JP6748546B2 - Overhead cable - Google Patents
Overhead cable Download PDFInfo
- Publication number
- JP6748546B2 JP6748546B2 JP2016193274A JP2016193274A JP6748546B2 JP 6748546 B2 JP6748546 B2 JP 6748546B2 JP 2016193274 A JP2016193274 A JP 2016193274A JP 2016193274 A JP2016193274 A JP 2016193274A JP 6748546 B2 JP6748546 B2 JP 6748546B2
- Authority
- JP
- Japan
- Prior art keywords
- cable
- optical fiber
- ice
- snow
- jacket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の実施形態は、架空ケーブルに係り、特に、氷雪の付着が抑制された架空ケーブルに関する。 The embodiment of the present invention relates to an aerial cable, and more particularly to an aerial cable in which adhesion of ice and snow is suppressed.
架空ケーブルについては、屋外に架空敷設されることから、冬期の降雪時に氷雪が付着しやすい。また、氷雪が付着しその重さにより架空ケーブルにねじれや回転が発生し、このねじれや回転が発生した架空ケーブルに氷雪が付着することにより、架空ケーブルの外周全体を覆うように筒状に氷雪が付着するいわゆる筒雪が発生しやすい。 Since overhead cables are laid outdoors, ice and snow tend to adhere to them during winter snowfall. In addition, ice and snow adhere to the aerial cable due to its weight, which causes twisting and rotation, and ice and snow adhere to the aerial cable where the twist and rotation occur. It is easy for so-called snow-covered snow to adhere.
筒雪は、架空ケーブルの重量を増加させることから、架空ケーブルの断線、伝送特性の低下、架空ケーブルの固定に用いられる引留金具の破損等の原因となる。特に、筒雪は、気温が低下する夜間に発生しやすく、気温が上昇する昼間まで成長を続けることがあり、このような場合、架空ケーブルの重量が増加しやすく、架空ケーブルの断線、伝送特性の低下、架空ケーブルの固定に用いられる引留金具の破損等が発生しやすい。 Cylinder snow increases the weight of the aerial cable, which causes breakage of the aerial cable, deterioration of transmission characteristics, breakage of the anchorage metal used for fixing the aerial cable, and the like. In particular, tube snow is likely to occur at night when the temperature drops, and may continue to grow until daytime when the temperature rises.In such a case, the weight of the overhead cable is likely to increase, and the disconnection and transmission characteristics of the overhead cable may occur. Is likely to occur, and the anchoring metal used to fix the overhead cable is easily damaged.
氷雪の付着を抑制する方法として、自身の発熱により氷雪を融解する融雪部材を用いる方法が知られている(例えば、特許文献1参照。)。しかしながら、融雪部材は、架空ケーブルとは別に製造されることから必ずしも生産性に優れない。また、融雪部材は架空ケーブルを囲むように設けられることから、架空ケーブルに熱的な影響が発生するおそれがある。 As a method of suppressing the adhesion of ice and snow, there is known a method of using a snow melting member that melts ice and snow by its own heat generation (see, for example, Patent Document 1). However, the snow melting member is not necessarily excellent in productivity because it is manufactured separately from the overhead cable. Further, since the snow melting member is provided so as to surround the aerial cable, the aerial cable may be thermally affected.
また、氷雪の付着を抑制する方法として、撥水性材料を用いる方法が知られている(例えば、特許文献2参照。)。撥水性材料は、架空ケーブルの外皮に混合することにより、または架空ケーブルの表面に塗布することにより、氷雪の付着を抑制することができる。しかしながら、氷雪の付着を抑制する効果が必ずしも十分でなく、さらなる効果の向上が求められている。 Further, as a method for suppressing the adhesion of ice and snow, a method using a water repellent material is known (see, for example, Patent Document 2). The water-repellent material can be prevented from adhering to ice and snow by being mixed with the outer cover of the aerial cable or by being applied to the surface of the aerial cable. However, the effect of suppressing the adhesion of ice and snow is not always sufficient, and further improvement of the effect is required.
さらに、氷雪の付着を抑制する方法として、親水性材料を用いる方法が知られている。親水性材料として、酸化チタンが用いられている(例えば、特許文献3参照。)。しかしながら、架空ケーブルの外被に酸化チタンを混合し、または外被の表面に酸化チタンを塗布した場合、酸化チタンの光触媒効果により、架空ケーブルの外被が損傷するおそれがある。 Furthermore, as a method for suppressing the adhesion of ice and snow, a method using a hydrophilic material is known. Titanium oxide is used as the hydrophilic material (see, for example, Patent Document 3). However, when titanium oxide is mixed in the jacket of the overhead cable or titanium oxide is applied to the surface of the jacket, the photocatalytic effect of titanium oxide may damage the jacket of the overhead cable.
