JP6950473B2 - Watch parts and watches - Google Patents
Watch parts and watches Download PDFInfo
- Publication number
- JP6950473B2 JP6950473B2 JP2017216498A JP2017216498A JP6950473B2 JP 6950473 B2 JP6950473 B2 JP 6950473B2 JP 2017216498 A JP2017216498 A JP 2017216498A JP 2017216498 A JP2017216498 A JP 2017216498A JP 6950473 B2 JP6950473 B2 JP 6950473B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- timepiece
- region
- metallic luster
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、時計用部品および時計に関する。 The present invention relates to timepiece parts and timepieces.
時計は、実用品としての機能が求められるとともに、装飾品として優れた審美性(美的外観)が要求される。 Watches are required to function as practical products and to have excellent aesthetics (aesthetic appearance) as ornaments.
このため、文字板、ケース等の時計用部品には、優れた質感を有する貴金属材料が用いられている(例えば、特許文献1参照)。 For this reason, precious metal materials having an excellent texture are used for watch parts such as dials and cases (see, for example, Patent Document 1).
しかしながら、貴金属材料は、一般に高価であり、また、埋蔵量等の関係から、過剰な使用を抑制することが求められている。 However, precious metal materials are generally expensive, and it is required to suppress excessive use due to the reserves and the like.
本発明の目的は、貴金属を主材料として使用しなくても、優れた外観を有する時計用部品を提供すること、また、前記時計用部品を備えた時計を提供することにある。 An object of the present invention is to provide a timepiece component having an excellent appearance without using a precious metal as a main material, and to provide a timepiece including the timepiece part.
このような目的は、下記の本発明により達成される。
本発明の時計用部品は、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含む第1の材料で構成され、金属光沢を呈する金属光沢部と、
3以上8以下の金属酸化物層の多層膜で構成され、色調を調整する機能を有する調色膜とを備えることを特徴とする。
Such an object is achieved by the following invention.
The watch component of the present invention is composed of a first material containing Ti nitride or carbide, Cr nitride or carbide, or a metallic material, and has a metallic luster portion exhibiting metallic luster.
It is characterized by being composed of a multilayer film of 3 or more and 8 or less metal oxide layers , and including a toning film having a function of adjusting a color tone.
これにより、貴金属を主材料として使用しなくても、優れた外観を有する時計用部品を提供することができる。 Thereby, it is possible to provide a timepiece component having an excellent appearance without using a precious metal as a main material.
本発明の時計用部品では、前記金属光沢部は、前記第1の材料で構成された基材であることが好ましい。 In the watch component of the present invention, the metallic luster portion is preferably a base material made of the first material.
これにより、時計用部品の構造をより単純なものとすることができ、時計用部品の生産性をより優れたものとすることができる。 As a result, the structure of the timepiece component can be made simpler, and the productivity of the timepiece part can be made more excellent.
本発明の時計用部品では、前記金属光沢部は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まない材料で構成された基材上に設けられた被膜であることが好ましい。 In the watch component of the present invention, the metallic luster is formed on a base material composed of a material substantially free of Ti nitrides and carbides, Cr nitrides and carbides, and a metal material. It is preferably a provided coating.
これにより、基材の構成材料等の選択の幅が広がり、時計用部品の成形方法の選択の幅、時計における時計用部品の配置部位の選択の幅等をより広いものとすることができる。また、時計用部品全体としての、金属材料の使用量をより少ないものとすることができる。 As a result, the range of selection of the constituent materials of the base material and the like can be expanded, and the range of selection of the molding method of the timepiece component, the range of selection of the arrangement portion of the timepiece component in the timepiece, and the like can be made wider. In addition, the amount of metal material used for the entire timepiece component can be reduced.
本発明の時計用部品では、前記金属光沢部は、30nm以上の厚さを有するものであることが好ましい。 In the watch component of the present invention, the metallic luster portion preferably has a thickness of 30 nm or more.
これにより、時計用部品全体としての光沢感、審美性をより優れたものとすることができる。 As a result, the glossiness and aesthetics of the entire timepiece component can be improved.
本発明の時計用部品では、前記調色膜は、Ta2O5、SiO2、TiO2、Al2O3、ZrO2、Nb2O5およびHfO2よりなる群から選択される少なくとも1種を含む材料で構成された層を有するものであることが好ましい。 In the watch component of the present invention, the toning film is at least one selected from the group consisting of Ta 2 O 5 , SiO 2 , TiO 2 , Al 2 O 3 , ZrO 2 , Nb 2 O 5 and HfO 2. It is preferable that it has a layer made of a material containing.
これにより、時計用部品の審美性をより優れたものとすることができるとともに、時計用部品全体として表現することのできる色調の範囲をより広いものとすることができる。また、これらの化合物は、各種の金属酸化物の中でも化学的安定性が特に高い材料であり、時計用部品全体としての外観の安定性、耐久性をより優れたものとすることができる。 As a result, the aesthetics of the timepiece parts can be made more excellent, and the range of color tones that can be expressed as the whole timepiece parts can be made wider. Further, these compounds are materials having particularly high chemical stability among various metal oxides, and can make the appearance stability and durability of the entire timepiece component more excellent.
本発明の時計用部品では、前記調色膜の厚さは、100nm以上2000nm以下であることが好ましい。 In the timepiece component of the present invention, the thickness of the toning film is preferably 100 nm or more and 2000 nm or less.
これにより、時計用部品の審美性をより優れたものとすることができ、表現することができる色範囲(色再現域)をより広いものとすることができるとともに、調色膜の不本意な剥離等をより効果的に防止することができ、時計用部品の耐久性、信頼性をより優れたものとすることができ、また、時計用部品の生産性をより優れたものとすることができる。 As a result, the aesthetics of the watch parts can be made more excellent, the color range (color reproduction range) that can be expressed can be made wider, and the toning film is unwilling. It is possible to prevent peeling and the like more effectively, to improve the durability and reliability of watch parts, and to improve the productivity of watch parts. can.
本発明の時計用部品では、前記調色膜を構成する各層の厚さは、それぞれ、10nm以上300nm以下であることが好ましい。 In the timepiece component of the present invention, the thickness of each layer constituting the toning film is preferably 10 nm or more and 300 nm or less, respectively.
これにより、時計用部品の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜の不本意な剥離等をより効果的に防止することができ、時計用部品の耐久性、信頼性をより優れたものとすることができる。 As a result, the aesthetics of the watch parts can be improved, the color reproduction range can be widened, and the unintentional peeling of the toning film can be prevented more effectively. This makes it possible to improve the durability and reliability of watch parts.
本発明の時計用部品では、前記金属光沢部は、Cr、Alの一方を含む材料で構成されたものであることが好ましい。 In the watch component of the present invention, the metallic luster portion is preferably made of a material containing either Cr or Al.
これにより、時計用部品全体として、青みがかった高級感のある金属光沢を好適に得ることができる。 As a result, it is possible to preferably obtain a bluish and high-quality metallic luster as the entire timepiece component.
本発明の時計用部品では、前記金属光沢部は、第1の領域と、前記第1の領域よりも前記調色膜側に、前記第1の領域と重ね合わせて層状に設けられた第2の領域とを有するものであり、
前記第2の領域は、前記第1の領域とは異なる材料で構成されたものであることが好ましい。
In the timepiece component of the present invention, the metallic luster portion is provided in a layered manner on the first region and on the toning film side of the first region so as to overlap the first region. Has an area of
The second region is preferably made of a material different from that of the first region.
これにより、微妙な色調整を行うことができ、時計用部品全体としての色再現域をより広いものとすることができ、時計用部品の審美性をより優れたものとすることができる。また、全体としての金属の使用量をさらに抑制しつつ、時計用部品の審美性を優れたものとすることができる。 As a result, delicate color adjustment can be performed, the color reproduction range of the entire timepiece component can be made wider, and the aesthetic appearance of the timepiece part can be made more excellent. In addition, the aesthetics of the timepiece parts can be improved while further suppressing the amount of metal used as a whole.
本発明の時計用部品では、前記第1の領域がTiNで構成されたものであり、
前記第2の領域がTi、Cr、AlまたはFeを含む金属材料で構成されたものであることが好ましい。
これにより、高級感が特に高い金色を表現することができる。
In the timepiece component of the present invention, the first region is made of TiN.
It is preferable that the second region is made of a metal material containing Ti, Cr, Al or Fe.
As a result, it is possible to express a golden color with a particularly high sense of quality.
本発明の時計用部品では、前記第1の領域は、層状に設けられたものであることが好ましい。 In the timepiece component of the present invention, the first region is preferably provided in a layered manner.
