JP6915728B1 - Gas barrier laminating adhesives, laminates and packaging - Google Patents
Gas barrier laminating adhesives, laminates and packaging Download PDFInfo
- Publication number
- JP6915728B1 JP6915728B1 JP2020086563A JP2020086563A JP6915728B1 JP 6915728 B1 JP6915728 B1 JP 6915728B1 JP 2020086563 A JP2020086563 A JP 2020086563A JP 2020086563 A JP2020086563 A JP 2020086563A JP 6915728 B1 JP6915728 B1 JP 6915728B1
- Authority
- JP
- Japan
- Prior art keywords
- acid
- adhesive
- gas barrier
- polyester polyol
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】高いガスバリア性と優れた接着強度とを両立するラミネート接着剤、並びに、該接着剤を用いてなる、高いガスバリア性と優れた接着強度とを両立する積層体及び包装体の提供。【解決手段】上記課題は、多価アルコールと多価カルボン酸から構成されるポリエステルポリオール成分を含むポリオールと、ポリイソシアネートとを含み、前記多価アルコールがジエチレングリコールを、多価アルコール全量を基準として50〜100モル%含み、前記多価カルボン酸が、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を、多価カルボン酸全量を基準として50〜90モル%含む、ガスバリア性ラミネート接着剤によって解決される。【選択図】 なしPROBLEM TO BE SOLVED: To provide a laminated adhesive having both high gas barrier property and excellent adhesive strength, and a laminate and a package having both high gas barrier property and excellent adhesive strength using the adhesive. The above problem includes a polyol containing a polyester polyol component composed of a polyhydric alcohol and a polyvalent carboxylic acid, and a polyisocyanate, and the polyhydric alcohol contains diethylene glycol based on the total amount of the polyhydric alcohol. By a gas barrier laminating adhesive containing ~ 100 mol%, the polyvalent carboxylic acid containing at least one selected from the group consisting of isocyanate and terephthalic acid in an amount of 50 to 90 mol% based on the total amount of the polyvalent carboxylic acid. It will be resolved. [Selection diagram] None
Description
本発明は、食品、医薬品、化粧品、洗剤等の用途に有用な、ガスバリア性ラミネート接着剤、積層体及び包装体に関する。 The present invention relates to gas barrier laminating adhesives, laminates and packages useful for applications such as foods, pharmaceuticals, cosmetics and detergents.
近年、食品の廃棄によるフードロスとして、食品保存期限を過ぎた食品が廃棄されることによる資源の無駄な消費が大きな社会問題となっており、食品保存期限を伸ばす様々な取り組みが検討されている。食品保存期限を延ばす方法としては、従来、ラミネートフィルムのガスバリア性を高めることによって酸素ガス等の食品を傷める気体の食品包装内部への侵入を阻害する方法が検討され、アルミ蒸着フィルムといったバリア性フィルムや、フィルムにバリア性等の機能性を付与するための機能性コート剤の開発・改良がなされてきた。 In recent years, as food loss due to food disposal, wasteful consumption of resources due to disposal of food that has passed the food preservation period has become a major social problem, and various efforts to extend the food preservation period are being studied. As a method of extending the food preservation period, conventionally, a method of inhibiting the invasion of gas that damages food such as oxygen gas into the food packaging by enhancing the gas barrier property of the laminated film has been studied, and a barrier film such as an aluminum vapor-deposited film has been studied. In addition, functional coating agents for imparting functionality such as barrier properties to films have been developed and improved.
一方、フィルムを貼り合わせるためのラミネート用接着剤のガスバリア性を高めることで、ラミネートフィルム全体のガスバリア性を高めることが提案されている。
このようなガスバリア性接着剤として、特許文献1には、比較的低分子量のジオール化合物と、3価以上のポリイソシアネート化合物と、ジイソシアネート化合物との混合物である接着剤が開示されている。また、特許文献2には、ポリイソシアネートとして芳香族環を分子内に有する3価以上のポリイソシアネート化合物と、芳香族環を分子内に有しないポリイソシアネート化合物との混合物を用いる接着剤が開示されている。
On the other hand, it has been proposed to enhance the gas barrier property of the entire laminated film by enhancing the gas barrier property of the laminating adhesive for bonding the films.
As such a gas barrier adhesive, Patent Document 1 discloses an adhesive which is a mixture of a diol compound having a relatively low molecular weight, a polyisocyanate compound having a trivalent or higher valence, and a diisocyanate compound. Further, Patent Document 2 discloses an adhesive using a mixture of a trivalent or higher valent polyisocyanate compound having an aromatic ring in the molecule as a polyisocyanate and a polyisocyanate compound having no aromatic ring in the molecule. ing.
しかしながら、特許文献1及び2に記載の接着剤は、接着剤をより固くしてガスバリア性を向上させるという設計思想であるため、柔軟性が不足し接着強度が低下するという課題がある。そして、特に基材としてアルミ蒸着フィルムやアルミ箔等のような変形し難い金属薄膜を用いた場合に、接着強度は大きく低下する。すなわち、ポリオールとポリイソシアネートとを含む2液硬化型のウレタン系ラミネート接着剤において、高いガスバリア性と優れた接着強度とを両立する接着剤は未だ実現していない。
したがって、本発明の課題は、高いガスバリア性と優れた接着強度とを両立するラミネート接着剤、並びに、該接着剤を用いてなる、高いガスバリア性と優れた接着強度とを両立する積層体及び包装体を提供することにある。
However, since the adhesives described in Patent Documents 1 and 2 have a design concept of making the adhesive harder and improving the gas barrier property, there is a problem that the flexibility is insufficient and the adhesive strength is lowered. In particular, when a metal thin film that is hard to be deformed, such as an aluminum vapor-deposited film or aluminum foil, is used as the base material, the adhesive strength is greatly reduced. That is, in a two-component curable urethane-based laminated adhesive containing a polyol and a polyisocyanate, an adhesive having both high gas barrier properties and excellent adhesive strength has not yet been realized.
Therefore, the subject of the present invention is a laminated adhesive having both high gas barrier properties and excellent adhesive strength, and a laminate and packaging having both high gas barrier properties and excellent adhesive strength using the adhesive. To provide the body.
本発明者は前記課題に対して鋭意研究を重ねた結果、以下に記載のラミネート接着剤を用いることで解決することを見出し、本発明に至った。 As a result of diligent research on the above problems, the present inventor has found that the problem can be solved by using the laminate adhesive described below, and has reached the present invention.
本発明の第1の態様は、多価アルコールと多価カルボン酸から構成されるポリエステルポリオール成分を含むポリオールと、ポリイソシアネートとを含むガスバリア性ラミネート接着剤であって、前記多価アルコールがジエチレングリコールを、多価アルコール全量を基準として50〜100モル%含み、前記多価カルボン酸が、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を、多価カルボン酸全量を基準として50〜90モル%含む、ガスバリア性ラミネート接着剤に関する。 The first aspect of the present invention is a gas barrier laminating adhesive containing a polyol containing a polyester polyol component composed of a polyhydric alcohol and a polyvalent carboxylic acid, and a polyisocyanate, wherein the polyhydric alcohol comprises diethylene glycol. , 50 to 100 mol% based on the total amount of polyhydric alcohol, and the polyvalent carboxylic acid is at least one selected from the group consisting of isocyanate and terephthalic acid, and 50 to 90 mol based on the total amount of polyhydric carboxylic acid. With respect to gas barrier laminating adhesives, including%.
本発明の別の態様は、前記多価カルボン酸が、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を、多価カルボン酸全量を基準として70〜90モル%含む、上記ガスバリア性ラミネート接着剤に関する。 In another aspect of the present invention, the gas barrier laminate comprises the polyvalent carboxylic acid containing at least one selected from the group consisting of isophthalic acid and terephthalic acid in an amount of 70 to 90 mol% based on the total amount of the polyvalent carboxylic acid. Regarding adhesives.
本発明の別の態様は、前記ポリエステルポリオール成分の数平均分子量が、1,000〜6,000である、上記ガスバリア性ラミネート接着剤に関する。 Another aspect of the present invention relates to the gas barrier laminating adhesive having a number average molecular weight of the polyester polyol component of 1,000 to 6,000.
本発明の別の態様は、さらに、分子量150以下の単官能アルコールを、前記ポリエステルポリオール成分を基準として0.3〜2質量%含む、上記ガスバリア性ラミネート接着剤に関する。 Another aspect of the present invention further relates to the gas barrier laminating adhesive containing 0.3 to 2% by mass of a monofunctional alcohol having a molecular weight of 150 or less based on the polyester polyol component.
本発明の別の態様は、上記ガスバリア性ラミネート接着剤からなる接着剤層が、少なくとも2つの基材の間に配置された積層体に関する。 Another aspect of the present invention relates to a laminate in which an adhesive layer made of the gas barrier laminated adhesive is arranged between at least two substrates.
本発明の別の態様は、金属蒸着層、金属酸化物蒸着層、及びアルミニウム箔層からなる群から選ばれる少なくとも1種のバリア層を有し、前記バリア層に接して、前記接着剤層が設けられている、上記積層体に関する。 Another aspect of the present invention has at least one barrier layer selected from the group consisting of a metal vapor deposition layer, a metal oxide vapor deposition layer, and an aluminum foil layer, and the adhesive layer is in contact with the barrier layer. The present invention relates to the above-mentioned laminated body provided.
本発明の別の態様は、上記積層体を用いた包装体に関する。 Another aspect of the present invention relates to a package using the above-mentioned laminate.
本発明により、高いガスバリア性と優れた接着強度とを両立するラミネート接着剤、並びに、該接着剤を用いてなる、高いガスバリア性と優れた接着強度とを両立する積層体及び包装体を提供することができる。 INDUSTRIAL APPLICABILITY The present invention provides a laminated adhesive having both high gas barrier properties and excellent adhesive strength, and a laminate and a packaging body using the adhesive that have both high gas barrier properties and excellent adhesive strength. be able to.
<ラミネート接着剤>
本発明のラミネート接着剤は、多価アルコールと多価カルボン酸から構成されるポリエステルポリオール成分を含むポリオールと、ポリイソシアネートとを含み、前記多価アルコールがジエチレングリコールを、多価アルコール全量を基準として50〜100モル%含み、前記多価カルボン酸が、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を、多価カルボン酸全量を基準として50〜90モル%含み、該接着剤から形成される接着剤層がガスバリア性を有することを特徴とする。
<Laminate adhesive>
The laminate adhesive of the present invention contains a polyol containing a polyester polyol component composed of a polyhydric alcohol and a polyvalent carboxylic acid, and a polyisocyanate, and the polyhydric alcohol contains diethylene glycol based on the total amount of the polyhydric alcohol 50. The polyvalent carboxylic acid contains ~ 100 mol%, and the polyvalent carboxylic acid contains at least one selected from the group consisting of isocyanate and terephthalic acid in an amount of 50 to 90 mol% based on the total amount of the polyvalent carboxylic acid, and is formed from the adhesive. The adhesive layer is characterized by having a gas barrier property.
