JP7135438B2 - Tire rubber composition and pneumatic tire - Google Patents

Description

TECHNICAL FIELD The present invention relates to a rubber composition for tires and a pneumatic tire.

In recent years, due to the growing interest in environmental issues, there is a strong demand for low fuel consumption in automobiles, and rubber compositions used for automobile tires are also required to be excellent in low fuel consumption. .

Tires are required to have grip performance such as dry grip performance and wet grip performance in order to ensure safety and the like. In order to meet this demand, styrene-butadiene rubber is widely used as a rubber component, but the use of styrene-butadiene rubber tends to reduce fuel efficiency. As described above, grip performance and fuel efficiency are in conflict with each other, and it is difficult to comprehensively improve them.

The present invention solves the above problems and provides a rubber composition for a tire that can comprehensively improve fuel efficiency, wet grip performance and dry grip performance, and a pneumatic tire produced using the rubber composition. With the goal.

The present invention provides a rubber component having a styrene-butadiene rubber content of 10 to 50% by mass, a butadiene rubber content of 10 to 50% by mass, and an isoprene rubber content of 10 to 50% by mass, and the rubber component. and silica in an amount of 80 parts by mass or more per 100 parts by mass, wherein the styrene-butadiene rubber has a styrene content of 30 mass % or less and a vinyl content of 50 mass % or more.

The rubber composition preferably contains a mercapto-based silane coupling agent.

The rubber composition preferably contains carbon black having a cetyltrimethylammonium bromide specific surface area of 160 m ² /g or more.

It is preferable that the content of the terpene-based resin is 25 parts by mass or less with respect to 100 parts by mass of the rubber component.

The nitrogen adsorption specific surface area of the silica is preferably 220 m ² /g or more.

The present invention also relates to a pneumatic tire produced using the rubber composition.

According to the present invention, the tire rubber composition contains predetermined amounts of styrene-butadiene rubber, butadiene rubber, isoprene-based rubber and silica, and the styrene content and vinyl content of the styrene-butadiene rubber are within specific ranges. It is possible to comprehensively improve fuel efficiency, wet grip performance and dry grip performance.

The rubber composition for tires of the present invention contains predetermined amounts of styrene-butadiene rubber (SBR), butadiene rubber (BR), isoprene-based rubber and silica, and the styrene content and vinyl content of SBR are within specific ranges.

The above-described effects of the rubber composition are obtained, and it is presumed that these effects are brought about by the following effects.
When SBR is used as the main component of the rubber component, the grip performance tends to be improved, but the fuel efficiency tends to decrease. On the other hand, in the above rubber composition, BR and isoprene rubber are used as rubber components other than SBR, the ratio of these is adjusted, the silica content is adjusted to a specific range, and the styrene content of SBR is adjusted. And by adjusting the amount of vinyl to a specific range, silica is well dispersed in the rubber composition. It is believed that this will result in comprehensive improvements in fuel efficiency, wet grip performance, and dry grip performance.

The rubber composition contains SBR as a rubber component.
The SBR is not particularly limited, and for example, emulsion-polymerized styrene-butadiene rubber (E-SBR), solution-polymerized styrene-butadiene rubber (S-SBR), etc. can be used. SBR may be either unmodified SBR or modified SBR.

The modified SBR may be an SBR having a functional group that interacts with a filler such as silica. SBR (end-modified SBR having the above functional group at the end), main chain-modified SBR having the above-mentioned functional group in the main chain, main chain end-modified SBR having the above-mentioned functional group in the main chain and end (for example, the main chain Main chain end-modified SBR having the above functional group and at least one end modified with the above modifier), or modified (coupled) with a polyfunctional compound having two or more epoxy groups in the molecule, hydroxyl group and terminal-modified SBR into which an epoxy group is introduced.

Examples of the functional groups include amino group, amido group, silyl group, alkoxysilyl group, isocyanate group, imino group, imidazole group, urea group, ether group, carbonyl group, oxycarbonyl group, mercapto group, sulfide group, disulfide group, sulfonyl group, sulfinyl group, thiocarbonyl group, ammonium group, imide group, hydrazo group, azo group, diazo group, carboxyl group, nitrile group, pyridyl group, alkoxy group, hydroxyl group, oxy group, epoxy group and the like. . In addition, these functional groups may have a substituent. Among them, an amino group (preferably an amino group in which the hydrogen atom of the amino group is substituted with an alkyl group having 1 to 6 carbon atoms), an alkoxy group (preferably an alkoxy group having 1 to 6 carbon atoms), an alkoxysilyl group ( An alkoxysilyl group having 1 to 6 carbon atoms is preferred.

（式中、Ｒ^１、Ｒ^２及びＲ^３は、同一又は異なって、アルキル基、アルコキシ基、シリルオキシ基、アセタール基、カルボキシル基（－ＣＯＯＨ）、メルカプト基（－ＳＨ）又はこれらの誘導体を表す。Ｒ^４及びＲ^５は、同一又は異なって、水素原子又はアルキル基を表す。Ｒ^４及びＲ^５は結合して窒素原子と共に環構造を形成してもよい。ｎは整数を表す。） As the modified SBR, an SBR modified with a compound (modifying agent) represented by the following formula is particularly suitable.

(wherein R ¹ , R ² and R ³ are the same or different and represent an alkyl group, alkoxy group, silyloxy group, acetal group, carboxyl group (--COOH), mercapto group (--SH) or derivatives thereof (R ⁴ and R ⁵ are the same or different and represent a hydrogen atom or an alkyl group. R ⁴ and R ⁵ may combine to form a ring structure together with a nitrogen atom. n represents an integer.)

As the modified SBR modified with the compound (modifier) represented by the above formula, among others, the polymerization terminal (active terminal) of solution-polymerized styrene-butadiene rubber (S-SBR) is modified with the compound represented by the above formula. Modified SBR (such as the modified SBR described in JP-A-2010-111753) is preferably used.

R ¹ , R ² and R ³ are preferably alkoxy groups (preferably C 1-8 alkoxy groups, more preferably C 1-4 alkoxy groups). An alkyl group (preferably an alkyl group having 1 to 3 carbon atoms) is suitable for R ⁴ and R ⁵ . n is preferably 1-5, more preferably 2-4, even more preferably 3. Also, when R ⁴ and R ⁵ combine to form a ring structure with a nitrogen atom, it is preferably a 4- to 8-membered ring. The alkoxy group also includes a cycloalkoxy group (cyclohexyloxy group, etc.) and an aryloxy group (phenoxy group, benzyloxy group, etc.).

