sulfide. Such heat-resistant resin is called a binder.
一方、プライマー塗料組成物を含むフッ素樹脂塗料組成物の媒体には、有機溶剤(溶剤系塗料)か水(水性塗料)が用いられており、環境負荷や人体への有害性の観点から、特に近年では水性(水系)塗料組成物が好ましく用いられている。水性塗料組成物において、基材との接着性を付与する耐熱性樹脂(バインダー)は、通常非水溶性であるため、その粒子を塗料組成物の液中に分散させて用いられるが、このとき、水溶性のポリアミドイミドを用いることもできる(特許文献2)。 On the other hand, organic solvents (solvent-based paints) or water (water-based paints) are used as the medium for fluororesin paint compositions, including primer paint compositions. In recent years, aqueous (water-based) coating compositions have been preferably used. In water-based paint compositions, the heat-resistant resin (binder) that provides adhesion to the substrate is usually water-insoluble, so its particles are dispersed in the liquid of the paint composition. , water-soluble polyamideimide can also be used (Patent Document 2).
耐熱性樹脂(バインダー)として水溶性ポリアミドイミド(水溶性PAI)を用いた場合、水性フッ素樹脂塗料組成物中に均一に溶解するため、少量でも高い接着力が得られる。このため、フッ素樹脂の含有量を多くすることができ、プライマー塗料としての使用だけでなく、プライマー無しの1層のみで効果を発現できるワンコート塗料としても利用が可能となる。 When water-soluble polyamideimide (water-soluble PAI) is used as the heat-resistant resin (binder), it is uniformly dissolved in the water-based fluororesin coating composition, so high adhesive strength can be obtained even with a small amount. Therefore, the content of fluororesin can be increased, and it can be used not only as a primer paint, but also as a one-coat paint that can exhibit effects with only one layer without a primer.
また、水溶性ポリアミドイミドは粘度が高いことから、増粘剤を低減するか不使用とすることができ、塗膜の純粋性を高め、より良好な性能を得ることができる。さらに、水溶性ポリアミドイミドを用いることで、耐熱性樹脂(バインダー)として一般的な各種エンジニアリングプラスチックの粉体を用いる場合に必要な分散工程や分散度合いの管理が不要となり、生産性に優れ、かつ品質管理もし易いという利点も有する。 Furthermore, since water-soluble polyamideimide has a high viscosity, the use of thickeners can be reduced or eliminated, increasing the purity of the coating film and providing better performance. Furthermore, by using water-soluble polyamide-imide, the dispersion process and control of the degree of dispersion that are required when using powders of general engineering plastics as heat-resistant resins (binder) are not required, resulting in excellent productivity and It also has the advantage of easy quality control.
したがって、水性塗料組成物において、基材との接着性を付与する耐熱性樹脂(バイン
ダー)として水溶性ポリアミドイミドを用いることが望まれている。
しかし、従来の水溶性ポリアミドイミドを用いたフッ素樹脂組成物から得られる塗膜では、耐水蒸気性と耐食性が不十分であったため、これらの特性が求められるフライパン・炊飯器などの調理器具の用途に適用することが困難であった。
Therefore, in water-based coating compositions, it is desired to use water-soluble polyamide-imide as a heat-resistant resin (binder) that provides adhesiveness to the substrate.
However, coating films obtained from conventional fluororesin compositions using water-soluble polyamide-imide have insufficient water vapor resistance and corrosion resistance, so they are used for cooking utensils such as frying pans and rice cookers that require these properties. was difficult to apply.
また、フライパン・炊飯器などの調理器具の素材としてはアルミニウムが主に用いられてきたが、IH調理器/IHクッキングヒーターに使用でき、コスト面でも有利であり、しかも高級感がある、ステンレス(SUS)を素材として用いたいという需要がある。
しかし、ステンレス(SUS)は、アルミニウムに比べて塗料組成物の接着性が劣るという問題があるため、ステンレス(SUS)に対して接着性の高い塗料組成物が望まれている。
In addition, aluminum has been mainly used as a material for cooking utensils such as frying pans and rice cookers, but stainless steel (SUS ) is in demand as a material.
However, since stainless steel (SUS) has a problem in that the adhesion of paint compositions to stainless steel (SUS) is inferior to that of aluminum, a paint composition that has high adhesion to stainless steel (SUS) is desired.
これまで、耐水蒸気性と耐食性に優れた水性塗料組成物としては、水溶性ポリアミドイミドと共にポリエーテルスルホン樹脂を用いたフッ素樹脂塗料組成物が提案されている(特許文献3)。 Until now, as a water-based coating composition with excellent water vapor resistance and corrosion resistance, a fluororesin coating composition using a polyether sulfone resin together with a water-soluble polyamide-imide has been proposed (Patent Document 3).
また、特許文献4では、3,3’-ジメチルビフェニル-4,4’-ジイソシアネート及び/又は3,3’-ジメチルビフェニル-4,4’-ジアミンを構造単位として含む水溶性ポリアミドイミドを用いることにより、形成される塗膜の耐水蒸気性等を改善したフッ素樹脂塗料組成物が提案されている。しかし、このフッ素樹脂塗料組成物においても、調理器具への適用に十分な耐水蒸気性・耐食性は得られていない。 Further, Patent Document 4 discloses that water-soluble polyamideimide containing 3,3'-dimethylbiphenyl-4,4'-diisocyanate and/or 3,3'-dimethylbiphenyl-4,4'-diamine as a structural unit is used. Accordingly, a fluororesin coating composition has been proposed in which the water vapor resistance of the formed coating film is improved. However, even this fluororesin coating composition does not have sufficient water vapor resistance and corrosion resistance for application to cooking utensils.
そして、従来、水溶性ポリアミドイミド樹脂の溶解・希釈・合成溶媒としてN-メチル-2-ピロリドン(NMP)が多く用いられているが、近年では、NMPの毒性(特に生殖毒性)が問題視されており、NMPの代わりに低毒性のN-ホルミルモルフォリンを溶媒として使用する水溶性ポリアミドイミド樹脂を含むフッ素樹脂塗料組成物も提案されている(特許文献5)。しかし、このフッ素樹脂塗料組成物も、調理器具への適用のための耐水蒸気性や耐食性の問題を解決するものでは無く、特にステンレス(SUS)基材に対する接着性は不十分であった。 Conventionally, N-methyl-2-pyrrolidone (NMP) has been widely used as a solvent for dissolving, diluting, and synthesizing water-soluble polyamide-imide resins, but in recent years, the toxicity (particularly reproductive toxicity) of NMP has become a problem. A fluororesin coating composition containing a water-soluble polyamideimide resin using low toxicity N-formylmorpholine as a solvent instead of NMP has also been proposed (Patent Document 5). However, this fluororesin coating composition also did not solve the problems of water vapor resistance and corrosion resistance when applied to cooking utensils, and in particular, its adhesion to stainless steel (SUS) substrates was insufficient.
本発明の目的は、金属基材、特にステンレス(SUS)基材と強固に接着し、フライパン・炊飯器などの調理器具にも好適に用いられる優れた耐水蒸気性と耐食性を兼ね備え、更に、環境・安全衛生面にも優れた、水性フッ素樹脂塗料組成物を提供することである。 The purpose of the present invention is to firmly adhere to metal substrates, particularly stainless steel (SUS) substrates, to have excellent water vapor resistance and corrosion resistance that can be suitably used in cooking utensils such as frying pans and rice cookers, and to be environmentally friendly. - To provide a water-based fluororesin coating composition that is also excellent in terms of safety and hygiene.
上記目的を達成するため、本発明の水性フッ素樹脂塗料組成物は、水溶性ポリアミドイミド樹脂、ポリエーテルイミド、ポリエーテルスルホン、及びフッ素樹脂を含むことを特徴とする。 In order to achieve the above object, the aqueous fluororesin coating composition of the present invention is characterized by containing a water-soluble polyamideimide resin, polyetherimide, polyethersulfone, and a fluororesin.
すなわち、本発明は以下のとおりのものである。
(1)水溶性ポリアミドイミド樹脂、ポリエーテルイミド、ポリエーテルスルホン、及びフッ素樹脂を含み、フッ素樹脂が非熱溶融性ポリテトラフルオロエチレンと熱溶融性フッ素樹脂を含むことを特徴とする水性フッ素樹脂塗料組成物。
(2)フッ素樹脂が、水溶性ポリアミドイミド樹脂、ポリエーテルイミド、ポリエーテルスルホン、及びフッ素樹脂の合計に対して35~90質量%である、(1)に記載の水性フッ素樹脂塗料組成物。
(3)熱溶融性フッ素樹脂がパーフルオロ樹脂である、(1)又は(2)に記載の水性フッ素樹脂塗料組成物。
(4)(1)~(3)のいずれかに記載の水性フッ素樹脂塗料組成物を、金属の基材に塗装してなる塗膜。
(5)金属がステンレスである、(4)に記載の塗膜。
(6)(4)又は(5)に記載の塗膜を有する塗装物品。
(7)調理器具である、(6)に記載の塗装物品。
That is, the present invention is as follows.
(1) A water-based fluororesin containing a water-soluble polyamide-imide resin, polyetherimide, polyether sulfone, and a fluororesin, wherein the fluororesin includes a non-heat-melting polytetrafluoroethylene and a heat-melting fluororesin. Paint composition.
(2) The aqueous fluororesin coating composition according to (1), wherein the fluororesin is 35 to 90% by mass based on the total of the water-soluble polyamideimide resin, polyetherimide, polyether sulfone, and fluororesin.
(3) The aqueous fluororesin coating composition according to (1) or (2), wherein the heat-melting fluororesin is a perfluororesin.
(4) A coating film obtained by coating a metal base material with the water-based fluororesin coating composition according to any one of (1) to (3).
(5) The coating film according to (4), wherein the metal is stainless steel.
(6) A coated article having the coating film described in (4) or (5).
(7) The coated article according to (6), which is a cooking utensil.