まず、ポリエステルポリオールの構成成分として、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を50〜90モル%という配合比率で含むことにより、高いガスバリア性付与と接着強度の維持とを満たすことができる。さらに、ポリエステルポリオールの構成成分として、非常に柔軟な骨格を有するジエチレングリコールを50〜100モル%という高い配合比率で用いることにより、接着剤に柔軟性が付与され接着強度が向上する。そして、この接着強度向上効果は、金属蒸着フィルム、金属酸化物蒸着フィルム、アルミ箔といった基材に対して顕著に表れる。
また、ジエチレングリコール由来のC−O−C結合が相互作用し、ポリエステルポリオールの密度が高まることで、柔軟な骨格を有するジエチレングリコールを高い配合比率で用いているにも関わらず、優れたガスバリア性を発揮することができる。
加えて、ポリエステルポリオール成分中には、ポリエステルジエチレングリコールと、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種の多価カルボン酸とに由来する環状化合物が存在し、この環状化合物が、ガスバリア性発現に寄与していると考えられる。具体的には、Π電子が非局在化した酸素原子を環内に複数有する環状化合物の酸素原子が、金属蒸着フィルム、金属酸化物蒸着フィルム、アルミ箔といった基材や溶剤に含まれる金属に配位し安定化することで、接着剤層と基材との界面における環状化合物の存在密度が高まり、ガスバリア性を発揮していると推察される。
First, by containing at least one selected from the group consisting of isophthalic acid and terephthalic acid as a constituent component of the polyester polyol in a blending ratio of 50 to 90 mol%, high gas barrier properties and maintenance of adhesive strength are satisfied. Can be done. Further, by using diethylene glycol having a very flexible skeleton as a constituent component of the polyester polyol in a high blending ratio of 50 to 100 mol%, flexibility is imparted to the adhesive and the adhesive strength is improved. Then, this effect of improving the adhesive strength is remarkably exhibited on the base material such as the metal vapor-deposited film, the metal oxide-deposited film, and the aluminum foil.
In addition, C—O-C bonds derived from diethylene glycol interact with each other to increase the density of polyester polyol, which exhibits excellent gas barrier properties despite the fact that diethylene glycol having a flexible skeleton is used in a high blending ratio. can do.
In addition, the polyester polyol component contains a cyclic compound derived from polyester diethylene glycol and at least one polyvalent carboxylic acid selected from the group consisting of isophthalic acid and terephthalic acid, and this cyclic compound has gas barrier properties. It is considered to contribute to the expression. Specifically, the oxygen atom of a cyclic compound having a plurality of oxygen atoms in which Π electrons are delocalized is used as a metal contained in a base material or a solvent such as a metal vapor deposition film, a metal oxide vapor deposition film, or an aluminum foil. It is presumed that the coordination and stabilization increase the abundance density of the cyclic compound at the interface between the adhesive layer and the base material, and exhibit gas barrier properties.
すなわち、ジエチレングリコールと、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種とを、特定の配合比率で用い組み合わせたポリエステルポリオール成分を用いることで、柔軟性とガスバリア性とを共に付与することが可能となり、高いガスバリア性と優れた接着強度とを両立することができる。これにより、本発明のラミネート接着剤を用いた積層体及び包装体は、食品、医薬品、化粧品、洗剤、雑貨等の様々な用途における包装体として利用することができる。
以下に本発明の実施の形態を詳細に説明するが、以下に記載する構成要件の説明は、本発明の実施態様の一例であり、本発明はその要旨を超えない限りこれらの内容に限定されない。
That is, by using a polyester polyol component in which diethylene glycol and at least one selected from the group consisting of isophthalic acid and terephthalic acid are used in a specific blending ratio and combined, both flexibility and gas barrier property can be imparted. This makes it possible to achieve both high gas barrier properties and excellent adhesive strength. As a result, the laminate and the package using the laminate adhesive of the present invention can be used as a package in various uses such as foods, pharmaceuticals, cosmetics, detergents, and miscellaneous goods.
Hereinafter, embodiments of the present invention will be described in detail, but the description of the constituent elements described below is an example of an embodiment of the present invention, and the present invention is not limited to these contents as long as the gist thereof is not exceeded. ..
<ポリオール>
本発明のガスバリア性ラミネート接着剤は、ポリオールとポリイソシアネートとを含む2液硬化型のウレタン系ラミネート接着剤であり、ポリオールとして、ジエチレングリコールを50〜100モル%含む多価アルコールと、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を50〜90モル%含む多価カルボン酸とから構成されるポリエステルポリオール成分を含むものである。
<Polyol>
The gas barrier laminating adhesive of the present invention is a two-component curable urethane-based laminating adhesive containing a polyol and a polyisocyanate, and as the polyol, a polyhydric alcohol containing 50 to 100 mol% of diethylene glycol, isophthalic acid and terephthalic acid. It contains a polyester polyol component composed of a polyvalent carboxylic acid containing 50 to 90 mol% of at least one selected from the group consisting of acids.
<ポリエステルポリオール成分>
本発明におけるポリエステルポリオール成分は、多価カルボン酸と多価アルコールとを反応させて得られるものであり、多価アルコールが、ジエチレングリコールを、多価アルコール全量を基準として50〜100モル%含み、多価カルボン酸が、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を、多価カルボン酸全量を基準として50〜90モル%含んでいればよく、1種を単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
ジエチレングリコール以外に用いてもよい多価アルコールとしては、例えば、エチレングリコール、プロピレングリコール、ジプロピレングリコール、トリエチレングリコール、ブチレングリコール、ネオペンチルグリコール、ジネオペンチルグリコール、トリメチロールプロパン、グリセリン、1,6−ヘキサンジオール、1,4−ブタンジオール、1,4−シクロヘキサンジメタノール、3−メチル−1,5−ペンタンジオール、3,3′−ジメチロールヘプタン、1,9−ノナンジオール、ポリオキシエチレングリコール、ポリオキシプロピレングリコール、ポリテトラメチレンエーテルグリコール、ポリエーテルポリオール、ポリカーボネートポリオール、ポリオレフィンポリオール、アクリルポリオール、ポリウレタンポリオール等のジオール類若しくはそれらの混合物が挙げられる。
イソフタル酸及びテレフタル酸以外に用いてもよい多価カルボン酸としては、例えば、ナフタレンジカルボン酸、無水フタル酸、アジピン酸、アゼライン酸、セバシン酸、コハク酸、グルタル酸、無水テトラヒドロフタル酸、無水ヘキサヒドロフタル酸、無水マレイン酸、無水イタコン酸等の二塩基酸若しくはそれらのジアルキルエステル又はそれらの混合物が挙げられる。
これらの多価カルボン酸及び多価アルコールは、各々1種を単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
<Polyester polyol component>
The polyester polyol component in the present invention is obtained by reacting a polyvalent carboxylic acid with a polyhydric alcohol, and the polyhydric alcohol contains diethylene glycol in an amount of 50 to 100 mol% based on the total amount of the polyhydric alcohol. The valent carboxylic acid may contain at least one selected from the group consisting of isophthalic acid and terephthalic acid in an amount of 50 to 90 mol% based on the total amount of the polyvalent carboxylic acid, and one type may be used alone. Two or more types may be used in combination.
Polyhydric alcohols that may be used in addition to diethylene glycol include, for example, ethylene glycol, propylene glycol, dipropylene glycol, triethylene glycol, butylene glycol, neopentyl glycol, dineopentyl glycol, trimethylolpropane, glycerin, 1,6. -Hexanediol, 1,4-butanediol, 1,4-cyclohexanedimethanol, 3-methyl-1,5-pentanediol, 3,3'-dimethylolheptan, 1,9-nonanediol, polyoxyethylene glycol , Polyoxypropylene glycol, polytetramethylene ether glycol, polyether polyol, polycarbonate polyol, polyolefin polyol, acrylic polyol, polyurethane polyol and other diols or mixtures thereof.
Examples of polyvalent carboxylic acids that may be used in addition to isophthalic acid and terephthalic acid include naphthalenedicarboxylic acid, phthalic anhydride, adipic acid, azelaic acid, sebacic acid, succinic acid, glutaric acid, tetrahydrophthalic anhydride, and hexachloride. Examples thereof include dibasic acids such as hydrophthalic acid, maleic anhydride and itaconic anhydride, dialkyl esters thereof, or mixtures thereof.
Each of these polyvalent carboxylic acids and polyhydric alcohols may be used alone or in combination of two or more.
ジエチレングリコールの含有量は、多価アルコール全量を基準として、好ましくは60〜90モル%であり、より好ましくは60〜80モル%である。イソフタル酸及びテレフタル酸の合計含有量は、多価カルボン酸全量を基準として、好ましくは60〜90モル%であり、より好ましくは70〜90モル%である。上記配合比率とすることで、良好なガスバリア性を発現するため好ましい。 The content of diethylene glycol is preferably 60 to 90 mol%, more preferably 60 to 80 mol%, based on the total amount of the polyhydric alcohol. The total content of isophthalic acid and terephthalic acid is preferably 60 to 90 mol%, more preferably 70 to 90 mol%, based on the total amount of the polyvalent carboxylic acid. It is preferable to use the above compounding ratio because it exhibits good gas barrier properties.
本発明におけるポリエステルポリオール成分は変性されていてもよく、ポリエステルポリオールにジイソシアネートを反応させたポリエステルウレタンポリオールであってもよいし、ポリエステルポリオールに酸無水物を反応させてカルボキシル基を導入したものであってもよい。
上記ジイソシアネートとしては、例えば、2,4−トリレンジイソシアネート、2,6−トリレンジイソシアネート、キシリレンジイソシアネート、ジフェニルメタンジイソシアネート、イソホロンジイソシアネート、1,5−ナフタレンジイソシアネート、ヘキサメチレンジイソシアネート、水添化ジフェニルメタンジイソシアネートが挙げられる。
上記酸無水物としては、例えば、無水ピロメリット酸、無水メリト酸、無水トリメリット酸、トリメリット酸エステル無水物が挙げられる。トリメリット酸エステル無水物としては、例えば、炭素数2〜30のアルキレングリコール又はアルカントリオールを無水トリメリット酸でエステル化反応させてなるエステル化合物が挙げられ、具体的には、エチレングリコールビスアンヒドロトリメリテート、プロピレングリコールビスアンヒドロトリメリテート等が挙げられる。
The polyester polyol component in the present invention may be modified, may be a polyester urethane polyol obtained by reacting a polyester polyol with a diisocyanate, or may be a polyester polyol reacted with an acid anhydride to introduce a carboxyl group. You may.
