JP6754145B1 - Conductive fabric - Google Patents
Conductive fabric Download PDFInfo
- Publication number
- JP6754145B1 JP6754145B1 JP2019119601A JP2019119601A JP6754145B1 JP 6754145 B1 JP6754145 B1 JP 6754145B1 JP 2019119601 A JP2019119601 A JP 2019119601A JP 2019119601 A JP2019119601 A JP 2019119601A JP 6754145 B1 JP6754145 B1 JP 6754145B1
- Authority
- JP
- Japan
- Prior art keywords
- conductive
- conductive fabric
- fabric
- less
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】本発明は、被覆体への密着性と安定的な導電性、適度な伸縮性に優れる導電性生地を提供することを目的とする。【解決手段】本発明では、繊維径が30デニール以下の極細導電性繊維を用いた生地とすることで、接着樹脂部を生地の少なくとも一方の面にドット状に設けて目付を80g/m2以下とせしめ、被覆体への密着性と安定的な導電性を発揮し、かつ、適度な伸縮性に優れる導電性生地を得る。【選択図】なしPROBLEM TO BE SOLVED: To provide a conductive fabric having excellent adhesion to a covering body, stable conductivity, and appropriate elasticity. According to the present invention, by using an ultrafine conductive fiber having a fiber diameter of 30 denier or less, an adhesive resin portion is provided in a dot shape on at least one surface of the fabric to have a basis weight of 80 g / m2 or less. A conductive fabric that exhibits adhesion to a covering body and stable conductivity, and is excellent in appropriate elasticity can be obtained. [Selection diagram] None
Description
本発明は、極細導電性繊維からなる接着樹脂部が付与された導電性生地に関する。 The present invention relates to a conductive fabric to which an adhesive resin portion made of ultrafine conductive fibers is provided.
導電性繊維からなる生地は、特に、銀メッキ繊維を用いた編物や織物が、電磁波シールド用途や抗菌用途、遮熱用途等に用いられてきた。ところで近年導電性繊維は、IoT技術の進歩に応じて、特にウエアラブルデバイス用の素材として注目を集めている。 As for the fabric made of conductive fibers, in particular, knitted fabrics and woven fabrics using silver-plated fibers have been used for electromagnetic wave shielding applications, antibacterial applications, heat shielding applications and the like. By the way, in recent years, conductive fibers have been attracting attention as a material especially for wearable devices in accordance with the progress of IoT technology.
例えば、特許文献1には赤外線反射特性を有する織物の開示があるが、ウエアラブルデバイス用途への適用については言及がない。また、特許文献2には、導電性織物を複数積層した導電性繊維材料が高シールド性を発揮することについて開示があるが、こちらもウエアラブルデバイス用途については開示がない。 For example, Patent Document 1 discloses a woven fabric having infrared reflection characteristics, but does not mention its application to wearable device applications. Further, Patent Document 2 discloses that a conductive fiber material in which a plurality of conductive woven fabrics are laminated exhibits high shielding properties, but there is also no disclosure regarding wearable device applications.
導電性繊維をウエアラブルデバイス用途とする場合に要求される機能として、着心地やバイタルデータ測定のための密着性、そしてデータ取得のための安定的な導電性が求められる。 When conductive fibers are used as wearable devices, the functions required are comfort, adhesion for measuring vital data, and stable conductivity for data acquisition.
被覆体への密着性と安定的な導電性、適度な伸縮性に優れる導電性生地を提供することを目的とする。 It is an object of the present invention to provide a conductive fabric having excellent adhesion to a covering body, stable conductivity, and appropriate elasticity.
本発明では、繊維径が30デニール以下の極細導電性繊維を用いた生地とすることで、接着樹脂部を生地の少なくとも一方の面にドット状に設けても目付を80g/m2以下とせしめ、被覆体への密着性(接着性)と安定的な導電性を発揮し、かつ、適度な伸縮性に優れる導電性生地を得る。 In the present invention, by using an ultrafine conductive fiber having a fiber diameter of 30 denier or less, even if the adhesive resin portion is provided in a dot shape on at least one surface of the fabric, the grain size is reduced to 80 g / m 2 or less. A conductive fabric that exhibits adhesion (adhesiveness) to the covering body and stable conductivity, and is excellent in appropriate elasticity can be obtained.
すなわち、本発明によれば以下の導電性生地と導電性生地を含む積層導電性生地を提供する。
(1)接着樹脂部を付与した導電性生地であって、導電性生地に用いる導電性繊維の繊維径が30デニール以下、導電性生地の目付が80g/m2以下、接着樹脂部が導電性生地の少なくとも一方の面に離散的に分散して設けられている導電性生地。
(2)前記導電性繊維は、合成繊維にメッキコーティングした導電性繊維、または、合成繊維に導電性ポリマーをコーティングした導電性繊維の少なくともいずれか1つを含む上記(1)に記載の導電性生地。
(3)前記接着樹脂部は、ドット状に設けられている上記(1)又は(2)に記載の導電性生地。
(4)前記接着樹脂部のドット数が、5個/2.54cm以上50個/2.54cm以下であり、前記接着樹脂部の見掛け質量は、1g/m2以上15g/m2以下である上記(3)に記載の導電性生地。
(5)導電性生地の幅が縦横共に、70cm以上である上記(1)から上記(4)のいずれかに記載の導電性生地。
(6)上記(1)から上記(5)のいずれかに記載の導電性生地に、さらに導電性生地を1層以上3層以下積層接着させた積層導電性生地。
(7)引張り強さが200N以上、表面抵抗が1.5Ω以下である上記(6)に記載の積層導電性生地。
That is, according to the present invention, a laminated conductive fabric containing the following conductive fabric and the conductive fabric is provided.
(1) A conductive fabric to which an adhesive resin portion is provided, the fiber diameter of the conductive fiber used for the conductive fabric is 30 denier or less, the texture of the conductive fabric is 80 g / m 2 or less, and the adhesive resin portion is conductive. A conductive fabric that is discretely dispersed on at least one surface of the fabric.
(2) The conductivity according to (1) above, wherein the conductive fiber contains at least one of a conductive fiber coated with a coating on a synthetic fiber or a conductive fiber coated with a conductive polymer on a synthetic fiber. Cloth.