また、筒雪の発生および成長を抑制する方法として、架空ケーブルの直径を大きくする方法が挙げられる。架空ケーブルの直径が大きくなると、ねじれや回転の発生が抑制されることから、筒雪の発生および成長が抑制される。 Further, as a method of suppressing the generation and growth of snow cylinders, there is a method of increasing the diameter of the overhead cable. When the diameter of the overhead cable is increased, twisting and rotation are suppressed, so that the generation and growth of snow can be suppressed.
しかしながら、架空ケーブルの直径が大きくなると、これまで架空ケーブルの敷設に用いていた敷設用部材を用いることができなくなり、敷設用部材を交換しなければならなくなる。敷設用部材として、架空ケーブルを固定するための引留金具、配線クリート等が挙げられる。 However, when the diameter of the aerial cable becomes large, the laying member that has been used for laying the aerial cable cannot be used, and the laying member must be replaced. Examples of the laying member include an anchor fitting for fixing an overhead cable, a wiring cleat, and the like.
本発明は、氷雪の付着が抑制された架空ケーブルを提供することを目的としている。 An object of the present invention is to provide an aerial cable in which adhesion of ice and snow is suppressed.
実施形態の架空ケーブルは、心線と、この心線を被覆する外被とを有する。前記架空ケーブルは、前記外被内部に支持線を有する支持線部と、前記外被内部に前記心線として少なくとも光ファイバ心線を有するケーブル部と、前記支持線部と前記ケーブル部とを連結する連結部とを有する、前記支持線部端部から前記ケーブル部端部に至る最大幅が15mm以下の光ファイバケーブルであり、前記外被の材料は、オレフィン類を重合させた熱可塑性樹脂と、フッ素系界面活性剤とを含有し、前記フッ素系界面活性剤は、前記熱可塑性樹脂100質量部に対して0.1質量部以上10質量部以下であり、前記支持線と少なくとも前記光ファイバ心線の外周に、前記外被の材料にて前記支持線部と、前記ケーブル部と、前記連結部が一体的に形成され、前記外被及び前記連結部は、20℃での水接触角が30度以下かつ0℃での氷塊密着力が10N/mm以下である。
The aerial cable of the embodiment has a core wire and a jacket covering the core wire. The overhead cable connects a support wire portion having a support wire inside the jacket, a cable portion having at least an optical fiber core wire as the core wire inside the jacket, and the support wire portion and the cable portion. Is a fiber optic cable having a maximum width of 15 mm or less from the end of the supporting wire portion to the end of the cable portion, and the material of the jacket is a thermoplastic resin obtained by polymerizing olefins. contains a fluorine-based surfactant, the fluorine-based surfactant is not more than the
本発明の架空ケーブルは、外被の材料がフッ素系界面活性剤を含み、かつ、この外被の材料の20℃での水接触角が30度以下かつ0℃での氷塊密着力が10N/mm以下である。本発明の架空ケーブルによれば、このような構成を有することにより、氷雪の付着を抑制することができる。 In the aerial cable of the present invention, the jacket material contains a fluorosurfactant, and the jacket material has a water contact angle at 20° C. of not more than 30 degrees and an ice block adhesion force at 0° C. of 10 N/ mm or less. According to the aerial cable of the present invention, by having such a configuration, it is possible to suppress the adhesion of ice and snow.
以下、本発明を実施するための形態について図面を用いて説明する。
図1は、第1の実施形態の光ファイバケーブルを示す断面図である。
Hereinafter, embodiments for carrying out the present invention will be described with reference to the drawings.
FIG. 1 is a sectional view showing an optical fiber cable according to the first embodiment.