これにより、基材、第1の領域の構成材料等の選択の幅が広がり、例えば、鋳造等が困難な材料でも好適に用いることができる。また、時計用部品全体としての金属材料の使用量をより少ないものとすることができる。 As a result, the range of selection of the base material, the constituent material of the first region, and the like is widened, and for example, even a material that is difficult to cast or the like can be suitably used. In addition, the amount of metal material used for the entire timepiece component can be reduced.
本発明の時計用部品は、風防ガラス、文字板、ケースまたはバンドであることが好ましい。 The watch component of the present invention is preferably a windshield, dial, case or band.
これらの部品(時計用部品)は、時計全体の外観に大きな影響を与えるものであるため、これらの部品に本発明が適用されることにより、時計全体としての審美性をより優れたものとすることができる。 Since these parts (watch parts) have a great influence on the appearance of the entire watch, the aesthetics of the watch as a whole can be improved by applying the present invention to these parts. be able to.
本発明の時計は、本発明の時計用部品を備えたことを特徴とする。
これにより、貴金属を主材料として使用しなくても、優れた外観を有する時計を提供することができる。
The timepiece of the present invention is characterized by comprising the parts for the timepiece of the present invention.
This makes it possible to provide a timepiece having an excellent appearance without using a precious metal as a main material.
以下、添付する図面を参照しつつ、好適な実施形態について詳細な説明をする。
《時計用部品》
まず、本発明の時計用部品について説明する。
Hereinafter, preferred embodiments will be described in detail with reference to the accompanying drawings.
《Watch parts》
First, the timepiece component of the present invention will be described.
[第1実施形態]
図1は、本発明の時計用部品の第1実施形態を模式的に示す断面図である。
[First Embodiment]
FIG. 1 is a cross-sectional view schematically showing a first embodiment of a timepiece component of the present invention.
時計用部品10は、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含む第1の材料で構成され、金属光沢を呈する金属光沢部1と、金属酸化物の多層膜(複数の金属酸化物層51の積層体)で構成され、時計用部品10全体としての色調を調整する機能を有する調色膜5とを備えている。
The
なお、本発明において、「窒化物」は、窒素(N)を含む金属化合物のことを指し、炭窒化物等を含む。また、本発明において、「炭化物」は、炭素(C)を含む金属化合物のことを指し、炭窒化物等を含む。 In the present invention, "nitride" refers to a metal compound containing nitrogen (N), and includes carbonitride and the like. Further, in the present invention, "carbide" refers to a metal compound containing carbon (C), and includes carbonitride and the like.
金属光沢部1は、金属光沢感を呈する部位である。
調色膜5は、金属光沢部1の金属光沢感を生かしつつ、時計用部品10全体としての色調を調整する機能を有するものである。
そして、観察者の視点は、図1中の上側(時計用部品10の調色膜5が設けられた面側(時計用部品10の金属光沢部1よりも調色膜5に近い側))である(後述する図2〜図6についても同様)。
The
The
Then, the viewpoint of the observer is the upper side in FIG. 1 (the surface side of the
このような構成により、貴金属を主材料として使用しなくても、優れた外観(金属光沢を呈する外観)、特に高級感を有する時計用部品10を提供することができる。また、貴金属を使用する場合であっても、その使用量を抑制することができる。より具体的には、例えば、貴金属を実質的に含まなくても貴金属材料が呈するような高級感のある外観を得ることができる。また、貴金属は、一般に、傷等が付きやすいという特徴があるが、上記のような構成とすることにより、時計用部品10全体として耐擦性等を優れたものとすることができる。特に、時計用部品10では、優れた外観と、優れた耐擦性とを両立することができる。また、金属材料だけでは、表現することが困難な青みがかった光沢感のある金属感や、赤みがかった光沢感のある金属感等、様々な色調を表現することができ、単に金属材料(特に、貴金属材料)のみを用いた場合には得ることのできない色調の外観を得ることができる。すなわち、表現することができる色範囲(色再現域)をより広いものとすることができる。また、金属光沢部1が金属材料(例えば、化学的安定性が比較的低く、酸化等の反応が進行しやすい金属材料等)で構成されたものであっても、化学的安定性に優れた酸化物で構成された調色膜5で被覆することにより、時計用部品10全体としての外観の安定性、耐久性が向上する。
With such a configuration, it is possible to provide the
特に、本実施形態の時計用部品10では、金属光沢部1は、第1の材料で構成された基材2である。言い換えると、本実施形態の時計用部品10は、金属光沢部1として機能する基材2と、調色膜5とを備えている。
In particular, in the
これにより、時計用部品10の構造をより単純なものとすることができ、時計用部品10の生産性をより優れたものとすることができる。
As a result, the structure of the
≪基材(金属光沢部)≫
本実施形態において、基材2(金属光沢部1)は、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含む第1の材料で構成されたものである。
≪Base material (metallic luster) ≫
In the present embodiment, the base material 2 (metallic luster portion 1) is made of a first material containing a Ti nitride or carbide, a Cr nitride or carbide, or a metal material.
金属光沢部1を構成する金属材料としては、貴金属より卑な金属であるのが好ましく、例えば、Al、Ti、V、Cr、Fe、Co、Ni、Cu、Zn、Zr、Nb、Mo、In、Sn、Hf、Ta、W、Bi、Mgや、これらのうち少なくとも1種を含む合金等が挙げられる。なお、少量の貴金属を含むことを妨げるものではない。
The metal material constituting the metal
特に、金属光沢部1が、Cr、Alの一方を含む材料で構成されたものであると、時計用部品10全体として、青みがかった高級感のある金属光沢を好適に得ることができる。
In particular, when the
また、金属光沢部1が、TiまたはCrの窒化物で構成されたものであると、時計用部品10全体として、高級感のある金色の外観(単体としてのAuに類似した外観)を好適に得ることができる。
Further, when the
また、金属光沢部1が、Tiの炭化物で構成されたものであると、時計用部品10全体として、高級感のある黒味を帯びた色の外観を好適に得ることができる。特に、時計用部品10全体として、従来では、表現が特に困難であった黒味がかった赤色や黒味がかった青色等の外観を得ることができる。
Further, when the
金属光沢部1がTiの炭窒化物を含む材料で構成されている場合、例えば、ピンクゴールドに類似の色調を好適に表現することができる。
When the
金属光沢部1は、貴金属元素(Au、Ag、Pt、Pd、Rh、Ir、Ru、Os)の含有率が十分に低いものであるのが好ましく、金属光沢部1中における貴金属元素の含有率(複数種の貴金属元素を含む場合はこれらの含有率の総和)は、1.0質量%以下であるのが好ましく、0.5質量%以下であるのがより好ましく、0.1質量%以下であるのがさらに好ましい。
The metallic
これにより、貴金属を主材料として使用しなくても、優れた外観が得られるという本発明による効果がより顕著に発揮される。 As a result, the effect of the present invention that an excellent appearance can be obtained without using a precious metal as a main material is more remarkably exhibited.
なお、金属光沢部1は、金属光沢感を有するものであれば、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料以外の成分を含むものであってもよい。ただし、金属光沢部1中における前記の材料(Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料)以外の成分の含有率は、5質量%以下であるのが好ましく、1質量%以下であるのがより好ましい。
The
基材2は、各部位で均一な組成を有するものであってもよいし、組成の異なる部位を有するものであってもよい。
The
金属光沢部1は、30nm以上の厚さを有するものであるのが好ましく、40nm以上の厚さを有するものであるのがより好ましく、50nm以上の厚さを有するものであるのがさらに好ましい。
The
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができる。
As a result, the glossiness and aesthetics of the
基材2の形状、大きさは、特に限定されず、通常、時計用部品10の形状、大きさに基づいて決定される。また、基材2には、文字、数字、記号、模様等の凹凸パターンが設けられていてもよい。
The shape and size of the
基材2は、例えば、表面に、鏡面加工、スジ目加工、梨地加工等の表面加工が施されたものであってもよい。
The
これにより、時計用部品10の表面の光沢具合にバリエーションを持たせることが可能となり、時計用部品10の審美性をさらに向上させることができる。鏡面加工は、例えば、周知の研磨方法を用いて行うことができ、例えば、バフ(羽布)研磨、バレル研磨、その他の機械研磨等を採用することができる。
As a result, the glossiness of the surface of the
また、このような表面加工を施した基材2を用いて製造される時計用部品10は、後に詳述する各種の膜に対して表面加工を直接施すことにより得られるものに比べて、ギラツキ等が抑制されたものとなり、特に審美性に優れたものとなる。また、後に詳述する各種の膜は通常比較的薄いものであり、当該膜に対して表面加工を直接施す場合には、当該表面加工を施す際に当該膜にカケ、剥離等の欠陥を生じ易く、時計用部品10の製造の歩留りが著しく低下する場合があるが、基材2に対して表面加工を行うことにより、このような問題の発生も効果的に防止することができ、かつ比較的膜厚が薄い為表面加工の審美性を損なうこともない。また、基材2に対する表面加工は、後に詳述する各種の膜に対する表面加工に比べて、温和な条件で容易に行うことができる。
Further, the
≪調色膜≫
調色膜5は、金属酸化物の多層膜で構成されたものである。言い換えると、調色膜5は、複数の金属酸化物層51を備える積層体である。
≪Toning film≫
The
調色膜5(金属酸化物層51)は、金属材料の酸化物で構成されたものであればよいが、調色膜5は、Ta2O5、SiO2、TiO2、Al2O3、ZrO2、Nb2O5およびHfO2よりなる群から選択される少なくとも1種を含む材料で構成された層(金属酸化物層51)を有するものであるのが好ましく、複数の金属酸化物層51として、前記群から選択される互いに異なる材料で構成された層を有するものであるのがより好ましい。
The toning film 5 (metal oxide layer 51) may be made of an oxide of a metal material, but the
これにより、時計用部品10の審美性をより優れたものとすることができるとともに、時計用部品10全体として表現することのできる色調の範囲をより広いものとすることができる。また、これらの化合物は、各種の金属酸化物の中でも化学的安定性が特に高い材料であり、時計用部品10全体としての外観の安定性、耐久性をより優れたものとすることができる。
As a result, the aesthetic appearance of the
中でも、Al2O3およびHfO2は、硬度が特に高い材料であり、化学的な耐久性だけでなく、機械的な力に対しても優れた耐久性を有する。 Among them, Al 2 O 3 and HfO 2 are materials having particularly high hardness, and have excellent durability not only in chemical durability but also in mechanical force.