( 3 ) The conductive fabric according to (1) or (2) above, wherein the adhesive resin portion is provided in a dot shape.
(4) The number of dots of the adhesive resin portion is 5 / 2.54 cm or more and 50 / 2.54 cm or less, and the apparent mass of the adhesive resin portion is 1 g / m 2 or more and 15 g / m 2 or less. The conductive fabric according to (3) above.
(5) The conductive fabric according to any one of (1) to (4) above, wherein the width of the conductive fabric is 70 cm or more in both vertical and horizontal directions.
(6) A laminated conductive fabric obtained by laminating and adhering one or more and three or less conductive fabrics to the conductive fabric according to any one of (1) to (5) above.
(7) The laminated conductive fabric according to (6) above , wherein the tensile strength is 200 N or more and the surface resistance is 1.5 Ω or less.
本発明により、被覆体への密着性(接着性)と安定的な導電性、適度な伸縮性に優れる導電性生地を得る。 INDUSTRIAL APPLICABILITY According to the present invention, a conductive fabric having excellent adhesion (adhesiveness) to a covering body, stable conductivity, and appropriate elasticity can be obtained.
本発明は、接着樹脂部を付与した導電性生地であって、導電性生地に用いる導電性繊維の繊維径が30デニール以下、導電性生地の目付(以下、見掛け質量、とも言う)が80g/m2以下、接着樹脂部が導電性生地の少なくとも一方の面に離散的に分散して設けられている導電性生地である。 The present invention is a conductive fabric to which an adhesive resin portion is provided, and the fiber diameter of the conductive fiber used for the conductive fabric is 30 denier or less, and the texture of the conductive fabric (hereinafter, also referred to as apparent mass) is 80 g /. It is a conductive fabric in which m 2 or less and adhesive resin portions are discretely dispersed on at least one surface of the conductive fabric.
(導電性繊維)
導電性生地に用いられる導電性繊維の素材に特に制限は無く、合成繊維にメッキコーティングした導電性繊維や、合成繊維に導電性ポリマーをコーティングした導電性繊維のほか、合成繊維の中に導電性の良い金属やカーボンブラックを配合した導電性繊維や、金属を繊維化した金属繊維を用いることができる。合成繊維としては特に制限は無く、ポリイミド、6ナイロン、66ナイロンなどを用いることができる。
(Conductive fiber)
The material of the conductive fiber used for the conductive fabric is not particularly limited, and the synthetic fiber is plated and coated, the synthetic fiber is coated with the conductive polymer, and the synthetic fiber is conductive. It is possible to use a conductive fiber containing a good metal or carbon black, or a metal fiber made from a metal fiber. The synthetic fiber is not particularly limited, and polyimide, 6 nylon, 66 nylon and the like can be used.
中でも、導電性、折り曲げ耐性、軽量性、経済性の観点から、合成繊維にメッキコーティングした導電性繊維が好ましく用いられる。メッキの金属種としては、導電性の観点から、銀、銅が好ましく、更なる導電性、人体に対する安全性、及び抗菌性の観点から、銀がより好ましい。 Among them, conductive fibers plated and coated on synthetic fibers are preferably used from the viewpoints of conductivity, bending resistance, light weight, and economy. As the metal type for plating, silver and copper are preferable from the viewpoint of conductivity, and silver is more preferable from the viewpoint of further conductivity, safety to the human body, and antibacterial property.
導電性繊維の繊維径は、導電性生地とした際の被覆体への密着性(接着性)及び安定的な導電性、並びに伸縮性を兼ね備える観点から30デニール以下であれば問題なく使用できるが、25デニール以下がより好ましく、20デニール以下が更に好ましい。 The fiber diameter of the conductive fiber can be used without any problem as long as it is 30 denier or less from the viewpoint of having adhesion (adhesiveness) to the covering body, stable conductivity, and elasticity when the conductive fabric is used. , 25 denier or less is more preferable, and 20 denier or less is further preferable.
(導電性生地)
導電性生地は、導電性繊維を用いて編上げや織上げ、または抄紙等によって製造した生地に接着樹脂部を付与したものであり、樹脂接着部が導電性生地の少なくとも一方の面に離散的に分散して設けられている。
(Conductive fabric)
The conductive fabric is a fabric produced by knitting, weaving, or papermaking using conductive fibers, to which an adhesive resin portion is added, and the resin adhesive portions are discretely applied to at least one surface of the conductive fabric. It is provided in a distributed manner.
導電性生地は導電特性を維持しつつ、接着樹脂部を導電性生地の少なくとも一方の面に離散的に分散して設けることで、被覆体の伸縮性を損なうことなく、被覆体へ密着(接着)させることができる。 By providing the conductive fabric in a discrete manner on at least one surface of the conductive fabric while maintaining the conductive characteristics, the conductive fabric adheres (adhesively) to the coating without impairing the elasticity of the coating. ) Can be made.
導電性生地は、当該生地に、必要に応じてプレス加工、熱プレス加工、精練加工、熱セット加工などで構造を固定化、形状を記憶させても良い。当該生地を加工する際に、生地の面積を拡大させても良いし、拡大させなくても良い。また、当該加工において、必要に応じて、固定用の樹脂や接着剤を用いることができる。 The structure of the conductive dough may be fixed and the shape may be stored in the dough by press working, hot pressing, scouring, heat setting, or the like, if necessary. When processing the dough, the area of the dough may or may not be expanded. Further, in the processing, a fixing resin or an adhesive can be used, if necessary.
なお、ここでは、固定化、形状記憶の工程を仕上げ工程と言い、仕上げ工程を経た、例えば縦横の寸法を仕上げ幅といい、仕上げ工程前の寸法を編上げ幅などという。 Here, the process of immobilization and shape memory is referred to as a finishing process, the vertical and horizontal dimensions that have undergone the finishing process are referred to as a finishing width, and the dimensions before the finishing process are referred to as a knitting width.