光ファイバケーブル10は、一般加入者宅内への引き込みに用いられるいわゆるドロップケーブルである。光ファイバケーブル10は、支持線部11、ケーブル部12、およびこれらを連結する連結部13を有する。
The
支持線部11は、支持線14の外周に外被15が設けられている。支持線14は、鋼線、ガラス繊維強化プラスチック(FRP)等から構成されている。外被15を構成する材料については後述する。
The
ケーブル部12は、上下に並列配置された2本の光ファイバ心線16を挟んで、その上下に間隔をおいて抗張力体17が並行に配置され、これらを覆うように外被18が設けられている。
The
外被18の両側のほぼ中央、すなわち、光ファイバ心線16が位置する部分には、引き裂き用のノッチ19が設けられている。ケーブル接続作業時、これらの引き裂き用ノッチ19を起点に外被18を引き裂くことにより、内部の光ファイバ心線16を容易に取り出すことができる。
A
抗張力体17は、鋼線、ガラス繊維強化プラスチック(FRP)の他、ポリ−p−フェニレンテレフタルアミド繊維等のアラミド繊維、ポリエチレンテレフタレート繊維等のポリエステル系繊維、ナイロン繊維、これらの繊維をポリエステル−アクリレート樹脂等で収束し結着させた複合材等からなる。外被18を構成する材料については後述する。
The
支持線部11とケーブル部12とは、連結部13により連結されている。具体的には、支持線部11の外被15、ケーブル部12の外被18、および連結部13が同一の材料から一体的に形成されることにより、支持線部11、ケーブル部12、および連結部13が連結されている。外被15、外被18、および連結部13は、樹脂と、フッ素系界面活性剤とを含有することが好ましい。
The
樹脂としては、熱可塑性樹脂が好ましく、特に、オレフィン類を重合させたものが好ましい。このようなものとしては、例えば、低密度ポリエチレン(LDPE)、中密度ポリエチレン(MDPE)、高密度ポリエチレン(HDPE)、超低密度ポリエチレン(VLDPE)、直鎖状低密度ポリエチレン(LLDPE)等のポリエチレン、エチレンに、プロピレン、1−ブテン、1−ペンテン、1−ヘキセン、1−オクテン、4−メチル−1−ペンテン等のα−オレフィンを共重合させたエチレン・α−オレフィン共重合体、エチレン・アクリル酸エチル共重合体(EEA)、エチレン・アクリル酸メチル共重合体(EMA)、エチレン・メタクリル酸エチル共重合体、エチレン・酢酸ビニル共重合体(EVA)、ポリプロピレン(PP)、ポリイソブチレン等が挙げられる。これらは、1種のみを用いてもよいし、2種以上を混合して用いてもよい。 As the resin, a thermoplastic resin is preferable, and a resin obtained by polymerizing olefins is particularly preferable. Examples of such a material include polyethylene such as low density polyethylene (LDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), ultra low density polyethylene (VLDPE) and linear low density polyethylene (LLDPE). An ethylene/α-olefin copolymer obtained by copolymerizing ethylene with an α-olefin such as propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, and 4-methyl-1-pentene, ethylene. Ethyl acrylate copolymer (EEA), ethylene/methyl acrylate copolymer (EMA), ethylene/ethyl methacrylate copolymer, ethylene/vinyl acetate copolymer (EVA), polypropylene (PP), polyisobutylene, etc. Is mentioned. These may be used alone or in combination of two or more.
フッ素系界面活性剤は、所定の水接触角および氷塊密着力が得られるものであれば特に限定されるものではないが、パーフルオロアルキルエチレンオキシド付加物を含むことが好ましい。パーフルオロアルキルエチレンオキシド付加物によれば、所定の水接触角および氷塊密着力を容易に得ることができ、氷雪の付着を抑制しやすい。 The fluorosurfactant is not particularly limited as long as it can obtain a predetermined water contact angle and ice block adhesion, but it is preferable to include a perfluoroalkylethylene oxide adduct. With the perfluoroalkylethylene oxide adduct, it is possible to easily obtain a predetermined water contact angle and ice block adhesion, and it is easy to suppress the adhesion of ice and snow.
また、パーフルオロアルキルエチレンオキシド付加物は、パーフルオロアルキル基の表面張力が低いために空気との親和性が高く、これにより表面側へと移行しやすい。これにより、表面を親水性に改質する効果に優れ、また仮に表面の親水性が失われたとしても再び親水性にすることができる。 In addition, the perfluoroalkylethylene oxide adduct has a high affinity with air due to the low surface tension of the perfluoroalkyl group, and thus is easily transferred to the surface side. Thereby, the effect of modifying the surface to be hydrophilic is excellent, and even if the hydrophilicity of the surface is lost, it can be made hydrophilic again.
パーフルオロアルキルエチレンオキシド付加物としては、市販品を好適に使用することができる。このようなものとしては、例えば、AGCセイミケミカル株式会社製の商品名S−242、S−243、S−420等が挙げられる。これらは、1種のみを用いてもよいし、2種以上を混合して用いてもよい。 As the perfluoroalkylethylene oxide adduct, a commercially available product can be preferably used. Examples of such materials include trade names S-242, S-243, and S-420 manufactured by AGC Seimi Chemical Co., Ltd. These may be used alone or in combination of two or more.
フッ素系界面活性剤は、パーフルオロアルキルエチレンオキシド付加物を70質量%以上含むことが好ましく、90質量%以上含むことがより好ましく、特に、パーフルオロアルキルエチレンオキシド付加物のみを含むことが好ましい。パーフルオロアルキルエチレンオキシド付加物の割合が高くなるほど、氷雪の付着が抑制される。 The fluorosurfactant preferably contains 70% by mass or more of a perfluoroalkylethylene oxide adduct, more preferably 90% by mass or more, and particularly preferably contains only a perfluoroalkylethylene oxide adduct. The higher the ratio of the perfluoroalkylethylene oxide adduct, the more suppressed the adhesion of ice and snow.