本発明によれば、金属基材、特にステンレス(SUS)基材、との十分な接着性と、調理器具にも好適に用いられる優れた耐水蒸気性と耐食性を兼ね備えた水性フッ素樹脂塗料組成物を提供することができる。また、本発明によれば、媒体として水を用い、環境・安全衛生面にも優れた水性フッ素樹脂塗料組成物を提供することができる。
さらに、本発明によれば、フッ素樹脂を多く含む塗膜を提供でき、フッ素樹脂コーティングの性能を向上させることができる。
According to the present invention, a water-based fluororesin coating composition has sufficient adhesion to metal substrates, particularly stainless steel (SUS) substrates, and excellent water vapor resistance and corrosion resistance suitable for use in cooking utensils. can be provided. Further, according to the present invention, it is possible to provide an aqueous fluororesin coating composition that uses water as a medium and is excellent in terms of environment, safety and hygiene.
Furthermore, according to the present invention, a coating film containing a large amount of fluororesin can be provided, and the performance of the fluororesin coating can be improved.
以下、本発明について詳細に説明する。
1.水性フッ素樹脂塗料組成物
本発明の「水性フッ素樹脂塗料組成物」は、水溶性ポリアミドイミド樹脂、ポリエーテルイミド、ポリエーテルスルホン及びフッ素樹脂を含み、フッ素樹脂として、非熱溶融性ポリテトラフルオロエチレンと熱溶融性フッ素樹脂を含む。
The present invention will be explained in detail below.
1. Water-based fluororesin coating composition The "aqueous fluororesin coating composition" of the present invention contains a water-soluble polyamideimide resin, polyetherimide, polyether sulfone, and a fluororesin, and the fluororesin is non-thermofusible polytetrafluoroethylene. and heat-melting fluororesin.
<水性フッ素樹脂塗料組成物>
本発明の「水性フッ素樹脂塗料組成物」とは、水溶性ポリアミドイミド樹脂、ポリエーテルイミド、ポリエーテルスルホン及びフッ素樹脂を含み、フッ素樹脂としては、非熱溶融性ポリテトラフルオロエチレンと熱溶融性フッ素樹脂を含むことを特徴とする水性(水系)分散体である。本発明の水性フッ素樹脂塗料組成物は、通常、基材にフッ素樹脂層を接着させるためのプライマー塗料(下塗り)として好適に用いられるが、プライマー塗料を用いないワンコート塗料としても利用が可能である。
<Aqueous fluororesin coating composition>
The "aqueous fluororesin coating composition" of the present invention includes water-soluble polyamideimide resin, polyetherimide, polyether sulfone, and fluororesin, and the fluororesin includes non-thermofusible polytetrafluoroethylene and thermofusible polytetrafluoroethylene. It is an aqueous (aqueous) dispersion characterized by containing a fluororesin. The water-based fluororesin coating composition of the present invention is normally suitably used as a primer coating (undercoat) for adhering a fluororesin layer to a base material, but it can also be used as a one-coat coating without using a primer coating. be.
<水溶性ポリアミドイミド樹脂(PAI)>
本発明に用いられる「水溶性ポリアミドイミド樹脂(水溶性PAI)」とは、アミド結合とイミド結合とを主鎖に持つ水溶性樹脂であり、好ましくは下記一般式:
The "water-soluble polyamide-imide resin (water-soluble PAI)" used in the present invention is a water-soluble resin having an amide bond and an imide bond in the main chain, and preferably has the following general formula:
本発明で用いられる水溶性PAIは、極性溶媒中で、アミン成分としてジイソシアネート化合物又はジアミン化合物と、酸成分として三塩基酸無水物又は三塩基酸ハライドとを共重合させることで得られる。水溶性PAIの合成条件は多様であり、特に限定されないが、通常、80~180℃の温度で行われ、空気中の水分の影響を低減するため、窒素等の雰囲気下で行うことが好ましい。 The water-soluble PAI used in the present invention is obtained by copolymerizing a diisocyanate compound or diamine compound as an amine component and a tribasic acid anhydride or tribasic acid halide as an acid component in a polar solvent. Synthesis conditions for water-soluble PAI vary and are not particularly limited, but it is usually carried out at a temperature of 80 to 180°C, and preferably carried out under an atmosphere of nitrogen or the like to reduce the influence of moisture in the air.
ジイソシアネート化合物としては、特に限定されないが、例えば、下記式(1)で表されるジイソシアネート化合物が挙げられる。式(1)中、Xは2価の有機基を示す。 The diisocyanate compound is not particularly limited, but includes, for example, a diisocyanate compound represented by the following formula (1). In formula (1), X represents a divalent organic group.
Xで示される2価の有機基としては、例えば、炭素数1~20のアルキレン基;未置換、メチル基等の炭素数1~5の低級アルキル基、又はメトキシ基等の炭素数1~5の低級アルコキシ基で置換されているフェニレン基、ナフチレン基等のアリーレン基;単結合、炭素数1~5の低級アルキレン基、オキシ基(-O-)、カルボニル基(-CO-)、又はスルホニル基(-SO2-)を介して上記アリーレン基が2つ結合してなる2価の有機基;上記アリーレン基を介して炭素数1~5の低級アルキレン基が2つ結合してなる2価の有機基などが挙げられる。アルキレン基の炭素数は、より好ましくは1~18であり、より好ましくは1~12であり、更に好ましくは1~6であり、特に好ましくは1~4である。 Examples of the divalent organic group represented by An arylene group such as a phenylene group or naphthylene group substituted with a lower alkoxy group; a single bond, a lower alkylene group having 1 to 5 carbon atoms, an oxy group (-O-), a carbonyl group (-CO-), or a sulfonyl group A divalent organic group formed by bonding two of the above arylene groups via a group (-SO 2 -); A divalent organic group formed by bonding two lower alkylene groups having 1 to 5 carbon atoms via the above arylene group Examples include organic groups such as The alkylene group preferably has 1 to 18 carbon atoms, more preferably 1 to 12 carbon atoms, still more preferably 1 to 6 carbon atoms, and particularly preferably 1 to 4 carbon atoms.
Xで示される2価の有機基は、反応性、塗膜の接着強度向上等の観点から、好ましくは、単結合、炭素数1~5の低級アルキレン基、オキシ基(-O-)、カルボニル基(-CO-)、又はスルホニル基(-SO2-)を介して上記アリーレン基が2つ結合してなる2価の有機基であり、より好ましくは単結合又は炭素数1~5の低級アルキレン基を介して上記アリーレン基が2つ結合してなる2価の有機基であり、更に好ましくは単結合又は炭素数1~5の低級アルキレン基を介してフェニレン基が2つ結合してなる2価の有機基である。ジイソシアネート化合物を2種以上組み合わせて用いる場合も、これらの好ましい態様の中から2種以上を選択して使用することが好ましい。また、アリーレン基は、反応性の観点からは、未置換であることが好ましく、塗膜の接着強度向上の観点からは、メ
チル基等の炭素数1~5の低級アルキル基、又はメトキシ基等の炭素数1~5の低級アルコキシ基で置換されていることが好ましい。
The divalent organic group represented by X is preferably a single bond, a lower alkylene group having 1 to 5 carbon atoms, an oxy group (-O-), a carbonyl group, etc. A divalent organic group formed by bonding two of the above arylene groups via a group (-CO-) or a sulfonyl group (-SO 2 -), more preferably a single bond or a lower group having 1 to 5 carbon atoms. A divalent organic group formed by bonding two of the above arylene groups via an alkylene group, more preferably two phenylene groups bonded via a single bond or a lower alkylene group having 1 to 5 carbon atoms. It is a divalent organic group. Even when using a combination of two or more types of diisocyanate compounds, it is preferable to select and use two or more types from these preferred embodiments. In addition, the arylene group is preferably unsubstituted from the viewpoint of reactivity, and from the viewpoint of improving the adhesive strength of the coating film, it is preferable to use a lower alkyl group having 1 to 5 carbon atoms such as a methyl group, or a methoxy group. is preferably substituted with a lower alkoxy group having 1 to 5 carbon atoms.
ジイソシアネート化合物として、具体的には、キシリレンジイソシアネート、パラフェニレンジイソシアネート、トリレンジイソシアネート、ナフタレンジイソシアネート、3,3'-ジフェニルメタンジイソシアネート、4,4'-ジフェニルメタンジイソシアネート、3,3'-ジメチルビフェニル-4,4'-ジイソシアネート、3,3'-ジメトキシビフェニル-4,4'-ジイソシアネート、ヘキサメチレンジイソシアネート、イソホロンジイソシアレート等が挙げられる。 Specific examples of the diisocyanate compound include xylylene diisocyanate, paraphenylene diisocyanate, tolylene diisocyanate, naphthalene diisocyanate, 3,3'-diphenylmethane diisocyanate, 4,4'-diphenylmethane diisocyanate, 3,3'-dimethylbiphenyl-4, Examples include 4'-diisocyanate, 3,3'-dimethoxybiphenyl-4,4'-diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate and the like.
ジアミン化合物としては、特に限定されないが、上記式(1)において、イソシアネート基をアミノ基に置き換えた化合物が挙げられる。ジアミン化合物として、具体的には、キシリレンジアミン、フェニレンジアミン、4,4'-ジアミノジフェニルメタン、4,4'-ジアミノジフェニルエーテル、4,4'-ジアミノジフェニルスルホン、3,3'-ジアミノジフェニルスルホン、3,3'-ジメチルビフェニル-4,4'-ジアミン、イソホロンジアミン等が挙げられる。 Examples of the diamine compound include, but are not particularly limited to, compounds obtained by replacing the isocyanate group with an amino group in the above formula (1). Specific examples of the diamine compound include xylylene diamine, phenylene diamine, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenylsulfone, 3,3'-diaminodiphenylsulfone, Examples include 3,3'-dimethylbiphenyl-4,4'-diamine and isophorone diamine.