なお、調色膜5(金属酸化物層51)は、主として金属酸化物で構成されたものであればよく、金属酸化物以外の成分を含むものであってもよい。ただし、調色膜5(金属酸化物層51)中における金属酸化物以外の成分の含有率は、5質量%以下であるのが好ましく、1質量%以下であるのがより好ましい。 The toning film 5 (metal oxide layer 51) may be mainly composed of a metal oxide and may contain a component other than the metal oxide. However, the content of the components other than the metal oxide in the toning film 5 (metal oxide layer 51) is preferably 5% by mass or less, and more preferably 1% by mass or less.
調色膜5の厚さは、100nm以上2000nm以下であるのが好ましく、150nm以上1000nm以下であるのがより好ましく、200nm以上800nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜5の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができ、また、時計用部品10の生産性をより優れたものとすることができる。
As a result, the aesthetics of the
調色膜5を構成する各層(各金属酸化物層51)の厚さは、それぞれ、10nm以上300nm以下であるのが好ましく、15nm以上200nm以下であるのがより好ましく、25nm以上150nm以下であるのがさらに好ましい。
The thickness of each layer (each metal oxide layer 51) constituting the
これにより、時計用部品10の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜5の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができる。
As a result, the aesthetics of the
調色膜5を構成する金属酸化物層51の数は、2以上であるのが好ましく、3以上であるのがより好ましい。
The number of the metal oxide layers 51 constituting the
これにより、時計用部品10の審美性をより優れたものとすることができ、色再現域をより広いものとすることができるとともに、調色膜5の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができる。
As a result, the aesthetics of the
調色膜5の形成方法は、特に限定されず、例えば、スピンコート、ディッピング、刷毛塗り、噴霧塗装、静電塗装、電着塗装等の塗装、電解めっき、浸漬めっき、無電解めっき等の湿式めっき法や、熱CVD、プラズマCVD、レーザーCVD等の化学蒸着法(CVD)、真空蒸着、スパッタリング、イオンプレーティング等の乾式めっき法(気相成膜法)、溶射等が挙げられるが、乾式めっき法(気相成膜法)が好ましい。
The method for forming the
調色膜5の形成方法として乾式めっき法(気相成膜法)を適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた調色膜5を確実に形成することができる。その結果、時計用部品10の審美的外観、耐久性を特に優れたものとすることができる。
By applying the dry plating method (gas phase film formation method) as the method for forming the
また、調色膜5の形成方法として乾式めっき法(気相成膜法)を適用することにより、形成すべき調色膜5を構成する各金属酸化物層51が比較的薄いものであっても、膜厚のばらつきを十分に小さいものとすることができる。このため、時計用部品10の信頼性を向上させる上でも有利である。
Further, by applying the dry plating method (gas phase film formation method) as the method for forming the
また、調色膜5の形成方法として乾式めっき法(気相成膜法)を適用することにより、調色膜5中の各部位(各金属酸化物層51)における酸素の含有率をより確実に制御することができる。
Further, by applying the dry plating method (gas phase film forming method) as the method for forming the
上記のような乾式めっき法(気相成膜法)の中でも、イオンプレーティングが特に好ましい。 Among the dry plating methods (gas phase film formation methods) as described above, ion plating is particularly preferable.
調色膜5の形成方法としてイオンプレーティングを適用することにより、上記のような効果はより顕著なものとなる。すなわち、調色膜5の形成方法としてイオンプレーティングを適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた調色膜5をより確実に形成することができる。その結果、最終的に得られる時計用部品10の審美的外観、耐久性をさらに優れたものとすることができる。
By applying ion plating as a method for forming the
また、調色膜5の形成方法としてイオンプレーティングを適用することにより、形成すべき調色膜5を構成する各金属酸化物層51が比較的薄いものであっても、膜厚のばらつきを特に小さいものとすることができる。
Further, by applying ion plating as a method for forming the
また、調色膜5の形成方法としてイオンプレーティングを適用することにより、調色膜5中の各部位(各金属酸化物層51)における酸素の含有率をより確実に制御することができる。
Further, by applying ion plating as a method for forming the
また、調色膜5を乾式めっき法により形成する場合、例えば、ターゲットを複数セットすることにより、基材2を装置内から取り出すことなく、同一装置内で、調色膜5を構成する各金属酸化物層51を引き続いて形成することができる。
When the
これにより、調色膜5を構成する各層間での密着性が特に優れたものとなるとともに、時計用部品10の生産性も向上する。
As a result, the adhesion between the layers constituting the
[第2実施形態]
次に、第2実施形態の時計用部品について説明する。
図2は、本発明の時計用部品の第2実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Second Embodiment]
Next, the timepiece parts of the second embodiment will be described.
FIG. 2 is a cross-sectional view schematically showing a second embodiment of the timepiece component of the present invention. In the following description, the differences from the above-described embodiment will be mainly described, and the description of the same matters will be omitted.