生地の面積を拡大させる場合は、拡大前の生地の特性を損なわない範囲で拡大することが可能であるが、通常は生地に対して、1軸方向に、1.1倍から1.7倍、好ましくは1.1倍から1.5倍、より好ましくは1.1倍から1.3倍の範囲である。 When expanding the area of the dough, it is possible to enlarge the dough within a range that does not impair the characteristics of the dough before the enlargement, but usually, 1.1 to 1.7 times in the uniaxial direction with respect to the dough. It is preferably in the range of 1.1 times to 1.5 times, more preferably 1.1 times to 1.3 times.
接着樹脂部は、導電性生地用の生地、すなわち、導電性生地の両面に離散的に分散して設けることで導電性生地を積層し易くなる。導電性生地の透気度は300cm3/(cm2・s)以上であれば、伸縮性と被覆体への密着性(接着性)を発揮できる。 By providing the adhesive resin portion on the fabric for the conductive fabric, that is, on both sides of the conductive fabric in a discrete manner, the conductive fabric can be easily laminated. If the air permeability of the conductive fabric is 300 cm 3 / (cm 2 · s) or more, elasticity and adhesion to the covering body (adhesiveness) can be exhibited.
接着樹脂部に用いる樹脂は、一般の接着芯地で用いられるものであれば良く、例えば、熱可塑性樹脂や熱硬化樹脂を用いることができる。中でも、熱可塑性樹脂が好ましく、アクリル系樹脂、ポリアミド系樹脂、ポリ酸化ビニール系(PVC)ポリエチレン系樹脂、ポリエステル系樹脂、エチレン酢ビ共重合体系(EVA)樹脂がより好ましく用いられる。中でも、アクリル系樹脂、ポリアミド系樹脂が好ましく用いられるが、アクリル樹脂を離散的に分散して付与した後にポリアミド樹脂粉を被覆した樹脂が、接着性の観点から、さらに好ましく用いられる。 The resin used for the adhesive resin portion may be any resin used in a general adhesive interlining, and for example, a thermoplastic resin or a thermosetting resin can be used. Of these, thermoplastic resins are preferable, and acrylic resins, polyamide resins, polyvinyl chloride (PVC) polyethylene resins, polyester resins, and ethylene-vinyl acetate copolymer (EVA) resins are more preferably used. Of these, acrylic resins and polyamide resins are preferably used, but a resin coated with a polyamide resin powder after the acrylic resin is discretely dispersed and applied is more preferably used from the viewpoint of adhesiveness.
導電性生地用の生地の製法に特に制限はなく、導電性繊維の織りや編み、または抄紙によって作成された編物、織物、不織布を用いることができる。中でも、導電性、引張強さ、伸び率、引裂強さの観点から編物または織物が好ましい。編物の中でも経編と緯編があるが、経編で編んだ編物が導電性の観点からより好ましい。緯編で編んだ編物としては、例えば、平編、ゴム編、両面編パール編、タック編、浮き編、片畔編、レース編、添え毛編がある。経編で編んだ編物としては、例えば、シングルデンビー編、シングルアトラス編、ダブルコード編、ハーフ編、ハーフベース編、サテン編、ハーフトリコット編、裏毛編、ジャガード編がある。織物としては、平織、綾織、朱子織等の三原組織、変化組織、たて二十織、よこ二十織等の片二重組織、たてビロードなどが例示される。 There are no particular restrictions on the method for producing the fabric for the conductive fabric, and knitted fabrics, woven fabrics, and non-woven fabrics produced by weaving or knitting conductive fibers or papermaking can be used. Of these, knitted or woven fabrics are preferable from the viewpoints of conductivity, tensile strength, elongation, and tear strength. There are warp knits and weft knits among knits, but knits knitted by warp knits are more preferable from the viewpoint of conductivity. Examples of knits knitted by weft knit include flat knit, rubber knit, double-sided pearl knit, tack knit, floating knit, one-sided knit, lace knit, and hair-covered knit. Examples of knits knitted by warp knitting include single denby edition, single atlas edition, double chord edition, half edition, half base edition, satin edition, half tricot edition, fleece edition, and jacquard edition. Examples of the woven fabric include three original structures such as plain weave, twill weave, and satin weave, a changing structure, a single double structure such as vertical twenty weave and horizontal twenty weave, and vertical velvet.
また、導電性生地用の生地には、通常のカレンダー加工、エンボス加工等を適宜施すことができる。 Further, the fabric for the conductive fabric can be appropriately subjected to ordinary calendar processing, embossing or the like.
接着樹脂部の付与法に制限はないが、接着樹脂部を導電性生地用の生地の少なくとも一方の面に離散的に分散して設けることで、柔軟性及び伸縮性を確保することができる。さらに、傾向として目付が小さい場合には、接着樹脂部の付与密度を大きくして強度を高め、一方で、傾向として目付が大きい場合には、接着樹脂部の付与密度を小さくして透気度を上げることが好ましい。さらに、生産性の観点から、接着樹脂部のホットメルト法でドット状に設けることが好ましい。 There is no limitation on the method of applying the adhesive resin portion, but flexibility and elasticity can be ensured by providing the adhesive resin portion in a discrete manner on at least one surface of the fabric for the conductive fabric. Further, when the basis weight is small as a tendency, the imparting density of the adhesive resin portion is increased to increase the strength, while when the basis weight is large as a tendency, the imparting density of the adhesive resin portion is decreased to increase the air permeability. It is preferable to raise it. Further, from the viewpoint of productivity, it is preferable to provide the adhesive resin portion in a dot shape by a hot melt method.
特にロールトゥロール法にて連続的に接着樹脂部を付与する場合は、装置で連続的に搬送させる必要から、導電性繊維の幅方向(TD方向)が70cm以上であることが好ましい。 In particular, when the adhesive resin portion is continuously applied by the roll-to-roll method, the width direction (TD direction) of the conductive fiber is preferably 70 cm or more because it is necessary to continuously convey the adhesive resin portion by the apparatus.
ロールトゥロール法にて連続的に接着樹脂部を付与した導電性生地は、反物等の長尺生地として得る場合、継ぎ目無く70cm以上の採寸が可能となるため、導電性に優れるだけでなく、使い勝手にも優れる。例えば、大型のサーバーの電磁波シールド用途に好適に用いることができる。 When the conductive fabric to which the adhesive resin portion is continuously applied by the roll-to-roll method is obtained as a long fabric such as a cloth, it is possible to measure 70 cm or more seamlessly, so that it is not only excellent in conductivity but also excellent in conductivity. It is also easy to use. For example, it can be suitably used for electromagnetic wave shielding of a large server.