Examples of the diisocyanate include 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, xylylene diisocyanate, diphenylmethane diisocyanate, isophorone diisocyanate, 1,5-naphthalenedi isocyanate, hexamethylene diisocyanate, and hydrogenated diphenylmethane diisocyanate. Can be mentioned.
Examples of the acid anhydride include pyromellitic anhydride, mellitic anhydride, trimellitic anhydride, and trimellitic acid ester anhydride. Examples of the trimellitic acid ester anhydride include an ester compound obtained by esterifying alkylene glycol or alcantriol having 2 to 30 carbon atoms with trimellitic anhydride, and specific examples thereof include ethylene glycol bisuanhydro. Examples thereof include trimellitate and propylene glycol bisanhydrotrimellitate.
ポリエステルポリオール成分の数平均分子量(Mn)は、塗工性の観点から、好ましくは1,000〜6,000であり、より好ましくは5,000以下である。数平均分子量が1,000〜6,000の範囲であると、塗工性に優れラミネートフィルムの外観に優れるため好ましい。
本明細書の数平均分子量は、昭和電工社製GPC(ゲルパーミエーションクロマトグラフィー)「ShodexGPCSystem−21」を用い、溶媒としてテトロヒドロフランを用いて、標準ポリスチレン換算した値である。ポリエステルポリオール成分が、複数のポリエステルポリオールを含む場合、ポリエステルポリオール成分の数平均分子量は、各々のポリエステルポリオールの数平均分子量とその質量比率から求めることができる。
The number average molecular weight (Mn) of the polyester polyol component is preferably 1,000 to 6,000, more preferably 5,000 or less, from the viewpoint of coatability. A number average molecular weight in the range of 1,000 to 6,000 is preferable because it is excellent in coatability and the appearance of the laminated film is excellent.
The number average molecular weight of the present specification is a value converted to standard polystyrene using GPC (gel permeation chromatography) "Shodex GPC System-21" manufactured by Showa Denko KK and Tetrohydrofuran as a solvent. When the polyester polyol component contains a plurality of polyester polyols, the number average molecular weight of the polyester polyol component can be obtained from the number average molecular weight of each polyester polyol and its mass ratio.
ポリエステルポリオール成分の酸価は、好ましくは0.1〜10mgKOH/gであり、より好ましくは0.1〜5mgKOH/gである。酸価が0.1mgKOH/g以上であるとアルミ基材に対する接着性が向上し、5mgKOH/g以下であると、基材塗工後の外観が向上するため好ましい。ポリエステルポリオール成分が複数のポリエステルポリオールを含む場合、ポリエステルポリオールの酸価は、各々のポリエステルポリオールの酸価とその質量比率から求めることができる。 The acid value of the polyester polyol component is preferably 0.1 to 10 mgKOH / g, more preferably 0.1 to 5 mgKOH / g. When the acid value is 0.1 mgKOH / g or more, the adhesiveness to the aluminum base material is improved, and when the acid value is 5 mgKOH / g or less, the appearance after coating the base material is improved, which is preferable. When the polyester polyol component contains a plurality of polyester polyols, the acid value of the polyester polyol can be obtained from the acid value of each polyester polyol and its mass ratio.
ポリエステルポリオール成分は、ポリオール全量を基準として、好ましくは90質量%以上であり、より好ましくは95質量%以上である。95質量%以上含むことで、ラミネート接着剤に、十分な柔軟性とガスバリア性とが付与されるため、好ましい。 The polyester polyol component is preferably 90% by mass or more, more preferably 95% by mass or more, based on the total amount of the polyol. A content of 95% by mass or more is preferable because it imparts sufficient flexibility and gas barrier properties to the laminated adhesive.
<その他ポリオール>
本発明におけるポリオールは、本発明の効果を損なわない範囲で、上記ポリエステルポリオール成分以外のポリオールを含有することができる。含んでもよいその他のポリオールとしては、例えば、ポリカプロラクトン、ポリバレロラクトン、ポリ(β−メチル−γ−バレロラクトン)等のラクトン類を開環重合して得られるポリエステルポリオール、ポリカーボネートポリオール、ポリカプロラクトンポリオール、ポリエーテルポリオール、ポリオレフィンポリオール、アクリルポリオール、シリコーンポリオール、ヒマシ油系ポリオール、フッ素系ポリオールが挙げられ、ポリオール中の水酸基の一部が酸変性された酸変性物であってもよいし、酸無水物を反応させてカルボキシ基を導入したものや、ジイソシアネートを反応させてウレタン結合を導入したものであってもよい。
これらのその他のポリオールは、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。
<Other polyols>
The polyol in the present invention may contain a polyol other than the polyester polyol component as long as the effect of the present invention is not impaired. Examples of other polyols that may be contained include polyester polyols, polycarbonate polyols, and polycaprolactone polyols obtained by ring-opening polymerization of lactones such as polycaprolactone, polyvalerolactone, and poly (β-methyl-γ-valerolactone). , Polyester polyol, polyolefin polyol, acrylic polyol, silicone polyol, castor oil-based polyol, fluorine-based polyol, and may be an acid-modified product in which some of the hydroxyl groups in the polyol are acid-modified, or acid anhydrous. It may be one in which a carboxy group is introduced by reacting an object, or one in which a urethane bond is introduced by reacting a diisocyanate.
These other polyols may be used alone or in combination of two or more.
<ポリイソシアネート>
本発明のポリイソシアネートは、イソシアネート基を2つ以上有する化合物であればよく、公知のポリイソシアネートから選択することができる。ポリイソシアネートとしては、例えば、芳香族ポリイソシアネート、芳香脂肪族ポリイソシアネート、脂肪族ポリイソシアネート、又は脂環族ポリイソシアネートが挙げられ、変性された変性体であってもよい。これらのポリイソシアネートは1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。
<Polyisocyanate>
The polyisocyanate of the present invention may be any compound having two or more isocyanate groups, and can be selected from known polyisocyanates. Examples of the polyisocyanate include aromatic polyisocyanates, aromatic aliphatic polyisocyanates, aliphatic polyisocyanates, and alicyclic polyisocyanates, which may be modified products. One of these polyisocyanates may be used alone, or two or more thereof may be used in combination.
芳香族ポリイソシアネートとしては、例えば、ジフェニルメタンジイソシアネート、カルボジイミド変性ジフェニルメタンジイソシアネート、フェニレンジイソシアネート、トリレンジイソシアネート、ナフタレンジイソシアネートのような芳香族ジイソシアネート;ポリメチレンポリフェニルポリイソシアネートのような芳香族ポリイソシアネート;が挙げられる。
芳香脂肪族ポリイソシアネートとしては、例えば、1,3−又は1,4−キシリレンジイソシアネート若しくはその混合物、ω,ω′−ジイソシアネート−1,4−ジエチルベンゼン、1,3−又は1,4−ビス(1−イソシアネート−1−メチルエチル)ベンゼン若しくはその混合物等の芳香脂肪族ジイソシアネート;が挙げられる。
脂肪族ポリイソシアネートとしては、例えば、トリメチレンジイソシアネート、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、1,2−プロピレンジイソシアネート、1,2−ブチレンジイソシアネート、2,3−ブチレンジイソシアネート、1,3−ブチレンジイソシアネート、2,4,4−又は2,2,4−トリメチルヘキサメチレンジイソシアネート、2,6−ジイソシアネートメチルカプロエート、リジンジイソシアネート、ダイマー酸ジイソシアネートのような脂肪族ジイソシアネート;が挙げられる。
脂環族ポリイソシアネートとしては、例えば、1,4−シクロヘキサンジイソシアネート、1,3−シクロヘキサンジイソシアネート、イソホロンジイソシアネート、4,4′−メチレンビス(シクロヘキシルイソシアネート)、メチル2,4−シクロヘキサンジイソシアネート、メチル2,6−シクロヘキサンジイソシアネート、1,4−ビス(イソシアネートメチル)シクロヘキサン、1,3−ビス(イソシアネートメチル)シクロヘキサン、ノルボルネンジイソシアネート等の脂環式ジイソシアネート;が挙げられる。
Examples of the aromatic polyisocyanate include aromatic diisocyanates such as diphenylmethane diisocyanate, carbodiimide-modified diphenylmethane diisocyanate, phenylenediocyanate, tolylene diisocyanate, and naphthalene diisocyanate; and aromatic polyisocyanates such as polymethylene polyphenyl polyisocyanate. ..
Examples of the aromatic aliphatic polyisocyanate include 1,3- or 1,4-xylylene diisocyanate or a mixture thereof, ω, ω'-diisocyanate-1,4-diethylbenzene, 1,3- or 1,4-bis (). 1-Isocyanate-1-methylethyl) Arophilic aliphatic diisocyanates such as benzene or a mixture thereof;
Examples of the aliphatic polyisocyanate include trimethylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, 1,2-propylene diisocyanate, 1,2-butylene diisocyanate, 2,3-butylene diisocyanate, 1,3-butylene diisocyanate, and 2 , 4,4- or 2,2,4-trimethylhexamethylene diisocyanate, 2,6-diisocyanate methyl caproate, lysine diisocyanate, aliphatic diisocyanates such as diisocyanate dimerate;
Examples of the alicyclic polyisocyanate include 1,4-cyclohexanediisocyanate, 1,3-cyclohexanediisocyanate, isophorone diisocyanate, 4,4'-methylenebis (cyclohexylisocyanate), methyl2,4-cyclohexanediisocyanate, and methyl2,6. -Alicyclic diisocyanates such as cyclohexanediisocyanate, 1,4-bis (isocyanatemethyl) cyclohexane, 1,3-bis (isocyanatemethyl) cyclohexane, and norbornenediisocyanate; can be mentioned.
ポリイソシアネートの変性体としては、例えば、アロファネート型変性体、イソシアヌレート型変性体、ビウレット型変性体、アダクト型変性体のほか、上記ポリイソシアネート成分とポリオールとをイソシアネート基過剰の条件下に反応させたイソシアネート基とウレタン結合とを有する反応生成物が挙げられる。
上記ポリイソシアネートの変性体を形成するポリオールとしては、特に制限されず、公知のポリオールから選択することができ、例えば、ポリエステルポリオール、ポリエステルウレタンポリオール、ポリカーボネートポリオール、ポリカプロラクトンポリオール、ポリエーテルポリオール、ポリエーテルウレタンポリオール、ポリオレフィンポリオール、アクリルポリオール、シリコーンポリオール、ヒマシ油系ポリオール、フッ素系ポリオールが挙げられる。
Examples of the modified polyisocyanate include an allophanate-type modified product, an isocyanurate-type modified product, a biuret-type modified product, and an adduct-type modified product, and the above-mentioned polyisocyanate component and a polyol are reacted under the condition of excess isocyanate group. Examples thereof include reaction products having an isocyanate group and a urethane bond.