本実施形態の時計用部品10は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まない材料で構成された基材2と、第1の材料で構成され基材2を被覆する被膜3と、被膜3を被覆する調色膜5とがこの順で積層されている。言い換えると、本実施形態の時計用部品10では、金属光沢部1は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まない材料で構成された基材2上に設けられた被膜3である。
The
このように、基材2とは異なる部位として、金属光沢部1としての被膜3を設けることにより、基材2の構成材料等の選択の幅が広がる。例えば、ガラス、セラミックス、プラスチック材料等も基材2の構成材料として好適に用いることができ、時計用部品10の成形方法の選択の幅、時計における時計用部品10の配置部位の選択の幅等をより広いものとすることができる。また、時計用部品10全体としての、金属材料の使用量をより少ないものとすることができる。これにより、例えば、時計用部品10の軽量化に寄与することができる。また、時計用部品10の電波透過性を優れたものとすることができ、例えば、時計用部品10を電波時計等に好適に適用することができる。また、基材2として光透過性を有する材料で構成されたものを用い、被膜3の厚さを比較的薄いものとすることにより、時計用部品10全体として、優れた光沢感、審美性を発揮しつつ、十分な光透過性を確保することができる。その結果、時計用部品10を、例えば、風防ガラスやスケルトンタイプの裏蓋のように光透過性が求められる部品に好適に適用することができる。
As described above, by providing the
≪基材≫
本実施形態において、基材2の構成材料としては、例えば、サファイアガラス、ソーダガラス、結晶性ガラス、石英ガラス、鉛ガラス、カリウムガラス、ホウケイ酸ガラス、無アルカリガラス等のガラス材料、アルミナ、チタニア等のセラミックス材料、各種熱可塑性樹脂、各種硬化性樹脂等のプラスチック材料等が挙げられる。
≪Base material≫
In the present embodiment, the constituent materials of the
なお、本実施形態において、基材2は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料のいずれをも実質的に含まないものであればよく、少量であれば、例えば、フィラーや不可避成分等として、Tiの窒化物もしくは炭化物、Crの窒化物もしくは炭化物、または、金属材料を含んでいてもよい。例えば、基材2は、Tiの窒化物および炭化物、Crの窒化物および炭化物、ならびに、金属材料を、これらの含有率の和が5質量%以下の含有率で含んでいてもよい。このような場合、前述したような効果が十分に得られる。
In the present embodiment, the
≪被膜(金属光沢部)≫
本実施形態においては、被膜3が金属光沢部1として機能する。
被膜3の構成材料としては、前述した実施形態での基材2(金属光沢部1)で挙げたものと同様である。すなわち、本実施形態において、被膜3は、第1の材料で構成されている。
≪Coating (metallic luster) ≫
In the present embodiment, the
The constituent material of the
被膜3の厚さは、30nm以上5000nm以下であるのが好ましく、40nm以上3000nm以下であるのがより好ましく、50nm以上500nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができるとともに、被膜3の不本意な剥離等をより効果的に防止し、時計用部品10の耐久性をより優れたものとすることができるとともに、時計用部品10の生産性をより優れたものとすることができる。
As a result, the glossiness and aesthetics of the
被膜3は、各部位で均一な組成を有するものであってもよいし、組成の異なる部位を有するものであってもよい。例えば、被膜3は、組成が傾斜的に変化する傾斜材料(例えば、厚さ方向に組成が傾斜的に変化する傾斜材料等)で構成されたもの等であってもよい。
The
被膜3の形成方法は、特に限定されず、例えば、スピンコート、ディッピング、刷毛塗り、噴霧塗装、静電塗装、電着塗装等の塗装、電解めっき、浸漬めっき、無電解めっき等の湿式めっき法や、熱CVD、プラズマCVD、レーザーCVD等の化学蒸着法(CVD)、真空蒸着、スパッタリング、イオンプレーティング等の乾式めっき法(気相成膜法)、溶射等が挙げられるが、乾式めっき法(気相成膜法)が好ましい。
The method for forming the
被膜3の形成方法として乾式めっき法(気相成膜法)を適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた被膜3を確実に形成することができる。その結果、時計用部品10の審美的外観、耐久性を特に優れたものとすることができる。
By applying the dry plating method (gas phase film formation method) as a method for forming the
また、被膜3の形成方法として乾式めっき法(気相成膜法)を適用することにより、形成すべき被膜3が比較的薄いものであっても、膜厚のばらつきを十分に小さいものとすることができる。このため、時計用部品10の信頼性を向上させる上でも有利である。
Further, by applying a dry plating method (gas phase film forming method) as a method for forming the
上記のような乾式めっき法(気相成膜法)の中でも、イオンプレーティングが特に好ましい。 Among the dry plating methods (gas phase film formation methods) as described above, ion plating is particularly preferable.
被膜3の形成方法としてイオンプレーティングを適用することにより、上記のような効果はより顕著なものとなる。すなわち、被膜3の形成方法としてイオンプレーティングを適用することにより、均一な膜厚を有し、均質で、かつ、基材2等との密着性が特に優れた被膜3をより確実に形成することができる。その結果、最終的に得られる時計用部品10の審美的外観、耐久性をさらに優れたものとすることができる。
By applying ion plating as a method for forming the
また、被膜3の形成方法としてイオンプレーティングを適用することにより、形成すべき被膜3が比較的薄いものであっても、膜厚のばらつきを特に小さいものとすることができる。
Further, by applying ion plating as a method for forming the
[第3実施形態]
次に、第3実施形態の時計用部品について説明する。
図3は、本発明の時計用部品の第3実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Third Embodiment]
Next, the timepiece parts of the third embodiment will be described.
FIG. 3 is a cross-sectional view schematically showing a third embodiment of the timepiece component of the present invention. In the following description, the differences from the above-described embodiment will be mainly described, and the description of the same matters will be omitted.
本実施形態の時計用部品10では、基材2が光透過性を有するものであり、基材2と、調色膜5と、被膜3(金属光沢部1)とがこの順で積層されている。
In the
このように、時計用部品10を構成する各部材の配置は、前述したものと異なるものであってもよい。
As described above, the arrangement of each member constituting the
また、本実施形態のように、基材2と、調色膜5と、被膜3(金属光沢部1)とがこの順で積層されていることにより、観察者に、光透過性を有する基材2を介して、調色膜5、被膜3(金属光沢部1)を視認させることができるため、調色膜5等を外部に露出しなくて済む。これにより、摩擦力等の外力により、調色膜5、被膜3(金属光沢部1)に損傷(例えば、傷や剥離等)が生じることをより効果的に防止することができ、時計用部品10の耐久性をより優れたものとすることができる。
Further, as in the present embodiment, the
基材2は、光透過性を有するものであればよいが、可視光の透過率(例えば、波長550nmの光の透過率)は、80%以上であるのが好ましく、85%以上であるのがより好ましく、90%以上であるのがさらに好ましい。
The
これにより、上記のような配置にすることによる効果を得つつ、時計用部品10の審美性をより優れたものとすることができる。
As a result, the aesthetics of the
[第4実施形態]
次に、第4実施形態の時計用部品について説明する。
図4は、本発明の時計用部品の第4実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Fourth Embodiment]
Next, the timepiece parts of the fourth embodiment will be described.
FIG. 4 is a cross-sectional view schematically showing a fourth embodiment of the timepiece component of the present invention. In the following description, the differences from the above-described embodiment will be mainly described, and the description of the same matters will be omitted.
本実施形態の時計用部品10では、第1の材料で構成された基材2(金属光沢部1の第1の領域11)と、第1の材料で構成された被膜3(金属光沢部1の第2の領域12)と、被膜3を被覆する調色膜5とがこの順で積層されており、基材2と被膜3とは、互いに異なる材料で構成されている。言い換えると、本実施形態では、金属光沢部1は、第1の領域11と、第1の領域11よりも調色膜5側に、第1の領域11と重ね合わせて層状に設けられた第2の領域12とを有するものであり、第2の領域12は、第1の領域11とは異なる材料で構成されたものである。
In the
これにより、微妙な色調整を行うことができ、時計用部品10全体としての色再現域をより広いものとすることができ、時計用部品10の審美性をより優れたものとすることができる。また、全体としての金属の使用量をさらに抑制しつつ、時計用部品10の審美性を優れたものとすることができる。
As a result, delicate color adjustment can be performed, the color reproduction range of the
第1の領域11の厚さは、20nm以上であるのが好ましく、25nm以上であるのがより好ましく、30nm以上であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができる。
As a result, the glossiness and aesthetics of the
第2の領域12の厚さは、30nm以下であるのが好ましく、20nm以下であるのがより好ましく、10nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10の審美性をより優れたものとすることができるとともに、第2の領域12の不本意な剥離等をより効果的に防止することができ、時計用部品10の耐久性、信頼性をより優れたものとすることができ、また、時計用部品10の生産性をより優れたものとすることができる。
As a result, the aesthetic appearance of the
第1の領域11および第2の領域12は、それぞれ、第1の材料で構成されたものであればよく、その材料の組み合わせは特に限定されず、第1の領域11および第2の領域12は、同一の組成を有するものであってもよいし、異なる組成を有するものであってもよいが、第1の領域11がTiNで構成されたものであり、かつ、第2の領域12がTi、Cr、AlまたはFeを含む金属材料で構成されたものであるのが好ましい。
これにより、高級感が特に高い金色を表現することができる。
The
As a result, it is possible to express a golden color with a particularly high sense of quality.
[第5実施形態]
次に、第5実施形態の時計用部品について説明する。
図5は、本発明の時計用部品の第5実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Fifth Embodiment]
Next, the timepiece parts of the fifth embodiment will be described.
FIG. 5 is a cross-sectional view schematically showing a fifth embodiment of the timepiece component of the present invention. In the following description, the differences from the above-described embodiment will be mainly described, and the description of the same matters will be omitted.
本実施形態の時計用部品10では、第1の材料以外の材料で構成された基材2と、第1の材料で構成された被膜3(金属光沢部1)と、被膜3(金属光沢部1)を被覆する調色膜5とがこの順で積層されており、金属光沢部1は、第1の領域11と、第1の領域11よりも調色膜5側に、第1の領域11と重ね合わせて層状に設けられた第2の領域12とを有するものであり、第2の領域12は、第1の領域11とは異なる材料で構成されたものである。すなわち、基材2が金属光沢部1を構成するものではなく、かつ、金属光沢部1としての被膜3が、第1の領域11(第1の層)と、第2の領域12(第2の層)とを有するものであること以外は、前述した第4実施形態と同様である。
In the
第1の領域11が層状に設けられたものであることにより、基材2、第1の領域11の構成材料等の選択の幅が広がり、例えば、鋳造等が困難な材料でも好適に用いることができる。また、時計用部品10全体としての金属材料の使用量をより少ないものとすることができる。
Since the
第1の領域11の厚さは、20nm以上1500nm以下であるのが好ましく、25nm以上1000nm以下であるのがより好ましく、30nm以上500nm以下であるのがさらに好ましい。
The thickness of the
これにより、時計用部品10全体としての光沢感、審美性をより優れたものとすることができるとともに、第1の領域11の不本意な剥離等をより効果的に防止し、時計用部品10の耐久性をより優れたものとすることができるとともに、時計用部品10の生産性をより優れたものとすることができる。
As a result, the glossiness and aesthetics of the
[第6実施形態]
次に、第6実施形態の時計用部品について説明する。
図6は、本発明の時計用部品の第6実施形態を模式的に示す断面図である。以下の説明では、前述した実施形態との相違点について中心的に説明し、同様の事項についての説明は省略する。
[Sixth Embodiment]
Next, the timepiece parts of the sixth embodiment will be described.