アミン成分(ジイソシアネート化合物、ジアミン化合物)として、3,3'-ジメチルビフェニル-4,4'-ジイソシアネート及び/又は3,3'-ジメチルビフェニル-4,4'-ジアミンを用いることが、塗膜の基材接着強度と耐水蒸気性を向上させることができるため、好ましい。更に、作業環境を向上させる観点から、3,3'-ジメチルビフェニル-4,4'-ジイソシアネートを用いることが好ましい(特許文献4)。 The use of 3,3'-dimethylbiphenyl-4,4'-diisocyanate and/or 3,3'-dimethylbiphenyl-4,4'-diamine as the amine component (diisocyanate compound, diamine compound) improves the coating film. This is preferable because it can improve the base material adhesive strength and water vapor resistance. Furthermore, from the viewpoint of improving the working environment, it is preferable to use 3,3'-dimethylbiphenyl-4,4'-diisocyanate (Patent Document 4).
反応には、ジイソシアネート化合物を単独で用いても、ジアミン化合物を単独で用いても、ジイソシアネート化合物とジアミン化合物を併用してもよい。反応を容易に行う観点から、ジイソシアネート化合物が好ましく使用される。 In the reaction, a diisocyanate compound may be used alone, a diamine compound may be used alone, or a diisocyanate compound and a diamine compound may be used in combination. From the viewpoint of facilitating the reaction, diisocyanate compounds are preferably used.
三塩基酸無水物としては、トリカルボン酸無水物が挙げられる。特に限定されないが、好ましくは芳香族三塩基酸無水物であり、より好ましくは芳香族トリカルボン酸無水物であり、更に好ましくは下記式(2)又は式(3)で表される化合物である。耐熱性、コスト等の観点からトリメリット酸無水物が特に好ましい。 Tricarboxylic acid anhydrides include tricarboxylic acid anhydrides. Although not particularly limited, it is preferably an aromatic tribasic acid anhydride, more preferably an aromatic tricarboxylic acid anhydride, and even more preferably a compound represented by the following formula (2) or formula (3). Trimellitic anhydride is particularly preferred from the viewpoints of heat resistance, cost, etc.
三塩基酸ハライドとしては、三塩基酸無水物ハライドが好ましく使用され、例えば、トリカルボン酸無水物ハライドが挙げられる。三塩基酸無水物ハライドは、三塩基酸無水物クロライドであることが好ましい。特に限定されないが、好ましくは芳香族三塩基酸無水物クロライドであり、より好ましくは芳香族トリカルボン酸無水物クロライドであり、更に好ましくは上記式(2)又は(3)において-COOR基を-COCl基に置き換えた化合物である。耐熱性、コスト等の観点から、トリメリット酸無水物クロライド(無水トリメリット酸クロライド)が特に好ましい。 As the tribasic acid halide, tribasic acid anhydride halides are preferably used, such as tricarboxylic acid anhydride halides. The tribasic acid anhydride halide is preferably a tribasic acid anhydride chloride. Although not particularly limited, aromatic tribasic acid anhydride chloride is preferred, aromatic tricarboxylic acid anhydride chloride is more preferred, and -COOR group in the above formula (2) or (3) is replaced with -COCl. This is a compound in which a group is replaced with a group. From the viewpoint of heat resistance, cost, etc., trimellitic anhydride chloride (trimellitic anhydride chloride) is particularly preferred.
環境への負荷を軽減させる観点から、トリカルボン酸無水物が好ましく使用され、トリメリット酸無水物が特に好ましい。 From the viewpoint of reducing the burden on the environment, tricarboxylic anhydride is preferably used, and trimellitic anhydride is particularly preferred.
酸成分としては、三塩基酸無水物及び三塩基酸ハライドの他に、親水性を向上させるために、ジカルボン酸、テトラカルボン酸二無水物等の多塩基酸又は多塩基酸無水物を、PAIの耐熱性等の特性を損なわない範囲で用いることができる。 In addition to tribasic acid anhydrides and tribasic acid halides, the acid components include polybasic acids or polybasic acid anhydrides such as dicarboxylic acids and tetracarboxylic dianhydrides in order to improve hydrophilicity. It can be used within a range that does not impair its properties such as heat resistance.
ジカルボン酸としては、特に限定されないが、テレフタル酸、イソフタル酸、アジピン酸、セバシン酸等が挙げられる。テトラカルボン酸二無水物としては、特に限定されないが、ピロメリット酸二無水物、ベンゾフェノンテトラカルボン酸二無水物、ビフェニルテトラカルボン酸二無水物等が挙げられる。多塩基酸及び多塩基酸無水物は、それぞれ1種のみ使用しても、2種以上を組み合わせて使用してもよい。 Examples of dicarboxylic acids include, but are not limited to, terephthalic acid, isophthalic acid, adipic acid, sebacic acid, and the like. Examples of the tetracarboxylic dianhydride include, but are not particularly limited to, pyromellitic dianhydride, benzophenone tetracarboxylic dianhydride, biphenyltetracarboxylic dianhydride, and the like. Each of the polybasic acids and polybasic acid anhydrides may be used alone or in combination of two or more.
三塩基酸無水物及び三塩基酸ハライド以外の多塩基酸及び多塩基酸無水物(例えば、ジカルボン酸、テトラカルボン酸二無水物)の使用量は、PAIの耐熱性等の特性を保つ観点から、全酸成分中に0~50モル%が好ましく、0~30モル%がより好ましく、0~15モル%が更に好ましい。 The amount of polybasic acids and polybasic acid anhydrides (e.g., dicarboxylic acids, tetracarboxylic dianhydrides) other than tribasic acid anhydrides and tribasic acid halides should be determined from the viewpoint of maintaining properties such as heat resistance of PAI. , preferably from 0 to 50 mol%, more preferably from 0 to 30 mol%, even more preferably from 0 to 15 mol%, based on the total acid components.
ジイソシアネート化合物及び/又はジアミン化合物と、酸成分(三塩基酸無水物及び/又は三塩基酸ハライド、並びに、必要に応じて用いられるジカルボン酸及び/又はテトラカルボン酸二無水物等)の使用比率は、生成させるPAIの分子量及び架橋度の観点から、酸成分の総量1.0モルに対してジイソシアネート化合物及び/又はジアミン化合物の総量が0.8~1.1モルであることが好ましく、0.95~1.08モルであることがより好ましく、1.0~1.08モルであることが更に好ましい。 The usage ratio of the diisocyanate compound and/or diamine compound and the acid component (tribasic acid anhydride and/or tribasic acid halide, dicarboxylic acid and/or tetracarboxylic dianhydride used as necessary, etc.) is From the viewpoint of the molecular weight and degree of crosslinking of the PAI to be produced, it is preferable that the total amount of the diisocyanate compound and/or diamine compound is 0.8 to 1.1 mol, and 0.8 to 1.1 mol, per 1.0 mol of the total amount of acid components. The amount is more preferably 95 to 1.08 mol, and even more preferably 1.0 to 1.08 mol.
PAIとして、ジイソシアネート化合物及び/又はジアミン化合物と、酸成分とを反応させて得られるPAIをそのまま使用することができる。また、ブロック剤で保護した後に使用することも可能である。 As the PAI, a PAI obtained by reacting a diisocyanate compound and/or a diamine compound with an acid component can be used as is. It is also possible to use it after protecting it with a blocking agent.
原料化合物としてジイソシアネート化合物を使用する場合、PAIを安定化させる目的で、末端イソシアネート基のブロック剤(末端ブロック剤)を任意で使用してもよい。ブロック剤で保護することにより、PAIは、イソシアネート基(-NCO基)を有しないか、又は、イソシアネート化合物と酸成分とを反応させて得られるPAIと比べ、イソシアネート基(-NCO基)の量が低減されたものとなる。 When a diisocyanate compound is used as a raw material compound, a terminal isocyanate group blocking agent (end blocking agent) may be optionally used for the purpose of stabilizing PAI. By protecting PAI with a blocking agent, PAI has no isocyanate groups (-NCO groups) or has a larger amount of isocyanate groups (-NCO groups) than PAI obtained by reacting an isocyanate compound with an acid component. is reduced.
ブロック剤としてアルコールが挙げられ、アルコールとしては、メタノール、エタノール、プロパノール等の炭素数1~6の低級アルコールが挙げられる。また、ブロック剤として、2-ブタノンオキシム、δ-バレロラクタム、ε-カプロラクタム等が挙げられる。ブロック剤は、これらの例示化合物に限定されることはない。ブロック剤を、1種を単独で、又は、2種以上を組み合わせて使用してもよい。 Examples of the blocking agent include alcohol, and examples of the alcohol include lower alcohols having 1 to 6 carbon atoms such as methanol, ethanol, and propanol. Further, examples of blocking agents include 2-butanone oxime, δ-valerolactam, and ε-caprolactam. Blocking agents are not limited to these exemplified compounds. One type of blocking agent may be used alone or two or more types may be used in combination.
重合に使用される極性溶媒としては、N-メチル-2-ピロリドン(NMP)、N-エチルモルフォリン、N-ホルミルモルフォリン、N-アセチルモルフォリン、N,N′-ジメチルエチレンウレア、N,N-ジメチルアセトアミド又はN,N-ジメチルホルムアミド、及びγ―ブチロラクトン等を用いることができる。入手容易であり、高沸点であることから、これまでNMPが好ましく用いられてきたが、人体への影響や、REACH規制や米国FDAなどの法規制の観点から、N-エチルモルフォリン、N-ホルミルモルフォリンを用いることが好ましい。 Polar solvents used in the polymerization include N-methyl-2-pyrrolidone (NMP), N-ethylmorpholine, N-formylmorpholine, N-acetylmorpholine, N,N'-dimethylethyleneurea, N, N-dimethylacetamide or N,N-dimethylformamide, γ-butyrolactone, etc. can be used. Up until now, NMP has been preferred because it is easily available and has a high boiling point, but N-ethylmorpholine, N-ethylmorpholine, N- Preferably, formylmorpholine is used.