接着樹脂部をドット状に設ける場合のドット数は、導電性生地の導電特性を維持しつつ、伸縮性と被覆体への密着性を発揮する観点から5個/2.54cm以上50個/2.54cm以下が好ましく、20個/2.54cm以上40個/2.54cm以下がさらに好ましい。特にドット部がマイクロドットである場合の接着樹脂部のドット数は、50個/2.54cm以上500個/2.54cm以下が好ましく、200個/2.54cm以上400個/2.54cm以下がさらに好ましい。 When the adhesive resin portion is provided in a dot shape, the number of dots is 5 / 2.54 cm or more and 50/2 from the viewpoint of exhibiting elasticity and adhesion to the covering while maintaining the conductive characteristics of the conductive fabric. It is preferably .54 cm or less, and more preferably 20 pieces / 2.54 cm or more and 40 pieces / 2.54 cm or less. In particular, when the dot portion is a microdot, the number of dots in the adhesive resin portion is preferably 50 / 2.54 cm or more and 500 / 2.54 cm or less, and 200 / 2.54 cm or more and 400 / 2.54 cm or less. More preferred.
また、離散的に分散して設けられた接着樹脂部の重量は、導電性生地の導電特性を維持しつつ、伸縮性と被覆体への密着性を発揮する観点から1g/m2以上15g/m2以下であることが好ましく、5g/m2以上10g/m2以下であることがより好ましく、5g/m2以上8g/m2以下であることが最も好ましい。導電性生地は、さらに導電性生地用の生地を1層積層接着させた積層導電性生地としてもよい。これにより、被覆体への密着性と適度な伸縮性を維持しつつ、更に導電性を向上できる。 Further, the weight of the adhesive resin portions provided dispersedly dispersed is 1 g / m 2 or more and 15 g / m from the viewpoint of exhibiting elasticity and adhesion to the covering body while maintaining the conductive characteristics of the conductive fabric. preferably m 2 or less, more preferably 5 g / m 2 or more 10 g / m 2 or less, and most preferably 5 g / m 2 or more 8 g / m 2 or less. The conductive fabric may be a laminated conductive fabric in which one layer of the fabric for the conductive fabric is laminated and adhered. As a result, the conductivity can be further improved while maintaining the adhesion to the covering body and the appropriate elasticity.
また、導電性生地は、さらに導電性生地を1層以上3層以下積層接着させた積層導電性生地としてもよい。これにより、導電性が導電性生地用の生地と同等に優れたまま、引っ張り強さを導電性生地用の生地より向上することができる。 Further, the conductive fabric may be a laminated conductive fabric in which one or more and three or less layers of the conductive fabric are laminated and adhered. As a result, the tensile strength can be improved as compared with the fabric for the conductive fabric while the conductivity is as excellent as the fabric for the conductive fabric.
また、導電性生地用の生地から導電性生地を作成するときは、汎用性を上げる観点及び想定される使用用途に求められる抵抗値の観点から、測定位置に関わらず導電性の上げ幅が1.5Ω以下であることが好ましく、1.0Ω以下であることがより好ましい。特に、導電性生地を後述の実施例1と実施例2で調整した場合に、当該関係性は明確になる。 In addition, when making a conductive fabric from a fabric for conductive fabric, the increase in conductivity is 1.5Ω regardless of the measurement position from the viewpoint of increasing versatility and the resistance value required for the expected intended use. It is preferably 1 or less, and more preferably 1.0 Ω or less. In particular, when the conductive fabric is adjusted in Examples 1 and 2 described later, the relationship becomes clear.
積層導電性生地は、引張り強さが200N以上、表面抵抗が1.5Ω以下であることで、ウエアラブルセンサーなどのウエアラブル用途に好適に用いられるが、さらに、見掛け質量160g/m2以下、引張り強さが200N以上、伸び率40%以上、表面抵抗が1.5Ω以下であることで、ウエアラブルセンサーなどのウエアラブル用途により好適に用いられる。これまでの素材では、本素材と同等の見掛け重量を維持しつつ、引張り強さが200N以上、伸び率40%以上、表面抵抗が1.5Ω以下の条件を満たす素材は存在しなかったが、今回、これらの物性を達成することで、柔軟性、軽量性の要求度の高い衣料資材における副資材の基準を満たすことができ、ウエアラブル用途での実用に耐えうる積層導電性生地とすることを可能とした。 Laminated conductive fabrics are suitable for wearable applications such as wearable sensors because they have a tensile strength of 200 N or more and a surface resistance of 1.5 Ω or less, but they also have an apparent mass of 160 g / m 2 or less and a tensile strength. With a mass of 200 N or more, an elongation rate of 40% or more, and a surface resistance of 1.5 Ω or less, it is more preferably used for wearable applications such as wearable sensors. Until now, there has been no material that satisfies the conditions of tensile strength of 200 N or more, elongation of 40% or more, and surface resistance of 1.5 Ω or less while maintaining the same apparent weight as this material. By achieving these physical properties, we have decided to make a laminated conductive fabric that can meet the standards for auxiliary materials in clothing materials, which are highly required for flexibility and light weight, and can withstand practical use in wearable applications. It was possible.
さらに、透気度が300cm3/(cm2・s)以上であると、伸縮性と被覆体への密着性(接着性)、及び通気性の面からも好ましい。 Further, when the air permeability is 300 cm 3 / (cm 2 · s) or more, it is preferable from the viewpoints of elasticity, adhesion to the covering body (adhesiveness), and breathability.