FIG. 6 is a cross-sectional view schematically showing a sixth embodiment of the timepiece component of the present invention. In the following description, the differences from the above-described embodiment will be mainly described, and the description of the same matters will be omitted.
本実施形態の時計用部品10では、基材2が光透過性を有するものであり、基材2と、調色膜5と、第2の領域12および第1の領域11を有する被膜3(金属光沢部1)とがこの順で積層されている。すなわち、本実施形態の時計用部品10は、構成部材の配置が異なること以外は、前記第5実施形態と同様である。また、本実施形態の時計用部品10は、被膜3(金属光沢部1)が異なること以外は、前記第3実施形態と同様である。
In the
時計用部品10は、時計を構成する部品であればいかなるものであってもよいが、時計の使用時において外部から視認しうる部品であるのが好ましく、具体的には、風防ガラス、ケース、ベゼル、裏蓋、バンド(バンドの駒、バンド中留、尾錠、バックル、バンド・バングル着脱機構等を含む)、文字板、時計用針、ローター、りゅうず(例えば、ネジロック式りゅうず等)、ボタン、ダイヤルリング、見切板等が挙げられ、中でも、風防ガラス、文字板、ケースまたはバンドであるのが好ましい。
The
これらの部品(時計用部品)は、時計全体の外観に大きな影響を与えるものであるため、これらの部品に本発明が適用されることにより、時計全体としての審美性をより優れたものとすることができる。 Since these parts (watch parts) have a great influence on the appearance of the entire watch, the aesthetics of the watch as a whole can be improved by applying the present invention to these parts. be able to.
《時計》
次に、本発明の時計について説明する。
図7は、本発明の時計(腕時計)の好適な実施形態を模式的に示す部分断面図である。
"clock"
Next, the clock of the present invention will be described.
FIG. 7 is a partial cross-sectional view schematically showing a preferred embodiment of the watch (wrist watch) of the present invention.
本実施形態の腕時計(時計)W10は、胴(ケース)W22と、裏蓋W23と、ベゼル(縁)W24と、ガラス板(風防ガラス)W25とを備えている。また、ケースW22内には、図示しないムーブメント(例えば、文字板、針付きのもの)が収納されている。 The wristwatch (clock) W10 of the present embodiment includes a body (case) W22, a back cover W23, a bezel (edge) W24, and a glass plate (windshield) W25. Further, a movement (for example, one with a dial and hands) (not shown) is housed in the case W22.
胴W22には巻真パイプW26が嵌入・固定され、この巻真パイプW26内にはりゅうずW27の軸部W271が回転可能に挿入されている。 A winding stem pipe W26 is fitted and fixed to the body W22, and a shaft portion W271 of a crown W27 is rotatably inserted into the winding stem pipe W26.
胴W22とベゼルW24とは、プラスチックパッキンW28により固定され、ベゼルW24とガラス板W25とはプラスチックパッキンW29により固定されている。 The body W22 and the bezel W24 are fixed by the plastic packing W28, and the bezel W24 and the glass plate W25 are fixed by the plastic packing W29.
また、胴W22に対し裏蓋W23が嵌合(または螺合)されており、これらの接合部(シール部)W50には、リング状のゴムパッキン(裏蓋パッキン)W40が圧縮状態で介挿されている。この構成によりシール部W50が液密に封止され、防水機能が得られる。 Further, the back cover W23 is fitted (or screwed) to the body W22, and a ring-shaped rubber packing (back cover packing) W40 is inserted into the joint portion (seal portion) W50 in a compressed state. Has been done. With this configuration, the seal portion W50 is liquid-tightly sealed, and a waterproof function can be obtained.
りゅうずW27の軸部W271の途中の外周には溝W272が形成され、この溝W272内にはリング状のゴムパッキン(りゅうずパッキン)W30が嵌合されている。ゴムパッキンW30は巻真パイプW26の内周面に密着し、該内周面と溝W272の内面との間で圧縮される。この構成により、りゅうずW27と巻真パイプW26との間が液密に封止され防水機能が得られる。なお、りゅうずW27を回転操作したとき、ゴムパッキンW30は軸部W271と共に回転し、巻真パイプW26の内周面に密着しながら周方向に摺動する。 A groove W272 is formed on the outer periphery of the shaft portion W271 of the crown W27, and a ring-shaped rubber packing (crown packing) W30 is fitted in the groove W272. The rubber packing W30 is in close contact with the inner peripheral surface of the winding pipe W26, and is compressed between the inner peripheral surface and the inner surface of the groove W272. With this configuration, the space between the crown W27 and the winding pipe W26 is liquid-tightly sealed, and a waterproof function can be obtained. When the crown W27 is rotated, the rubber packing W30 rotates together with the shaft portion W271 and slides in the circumferential direction while being in close contact with the inner peripheral surface of the winding stem pipe W26.
本発明の時計としての腕時計W10は、その構成部品のうち少なくとも1つが前述したような本発明の時計用部品で構成されたものである。言い換えると、本発明の時計は、本発明の時計用部品を備えたものである。 The wristwatch W10 as a timepiece of the present invention has at least one of its components composed of the timepiece parts of the present invention as described above. In other words, the timepiece of the present invention is provided with the timepiece parts of the present invention.
これにより、貴金属を主材料として使用しなくても、優れた外観(金属光沢を呈する外観)を有する時計W10を提供することができる。 Thereby, it is possible to provide the watch W10 having an excellent appearance (appearance exhibiting metallic luster) without using a precious metal as a main material.
以上、本発明の好適な実施形態について説明したが、本発明は、これらに限定されるものではない。 Although preferred embodiments of the present invention have been described above, the present invention is not limited thereto.
例えば、本発明の時計用部品、時計では、各部の構成は、同様の機能を発揮する任意の構成のものに置換することができ、また、任意の構成を付加することもできる。
例えば、金属光沢部と調色膜との間や、基材と被膜との間には、少なくとも1層の中間層を有していてもよい。
For example, in the timepiece parts and the timepiece of the present invention, the configuration of each part can be replaced with an arbitrary configuration that exhibits the same function, or an arbitrary configuration can be added.
For example, at least one intermediate layer may be provided between the metallic luster portion and the toning film or between the base material and the coating film.
また、前述した第4、第5、第6実施形態では、金属光沢部は、第1の領域および第2の領域を有するものとして説明したが、さらに、これらとは異なる第3の領域を有していてもよい。 Further, in the fourth, fifth, and sixth embodiments described above, the metallic luster portion has been described as having a first region and a second region, but further, it has a third region different from these. You may be doing it.
また、前述した実施形態では、金属光沢部の一方の面側に調色膜が設けられた構成について代表的に説明したが、金属光沢部の両側の面にそれぞれ調色膜が設けられていてもよい。 Further, in the above-described embodiment, the configuration in which the toning film is provided on one surface side of the metallic luster portion has been typically described, but the toning film is provided on both surfaces of the metallic luster portion. May be good.
また、時計用部品の表面の少なくとも一部には、耐食性、耐候性、耐水性、耐油性、耐擦傷性、耐摩耗性、耐変色性等を付与し、防錆、防汚、防曇、防傷等の効果を向上するコート層(保護層)等が形成されていてもよい。このようなコート層は、時計用部品の使用時等において除去されるものであってもよい。 In addition, at least a part of the surface of watch parts is provided with corrosion resistance, weather resistance, water resistance, oil resistance, scratch resistance, abrasion resistance, discoloration resistance, etc., and is rust-proof, stain-proof, anti-fog, etc. A coat layer (protective layer) or the like that improves the effect of scratch protection or the like may be formed. Such a coat layer may be removed when a timepiece component is used or the like.
次に、本発明の具体的実施例について説明する。
[1]時計用部品の製造
(実施例1)
まず、SUS304製の板材を打ち抜き成形し、文字板の形状を有する基材(金属光沢部)を作製し、その後、必要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
Next, specific examples of the present invention will be described.