フッ素系界面活性剤は、樹脂100質量部に対して、0.1質量部以上であることが好ましい。0.1質量部以上であると、光ファイバケーブル10への氷雪の付着が顕著に抑制される。氷雪の付着を抑制する観点から、0.5質量部以上がより好ましく、1.0質量部以上がさらに好ましく、1.5質量部以上が特に好ましい。
The fluorine-based surfactant is preferably 0.1 part by mass or more based on 100 parts by mass of the resin. When the amount is 0.1 parts by mass or more, the adhesion of ice and snow to the
一方、フッ素系界面活性剤が多くなると、連結部13、外被15、外被18の機械的強度が低下するおそれがある。また、フッ素系界面活性剤は比較的に高価であることから、その使用量を抑えることが好ましい。このため、10質量部以下が好ましく、7質量部以下がより好ましく、5質量部以下がさらに好ましい。
On the other hand, when the amount of the fluorine-based surfactant is large, the mechanical strength of the connecting
連結部13、外被15、および外被18は、樹脂、フッ素系界面活性剤以外の成分を含むことができる。このような成分としては、紫外線吸収剤、光安定剤、難燃剤、滑剤、着色剤、充填剤、加工性改良材等が挙げられる。これらは、従来公知のものを用いることができ、その含有量も用途に合わせて適宜変更することができる。
The connecting
連結部13、外被15、および外被18は、20℃での水接触角が30度以下かつ0℃での氷塊密着力が10N/mm以下である。水接触角、氷塊密着力は、以下のようにして求められる。
The connecting
水接触角は、20℃の温度中、連結部13、外被15、または外被18と同一の材料からなる厚さ1mmのシート上にシリンジから6μLの純水を滴下して30秒後に測定して求める。なお、水接触角は、θ/2法により算出される。
The water contact angle is measured 30 seconds after dropping 6 μL of pure water from a syringe onto a sheet having a thickness of 1 mm and made of the same material as that of the connecting
氷塊密着力は、まず、200mm以上の長さを有する光ファイバケーブル10の一方の端部側の20mmの部分を純水に浸漬した後、これらを−20℃の温度にして光ファイバケーブル10の外周に氷塊を形成する。その後、氷塊が形成された光ファイバケーブル10を0℃に設定した恒温槽に移動させて氷塊を0℃にする。そして、引張試験機を用いて、氷塊から光ファイバケーブル10を50mm/分の速さで引き抜いて引抜力の最大値を求める。同様の操作を合計で5回行って、これら5回の引抜力の最大値の平均値を求める。この平均値は、20mmあたりのものであることから、長さ1mmあたりに換算、すなわち1/20倍することにより、氷塊密着力を求める。
The ice lump adhesion is obtained by first immersing a 20 mm portion on one end side of the
水接触角が30度以下である場合、表面が親水性となり、氷雪の付着が抑制される。すなわち、表面が親水性である場合、表面と氷雪との間に水膜として多くの水分が保持される。水分の粘性は低いことから、表面と氷雪との間に多くの水分が水膜として保持されることにより、氷雪の付着力や摩擦力が低下する。この結果、表面における氷雪の移動が容易となり、氷雪が早期に脱落しやすくなる。水接触角は、氷雪の付着を抑制する観点から小さいほど好ましいが、通常、10度もあれば十分である。 When the water contact angle is 30 degrees or less, the surface becomes hydrophilic and the adhesion of ice and snow is suppressed. That is, when the surface is hydrophilic, a large amount of water is retained as a water film between the surface and ice and snow. Since the viscosity of water is low, a large amount of water is retained as a water film between the surface and the ice and snow, which reduces the adhesion and frictional force of the ice and snow. As a result, it becomes easier for ice and snow to move on the surface, and ice and snow are likely to fall off early. The water contact angle is preferably as small as possible from the viewpoint of suppressing the adhesion of ice and snow, but 10 degrees is usually sufficient.
親水性にすることの効果は、気温が氷雪の融点に近い場合、例えば、気温が−5℃以上である場合、特に、−3℃以上である場合に顕著となる。すなわち、気温が氷雪の融点に近いと、凍結しない水分が多くなり、表面と氷雪との間に水膜としてより多くの水分が保持される。 The effect of making hydrophilic is remarkable when the air temperature is close to the melting point of ice and snow, for example, when the air temperature is -5°C or higher, particularly when it is -3°C or higher. That is, when the temperature is close to the melting point of ice and snow, the amount of water that does not freeze increases, and more water is retained as a water film between the surface and the ice and snow.