The polyol forming the modified product of the polyisocyanate is not particularly limited and can be selected from known polyols. For example, polyester polyol, polyester urethane polyol, polycarbonate polyol, polycaprolactone polyol, polyether polyol, polyether. Examples thereof include urethane polyols, polyolefin polyols, acrylic polyols, silicone polyols, castor oil-based polyols, and fluorine-based polyols.
ポリイソシアネートは、接着性とガスバリア性の観点から、好ましくは、芳香族ポリイソシアネート及び芳香脂肪族ポリイソシアネートからなる群から選ばれる少なくとも1種のポリイソシアネートの変性体であり、より好ましくは、トリレンジイソシアネート又はキシリレンジイソシアネートのトリメチロールプロパンとのアダクト体である。 From the viewpoint of adhesiveness and gas barrier property, the polyisocyanate is preferably a modified product of at least one polyisocyanate selected from the group consisting of aromatic polyisocyanates and aromatic aliphatic polyisocyanates, and more preferably trimethylolpropane. It is an adduct of isocyanate or xylylene diisocyanate with trimethylolpropane.
<単官能アルコール>
本発明のラミネート接着剤は、ポリオールとポリイソシアネート以外に、さらに分子量150以下の単官能アルコールを含有してもよい。分子量150以下の単官能アルコールを含有することで、単官能アルコールとポリイソシアネートとが反応し塗膜が柔軟化し、ラミネート強度が向上するため好ましい。
分子量150以下の単官能アルコールの含有量は、好ましくはポリエステルポリオール成分を基準として0.3〜2質量%である。0.3質量%以上であると接着強度が向上し、2質量%以下であるとガスバリア性が向上するため好ましい。これら単官能アルコールは、1種を檀独で用いてもよく、2種以上を組み合わせて用いてもよい。
分子量150以下の単官能アルコールとしては、例えば、1−ブタノール、1−プロパノール、1−ペンタノール、1−ヘキサノール、1−ヘプタノール、1−オクタノール、2−エチルヘキサノール、1−ノナノール、ベンジルアルコールが挙げられる。
<Monofunctional alcohol>
In addition to the polyol and polyisocyanate, the laminate adhesive of the present invention may further contain a monofunctional alcohol having a molecular weight of 150 or less. By containing a monofunctional alcohol having a molecular weight of 150 or less, the monofunctional alcohol reacts with the polyisocyanate to soften the coating film and improve the lamination strength, which is preferable.
The content of the monofunctional alcohol having a molecular weight of 150 or less is preferably 0.3 to 2% by mass based on the polyester polyol component. When it is 0.3% by mass or more, the adhesive strength is improved, and when it is 2% by mass or less, the gas barrier property is improved, which is preferable. These monofunctional alcohols may be used alone or in combination of two or more.
Examples of monofunctional alcohols having a molecular weight of 150 or less include 1-butanol, 1-propanol, 1-pentanol, 1-hexanol, 1-heptanol, 1-octanol, 2-ethylhexanol, 1-nonanol, and benzyl alcohol. Be done.
<溶剤>
本発明の接着剤は、溶剤型又は無溶剤型の接着剤として使用することができ、必要に応じて溶剤を含有してもよい。なお本発明の「溶剤」とは、上記ポリオールやポリイソシアネートを溶解可能な溶解性の高い有機溶剤を指す。
上記溶解性の高い有機溶剤としては、例えば、トルエン、キシレン、塩化メチレン、テトラヒドロフラン、メタノール、エタノール、イソプロピルアルコール、酢酸メチル、酢酸エチル、酢酸n−ブチル、アセトン、メチルエチルケトン、シクロヘキサノン、トルオール、キシロール、n−ヘキサン、シクロヘキサンが挙げられる。有機溶剤として好ましくは、ポリイソシアネートに対して不活性なものであり、例えば、酢酸エチル等のエステル系;メチルエチルケトン等のケトン系;トルエン、キシレン等の芳香族炭化水素系;が挙げられる。
<Solvent>
The adhesive of the present invention can be used as a solvent-type or solvent-free adhesive, and may contain a solvent if necessary. The "solvent" of the present invention refers to a highly soluble organic solvent capable of dissolving the above-mentioned polyol or polyisocyanate.
Examples of the highly soluble organic solvent include toluene, xylene, methylene chloride, tetrahydrofuran, methanol, ethanol, isopropyl alcohol, methyl acetate, ethyl acetate, n-butyl acetate, acetone, methyl ethyl ketone, cyclohexanone, toluol, xylol, n. -Hexene and cyclohexane can be mentioned. The organic solvent is preferably inert to polyisocyanate, and examples thereof include ester-based solvents such as ethyl acetate; ketone-based solvents such as methyl ethyl ketone; aromatic hydrocarbon-based solvents such as toluene and xylene.
本発明のラミネート接着剤の粘度は、常温〜150℃において好ましくは100〜10,000mPa・s、より好ましくは100〜5,000mPa・sであり、さらに好ましくは常温〜100℃において100〜10,000mPa・s、より好ましくは100〜5,000mPa・sである。常温〜100℃において100〜5,000mPa・sである場合は、無溶剤型の接着剤として用いることができる。
接着剤の粘度が上記範囲より高い場合は、上記有機溶剤で希釈してもよい。有機溶剤の含有量は所要される粘度によるが、一般的に接着剤樹脂に対して50〜70質量%の範囲で含有することが望ましい。
The viscosity of the laminate adhesive of the present invention is preferably 100 to 10,000 mPa · s at room temperature to 150 ° C., more preferably 100 to 5,000 mPa · s, and even more preferably 100 to 10 mPa · s at room temperature to 100 ° C. It is 000 mPa · s, more preferably 100 to 5,000 mPa · s. When it is 100 to 5,000 mPa · s at room temperature to 100 ° C., it can be used as a solvent-free adhesive.
If the viscosity of the adhesive is higher than the above range, it may be diluted with the above organic solvent. The content of the organic solvent depends on the required viscosity, but it is generally desirable to contain the organic solvent in the range of 50 to 70% by mass with respect to the adhesive resin.
本発明のラミネート接着剤は、特定のポリエステルポリオール成分を含むポリオール及びポリイソシアネートを配合して得られる2液硬化型のウレタン系接着剤であって、ポリオールとポリイソシアネートとの配合割合は特に制限されないが、好ましくは、前記イソシアネートが含有する全イソシアネート基と、前記ポリオールが含有する全水酸基とのモル当量比[NCOモル数/OHモル数]が0.3〜5.0の範囲であり、より好ましくは0.3〜2.0の範囲、さらに好ましくは0.5〜1.5の範囲である。 The laminate adhesive of the present invention is a two-component curable urethane-based adhesive obtained by blending a polyol containing a specific polyester polyol component and a polyisocyanate, and the blending ratio of the polyol and the polyisocyanate is not particularly limited. However, preferably, the molar equivalent ratio [NCO molar number / OH molar number] of the total isocyanate groups contained in the isocyanate to the total hydroxyl groups contained in the polyol is in the range of 0.3 to 5.0, and more. It is preferably in the range of 0.3 to 2.0, more preferably in the range of 0.5 to 1.5.
また、ポリイソシアネートの配合量は、ポリオール100質量部を基準として、好ましくは10〜50質量部である。10質量部以上であると良好なガスバリア性を発揮し、50質量部以下であると、良好な接着強度を発揮するため好ましい。 The blending amount of the polyisocyanate is preferably 10 to 50 parts by mass based on 100 parts by mass of the polyol. When it is 10 parts by mass or more, good gas barrier property is exhibited, and when it is 50 parts by mass or less, good adhesive strength is exhibited, which is preferable.
本発明のラミネート接着剤は、ポリオール及びポリイソシアネートを配合した直後の酸価が、0.1〜9mgKOH/gであることが好ましく、より好ましくは0.1〜8mgKOH/gであり、さらに好ましく0.1〜5mgKOH/gである。上記範囲内であると、接着強度がより向上するため好ましい。 The laminated adhesive of the present invention preferably has an acid value of 0.1 to 9 mgKOH / g immediately after blending the polyol and polyisocyanate, more preferably 0.1 to 8 mgKOH / g, and further preferably 0. .1-5 mgKOH / g. When it is within the above range, the adhesive strength is further improved, which is preferable.
<その他成分>
本発明のラミネート接着剤は、接着剤又は包装材料に要求される各種物性を満たすために、ポリオール及びポリイソシアネート以外のその他成分を含有してもよい。これらのその他成分は、ポリオール又はポリイソシアネートのいずれに配合してもよいし、ポリオールとポリイソシアネートとを配合する際に配合してもよい。これらのその他成分は、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。
<Other ingredients>
The laminated adhesive of the present invention may contain other components other than polyol and polyisocyanate in order to satisfy various physical properties required for the adhesive or packaging material. These other components may be blended with either a polyol or a polyisocyanate, or may be blended when the polyol and the polyisocyanate are blended. These other components may be used alone or in combination of two or more.
(シランカップリング剤)
本発明のラミネート接着剤は、耐熱水性を高めるため、さらにシランカップリング剤を含有することができる。シランカップリング剤としては、例えば、ビニルトリメトキシシラン、ビニルトリエトキシシランのようなビニル基を有するトリアルコキシシラン;3−アミノプロピルトリエトキシシラン、N−(2−アミノエチル)3−アミノプロピルトリメトキシシランのようなアミノ基を有するトリアルコキシシラン;3−グリシドキシプロピルトリメトキシシラン、2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、3−グリシドキシプロピルトリエトキシシランのようなグリシジル基を有するトリアルコキシシラン;が挙げられる。シランカップリング剤の配合量は、接着剤の固形分を基準として、好ましくは0.1〜5質量%であり、より好ましくは0.5〜3質量%である。
(Silane coupling agent)
The laminated adhesive of the present invention can further contain a silane coupling agent in order to increase heat resistance and water resistance. Examples of the silane coupling agent include trialkoxysilanes having a vinyl group such as vinyltrimethoxysilane and vinyltriethoxysilane; 3-aminopropyltriethoxysilane and N- (2-aminoethyl) 3-aminopropyltri. Trialkoxysilanes with amino groups such as methoxysilane; such as 3-glycidoxypropyltrimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane Trialkoxysilanes having a glycidyl group; The blending amount of the silane coupling agent is preferably 0.1 to 5% by mass, more preferably 0.5 to 3% by mass, based on the solid content of the adhesive.
