JP7261611B2 - Polyisocyanate composition, coating composition and coating film - Google Patents

Description

The present invention relates to polyisocyanate compositions, coating compositions and coatings.

Coating compositions using polyisocyanate compositions are widely used as coatings for construction, automobiles, information appliances, etc., because of their excellent appearance, weather resistance and durability. Above all, in applications that require a high-quality appearance and excellent weather resistance and durability, such as topcoat applications for automobiles and buildings, it is possible to form a dense crosslinked coating film and have a good finished appearance. Liquid polyurethane paints are highly regarded.
In addition to the above properties, there is a demand for a coating composition that has good water resistance and spreadability for use in automobiles, construction, and the like. Conventionally, when preparing such a coating composition, polyols such as acrylic polyols and polyester polyols are used as the main component, and hexamethylene diisocyanate (hereinafter sometimes abbreviated as "HDI") as the curing component. A method of imparting high hardness to a coating film by using a composition obtained by isocyanurating a diisocyanate and a polyhydric alcohol as raw materials has been used. However, since the isocyanurated composition hardens the coating film, the flexibility thereof is lowered, and the coating film cannot follow expansion and contraction due to temperature changes, and the coating film may crack. In order to solve this problem, a method for imparting extensibility to a coating film is disclosed in Patent Document 1, for example. Patent Document 1 discloses a reaction product of an aliphatic diisocyanate or an alicyclic diisocyanate and a polycaprolactone polyol.

Other than the isocyanurated composition, another method for producing a highly functional polyisocyanate composition includes, for example, a method of allophanatizing using a diisocyanate such as HDI and an alcohol as raw materials. The allophanatization reaction is a method of adding an isocyanate group to a urethane group, and the urethane group, which is the starting material for the allophanatization reaction, gradually decreases due to the reaction. As a result, the reaction converges spontaneously, and a polyisocyanate composition with a relatively low viscosity is obtained because the polymerization reaction such as the isocyanurate-forming reaction is less likely to occur. For example, Patent Document 2 discloses a method for producing a polyisocyanate composition having allophanate groups using a polyester polyol derived from ε-caprolactone. Patent Document 2 discloses a polyisocyanate composition having an allophanate group, which uses a diisocyanate such as HDI as raw materials and a polyester polyol derived from an alcohol and ε-caprolactone and having a number average molecular weight of 250 or more and 2000 or less. Weather resistance, durability, scratch resistance and drying property can be imparted by using a curing agent containing the polyisocyanate composition and a main agent containing a polyol.

JP-A-61-028518 JP 2011-105886 A

In the method disclosed in Patent Document 1, the resulting coating film may lack water resistance and weather resistance.
In addition, the composition disclosed in Patent Document 2 does not examine the effect of the composition on the water resistance of the resulting coating film.

The present invention has been made in view of the above circumstances, and a polyisocyanate composition having excellent water resistance, weather resistance and spreadability when formed into a coating film, and a coating composition using the polyisocyanate composition. and coatings.

As a result of extensive research, the present inventors have found that a polyisocyanate obtained from a specific diisocyanate and a polyester polyol derived from a specific compound and having a number average molecular weight of 250 or more and 4000 or less, and a urethane group. The inventors have found that the above object can be achieved by using a polyisocyanate composition having allophanate groups and isocyanurate groups in a specific ratio, and have completed the present invention.

That is, the present invention includes the following aspects.
The polyisocyanate composition according to the first aspect of the present invention includes (A) at least one diisocyanate selected from the group consisting of aliphatic diisocyanates and alicyclic diisocyanates, (B) a divalent to trivalent alcohol and A polyisocyanate obtained from a polyester polyol derived from ε-caprolactone and having a number average molecular weight of 250 or more and 4000 or less, containing a urethane group, an allophanate group and an isocyanurate group, wherein the number of moles of the urethane group is A, A / (A + B) is 0.45 or more and 0.99 or less when the number of moles of allophanate groups is B and the number of moles of isocyanurate groups is C, and C / (A + B + C) is 0.40 or more .90 or less.

A coating composition according to a second aspect of the present invention includes a polyol having a hydroxyl value of 5 mgKOH/g or more and 200 mgKOH/g or less, and the polyisocyanate composition according to the first aspect.
The coating composition according to the second aspect may be used for coating metals or plastics.
The coating composition according to the second aspect may be used as a top clear coating for building structures, automobile bodies, metal parts for automobiles, plastic parts for automobiles, metal parts for information home appliances, or plastic parts for information home appliances. good.

The coating film according to the third aspect of the present invention is obtained by curing the coating composition according to the second aspect.

According to the polyisocyanate composition of the above aspect, it is possible to provide a polyisocyanate composition that is excellent in water resistance, weather resistance and extensibility when formed into a coating film. The coating composition of the above aspect contains the polyisocyanate composition and provides a coating film having excellent water resistance, weather resistance and spreadability. The coating film of the above aspect is obtained by curing the coating composition and is excellent in water resistance, weather resistance and extensibility.

EMBODIMENT OF THE INVENTION Hereinafter, the form (henceforth "this embodiment") for implementing this invention is demonstrated in detail. The following embodiments are examples for explaining the present invention, and are not intended to limit the present invention to the following contents. Various modifications are possible for the present invention without departing from the gist thereof.

As used herein, "polyol" means a compound having two or more hydroxy groups (--OH) in one molecule.
In this specification, "polyisocyanate" means a reactant in which a plurality of monomeric compounds having two or more isocyanate groups (--NCO) are bonded.
In this specification, unless otherwise specified, "(meth)acryl" includes methacryl and acryl, and "(meth)acrylate" includes methacrylate and acrylate.

<<Polyisocyanate composition>>
The polyisocyanate composition of the present embodiment contains a polyisocyanate obtained from (A) a diisocyanate and (B) a polyester polyol. That is, the polyisocyanate is a reaction product of (A) diisocyanate and (B) polyester polyol. The (A) diisocyanate is at least one diisocyanate selected from the group consisting of aliphatic diisocyanates and alicyclic diisocyanates. The (B) polyester-based polyol is derived from a divalent to trivalent alcohol and ε-caprolactone, that is, a reaction product of a divalent to trivalent alcohol and ε-caprolactone, and the number average It has a molecular weight of 250 or more and 4000 or less.