また、気温が氷雪の融点に近い場合、撥水性に比べて有利な効果を得ることができる。すなわち、既に説明したように、親水性であると、表面と氷雪との間に水膜として多くの水分が保持されることから氷雪の移動が容易となる。一方、撥水性であると、水分がはじかれることから、表面と氷雪との間に水膜として保持される水分が少なく、氷雪の移動は必ずしも容易とならない。 Further, when the temperature is close to the melting point of ice and snow, an advantageous effect can be obtained as compared with water repellency. That is, as described above, if the surface is hydrophilic and a large amount of water is retained as a water film between the surface and the ice and snow, the ice and snow can easily move. On the other hand, if water-repellent, the water is repelled, so that less water is retained as a water film between the surface and the ice and snow, and the movement of ice and snow is not always easy.
また、氷塊密着力が10N/mm以下である場合、氷雪との密着力が十分に小さいことから、氷雪の付着が効果的に抑制される。氷塊密着力は、氷雪の付着を抑制する観点から小さいほど好ましいが、通常、1N/mmもあれば十分である。 Further, when the adhesion force of ice blocks is 10 N/mm or less, the adhesion force to ice and snow is sufficiently small, so that the adhesion of ice and snow is effectively suppressed. From the viewpoint of suppressing the adhesion of ice and snow, the smaller the ice block adhesion is, the more preferable it is, but 1 N/mm is usually sufficient.
水接触角、氷塊密着力は、フッ素系界面活性剤の含有量により調整することができる。通常、フッ素系界面活性剤の含有量を多くすることにより、水接触角、氷塊密着力を小さくすることができる。既に説明したように、樹脂材料100質量部に対して、フッ素系界面活性剤を好ましくは0.1質量部以上、より好ましくは0.5質量部以上、さらに好ましくは1.0質量部以上、特に好ましくは1.5質量部以上とすることにより、水接触角を30度以下かつ氷塊密着力を10N/mm以下にすることができる。 The water contact angle and the ice block adhesion can be adjusted by the content of the fluorosurfactant. Generally, by increasing the content of the fluorine-based surfactant, the water contact angle and the ice block adhesion can be reduced. As described above, the fluorosurfactant is preferably 0.1 part by mass or more, more preferably 0.5 part by mass or more, still more preferably 1.0 part by mass or more, relative to 100 parts by mass of the resin material. Particularly preferably, when the amount is 1.5 parts by mass or more, the water contact angle can be 30 degrees or less and the ice block adhesion force can be 10 N/mm or less.
なお、従来、親水性材料として酸化チタンが知られている。しかしながら、連結部13、外被15、および外被18の樹脂が酸化チタンを用いて親水性を付与した樹脂の場合、酸化チタンの光触媒効果により損傷するおそれがある。樹脂への親水性の付与がフッ素系界面活性剤によれば、連結部13、外被15、および外被18の樹脂に用いたとしても、損傷させるおそれがない。
Incidentally, titanium oxide is conventionally known as a hydrophilic material. However, when the resin of the connecting
また、フッ素系界面活性剤を、連結部13、外被15、および外被18に含有させることにより、仮に表面の親水性が失われたとしても、内部に含有されるフッ素系界面活性剤が表面側へと移行することにより、再び表面を親水性にすることができる。これにより、氷雪の付着を長期に抑制することができる。
Further, even if the hydrophilicity of the surface is lost by including the fluorine-based surfactant in the connecting
さらに、フッ素系界面活性剤を、連結部13、外被15、および外被18に含有させることにより、これらをコーティングする場合に比べて、生産性に優れたものとなる。例えば、連結部13、外被15、および外被18の表面にフッ素系界面活性剤をコーティングする場合、これらをフッ素系界面活性剤に浸漬した後、これらの表面に付着したフッ素系界面活性剤を乾燥させる必要がある。一方、連結部13、外被15、および外被18にフッ素系界面活性剤を含有させる場合、浸漬、乾燥等の工程が不要となり、生産性に優れたものとなる。
Further, by containing the fluorine-based surfactant in the connecting
また、連結部13、外被15、および外被18の表面にフッ素系界面活性剤をコーティングする場合、プライマー処理等の下地処理が必要となる場合があり、下地処理の最適化等について検討が必要となる。一方、連結部13、外被15、および外被18にフッ素系界面活性剤を含有させる場合、このような検討が不要となる。
In addition, when coating the surface of the connecting
光ファイバケーブル10は、最大幅(図中、縦方向の幅)が15mm以下であることが好ましい。15mm以下である場合、従来の光ファイバケーブルの敷設に用いられていた敷設用部材をそのまま用いることができる。このような敷設用部材として、光ファイバケーブルを固定するための引留金具、配線クリート等が挙げられる。
The
また、従来、最大幅が15mm以下になると筒雪が発生しやすくなるが、フッ素系界面活性剤を用いるとともに、所定の水接触角および氷塊密着力とすることにより、氷雪の付着を抑制することができる。 Further, conventionally, if the maximum width is 15 mm or less, snow snow is likely to be generated, but by using a fluorosurfactant and by setting a predetermined water contact angle and ice block adhesion, it is possible to suppress the adhesion of ice and snow. it can.