Specific examples of the modifier include 2-dimethylaminoethyltrimethoxysilane, 3-dimethylaminopropyltrimethoxysilane, 2-dimethylaminoethyltriethoxysilane, 3-dimethylaminopropyltriethoxysilane, 2-diethylaminoethyltrimethoxysilane, methoxysilane, 3-diethylaminopropyltrimethoxysilane, 2-diethylaminoethyltriethoxysilane, 3-diethylaminopropyltriethoxysilane and the like. Among them, 3-dimethylaminopropyltrimethoxysilane, 3-dimethylaminopropyltriethoxysilane, and 3-diethylaminopropyltrimethoxysilane are preferred. These may be used alone or in combination of two or more.

As modified SBR, modified SBR modified with the following compounds (modifying agents) can also be suitably used. Modifiers include, for example, polyglycidyl ethers of polyhydric alcohols such as ethylene glycol diglycidyl ether, glycerin triglycidyl ether, trimethylolethane triglycidyl ether, trimethylolpropane triglycidyl ether; polyglycidyl ethers of aromatic compounds having a phenol group of; 1,4-diglycidylbenzene, 1,3,5-triglycidylbenzene, polyepoxy compounds such as polyepoxidized liquid polybutadiene; 4,4'-diglycidyl-diphenyl epoxy group-containing tertiary amines such as methylamine and 4,4'-diglycidyl-dibenzylmethylamine; diglycidylaniline, N,N'-diglycidyl-4-glycidyloxyaniline, diglycidylorthotoluidine, tetraglycidylmetaxylenediamine , tetraglycidylaminodiphenylmethane, tetraglycidyl-p-phenylenediamine, diglycidylaminomethylcyclohexane, tetraglycidyl-1,3-bisaminomethylcyclohexane and other diglycidylamino compounds;

amino group-containing acid chlorides such as bis-(1-methylpropyl)carbamic acid chloride, 4-morpholinecarbonyl chloride, 1-pyrrolidinecarbonyl chloride, N,N-dimethylcarbamic acid chloride and N,N-diethylcarbamic acid chloride;1 , 3-bis-(glycidyloxypropyl)-tetramethyldisiloxane, (3-glycidyloxypropyl)-pentamethyldisiloxane and other epoxy group-containing silane compounds;

(trimethylsilyl)[3-(trimethoxysilyl)propyl]sulfide, (trimethylsilyl)[3-(triethoxysilyl)propyl]sulfide, (trimethylsilyl)[3-(tripropoxysilyl)propyl]sulfide, (trimethylsilyl)[3 -(tributoxysilyl) propyl] sulfide, (trimethylsilyl) [3-(methyldimethoxysilyl) propyl] sulfide, (trimethylsilyl) [3-(methyldiethoxysilyl) propyl] sulfide, (trimethylsilyl) [3-(methyldi sulfide group-containing silane compounds such as propoxysilyl)propyl]sulfide, (trimethylsilyl)[3-(methyldibutoxysilyl)propyl]sulfide;

N-substituted aziridine compounds such as ethyleneimine and propyleneimine; methyltriethoxysilane, N,N-bis(trimethylsilyl)-3-aminopropyltrimethoxysilane, N,N-bis(trimethylsilyl)-3-aminopropyltriethoxy Alkoxysilanes such as silane, N,N-bis(trimethylsilyl)aminoethyltrimethoxysilane, N,N-bis(trimethylsilyl)aminoethyltriethoxysilane; 4-N,N-dimethylaminobenzophenone, 4-N,N- Di-t-butylaminobenzophenone, 4-N,N-diphenylaminobenzophenone, 4,4'-bis(dimethylamino)benzophenone, 4,4'-bis(diethylamino)benzophenone, 4,4'-bis(diphenylamino ) benzophenone, N,N,N',N'-bis-(tetraethylamino)benzophenone and other (thio)benzophenone compounds having amino groups and/or substituted amino groups; 4-N,N-dimethylaminobenzaldehyde, 4- N,N-diphenylaminobenzaldehyde, 4-N,N-divinylaminobenzaldehyde and other benzaldehyde compounds having amino groups and/or substituted amino groups; N-methyl-2-pyrrolidone, N-vinyl-2-pyrrolidone, N- N-substituted pyrrolidones such as phenyl-2-pyrrolidone, Nt-butyl-2-pyrrolidone, N-methyl-5-methyl-2-pyrrolidone, N-methyl-2-piperidone, N-vinyl-2-piperidone, N - N-substituted piperidones such as phenyl-2-piperidone; - N-substituted lactams such as methyl-β-propiolactam and N-phenyl-β-propiolactam;

N,N-bis-(2,3-epoxypropoxy)-aniline, 4,4-methylene-bis-(N,N-glycidylaniline), tris-(2,3-epoxypropyl)-1,3,5 -triazine-2,4,6-triones, N,N-diethylacetamide, N-methylmaleimide, N,N-diethylurea, 1,3-dimethylethyleneurea, 1,3-divinylethyleneurea, 1,3 -diethyl-2-imidazolidinone, 1-methyl-3-ethyl-2-imidazolidinone, 4-N,N-dimethylaminoacetophenone, 4-N,N-diethylaminoacetophenone, 1,3-bis(diphenyl amino)-2-propanone, 1,7-bis(methylethylamino)-4-heptanone and the like. Among them, modified SBR modified with alkoxysilane is preferable.
Modification with the above compound (modifying agent) can be carried out by a known method.

The weight average molecular weight (Mw) of SBR is preferably 50,000 or more, more preferably 150,000 or more, and preferably 800,000 or less, more preferably 500,000 or less. Within the above range, the effects of the present invention tend to be obtained more favorably.
Note that Mw is based on the value measured by gel permeation chromatography (GPC) (GPC-8000 series manufactured by Tosoh Corporation, detector: differential refractometer, column: TSKGEL SUPERMULTIPORE HZ-M manufactured by Tosoh Corporation). can be obtained by standard polystyrene conversion.

When multiple SBRs are contained in the rubber composition, the "styrene content" in the present invention means the average styrene content of the multiple SBRs, and when only one type of SBR is contained, it means the styrene content of the SBR. . The average styrene content of SBR is {Σ(content of each SBR×styrene content of each SBR)}/total content of all SBRs. For example, when the rubber component consists of 90% by mass of SBR (A) (40% by mass of styrene), 5% by mass of SBR (B) (25% by mass of styrene), and 5% by mass of BR, the average styrene content is 39.5% by mass. 21% by mass (=(90×40+5×25)/(90+5)). The styrene content (average styrene content) of SBR may be 30% by mass or less, preferably 28% by mass or less, more preferably 15% by mass or more, more preferably 25% by mass or more. Within the above range, the effects of the present invention tend to be obtained more favorably.
The styrene content can be measured by the method described in Examples below.