The polyisocyanate composition of this embodiment also contains urethane groups, allophanate groups and isocyanurate groups. In the polyisocyanate composition of this embodiment, all of these functional groups may be contained in one polyisocyanate, or the polyisocyanate composition of this embodiment may contain at least one of these functional groups. It may be a mixture of polyisocyanates containing

In the polyisocyanate composition of the present embodiment, where A is the number of moles of urethane groups, B is the number of moles of allophanate groups, and C is the number of moles of isocyanurate groups, A/(A+B) is 0.45 or more. 0.99 or less, preferably 0.50 or more and 0.98 or less, more preferably 0.57 or more and 0.97 or less, further preferably 0.70 or more and 0.97 or less, and 0.80 or more and 0.96 or less is particularly preferred. When A/(A+B) is at least the above lower limit, the water resistance and extensibility of the coating film can be further improved.
C/(A+B+C) is 0.40 or more and 0.90 or less, preferably 0.40 or more and 0.85 or less, more preferably 0.50 or more and 0.85 or less, and 0.60 or more and 0.85 The following are more preferable, and 0.72 or more and 0.85 or less are particularly preferable. When C/(A+B+C) is at least the above lower limit, the weather resistance and water resistance can be further improved. can.
The respective molar ratios of urethane groups, allophanate groups and isocyanurate groups can be determined by ¹³ C-NMR measurement as described in Examples below.

The polyisocyanate composition of the present embodiment has the above-described structure, so that it is excellent in water resistance, weather resistance and extensibility when formed into a coating film.
Next, each constituent component of the polyisocyanate composition of the present embodiment will be described in detail below.

<(A) Diisocyanate>
(A) Diisocyanate is at least one diisocyanate selected from the group consisting of aliphatic diisocyanates and alicyclic diisocyanates.
An aliphatic diisocyanate is a compound having a saturated aliphatic group in its molecule. On the other hand, an alicyclic diisocyanate is a compound having a cyclic aliphatic group in its molecule. The use of an aliphatic diisocyanate is preferred because the resulting polyisocyanate composition has a low viscosity.
Aliphatic diisocyanates such as 1,4-diisocyanatobutane, 1,5-diisocyanatopentane, 1,6-diisocyanatohexane (HDI), 1,6-diisocyanato-2,2,4-trimethyl Hexane, methyl 2,6-diisocyanatohexanoate (lysine diisocyanate) and the like can be mentioned.
Examples of alicyclic diisocyanates include 5-isocyanato-1-isocyanatomethyl-1,3,3-trimethylcyclohexane (isophorone diisocyanate; hereinafter sometimes abbreviated as "IPDI"), 1,3-bis ( isocyanatomethyl)cyclohexane (hydrogenated xylylene diisocyanate), bis(4-isocyanatocyclohexyl)methane (hydrogenated diphenylmethane diisocyanate), 1,4-diisocyanatocyclohexane and the like.
These diisocyanates may be used singly or in combination of two or more.
Among them, (A) diisocyanate is preferably HDI, IPDI, hydrogenated xylylene diisocyanate or hydrogenated diphenylmethane diisocyanate because of its industrial availability. HDI is particularly preferred because of its excellent weather resistance and flexibility of the coating film.
Hereinafter, aliphatic diisocyanates and alicyclic diisocyanates may be collectively referred to as diisocyanates.

<(B) Polyester Polyol>
(B) The polyester-based polyol is derived from a divalent to trivalent alcohol and ε-caprolactone, that is, a reaction product of a divalent to trivalent alcohol and ε-caprolactone. ε-Caprolactone is one of cyclic esters and lactones, and is a seven-membered ring compound represented by the chemical formula: (CH ₂ ) ₅ CO ₂ . Polycaprolactone, which is a polyester polymer, is obtained by ring-opening polymerization of ε-caprolactone.
Examples of divalent to trivalent alcohols include 1,2-propylene glycol, 1,3-butylene glycol, neopentyl glycol, hydroxypivalic acid ester of neopentyl glycol, 2-methyl-1,3 propanediol, 2,3,5-trimethylpentanediol, ethylene glycol, diethylene glycol, 1,3-propanediol, 1,4-butylenediol, 1,5-pentanediol, 1,6-hexanediol, trimethylolpropane, glycerin, 1,1,7-trimethylolheptane, 1,2,7-trimethylolheptane and the like. These divalent to trivalent alcohols may be used singly or in combination of two or more.

(B) The upper limit of the number average molecular weight of the polyester-based polyol is 4,000, preferably 3,000, and more preferably 2,500. On the other hand, the lower limit of the number average molecular weight of (B) the polyester-based polyol is 250.
That is, the number average molecular weight of (B) the polyester-based polyol is 250 or more and 4000 or less, preferably 250 or more and 3000 or less, and more preferably 250 or more and 2500 or less.
(B) When the number average molecular weight of the polyester-based polyol is within the above range, the extensibility when formed into a coating film becomes more sufficient, and excessive increase in the viscosity of the resulting coating solution is more effectively suppressed. be able to.
The number average molecular weight of the polyester-based polyol can be obtained by gel permeation chromatography (hereinafter sometimes abbreviated as "GPC") measurement.

(B) The polyester-based polyol may be used singly or in combination of two or more.

<Method for producing polyisocyanate composition>
At least HDI is preferably used as a raw material in the production of the polyisocyanate composition of the present embodiment.
In the polyisocyanate composition of the present embodiment, for example, the isocyanurate reaction, allophanatization reaction and urethanization reaction can be performed sequentially or some of them in parallel, and these reactions can be performed in excess of the diisocyanate monomer and It is obtained by carrying out in the presence of a polyester-based polyol and removing unreacted diisocyanate monomers after the completion of the reaction. A polyisocyanate composition can also be obtained by mixing the above three reactions separately.
Furthermore, in the method for producing the polyisocyanate composition of the present embodiment, alcohols such as alkyl monoalcohols and alkyl diols can be used together as auxiliary raw materials. Here, when alcohol is used, as described above, it is preferable to use it so that A/(A+B) and C/(A+B+C) in the polyisocyanate composition of the present embodiment are within the above ranges.
Alternatively, the polyisocyanate composition of the present embodiment is obtained, for example, by subjecting a diisocyanate to an isocyanurate reaction and an allophanate reaction, and then a urethanization reaction of the obtained reaction product and a polyester-based polyol. be done. At this time, the molar ratio of the isocyanate groups in the reactant to the hydroxyl groups of the polyester polyol is preferably 2/1 or more and 40/1 or less, more preferably 3/1 or more and 30/1 or less, and 4/1 or more and 20/1. More preferred are:

Next, the isocyanurate-forming reaction, allophanat-forming reaction, and urethanization reaction are described in detail below.