溶媒の使用量に特に制限はないが、アミン成分と酸成分の総量100質量部に対して50~500質量部とすることが、得られる樹脂の溶解性の観点から好ましい。 There is no particular restriction on the amount of the solvent used, but it is preferably from 50 to 500 parts by weight based on 100 parts by weight of the total amount of the amine component and acid component from the viewpoint of solubility of the resulting resin.
PAIの数平均分子量は、塗膜の強度を確保する観点から、5,000以上が好ましく、10,000以上がより好ましく、13,000以上が更に好ましく、15,000以上が特に好ましい。また、数平均分子量は、水への溶解性を確保する観点から、50,000以下が好ましく、30,000以下がより好ましく、25,000以下が更に好ましく、20,000以下が特に好ましい。 From the viewpoint of ensuring the strength of the coating film, the number average molecular weight of PAI is preferably 5,000 or more, more preferably 10,000 or more, even more preferably 13,000 or more, and particularly preferably 15,000 or more. Moreover, from the viewpoint of ensuring solubility in water, the number average molecular weight is preferably 50,000 or less, more preferably 30,000 or less, even more preferably 25,000 or less, and particularly preferably 20,000 or less.
PAIの数平均分子量は、合成時にPAIをサンプリングして、数平均分子量を測定し、目的とする数平均分子量が得られるまで合成を継続することによって管理できる。数平均分子量は、ゲルパーミエーションクロマトグラフ(GPC)により、標準ポリスチレンの検量線を用いて測定することができる。 The number average molecular weight of PAI can be controlled by sampling PAI during synthesis, measuring the number average molecular weight, and continuing the synthesis until the desired number average molecular weight is obtained. The number average molecular weight can be measured by gel permeation chromatography (GPC) using a standard polystyrene calibration curve.
PAIは、樹脂中のカルボキシル基と酸無水物基を開環させたカルボキシル基とを合わせた酸価が、10mgKOH/g以上であることが好ましい。より好ましくは25mgKOH/g以上、更に好ましくは35mgKOH/g以上である。これらの範囲は、PAIの溶解又は分散を容易にする観点から、好ましい範囲である。また、後述する塩基性化合物を含有する場合に、塩基性化合物と反応するカルボキシル基の量が十分となり、水溶化が容易になることからも好ましい範囲である。 The PAI preferably has an acid value of 10 mgKOH/g or more, which is the sum of the carboxyl group in the resin and the carboxyl group formed by opening the acid anhydride group. More preferably, it is 25 mgKOH/g or more, and still more preferably 35 mgKOH/g or more. These ranges are preferred from the viewpoint of facilitating dissolution or dispersion of PAI. Furthermore, when the basic compound described below is contained, the amount of carboxyl groups that react with the basic compound is sufficient, and water solubilization becomes easy, which is also a preferable range.
また、酸価は、最終的に得られるフッ素樹脂塗料組成物について、経日によりゲル化を防止する観点から、80mgKOH/g以下が好ましい。より好ましくは60mgKOH/g以下、更には50mgKOH/g以下である。 Further, the acid value is preferably 80 mgKOH/g or less from the viewpoint of preventing gelation of the finally obtained fluororesin coating composition over time. More preferably it is 60 mgKOH/g or less, further preferably 50 mgKOH/g or less.
酸価は、以下の方法で得ることができる。まず、PAIを0.5g採取し、これに1,4-ジアザビシクロ[2,2,2]オクタンを0.15g加え、更にN-メチル-2-ピロリドン60gとイオン交換水1mLを加え、PAIが完全に溶解するまで撹拌し、評価用溶液を調製する。評価用溶液を用いて、電位差滴定法により、0.05mol/Lの水酸化カリウムエタノール溶液で滴定し、酸価を得る。酸価は、樹脂中のカルボキシル基と酸無水物基を開環させたカルボキシル基とを合わせた酸価である。 Acid value can be obtained by the following method. First, 0.5 g of PAI was collected, 0.15 g of 1,4-diazabicyclo[2,2,2]octane was added to it, and 60 g of N-methyl-2-pyrrolidone and 1 mL of ion-exchanged water were added. Stir until completely dissolved to prepare a solution for evaluation. The evaluation solution is titrated with a 0.05 mol/L potassium hydroxide ethanol solution by potentiometric titration to obtain the acid value. The acid value is the sum of the carboxyl groups in the resin and the carboxyl groups formed by opening the acid anhydride group.
さらに、PAIの水への溶解性を高めるために、塩基性化合物を作用させてもよい。塩基性化合物は、PAIに含まれるカルボキシル基と反応し、塩基性化合物とPAIとによる塩が形成される。塩基性化合物の作用により、PAIの水への溶解性を高めることができる。 Furthermore, a basic compound may be used to increase the solubility of PAI in water. The basic compound reacts with the carboxyl group contained in PAI to form a salt between the basic compound and PAI. The solubility of PAI in water can be increased by the action of the basic compound.
本発明において、塩基性化合物としては、トリエチルアミン、トリブチルアミン、N,N-ジメチルシクロヘキシルアミン、N,N-ジメチルベンジルアミン、トリエチレンジアミン、N-メチルモルホリン、N,N,N',N'-テトラメチルエチレンジアミン、N,N,N',N",N"-ペンタメチルジエチレントリアミン、N,N',N'-トリメチルアミノエチルピペラジン、ジエチルアミン、ジイソプロピルアミン、ジブチルアミン、エ
チルアミン、イソプロピルアミン、ブチルアミン等のアルキルアミン類;モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、ジプロパノールアミン、トリプロパノールアミン、N-エチルエタノールアミン、N,N-ジメチルエタノールアミン、N,N-ジエチルエタノールアミン、シクロヘキサノールアミン、N-メチルシクロヘキサノールアミン、N-ベンジルエタノールアミン等のアルカノールアミン類;水酸化ナトリウム、水酸化カリウム等の苛性アルカリ;又はアンモニア等が挙げられる。PAIの水への溶解性を高める観点から、アルキルアミン類及び/又はアルカノールアミン類が適している。
In the present invention, basic compounds include triethylamine, tributylamine, N,N-dimethylcyclohexylamine, N,N-dimethylbenzylamine, triethylenediamine, N-methylmorpholine, N,N,N',N'-tetra Alkyl such as methylethylenediamine, N,N,N',N'',N''-pentamethyldiethylenetriamine, N,N',N'-trimethylaminoethylpiperazine, diethylamine, diisopropylamine, dibutylamine, ethylamine, isopropylamine, butylamine, etc. Amines; monoethanolamine, diethanolamine, triethanolamine, dipropanolamine, tripropanolamine, N-ethylethanolamine, N,N-dimethylethanolamine, N,N-diethylethanolamine, cyclohexanolamine, N-methyl Examples include alkanolamines such as cyclohexanolamine and N-benzylethanolamine; caustic alkalis such as sodium hydroxide and potassium hydroxide; or ammonia. From the viewpoint of increasing the solubility of PAI in water, alkylamines and/or alkanolamines are suitable.
塩基性化合物は、PAIの水溶化を容易とし、かつ、塗膜の強度を向上させる観点から、樹脂中に含まれるカルボキシル基及び開環させた酸無水物基に対して、2.5当量以上となる量で使用されることが好ましく、より好ましくは3.5当量以上、更に好ましくは4当量以上である。また、塩基性化合物の含有量は、強度を維持する観点から、10当量以下となる量で使用されることが好ましく、より好ましくは8当量以下、更に好ましくは6当量以下である。 The basic compound should be used in an amount of 2.5 equivalents or more based on the carboxyl group and ring-opened acid anhydride group contained in the resin, from the viewpoint of facilitating water solubilization of PAI and improving the strength of the coating film. It is preferably used in an amount such that the amount is more preferably 3.5 equivalents or more, still more preferably 4 equivalents or more. Further, from the viewpoint of maintaining strength, the content of the basic compound is preferably used in an amount of 10 equivalents or less, more preferably 8 equivalents or less, still more preferably 6 equivalents or less.
具体的な水溶性PAI及びその製造法は、特許文献3、特許文献4、特許文献5、特開2016-17084号、特開2018-2802などに記載されている。 Specific water-soluble PAI and its manufacturing method are described in Patent Document 3, Patent Document 4, Patent Document 5, JP 2016-17084, JP 2018-2802, and the like.
本発明に用いられる水溶性PAIは、通常、溶液として、フッ素樹脂塗料組成物の調製に用いられる。水溶性PAI溶液は、有機溶剤を含む水に水溶性PAIを溶解することにより容易に得ることができる。 The water-soluble PAI used in the present invention is usually used in the form of a solution to prepare a fluororesin coating composition. A water-soluble PAI solution can be easily obtained by dissolving water-soluble PAI in water containing an organic solvent.
上記有機溶剤としては、極性が高く高沸点を有するものであれば特に限定されず、PAIの重合に用いることのできる各種の極性溶媒が利用可能である。重合に用いる溶媒と同様に、入手容易であり、高沸点であることから、これまでNMPが好ましく用いられてきたが、人体への影響や、REACH規制や米国FDAなどの法規制の観点から、N-エチルモルフォリン、N-ホルミルモルフォリンを用いることが好ましい。
上記有機溶剤は、本発明のフッ素樹脂塗料組成物における後述の水性媒体に含有され得る溶剤と同じものであってもよい。
The organic solvent is not particularly limited as long as it is highly polar and has a high boiling point, and various polar solvents that can be used in the polymerization of PAI can be used. Like the solvent used in polymerization, NMP has been preferred because it is easy to obtain and has a high boiling point, but from the viewpoint of the impact on the human body and regulations such as REACH regulations and the US FDA, It is preferable to use N-ethylmorpholine and N-formylmorpholine.
The organic solvent may be the same as the solvent that can be contained in the aqueous medium described below in the fluororesin coating composition of the present invention.
水溶性PAIは、粘度の点で、水溶性PAI溶液の1~50質量%の濃度であることが好ましく、より好ましくは5~40質量%である。 In terms of viscosity, the water-soluble PAI preferably has a concentration of 1 to 50% by weight, more preferably 5 to 40% by weight of the water-soluble PAI solution.