When multiple SBRs are contained in the rubber composition, the "vinyl content" in the present invention means the average vinyl content of the multiple SBRs, and when only one type of SBR is contained, it means the vinyl content of the SBR. . The average vinyl content of SBR is {Σ(content of each SBR×vinyl content of each SBR)}/total content of all SBRs. For example, when the rubber component consists of 90% by mass of SBR (A) (30% by mass of vinyl), 5% by mass of SBR (B) (20% by mass of vinyl), and 5% by mass of BR, the average styrene content is 29.5% by mass. 47% by mass (=(90×30+5×20)/(90+5)). The vinyl content (average vinyl content) of SBR may be 50% by mass or more, preferably 52% by mass or more, and preferably 70% by mass or less, more preferably 60% by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.
The vinyl content (1,2-bonded butadiene unit content) can be measured by the method described in Examples below.

As SBR, for example, SBR manufactured and sold by Sumitomo Chemical Co., Ltd., JSR Co., Ltd., Asahi Kasei Co., Ltd., Nippon Zeon Co., Ltd., etc. can be used.

The SBR content in 100% by mass of the rubber component may be 10 to 50% by mass, preferably 20% by mass or more, and preferably 40% by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition contains BR as a rubber component.
The BR is not particularly limited, and BR with a high cis content, BR with a low cis content, BR containing syndiotactic polybutadiene crystals, and the like can be used. BR may be either non-modified BR or modified BR, and modified BR includes modified BR into which the aforementioned functional groups have been introduced. These may be used alone or in combination of two or more. The cis content of BR is preferably 90% by mass or more (preferably 95% by mass or more).
The cis content can be measured by infrared absorption spectrometry.

As BR, for example, products of Ube Industries, Ltd., JSR Corporation, Asahi Kasei Co., Ltd., Nippon Zeon Co., Ltd., etc. can be used.

The BR content in 100% by mass of the rubber component may be 10 to 50% by mass, preferably 20% by mass or more, and preferably 40% by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition contains an isoprene-based rubber as a rubber component.
The isoprene rubber includes natural rubber (NR), isoprene rubber (IR), modified NR, modified NR, modified IR, and the like. As NR, for example, those commonly used in the tire industry, such as SIR20, RSS#3, and TSR20, can be used. The IR is not particularly limited, and for example IR2200 or the like commonly used in the tire industry can be used. Modified NR includes deproteinized natural rubber (DPNR), high-purity natural rubber (UPNR), etc. Modified NR includes epoxidized natural rubber (ENR), hydrogenated natural rubber (HNR), grafted natural rubber, etc. Examples of modified IR include epoxidized isoprene rubber, hydrogenated isoprene rubber, grafted isoprene rubber, and the like. These may be used alone or in combination of two or more.

The content of isoprene-based rubber in 100% by mass of the rubber component may be 10 to 50% by mass, preferably 20% by mass or more, and preferably 40% by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

Rubber components that can be used in addition to SBR, BR, and isoprene rubber include acrylonitrile butadiene rubber (NBR), chloroprene rubber (CR), butyl rubber (IIR), and diene rubber such as styrene-isoprene-butadiene copolymer rubber (SIBR). rubber. These diene rubbers may be used alone or in combination of two or more.

The rubber composition contains silica.
Examples of silica include dry silica (anhydrous silicic acid) and wet silica (hydrated silicic acid), but wet silica is preferred because it contains many silanol groups. These may be used alone or in combination of two or more.

The nitrogen adsorption specific surface area (N ₂ SA) of silica is preferably 110 m ² /g or more, more preferably 150 m ² /g or more, still more preferably 200 m ² /g or more, particularly preferably 220 m ² /g or more, Also, it is preferably 300 m ² /g or less, more preferably 260 m ² /g or less. Within the above range, the effects of the present invention tend to be obtained more favorably.
The nitrogen adsorption specific surface area of silica is a value measured by the BET method according to ASTM D3037-81.

As silica, for example, products of Degussa, Rhodia, Tosoh Silica, Solvay Japan, Tokuyama, etc. can be used.

The content of silica relative to 100 parts by mass of the rubber component may be 80 parts by mass or more, preferably 85 parts by mass or more, more preferably 90 parts by mass or more, and more preferably 130 parts by mass or less. is 115 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition preferably contains a silane coupling agent together with silica. As a result, the effects of the present invention tend to be obtained more favorably.
The silane coupling agent is not particularly limited, and examples thereof include bis(3-triethoxysilylpropyl)tetrasulfide, bis(2-triethoxysilylethyl)tetrasulfide, bis(4-triethoxysilylbutyl)tetrasulfide, Bis (3-trimethoxysilylpropyl) tetrasulfide, bis (2-trimethoxysilylethyl) tetrasulfide, bis (2-triethoxysilylethyl) trisulfide, bis (4-trimethoxysilylbutyl) trisulfide, bis ( 3-triethoxysilylpropyl) disulfide, bis(2-triethoxysilylethyl) disulfide, bis(4-triethoxysilylbutyl) disulfide, bis(3-trimethoxysilylpropyl) disulfide, bis(2-trimethoxysilylethyl) ) disulfide, bis(4-trimethoxysilylbutyl) disulfide, 3-trimethoxysilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, 2-triethoxysilylethyl-N,N-dimethylthiocarbamoyl tetrasulfide, 3- Sulfides such as triethoxysilylpropyl methacrylate monosulfide, mercaptos such as 3-mercaptopropyltrimethoxysilane and 2-mercaptoethyltriethoxysilane, vinyls such as vinyltriethoxysilane and vinyltrimethoxysilane, and 3-aminopropyl Amino compounds such as triethoxysilane and 3-aminopropyltrimethoxysilane, glycidoxy compounds such as γ-glycidoxypropyltriethoxysilane and γ-glycidoxypropyltrimethoxysilane, 3-nitropropyltrimethoxysilane, 3- Examples include nitro-based solvents such as nitropropyltriethoxysilane, and chloro-based solvents such as 3-chloropropyltrimethoxysilane and 3-chloropropyltriethoxysilane. These may be used alone or in combination of two or more. Among these, sulfide-based and mercapto-based agents are preferred, and mercapto-based agents are more preferred, because the effects of the present invention can be obtained more favorably.

As the mercapto-based silane coupling agent, in addition to a compound having a mercapto group, a compound having a structure in which the mercapto group is protected by a protecting group (for example, a compound represented by the following formula (S1)) can also be used. .