(リンの酸素酸又はその誘導体)
本発明のラミネート接着剤は、耐酸性を高めるため、さらにリンの酸素酸又はその誘導体を含有することができる。リンの酸素酸又はその誘導体の内、リンの酸素酸としては、遊離の酸素酸を少なくとも1個有しているものであればよく、例えば、次亜リン酸、亜リン酸、オルトリン酸、次リン酸のようなリン酸類;メタリン酸、ピロリン酸、トリポリリン酸、ポリリン酸、ウルトラリン酸のような縮合リン酸類;が挙げられる。また、リンの酸素酸の誘導体としては、例えば、上記のリンの酸素酸を遊離の酸素酸を少なくとも1個残した状態でアルコール類と部分的にエステル化されたものが挙げられる。これらのアルコールとしては、メタノール、エタノール、エチレングリコール、グリセリンのような脂肪族アルコール;フェノール、キシレノール、ハイドロキノン、カテコール、フロログリシノールのような芳香族アルコール;が挙げられる。リンの酸素酸又はその誘導体の配合量は、接着剤の固形分を基準として、好ましくは0.01〜10質量%であり、より好ましくは0.05〜5質量%であり、さらに好ましくは0.1〜1質量%である。
(Oxygen acid of phosphorus or its derivative)
The laminated adhesive of the present invention may further contain an oxygen acid of phosphorus or a derivative thereof in order to enhance acid resistance. Among the oxygen acids of phosphorus or derivatives thereof, the oxygen acid of phosphorus may be any one having at least one free oxygen acid, for example, hypophosphoric acid, phosphoric acid, orthophosphoric acid, the following. Phosphoric acids such as phosphoric acid; condensed phosphoric acids such as metaphosphoric acid, pyrophosphoric acid, tripolyphosphoric acid, polyphosphoric acid, ultraphosphoric acid; Examples of the derivative of the oxygen acid of phosphorus include those in which the oxygen acid of phosphorus is partially esterified with alcohols while leaving at least one free oxygen acid. Examples of these alcohols include aliphatic alcohols such as methanol, ethanol, ethylene glycol and glycerin; aromatic alcohols such as phenol, xylenol, hydroquinone, catechol and fluoroglycinol. The blending amount of the oxygen acid of phosphorus or a derivative thereof is preferably 0.01 to 10% by mass, more preferably 0.05 to 5% by mass, and further preferably 0, based on the solid content of the adhesive. .1-1% by mass.
(レベリング剤又は消泡剤)
本発明のラミネート接着剤は、積層体の外観を向上させるため、さらにレベリング剤又は消泡剤を含有することができる。レベリング剤としては、例えば、ポリエーテル変性ポリジメチルシロキサン、ポリエステル変性ポリジメチルシロキサン、アラルキル変性ポリメチルアルキルシロキサン、ポリエステル変性水酸基含有ポリジメチルシロキサン、ポリエーテルエステル変性水酸基含有ポリジメチルシロキサン、アクリル系共重合物、メタクリル系共重合物、ポリエーテル変性ポリメチルアルキルシロキサン、アクリル酸アルキルエステル共重合物、メタクリル酸アルキルエステル共重合物、レシチンが挙げられる。
消泡剤としては、例えば、シリコーン樹脂、シリコーン溶液、アルキルビニルエーテルとアクリル酸アルキルエステルとメタクリル酸アルキルエステルとの共重合物が挙げられる。
(Leveling agent or antifoaming agent)
The laminated adhesive of the present invention may further contain a leveling agent or an antifoaming agent in order to improve the appearance of the laminated body. Examples of the leveling agent include polyether-modified polydimethylsiloxane, polyester-modified polydimethylsiloxane, aralkyl-modified polymethylalkylsiloxane, polyester-modified hydroxyl group-containing polydimethylsiloxane, polyether ester-modified hydroxyl group-containing polydimethylsiloxane, and acrylic copolymer. , Methacrylic copolymers, polyether-modified polymethylalkylsiloxanes, acrylic acid alkyl ester copolymers, methacrylic acid alkyl ester copolymers, and lecithin.
Examples of the defoaming agent include a silicone resin, a silicone solution, and a copolymer of an alkyl vinyl ether, an acrylic acid alkyl ester, and a methacrylic acid alkyl ester.
(反応促進剤)
本発明のラミネート接着剤は、ポリオールとポリイソシアネートとのウレタン化硬化反応を促進するため、さらに反応促進剤を含有することができる。反応促進剤としては、例えば、ジブチルチンジアセテート、ジブチルチンジラウレート、ジオクチルチンジラウレート、ジブチルチンジマレートのような金属系触媒;1,8−ジアザ−ビシクロ(5,4,0)ウンデセン−7、1,5−ジアザビシクロ(4,3,0)ノネン−5、6−ジブチルアミノ−1,8−ジアザビシクロ(5,4,0)ウンデセン−7のような3級アミン;トリエタノールアミンのような反応性3級アミン;が挙げられる。
(Reaction accelerator)
Since the laminate adhesive of the present invention promotes the urethanization curing reaction between the polyol and the polyisocyanate, it can further contain a reaction accelerator. Reaction accelerators include, for example, metal-based catalysts such as dibutyltin diacetate, dibutyltin dilaurate, dioctyltin dilaurate, dibutyltin dimalate; 1,8-diazabicyclo (5,4,0) undecene-7,1 , 5-Diazabicyclo (4,5,0) Nonen-5,6-dibutylamino-1,8-Diazabicyclo (5,4,0) Undecene-7 and other tertiary amines; Reactive like triethanolamine Tertiary amines;
(板状無機化合物)
本発明のラミネート接着剤は、より高いガスバリア性を付与する目的で、さらに板状無機化合物を含有してもよい。板状無機化合物を併用した場合、形状が板状であることにより、バリア性だけでなくラミネート強度が向上する傾向がある。本発明で使用してもよい板状無機化合物としては、例えば、含水ケイ酸塩(フィロケイ酸塩鉱物等)、カオリナイト−蛇紋族粘土鉱物(ハロイサイト、カオリナイト、エンデライト、ディッカイト、ナクライト等、アンチゴライト、クリソタイル等)、パイロフィライト−タルク族(パイロフィライト、タルク、ケロライ等)、スメクタイト族粘土鉱物(モンモリロナイト、バイデライト、ノントロナイト、サポナイト、ヘクトライト、ソーコナイト、スチブンサイト等)、バーミキュライト族粘土鉱物(バーミキュライト等)、雲母又はマイカ族粘土鉱物(白雲母、金雲母等の雲母、マーガライト、テトラシリリックマイカ、テニオライト等)、緑泥石族(クッケアイト、スドーアイト、クリノクロア、シャモサイト、ニマイト等)、ハイドロタルサイト、板状硫酸バリウム、ベーマイト、ポリリン酸アルミニウムが挙げられる。
これらの鉱物は天然粘土鉱物であっても合成粘土鉱物であってもよい。
(Plate-shaped inorganic compound)
The laminated adhesive of the present invention may further contain a plate-like inorganic compound for the purpose of imparting higher gas barrier properties. When a plate-shaped inorganic compound is used in combination, not only the barrier property but also the lamination strength tends to be improved due to the plate-like shape. Plate-like inorganic compounds that may be used in the present invention include, for example, hydrous silicates (phylosilicate minerals, etc.), kaolinite-serpentine clay minerals (halosite, kaolinite, enderite, dikite, nacrite, etc.). Antigolite, chrysotile, etc.), Pyrophyllite-Tark (Pyrophyllite, Tarku, Kerorai, etc.), Smectite clay minerals (Montmorillonite, Bidelite, Nontronite, Saponite, Hectrite, Sauconite, Stevensite, etc.), Vermiculite Group clay minerals (vermiculite, etc.), mica or mica group clay minerals (white mica, gold mica, etc., margarite, tetrasilic mica, teniolite, etc.) Etc.), hydrotalcite, plate-shaped barium sulfate, mica, aluminum polyphosphate.
These minerals may be natural clay minerals or synthetic clay minerals.
上記板状無機化合物を用いる際は、ラミネート接着剤中に分散されていることが好ましい。分散方法は特に制限されないが、分散機を用いて分散することが好ましく、分散機としては、例えば、超音波ホモジナイザー、高圧ホモジナイザー、ペイントコンディショナー、ボールミル、ロールミル、サンドミル、サンドグラインダー、ダイノーミル、ディスパーマット、ナノミル、SCミル、ナノマイザーが挙げられる。分散機としてより好ましくは、高い剪断力を発生させることのできる機器であり、例えば、ヘンシェルミキサー、加圧ニーダー、バンバリーミキサー、プラネタリーミキサー、二本ロール、三本ロールが挙げられる。
これら分散機は、1種の装置を単独で用いてもよいし、2種類以上の装置を組み合わせて用いてもよい。
When the plate-shaped inorganic compound is used, it is preferably dispersed in the laminate adhesive. The dispersion method is not particularly limited, but it is preferable to disperse using a disperser. Examples of the disperser include an ultrasonic homogenizer, a high-pressure homogenizer, a paint conditioner, a ball mill, a roll mill, a sand mill, a sand grinder, a dyno mill, and a dispermat. Examples include nanomills, SC mills, and nanomizers. More preferably, the disperser is a device capable of generating a high shearing force, and examples thereof include a Henschel mixer, a pressurized kneader, a Banbury mixer, a planetary mixer, a two-roll, and a three-roll.
For these dispersers, one type of device may be used alone, or two or more types of devices may be used in combination.
(添加剤)
本発明のラミネート接着剤は、本発明の効果を損なわない範囲で、各種の添加剤を含有してもよい。添加剤としては、例えば、シリカ、アルミナ、マイカ、タルク、アルミニウムフレーク、ガラスフレーク等の無機充填剤、安定剤(酸化防止剤、熱安定剤、紫外線吸収剤、加水分解防止剤等)、防錆剤、増粘剤、可塑剤、帯電防止剤、滑剤、ブロッキング防止剤、着色剤、フィラー、結晶核剤、硬化反応を調整するための触媒が挙げられる。
(Additive)
The laminated adhesive of the present invention may contain various additives as long as the effects of the present invention are not impaired. Additives include, for example, inorganic fillers such as silica, alumina, mica, talc, aluminum flakes, and glass flakes, stabilizers (antioxidants, heat stabilizers, ultraviolet absorbers, hydrolysis inhibitors, etc.), and rust preventives. Examples thereof include agents, thickeners, plasticizers, antistatic agents, lubricants, antiblocking agents, colorants, fillers, crystal nucleating agents, and catalysts for adjusting the curing reaction.