導電性生地の見掛け質量(目付)は、単層である場合には被覆体への密着性(接着性)と伸縮性の観点から40g/m2以上80g/m2以下が好ましい。さらに導電性生地を1層積層接着させた2層積層導電性生地の見掛け質量は80g/m2以上160g/m2以下が好ましく、同様にもう1層積層接着させた2層積層導電性生地の見掛け質量は120g/m2以上240g/m2以下が好ましく、3層積層導電性生地の見掛け質量は160g/m2以上320g/m2以下が好ましい。 In the case of a single layer, the apparent mass (weight) of the conductive fabric is preferably 40 g / m 2 or more and 80 g / m 2 or less from the viewpoint of adhesion (adhesiveness) to the covering body and elasticity. Further, the apparent mass of the two-layer laminated conductive fabric in which one layer of the conductive fabric is laminated and bonded is preferably 80 g / m 2 or more and 160 g / m 2 or less, and similarly, the two-layer laminated conductive fabric in which another layer is laminated and bonded is used. The apparent mass is preferably 120 g / m 2 or more and 240 g / m 2 or less, and the apparent mass of the three-layer laminated conductive fabric is preferably 160 g / m 2 or more and 320 g / m 2 or less.
導電性生地及び積層導電性生地の厚さは、0.2mm以上2.0mm以下であることが好ましい。0.2mm以上であれば十分な引張強さ及び引裂き強さを発揮し、2.0mm以下であれば十分な密着性(接着性)を発揮する。より好ましくは0.2mm以上1.2mm以下であり、さらに好ましくは0.2mm以上、0.8mm以下である。 The thickness of the conductive fabric and the laminated conductive fabric is preferably 0.2 mm or more and 2.0 mm or less. If it is 0.2 mm or more, it exhibits sufficient tensile strength and tear strength, and if it is 2.0 mm or less, it exhibits sufficient adhesion (adhesiveness). It is more preferably 0.2 mm or more and 1.2 mm or less, and further preferably 0.2 mm or more and 0.8 mm or less.
導電性生地及び積層導電性生地の引張強さは、引張の方向に依らず、強度の面から100N以上であることが好ましく、200N以上であることが、より好ましい。 The tensile strength of the conductive fabric and the laminated conductive fabric is preferably 100 N or more, and more preferably 200 N or more, regardless of the direction of tension.
導電性生地及び積層導電性生地の伸び率は、伸びの方向に依らず、伸縮性と被覆体への密着性(接着性)の観点から20%以上であることが好ましく、30%以上であることがより好ましい。 The elongation rate of the conductive fabric and the laminated conductive fabric is preferably 20% or more, preferably 30% or more, from the viewpoint of elasticity and adhesion to the covering body (adhesiveness) regardless of the direction of elongation. Is more preferable.
導電性生地及び積層導電性生地の引裂き強さは、強度の面から8N以上であることが好ましい。 The tear strength of the conductive fabric and the laminated conductive fabric is preferably 8N or more in terms of strength.
導電性生地及び積層導電性生地の用途としては、まったく制限されるものではないが、ウエアラブル用途、電磁波シールド用途において好適に用いられる。 The uses of the conductive fabric and the laminated conductive fabric are not limited at all, but are preferably used in wearable applications and electromagnetic wave shielding applications.
[実施例1]
以下の材料を用いて、導電性生地を作成した。
[Example 1]
A conductive fabric was prepared using the following materials.
<使用材料>
(銀メッキ糸)大阪電気工業製0dex(ナイロン6.6繊維に銀メッキをコーティングした糸。繊度30デニールの10フィラメント)
<Material used>
(Silver-plated yarn) Osaka Denki Kogyo 0dex (Nylon 6.6 fiber coated with silver plating. 10 filaments with a fineness of 30 denier)
<作成方法>
1.導電性生地用の生地の作成
銀メッキ糸を用いて、ハーフトリコットで編上げ幅70cmの導電性生地用の生地を作成した。次いで、精練加工と熱セット加工することで、製品仕上げ幅90cmの生地を作成した。なお、以後の説明では、生地のたて方向とは編物組織におけるウェール方向を意味し、生地のよこ方向とは編物組織におけるコース方向を意味する。
<How to create>
1. Preparation of fabric for conductive fabric Using silver-plated yarn, a fabric for conductive fabric with a knitted width of 70 cm was prepared with a half tricot. Next, a dough having a product finishing width of 90 cm was prepared by scouring and heat-setting. In the following description, the vertical direction of the fabric means the wale direction in the knitted structure, and the horizontal direction of the fabric means the course direction in the knitted structure.
<導電性生地用の生地の評価>
(1)引張強さ(N) たて:243.7 よこ:157.7
JIS L 1096A法(カットスリップ法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を200mmとし、引張速度200mm/minで測定した。
(2)伸び率(%) たて:69.1 よこ:75.5
JIS L 1096A法(カットスリップ法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を200mmとし、引張速度200mm/minで測定した。
(3)引裂き強さ(N) たて方向:11.5 よこ方向:11.9
(よこ方向は引裂き方向に対して斜めに切断した)
JIS L 1096A−1法(シングルタング法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を100mmとし、引張速度100mm/minで測定した。
(4)見掛け質量(目付)(g/m2) 50.8
JIS L 1096A法に準拠し測定した。
(5)厚さ(mm) 0.31
JIS L 1096A法(JIS法)に準拠し、一定圧力0.7kPaにて測定した。
(6)透気度(cm3/(cm2・s)) 684.5
JIS L 1096A法(フラジール形法)にて測定した。
(7) 表面抵抗(Ω)
表面抵抗の測定法について、図1を用いながら説明する。よこ方向(90cm)の端から端までの間隔において、たて方向がそれぞれA.0cm、B.25cm、C.50cm、D.75cm、E.100cmの位置にて、デジタルマルチテスターを用いて抵抗値を測定した。デジタルマルチテスターとしては、カイセ株式会社製KU−1188を用い、測定条件は、測定レンジ200Ω、2端子法で測定した。その結果、たて方向の小さい距離から順に、4.4Ω、2.8Ω、2.5Ω、3.0Ω、4.8Ωとなった。
同様に、たて方向(100cm)の端から端までの間隔において、よこ方向がそれぞれA.0cm、B.25cm、C.50cm、D.75cm、E.90cmの位置にて測定した。その結果、よこ方向の小さい距離から順に、5.2Ω、3.9Ω、3.4Ω、3.6Ω、5.4Ωとなった。
また、たて方向とよこ方向にほぼ対角線方向(斜め方向)に100cmの間隔で測定すると、2.8Ωとなった。
<Evaluation of fabrics for conductive fabrics>
(1) Tensile strength (N) Vertical: 243.7 Horizontal: 157.7
According to the JIS L 1096A method (cut slip method), the tester was used for low-speed extension type, the width of the test piece was 50 mm, the grip interval was 200 mm, and the measurement was performed at a tensile speed of 200 mm / min.