光ファイバケーブル10の最大幅は、13mm以下がより好ましく、10mm以下がさらに好ましい。通常、最大幅は、1mm以上である。
The maximum width of the
なお、光ファイバケーブル10としては、図示されるような矩形状の断面を有するものに限られず、図示しないが円形状の断面を有するものでもよい。円形状の断面を有するものの場合、最大幅(直径)は、15mm以下が好ましく、13mm以下がより好ましく、10mm以下がさらに好ましい。
The
本実施形態の光ファイバケーブル10は、一般加入者宅内への引き込みに好適に用いられる。すなわち、電柱から引き落とされた後、宅外の軒先に支持線部11が固定され、家屋の管路や通気口を通線されて宅内に配線される。
The
以上、第1の実施形態の光ファイバケーブル10について説明したが、第1の実施形態の光ファイバケーブル10では、少なくとも光ファイバ心線16を被覆する外被18が、フッ素系界面活性剤を含み、水接触角が30度以下かつ氷塊密着力が10N/mm以下であればよい。
Although the
なお、氷雪の付着を抑制する観点から、表面部の全て、すなわち、連結部13、外被15、および外被18の全てが、フッ素系界面活性剤を含むとともに、水接触角が30度以下かつ氷塊密着力が10N/mm以下であることが好ましい。
From the viewpoint of suppressing the adhesion of ice and snow, all of the surface portions, that is, all of the connecting
次に、第2の実施形態の光ファイバケーブルについて説明する。
図2は、第2の実施形態の光ファイバケーブルを示す断面図である。なお、図1に共通する部分には同一符号を付し、重複する説明を省略する。
Next, the optical fiber cable of the second embodiment will be described.
FIG. 2 is a sectional view showing an optical fiber cable according to the second embodiment. It should be noted that parts common to FIG. 1 are denoted by the same reference numerals, and redundant description will be omitted.
図2に示されるように、抗張力体17は、必ずしも光ファイバ心線16の上下に配置される必要はなく、光ファイバ心線16の上下のいずれか一方にのみ配置されてもよい。なお、図2においては、光ファイバ心線16の下方にのみ抗張力体17が配置されている。
As shown in FIG. 2, the
一方の抗張力体17を廃止する場合、その分だけケーブル部12の最大幅方向の長さを縮小することができる。このようにケーブル部12の長さが縮小された場合、これに合わせてノッチ19の位置も変更される。すなわち、光ファイバ心線16の変更後の位置にノッチ19の位置が変更される。
When one of the
以上、本発明の架空ケーブルについて、第1の実施形態の光ファイバケーブルおよび第2の実施形態の光ファイバケーブルを例に挙げて説明したが、本発明の架空ケーブルは、光ファイバケーブルに限られず、これ以外の架空ケーブルとすることもできる。このようなものとしては、架空敷設されるものであって、心線とこれを被覆する外被とを有するものであればよく、例えば、電話用ケーブル、同軸ケーブル等の通信用ケーブル、電力用ケーブルにも適用することができる。 Although the aerial cable of the present invention has been described above by taking the optical fiber cable of the first embodiment and the optical fiber cable of the second embodiment as examples, the aerial cable of the present invention is not limited to the optical fiber cable. Other overhead cables are also possible. As such a thing, it may be laid imaginary and has a core wire and an outer covering that covers the core wire, for example, a telephone cable, a communication cable such as a coaxial cable, and a power cable. It can also be applied to cables.
以下、実施例を参照してさらに具体的に説明する。
なお、本発明はこれらの実施例に限定されない。
Hereinafter, it will be described more specifically with reference to examples.
The present invention is not limited to these examples.
(実施例1)
光ファイバケーブルとして、図1に示すような光ファイバケーブル10を作製した。光ファイバケーブル10の作製では、押出機に、支持線14、光ファイバ心線16、および抗張力体17を並べて導入し、これらの外周に被覆材料を一括押出被覆することにより、連結部13、外被15、および外被18を形成した。このようにして作製された光ファイバケーブル10の高さは約5mm、幅は約2mmである。
(Example 1)
As the optical fiber cable, an
なお、支持線14には、外径1.2mmの単鋼線、光ファイバ心線16には、外径250μmの単心光ファイバ心線、抗張力体17には、外径0.4mmの単鋼線を用いた。
The
被覆材料は、表1に示すように、ノンハロゲン難燃化ポリエチレン樹脂100質量部に対して、フッ素系界面活性剤(AGCセイミケミカル株式会社製、商品名:S−420、パーフルオロアルキルエチレンオキシド付加物)3質量部とした。 As shown in Table 1, the coating material is a fluorosurfactant (manufactured by AGC Seimi Chemical Co., Ltd., trade name: S-420, perfluoroalkylethylene oxide adduct) with respect to 100 parts by mass of the halogen-free flame-retardant polyethylene resin. ) 3 parts by mass.