このような水溶性PAI溶液の市販品としては、日立化成工業(株)製HPC-1000-28、HPC-2100D-28が挙げられ、好ましくはHPC-2100D-28である。 Commercially available water-soluble PAI solutions include HPC-1000-28 and HPC-2100D-28 manufactured by Hitachi Chemical Co., Ltd., with HPC-2100D-28 being preferred.
<ポリエーテルイミド(PEI)>
本発明に用いられる「ポリエーテルイミド(PEI)」は、主鎖中に、イミド結合とエーテル結合を有する非晶性ポリマーであれば特に限定されないが、2,2-ビス[4-(3,4-ジカルボキシフェノキシ)フェニル]プロパンとm-フェニレンジアミンとの縮重合が好ましい。
本発明に用いられるPEIの市販品としては、SABIC社製 Ultem 1000F3SP-1000が挙げられる。
<Polyetherimide (PEI)>
The "polyetherimide (PEI)" used in the present invention is not particularly limited as long as it is an amorphous polymer having an imide bond and an ether bond in the main chain, but 2,2-bis[4-(3, Polycondensation of 4-dicarboxyphenoxy)phenyl]propane and m-phenylenediamine is preferred.
A commercially available PEI used in the present invention includes Ultem 1000F3SP-1000 manufactured by SABIC.
PEIは、本発明の水性フッ素樹脂塗料組成物において、後述の水性媒体に粒子として分散したもの、又は、水性媒体に溶解したものである。水性媒体に粒子として分散している場合、粒子は、平均粒子径が0.1~20μmである粒子であることが好ましい。PEIの平均粒子径が上記範囲内であると、本発明の水性フッ素樹脂塗料組成物から得られる
塗膜の耐食性が良好である。上記平均粒子径は、遠心沈降法により測定して得られる値(D50)である。更に、遠心沈降法により測定して得られる最大粒子径(Dmax)が75μmより小さいことが好ましい。
In the aqueous fluororesin coating composition of the present invention, PEI is dispersed as particles in the aqueous medium described below or dissolved in the aqueous medium. When dispersed as particles in an aqueous medium, the particles preferably have an average particle diameter of 0.1 to 20 μm. When the average particle diameter of PEI is within the above range, the corrosion resistance of the coating film obtained from the aqueous fluororesin coating composition of the present invention is good. The above average particle diameter is a value (D50) obtained by measurement by a centrifugal sedimentation method. Furthermore, it is preferable that the maximum particle diameter (D max ) measured by centrifugal sedimentation is smaller than 75 μm.
<ポリエーテルスルホン(PES)>
本発明に用いられる「ポリエーテルスルホン(PES)」は、少なくとも下記の繰り返し単位を有する高分子化合物であり、その単独重合体または共重合体のいずれも用いることができ、NMPやN-エチルモルフォリン、N-ホルミルモルフォリンなどの極性溶媒に溶解できるものが好ましく用いられる。
The "polyethersulfone (PES)" used in the present invention is a polymer compound having at least the following repeating units, and either its homopolymer or copolymer can be used, and NMP and N-ethyl morpholymer can be used. Those that can be dissolved in polar solvents such as phosphorus and N-formylmorpholine are preferably used.
本発明で用いられるバインダー樹脂(水溶性PAI、PEI、PES、その他耐熱性樹脂)の中で、水溶性PAIの組成比は30wt%以上、好ましくは40wt%以上である。PAIは熱硬化性樹脂であり、塗膜の焼成の際に流動せずに膜を形成する効果があると思われ、少ないと、均一な膜を形成できずに、欠陥を生じやすい。
PEI及びPESについては、バインダー樹脂中で、それぞれ10wt%以上含まれることが好ましい。PEIは基材への接着力、耐加水分解性能を改善させる効果があり、PESは成膜性を向上させ、かつ耐加水分解性能も改善させる効果があり、これらを併用することで、高い基材への接着力、均一な膜を形成する成膜性、優れた耐加水分解性能を持つ塗膜が得られると考えられる。
Among the binder resins (water-soluble PAI, PEI, PES, and other heat-resistant resins) used in the present invention, the composition ratio of water-soluble PAI is 30 wt% or more, preferably 40 wt% or more. PAI is a thermosetting resin and is thought to have the effect of forming a film without flowing during baking of the coating film, and if the amount is too low, a uniform film cannot be formed and defects are likely to occur.
It is preferable that PEI and PES are each contained in an amount of 10 wt% or more in the binder resin. PEI has the effect of improving adhesion to the base material and hydrolysis resistance, and PES has the effect of improving film formability and hydrolysis resistance. By using these together, a high base material can be obtained. It is believed that a coating film with adhesive strength to materials, uniform film forming properties, and excellent hydrolysis resistance can be obtained.
<フッ素樹脂>
本発明において、フッ素樹脂としては、非熱溶融性ポリテトラフルオロエチレンと熱溶融性フッ素樹脂を含む。
<非熱溶融性ポリテトラフルオロエチレン>
本発明に用いられる非熱溶融性ポリテトラフルオロエチレンは、融点以上で溶融流動性を示さない高分子量のポリテトラフルオロエチレン(PTFE)であり、テトラフルオロエチレン(TFE)の単独重合体(TFEのホモポリマー)、TFEと共重合可能な単量体が1重量%以下の範囲で含まれるTFE共重合体(変性PTFE)の何れでも良く、またはその両者を組合せて使用することもできる。このようなPTFEを用いることで、加熱
後の塗膜に残留する応力を低下させることができ、コストの低減も可能となる。
<熱溶融性フッ素樹脂>
本発明において、非熱溶融性ポリテトラフルオロエチレンと共に用いられる「熱溶融性フッ素樹脂」としては、例えば、テトラフルオロエチレン・パーフルオロ(アルキルビニルエーテル)共重合体(PFA)、テトラフルオロエチレン・ヘキサフルオロプロピレン共重合体(FEP)、テトラフルオロエチレン・ヘキサフルオロプロピレン・パーフルオロ(アルキルビニルエーテル)共重合体、テトラフルオロエチレン・エチレン共重合体、ポリビニリデンフルオライド、ポリクロロトリフルオロエチレン、クロロトリフルオロエチレン・エチレン共重合体が挙げられ、これらは、溶液重合、乳化重合、懸濁重合等の従来公知の方法によって製造することができる。
<Fluororesin>
In the present invention, the fluororesin includes non-heat-melting polytetrafluoroethylene and heat-melting fluororesin.
<Non-thermofusible polytetrafluoroethylene>
The non-thermofusible polytetrafluoroethylene used in the present invention is a high molecular weight polytetrafluoroethylene (PTFE) that does not exhibit melt flowability above its melting point, and is a homopolymer of tetrafluoroethylene (TFE) (TFE). homopolymer), a TFE copolymer (modified PTFE) containing a monomer copolymerizable with TFE in an amount of 1% by weight or less, or a combination of both may be used. By using such PTFE, stress remaining in the coating film after heating can be reduced, and costs can also be reduced.
<Thermofusible fluororesin>
In the present invention, examples of the "thermal melting fluororesin" used together with non-thermal melting polytetrafluoroethylene include tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer (PFA), tetrafluoroethylene/hexafluoroethylene Propylene copolymer (FEP), tetrafluoroethylene/hexafluoropropylene/perfluoro(alkyl vinyl ether) copolymer, tetrafluoroethylene/ethylene copolymer, polyvinylidene fluoride, polychlorotrifluoroethylene, chlorotrifluoroethylene Examples include ethylene copolymers, which can be produced by conventionally known methods such as solution polymerization, emulsion polymerization, and suspension polymerization.
本発明の水性フッ素樹脂塗料組成物に用いる熱溶融性フッ素樹脂としては、PFA、FEP、テトラフルオロエチレン・ヘキサフルオロプロピレン・パーフルオロ(アルキルビニルエーテル)共重合体といった、分子鎖中の水素原子が全てフッ素に置き換えられたパーフルオロ樹脂が、塗膜の非粘着性、耐熱性の観点から好ましく用いられる。融点以上になると溶融流動性を示す熱溶融性フッ素樹脂を用いることで、塗膜とした際にピンホールの発生を抑制でき、一様で平滑な塗膜が得られる。 The heat-melting fluororesin used in the aqueous fluororesin coating composition of the present invention includes PFA, FEP, and tetrafluoroethylene/hexafluoropropylene/perfluoro(alkyl vinyl ether) copolymer, in which all hydrogen atoms in the molecular chain are A perfluoro resin substituted with fluorine is preferably used from the viewpoint of non-adhesion and heat resistance of the coating film. By using a heat-fusible fluororesin that exhibits melt flowability above its melting point, it is possible to suppress the formation of pinholes when formed into a coating film, and a uniform and smooth coating film can be obtained.
熱溶融性フッ素樹脂の中でも、PFAは耐熱性に優れることから特に好ましい。PFAを使用する場合、PFA中のパーフルオロ(アルキルビニルエーテル)のアルキル基は、炭素数が1~5であることが好ましく、1~3であることがより好ましい。またここで、PFA中のパーフルオロ(アルキルビニルエーテル)の量としては、1~50質量%の範囲にあることが好ましい。 Among the heat-melting fluororesins, PFA is particularly preferred because it has excellent heat resistance. When PFA is used, the alkyl group of perfluoro(alkyl vinyl ether) in PFA preferably has 1 to 5 carbon atoms, more preferably 1 to 3 carbon atoms. Further, the amount of perfluoro(alkyl vinyl ether) in PFA is preferably in the range of 1 to 50% by mass.