(2) Growth rate (%) Vertical: 69.1 Horizontal: 75.5
According to the JIS L 1096A method (cut slip method), the tester was used for low-speed extension type, the width of the test piece was 50 mm, the grip interval was 200 mm, and the measurement was performed at a tensile speed of 200 mm / min.
(3) Tear strength (N) Vertical direction: 11.5 Horizontal direction: 11.9
(The horizontal direction was cut diagonally with respect to the tearing direction)
According to the JIS L 1096A-1 method (single tongue method), the tester was set to a low-speed extension type, the width of the test piece was 50 mm, the grip interval was 100 mm, and the measurement was performed at a tensile speed of 100 mm / min.
(4) Apparent mass (Metsuke) (g / m 2 ) 50.8
The measurement was performed according to the JIS L 1096A method.
(5) Thickness (mm) 0.31
The measurement was performed at a constant pressure of 0.7 kPa in accordance with the JIS L 1096A method (JIS method).
(6) Air permeability (cm 3 / (cm 2 · s)) 684.5
The measurement was performed by the JIS L 1096A method (Frazier type method).
(7) Surface resistance (Ω)
A method for measuring surface resistance will be described with reference to FIG. In the horizontal direction (90 cm), the vertical direction is A. 0 cm, B. 25 cm, C.I. 50 cm, D. 75 cm, E.I. The resistance value was measured using a digital multitester at a position of 100 cm. As the digital multitester, KU-1188 manufactured by Kaise Co., Ltd. was used, and the measurement conditions were measured with a measurement range of 200Ω and a two-terminal method. As a result, the distances were 4.4Ω, 2.8Ω, 2.5Ω, 3.0Ω, and 4.8Ω in ascending order from the smallest distance in the vertical direction.
Similarly, in the vertical direction (100 cm), the horizontal direction is A. 0 cm, B. 25 cm, C.I. 50 cm, D. 75 cm, E.I. It was measured at a position of 90 cm. As a result, it became 5.2Ω, 3.9Ω, 3.4Ω, 3.6Ω, and 5.4Ω in order from the smallest distance in the horizontal direction.
Moreover, it was 2.8Ω when measured at intervals of 100 cm in the vertical direction and the horizontal direction in the substantially diagonal direction (diagonal direction).
2.導電性生地用の生地に接着樹脂部を付与した導電性生地の作成
得られた導電性生地用の生地にホットメルトとして、アクリル樹脂の上からポリアミド樹脂粉を被覆した接着樹脂部を1つのドットとして、ドット数26個/2.54cmで付与し、導電性生地を得た。
2. Creation of a conductive fabric in which an adhesive resin part is added to the fabric for the conductive fabric One dot is formed on the obtained fabric for the conductive fabric as a hot melt and coated with a polyamide resin powder on the acrylic resin. As a result, the number of dots was 26 / 2.54 cm, and a conductive cloth was obtained.
<導電性生地の評価>
(1)引張強さ(N) たて:166.1 よこ:135.2
JIS L 1096A法(カットスリップ法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を200mmとし、引張速度200mm/minで測定した。
(2)伸び率(%) たて:28.2 よこ:39.9
JIS L 1096A法(カットスリップ法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を200mmとし、引張速度200mm/minで測定した。
(3)引裂き強さ(N) たて方向:10.1 よこ方向:10.6
(よこ方向は引裂き方向に対して斜めに切断)
JIS L 1096A−1法(シングルタング法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を100mmとし、引張速度100mm/minで測定した。
(4)見掛け質量(目付)(g/m2) 57.4
JIS L 1096A法に準拠し測定した。
(5) 厚さ(mm) 0.41
JIS L 1096A法(JIS法)に準拠し、一定圧力0.7kPaにて測定した。
(6) 透気度(cm3/(cm2・s)) 693.4
JIS L 1096A法(フラジール形法)にて測定した。
(7) 表面抵抗(Ω)
よこ方向(90cm)の端から端までの間隔において、たて方向がそれぞれA.0cm、B.25cm、C.50cm、D.75cm、E.100cmの位置にて、デジタルマルチテスターを用いて抵抗値を測定した。その結果、たて方向の小さい距離から順に、5.5Ω、4.0Ω、3.0Ω、4.0Ω、4.4Ωとなった。
同様に、たて方向(100cm)の端から端までの間隔において、よこ方向がそれぞれA.0cm、B.25cm、C.50cm、D.75cm、E.90cmの位置にて測定した。その結果、よこ方向の小さい距離から順に、4.9Ω、4.5Ω、4.0Ω、4.5Ω、5.6Ωとなった。
また、たて方向とよこ方向にほぼ対角線方向(斜め方向)に100cmの間隔で測定すると、3.9Ωとなった。
この結果から、導電性生地の中央部がより表面抵抗が低く、また、対角線方向がより表面抵抗が低くなることが解った。
<Evaluation of conductive fabric>
(1) Tensile strength (N) Vertical: 166.1 Horizontal: 135.2
According to the JIS L 1096A method (cut slip method), the tester was used for low-speed extension type, the width of the test piece was 50 mm, the grip interval was 200 mm, and the measurement was performed at a tensile speed of 200 mm / min.
(2) Growth rate (%) Vertical: 28.2 Horizontal: 39.9
According to the JIS L 1096A method (cut slip method), the tester was used for low-speed extension type, the width of the test piece was 50 mm, the grip interval was 200 mm, and the measurement was performed at a tensile speed of 200 mm / min.
(3) Tear strength (N) Vertical direction: 10.1 Horizontal direction: 10.6
(The horizontal direction is cut diagonally with respect to the tearing direction)
According to the JIS L 1096A-1 method (single tongue method), the tester was set to a low-speed extension type, the width of the test piece was 50 mm, the grip interval was 100 mm, and the measurement was performed at a tensile speed of 100 mm / min.