（式中、Ｒ^１００１は－Ｃｌ、－Ｂｒ、－ＯＲ^１００６、－Ｏ（Ｏ＝）ＣＲ^１００６、－ＯＮ＝ＣＲ^１００６Ｒ^１００７、－ＯＮ＝ＣＲ^１００６Ｒ^１００７、－ＮＲ^１００６Ｒ^１００７及び－（ＯＳｉＲ^１００６Ｒ^１００７）_ｈ（ＯＳｉＲ^１００６Ｒ^１００７Ｒ^１００８）から選択される一価の基（Ｒ^１００６、Ｒ^１００７及びＲ^１００８は同一でも異なっていても良く、各々水素原子又は炭素数１～１８の一価の炭化水素基であり、ｈは平均値が１～４である。）であり、Ｒ^１００２はＲ^１００１、水素原子又は炭素数１～１８の一価の炭化水素基、Ｒ^１００３は－［Ｏ（Ｒ^１００９Ｏ）_ｊ］－基（Ｒ^１００９は炭素数１～１８のアルキレン基、ｊは１～４の整数である。）、Ｒ^１００４は炭素数１～１８の二価の炭化水素基、Ｒ^１００５は炭素数１～１８の一価の炭化水素基を示し、ｘ、ｙ及びｚは、ｘ＋ｙ＋２ｚ＝３、０≦ｘ≦３、０≦ｙ≦２、０≦ｚ≦１の関係を満たす数である。）

（式中、ｖは０以上の整数、ｗは１以上の整数である。Ｒ^１１は水素、ハロゲン、分岐若しくは非分岐の炭素数１～３０のアルキル基、分岐若しくは非分岐の炭素数２～３０のアルケニル基、分岐若しくは非分岐の炭素数２～３０のアルキニル基、又は該アルキル基の末端の水素が水酸基若しくはカルボキシル基で置換されたものを示す。Ｒ^１２は分岐若しくは非分岐の炭素数１～３０のアルキレン基、分岐若しくは非分岐の炭素数２～３０のアルケニレン基、又は分岐若しくは非分岐の炭素数２～３０のアルキニレン基を示す。Ｒ^１１とＲ^１２とで環構造を形成してもよい。） Particularly suitable mercapto-based silane coupling agents include a silane coupling agent represented by the following formula (S1), or a combination of a bonding unit A represented by the following formula (I) and a bonding unit B represented by the following formula (II). silane coupling agents containing.

(wherein R ¹⁰⁰¹ is -Cl, -Br, -OR ¹⁰⁰⁶ , -O(O=)CR ¹⁰⁰⁶ , -ON=CR ¹⁰⁰⁶ R ¹⁰⁰⁷ , -ON=CR ¹⁰⁰⁶ R ¹⁰⁰⁷ , -NR ¹⁰⁰⁶ R ¹⁰⁰⁷ and -( OSiR ¹⁰⁰⁶ R ¹⁰⁰⁷ ) _h Monovalent groups (R ¹⁰⁰⁶ , R ¹⁰⁰⁷ and R ¹⁰⁰⁸ ) selected from h (OSiR ¹⁰⁰⁶ R ¹⁰⁰⁷ R ¹⁰⁰⁸ ) may be the same or different and each represents a hydrogen atom or a is a monovalent hydrocarbon group, h has an average value of 1 to 4), R ¹⁰⁰² is R ¹⁰⁰¹ , a hydrogen atom or a monovalent hydrocarbon group with 1 to 18 carbon atoms, R ¹⁰⁰³ is - [O(R ¹⁰⁰⁹ O) _j ]—group (R ¹⁰⁰⁹ is an alkylene group having 1 to 18 carbon atoms and j is an integer of 1 to 4), R ¹⁰⁰⁴ is a divalent hydrocarbon having 1 to 18 carbon atoms group, R ¹⁰⁰⁵ represents a monovalent hydrocarbon group having 1 to 18 carbon atoms, x, y and z are in the relationship of x + y + 2z = 3, 0 ≤ x ≤ 3, 0 ≤ y ≤ 2, 0 ≤ z ≤ 1 is a number that satisfies

(Wherein, v is an integer of 0 or more, w is an integer of 1 or more, R ¹¹ is hydrogen, halogen, a branched or unbranched alkyl group having 1 to 30 carbon atoms, a branched or unbranched C 2 to A 30 alkenyl group, a branched or unbranched alkynyl group having 2 to 30 carbon atoms, or an alkyl group in which the terminal hydrogen is substituted with a hydroxyl group or a carboxyl group, where R ¹² is a branched or unbranched carbon number represents an alkylene group having 1 to 30 carbon atoms, a branched or unbranched alkenylene group having 2 to 30 carbon atoms, or a branched or unbranched alkynylene group having 2 to 30 carbon atoms, wherein R ¹¹ and R ¹² form a ring structure; may be used.)

In formula (S1), R ¹⁰⁰⁵ , R ¹⁰⁰⁶ , R ¹⁰⁰⁷ and R ¹⁰⁰⁸ are each independently selected from linear, cyclic or branched alkyl, alkenyl, aryl and aralkyl groups having 1 to 18 carbon atoms. It is preferably a group selected from the group consisting of When R ¹⁰⁰² is a monovalent hydrocarbon group having 1 to 18 carbon atoms, it is selected from the group consisting of linear, cyclic or branched alkyl groups, alkenyl groups, aryl groups and aralkyl groups. It is preferably a group. R ¹⁰⁰⁹ is preferably a linear, cyclic or branched alkylene group, particularly preferably a linear one. R ¹⁰⁰⁴ is, for example, an alkylene group having 1 to 18 carbon atoms, an alkenylene group having 2 to 18 carbon atoms, a cycloalkylene group having 5 to 18 carbon atoms, a cycloalkylalkylene group having 6 to 18 carbon atoms, or an arylene group having 6 to 18 carbon atoms. and an aralkylene group having 7 to 18 carbon atoms. Alkylene groups and alkenylene groups may be linear or branched, and cycloalkylene groups, cycloalkylalkylene groups, arylene groups and aralkylene groups have functional groups such as lower alkyl groups on their rings. You may have R ¹⁰⁰⁴ is preferably an alkylene group having 1 to 6 carbon atoms, more preferably a linear alkylene group such as methylene, ethylene, trimethylene, tetramethylene, pentamethylene and hexamethylene.

Specific examples of R ¹⁰⁰² , R ¹⁰⁰⁵ , R ¹⁰⁰⁶ , R ¹⁰⁰⁷ and R ¹⁰⁰⁸ in formula (S1) include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group and sec-butyl group, tert-butyl group, pentyl group, hexyl group, octyl group, decyl group, dodecyl group, cyclopentyl group, cyclohexyl group, vinyl group, propenyl group, allyl group, hexenyl group, octenyl group, cyclopentenyl group, cyclo hexenyl group, phenyl group, tolyl group, xylyl group, naphthyl group, benzyl group, phenethyl group, naphthylmethyl group and the like.
Examples of R ¹⁰⁰⁹ in the formula (S1) include a methylene group, an ethylene group, an n-propylene group, an n-butylene group, a hexylene group and the like as linear alkylene groups, and branched alkylene groups such as isopropylene group, isobutylene group, 2-methylpropylene group and the like.