本発明のフッ素樹脂は、公知の重合方法により得た樹脂を分離・乾燥することにより得られる粉体や、それを更に粉砕した粉体、また、特公昭52-44576に記載の方法などにより微細造粒化された粉体を、塗料組成物中に分散させて用いることができる。さらに、乳化重合により重合されたままのフッ素樹脂分散液(ディスパージョン)を、そのまま用いることもできるし、フッ素樹脂分散液に界面活性剤を添加して安定化させたもの、米国特許第3,037,953号に記載の方法などの公知の技術により濃縮してフッ素樹脂の濃度を高く調整したものを用いることもできる。安定化させたフッ素樹脂分散液は、フッ素樹脂が凝集や沈降せずに長期にわたって分散状態を維持できるため好ましい。 The fluororesin of the present invention can be obtained as a powder obtained by separating and drying a resin obtained by a known polymerization method, as a powder obtained by further pulverizing the same, or as a fine powder obtained by the method described in Japanese Patent Publication No. 52-44576. The granulated powder can be used by being dispersed in a coating composition. Furthermore, the fluororesin dispersion that has been polymerized by emulsion polymerization can be used as it is, or the fluororesin dispersion can be stabilized by adding a surfactant to it. It is also possible to use a fluororesin that has been concentrated to a high concentration using known techniques such as the method described in No. 037,953. A stabilized fluororesin dispersion is preferable because the fluororesin can maintain a dispersed state for a long period of time without agglomerating or settling.
本発明の塗料組成物に用いられるフッ素樹脂分散液の濃度としては、20~70質量%であることが好ましく、濃縮により40~70質量%としたものを用いることが、塗料組成物中のフッ素樹脂濃度の調整が容易となり好ましい。本発明に用いられるフッ素樹脂分散液の市販品としては、三井・ケマーズフロロプロダクツ(株)製テフロン(登録商標)PTFE 31-JR、PTFE 34-JR、PFA 334-JR、PFA 335-JR、FEP 120-JRが例示される。 The concentration of the fluororesin dispersion used in the coating composition of the present invention is preferably 20 to 70% by mass, and it is preferable to use a concentration of 40 to 70% by mass. This is preferable because the resin concentration can be easily adjusted. Commercially available products of the fluororesin dispersion used in the present invention include Teflon (registered trademark) PTFE 31-JR, PTFE 34-JR, PFA 334-JR, PFA 335-JR, manufactured by Mitsui Chemours Fluoro Products Co., Ltd. FEP 120-JR is exemplified.
本発明の水性フッ素樹脂塗料組成物をプライマー塗料として用いる場合、フッ素樹脂は、バインダー樹脂とフッ素樹脂の合計に対して35~90質量%であることが好ましく、45~80質量%であることが特に好ましい。フッ素樹脂が35質量%未満であると、塗膜の耐水蒸気性・耐食性が低下し、さらに、トップコートの接着性が低下するおそれがあり、一方、フッ素樹脂が90質量%を超えると、塗膜の耐食性が低下し、さらに、基材への接着力・塗膜の強度が低下するおそれがある。 When the aqueous fluororesin coating composition of the present invention is used as a primer coating, the fluororesin content is preferably 35 to 90% by mass, and preferably 45 to 80% by mass, based on the total of the binder resin and fluororesin. Particularly preferred. If the fluororesin content is less than 35% by mass, the water vapor resistance and corrosion resistance of the coating film may decrease, and the adhesion of the top coat may also decrease. On the other hand, if the fluororesin content exceeds 90% by mass, the coating may deteriorate. The corrosion resistance of the film may decrease, and the adhesion to the substrate and the strength of the coating film may also decrease.
また、本発明の水性フッ素樹脂塗料組成物をワンコート塗料として用いる場合、フッ素樹脂は、樹脂固形分の合計に対して5~90質量%であることが好ましく、10~70質量%であることが特に好ましい。フッ素樹脂が5質量%未満であると、塗膜の耐水蒸気性
・耐食性が低下し、さらに、離型性など、フッ素樹脂塗料の特性が十分得られないおそれがあり、一方、フッ素樹脂が90質量%を超えると、プライマー塗料の場合と同様に、塗膜の耐食性が低下し、さらに、基材への接着力・塗膜の強度が低下するおそれがある。
Furthermore, when the aqueous fluororesin coating composition of the present invention is used as a one-coat coating, the fluororesin content is preferably 5 to 90% by mass, and preferably 10 to 70% by mass based on the total resin solid content. is particularly preferred. If the fluororesin content is less than 5% by mass, the water vapor resistance and corrosion resistance of the coating film will decrease, and furthermore, there is a risk that the properties of the fluororesin paint, such as mold releasability, will not be sufficiently obtained. If it exceeds % by mass, the corrosion resistance of the coating film may decrease, as in the case of the primer paint, and furthermore, the adhesive strength to the substrate and the strength of the coating film may decrease.
本発明において、上記「樹脂固形分」とは、本発明のフッ素樹脂塗料組成物を被塗装物上に塗布したのち80~100℃以下の温度で乾燥し、約380℃で45分間焼成した後の残渣におけるバインダー樹脂(水溶性PAI、PEI、PES、その他耐熱性樹脂)とフッ素樹脂との合計質量を意味する。 In the present invention, the above-mentioned "resin solid content" refers to the fluororesin coating composition of the present invention applied to the object to be coated, dried at a temperature of 80 to 100°C or less, and baked at about 380°C for 45 minutes. It means the total mass of binder resin (water-soluble PAI, PEI, PES, and other heat-resistant resins) and fluororesin in the residue.
本発明のフッ素樹脂塗料組成物において、フッ素樹脂は、水性媒体に粒子として分散したものである。上記フッ素樹脂は、平均粒子径が0.01~50μmである粒子からなるものが好ましい。0.01μm未満であると、粒子の分散性が悪く、得られる塗料組成物が機械的安定性及び貯蔵安定性に劣るおそれがある。50μmを超えると、粒子の均一分散性に欠け、得られる塗料組成物を用いて塗装する際、表面が平滑な塗膜が得られず、塗膜物性が劣る場合がある。より好ましい上限は、5μmであり、更に好ましい上限は、0.5μmであり、より好ましい下限は、0.05μmである。上記機械的安定性とは、送液・再分散の際、ホモジナイザー等による強い攪拌や剪断力を与えても、再分散不可能な凝集体を生成しにくい性質のことである。 In the fluororesin coating composition of the present invention, the fluororesin is dispersed in the form of particles in an aqueous medium. The above-mentioned fluororesin preferably consists of particles having an average particle diameter of 0.01 to 50 μm. If it is less than 0.01 μm, the particles may have poor dispersibility, and the resulting coating composition may have poor mechanical stability and storage stability. If it exceeds 50 μm, the particles will lack uniform dispersibility, and when the resulting coating composition is used for coating, a coating film with a smooth surface may not be obtained, and the physical properties of the coating film may be poor. A more preferable upper limit is 5 μm, an even more preferable upper limit is 0.5 μm, and a more preferable lower limit is 0.05 μm. The above-mentioned mechanical stability refers to the property of not easily forming aggregates that cannot be redispersed even when strong stirring or shearing force is applied using a homogenizer or the like during liquid feeding and redispersion.
<その他の成分>
本発明の水性フッ素樹脂塗料組成物には、分散性・導電性・発泡防止・耐摩耗改善など求める特性に応じて通常の塗料に使用される各種の添加剤、例えば、界面活性剤(例えば、ライオン(株)製レオコール、ダウケミカルカンパニー製TRITON、TERGITOLシリーズ、花王(株)製エマルゲンなどのポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル系の非イオン系界面活性剤や、ライオン(株)製リパール、花王(株)製エマール、ぺレックスなどのスルホコハク酸塩、アルキルエーテルスルホン酸ナトリウム塩、硫酸モノ長鎖アルキル系の陰イオン系界面活性剤、ライオン(株)製レオアール、ダウケミカルカンパニー製OROTANなどのポリカルボン酸塩、アクリル酸塩系の高分子界面活性剤、モメンティブ社製L-77、AirProduct製サーフィノールシリーズ(サーフィノール420、サーフィノール440、サーフィノール465、サーフィノール485など))、造膜剤(例えば、ポリアミドやポリアミドイミド、アクリル、アセテートなどの高分子系造膜剤、高級アルコールやエーテル、造膜効果を有する高分子界面活性剤)、増粘剤(水溶性セルロール類や、溶剤分散系増粘剤、アルギン酸ソーダ、カゼイン、カゼイン酸ソーダ、キサンタンガム、ポリアクリル酸、アクリル酸エステル)なども加えることができる。
<Other ingredients>
The aqueous fluororesin coating composition of the present invention contains various additives used in ordinary coatings, such as surfactants (e.g., Nonionic surfactants based on polyoxyethylene alkyl ethers and polyoxyethylene alkyl phenyl ethers such as Lion Co., Ltd.'s Rheocol, Dow Chemical Company's TRITON, TERGITOL series, Kao Corporation's Emulgen, and Lion Co., Ltd. Sulfosuccinates, alkyl ether sulfonic acid sodium salts, mono-long chain alkyl sulfate anionic surfactants such as Riparl manufactured by Kao Corporation, Emar manufactured by Kao Corporation, and Perex, Leoard manufactured by Lion Corporation, manufactured by The Dow Chemical Company. Polycarboxylate salts such as OROTAN, acrylate-based polymer surfactants, L-77 manufactured by Momentive, Surfynol series manufactured by AirProduct (Surfynol 420, Surfynol 440, Surfynol 465, Surfynol 485, etc.)) , film-forming agents (e.g., polymeric film-forming agents such as polyamide, polyamide-imide, acrylic, acetate, higher alcohols and ethers, polymeric surfactants with film-forming effects), thickeners (water-soluble cellulose, etc.), , solvent-dispersed thickeners, sodium alginate, casein, sodium caseinate, xanthan gum, polyacrylic acid, acrylic esters), etc. can also be added.