(4) Apparent mass (Metsuke) (g / m 2 ) 57.4
The measurement was performed according to the JIS L 1096A method.
(5) Thickness (mm) 0.41
The measurement was performed at a constant pressure of 0.7 kPa in accordance with the JIS L 1096A method (JIS method).
(6) Air permeability (cm 3 / (cm 2 · s)) 693.4
The measurement was performed by the JIS L 1096A method (Frazier type method).
(7) Surface resistance (Ω)
In the horizontal direction (90 cm), the vertical direction is A. 0 cm, B. 25 cm, C.I. 50 cm, D. 75 cm, E.I. The resistance value was measured using a digital multitester at a position of 100 cm. As a result, the distances were 5.5Ω, 4.0Ω, 3.0Ω, 4.0Ω, and 4.4Ω in ascending order from the smallest distance in the vertical direction.
Similarly, in the vertical direction (100 cm), the horizontal direction is A. 0 cm, B. 25 cm, C.I. 50 cm, D. 75 cm, E.I. It was measured at a position of 90 cm. As a result, it became 4.9Ω, 4.5Ω, 4.0Ω, 4.5Ω, 5.6Ω in order from the smallest distance in the horizontal direction.
Further, when measured at intervals of 100 cm in the vertical direction and the horizontal direction substantially diagonally (diagonally), it was 3.9 Ω.
From this result, it was found that the surface resistance of the central portion of the conductive fabric was lower and the surface resistance was lower in the diagonal direction.
[実施例2]
3.積層導電性生地の作成
<作成方法>
導電性生地の大きさを、たて方向200cm、よこ方向90cmとした以外は実施例1と同じ方法で導電性生地を得た。次いで、たて方向100cmの位置で接着樹脂部が内側になるように二つ折りにし、その上からアイロンにて150℃で5秒間押し当てることで、たて方向100cm、よこ方向90の実質的に2枚を積層接着させた導電性生地を得た。
[Example 2]
3. Creation of laminated conductive fabric <How to create>
A conductive dough was obtained by the same method as in Example 1 except that the size of the conductive dough was 200 cm in the vertical direction and 90 cm in the horizontal direction. Next, fold it in half so that the adhesive resin part is on the inside at a position 100 cm in the vertical direction, and press it with an iron at 150 ° C. for 5 seconds to substantially 100 cm in the vertical direction and 90 in the horizontal direction. A conductive cloth obtained by laminating and adhering two sheets was obtained.
以下の結果から、積層接着体にすることで表面抵抗値が明らかに低くなる事が解った。<積層導電性生地の評価>
(1)引張強さ(N) たて:410.2 よこ:273.6
JIS L 1096A法(カットスリップ法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を200mmとし、引張速度200mm/minで測定した。
(2)伸び率(%) たて:48.8 よこ:57.0
JIS L 1096A法(カットスリップ法)に準拠し、試験機に低速伸長形、試験片幅を50mm、つかみ間隔を200mmとし、引張速度200mm/minで測定した。
(3)見掛け質量(目付)(g/m2) 122.4
JIS L 1096A法に準拠し測定した。
(4)厚さ(mm) 0.60
JIS L 1096A法(JIS法)に準拠し、一定圧力0.7kPaにて測定した。
(5)透気度(cm3/(cm2・s)) 373.8
JIS L 1096A法(フラジール形法)にて測定した。
(6) 表面抵抗(Ω)
よこ方向(90cm)の端から端までの間隔において、たて方向がそれぞれA.0cm、B.25cm、C.50cm、D.75cm、E.100cmの位置にて、デジタルマルチテスターを用いて抵抗値を測定した。その結果、たて方向の小さい距離から順に、2.0Ω、1.5Ω、1.3Ω、1.5Ω、1.7Ωとなった。
同様に、たて方向(100cm)の端から端までの間隔において、よこ方向がそれぞれA.0cm、B.25cm、C.50cm、D.75cm、E.90cmの位置にて測定した。その結果、よこ方向の小さい距離から順に、2.3Ω、1.7Ω、1.6Ω、1.7Ω、2.0Ωとなった。
また、たて方向とよこ方向にほぼ対角線方向(斜め方向)に100cmの間隔で測定すると、1.4Ωとなった。
From the following results, it was found that the surface resistance value was clearly reduced by using a laminated adhesive. <Evaluation of laminated conductive fabric>
(1) Tensile strength (N) Vertical: 410.2 Horizontal: 273.6
According to the JIS L 1096A method (cut slip method), the tester was used for low-speed extension type, the width of the test piece was 50 mm, the grip interval was 200 mm, and the measurement was performed at a tensile speed of 200 mm / min.
(2) Growth rate (%) Vertical: 48.8 Horizontal: 57.0
According to the JIS L 1096A method (cut slip method), the tester was used for low-speed extension type, the width of the test piece was 50 mm, the grip interval was 200 mm, and the measurement was performed at a tensile speed of 200 mm / min.
(3) Apparent mass (Metsuke) (g / m 2 ) 122.4
The measurement was performed according to the JIS L 1096A method.
(4) Thickness (mm) 0.60
The measurement was performed at a constant pressure of 0.7 kPa in accordance with the JIS L 1096A method (JIS method).
(5) Air permeability (cm 3 / (cm 2 · s)) 373.8
The measurement was performed by the JIS L 1096A method (Frazier type method).
(6) Surface resistance (Ω)
In the horizontal direction (90 cm), the vertical direction is A. 0 cm, B. 25 cm, C.I. 50 cm, D. 75 cm, E.I. The resistance value was measured using a digital multitester at a position of 100 cm. As a result, the distances were 2.0Ω, 1.5Ω, 1.3Ω, 1.5Ω, and 1.7Ω in ascending order from the smallest distance in the vertical direction.
Similarly, in the vertical direction (100 cm), the horizontal direction is A. 0 cm, B. 25 cm, C.I. 50 cm, D. 75 cm, E.I. It was measured at a position of 90 cm. As a result, the distances were 2.3Ω, 1.7Ω, 1.6Ω, 1.7Ω, and 2.0Ω in order from the smallest distance in the horizontal direction.
In addition, it was 1.4Ω when measured at intervals of 100 cm in the diagonal direction (diagonal direction) in the vertical and horizontal directions.