[Isocyanurate reaction]
When deriving an isocyanurate group-containing polyisocyanate from a diisocyanate monomer, an isocyanurate reaction catalyst is usually used.
As the isocyanurate reaction catalyst, one having basicity is preferred. Examples of such an isocyanurate reaction catalyst include those shown in 1) to 7) below.
1) tetraalkylammonium hydroxides or organic weak acid salts;
2) hydroxyalkylammonium hydroxides or organic weak acid salts;
3) metal salts of alkylcarboxylic acids;
4) metal alcoholates such as sodium and potassium;
5) aminosilyl group-containing compounds such as hexamethyldisilazane;
6) Mannich bases;
7) Combined use of tertiary amines and epoxy compounds

Examples of tetraalkylammonium include tetramethylammonium and tetraethylammonium.
Examples of weak organic acids include acetic acid and capric acid.
Hydroxyalkylammonium includes, for example, trimethylhydroxypropylammonium, trimethylhydroxyethylammonium, triethylhydroxypropylammonium, triethylhydroxyethylammonium and the like.
Examples of alkylcarboxylic acids include acetic acid, caproic acid, octylic acid, myristic acid and the like.
Examples of metals constituting metal salts include tin, zinc, lead, sodium, and potassium.

Among them, from the viewpoint of catalytic efficiency, the isocyanurate reaction catalyst is preferably the above 1), 2), 3), 4) or 5), and more preferably the organic weak acid salt of 1).

The amount of the isocyanurate reaction catalyst added is preferably 10 ppm or more and 1000 ppm or less, more preferably 10 ppm or more and 500 ppm or less, and even more preferably 10 ppm or more and 100 ppm or less, relative to the mass of the charged diisocyanate.
The lower limit of the isocyanurate-forming reaction temperature is preferably 50°C, more preferably 54°C, still more preferably 57°C, and particularly preferably 60°C. On the other hand, the upper limit of the isocyanurate-forming reaction temperature is preferably 120°C, more preferably 100°C, still more preferably 90°C, and particularly preferably 80°C.
That is, the isocyanurate-forming reaction temperature is preferably 50°C or higher and 120°C or lower, more preferably 54°C or higher and 100°C or lower, still more preferably 57°C or higher and 90°C or lower, and particularly preferably 60°C or higher and 80°C or lower.
When the isocyanurate-forming reaction temperature is equal to or lower than the above upper limit, it is possible to more effectively prevent changes in properties such as coloring.

[Allophanatization reaction]
An allophanate group-containing polyisocyanate is obtained by adding an alcohol to a diisocyanate and using an allophanatization reaction catalyst. The alcohol used may contain an ether group, an ester group, or a carbonyl group in the molecule, but is preferably a monoalcohol composed of a saturated hydrocarbon group and a hydroxyl group, and more preferably a branched monoalcohol. Such monoalcohols include, for example, methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, isobutanol, 1-pentanol, 2-pentanol, isoamyl alcohol, 1-hexanol, 2-hexanol, 1-heptanol, 1-octanol, 2-ethyl-1-hexanol, 3,3,5-trimethyl-1-hexanol, tridecanol, pentadecanol, palmityl alcohol, stearyl alcohol, cyclopentanol, cyclo hexanol, methylcyclohexanol, trimethylcyclohexanol, and the like. Among them, as a monoalcohol, because of its particularly excellent solubility in low-polarity organic solvents, isobutanol, 1-butanol, isoamyl alcohol, 1-hexanol, 1-heptanol, 1-octanol, 2-ethyl-1 -hexanol, tridecanol, pentadecanol, palmityl alcohol, stearyl alcohol or 1,3,5-trimethylcyclohexanol are preferred. Also, due to lower viscosity, 1-propanol, isobutanol, 1-butanol, isoamyl alcohol, 1-pentanol, 2-pentanol, 1-hexanol, 2-hexanol, 1-heptanol, 1-octanol, 2 -octanol, 2-ethyl-hexyl alcohol or 3,3,5-trimethyl-1-hexanol are preferred. In addition, isobutanol, 2-hexanol, 2-octanol, 2-ethyl-1-hexanol or 3,3,5-trimethyl-1-hexanol is preferred because of its very good solubility in low-polarity organic solvents. preferable.

The amount of alcohol added is not limited to the following, but is preferably such that the molar ratio of the isocyanate group of the diisocyanate to the hydroxyl group of the alcohol is 10/1 or more and 1000/1 or less, and 100/1 or more and 1000/1 or less. is more preferable. When the molar ratio of the isocyanate groups of the diisocyanate to the hydroxyl groups of the alcohol is at least the above lower limit, a more appropriate average number of isocyanate groups can be ensured in the resulting polyisocyanate.

Examples of the allophanatization reaction catalyst include, but are not limited to, alkyl carboxylates of tin, lead, zinc, bismuth, zirconium, zirconyl, and the like.
Examples of alkyl carboxylates of tin (organotin compounds) include tin 2-ethylhexanoate and dibutyltin dilaurate.
Examples of lead alkyl carboxylates (organic lead compounds) include lead 2-ethylhexanoate.
Examples of zinc alkylcarboxylates (organozinc compounds) include zinc 2-ethylhexanoate and the like.
Bismuth alkyl carboxylates include, for example, bismuth 2-ethylhexanoate.
Examples of alkyl carboxylates of zirconium include zirconium 2-ethylhexanoate and the like.
Alkyl carboxylates of zirconyl include, for example, zirconyl 2-ethylhexanoate.

When the desired yield is achieved, the allophanatization reaction can be terminated by adding a deactivator for the allophanatization reaction catalyst, such as phosphoric acid or methyl p-toluenesulfonate.

The amount of the allophanatization reaction catalyst used is preferably 10 ppm or more and 10000 ppm or less, more preferably 10 ppm or more and 1000 ppm or less, and even more preferably 10 ppm or more and 500 ppm or less, relative to the raw material diisocyanate.

The allophanatization reaction temperature is preferably 60° C. or higher and 160° C. or lower, more preferably 70° C. or higher and 155° C. or lower, still more preferably 80° C. or higher and 150° C. or lower, and particularly preferably 90° C. or higher and 145° C. or lower.
When the allophanatization reaction temperature is equal to or lower than the above upper limit, it is possible to more effectively prevent changes in properties such as coloring of the resulting polyisocyanate.

The reaction time for allophanatization is preferably 0.2 hours or more and 8 hours or less, more preferably 0.4 hours or more and 6 hours or less, further preferably 0.6 hours or more and 4 hours or less, and 0.8 hours or more and 3 hours or less. It is particularly preferred and most preferably 1.0 hours or more and 2 hours or less.
By setting the reaction time for allophanatization to the above lower limit or more, the viscosity can be further reduced, and by setting the reaction time to the above upper limit or less, the coloring of the polyisocyanate itself can be further suppressed.

Further, the isocyanurate-forming reaction catalyst can be used as an allophanate-forming reaction catalyst. When the allophanatization reaction is performed using the above isocyanurate reaction catalyst, an isocyanurate group-containing polyisocyanate is also produced at the same time. Among them, from the viewpoint of improving productivity from an economic standpoint, it is preferable to perform the allophanatization reaction and the isocyanuration reaction using the above isocyanuration reaction catalyst as the allophanatization reaction catalyst.