ここで、光ファイバケーブルの表面部の水接触角は28度であった。水接触角は、被覆材料を用いて厚さ1mmのシートを作製し、20℃の温度中、このシートの上にシリンジから6μLの純水を滴下して30秒後に測定することにより求めた。なお、水接触角は、θ/2法により算出される。 Here, the water contact angle of the surface portion of the optical fiber cable was 28 degrees. The water contact angle was determined by preparing a sheet having a thickness of 1 mm using the coating material, dropping 6 μL of pure water from the syringe onto the sheet at a temperature of 20° C., and measuring it 30 seconds later. The water contact angle is calculated by the θ/2 method.
また、光ファイバケーブルの表面部の氷塊密着力は、6N/mmであった。氷塊密着力は、以下のように求めた。まず、200mm以上の長さを有する光ファイバケーブル10の一方の端部側の20mmの長さの部分を純水に浸漬した後、これらの温度を−20℃にして浸漬部分の外周に氷塊を付着させた。その後、氷塊が付着した光ファイバケーブル10を0℃に設定した恒温槽に移動させて氷塊を0℃にした。そして、引張試験機を用いて、氷塊から光ファイバケーブル10を50mm/分の速さで引き抜いて引抜力の最大値を求めた。同様の操作を合計で5回行って、これら5回の引抜力の最大値の平均値を求めた。その後、長さ1mmあたりに換算、すなわち1/20倍することにより、氷塊密着力を求めた。
In addition, the adhesion force of ice blocks on the surface of the optical fiber cable was 6 N/mm. The ice block adhesion was determined as follows. First, a portion having a length of 20 mm on one end side of the
(実施例2)
表1に示すように、被覆材料として、ノンハロゲン難燃化ポリエチレン樹脂100質量部に対して、フッ素系界面活性剤(AGCセイミケミカル株式会社製、商品名:S−420、パーフルオロアルキルエチレンオキシド付加物)6質量部としたものを用いたことを除いて、実施例1と同様にして光ファイバケーブルを作製した。なお、光ファイバケーブルの表面部の水接触角は29度、氷塊密着力は6N/mmであった。
(Example 2)
As shown in Table 1, as a coating material, a fluorosurfactant (manufactured by AGC Seimi Chemical Co., Ltd., trade name: S-420, perfluoroalkylethylene oxide adduct) relative to 100 parts by mass of a halogen-free flame-retardant polyethylene resin. ) An optical fiber cable was produced in the same manner as in Example 1 except that 6 parts by mass was used. The water contact angle on the surface of the optical fiber cable was 29 degrees, and the ice block adhesion was 6 N/mm.
(実施例3)
表1に示すように、被覆材料として、ノンハロゲン難燃化ポリエチレン樹脂100質量部に対して、フッ素系界面活性剤(AGCセイミケミカル株式会社製、商品名:S−420、パーフルオロアルキルエチレンオキシド付加物)1質量部としたものを用いたことを除いて、実施例1と同様にして光ファイバケーブルを作製した。なお、光ファイバケーブルの表面部の水接触角は30度、氷塊密着力は8N/mmであった。
(Example 3)
As shown in Table 1, as a coating material, a fluorosurfactant (manufactured by AGC Seimi Chemical Co., Ltd., trade name: S-420, perfluoroalkylethylene oxide adduct) relative to 100 parts by mass of a halogen-free flame-retardant polyethylene resin. ) An optical fiber cable was produced in the same manner as in Example 1 except that 1 part by mass was used. The water contact angle of the surface of the optical fiber cable was 30 degrees, and the ice block adhesion was 8 N/mm.
(比較例1)
表1に示すように、被覆材料として、ノンハロゲン難燃化ポリエチレン樹脂100質量部に対して、シリコーン系撥水剤(東レ・ダウコーニング株式会社製、商品名:DOW CORNING TORAY BY 27−202 H)6質量部としたものを用いたことを除いて、実施例1と同様にして光ファイバケーブルを作製した。なお、光ファイバケーブルの表面部の水接触角は112度、氷塊密着力は10N/mmであった。
(Comparative example 1)
As shown in Table 1, as a coating material, a silicone water repellent (manufactured by Toray Dow Corning Co., Ltd., trade name: DOW CORNING TORAY BY 27-202 H) is used with respect to 100 parts by mass of a halogen-free flame-retardant polyethylene resin. An optical fiber cable was produced in the same manner as in Example 1 except that 6 parts by mass was used. The water contact angle on the surface of the optical fiber cable was 112 degrees, and the ice block adhesion was 10 N/mm.