[1] Manufacture of watch parts (Example 1)
First, a plate material made of SUS304 was punched and molded to prepare a base material (metallic luster portion) having the shape of a dial, and then necessary parts were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline electrolytic degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Next, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on one surface of the base material, and a dial as a watch component was obtained.
調色膜は、基材側から、TiO2層(厚さ50nm)、SiO2層(厚さ103nm)、TiO2層(厚さ61nm)、SiO2層(厚さ40nm)、TiO2層(厚さ30nm)、SiO2層(厚さ87nm)、TiO2層(厚さ116nm)およびSiO2層(厚さ76nm)がこの順に積層されたものとして形成した。 Choiromaku from the substrate side, TiO 2 layer (thickness 50 nm), SiO 2 layer (thickness 103 nm), TiO 2 layer (thickness 61 nm), SiO 2 layer (thickness 40 nm), TiO 2 layers ( thickness 30 nm), a SiO 2 layer (thickness 87 nm), TiO 2 layer (thickness 116 nm) and SiO 2 layer (thickness 76 nm) was formed as laminated in this order.
(実施例2)
まず、ポリカーボネートを用いて、圧縮成形により、文字板の形状を有する基材を作製し、その後、必要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
(Example 2)
First, a base material having the shape of a dial was produced by compression molding using polycarbonate, and then necessary parts were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline immersion degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、TiNで構成された厚さ160nmの被膜(金属光沢部)を形成した。 Next, a film (metallic luster portion) having a thickness of 160 nm composed of TiN was formed on one surface of the base material by ion plating.
引き続き、イオンプレーティングにより、被膜(金属光沢部)の表面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Subsequently, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on the surface of the film (metallic luster part) to obtain a dial as a watch component.
調色膜は、被膜(金属光沢部)側から、SiO2層(厚さ82nm)、Ta2O5層(厚さ63nm)、SiO2層(厚さ93nm)およびTa2O5層(厚さ105nm)がこの順に積層されたものとして形成した。 The toning film is composed of SiO 2 layer (thickness 82 nm), Ta 2 O 5 layer (thickness 63 nm), SiO 2 layer (thickness 93 nm) and Ta 2 O 5 layer (thickness) from the film (metallic luster) side. 105 nm) was formed as being laminated in this order.
(実施例3)
被膜(金属光沢部)形成時における成膜条件、調色膜形成時における成膜条件を調整することにより、被膜(金属光沢部)および調色膜の構成を表1に示すようにした以外は、前記実施例2と同様にして時計用部品(文字板)を製造した。
(Example 3)
Except that the composition of the film (metallic luster) and the toning film was shown in Table 1 by adjusting the film forming conditions at the time of forming the film (metallic luster) and the film forming conditions at the time of forming the toning film. , A clock part (dial) was manufactured in the same manner as in the second embodiment.
(実施例4)
まず、風防ガラス形状を有する無機ガラス製の基材を用意した。
(Example 4)
First, a base material made of inorganic glass having a windshield shape was prepared.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline immersion degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、金属酸化物の多層膜で構成された調色膜を形成した。 Next, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on one surface of the base material.
調色膜は、基材側から、TiO2層(厚さ14nm)、SiO2層(厚さ93nm)、TiO2層(厚さ45nm)、SiO2層(厚さ30nm)、TiO2層(厚さ58nm)、SiO2層(厚さ106nm)およびTiO2層(厚さ53nm)がこの順に積層されたものとして形成した。 The toning film is composed of two layers of TiO (thickness 14 nm), two layers of SiO (thickness 93 nm), two layers of TiO (thickness 45 nm), two layers of SiO (thickness 30 nm), and two layers of TiO (thickness 30 nm) from the substrate side. It was formed as a stack of two layers of SiO (thickness: 58 nm), two layers of SiO (thickness: 106 nm), and two layers of TIO (thickness: 53 nm) in this order.
引き続き、イオンプレーティングにより、調色膜の表面に、Tiで構成された厚さ52nmの被膜(金属光沢部)を形成し、時計用部品としての風防ガラスを得た。 Subsequently, a film (metallic luster portion) having a thickness of 52 nm made of Ti was formed on the surface of the toning film by ion plating to obtain a windshield as a watch component.
(実施例5)
まず、アルミニウム板を打ち抜き成形し、文字板の形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
(Example 5)
First, an aluminum plate was punched and molded to prepare a base material (first region of a metallic luster portion) having the shape of a dial, and then necessary parts were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline electrolytic degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、TiNで構成された厚さ160nmの被膜(金属光沢部の第2の領域)を形成した。 Next, by ion plating, a film having a thickness of 160 nm (second region of the metallic luster portion) composed of TiN was formed on one surface of the base material.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Subsequently, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on the surface of the film to obtain a dial as a watch component.
調色膜は、被膜側から、SiO2層(厚さ82nm)、Ta2O5層(厚さ63nm)、SiO2層(厚さ93nm)およびTa2O5層(厚さ105nm)がこの順に積層されたものとして形成した。 From the coating film side, the toning film consists of a SiO 2 layer (thickness 82 nm), a Ta 2 O 5 layer (thickness 63 nm), a SiO 2 layer (thickness 93 nm), and a Ta 2 O 5 layer (thickness 105 nm). It was formed as being laminated in order.
(実施例6)
調色膜形成時における成膜条件を調整することにより、調色膜の構成を表1に示すようにした以外は、前記実施例5と同様にして時計用部品(文字板)を製造した。
(Example 6)
By adjusting the film forming conditions at the time of forming the toning film, a timepiece component (dial) was manufactured in the same manner as in Example 5 except that the configuration of the toning film was shown in Table 1.
(実施例7)
まず、ポリカーボネートを用いて、圧縮成形により、文字板の形状を有する基材を作製し、その後、要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
(Example 7)
First, using polycarbonate, a base material having the shape of a dial was produced by compression molding, and then key points were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline immersion degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、第1の領域(第1の層)および第2の領域(第2の層)がこの順で積層された積層体としての被膜(金属光沢部)を形成した。 Next, by ion plating, a coating film (a laminated body) in which a first region (first layer) and a second region (second layer) are laminated in this order on one surface of a base material (a first layer). A metallic luster part) was formed.
第1の領域(第1の層)は、TiNで構成されたものであり、厚さが162nmのものであった。また、第2の領域(第2の層)は、Alで構成されたものであり、厚さが6nmのものであった。 The first region (first layer) was composed of TiN and had a thickness of 162 nm. The second region (second layer) was composed of Al and had a thickness of 6 nm.
引き続き、イオンプレーティングにより、被膜(金属光沢部)の表面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Subsequently, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on the surface of the film (metallic luster part) to obtain a dial as a watch component.
調色膜は、被膜(金属光沢部)側から、Ta2O5層(厚さ120nm)およびSiO2層(厚さ44nm)がこの順に積層されたものとして形成した。 The toning film was formed as a Ta 2 O 5 layer (thickness 120 nm) and a SiO 2 layer (thickness 44 nm) laminated in this order from the film (metallic luster) side.
(実施例8)
まず、風防ガラス形状を有する無機ガラス製の基材を用意した。
(Example 8)
First, a base material made of inorganic glass having a windshield shape was prepared.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ浸漬脱脂を30秒間行い、その後、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline immersion degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、金属酸化物の多層膜で構成された調色膜を形成した。 Next, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on one surface of the base material.
調色膜は、基材側から、Ta2O5層(厚さ79nm)およびSiO2層(厚さ110nm)がこの順に積層されたものとして形成した。 The toning film was formed as a Ta 2 O 5 layer (thickness 79 nm) and a SiO 2 layer (thickness 110 nm) laminated in this order from the substrate side.
引き続き、イオンプレーティングにより、調色膜の表面に、第2の領域(第2の層)および第1の領域(第1の層)がこの順で積層された積層体としての被膜(金属光沢部)を形成し、時計用部品としての風防ガラスを得た。 Subsequently, a coating film (metallic luster) as a laminate in which a second region (second layer) and a first region (first layer) are laminated in this order on the surface of the toning film by ion plating. Part) was formed, and a windshield as a watch part was obtained.
第2の領域(第2の層)は、Alで構成されたものであり、厚さが5nmのものであった。また、第1の領域(第1の層)は、TiNで構成されたものであり、厚さが100nmのものであった。 The second region (second layer) was composed of Al and had a thickness of 5 nm. The first region (first layer) was composed of TiN and had a thickness of 100 nm.
(実施例9)
まず、アルミニウム板を打ち抜き成形し、文字板の形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
(Example 9)
First, an aluminum plate was punched and molded to prepare a base material (first region of a metallic luster portion) having the shape of a dial, and then necessary parts were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline electrolytic degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、TiNで構成された厚さ160nmの被膜(金属光沢部の第2の領域)を形成した。 Next, by ion plating, a film having a thickness of 160 nm (second region of the metallic luster portion) composed of TiN was formed on one surface of the base material.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Subsequently, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on the surface of the film to obtain a dial as a watch component.