[Urethane reaction]
In the method for producing the polyisocyanate composition of the present embodiment, the urethanization reaction is preferably performed after the isocyanurate reaction and the allophanatization reaction. Specifically, the isocyanurate reaction and the allophanatization reaction are performed sequentially or respectively. After obtaining polyisocyanate containing an isocyanurate group and an allophanate group by carrying out in parallel, it is preferable to subject the obtained polyisocyanate to a urethanization reaction with a polyester-based polyol.

The lower limit of the urethanization reaction temperature is preferably 80°C, more preferably 100°C. On the other hand, the upper limit of the reaction temperature is preferably 150°C, more preferably 130°C.
That is, the urethanization reaction temperature is preferably 80° C. or higher and 150° C. or lower, more preferably 100° C. or higher and 130° C. or lower.

When the polymerization reaction of the isocyanurate-forming reaction, allophanat-forming reaction and urethanization reaction reaches a desired degree of polymerization, the polymerization reaction is terminated. Termination of the polymerization reaction is not limited to the following, but can be achieved, for example, by adding an acidic compound to the reaction solution to neutralize the polymerization reaction catalyst, or by inactivating it by thermal decomposition, chemical decomposition, or the like. . Examples of acidic compounds include phosphoric acid, acidic phosphate esters, sulfuric acid, hydrochloric acid, and sulfonic acid compounds.
After stopping the reaction, filtration is performed if necessary.

Since the reaction solution immediately after stopping the reaction usually contains an unreacted diisocyanate monomer, it is preferable to remove it by a thin film evaporator, extraction, or the like. It is preferable to control the diisocyanate monomer concentration contained in the polyisocyanate composition to 1% by mass or less by performing such a post-treatment.
For example, when the diisocyanate monomer is HDI, the diisocyanate monomer concentration can be measured using the method described in the examples below.

<Physical properties of the polyisocyanate composition>
[viscosity]
The viscosity at 25° C. when the polyisocyanate composition is diluted with butyl acetate and adjusted to a solid content of 64% by mass is not particularly limited. , more preferably 150 mPa·s or more and 1500 mPa·s or less, and even more preferably 300 mPa·s or more and 1000 mPa·s or less. If the viscosity is at least the above lower limit, the number of functional groups can be sufficiently increased, while if it is at most the above upper limit, the amount of organic solvent can be reduced.
As the viscosity, a value measured at 25° C. using an E-type viscometer (Tokimec Co., Ltd.) can be adopted as described in the examples below.

[Number average functional group number (fn)]
The number average functional group number of the isocyanate groups of the polyisocyanate composition (hereinafter sometimes abbreviated as "fn") is not particularly limited, but is preferably 3.0 or more and 10.0 or less from the viewpoint of curability and viscosity, 3.2 or more and 9.0 or less are more preferable, 3.4 or more and 8.0 or less are still more preferable, and 3.6 or more and 7.0 or less are especially preferable. When fn is at least the above lower limit, more sufficient curability can be obtained, and when it is at most the above upper limit, the viscosity does not become too high.

[Isocyanate group content (NCO%)]
The isocyanate group content (NCO%) of the polyisocyanate composition is 3 from the viewpoint of performance when the polyisocyanate composition is diluted with butyl acetate and adjusted to a solid content of 64% by mass. 0% or more and 20.0% or less is preferable, 3.5% or more and 17.0% or less is more preferable, 4.0% or more and 14.0% or less is still more preferable, 4.5% or more and 11.0% or less is particularly preferred. If the NCO% is at least the above lower limit, the performance of the coating film will be better, while if it is at most the above upper limit, the crosslink density will not be too high and a coating film that is less likely to crack will be formed.
NCO% can be determined by back titration with 1N hydrochloric acid after neutralizing the isocyanate groups with excess 2N amine, as described in the examples below.

<Application>
The polyisocyanate composition of this embodiment can be used as a raw material for paints, inks, adhesives, casting materials, elastomers, foams, and plastic materials.

≪Paint composition≫
The coating composition of the present embodiment contains a polyol as a main component and the above polyisocyanate composition as a curing agent component.
The coating composition of the present embodiment may contain other main components in addition to the above polyol as the main component, but the coating composition of the present embodiment preferably contains only the above polyol as the main component. .
In addition, the coating composition of the present embodiment may contain other curing agent components in addition to the polyisocyanate composition as a curing agent component. It preferably contains only the above polyisocyanate composition.

The lower limit of the hydroxyl value of the polyol is 5 mgKOH/g, preferably 10 mgKOH/g, more preferably 15 mgKOH/g, still more preferably 20 mgKOH/g. On the other hand, the upper limit of the hydroxyl value of the polyol is 200 mgKOH/g, preferably 160 mgKOH/g, more preferably 120 mgKOH/g, and even more preferably 80 mgKOH/g.
That is, the hydroxyl value of the polyol is 5 mgKOH/g or more and 200 mgKOH/g or less, preferably 10 mgKOH/g or more and 160 mgKOH/g or less, more preferably 15 mgKOH/g or more and 120 mgKOH/g or less, and 20 mgKOH/g or more and 80 mgKOH/g. More preferred are:
When the hydroxyl value is within the above range, a more flexible and tougher coating film can be obtained.

<Polyol>
Examples of polyols include acrylic polyols, polyester polyols, polyether polyols, polyolefin polyols, silicon-containing polyols, fluorine-containing polyols, polycarbonate polyols, epoxy resins, alkyd polyols, and the like. . These polyols may be used singly or in combination of two or more. As the polyol, urethane-modified acrylic polyol, urethane-modified polyester polyol or urethane-modified polyol obtained by modifying acrylic polyol, polyester polyol or polyether polyol with aliphatic diisocyanate, alicyclic diisocyanate or polyisocyanate obtained therefrom. Ether polyols and the like can also be used.

Polyols can be produced by known techniques, and methods for producing typical acrylic polyols, polyester polyols, and polyether polyols will be described below.

[Acrylic polyols]
Acrylic polyols, for example, polymerize only polymerizable monomers having one or more active hydrogens in one molecule, or polymerizable monomers having one or more active hydrogens in one molecule, and optionally , can be obtained by copolymerizing the polymerizable monomer and another copolymerizable monomer.

Examples of the polymerizable monomer having one or more active hydrogens in one molecule include the following (i) to (vi). These may be used alone or in combination of two or more.
(i) acrylic acid esters having active hydrogen such as 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate and 2-hydroxybutyl acrylate;
(ii) Methacrylic acids having active hydrogen such as 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 2-hydroxybutyl methacrylate, 3-hydroxypropyl methacrylate, and 4-hydroxybutyl methacrylate esters.
(iii) (meth)acrylic acid esters having polyvalent active hydrogen, such as (meth)acrylic acid monoesters of triols;
Examples of the triol include glycerin and trimethylolpropane.
(iv) Monoethers of polyether polyols and the above (meth)acrylic acid esters having active hydrogen.
Examples of the polyether polyols include polyethylene glycol, polypropylene glycol, polybutylene glycol and the like.
(v) an adduct of glycidyl (meth)acrylate and a monobasic acid;
Examples of the monobasic acid include acetic acid, propionic acid, p-tert-butylbenzoic acid and the like.
(vi) an adduct obtained by ring-opening polymerization of the active hydrogen of the (meth)acrylic acid ester having an active hydrogen with a lactone;
Examples of the lactones include ε-caprolactone and γ-valerolactone.