(比較例2)
表1に示すように、被覆材料として、ノンハロゲン難燃化ポリエチレン樹脂のみを用いたことを除いて、実施例1と同様にして光ファイバケーブルを作製した。なお、光ファイバケーブルの表面部の水接触角は100度、氷塊密着力は14N/mmであった。
(Comparative example 2)
As shown in Table 1, an optical fiber cable was produced in the same manner as in Example 1 except that only non-halogen flame-retardant polyethylene resin was used as the coating material. The water contact angle on the surface of the optical fiber cable was 100 degrees, and the ice block adhesion was 14 N/mm.
次に、実施例1、2、3、比較例1、2の光ファイバケーブルについて、以下のようにして、筒雪、敷設張力の評価を行った。 Next, with respect to the optical fiber cables of Examples 1, 2, and 3 and Comparative Examples 1 and 2, the snow cover and the laying tension were evaluated as follows.
図3に示すように、2本の電柱31、電柱32を30m程の間隔を設けて設置し、これらの間に、引留部33、引留部34を用いて、光ファイバケーブル35を敷設した。なお、光ファイバケーブル35の途中には、敷設張力を測定するためのロードセル36を配置した。また、電柱31の上部には、観察を行うためのカメラ37を配置した。
As shown in FIG. 3, two
筒雪については、降雪時の夜間から昼間にかけてカメラ37により光ファイバケーブル35における筒雪の状態を観察することにより評価を行った。表中、「○」は、観察期間中、いずれの部分にも光ファイバケーブル35の高さの5倍を超えるような直径の筒雪が発生しなかったこと、「×」は、観察期間中、いずれかの部分に光ファイバケーブル35の高さの5倍を超えるような直径の筒雪が発生したことを示す。
The snowfall was evaluated by observing the snowfall state of the
敷設張力については、ロードセル36により光ファイバケーブル35の敷設張力を測定した。表中、敷設張力は、測定期間中の最大値である。なお、敷設張力が小さいほど、氷雪の付着を抑制する効果が高い。
Regarding the laying tension, the laying tension of the
表1からも明らかなように、実施例1、2、3の光ファイバケーブルについては、フッ素系界面活性剤を含有することにより、水接触角が30度以下かつ氷塊密着力が10N/mm以下になっている。また、水接触角が30度以下かつ氷塊密着力が10N/mm以下である場合、氷雪の付着が抑制され、筒雪の形成および成長が抑制される。 As is clear from Table 1, regarding the optical fiber cables of Examples 1, 2, and 3, the inclusion of the fluorine-based surfactant results in a water contact angle of 30 degrees or less and an ice block adhesion of 10 N/mm or less. It has become. When the water contact angle is 30 degrees or less and the ice block adhesion is 10 N/mm or less, the adhesion of ice and snow is suppressed, and the formation and growth of tube snow is suppressed.
10…光ファイバケーブル、11…支持線部、12…ケーブル部、13…連結部、14…支持線、15…外被、16…光ファイバ心線、17…抗張力体、18…外被、19…ノッチ。
DESCRIPTION OF
Claims (3)
前記架空ケーブルは、前記外被内部に支持線を有する支持線部と、前記外被内部に前記心線として少なくとも光ファイバ心線を有するケーブル部と、前記支持線部と前記ケーブル部とを連結する連結部とを有する、前記支持線部端部から前記ケーブル部端部に至る最大幅が15mm以下の光ファイバケーブルであり、
前記外被の材料は、オレフィン類を重合させた熱可塑性樹脂と、フッ素系界面活性剤とを含有し、
前記フッ素系界面活性剤は、前記熱可塑性樹脂100質量部に対して0.1質量部以上10質量部以下であり、
前記支持線と少なくとも前記光ファイバ心線の外周に、前記外被の材料にて前記支持線部と、前記ケーブル部と、前記連結部が一体的に形成され、
前記外被及び前記連結部は、20℃での水接触角が30度以下かつ0℃での氷塊密着力が10N/mm以下であることを特徴とする架空ケーブル。 An aerial cable having a core wire and a jacket covering the core wire,
The overhead cable connects a support wire portion having a support wire inside the jacket, a cable portion having at least an optical fiber core wire as the core wire inside the jacket, and the support wire portion and the cable portion. An optical fiber cable having a maximum width of 15 mm or less from the end of the support wire portion to the end of the cable portion.
The jacket material includes a thermoplastic resin obtained by polymerizing olefins containing a fluorine-based surfactant,
The fluorine-based surfactant is 0.1 parts by mass or more and 10 parts by mass or less with respect to 100 parts by mass of the thermoplastic resin,
On the outer periphery of the support wire and at least the optical fiber core wire, the support wire portion, the cable portion, and the connecting portion are integrally formed of the material of the jacket,
The outer cable and the connecting portion have a water contact angle at 20° C. of 30 degrees or less and an ice block adhesion force at 0° C. of 10 N/mm or less.