この結果は、単層の導電性生地に比べ、2層を積層接着させた積層導電性生地の導電性が優れているばかりでなく、接着樹脂を用いていない単層の導電性生地用の生地の導電性とほぼ同程度の導電性を示している。 As a result, not only the conductivity of the laminated conductive fabric in which two layers are laminated and bonded is superior to that of the single-layer conductive fabric, but also the fabric for the single-layer conductive fabric that does not use an adhesive resin is used. It shows almost the same conductivity as the conductivity of.
このことより、接着樹脂部を設けても、導電性生地を積層接着させることで、驚くべきことに、接着樹脂部による導電性低減の悪影響が消失し、単層の導電性生地用の生地と同等の導電性を示すばかりでなく、単層の導電性生地用の生地に比べ、透気度及び伸び率は維持したまま、引っ張り強さが向上したことが解った。 From this, even if the adhesive resin portion is provided, by laminating and adhering the conductive fabric, surprisingly, the adverse effect of the reduced conductivity due to the adhesive resin portion disappears, and the fabric for the single-layer conductive fabric can be used. It was found that not only the same conductivity was exhibited, but also the tensile strength was improved while maintaining the air permeability and the elongation rate as compared with the fabric for a single-layer conductive fabric.
以上の表面抵抗の結果を表1に示す。表1に示す測定結果から以下の定量的な関係が見出せる。
(実施例1に関する表面抵抗)−(導電性生地用の生地の表面抵抗)<1.5Ω
(導電性生地用の生地の表面抵抗)−(実施例2に関する表面抵抗)>1.0Ω
(Surface resistance according to Example 1)-(Surface resistance of fabric for conductive fabric) <1.5Ω
(Surface resistance of fabric for conductive fabric)-(Surface resistance of Example 2)> 1.0Ω
[実施例3−1]〜[実施例3−5]
実施例1と同じ方法で作成した導電性生地を3cm×20cmに裁断し、図2に示す導電性生地を得た。
[Example 3-1] to [Example 3-5]
The conductive dough prepared by the same method as in Example 1 was cut into 3 cm × 20 cm to obtain the conductive dough shown in FIG.
得られた導電性生地と、得られた導電性生地を2枚重ねて実施例2と同じ方法で積層接着させた積層導電性生地と、3枚重ねて実施例2と同じ方法で積層接着させた積層導電性生地と、2枚重ねて積層させた導電性生地(接着無し)と、3枚重ねて積層させた導電性生地(接着無し)を得た。 The obtained conductive dough and the obtained conductive dough were laminated and adhered by the same method as in Example 2 by laminating and adhering two sheets of the obtained conductive dough, and three layers and laminating and adhering by the same method as in Example 2. A laminated conductive cloth, a conductive cloth in which two layers were laminated (without adhesion), and a conductive cloth in which three layers were laminated (without adhesion) were obtained.
それぞれのたて方向1.5mmの位置からよこ方向の0cmを起点とし、1cm、3cm、5cm、20cmの位置にて、デジタルマルチテスターを用いて抵抗値を測定した。 その結果、導電性生地(実施例3−1)では、よこ方向の0cmの起点から順に、0.6Ω、0.8Ω、1.0Ω、1.5Ω、2.5Ω、2枚重ねて積層接着させた積層導電性生地(実施例3−2)では、0.6Ω、0.8Ω、1.0Ω、2.5Ω、3枚重ねて積層接着させた積層導電性生地(実施例3−3)では、0.4Ω、0.6Ω、0.7Ω、1.0Ω、1.6Ω、2枚重ねて積層させた導電性生地(接着無し)(実施例3−4)では、0.6Ω、1.0Ω、1.3Ω、2.0Ω、4.0Ω、3枚重ねて積層させた導電性生地(接着無し)(実施例3−5)では、0.5Ω、0.7Ω、0.9Ω、1.3Ω、2.2Ωとなった。 The resistance value was measured using a digital multitester at positions of 1 cm, 3 cm, 5 cm, and 20 cm starting from 0 cm in the horizontal direction from the position of 1.5 mm in each vertical direction. As a result, in the conductive fabric (Example 3-1), two layers of 0.6Ω, 0.8Ω, 1.0Ω, 1.5Ω, 2.5Ω are laminated and bonded in this order from the starting point of 0 cm in the horizontal direction. In the laminated conductive fabric (Example 3-2), the laminated conductive fabric (Example 3-3) in which three layers of 0.6Ω, 0.8Ω, 1.0Ω, 2.5Ω and three layers were laminated and adhered. Then, 0.4Ω, 0.6Ω, 0.7Ω, 1.0Ω, 1.6Ω, and 0.6Ω, 1 in the conductive fabric (without adhesion) (Example 3-4) in which two layers are laminated. In the case of the conductive fabric (without adhesion) (Example 3-5) in which three layers of conductive fabric (without adhesion) were laminated, 0.5Ω, 0.7Ω, 0.9Ω, It became 1.3Ω and 2.2Ω.
この結果を表2及び図3に示す。
この結果から、実施例3−4及び実施例3−5のように、積層することで抵抗値が低くなることは、他の導電素材においても想定することが可能だが、織物、編物のような導電体の接触点が流動的に変化する可能性が高い部材において、その通気性や柔軟性を維持しつつ、通電性を維持安定させるには、実施例3−2で示すように、ドット状に接着樹脂部を設けた導電性生地を積層接着させた方が好ましいことが解った。さらに、実施例3−3で示すように、さらに複数枚積層接着させることで、より効果的に抵抗値を下げ、導電性を向上させることができることが解った。 From this result, it can be assumed that the resistance value is lowered by laminating as in Examples 3-4 and 3-5 in other conductive materials, but such as woven fabrics and knitted fabrics. In a member in which the contact point of the conductor is likely to change fluidly, in order to maintain and stabilize the electrical conductivity while maintaining the air permeability and flexibility, as shown in Example 3-2, a dot shape is used. It was found that it is preferable to laminate and bond the conductive fabric provided with the adhesive resin portion. Further, as shown in Example 3-3, it was found that the resistance value can be lowered and the conductivity can be improved more effectively by laminating and adhering a plurality of sheets.
Claims (4)