Other monomers copolymerizable with the polymerizable monomer include, for example, the following (i) to (v). These may be used alone or in combination of two or more.
(i) methyl acrylate, ethyl acrylate, isopropyl acrylate, n-butyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, methacrylic acid (meth)acrylic acid esters such as isobutyl, n-hexyl methacrylate, cyclohexyl methacrylate, lauryl methacrylate, and glycidyl methacrylate;
(ii) unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic acid, itaconic acid;
(iii) unsaturated amides such as acrylamide, N-methylol acrylamide, diacetone acrylamide;
(iv) vinyl monomers having a hydrolyzable silyl group such as vinyltrimethoxysilane, vinylmethyldimethoxysilane, γ-(meth)acrylopropyltrimethoxysilane;
(v) other polymerizable monomers such as styrene, vinyl toluene, vinyl acetate, acrylonitrile, dibutyl fumarate

As a specific method for producing acrylic polyols, for example, the above monomers are solution-polymerized in the presence of a radical polymerization initiator such as a known peroxide or an azo compound, and diluted with an organic solvent or the like as necessary. By doing so, acrylic polyols can be obtained.

When the coating composition of the present embodiment contains a solvent with a large water content, it can be produced by a known method such as solution polymerization of the above monomers and conversion to a water layer, or emulsion polymerization. In that case, water-solubility or water-dispersibility can be imparted to acrylic polyols by neutralizing acidic moieties such as carboxylic acid-containing monomers such as acrylic acid and methacrylic acid and sulfonic acid-containing monomers with amines or ammonia. can be done.

[Polyester polyols]
Polyester polyols can be obtained, for example, by condensing a dibasic acid alone or a mixture of two or more kinds and a polyhydric alcohol alone or a mixture of two or more kinds.
Examples of the dibasic acid include carboxylic acids such as succinic acid, adipic acid, dimer acid, maleic anhydride, phthalic anhydride, isophthalic acid, terephthalic acid, and 1,4-cyclohexanedicarboxylic acid.
Examples of the polyhydric alcohol include ethylene glycol, propylene glycol, diethylene glycol, 1,4-butanediol, neopentyl glycol, 1,6-hexanediol, trimethylpentanediol, cyclohexanediol, trimethylolpropane, glycerin, and pentaerythritol. , 2-methylolpropanediol, ethoxylated trimethylolpropane, and the like.

As a specific method for producing polyester polyols, for example, the above components are mixed and heated at about 160° C. or higher and 220° C. or lower to carry out a condensation reaction. Alternatively, for example, polycaprolactones obtained by ring-opening polymerization of lactones such as ε-caprolactone using a polyhydric alcohol can also be used as polyester polyols.

[Polyether polyols]
Polyether polyols can be obtained, for example, using any one of the following methods (1) to (3).
(1) A method of randomly or block-adding an alkylene oxide alone or a mixture to a polyhydric hydroxy compound alone or a mixture using a catalyst to obtain polyether polyols.
Examples of the catalyst include hydroxides of lithium, sodium, potassium, etc., strongly basic catalysts, double metal cyanide complexes, and the like. Examples of strongly basic catalysts include alcoholates and alkylamines. Examples of double metal cyanide complexes include metal porphyrins and zinc hexacyanocobaltate complexes.
Examples of the alkylene oxide include ethylene oxide, propylene oxide, butylene oxide, cyclohexene oxide, and styrene oxide.
(2) A method of reacting a polyamine compound with an alkylene oxide to obtain a polyether polyol.
Examples of the polyamine compound include ethylenediamines.
Examples of the alkylene oxide include those exemplified in (1).
(3) A method of obtaining so-called polymer polyols by polymerizing acrylamide or the like using the polyether polyols obtained in (1) or (2) as a medium.
Examples of the polyvalent hydroxy compound include those shown in (i) to (vi) below.
(i) diglycerin, ditrimethylolpropane, pentaerythritol, dipentaerythritol, etc.;
(ii) sugar alcohol compounds such as erythritol, D-threitol, L-arabinitol, ribitol, xylitol, sorbitol, mannitol, galactitol and rhamnitol;
(iii) monosaccharides such as arabinose, ribose, xylose, glucose, mannose, galactose, fructose, sorbose, rhamnose, fucose, ribodesose;
(iv) disaccharides such as trehalose, sucrose, maltose, cellobiose, gentiobiose, lactose, melibiose;
(v) trisaccharides such as raffinose, gentianose, melezitose;
(vi) tetrasaccharides such as stachyose

<NCO/OH>
In the coating composition of this embodiment, the mixing ratio of the curing agent to the main agent can be represented by the molar ratio of isocyanate groups to hydroxyl groups (NCO/OH). The lower limit of NCO/OH is preferably 0.1, more preferably 0.3, still more preferably 0.4, and particularly preferably 0.5. On the other hand, the upper limit of NCO/OH is preferably 5.0, more preferably 4.0, even more preferably 3.0, and particularly preferably 2.0.
That is, NCO/OH is preferably 0.1 or more and 5.0 or less, more preferably 0.3 or more and 4.0 or less, further preferably 0.4 or more and 3.0 or less, and 0.5 or more and 2.0 or less. Especially preferred.
When the NCO/OH is within the above range, a tougher coating film can be formed.

<Various additives>
In addition to the above polyol and the above polyisocyanate composition, the coating composition of the present embodiment can improve adhesion of coloring pigments, dyes, and coating films depending on the purpose and application within a range that does not impair the effects of the present invention. Silane coupling agents, UV absorbers, curing accelerators, light stabilizers, matting agents, coating surface hydrophilic agents, catalysts for curing acceleration, drying improvers, leveling agents, antioxidants, plasticizers, Various additives used in the art such as surfactants may also be included.

The color pigment may be an inorganic pigment or an organic pigment. Examples of inorganic pigments include carbon black and titanium oxide, which have good weather resistance. Examples of organic pigments include phthalocyanine blue, phthalocyanine green, quinacridone red, indanthrene orange, and isoindolinone yellow.

Silane coupling agents include, for example, 3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, N-2-(aminoethyl)-3-aminopropyltrimethoxysilane, ureidopropyltriethoxysilane, vinyltriethoxysilane, Ethoxysilane, Vinyltrimethoxysilane, 3-Methacryloxypropyltrimethoxysilane, 3-Methacryloxypropyltriethoxysilane, 2-(3,4-Epoxycyclohexyl)ethyltrimethoxysilane, 3-Glycidoxypropyltrimethoxysilane , 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, methyltriethoxysilane, methyltrimethoxysilane and the like.