Specific examples of the silane coupling agent represented by formula (S1) include 3-hexanoylthiopropyltriethoxysilane, 3-octanoylthiopropyltriethoxysilane, 3-decanoylthiopropyltriethoxysilane, 3- Lauroylthiopropyltriethoxysilane, 2-hexanoylthioethyltriethoxysilane, 2-octanoylthioethyltriethoxysilane, 2-decanoylthioethyltriethoxysilane, 2-lauroylthioethyltriethoxysilane, 3-hexanoy Luthiopropyltrimethoxysilane, 3-octanoylthiopropyltrimethoxysilane, 3-decanoylthiopropyltrimethoxysilane, 3-lauroylthiopropyltrimethoxysilane, 2-hexanoylthioethyltrimethoxysilane, 2-octanoylthio Ethyltrimethoxysilane, 2-decanoylthioethyltrimethoxysilane, 2-lauroylthioethyltrimethoxysilane and the like can be mentioned. These may be used alone or in combination of two or more. Among them, 3-octanoylthiopropyltriethoxysilane is particularly preferred.

In the silane coupling agent containing the linking unit A represented by the formula (I) and the linking unit B represented by the formula (II), the content of the linking unit A is preferably 30 mol% or more, more preferably 50 mol. % or more, preferably 99 mol % or less, more preferably 90 mol % or less. The content of the binding unit B is preferably 1 mol% or more, more preferably 5 mol% or more, still more preferably 10 mol% or more, preferably 70 mol% or less, more preferably 65 mol% or less, More preferably, it is 55 mol % or less. Also, the total content of the binding units A and B is preferably 95 mol % or more, more preferably 98 mol % or more, and particularly preferably 100 mol %.
In addition, the content of the bonding units A and B is the amount including the case where the bonding units A and B are positioned at the terminal of the silane coupling agent. When the bonding units A and B are located at the ends of the silane coupling agent, the form is not particularly limited as long as they form units corresponding to the formulas (I) and (II) representing the bonding units A and B. .

Halogen for R ¹¹ in formulas (I) and (II) includes chlorine, bromine, and fluorine. Examples of the branched or unbranched alkyl group having 1 to 30 carbon atoms include a methyl group and an ethyl group. Examples of the branched or unbranched alkenyl group having 2 to 30 carbon atoms include a vinyl group and a 1-propenyl group. Examples of the branched or unbranched alkynyl group having 2 to 30 carbon atoms include ethynyl group and propynyl group.

Examples of the branched or unbranched alkylene group having 1 to 30 carbon atoms for R ¹² in formulas (I) and (II) include ethylene group and propylene group. Examples of the branched or unbranched alkenylene group having 2 to 30 carbon atoms include vinylene group and 1-propenylene group. Examples of the branched or unbranched alkynylene group having 2 to 30 carbon atoms include an ethynylene group and a propynylene group.

In a silane coupling agent containing a bonding unit A represented by formula (I) and a bonding unit B represented by formula (II), the number of repetitions (v) of bonding unit A and the repetition number (w) of bonding unit B The total number of repetitions (v+w) is preferably in the range of 3-300.

When a silane coupling agent is contained, the content of the silane coupling agent is preferably 3 parts by mass or more, more preferably 5 parts by mass or more, and preferably 20 parts by mass with respect to 100 parts by mass of silica. Below, more preferably 15 mass parts or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition preferably contains carbon black. As a result, the effects of the present invention tend to be obtained more favorably.
Examples of carbon black include, but are not limited to, N134, N110, N220, N234, N219, N339, N330, N326, N351, N550 and N762. These may be used alone or in combination of two or more.

The cetyltrimethylammonium bromide (CTAB) specific surface area of carbon black is preferably 110 m ² /g or more, more preferably 160 m ² /g or more, still more preferably 170 m ² /g or more, and particularly preferably 180 m ² /g or more. Also, it is preferably 250 m ² /g or less, more preferably 200 m ² /g or less. Within the above range, the effects of the present invention tend to be obtained more favorably.
The CTAB specific surface area of carbon black is a value measured according to JIS K6217-3:2001.

The nitrogen adsorption specific surface area (N ₂ SA) of carbon black is preferably 120 m ² /g or more, more preferably 146 m ² /g or more, and is preferably 200 m ² /g or less, more preferably 180 m ² /g. It is below. Within the above range, the effects of the present invention tend to be obtained more favorably.
The N ₂ SA of carbon black is a value measured according to JIS K6217-2:2001.

The iodine adsorption amount (IA) of carbon black is preferably 110 mg/g or more, more preferably 170 mg/g or more, still more preferably 188 mg/g or more, and is preferably 250 mg/g or less, more preferably 200 mg/g. g or less. Within the above range, the effects of the present invention tend to be obtained more favorably.
The IA of carbon black is a value measured according to JIS K6217-1:2008.

As carbon black, for example, products of Asahi Carbon Co., Ltd., Cabot Japan Co., Ltd., Tokai Carbon Co., Ltd., Mitsubishi Chemical Co., Ltd., Lion Corporation, Shin Nikka Carbon Co., Ltd., Columbia Carbon Co., Ltd. can be used.

When carbon black is contained, the content of carbon black is preferably 1 part by mass or more, more preferably 5 parts by mass or more, and preferably 20 parts by mass or less, or more, with respect to 100 parts by mass of the rubber component. It is preferably 15 parts by mass or less. Within the above range, the effects of the present invention can be obtained more favorably.

The rubber composition preferably contains a terpene resin. As a result, the effects of the present invention tend to be obtained more favorably.
As the terpene-based resin, a polyterpene resin obtained by polymerizing a terpene compound, an aromatic modified terpene resin obtained by polymerizing a terpene compound and an aromatic compound, or the like can be used. Hydrogenated products thereof can also be used.

A polyterpene resin is a resin obtained by polymerizing a terpene compound. Terpene compounds are hydrocarbons represented by the composition (C ₅ H ₈ ) _n and their oxygen-containing derivatives, such as monoterpene (C ₁₀ H ₁₆ ), sesquiterpene (C ₁₅ H ₂₄ ), diterpene (C ₂₀ H ₃₂ ) and the like, which are compounds having a terpene as a basic skeleton, such as α-pinene, β-pinene, dipentene, limonene, myrcene, alloocimene, ocimene, α-phellandrene, α-terpinene, γ-terpinene, terpinolene , 1,8-cineole, 1,4-cineole, α-terpineol, β-terpineol, γ-terpineol and the like.