本発明の接着剤は、被接着物同士の貼り合わせた後、20℃〜60℃の温度条件下にて硬化させることにより接着剤の硬化反応が進行し硬化物となる。接着剤の用途は、特定されるべきものではないが、複数のフィルム等の基材をラミネートして積層体とする際の接着剤として有用である。 The adhesive of the present invention is formed into a cured product by adhering the adherends to each other and then curing the adhesive under temperature conditions of 20 ° C. to 60 ° C. to promote the curing reaction of the adhesive. The use of the adhesive should not be specified, but it is useful as an adhesive when laminating base materials such as a plurality of films to form a laminate.
<積層体>
本発明の積層体は、上述のラミネート接着剤からなる接着剤層が、少なくとも2つの基材の間に配置されたものであり、接着剤による優れたガスバリア性を示す。該積層体は、例えば、ラミネート接着剤を第1の基材に塗布し、必要に応じて乾燥工程を経た後に、第2の基材を貼り合わせ、両基材の間に位置する前記接着剤層を硬化して形成することができるが、この構成に限定されず、さらに接着剤層等を介して別の層が配置されていてもよい。
接着剤の乾燥後塗布量は任意であるが、接着強度とガスバリア性発現の観点から、無溶剤型接着剤の場合は、好ましくは1〜4g/m2、より好ましくは1〜2g/m2の範囲であり、溶剤型接着剤の場合は、好ましくは1〜6g/m2、より好ましくは2〜4g/m2の範囲である。また、積層体の厚みは、包装材としての強度や耐久性の観点から、好ましくは10μm以上である。
<Laminated body>
In the laminate of the present invention, an adhesive layer made of the above-mentioned laminated adhesive is arranged between at least two base materials, and exhibits excellent gas barrier properties due to the adhesive. In the laminate, for example, a laminate adhesive is applied to a first base material, and after undergoing a drying step if necessary, a second base material is bonded to the laminate, and the adhesive is located between the two base materials. The layer can be formed by curing, but the present invention is not limited to this, and another layer may be further arranged via an adhesive layer or the like.
The amount of the adhesive applied after drying is arbitrary, but from the viewpoint of adhesive strength and gas barrier property development, the solvent-free adhesive is preferably 1 to 4 g / m 2 , more preferably 1 to 2 g / m 2. In the case of a solvent-based adhesive, the range is preferably 1 to 6 g / m 2 , and more preferably 2 to 4 g / m 2. The thickness of the laminate is preferably 10 μm or more from the viewpoint of strength and durability as a packaging material.
[基材]
基材は特に制限されず、包装体用途に一般的に使用される、プラスチックフィルム、紙、ガスバリア基材、シーラント等が挙げられ、2つの基材は同種であってもよく、異種であってもよい。
プラスチックフィルムとしては、例えば、ポリエチレンテレフタレート、ポリエチレンナフタレート(PEN)、ポリ乳酸(PLA)等のポリエステル樹脂フィルム;ポリエチレン(PE)、ポリプロピレン(PP)等のポリオレフィン樹脂フィルム;ポリスチレン樹脂フィルム;ナイロン6、ポリ−p−キシリレンアジパミド(MXD6ナイロン)等のポリアミド樹脂フィルム;ポリカーボネート樹脂フィルム;ポリアクリルニトリル樹脂フィルム;ポリイミド樹脂フィルム;これらの複層体(例えば、ナイロン6/MXD6/ナイロン6、ナイロン6/エチレン−ビニルアルコール共重合体/ナイロン6)や混合体等が用いられる。中でも、機械的強度や寸法安定性を有するものが好ましい。
プラスチックフィルムは、好ましくは5〜50μm、より好ましくは10〜30μmの厚さを有するものである。
[Base material]
The base material is not particularly limited, and examples thereof include plastic films, papers, gas barrier base materials, sealants, etc., which are generally used for packaging applications, and the two base materials may be of the same type or different types. May be good.
Examples of the plastic film include polyester resin films such as polyethylene terephthalate, polyethylene naphthalate (PEN), and polylactic acid (PLA); polyolefin resin films such as polyethylene (PE) and polypropylene (PP); polystyrene resin films; nylon 6, Polyamide resin film such as poly-p-xylylene adipamide (MXD6 nylon); polycarbonate resin film; polyacrylic nitrile resin film; polyimide resin film; these multilayer bodies (for example, nylon 6 / MXD6 / nylon 6, nylon) 6 / ethylene-vinyl alcohol copolymer / nylon 6) or a mixture or the like is used. Among them, those having mechanical strength and dimensional stability are preferable.
The plastic film preferably has a thickness of 5 to 50 μm, more preferably 10 to 30 μm.
紙としては、天然紙や合成紙等が挙げられる。
ガスバリア基材としては、アルミニウム箔の他、アルミニウム、シリカ、アルミナ等の蒸着層を有するプラスチックフィルムが好ましい。例えばアルミニウム箔の場合は、経済的な面から3〜50μmの範囲の厚みが好ましい。
Examples of paper include natural paper and synthetic paper.
As the gas barrier base material, a plastic film having a vapor-deposited layer of aluminum, silica, alumina or the like is preferable in addition to the aluminum foil. For example, in the case of aluminum foil, a thickness in the range of 3 to 50 μm is preferable from the economical point of view.
シーラントとしては、例えば、低密度ポリエチレン(LDPE)、直鎖状低密度ポリエチレン(LLDPE)や高密度ポリエチレン(HDPE)等のポリエチレン、酸変性ポリエチレン、ポリプロピレン(PP)、酸変性ポリプロピレン、共重合ポリプロピレン、エチレン−ビニルアセテート共重合体、エチレン−(メタ)アクリル酸エステル共重合体、エチレン−(メタ)アクリル酸共重合体、アイオノマー等のポリオレフィン樹脂等が挙げられる。中でもレトルト時の耐熱性の観点から、ポリプロピレン系樹脂が好ましく、ヒートシール性の観点から未延伸ポリプロピレンが特に好ましい。
シーラントの厚みは特に限定されないが、包装体への加工性やヒートシール性等を考慮して10〜60μmの範囲が好ましく、15〜40μmの範囲がより好ましい。また、シーラントに高低差5〜20μmの凸凹を設けることで、シーラントに滑り性や包装体の引き裂き性を付与することが可能である。
また、各種シーラントはアルミニウム箔の他、アルミニウム、シリカ、アルミナ等の蒸着層を有していてもよい。
Examples of the sealant include polyethylene such as low-density polyethylene (LDPE), linear low-density polyethylene (LLDPE) and high-density polyethylene (HDPE), acid-modified polyethylene, polypropylene (PP), acid-modified polypropylene, and copolymerized polypropylene. Examples thereof include an ethylene-vinyl acetate copolymer, an ethylene- (meth) acrylic acid ester copolymer, an ethylene- (meth) acrylic acid copolymer, and a polyolefin resin such as ionomer. Among them, polypropylene-based resin is preferable from the viewpoint of heat resistance at the time of retort, and unstretched polypropylene is particularly preferable from the viewpoint of heat sealability.
The thickness of the sealant is not particularly limited, but is preferably in the range of 10 to 60 μm, more preferably in the range of 15 to 40 μm, in consideration of processability to the package, heat sealability, and the like. Further, by providing the sealant with irregularities having a height difference of 5 to 20 μm, it is possible to impart slipperiness and tearability of the package to the sealant.
Further, various sealants may have a vapor-deposited layer of aluminum, silica, alumina or the like in addition to the aluminum foil.
基材は、基材上に印刷層を有していてもよい。印刷層は、装飾、内容物の表示、賞味期間の表示、製造者、販売者などの表示、その他などの表示や美感の付与のために、文字、数字、絵柄、図形、記号、模様などの所望の任意の印刷模様を形成する層であり、ベタ印刷層も含む。印刷層は、従来公知の顔料や染料を用いて形成することができ、印刷層の形成方法は特に限定されない。
一般的には、印刷層は、顔料や染料等の着色剤を含む印刷インキを用いて形成される。印刷インキの塗工方法は特に限定されず、グラビアコート法、フレキソコート法、ロールコート法、バーコート法、ダイコート法、カーテンコート法、スピンコート法、インクジェット法等の方法により塗布することができる。これを放置するか、必要により送風、加熱、減圧乾燥、紫外線照射等を行うことにより印刷層を形成することができる。
印刷層は、好ましくは0.1〜10μm、より好ましくは1〜5μm、さらに好ましくは1〜3μmの厚さを有するものである。
The base material may have a printing layer on the base material. The printing layer is used for decoration, display of contents, display of expiration date, display of manufacturers, sellers, etc., and for display of other things and giving aesthetics, such as letters, numbers, patterns, figures, symbols, patterns, etc. A layer that forms any desired print pattern, including a solid print layer. The print layer can be formed by using a conventionally known pigment or dye, and the method for forming the print layer is not particularly limited.
Generally, the printing layer is formed by using a printing ink containing a colorant such as a pigment or a dye. The method of applying the printing ink is not particularly limited, and the printing ink can be applied by a method such as a gravure coating method, a flexographic coating method, a roll coating method, a bar coating method, a die coating method, a curtain coating method, a spin coating method, or an inkjet method. .. The printed layer can be formed by leaving it as it is or, if necessary, by blowing air, heating, drying under reduced pressure, irradiating with ultraviolet rays, or the like.
The printed layer preferably has a thickness of 0.1 to 10 μm, more preferably 1 to 5 μm, and even more preferably 1 to 3 μm.
積層体の構成は特に限定されないが、少なくとも1層以上のプラスチックフィルムやガスバリア基材と、シーラントとを積層した構成であることが好ましい。
具体的な積層体構成としては、レトルトパウチ等に好適に用いることが可能な、2軸延伸ポリプロピレン(OPP)/接着剤層/無延伸ポリプロピレン(CPP)、OPP/接着剤層/AL蒸着CPP、ナイロン(NY)/接着剤層/PE、NY/接着剤層/CPP、PET/接着剤層/NY/接着剤層/CPP、透明蒸着PET/接着剤層/NY/接着剤層/CPP、PET/接着剤層/AL/接着剤層/CPP、PET/接着剤層/AL/接着剤層/PE、PET/接着剤層/NY/接着剤層/AL/接着剤層/CPP、PET/接着剤層/AL/接着剤層/NY/接着剤層/CPP等が挙げられる。
これら積層体は、必要に応じて、プライマー層やトップコート層等を有していてもよい。
The structure of the laminated body is not particularly limited, but a structure in which at least one or more layers of a plastic film or gas barrier base material and a sealant are laminated is preferable.