Examples of the ultraviolet absorber include benzophenone-based, benzotriazole-based, triazine-based, and cyanoacrylate-based ultraviolet absorbers.

Examples of light stabilizers include hindered amine-based light stabilizers, etc. Specific commercial products include, for example, Adekastab LA62, Adekastab LA67 (trade names, all manufactured by Adeka Argas Chemicals), Tinuvin 292, Tinuvin 144, Tinuvin 123, Tinuvin 440 (trade name, all manufactured by Ciba Specialty Chemicals), Sanol LS765 (trade name, manufactured by Sankyo Lifetech Co., Ltd.), and the like.

The matting agent includes, for example, ultrafine synthetic silica, etc., and when the matting agent is used, a coating film with an elegant semi-gloss and matte finish can be formed.

A silicate compound is preferable as the coating film surface hydrophilic agent. By containing the silicate compound, when a coating film is produced using the coating composition of the present embodiment, the coating film surface becomes hydrophilic, and resistance to rain streak staining is exhibited. Since the silicate compound reacts with hydroxyl groups, it is preferably added to the polyisocyanate composition, which is the curing agent component, when mixed in advance. Alternatively, they may be mixed at the same time when the polyol, which is the main component, and the polyisocyanate composition, which is the curing agent component, are mixed.
Examples of silicate compounds include tetramethoxysilane, tetraethoxysilane, tetra-n-propoxysilane, tetraisopropoxysilane, tetra-n-butoxysilane, tetraisobutoxysilane, tetra-tert-butoxysilane, dimethoxydiethoxysilane. , tetraphenoxysilane, condensates thereof, and the like. Among them, the silicate compound is preferably a condensate of tetramethoxysilane or a condensate of tetraethoxysilane, because the surface of the coating film is likely to be hydrophilic when the coating film is produced.

Examples of catalysts for accelerating curing include, but are not limited to, metal salts, tertiary amines, and the like.
Examples of metal salts include dibutyltin dilaurate, tin 2-ethylhexanoate, zinc 2-ethylhexanoate, cobalt salts and the like.
Examples of tertiary amines include triethylamine, pyridine, methylpyridine, benzyldimethylamine, N,N-dimethylcyclohexylamine, N-methylpiperidine, pentamethyldiethylenetriamine, N,N'-endoethylenepiperazine, N,N' - dimethylpiperazine and the like.

Examples of dryness improvers include CAB (cellulose acetate butrate) and NC (nitrocellulose).

[Leveling agent]
Examples of leveling agents include, but are not limited to, silicones, aerosils, waxes, stearates, and polysiloxanes.

[Plasticizer]
Examples of plasticizers include, but are not limited to, phthalates, phosphates, fatty acid esters, pyromellitic esters, epoxy plasticizers, polyether plasticizers, liquid rubbers, and non-aromatic paraffin oils. etc.
Examples of phthalates include dioctyl phthalate, dibutyl phthalate, diethyl phthalate, butylbenzyl phthalate, di-2-ethylhexyl phthalate, diisodecyl phthalate, diundecyl phthalate, and diisononyl phthalate.
Phosphate esters include, for example, tricresyl phosphate, triethyl phosphate, tributyl phosphate, tri-2-ethylhexyl phosphate, trimethylhexyl phosphate, tris-chloroethyl phosphate, tris-dichloropropyl phosphate and the like.
Examples of fatty acid esters include trimellitic acid esters, dipentaerythritol esters, dioctyl adipate, dimethyl adipate, di-2-ethylhexyl azelate, dioctyl azelate, dioctyl sebacate, di-2-ethylhexyl sebacate, and methyl acetyl lysinocate. Examples of trimellitates include octyl trimellitate and isodecyl trimellitate.
Examples of pyromellitic acid esters include pyromellitic acid octyl ester and the like.
Examples of epoxy plasticizers include epoxidized soybean oil, epoxidized linseed oil, and epoxidized fatty acid alkyl esters.
Examples of polyether plasticizers include adipate ether esters and polyethers.
Examples of liquid rubber include liquid NBR, liquid acrylic rubber, and liquid polybutadiene.

[Surfactant]
Examples of surfactants include known anionic surfactants, cationic surfactants, and amphoteric surfactants.

<Method for producing paint composition>
The coating composition of the present embodiment is useful as a solvent coating composition, and can be obtained by the manufacturing method described below.

When the coating composition of the present embodiment is a solvent-based coating composition, for example, first, a polyol or a solvent dilution thereof as a main agent, and, if necessary, various additives are added to the above poly An isocyanate composition is added as a curing agent. Then, if necessary, a solvent is further added to adjust the viscosity. A solvent-based coating composition can then be obtained by stirring by hand or by using a stirring device such as a Masellar.
Further, the order of mixing the main agent component containing the polyol as the main component, the curing agent component containing the polyisocyanate composition as the main component, and the various additives is not particularly limited. can be done.
1) Mixing a curing agent component with a main component in which various additives are premixed at the painting site;
2) After mixing the main agent component and the curing agent component at the painting site, various additives are mixed;
3) The hardener component, which is pre-mixed with various additives, is mixed with the main component, which is pre-mixed with various additives, at the painting site.

<Application>
The coating composition of the present embodiment is not limited to the following, but for example, spray coating, air spray coating, brush coating, coating by dipping method, roll coating, curtain flow coating, bell coating, electrostatic coating, etc. can be used.
In addition, the coating composition of the present embodiment is also useful as a coating for materials such as metals (steel plates, surface-treated steel plates, etc.), plastics, wood, films, inorganic materials, etc., and is particularly suitable as a coating for metals or plastics. is.
Further, the coating composition of the present embodiment is suitable for, for example, architectural coatings, heavy-duty anticorrosive coatings, automotive coatings, information appliance coatings, and information equipment coatings such as personal computers and mobile phones. It is particularly suitable as a top clear paint for automobile bodies, metal parts for automobiles, plastic parts for automobiles, metal parts for information home appliances, or plastic parts for information home appliances.

≪Paint film≫
The coating film of the present embodiment is obtained by curing the above coating composition, always exhibits stable quality, and is excellent in water resistance, weather resistance and extensibility.

<Method for producing coating film>
The method for producing a coating film of the present embodiment is a method including the step of curing the coating composition.

The coating film of the present embodiment is formed by coating the above coating composition with a known coating such as spray coating, air spray coating, brush coating, dip coating, roll coating, curtain flow coating, bell coating, and electrostatic coating. It can be produced by curing after coating on the object to be coated using the method.
Examples of the object to be coated include the same materials as exemplified in the above "<Usage of use of the coating composition>".