Examples of polyterpene resins include pinene resins, limonene resins, dipentene resins, and pinene/limonene resins made from the above-described terpene compounds. Among them, pinene resin is preferable. Pinene resins usually contain both α-pinene and β-pinene, which are in an isomer relationship. It is classified as α-pinene resin, which is mainly composed of pinene.

Examples of aromatic modified terpene resins include terpene phenol resins made from a terpene compound and a phenolic compound, and terpene styrene resins made from a terpene compound and a styrene compound. In addition, terpene phenol-styrene resins made from terpene compounds, phenolic compounds and styrene compounds can also be used.

The softening point of the terpene resin is preferably 100° C. or higher, more preferably 125° C. or higher, and preferably 160° C. or lower, more preferably 130° C. or lower. Within the above range, the effects of the present invention tend to be obtained more favorably.

When a terpene-based resin is contained, the content of the terpene-based resin is preferably 1 part by mass or more, more preferably 5 parts by mass or more, and still more preferably 10 parts by mass or more with respect to 100 parts by mass of the rubber component, Also, it is preferably 25 parts by mass or less, more preferably 20 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain other resins in addition to the terpene-based resin. Other resins are not particularly limited as long as they are commonly used in the tire industry, and include rosin-based resins, coumarone-indene resins, styrene-based resins, pt-butylphenolacetylene resins, acrylic-based resins, C5 resins, C9 resin etc. are mentioned. These may be used alone or in combination of two or more.

Commercial products of terpene resins and other resins include, for example, Maruzen Petrochemical Co., Ltd., Sumitomo Bakelite Co., Ltd., Yasuhara Chemical Co., Ltd., Tosoh Corporation, Rutgers Chemicals, BASF, Arizona Chemicals, Japan Products of Nuri Kagaku Co., Ltd., Nippon Shokubai Co., Ltd., JX Energy Co., Ltd., Arakawa Chemical Co., Ltd., Taoka Chemical Co., Ltd., etc. can be used.

The rubber composition may contain oil.
Oils include, for example, process oils, vegetable oils, or mixtures thereof. As the process oil, for example, paraffinic process oil, aromatic process oil, naphthenic process oil, or the like can be used. Vegetable oils include castor oil, cottonseed oil, linseed oil, rapeseed oil, soybean oil, palm oil, coconut oil, peanut oil, rosin, pine oil, pine tar, tall oil, corn oil, rice bran oil, safflower oil, sesame oil, Olive oil, sunflower oil, palm kernel oil, camellia oil, jojoba oil, macadamia nut oil, tung oil and the like. These may be used alone or in combination of two or more. Of these, process oils are preferable, and aromatic process oils are more preferable, because the effects of the present invention can be obtained satisfactorily.

When oil is contained, the content of oil is preferably 5 parts by mass or more, more preferably 15 parts by mass or more, and preferably 60 parts by mass or less, more preferably 100 parts by mass of the rubber component. It is 45 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain wax.
The wax is not particularly limited, and includes petroleum waxes such as paraffin wax and microcrystalline wax; natural waxes such as plant waxes and animal waxes; synthetic waxes such as polymers of ethylene and propylene. These may be used alone or in combination of two or more. Among them, petroleum waxes are preferred, and paraffin waxes are more preferred.

As the wax, for example, products of Ouchi Shinko Kagaku Kogyo Co., Ltd., Nippon Seiro Co., Ltd., Seiko Kagaku Co., Ltd., etc. can be used.

When wax is contained, the wax content is preferably 1 part by mass or more, more preferably 2 parts by mass or more, and preferably 20 parts by mass or less, more preferably It is 10 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain an antioxidant.
Examples of anti-aging agents include naphthylamine-based anti-aging agents such as phenyl-α-naphthylamine; diphenylamine-based anti-aging agents such as octylated diphenylamine and 4,4′-bis(α,α′-dimethylbenzyl)diphenylamine; -Isopropyl-N'-phenyl-p-phenylenediamine, N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine, N,N'-di-2-naphthyl-p-phenylenediamine, etc. p-phenylenediamine-based antioxidants; quinoline-based antioxidants such as polymers of 2,2,4-trimethyl-1,2-dihydroquinoline; 2,6-di-t-butyl-4-methylphenol, monophenolic anti-aging agents such as styrenated phenol; inhibitors and the like. These may be used alone or in combination of two or more. Among them, p-phenylenediamine antioxidants and quinoline antioxidants are preferred.

As the anti-aging agent, products of Seiko Chemical Co., Ltd., Sumitomo Chemical Co., Ltd., Ouchi Shinko Kagaku Kogyo Co., Ltd., Flexis, etc. can be used, for example.

When an anti-aging agent is contained, the content of the anti-aging agent is preferably 1 part by mass or more, more preferably 3.5 parts by mass or more, and preferably 10 parts by mass with respect to 100 parts by mass of the rubber component. parts or less, more preferably 8 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain stearic acid.
Conventional stearic acid can be used, for example, NOF Corporation, NOF Corporation, Kao Corporation, Wako Pure Chemical Industries, Ltd., Chiba Fatty Acids Co., Ltd. products can be used.

When stearic acid is contained, the content of stearic acid is preferably 1 part by mass or more, more preferably 2 parts by mass or more, and preferably 10 parts by mass or less, or more, relative to 100 parts by mass of the rubber component. It is preferably 5 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain zinc oxide.
As the zinc oxide, conventionally known ones can be used, for example, products of Mitsui Kinzoku Mining Co., Ltd., Toho Zinc Co., Ltd., Hakusui Tech Co., Ltd., Seido Chemical Industry Co., Ltd., Sakai Chemical Industry Co., Ltd., etc. can be used.

When zinc oxide is contained, the content of zinc oxide is preferably 1 part by mass or more, more preferably 2 parts by mass or more, and preferably 10 parts by mass or less, or more, relative to 100 parts by mass of the rubber component. It is preferably 5 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain sulfur.
Sulfur includes powdered sulfur, precipitated sulfur, colloidal sulfur, insoluble sulfur, highly dispersible sulfur, soluble sulfur and the like commonly used in the rubber industry. These may be used alone or in combination of two or more.

As sulfur, for example, products of Tsurumi Chemical Industry Co., Ltd., Karuizawa Io Co., Ltd., Shikoku Kasei Kogyo Co., Ltd., Flexis Co., Ltd., Nippon Kantan Kogyo Co., Ltd., Hosoi Chemical Industry Co., Ltd., etc. can be used.