Specific laminate configurations include biaxially stretched polypropylene (OPP) / adhesive layer / non-stretched polypropylene (CPP), OPP / adhesive layer / AL vapor-deposited CPP, which can be suitably used for retort pouches and the like. Nylon (NY) / adhesive layer / PE, NY / adhesive layer / CPP, PET / adhesive layer / NY / adhesive layer / CPP, transparent vapor-deposited PET / adhesive layer / NY / adhesive layer / CPP, PET / Adhesive layer / AL / Adhesive layer / CPP, PET / Adhesive layer / AL / Adhesive layer / PE, PET / Adhesive layer / NY / Adhesive layer / AL / Adhesive layer / CPP, PET / Adhesive Examples thereof include agent layer / AL / adhesive layer / NY / adhesive layer / CPP.
These laminates may have a primer layer, a top coat layer, or the like, if necessary.
本発明の積層体は、良好なガスバリア性を有することから、食品包装用パウチの他、洗剤、薬剤等の詰め替え用パウチ等に好適に用いることができる。 Since the laminate of the present invention has a good gas barrier property, it can be suitably used for a pouch for food packaging, a pouch for refilling detergents, chemicals, and the like.
以下、実施例及び比較例を挙げて本発明を更に具体的に説明する。実施例及び比較例中の「部」及び「%」は、特に断りの無い限り「質量部」及び「質量%」を意味する。 Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. “Parts” and “%” in Examples and Comparative Examples mean “parts by mass” and “% by mass” unless otherwise specified.
<酸価の測定>
酸価の測定は以下の手順で行った。まず、共栓三角フラスコ中に試料約1gを精密に量り採り、トルエン/エタノール(容量比:トルエン/エタノール=2/1)混合液100mlを加えて溶解し、フェノールフタレイン試液を指示薬として加え、30秒間保持した。その後、溶液が淡紅色を呈するまで0.1Nアルコール性水酸化カリウム溶液で滴定し、次式により酸価を求めた。
酸価(mgKOH/g)=(5.611×a×F)/S
S:試料の採取量(g)
a:0.1Nアルコール性水酸化カリウム溶液の消費量(ml)
F:0.1Nアルコール性水酸化カリウム溶液のファクター
<Measurement of acid value>
The acid value was measured according to the following procedure. First, about 1 g of a sample is precisely weighed in an Erlenmeyer flask with a stopper, and 100 ml of a toluene / ethanol (volume ratio: toluene / ethanol = 2/1) mixed solution is added to dissolve the sample, and a phenolphthalein test solution is added as an indicator. It was held for 30 seconds. Then, the solution was titrated with a 0.1 N alcoholic potassium hydroxide solution until the solution turned pink, and the acid value was determined by the following formula.
Acid value (mgKOH / g) = (5.611 × a × F) / S
S: Sample collection amount (g)
a: Consumption of 0.1N alcoholic potassium hydroxide solution (ml)
F: Factor of 0.1N alcoholic potassium hydroxide solution
<ポリエステルポリオール成分の製造>
(製造例1)ポリエステルポリオール(P−1)
四つ口セパラブルフラスコにイソフタル酸320部、アジピン酸31部、ジエチレングリコール212部、エチレングリコール23部、ネオペンチルグリコール13部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量5,000、酸価0.3mgKOH/gのポリエステルポリオール(P−1)溶液を得た。
<Manufacturing of polyester polyol component>
(Production Example 1) Polyester polyol (P-1)
320 parts of isophthalic acid, 31 parts of adipic acid, 212 parts of diethylene glycol, 23 parts of ethylene glycol and 13 parts of neopentyl glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-1) solution having an acid value of 0.3 mgKOH / g was obtained.
(製造例2)ポリエステルポリオール(P−2)
四つ口セパラブルフラスコにイソフタル酸161部、テレフタル酸161部、アジピン酸31部、ジエチレングリコール214部、エチレングリコール31部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量6,000、酸価0.3mgKOH/gのポリエステルポリオール(P−2)溶液を得た。
(Production Example 2) Polyester polyol (P-2)
161 parts of isophthalic acid, 161 parts of terephthalic acid, 31 parts of adipic acid, 214 parts of diethylene glycol and 31 parts of ethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-2) solution having an acid value of 0.3 mgKOH / g was obtained.
(製造例3)ポリエステルポリオール(P−3)
四つ口セパラブルフラスコにイソフタル酸260部、アジピン酸98部、ジエチレングリコール193部、エチレングリコール48部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量3,000、酸価0.3mgKOH/gのポリエステルポリオール(P−3)溶液を得た。
(Production Example 3) Polyester polyol (P-3)
260 parts of isophthalic acid, 98 parts of adipic acid, 193 parts of diethylene glycol and 48 parts of ethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-3) solution having an acid value of 0.3 mgKOH / g was obtained.
(製造例4)ポリエステルポリオール(P−4)
四つ口セパラブルフラスコにイソフタル酸279部、アジピン酸61部、ジエチレングリコール259部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量5,000、酸価0.3mgKOH/gのポリエステルポリオール(P−4)溶液を得た。
(Production Example 4) Polyester polyol (P-4)
279 parts of isophthalic acid, 61 parts of adipic acid and 259 parts of diethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-4) solution having an acid value of 0.3 mgKOH / g was obtained.
(製造例5)ポリエステルポリオール(P−5)
四つ口セパラブルフラスコにイソフタル酸324部、アジピン酸32部、ジエチレングリコール133部、エチレングリコール31部、ネオペンチルグリコール79部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量9,000、酸価0.3mgKOH/gのポリエステルポリオール(P−5)溶液を得た。
(Production Example 5) Polyester polyol (P-5)
324 parts of isophthalic acid, 32 parts of adipic acid, 133 parts of diethylene glycol, 31 parts of ethylene glycol and 79 parts of neopentyl glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. for 5 hours, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-5) solution having an acid value of 0.3 mgKOH / g was obtained.
(製造例6)ポリエステルポリオール(P−6)
四つ口セパラブルフラスコにイソフタル酸144部、テレフタル酸144部、アジピン酸63部、ジエチレングリコール215部、エチレングリコール31部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量5,000、酸価0.3mgKOH/gのポリエステルポリオール(P−6)溶液を得た。
(Production Example 6) Polyester polyol (P-6)
144 parts of isophthalic acid, 144 parts of terephthalic acid, 63 parts of adipic acid, 215 parts of diethylene glycol, and 31 parts of ethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-6) solution having an acid value of 0.3 mgKOH / g was obtained.
(製造例7)ポリエステルポリオール(P−7)
四つ口セパラブルフラスコにイソフタル酸178部、アジピン酸156部、ジエチレングリコール265部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量2,000、酸価0.3mgKOH/gのポリエステルポリオール(P−7)溶液を得た。
(Production Example 7) Polyester polyol (P-7)
178 parts of isophthalic acid, 156 parts of adipic acid and 265 parts of diethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. for 5 hours, and then diluted with ethyl acetate until the non-volatile content reaches 50%. A polyester polyol (P-7) solution having an acid value of 0.3 mgKOH / g was obtained.
(比較製造例1)ポリエステルポリオール(P−8)
四つ口セパラブルフラスコにイソフタル酸356部、アジピン酸35部、ジエチレングリコール88部、エチレングリコール120部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量6,000、酸価0.3mgKOH/gのポリエステルポリオール(P−8)溶液を得た。
(Comparative Production Example 1) Polyester Polyol (P-8)
356 parts of isophthalic acid, 35 parts of adipic acid, 88 parts of diethylene glycol, and 120 parts of ethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-8) solution having an acid value of 0.3 mgKOH / g was obtained.
(比較製造例2)ポリエステルポリオール(P−9)
四つ口セパラブルフラスコにイソフタル酸358部、ジエチレングリコール133部、エチレングリコール31部、ネオペンチルグリコール78部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量6,000、酸価0.3mgKOH/gのポリエステルポリオール(P−9)溶液を得た。
(Comparative Production Example 2) Polyester Polyol (P-9)
358 parts of isophthalic acid, 133 parts of diethylene glycol, 31 parts of ethylene glycol and 78 parts of neopentyl glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-9) solution having an acid value of 0.3 mgKOH / g was obtained.
(比較製造例3)ポリエステルポリオール(P−10)
四つ口セパラブルフラスコにイソフタル酸72部、テレフタル酸72部、アジピン酸190部、ジエチレングリコール267部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量1,500、酸価0.3mgKOH/gのポリエステルポリオール(P−10)溶液を得た。
(Comparative Production Example 3) Polyester Polyol (P-10)
72 parts of isophthalic acid, 72 parts of terephthalic acid, 190 parts of adipic acid and 267 parts of diethylene glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-10) solution having 500 and an acid value of 0.3 mgKOH / g was obtained.
(比較製造例4)ポリエステルポリオール(P−11)
四つ口セパラブルフラスコにイソフタル酸300部、アジピン酸113部、エチレングリコール186部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量5,000、酸価0.3mgKOH/gのポリエステルポリオール(P−11)溶液を得た。
(Comparative Production Example 4) Polyester Polyol (P-11)
300 parts of isophthalic acid, 113 parts of adipic acid and 186 parts of ethylene glycol were charged in a four-necked separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-11) solution having an acid value of 0.3 mgKOH / g was obtained.
(比較製造例5)ポリエステルポリオール(P−12)
四つ口セパラブルフラスコにイソフタル酸350部、アジピン酸34部、エチレングリコール101部、ネオペンチルグリコール113部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量5,000、酸価0.3mgKOH/gのポリエステルポリオール(P−12)溶液を得た。
(Comparative Production Example 5) Polyester Polyol (P-12)
350 parts of isophthalic acid, 34 parts of adipic acid, 101 parts of ethylene glycol and 113 parts of neopentyl glycol were charged in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-12) solution having an acid value of 0.3 mgKOH / g was obtained.
(比較製造例6)ポリエステルポリオール(P−13)
四つ口セパラブルフラスコにイソフタル酸386部、エチレングリコール100部、ネオペンチルグリコール112部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量9,000、酸価0.3mgKOH/gのポリエステルポリオール(P−13)溶液を得た。
(Comparative Production Example 6) Polyester Polyol (P-13)
386 parts of isophthalic acid, 100 parts of ethylene glycol, and 112 parts of neopentyl glycol were placed in a four-neck separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. for 5 hours, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-13) solution having an acid value of 0.3 mgKOH / g was obtained.