調色膜は、被膜側から、SiO2層(厚さ92nm)、Nb2O5層(厚さ50nm)、SiO2層(厚さ108nm)およびNb2O5層(厚さ90nm)がこの順に積層されたものとして形成した。 From the coating film side, the toning film consists of a SiO 2 layer (thickness 92 nm), an Nb 2 O 5 layer (thickness 50 nm), a SiO 2 layer (thickness 108 nm), and an Nb 2 O 5 layer (thickness 90 nm). It was formed as being laminated in order.
(実施例10)
まず、アルミニウム板を打ち抜き成形し、文字板の形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
(Example 10)
First, an aluminum plate was punched and molded to prepare a base material (first region of a metallic luster portion) having the shape of a dial, and then necessary parts were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline electrolytic degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、TiNで構成された厚さ160nmの被膜(金属光沢部の第2の領域)を形成した。 Next, by ion plating, a film having a thickness of 160 nm (second region of the metallic luster portion) composed of TiN was formed on one surface of the base material.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Subsequently, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on the surface of the film to obtain a dial as a watch component.
調色膜は、被膜側から、SiO2層(厚さ79nm)、ZrO2層(厚さ70nm)、SiO2層(厚さ92nm)およびZrO2層(厚さ110nm)がこの順に積層されたものとして形成した。 In the toning film, two layers of SiO (thickness 79 nm), two layers of ZrO (thickness 70 nm), two layers of SiO (thickness 92 nm) and two layers of ZrO (thickness 110 nm) were laminated in this order from the film side. Formed as a thing.
(実施例11〜13)
被膜(金属光沢部)形成時における成膜条件、調色膜形成時における成膜条件を調整することにより、被膜(金属光沢部)および調色膜の構成を表1に示すようにした以外は、前記実施例7と同様にして計用部品(文字板)を製造した。
(Examples 11 to 13)
By adjusting the film forming conditions at the time of forming the film (metallic luster) and the film forming conditions at the time of forming the toning film, the configurations of the film (metallic luster) and the toning film are shown in Table 1. , A meter part (dial) was manufactured in the same manner as in Example 7.
(実施例14)
まず、SUS304製の板材を打ち抜き成形し、文字板の形状を有する基材(金属光沢部の第1の領域)を作製し、その後、必要箇所を切削、研磨した。得られた基材は、略円盤状をなし、直径:約27mm×厚さ:約0.5mmであった。
(Example 14)
First, a plate material made of SUS304 was punched and molded to prepare a base material having the shape of a dial (the first region of the metallic luster portion), and then the necessary parts were cut and polished. The obtained base material had a substantially disk shape, and had a diameter of about 27 mm and a thickness of about 0.5 mm.
次に、この基材を洗浄した。基材の洗浄としては、まず、アルカリ電解脱脂を30秒間行い、次いで、中和を10秒間、水洗を10秒間、純水洗浄を10秒間行った。 The substrate was then washed. As the washing of the base material, first, alkaline electrolytic degreasing was carried out for 30 seconds, then neutralization was carried out for 10 seconds, water washing was carried out for 10 seconds, and pure water washing was carried out for 10 seconds.
次に、イオンプレーティングにより、基材の一方の面に、TiCNで構成された厚さ100nmの被膜(金属光沢部の第2の領域)を形成した。 Next, a coating film having a thickness of 100 nm (second region of the metallic luster portion) composed of TiCN was formed on one surface of the base material by ion plating.
引き続き、イオンプレーティングにより、被膜の表面に、金属酸化物の多層膜で構成された調色膜を形成し、時計用部品としての文字板を得た。 Subsequently, by ion plating, a toning film composed of a multilayer film of metal oxide was formed on the surface of the film to obtain a dial as a watch component.
調色膜は、被膜側から、Ta2O5層(厚さ113nm)およびSiO2層(厚さ77nm)がこの順に積層されたものとして形成した。 The toning film was formed as a Ta 2 O 5 layer (thickness 113 nm) and a SiO 2 layer (thickness 77 nm) laminated in this order from the film side.
(実施例15)
被膜(金属光沢部の第2の領域)形成時における成膜条件、調色膜形成時における成膜条件を調整することにより、被膜(金属光沢部の第2の領域)および調色膜の構成を表1に示すようにした以外は、前記実施例14と同様にして時計用部品(文字板)を製造した。
(Example 15)
By adjusting the film formation conditions at the time of forming the film (second region of the metallic luster portion) and the film formation conditions at the time of forming the toning film, the composition of the film (second region of the metallic luster portion) and the toning film A clock part (dial) was manufactured in the same manner as in Example 14 except that the above was shown in Table 1.
(実施例16)
被膜(金属光沢部)形成時における成膜条件、調色膜形成時における成膜条件を調整することにより、被膜(金属光沢部)および調色膜の構成を表1に示すようにした以外は、前記実施例2と同様にして時計用部品(文字板)を製造した。
(Example 16)
Except that the composition of the film (metallic luster) and the toning film was shown in Table 1 by adjusting the film forming conditions at the time of forming the film (metallic luster) and the film forming conditions at the time of forming the toning film. , A clock part (dial) was manufactured in the same manner as in the second embodiment.
(実施例17)
被膜(金属光沢部の第2の領域)形成時における成膜条件、調色膜形成時における成膜条件を調整することにより、被膜(金属光沢部の第2の領域)および調色膜の構成を表1に示すようにした以外は、前記実施例14と同様にして時計用部品(文字板)を製造した。
(Example 17)
By adjusting the film formation conditions at the time of forming the film (second region of the metallic luster portion) and the film formation conditions at the time of forming the toning film, the composition of the film (second region of the metallic luster portion) and the toning film A clock part (dial) was manufactured in the same manner as in Example 14 except that the above was shown in Table 1.
(実施例18)
被膜(金属光沢部)形成時における成膜条件、調色膜形成時における成膜条件を調整することにより、被膜(金属光沢部)および調色膜の構成を表1に示すようにした以外は、前記実施例2と同様にして時計用部品(文字板)を製造した。
(Example 18)
Except that the composition of the film (metallic luster) and the toning film was shown in Table 1 by adjusting the film forming conditions at the time of forming the film (metallic luster) and the film forming conditions at the time of forming the toning film. , A clock part (dial) was manufactured in the same manner as in the second embodiment.
(比較例1)
調色膜を形成しなかった以外は、前記実施例1と同様にして時計用部品(文字板)を製造した。
(Comparative Example 1)
A timepiece part (dial) was manufactured in the same manner as in Example 1 except that the toning film was not formed.
(比較例2)
鋳造により、Au製の円盤状の部材を作製し、その後、必要箇所を切削、研磨し、直径:約27mm×厚さ:約0.5mmの寸法の文字板(時計用部品)を得た。すなわち、本比較例の時計用部品は、金無垢の材料で構成されたものである。
(Comparative Example 2)
A disk-shaped member made of Au was produced by casting, and then the necessary parts were cut and polished to obtain a dial (clock parts) having a diameter of about 27 mm and a thickness of about 0.5 mm. That is, the watch parts of this comparative example are made of solid gold material.
各実施例および比較例の時計用部品の構成を表1にまとめて示す。なお、基材を除く各部位の厚さは、括弧書きで示した。また、表中、ポリカーボネートをPC、無機ガラスをGで示した。また、時計用部品を構成する各部位について、表中に示す成分の含有率は、いずれも、99.9質量%以上であった。 Table 1 summarizes the configurations of the timepiece parts of each Example and Comparative Example. The thickness of each part excluding the base material is shown in parentheses. In the table, polycarbonate is indicated by PC and inorganic glass is indicated by G. In addition, the content of the components shown in the table for each part constituting the timepiece component was 99.9% by mass or more.
また、前記各実施例のうちTiCで構成された層を有するものについては、いずれも、当該層におけるC(炭素)の含有率は、50質量%以上60質量%以下の範囲内の値であった。 Further, in each of the above-mentioned examples having a layer composed of TiC, the content of C (carbon) in the layer is a value within the range of 50% by mass or more and 60% by mass or less. rice field.
また、前記各実施例のうちTiCNで構成された層を有するものについては、いずれも、当該層におけるC(炭素)の含有率は、5質量%以上15質量%以下の範囲内の値であり、かつ、当該層におけるN(窒素)の含有率は、1質量%以上5質量%以下の範囲内の値であった。 Further, in each of the above-mentioned examples having a layer composed of TiCN, the content of C (carbon) in the layer is a value within the range of 5% by mass or more and 15% by mass or less. Moreover, the content of N (nitrogen) in the layer was a value in the range of 1% by mass or more and 5% by mass or less.