When sulfur is contained, the content of sulfur is preferably 0.5 parts by mass or more, more preferably 1.5 parts by mass or more, and preferably 10 parts by mass or less with respect to 100 parts by mass of the rubber component. , more preferably 5 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

The rubber composition may contain a vulcanization accelerator.
Vulcanization accelerators include thiazole-based vulcanization accelerators such as 2-mercaptobenzothiazole, di-2-benzothiazolyl disulfide, and N-cyclohexyl-2-benzothiazylsulfenamide; tetramethylthiuram disulfide (TMTD ), tetrabenzyl thiuram disulfide (TBzTD), tetrakis (2-ethylhexyl) thiuram disulfide (TOT-N) and other thiuram vulcanization accelerators; N-cyclohexyl-2-benzothiazolesulfenamide, Nt-butyl- 2-benzothiazolylsulfenamide, N-oxyethylene-2-benzothiazolesulfenamide, N-oxyethylene-2-benzothiazolesulfenamide, N,N'-diisopropyl-2-benzothiazolesulfenamide, etc. and guanidine-based vulcanization accelerators such as diphenylguanidine, diorthotolylguanidine and orthotolylbiguanidine. These may be used alone or in combination of two or more. Among these, sulfenamide-based vulcanization accelerators and guanidine-based vulcanization accelerators are preferred because the effects of the present invention can be obtained more favorably.

When a vulcanization accelerator is contained, the content of the vulcanization accelerator is preferably 1 part by mass or more, more preferably 3.5 parts by mass or more, relative to 100 parts by mass of the rubber component. It is 10 parts by mass or less, more preferably 8 parts by mass or less. Within the above range, the effects of the present invention tend to be obtained more favorably.

In addition to the above components, the rubber composition contains additives commonly used in the tire industry, such as organic peroxides; fillers such as calcium carbonate, talc, alumina, clay, aluminum hydroxide, and mica. ; and the like may be further added. The content of these additives is preferably 0.1 to 200 parts by mass with respect to 100 parts by mass of the rubber component.

The above rubber composition can be produced, for example, by kneading each of the above components using a rubber kneading apparatus such as an open roll mixer or a Banbury mixer, followed by vulcanization.

As for the kneading conditions, the kneading temperature is usually 100 to 180°C, preferably 120 to 170°C in the base kneading step in which additives other than the vulcanizing agent and the vulcanization accelerator are kneaded. In the finishing kneading step of kneading the vulcanizing agent and the vulcanization accelerator, the kneading temperature is usually 120°C or lower, preferably 85 to 110°C. A composition obtained by kneading a vulcanizing agent and a vulcanization accelerator is usually subjected to vulcanization treatment such as press vulcanization. The vulcanization temperature is generally 140-190°C, preferably 150-185°C. Vulcanization time is usually 5 to 15 minutes.

The above rubber composition is suitably used for treads (cap treads), but is used for members other than treads, such as sidewalls, base treads, undertreads, clinch apex, bead apex, breaker cushion rubber, and carcass cord coating. It may be used for rubber, insulation, chafer, inner liner, etc., and for side reinforcing layers of run-flat tires.

The pneumatic tire of the present invention is manufactured by a normal method using the rubber composition.
That is, the rubber composition is extruded according to the shape of each tire member of the tread in an unvulcanized stage, and molded together with other tire members on a tire molding machine by a normal method to obtain an unvulcanized rubber composition. Form a vulcanized tire. A tire is obtained by heating and pressurizing this unvulcanized tire in a vulcanizer.

The pneumatic tire can be used for passenger car tires, truck and bus tires, motorcycle tires, high-performance tires, etc., and is particularly suitable for passenger car tires.

EXAMPLES The present invention will be specifically described based on Examples, but the present invention is not limited to these.
Various chemicals used in the examples are described below.
SBR1: Modified SBR synthesized in Production Example 1 below (styrene content: 25% by mass, vinyl content: 60% by mass, Mw: 150,000)
SBR2: Buna VSL 5228-2 manufactured by LANXESS (styrene content: 28% by mass, vinyl content: 52% by mass, oil content of 37.5 parts by mass per 100 parts by mass of rubber solids)
BR: BR730 manufactured by JSR Corporation (cis content: 95% by mass)
NR: TSR20
Carbon black 1: prototype (CTAB: 180 m ² /g, N ₂ SA: 177 m ² /g, IA: 188 mg/g)
Carbon black 2: N134 (CTAB: 135 m ² /g)
Silica 1: Ultrasil 9000GR (N ₂ SA: 240 m ² /g) manufactured by Evonik Degussa
Silica 2: Ultrasil VN3 from Evonik Degussa (N ₂ SA: 167 m ² /g)
Silica 3: ZEOSIL 1115MP from Rhodia (N ₂ SA: 115 m ² /g)
Silane coupling agent 1: Momentive NXT-Z45 (copolymer of bonding unit A and bonding unit B (bonding unit A: 55 mol%, bonding unit B: 45 mol%))
Silane coupling agent 2: NXT (3-octanoylthiopropyltriethoxysilane) manufactured by Momentive
Oil: VIVATEC500 (TDAE oil) manufactured by H&R
Terpene resin: YS resin TO125 (aromatic modified terpene resin, softening point: 125°C) manufactured by Yasuhara Chemical Co., Ltd.
Wax: Ozoace 0355 manufactured by Nippon Seiro Co., Ltd.
Antiaging agent 1: Nocrack 6C (N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine) manufactured by Ouchi Shinko Kagaku Kogyo Co., Ltd.
Antiaging agent 2: Nocrac RD (poly (2,2,4-trimethyl-1,2-dihydroquinoline)) manufactured by Ouchi Shinko Kagaku Kogyo Co., Ltd.
Stearic acid: stearic acid "Tsubaki" manufactured by NOF Corporation
Zinc oxide: Zinc white No. 1 manufactured by Mitsui Mining & Smelting Co., Ltd. Sulfur: Powdered sulfur manufactured by Tsurumi Chemical Co., Ltd. Vulcanization accelerator 1: Noccellar CZ (N-cyclohexyl-2 manufactured by Ouchi Shinko Kagaku Kogyo Co., Ltd.) -benzothiazolylsulfenamide)
Vulcanization accelerator 2: Noxceler D (1,3-diphenylguanidine) manufactured by Ouchi Shinko Kagaku Kogyo Co., Ltd.

(Production example 1)
A nitrogen purged autoclave reactor was charged with cyclohexane, tetrahydrofuran, styrene, and 1,3-butadiene. After adjusting the temperature of the contents of the reactor to 20° C., n-butyllithium was added to initiate the polymerization. Polymerization was carried out under adiabatic conditions, and the maximum temperature reached 85°C. When the polymerization conversion rate reached 99%, 1,3-butadiene was added and the mixture was further polymerized for 5 minutes, and then 3-diethylaminopropyltrimethoxysilane was added as a modifier to carry out the reaction. After completion of the polymerization reaction, 2,6-di-tert-butyl-p-cresol was added. Then, the solvent was removed by steam stripping and dried with a hot roll adjusted to 110° C. to obtain SBR1.