Hereinafter, the present embodiment will be described in more detail by showing specific examples and comparative examples, but the present embodiment is not limited by the following examples and comparative examples as long as the gist thereof is not exceeded. .

<Physical properties of polyisocyanate and polyisocyanate composition>
[Physical property 1] A / (A + B) and C (A + B + C)
The resulting polyisocyanate composition was subjected to ¹³ C-NMR measurement using Biospin Avance 600 (trade name) manufactured by Bruker. Specific measurement conditions were as follows.

(Measurement condition)
¹³ C-NMR device: AVANCE600 (manufactured by Bruker)
Cryoprobe (manufactured by Bruker)
CryoProbe®
CPDUL
600S3-C/HD-05Z
Resonance frequency: 150MHz
Concentration: 60wt/vol%
Shift reference: CDCl ₃ (77 ppm)
Number of times of integration: 10000 times Pulse program: zgpg30 (proton complete decoupling method, waiting time 2 sec)

Each molar ratio of urethane groups, allophanate groups and isocyanurate groups was obtained by dividing the integrated value of the following signals by the number of carbon atoms being measured. Then, A/(A+B) and C/(A+B+C) were calculated, where A is the number of moles of urethane groups, B is the number of moles of allophanate groups, and C is the number of moles of isocyanurate groups.

Isocyanurate group: (Integral value around 148.6 ppm) ÷ 3
Urethane group: (integrated value near 156.5 ppm)/1
Allophanate group: (Integral value around 154 ppm) ÷ 1

[Physical property 2] Viscosity at 25°C Viscosity was measured at 25°C with an E-type viscometer (manufactured by Tokimec Co., Ltd.). A standard rotor (1°34′×R24) was used. The number of revolutions is as follows.

(Number of revolutions)
100r. p. m. (When less than 128 mPa s)
50r. p. m. (In the case of 128 mPa s or more and less than 256 mPa s)
20r. p. m. (In the case of 256 mPa·s or more and less than 640 mPa·s)
10r. p. m. (640 mPa·s or more and less than 1280 mPa·s)
5r. p. m. (In the case of 1280 mPa s or more and less than 2560 mPa s)
2.5r. p. m. (In the case of 2560 mPa s or more and less than 5120 mPa s)
1r. p. m. (In the case of 5120 mPa s or more and less than 10240 mPa s)
0.5r. p. m. (In the case of 10240 mPa s or more and less than 20480 mPa s)

[Physical property 3] Isocyanate content (NCO%)
NCO% was determined by back titration with 1N hydrochloric acid after neutralizing the isocyanate groups with an excess of 2N amine.

[Physical Property 4] HDI Monomer Concentration A polystyrene-based number average molecular weight was measured by GPC measurement under the following measurement conditions. Then, the peak area % of the molecular weight (168) corresponding to the unreacted HDI monomer was calculated as the HDI monomer concentration.

<Method for evaluating coating film>
Using each polyisocyanate composition, coating compositions were produced and evaluated as follows.

[Production Example 1] Production of coating composition They were blended so that the equivalent ratio of hydroxyl groups and isocyanate groups was 1:1. After that, the paint viscosity was changed to Ford Cup No. 1 with butyl acetate. 4 for 20 seconds to obtain each coating composition.

[Evaluation 1] Water resistance Each coating composition was applied to a glass plate so that the dry film thickness was 30 μm, allowed to stand at room temperature for 15 minutes, and then cured in an oven at 60° C. for 120 minutes to obtain each coating film. . After cooling to room temperature, this coating film was held for 72 hours under conditions of 60° C. and 87% humidity. After that, it was allowed to stand at room temperature for 60 minutes, and the coating film after the test was visually observed. The water resistance of each coating film was evaluated according to the evaluation criteria shown below. Table 1 shows the evaluation results.

(Evaluation criteria)
◎: Whitening, spots, etc. were not observed ○: Whitening, spots were observed in 1 or 2 places ×: Whitening, spots were observed in 3 or more places

[Evaluation 2] Weather resistance Each coating composition was applied to a white enamel coated plate with an applicator so that the film thickness after drying was 40 μm, and the coating film was cured for 1 week under the conditions of 20 ° C. and 63% humidity, and then the coated plate. was evaluated for weather resistance. A due panel weather meter (manufactured by Suga Test Instruments) was used for weather resistance evaluation. According to JIS D0205, the evaluation conditions were irradiation intensity of 30 W/m ² , panel temperature of 60° C., irradiation time and dew condensation time were cycled every 4 hours. The water resistance of each coating film was evaluated according to the evaluation criteria shown below. Table 1 shows the evaluation results.

(Evaluation criteria)
◎: Gloss retention rate of 80% or more at 1200 hours of exposure time ○: Gloss retention rate of 70% or more and less than 80% at 1200 hours of exposure time ×: Gloss retention rate of 70 at 1200 hours exposure time less than %

[Evaluation 3] Extensibility (coating film elongation)
Each coating composition was applied with an applicator so that the film thickness after drying was 50 μm. After coating, each coating film was obtained by curing for 7 days under conditions of 23° C. and 50% humidity. A tensile test was performed using the obtained coating film. The elongation of the coating film was measured at a temperature of 23° C. and humidity of 50% using a tensile tester (AGS 500G manufactured by Shimadzu Corporation) at a tensile speed of 20 mm/min and a grip interval of 20 mm. The water resistance of each coating film was evaluated according to the evaluation criteria shown below. Table 1 shows the evaluation results.

(Evaluation criteria)
◎: The coating film elongation is 150% or more ○: The coating film elongation is 100% or more and less than 150% ×: The coating film elongation is 0% or more and less than 100%

<Synthesis of polyisocyanate>
[Synthesis Example 1] Synthesis of polyisocyanate A-1 A four-necked flask equipped with a stirrer, thermometer, reflux condenser, nitrogen blowing tube and dropping funnel was set to a nitrogen atmosphere, 1000 g of HDI was charged, and the reaction was carried out with stirring. The temperature inside the vessel was kept at 80° C. for 2 hours. After that, 1 g of a solution of tetramethylammonium caprate diluted with isobutanol to 5% by mass was added as an isocyanurate-forming catalyst to carry out an isocyanurate-forming reaction. When the refractive index of the reaction liquid increased to 0.012, phosphoric acid was added to terminate the reaction. After filtering the reaction solution, it was purified twice under conditions of 160° C. and 0.2 Torr using a thin film evaporator to obtain polyisocyanate A-1. The resulting polyisocyanate A-1 had a viscosity of 1,300 mPa·s (25° C.), an NCO content of 23.1% by mass, and an HDI monomer concentration of 0.11% by mass.