[2]評価
上記各実施例および比較例で製造した各時計用部品について、目視による観察を行った。
[2] Evaluation Visual observation was performed on each watch component manufactured in each of the above Examples and Comparative Examples.
その結果、前記各実施例の時計用部品は、いずれも、高級感にあふれる優れた外観を呈していた。特に、実施例2、5、6、7、8、9、10、11、12、13、15の時計用部品は、比較例2と同様に、高級感のある金色を呈しており、実施例1、3、4、16、17、18では、高級感のある青みがかった光沢を呈する優れた外観が得られた。また、金属光沢部が、Tiの炭窒化物で構成されている実施例14の時計用部品では、ピンクゴールドに類似の高級感のある外観が得られた。また、標準光源D50を用いたときの、実施例1についてのL*は37.2、a*は42.1、b*は−87.2であり、実施例2についてのL*は86.0、a*は13.6、b*は41.9であり、実施例3についてのL*は42.9、a*は37.8、b*は−85.2であり、実施例4についてのL*は30.4、a*は55.4、b*は−103.3であり、実施例5についてのL*は86.0、a*は13.6、b*は41.9であり、実施例6についてのL*は87.5、a*は10.1、b*は41.4であり、実施例7についてのL*は85.9、a*は0.9、b*は35.6であり、実施例8についてのL*は86.7、a*は2.3、b*は36.3であり、実施例9についてのL*は88.2、a*は12.3、b*は43.3であり、実施例10についてのL*は84.4、a*は16.2、b*は38.4であり、実施例11についてのL*は81.8、a*は10.1、b*は40.1であり、実施例12についてのL*は86.1、a*は8.3、b*は35.3であり、実施例13についてのL*は80.4、a*は12.0、b*は34.4であり、実施例14についてのL*は85.4、a*は10.4、b*は23.9であり、実施例15についてのL*は89.3、a*は8.0、b*は35.3であり、実施例16についてのL*は48.7、a*は28.8、b*は−77.6であり、実施例17についてのL*は25.5、a*は2.2、b*は−34.4であり、実施例18についてのL*は40.5、a*は41.7、b*は−88.8であった。 As a result, all of the clock parts of each of the above-described embodiments exhibited an excellent appearance full of a sense of quality. In particular, the watch parts of Examples 2, 5, 6, 7, 8, 9, 10, 11, 12, 13, and 15 have a high-grade golden color as in Comparative Example 2, and are of Examples. At 1, 3, 4, 16, 17, and 18, an excellent appearance with a luxurious bluish luster was obtained. Further, in the watch component of Example 14 in which the metallic luster portion is made of titanium carbonitride, a high-class appearance similar to pink gold was obtained. Further, when the standard light source D50 is used, L * for Example 1 is 37.2, a * is 42.1, b * is −87.2., And L * for Example 2 is 86. 0, a * is 13.6, b * is 41.9, L * for Example 3 is 42.9, a * is 37.8, b * is -85.2, and Example 4 L * is 30.4, a * is 55.4, b * is -103.3, and L * for Example 5 is 86.0, a * is 13.6, and b * is 41. 9, L * for Example 6 is 87.5, a * is 10.1, b * is 41.4, L * for Example 7 is 85.9, and a * is 0.9. , B * is 35.6, L * for Example 8 is 86.7, a * is 2.3, b * is 36.3, and L * for Example 9 is 88.2, a * is 12.3, b * is 43.3, L * for Example 10 is 84.4, a * is 16.2, b * is 38.4, and L for Example 11 is L. * Is 81.8, a * is 10.1, b * is 40.1, L * for Example 12 is 86.1, a * is 8.3, and b * is 35.3. L * is 80.4, a * is 12.0, and b * is 34.4 for Example 13, L * is 85.4, a * is 10.4, and b * is 34.4 for Example 14. 23.9, L * for Example 15 is 89.3, a * is 8.0, b * is 35.3, L * for Example 16 is 48.7, a * is 28. 8.8, b * is -77.6, L * for Example 17 is 25.5, a * is 2.2, b * is -34.4, and L * for Example 18 is 40.5, a * was 41.7, and b * was −88.8.
これに対し、比較例1では、高級感に劣った外観しか得られなかった。比較例2については、優れた外観を呈していたものの、時計用部品の製造に多量の貴金属を必要とした。 On the other hand, in Comparative Example 1, only an appearance inferior in luxury was obtained. Although Comparative Example 2 exhibited an excellent appearance, a large amount of precious metal was required for manufacturing the timepiece parts.
なお、実施例1〜3、5〜7、9〜18については、基材とは反対側の面から観察を行い、実施例4、8については、基材側の面から観察を行った。 In Examples 1 to 3, 5 to 7, 9 to 18, observation was performed from the surface opposite to the base material, and in Examples 4 and 8, observation was performed from the surface on the base material side.
基材の形状をケース、バンドに変更した以外は、前記各実施例および比較例と同様にして時計用部品(ケース、バンド)を製造して、前記と同様の評価を行ったところ、前記と同様の結果が得られた。 A watch component (case, band) was manufactured in the same manner as in each of the above Examples and Comparative Examples except that the shape of the base material was changed to a case and a band, and the same evaluation as described above was performed. Similar results were obtained.
また、金属光沢部の材料として、Alの代わりに、Crを用いた以外は、前記実施例1、5〜8と同様にして時計用部品を製造して、前記と同様の評価を行ったところ、前記と同様の結果が得られた。 Further, a timepiece component was manufactured in the same manner as in Examples 1 and 5 to 8 except that Cr was used as the material for the metallic luster portion, and the same evaluation as described above was performed. , The same result as described above was obtained.
また、第2の領域の構成材料として、Alの代わりに、Ti、Cr、Feを用いた以外は、前記実施例7、8と同様にして時計用部品を製造して、前記と同様の評価を行ったところ、前記と同様の結果が得られた。 Further, clock parts are manufactured in the same manner as in Examples 7 and 8 except that Ti, Cr, and Fe are used as the constituent materials of the second region, and the same evaluation as described above is performed. The same result as described above was obtained.
また、前記各実施例および比較例で製造した時計用部品を用いて、図7に示すような腕時計を組み立てた。これらの腕時計にて、上記と同様な評価を行ったところ、上記と同様の結果が得られた。 In addition, a wristwatch as shown in FIG. 7 was assembled using the clock parts manufactured in the above Examples and Comparative Examples. When the same evaluation as above was performed on these watches, the same results as above were obtained.
10…時計用部品、1…金属光沢部、11…第1の領域、12…第2の領域、2…基材、3…被膜、5…調色膜、51…金属酸化物層、W10…腕時計(時計)、W22…胴(ケース)、W23…裏蓋、W24…ベゼル(縁)、W25…ガラス板(風防ガラス)、W26…巻真パイプ、W27…りゅうず、W271…軸部、W272…溝、W28…プラスチックパッキン、W29…プラスチックパッキン、W30…ゴムパッキン(りゅうずパッキン)、W40…ゴムパッキン(裏蓋パッキン)、W50…接合部(シール部) 10 ... Watch parts, 1 ... Metal glossy part, 11 ... First region, 12 ... Second region, 2 ... Base material, 3 ... Coating, 5 ... Toning film, 51 ... Metal oxide layer, W10 ... Watch (clock), W22 ... Body (case), W23 ... Back cover, W24 ... Bezel (edge), W25 ... Glass plate (windshield), W26 ... Winding plastic, W27 ... Crown, W271 ... Shaft, W272 ... Groove, W28 ... Plastic packing, W29 ... Plastic packing, W30 ... Rubber packing (crown packing), W40 ... Rubber packing (back cover packing), W50 ... Joint (seal part)
Claims (13)
3以上8以下の金属酸化物層の多層膜で構成され、色調を調整する機能を有する調色膜とを備えることを特徴とする時計用部品。 A metallic luster portion composed of a first material containing a nitride or carbide of Ti, a nitride or carbide of Cr, or a metallic material and exhibiting a metallic luster.
A timepiece component characterized by being composed of a multilayer film of a metal oxide layer of 3 or more and 8 or less, and including a color tone film having a function of adjusting a color tone.
前記第2の領域は、前記第1の領域とは異なる材料で構成されたものである請求項1ないし8のいずれか1項に記載の時計用部品。 The metallic luster portion has a first region and a second region provided in a layered manner on the toning film side of the first region so as to overlap the first region. ,
The timepiece component according to any one of claims 1 to 8, wherein the second region is made of a material different from that of the first region.
前記第2の領域がTi、Cr、AlまたはFeを含む金属材料で構成されたものである請求項9に記載の時計用部品。 The first region is composed of TiN.
The timepiece component according to claim 9, wherein the second region is made of a metal material containing Ti, Cr, Al or Fe.