(Analysis of SBR)
Structural identification of SBR (measurement of styrene content and vinyl content) was performed using a JNM-ECA series device manufactured by JEOL Ltd. For the measurement, 0.1 g of polymer was dissolved in 15 ml of toluene, slowly poured into 30 ml of methanol to reprecipitate, and then dried under reduced pressure.

(Examples and Comparative Examples)
According to the formulation shown in Table 1, using a 1.7 L Banbury mixer manufactured by Kobe Steel, Ltd., materials other than sulfur and vulcanization accelerator were kneaded at 150 ° C. for 5 minutes, and the kneaded product was obtained. Obtained. Next, sulfur and a vulcanization accelerator were added to the resulting kneaded material, and the mixture was kneaded at 80° C. for 5 minutes using an open roll to obtain an unvulcanized rubber composition. The resulting unvulcanized rubber composition was molded into a tread shape, laminated with other tire members to form an unvulcanized tire, press-vulcanized at 150 ° C. for 12 minutes, and a test tire ( Size: 195/65R15) was manufactured. The obtained test tires were used for the following evaluations, and the results are shown in Table 1.
In Table 1, the rubber content in the oil-extended rubber is listed in the rubber column, and the oil content in the oil-extended rubber is added to the oil column.

(Low fuel consumption)
Using a rolling resistance tester, measure the rolling resistance when running each test tire with a rim (15 × 6 JJ), internal pressure (230 kPa), load (3.43 kN), speed (80 km / h), It was indicated as an index with Comparative Example 2 as 100 (fuel efficiency index). A larger index indicates better fuel efficiency. In this embodiment, the target is 200 or more.

(wet grip performance)
Each test tire was mounted on all wheels of a vehicle (made in Japan FF 2000cc), and the braking distance from an initial speed of 100 km / h on a wet asphalt road surface was obtained. grip performance index). A larger index indicates a shorter braking distance and better wet grip performance. In this embodiment, the target is 400 or more.

(dry grip performance)
Each test tire was mounted on all wheels of a vehicle (made in Japan FF 2000cc), and the actual vehicle was run for 10 laps on a dry asphalt test course. The test place was the Okayama test course of Sumitomo Rubber Industries, Ltd., and the temperature was 20 to 25°C. Then, a test driver evaluated the stability of the control during steering at that time, and the result was expressed as an index based on Comparative Example 2 being 100 (dry grip performance index). A larger index indicates better grip performance on a dry road surface. In this embodiment, the target is 50 or more.

Claims (5)

a rubber component having a styrene-butadiene rubber content of 10 to 40% by mass, a butadiene rubber content of 10 to 50% by mass, and an isoprene-based rubber content of 10 to 50% by mass;
silica having a content of 80 parts by mass or more with respect to 100 parts by mass of the rubber component;
containing a mercapto-based silane coupling agent,
The styrene-butadiene rubber has a styrene content of 30% by mass or less and a vinyl content of 50% by mass or more,
A rubber composition for tires in which the silica has a nitrogen adsorption specific surface area of 200 m ² /g or more (excluding a rubber composition for tires containing a polysulfide compound represented by the following formulas (I) and/or (II)).

(In the formula, R ¹ is the same or different and represents a monovalent hydrocarbon group having 3 to 15 carbon atoms which may have a substituent. n represents an integer of 2 to 6.)

(In the formula, R ² is the same or different and represents a divalent hydrocarbon group having 3 to 15 carbon atoms which may have a substituent. m represents an integer of 2 to 6.) The mercapto-based silane coupling agent includes a silane coupling agent represented by the following formula (S1), and a bonding unit A represented by the following formula (I) and a bonding unit B represented by the following formula (II). The rubber composition for tires according to claim 1, which is at least one selected from the group consisting of silane coupling agents.

(wherein R ¹⁰⁰¹ is -Cl, -Br, -OR ¹⁰⁰⁶ , -O(O=)CR ¹⁰⁰⁶ , -ON=CR ¹⁰⁰⁶ R ¹⁰⁰⁷ , -ON=CR ¹⁰⁰⁶ R ¹⁰⁰⁷ , -NR ¹⁰⁰⁶ R ¹⁰⁰⁷ and -( OSiR ¹⁰⁰⁶ R ¹⁰⁰⁷ ) _h Monovalent groups (R ¹⁰⁰⁶ , R ¹⁰⁰⁷ and R ¹⁰⁰⁸ ) selected from h (OSiR ¹⁰⁰⁶ R ¹⁰⁰⁷ R ¹⁰⁰⁸ ) may be the same or different and each represents a hydrogen atom or a is a monovalent hydrocarbon group, h has an average value of 1 to 4), R ¹⁰⁰² is R ¹⁰⁰¹ , a hydrogen atom or a monovalent hydrocarbon group with 1 to 18 carbon atoms, R ¹⁰⁰³ is - [O(R ¹⁰⁰⁹ O) _j ]—group (R ¹⁰⁰⁹ is an alkylene group having 1 to 18 carbon atoms and j is an integer of 1 to 4), R ¹⁰⁰⁴ is a divalent hydrocarbon having 1 to 18 carbon atoms group, R ¹⁰⁰⁵ represents a monovalent hydrocarbon group having 1 to 18 carbon atoms, x, y and z are in the relationship of x + y + 2z = 3, 0 ≤ x ≤ 3, 0 ≤ y ≤ 2, 0 ≤ z ≤ 1 is a number that satisfies

(Wherein, v is an integer of 0 or more, w is an integer of 1 or more, R ¹¹ is hydrogen, halogen, a branched or unbranched alkyl group having 1 to 30 carbon atoms, a branched or unbranched C 2 to A 30 alkenyl group, a branched or unbranched alkynyl group having 2 to 30 carbon atoms, or an alkyl group in which the terminal hydrogen is substituted with a hydroxyl group or a carboxyl group, where R ¹² is a branched or unbranched carbon number represents an alkylene group having 1 to 30 carbon atoms, a branched or unbranched alkenylene group having 2 to 30 carbon atoms, or a branched or unbranched alkynylene group having 2 to 30 carbon atoms, wherein R ¹¹ and R ¹² form a ring structure; may be used.) The rubber composition for tires according to claim 1 or 2, comprising carbon black having a cetyltrimethylammonium bromide specific surface area of 160 m ² /g or more. The rubber composition for tires according to any one of claims 1 to 3 , wherein the silica has a nitrogen adsorption specific surface area of 220 m ² /g or more. A pneumatic tire produced using the rubber composition according to any one of claims 1 to 4 .