[Synthesis Example 2] Synthesis of Polyisocyanate A-2 Into the same apparatus as in Synthesis Example 1, 1000 g of HDI and 30 g of 2-ethylhexanol were charged, and a urethanization reaction was carried out at 90° C. for 1 hour while stirring. As an allophanatization and isocyanuration catalyst, 1 g of a solution of tetramethylammonium caprate diluted with isobutanol to 5% by mass was added to carry out an isocyanuration reaction. When the refractive index of the reaction liquid increased to 0.012, phosphoric acid was added to terminate the reaction. After filtering the reaction solution, unreacted HDI was removed in the same manner as in Synthesis Example 1 to obtain Polyisocyanate A-2. The obtained polyisocyanate A-2 had a viscosity of 500 mPa·s (25° C.), an NCO content of 20.6% by mass, and an HDI monomer concentration of 0.11% by mass.

[Synthesis Example 3] Synthesis of Polyisocyanate A-3 Into the same apparatus as in Synthesis Example 1, 1000 g of HDI and 78 g of 2-ethylhexanol were charged, and a urethanization reaction was carried out at 130° C. for 1 hour while stirring. As an allophanatization catalyst, 0.35 g of a 20% solution of zirconyl 2-ethylhexanoate in mineral spirits was added. After 60 minutes, when the refractive index of the reaction solution increased to 0.0055, a 39% solid content ethanol solution of pyrophosphoric acid (manufactured by Taihei Kagaku Sangyo, trade name "Phosphoric acid (105%)"): 0. 47 g was added to stop the reaction. Then, unreacted HDI was removed in the same manner as in Synthesis Example 1 to obtain polyisocyanate A-3. The resulting polyisocyanate A-3 was a transparent liquid with a viscosity of 100 mPa.s. s, the NCO content was 17.4%, and the HDI monomer concentration was 0.11% by mass.

<Production of polyisocyanate composition>
[Example 1] Production of polyisocyanate composition Pa1 In the same apparatus as in Synthesis Example 1, the polyisocyanate A-1 obtained in Synthesis Example 1: 100 g, polyester polyol B-1 (manufactured by DIC Corporation, " Polylite OD-X-2722" (trade name), molecular weight 2000): 60 g, and 2-ethylhexyl phosphate (manufactured by Johoku Kagaku Kogyo Co., Ltd., trade name: "JP-508"): 0.01 g were added. Then, the mixed solution was subjected to a urethanization reaction at 110° C. for 4 hours with stirring, and then 90 g of n-butyl acetate was added as a diluting solvent to obtain a polyisocyanate composition Pa1. The resulting polyisocyanate composition Pa1 was a transparent liquid with a viscosity of 650 mPa·s and an NCO content of 8.3%. Also, using the obtained polyisocyanate composition Pa1, water resistance, weather resistance and coating film elongation were evaluated by the methods described above. Table 1 shows the results.

[Examples 2 to 7 and Comparative Examples 1 to 4, 6] Production of polyisocyanate compositions Pa2 to Pa7, Pb1 to P-b4, and P-b6 , Using the same method as in Example 1, polyisocyanate compositions Pa2 to Pa7, Pb1 to Pb4, and Pb6 were obtained. Using each polyisocyanate composition obtained, the water resistance, weather resistance and coating elongation were evaluated by the methods described above. Table 1 shows the results. In Table 1, "polyester polyol B-2" indicates the following commercial products.

Polyester polyol B-2: manufactured by DIC Corporation, "Polylite OD-X-2542C (trade name), molecular weight 850

[Comparative Example 5] Production of polyisocyanate composition P-b5 In the same apparatus as in Synthesis Example 1, 562 g of HDI and polyester polyol B-3 (polycaprolactone polyol, manufactured by Daicel Corporation, "PLAXEL 305" (trade name) , and a molecular weight of 550): 115 g were charged, and the urethanization reaction was carried out at 100° C. for 1 hour while stirring. Next, after removing unreacted HDI in the same manner as in Synthesis Example 1, 90 g of n-butyl acetate was added as a diluting solvent to obtain a polyisocyanate composition P-b5 (composition (unit: g): HDI /polyester polyol B-3/n-butyl acetate=45/115/90). The resulting polyisocyanate composition P-b5 was a transparent liquid with a viscosity of 100 mPa·s and an NCO content of 7.4%. Also, using the obtained polyisocyanate composition P-b5, water resistance, weather resistance and coating film elongation were evaluated by the methods described above. Table 1 shows the results.

From Table 1, by using the polyisocyanate compositions Pa1 to Pa7 (Examples 1 to 7), it is possible to obtain a coating film having excellent water resistance, weather resistance and extensibility (coating film elongation). confirmed.
In addition, in the polyisocyanate compositions Pa1 to Pa7 (Examples 1 to 7), when A/(A+B) is 0.57 or more, there is a tendency that the water resistance when formed into a coating film is superior. When A / (A + B) is 0.93 or more, in addition to water resistance when made into a coating film, there is a tendency to be more excellent in extensibility, and C / (A + B + C) is 0.51 or more When C / (A + B + C) is 0.73 or more, in addition to water resistance when it is a coating film, it tends to be more excellent in weather resistance. It was observed.

On the other hand, when the polyisocyanate compositions P-b1 to P-b6 (Comparative Examples 1 to 6) were used, a coating film excellent in all of water resistance, weather resistance and spreadability (coating film elongation) was not obtained. rice field.

According to the polyisocyanate composition of the present embodiment, it is possible to provide a polyisocyanate composition that is excellent in water resistance, weather resistance and extensibility when formed into a coating film. The polyisocyanate composition of this embodiment can be used as a raw material for paints, inks, adhesives, casting materials, elastomers, foams, and plastic materials. The coating composition of the present embodiment is suitable for architectural coatings, heavy-duty anti-corrosion coatings, automotive coatings, information appliance coatings, and information equipment coatings such as personal computers and mobile phones.

Claims (5)

(A) at least one diisocyanate selected from the group consisting of aliphatic diisocyanates and alicyclic diisocyanates, and (B) a divalent to trivalent alcohol and ε-caprolactone having a number average molecular weight of 250 to 4000. The following polyester-based polyol and a polyisocyanate obtained from
containing a urethane group, an allophanate group and an isocyanurate group,
A/(A+B) is 0.45 or more and 0.99 or less, and C/( A polyisocyanate composition in which A+B+C) is 0.40 or more and 0.90 or less. a polyol having a hydroxyl value of 5 mgKOH/g or more and 200 mgKOH/g or less;
The polyisocyanate composition of claim 1;
A coating composition comprising: 3. The coating composition according to claim 2, which is used for coating metals or plastics. 4. The coating composition according to claim 2, which is used as a top clear coating for building structures, automobile bodies, metal parts for automobiles, plastic parts for automobiles, metal parts for home information appliances, or plastic parts for home information appliances. A coating film obtained by curing the coating composition according to any one of claims 2 to 4.