(比較製造例7)ポリエステルポリオール(P−14)
四つ口セパラブルフラスコに無水フタル酸206部、エチレングリコール150.6部、コハク酸60部を仕込み、220〜260℃でエステル化反応を行った。所定量の水の留出後、徐々に減圧し1mmHg以下で240〜260℃で5時間脱グリコール反応を行い、次いで不揮発分50%になるまで酢酸エチルで希釈することで、数平均分子量1,800、酸価0.9mgKOH/gのポリエステルポリオール(P−14)溶液を得た。
(Comparative Production Example 7) Polyester Polyol (P-14)
206 parts of phthalic anhydride, 150.6 parts of ethylene glycol and 60 parts of succinic acid were placed in a four-necked separable flask, and an esterification reaction was carried out at 220 to 260 ° C. After distilling out a predetermined amount of water, the pressure is gradually reduced, a deglycolation reaction is carried out at 240 to 260 ° C. at 240 to 260 ° C. at 1 mmHg or less, and then diluted with ethyl acetate until the non-volatile content becomes 50%. A polyester polyol (P-14) solution having 800 and an acid value of 0.9 mgKOH / g was obtained.
得られたポリエステルポリオールを表1に示す。表1中の多価カルボン酸及び多価アルコールの数値は、多価カルボン酸又は多価アルコール全量を基準とした場合の、各成分の含有量(モル%)を表す。 The obtained polyester polyol is shown in Table 1. The numerical values of the polyvalent carboxylic acid and the polyhydric alcohol in Table 1 represent the content (mol%) of each component based on the total amount of the polyvalent carboxylic acid or the polyhydric alcohol.
<ラミネート接着剤の製造>
[実施例1〜10、比較例1〜8]
製造例1〜7及び比較製造例1〜7で得られたポリエステルポリオール溶液、ポリイソシアネート、単官能アルコール及びその他の成分を、表2に示す割合(質量比)で配合し、酢酸エチルを加えて不揮発分30%の接着剤溶液を調整した。
<Manufacturing of laminated adhesive>
[Examples 1 to 10, Comparative Examples 1 to 8]
The polyester polyol solution, polyisocyanate, monofunctional alcohol and other components obtained in Production Examples 1 to 7 and Comparative Production Examples 1 to 7 were blended in the ratio (mass ratio) shown in Table 2, and ethyl acetate was added. An adhesive solution having a non-volatile content of 30% was prepared.
<ラミネート接着剤の評価>
得られた接着剤溶液を用いて積層体を作製し、以下の評価を行った。結果を表2に示す。
<Evaluation of laminated adhesive>
A laminate was prepared using the obtained adhesive solution, and the following evaluation was performed. The results are shown in Table 2.
(積層体の作製)
ラミネーターを用いて、接着剤溶液を常温にてPETフィルム(東洋紡株式会社製:E5102、厚み12μm)に塗布し、溶剤を揮散させた後、塗布面をアルミ蒸着CPPフィルム(東レフィルム加工株式会社製:VMCPP2203、厚み25μm)のアルミ蒸着側と貼り合わせた。次いで、得られた積層体を40℃で3日間保温し、接着剤を硬化させて、PETフィルム/接着剤層/アルミ蒸着CPPフィルムの構成である積層体を得た。接着剤の塗布量は、3.5g/m2とした。
(Preparation of laminate)
Using a laminator, apply the adhesive solution to a PET film (manufactured by Toyo Boseki Co., Ltd .: E5102, thickness 12 μm) at room temperature, volatilize the solvent, and then surface the coated surface with an aluminum-deposited CPP film (manufactured by Toray Film Processing Co., Ltd.). : VMCPP2203, thickness 25 μm) was bonded to the aluminum vapor deposition side. Next, the obtained laminate was kept warm at 40 ° C. for 3 days, and the adhesive was cured to obtain a laminate having a composition of PET film / adhesive layer / aluminum-deposited CPP film. The amount of the adhesive applied was 3.5 g / m 2 .
(外観評価)
得られた積層体の外観を目視で観察し、下記基準で評価を行った。
◎:外観に気泡、濡れムラが全く確認されない(非常に良好)
○:外観に気泡は若干あるものの、濡れムラは確認されない(良好)
△:若干の気泡が確認される(使用可能)
×:多くの気泡が確認される(使用不可)
(Appearance evaluation)
The appearance of the obtained laminate was visually observed and evaluated according to the following criteria.
◎: No air bubbles or uneven wetting are confirmed on the appearance (very good)
◯: Although there are some bubbles in the appearance, uneven wetting is not confirmed (good).
Δ: Some bubbles are confirmed (usable)
×: Many bubbles are confirmed (cannot be used)
(ラミネート強度)
得られた積層体から、15mm×300mmの大きさの試験片を切り出し、引張り試験機を用い、温度20℃、相対湿度65%の条件下で、T型剥離により剥離速度30cm/分で、PETフィルム/アルミ蒸着CPPフィルム間のラミネート強度(N/15mm)を測定し、下記基準で評価した。
◎:ラミネート強度が1.0N/15mm以上(非常に良好)
○:ラミネート強度が0.8N/15mm以上、1.0N/15mm未満(良好)
△:ラミネート強度が0.5N/15mm以上、0.8N/15mm未満(使用可能)
×:ラミネート強度が0.5N/15mm未満(使用不可)
(Laminate strength)
A test piece having a size of 15 mm × 300 mm was cut out from the obtained laminate, and PET was subjected to T-type peeling at a peeling speed of 30 cm / min under the conditions of a temperature of 20 ° C. and a relative humidity of 65% using a tensile tester. The lamination strength (N / 15 mm) between the film / aluminum-deposited CPP film was measured and evaluated according to the following criteria.
⊚: Laminate strength is 1.0 N / 15 mm or more (very good)
◯: Laminate strength is 0.8 N / 15 mm or more and less than 1.0 N / 15 mm (good)
Δ: Laminate strength is 0.5 N / 15 mm or more and less than 0.8 N / 15 mm (usable)
X: Laminate strength is less than 0.5N / 15mm (cannot be used)
(ガスバリア性)
得られた積層体について、温度23℃、相対湿度0%RH条件の酸素透過度を測定し、以下の基準で評価した。酸素透過度の測定は、MOCON社製酸素透過率測定装置 OX−TRAN2/21を用い、JIS K 7126に準拠して、等圧法にて行った。
◎:酸素透過度が1.0cc/m2・day・atm未満(非常に良好)
○:酸素透過度が1.0cc/m2・day・atm以上、1.5cc/m2・day・atm未満(良好)
△:酸素透過度が1.5cc/m2・day・atm以上、2.0cc/m2・day・atm未満(使用可能)
×:酸素透過度が2.0cc/m2・day・atm以上(使用不可)
(Gas barrier property)
The obtained laminate was measured for oxygen permeability under a temperature of 23 ° C. and a relative humidity of 0% RH, and evaluated according to the following criteria. The oxygen permeability was measured by the isobaric method in accordance with JIS K 7126 using the oxygen permeability measuring device OX-TRAN2 / 21 manufactured by MOCON.
⊚: Oxygen permeability is less than 1.0 cc / m 2 , day, atm (very good)
◯: Oxygen permeability is 1.0 cc / m 2・ day ・ atm or more and less than 1.5 cc / m 2・ day ・ atm (good)
Δ: Oxygen permeability is 1.5 cc / m 2 · day · atm or more and less than 2.0 cc / m 2 · day · atm (usable)
X: Oxygen permeability is 2.0 cc / m 2 , day, atm or more (cannot be used)
表2中の略称を以下に示す。
2−エチルヘキサノール:分子量130.2
ベンジルアルコール:分子量108.1
CAT−RT1: 東洋モートン社製、脂環族ポリイソシアネート
CAT−RT8: 東洋モートン社製、芳香脂肪族ポリイソシアネート
CAT−10L: 東洋モートン社製、芳香族ポリイソシアネート
The abbreviations in Table 2 are shown below.
2-Ethylhexanol: molecular weight 130.2
Benzyl alcohol: molecular weight 108.1
CAT-RT1: Toyo Morton, alicyclic polyisocyanate CAT-RT8: Toyo Morton, aromatic aliphatic polyisocyanate CAT-10L: Toyo Morton, aromatic polyisocyanate
表2の結果によれば、ジエチレングリコールと、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種とを、特定の配合比率で用い組み合わせたポリエステルポリオール成分を用いた実施例1〜12は、高いガスバリア性と優れた接着強度とを示した。特にジエチレングリコールを、多価アルコール全量を基準として60モル%以上含有する実施例1〜6、8〜10は良好なガスバリア性を示した。また、分子量150以下の単管能アルコールを含む実施例4及び実施例5は、含まない実施例3と比較して、ラミネート強度に優れていた。
一方、ジエチレングリコールと、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種と、を特定の配合比率で用いていない比較例1〜8は、高いガスバリア性と優れた接着強度とを両立しなかった。
According to the results in Table 2, Examples 1 to 12 using the polyester polyol component in which diethylene glycol and at least one selected from the group consisting of isophthalic acid and terephthalic acid are used in a specific blending ratio and combined are high. It showed gas barrier properties and excellent adhesive strength. In particular, Examples 1 to 6 and 8 to 10 containing 60 mol% or more of diethylene glycol based on the total amount of the polyhydric alcohol showed good gas barrier properties. In addition, Examples 4 and 5 containing a monotubic alcohol having a molecular weight of 150 or less were superior in lamination strength as compared with Example 3 not containing it.
On the other hand, Comparative Examples 1 to 8 in which diethylene glycol and at least one selected from the group consisting of isophthalic acid and terephthalic acid were not used in a specific compounding ratio did not achieve both high gas barrier properties and excellent adhesive strength. rice field.
Claims (6)
前記多価アルコールがジエチレングリコールを、多価アルコール全量を基準として50〜100モル%含み、
前記多価カルボン酸が、イソフタル酸及びテレフタル酸からなる群から選ばれる少なくとも1種を、多価カルボン酸全量を基準として50〜90モル%含み、
さらに、分子量150以下の単官能アルコールを、前記ポリエステルポリオール成分を基準として0.3〜2質量%含む、ガスバリア性ラミネート接着剤。 A gas barrier laminating adhesive containing a polyester polyol component composed of a polyhydric alcohol and a polyvalent carboxylic acid, and a polyisocyanate.
The polyhydric alcohol contains diethylene glycol in an amount of 50 to 100 mol% based on the total amount of the polyhydric alcohol.
The polyvalent carboxylic acid, at least one selected from the group consisting of isophthalic acid and terephthalic acid, see containing 50 to 90 mol% based on the total amount polycarboxylic acid,
Further, a gas barrier laminating adhesive containing 0.3 to 2% by mass of a monofunctional alcohol having a molecular weight of 150 or less based on the polyester polyol component.