また、本発明の水性フッ素樹脂塗料組成物は、求める特性に応じて、各種の有機物・無機物をバインダーや充填材として加えることもできる。有機物としては、例えば、ポリフェニレンサルファイド、ポリエーテルエーテルケトン、ポリエーテルスルホン、ポリフェニルスルホン、ポリアミド、ポリイミド、フェノール樹脂、尿素樹脂、エポキシ樹脂、ウレタン樹脂、メラミン樹脂、ポリエステル樹脂、ポリエーテル樹脂、アクリル樹脂、アクリルシリコーン樹脂、シリコーン樹脂、シリコーンポリエステル樹脂などのエンジニアリングプラスチックが挙げられる。無機物としては、金属粉、金属酸化物(酸化アルミ、酸化亜鉛、酸化スズ、酸化チタン等)、ガラス、セラミックス、炭化珪素、酸化珪素、弗化カルシウム、カーボンブラック、グラフアイト、マイカ、硫酸バリウムなどが挙げられる。充填材の形状としては、粒子状、繊維状、フレーク状など、各種の形状の物質が使用可能である。 Furthermore, various organic and inorganic substances can be added to the aqueous fluororesin coating composition of the present invention as binders and fillers depending on the desired properties. Examples of organic substances include polyphenylene sulfide, polyetheretherketone, polyethersulfone, polyphenylsulfone, polyamide, polyimide, phenol resin, urea resin, epoxy resin, urethane resin, melamine resin, polyester resin, polyether resin, and acrylic resin. Examples include engineering plastics such as acrylic silicone resin, silicone resin, and silicone polyester resin. Inorganic substances include metal powder, metal oxides (aluminum oxide, zinc oxide, tin oxide, titanium oxide, etc.), glass, ceramics, silicon carbide, silicon oxide, calcium fluoride, carbon black, graphite, mica, barium sulfate, etc. can be mentioned. Various shapes of fillers can be used, such as particles, fibers, and flakes.
<水性媒体>
本発明の水性フッ素樹脂塗料組成物は、水を主な媒体とするものである。ただし、環境
面やコスト面からは好ましくないが、水性フッ素樹脂塗料組成物の液体粘度などのレオロジー特性の適切な調整や、PEIや充填材などの分散性改善のために、水と相溶性のある極性溶剤を加えたり、水と非相溶性の有機溶剤を分散させることもできる。また、極性溶剤を加えることで、耐熱性樹脂(バインダー)を溶解させ、塗装後の乾燥過程において耐熱性樹脂(バインダー)がより均一になり、塗膜が緻密化することや、基材の凹凸の凹部に耐熱性樹脂(バインダー)が入り込みやすくなることで基材との接着力向上といった効果が期待できる。
<Aqueous medium>
The aqueous fluororesin coating composition of the present invention uses water as a main medium. However, although it is unfavorable from an environmental and cost perspective, it is necessary to properly adjust the rheological properties such as liquid viscosity of water-based fluoropolymer coating compositions and to improve the dispersibility of PEI and fillers. It is also possible to add a certain polar solvent or to disperse an organic solvent that is incompatible with water. In addition, by adding a polar solvent, the heat-resistant resin (binder) is dissolved, and during the drying process after painting, the heat-resistant resin (binder) becomes more uniform, and the coating film becomes denser and the unevenness of the base material becomes more uniform. By making it easier for the heat-resistant resin (binder) to enter the recesses, it is expected that the adhesive strength with the base material will be improved.
<ステンレス(SUS)>
ステンレス(SUS)とは、鉄にクロム、ニッケルなどを加えて製造される合金であり、オーステナイト系ステンレス、マルテンサイト系ステンレス、フェライト系ステンレス、オーステナイト・フェライト系ステンレスに大別され、合金の成分により多様な種類があり、JIS規格では、代表的なものではSUS304、SUS303,SUS316、SUS410、SUS430、SUS630などが規定されている。
<Stainless steel (SUS)>
Stainless steel (SUS) is an alloy manufactured by adding chromium, nickel, etc. to iron, and is broadly classified into austenitic stainless steel, martensitic stainless steel, ferritic stainless steel, and austenitic/ferritic stainless steel, depending on the alloy composition. There are various types, and the JIS standards specify SUS304, SUS303, SUS316, SUS410, SUS430, SUS630, etc. as typical ones.
<水性フッ素樹脂塗料組成物の製造プロセス>
本発明の水性フッ素樹脂塗料組成物は、従来公知の方法等により調製することができ、例えば、有機溶剤を含んだ水に溶解している上記水溶性PAI溶液と、PEI、PES、フッ素樹脂、及び、必要に応じて配合するその他の添加剤や充填材を適宜混合することにより得られる。本発明の水性フッ素樹脂塗料組成物において、PEI、PES、フッ素樹脂、顔料等は、また、それぞれの分散体(分散液)を予め調製し、得られる分散体を混合することより調製を行うものであってもよい。
<Manufacturing process of water-based fluororesin coating composition>
The aqueous fluororesin coating composition of the present invention can be prepared by a conventionally known method, and includes, for example, the water-soluble PAI solution dissolved in water containing an organic solvent, PEI, PES, fluororesin, It can also be obtained by appropriately mixing other additives and fillers that are added as necessary. In the aqueous fluororesin coating composition of the present invention, PEI, PES, fluororesin, pigment, etc. are prepared by preparing respective dispersions (dispersions) in advance and mixing the resulting dispersions. It may be.
本発明の水性フッ素樹脂塗料組成物は、25℃における粘度が0.1~50000mPa・sであることが好ましい。粘度が0.1mPa・s未満であると、被塗装物上への塗布時にタレ等を生じやすく、目的とする膜厚を得ることが困難となる場合があり、50000mPa・sを超えると、塗装作業性が悪くなる場合があり、得られる塗膜の膜厚が均一とならず、表面平滑性等に劣る場合がある。より好ましい下限は、1mPa・sであり、より好ましい上限は、30000mPa・sである。上記粘度は、BM型単一円筒型回転粘度計(東京計器社製)を用いて測定することにより得られる値である。 The aqueous fluororesin coating composition of the present invention preferably has a viscosity of 0.1 to 50,000 mPa·s at 25°C. If the viscosity is less than 0.1 mPa・s, sagging etc. may easily occur during application onto the object to be coated, and it may be difficult to obtain the desired film thickness. If the viscosity exceeds 50,000 mPa・s, the coating Workability may deteriorate, the thickness of the resulting coating film may not be uniform, and surface smoothness may be poor. A more preferable lower limit is 1 mPa·s, and a more preferable upper limit is 30000 mPa·s. The above viscosity is a value obtained by measurement using a BM type single cylinder rotational viscometer (manufactured by Tokyo Keiki Co., Ltd.).
2.塗膜
本発明の「塗膜」は、本発明の水性フッ素樹脂塗料組成物を塗装してなる塗膜である。本発明の塗料組成物を基材と接着するプライマー層とし、その上に複数の層を塗装して積層した塗膜も含まれる。
本発明の「塗膜」は、各種既存の塗装方法、例えば、スプレー塗装、ディップ塗装、スピンコート等通常一般的に用いられる方法により形成することができ、溶融流動させ均一な塗膜を得るために、フッ素樹脂の融点以上に加熱しておくことが好ましい。
2. Coating Film The "coating film" of the present invention is a coating formed by applying the aqueous fluororesin coating composition of the present invention. Also included are coating films in which the coating composition of the present invention is used as a primer layer that adheres to a base material, and a plurality of layers are coated and laminated thereon.
The "coating film" of the present invention can be formed by various existing coating methods, such as spray coating, dip coating, spin coating, etc., and can be formed by melting and flowing to obtain a uniform coating film. It is preferable to heat the fluororesin to a temperature higher than its melting point.
3.塗装物品
本発明の「塗装物品」は、本発明の水性フッ素樹脂塗料組成物を塗装してなる塗膜を有する物品である。
本発明の「塗装物品」としては、フライパン・炊飯器などの調理器具、工場ラインなどでの耐熱離型性トレイ(パン焼き工程など)、定着ロール・ベルト・インクジェットノズルなどのOA機器関連物品、配管などの化学プラントの工業設備関連物品等、非粘着性、撥水撥油性が要求される物品が挙げられ、好ましくは、高い耐水蒸気性と耐食性も要求される調理器具である。
3. Coated Article The "coated article" of the present invention is an article having a coating film formed by coating the aqueous fluororesin coating composition of the present invention.
The "coated articles" of the present invention include cooking utensils such as frying pans and rice cookers, heat-resistant release trays for factory lines (for bread baking processes, etc.), OA equipment-related articles such as fixing rolls, belts, and inkjet nozzles, and piping. Examples include articles that require non-adhesion, water and oil repellency, such as articles related to industrial equipment of chemical plants, etc., and preferably cooking utensils that also require high water vapor resistance and corrosion resistance.
(水性フッ素樹脂塗料組成物の調製)
本実施例及び比較例には、以下の試薬を使用した。
水溶性ポリアミドイミド(PAI)樹脂
日立化成工業(株)製 HPC-2100D-28(PAI濃度約28質量%、水22-32質量%、N-ホルミルモルフォリン30-40質量%の溶液)
ポリエーテルイミド(PEI)樹脂
PEI粉末:SABIC社製 Ultem 1000F3SP-1000
ポリエーテルスルホン(PES)樹脂
PES粉末:住友化学(株)製 スミカエクセル 4100MP
その他のバインダー樹脂
ポリイミド(PI):熱硬化性イミドの水性エマルジョン 中京油脂株式会社製 レゼムIM-3(イミド濃度:40質量%)
フッ素樹脂
PTFE水性分散液(1):三井・ケマーズフロロプロダクツ(株)製テフロン(登録商標)PTFE 34-JR(PTFE濃度58質量%)
PTFE水性分散液(2):三井・ケマーズフロロプロダクツ(株)製テフロン(登録商標)PTFE 31-JR(PTFE濃度60質量%)
PFA水性分散液(1):三井・ケマーズフロロプロダクツ(株)製テフロン(登録商標)PFA 334-JR(PFA濃度60質量%)
PFA水性分散液(2):三井・ケマーズフロロプロダクツ(株)製テフロン(登録商標)PFA 335-JR(PFA濃度60質量%)
FEP水性分散液:三井・ケマーズフロロプロダクツ(株)製テフロン(登録商標)FEP 120-JR(FEP濃度54質量%)
(Preparation of water-based fluororesin coating composition)
The following reagents were used in the present examples and comparative examples.
Water-soluble polyamideimide (PAI) resin
Hitachi Chemical Co., Ltd. HPC-2100D-28 (solution of PAI concentration approximately 28% by mass, water 22-32% by mass, and N-formylmorpholine 30-40% by mass)
Polyetherimide (PEI) resin
PEI powder: Ultem 1000F3SP-1000 manufactured by SABIC
Polyethersulfone (PES) resin
PES powder: Sumika Excel 4100MP manufactured by Sumitomo Chemical Co., Ltd.
Other binder resins
Polyimide (PI): Aqueous emulsion of thermosetting imide, manufactured by Chukyo Yushi Co., Ltd. Rezem IM-3 (imide concentration: 40% by mass)
Fluororesin
PTFE aqueous dispersion (1): Teflon (registered trademark) PTFE 34-JR manufactured by Mitsui Chemours Fluoro Products Co., Ltd. (PTFE concentration 58% by mass)
PTFE aqueous dispersion (2): Teflon (registered trademark) PTFE 31-JR manufactured by Mitsui Chemours Fluoro Products Co., Ltd. (PTFE concentration 60% by mass)
PFA aqueous dispersion (1): Teflon (registered trademark) PFA 334-JR manufactured by Mitsui Chemours Fluoro Products Co., Ltd. (PFA concentration 60% by mass)
PFA aqueous dispersion (2): Teflon (registered trademark) PFA 335-JR manufactured by Mitsui Chemours Fluoro Products Co., Ltd. (PFA concentration 60% by mass)
FEP aqueous dispersion: Teflon (registered trademark) FEP 120-JR manufactured by Mitsui Chemours Fluoro Products Co., Ltd. (FEP concentration 54% by mass)
実施例1
1Lステンレス容器に純水300gを入れ、攪拌機(YAMATO SCIENTIFIC CO.LTD.製)を用いて、140回転/分で攪拌しながら、非イオン系界面活性剤水溶液(濃度81質量%)を15g添加した。この界面活性剤分散液にPEI粉末40gおよびPES粉末を17g加え10分間撹拌して分散させた。更に、カーボンブラック水性分散液(固形分25質量%水分散液)を41g加えて、10分間攪拌し、次いでこれに、PFA水性分散液(1)を138g加えて、更にPTFE水性分散液(1)を240g加え、10分間攪拌した後、水溶性PAIを169g加えて、更に10分間攪拌を行い、水性フッ素樹脂塗料組成物を得た。
Example 1
300 g of pure water was placed in a 1 L stainless steel container, and 15 g of a nonionic surfactant aqueous solution (concentration 81% by mass) was added while stirring at 140 revolutions/min using a stirrer (manufactured by YAMATO SCIENTIFIC CO. LTD.). . 40 g of PEI powder and 17 g of PES powder were added to this surfactant dispersion and stirred for 10 minutes to disperse them. Furthermore, 41 g of carbon black aqueous dispersion (solid content 25% by mass aqueous dispersion) was added and stirred for 10 minutes. Next, 138 g of PFA aqueous dispersion (1) was added thereto, and further PTFE aqueous dispersion (1) was added. ) and stirred for 10 minutes, 169 g of water-soluble PAI was added and stirred for another 10 minutes to obtain an aqueous fluororesin coating composition.
実施例2~8
下表1に記載の塗料組成(樹脂固形分中の組成比(質量%))となるように、各成分の量を調整して、実施例1と同様の手順にて水性フッ素樹脂塗料組成物を得た。
Examples 2-8
A water-based fluororesin coating composition was prepared in the same manner as in Example 1 by adjusting the amount of each component so that the coating composition (composition ratio (mass %) in resin solid content) was as shown in Table 1 below. I got it.
比較例1~6
下表2に記載の塗料組成(樹脂固形分中の組成比(質量%))となるように、各成分の量を調整して、比較例1と同様の手順にてフッ素樹脂塗料組成物を得た。
Comparative examples 1 to 6
A fluororesin coating composition was prepared in the same manner as in Comparative Example 1 by adjusting the amount of each component so that the coating composition (composition ratio (mass%) in resin solid content) was as shown in Table 2 below. Obtained.
実施例の塗料組成物の樹脂固形分中の組成比(質量%)を下表1に、比較例の塗料組成物の樹脂固形分中の組成比(質量%)を下表2に示す。 The composition ratios (mass %) in the resin solid content of the coating compositions of Examples are shown in Table 1 below, and the composition ratios (mass %) in the resin solid content of the coating compositions of Comparative Examples are shown in Table 2 below.
性能評価に使用する塗膜を以下の手順で作成した。
<評価用試験片の作成>
まず、170mm角の正方形のアルミニウム(JIS A1050準拠品、厚み2mm)を基材として用い、イソプロピルアルコールで拭き取った後、#60アルミナによるショットブラストを施し表面粗度(Ra)を1~5μmとした後に、各実施例及び比較例のフッ素樹脂塗料組成物をスプレーガン(W-101-101G、アネスト岩田社製)を用いてスプレー塗装し(塗料組成物1.2~1.5g)、120℃にて20分間、続いて250℃にて20分間乾燥させ、プライマー層(フッ素樹脂塗料組成物層)を形成した。プライマー層が形成された基材に、PFA粉体塗料(三井・ケマーズフロロプロダクツ(株)製
テフロン(登録商標)塗料 MJ-102)を、全面に粉体スプレーガン(PARKER IONICS社製 GX355HW)を用いて静電粉体塗装(塗料重量3.0~3.5g)し、400℃(基材温度)にて30分間焼成し、トップコート層(PFA層)を形成した。
A coating film used for performance evaluation was created using the following procedure.
<Creation of test piece for evaluation>
First, a 170 mm square aluminum (JIS A1050 compliant, 2 mm thick) was used as a base material, and after wiping it with isopropyl alcohol, it was shot blasted with #60 alumina to give a surface roughness (Ra) of 1 to 5 μm. Afterwards, the fluororesin coating compositions of each Example and Comparative Example were spray-coated using a spray gun (W-101-101G, manufactured by Anest Iwata Co., Ltd.) (1.2 to 1.5 g of coating composition) and heated at 120°C. It was dried for 20 minutes at 250° C. and then for 20 minutes at 250° C. to form a primer layer (fluororesin coating composition layer). PFA powder paint (Teflon (registered trademark) paint MJ-102 manufactured by Mitsui Chemours Fluoro Products Co., Ltd.) is applied to the entire surface of the base material on which the primer layer has been formed using a powder spray gun (GX355HW manufactured by PARKER IONICS). Electrostatic powder coating (paint weight: 3.0 to 3.5 g) was applied using the same method, and baking was performed at 400° C. (substrate temperature) for 30 minutes to form a top coat layer (PFA layer).
アルミニウムに替えて、ステンレス(JIS SUS304、厚み1mm)を使用して、同様に接着性評価用試験片を作成し、評価試験に用いた。
(性能評価方法)
上記の評価用試験片(アルミニウム基材)を、170℃で0.8メガパスカルの水蒸気中に100時間放置した後、常温になるまで静置して冷却し、塗膜の状態を観察した。続いて、基材をガスコンロで200℃まで加熱した後、水で急冷させた塗膜の状態を確認した。膨れやブリスターが発生していれば、そこで試験を終了とし、塗膜の状態が良好であ
れば、更にこれを繰り返し、100時間毎に300時間まで、3回水蒸気加圧処理を行った。その後、下記の方法により塗膜の接着強度を測定した。
ステンレス基材の試験片については、水蒸気の温度を150℃にした以外は上記の方法と同様に評価を行った。
A test piece for adhesion evaluation was similarly prepared using stainless steel (JIS SUS304, thickness 1 mm) instead of aluminum, and used in the evaluation test.
(Performance evaluation method)
The above evaluation test piece (aluminum base material) was left in water vapor of 0.8 megapascals at 170° C. for 100 hours, then left to cool to room temperature, and the state of the coating film was observed. Subsequently, the substrate was heated to 200° C. on a gas stove, then rapidly cooled with water, and the state of the coating film was checked. If blistering or blistering occurred, the test was terminated, and if the coating film was in good condition, this was repeated, and the steam pressurization treatment was performed three times every 100 hours up to 300 hours. Thereafter, the adhesive strength of the coating film was measured by the method described below.
Regarding the stainless steel base material test piece, evaluation was performed in the same manner as in the above method except that the temperature of the water vapor was set to 150°C.
<接着強度測定方法>
上記の試験片の中央部に1cm幅になるように塗膜にカッターで切り込みをいれ、その端部の塗膜を1cmほど剥がし、接着強度測定の掴み部分とした。
テンシロン万能試験機(エイ・アンド・デイ社製)を用い、JIS K 6854に規定される接着剤の剥離強さ(90度剥離試験法)の測定方法に準拠し、上記の剥離させた塗膜を試験機のチャックに挟み、速度50mm/分で引っ張り、接着強度(剥離強度)を測定した。単位はkgf(重量キログラム)である。
結果を下表に示す。膨れやブリスターが発生せず、接着強度が0.3kgfより大きいものを、評価結果:○、として、それ以外は評価結果:×、とした。
<Adhesive strength measurement method>
A cut with a width of 1 cm was made in the coating film in the center of the above test piece, and about 1 cm of the coating film was peeled off at the end to use as a gripping part for measuring adhesive strength.
Using a Tensilon universal testing machine (manufactured by A & D Co., Ltd.), the above peeled coating film was measured in accordance with the method for measuring adhesive peel strength (90 degree peel test method) specified in JIS K 6854. was held in the chuck of a testing machine and pulled at a speed of 50 mm/min to measure the adhesive strength (peel strength). The unit is kgf (kilogram weight).
The results are shown in the table below. If no blistering or blistering occurred and the adhesive strength was greater than 0.3 kgf, the evaluation result was given as ◯, and in other cases, the evaluation result was given as ×.
Claims (7)