JP6733412B2

JP6733412B2 - Toilet roll

Info

Publication number: JP6733412B2
Application number: JP2016156380A
Authority: JP
Inventors: 真悟服部; 宏幸永谷
Original assignee: Oji Holdings Corp; Oji Paper Co Ltd
Current assignee: New Oji Paper Co Ltd; Oji Holdings Corp
Priority date: 2016-08-09
Filing date: 2016-08-09
Publication date: 2020-07-29
Anticipated expiration: 2036-08-09
Also published as: JP2018023490A

Description

本発明は、トイレットロールに関する。 The present invention relates to a toilet roll.

トイレットペーパー製品は、トイレットペーパーウェブを１枚又は２枚以上に重ねたトイレットペーパーを所定の大きさに切断して製造される。一般的には長尺のトイレットペーパーがロール状に巻回されてなるトイレットロール（ロール状トイレットペーパー）が多用されている。１枚のトイレットペーパーウェブからなるトイレットペーパーは１プライのトイレットペーパーと称され、２枚重ねのトイレットペーパーウェブからなるトイレットペーパーは２プライのトイレットペーパーと称されている。 The toilet paper product is produced by cutting one or two or more toilet paper webs into a predetermined size. Generally, a toilet roll (rolled toilet paper) formed by winding a long toilet paper in a roll shape is often used. Toilet paper consisting of one sheet of toilet paper web is referred to as 1-ply toilet paper, and toilet paper consisting of two-ply toilet paper web is referred to as 2-ply toilet paper.

トイレットペーパーは、例えば、１２ロールや１６ロールといった単位で包装されたものが広く流通している。しかし、これらの包装体は嵩張るため、持ち運べる量は限られている。また、公共施設等においてはトイレットロールの保管スペースも不足しがちである。このため、トイレットロールを構成するトイレットペーパーの紙厚を調整したり、ロール状に巻き取る際の巻き締め力を強くすることで巻長を長くしたロール製品の利用も進んでいる（例えば、特許文献１及び２）。 The toilet paper, which is packaged in units such as 12 rolls or 16 rolls, is widely distributed. However, since these packages are bulky, the amount that can be carried is limited. Moreover, the storage space for toilet rolls tends to be insufficient in public facilities and the like. For this reason, the use of roll products having a longer winding length by adjusting the paper thickness of the toilet paper that constitutes the toilet roll, or by increasing the winding tightening force when winding the toilet roll (for example, patents References 1 and 2).

特許文献１には、１枚の衛生薄葉紙をロール状に巻き取った衛生薄葉紙ロールであって、衛生薄葉紙の１枚当りの坪量が１６．５〜２１．５ｇ／ｍ²、かつ紙厚が０．６〜１．１ｍｍ／１０枚以下であり、衛生薄葉紙ロールの巻長が１２０〜１８５ｍ、巻直径が１００〜１３２ｍｍである衛生薄葉紙ロールが開示されている。ここでは、坪量を下げずに、風合いや使用感を向上させることが検討されている。
また、特許文献２には、フィルムからなる包装袋にロール製品を複数個収納してなるロール製品パッケージが開示されている。特許文献２には、ロール製品が１プライの場合、坪量が１６．５〜２１．５ｇ／ｍ²であることが好ましいと記載されている。 Patent Document 1 discloses a sanitary thin paper roll obtained by winding a single sheet of sanitary thin paper into a roll having a basis weight of 16.5 to 21.5 g/m ² and a paper thickness of one sheet of sanitary thin paper. There is disclosed a sanitary thin paper roll having a size of 0.6 to 1.1 mm/10 or less, a sanitary thin paper roll having a winding length of 120 to 185 m and a winding diameter of 100 to 132 mm. Here, it is considered to improve the texture and the feeling of use without reducing the basis weight.
Further, Patent Document 2 discloses a roll product package in which a plurality of roll products are stored in a packaging bag made of a film. Patent Document 2 describes that when the roll product has one ply, the basis weight is preferably 16.5 to 21.5 g/m ² .

特開２０１４−２３３３６３号公報JP, 2014-233363, A 特開２０１５−１０１３８８号公報JP, 2005-101388, A

従来の巻長を長くしたトイレットロールにおいては、巻長を長くするために、トイレットペーパーをきつく巻き締めるため、トイレットペーパーの強度を高める必要があった。しかしながら、巻き締めに耐え得るトイレットペーパーにおいては、強度が高められている一方で、それ自体の柔らかさや肌触りが悪化する傾向にあった。 In the conventional toilet roll having a long winding length, it is necessary to increase the strength of the toilet paper by tightly winding the toilet paper in order to increase the winding length. However, the strength of the toilet paper that can withstand winding has been increased, but the softness and touch of the toilet paper itself tend to deteriorate.

また、１プライのトイレットロールにおいては、巻長を長くするために、巻き取り工程で得られる巻取が固くなり、所定の幅に断裁する際に、コア芯（紙管）が潰れる場合があった。コア芯（紙管）が潰れたトイレットロールは、外観が悪化するだけでなく、使用時にトイレットペーパーをスムーズに引き出すことができないという問題も引き起こす。 Further, in the case of a 1-ply toilet roll, since the winding length is increased, the winding obtained in the winding step becomes hard, and the core (paper tube) may be crushed when cut into a predetermined width. It was A toilet roll with a crushed core (paper tube) not only deteriorates the appearance, but also causes a problem that the toilet paper cannot be pulled out smoothly during use.

そこで本発明者らは、このような従来技術の課題を解決するために、良好な肌触りを有するトイレットペーパーから構成されたトイレットロールを提供することを目的として検討を進めた。また、本発明者らは、コア芯潰れのないトイレットロールを提供することも目的として検討を進めた。 In order to solve such problems of the prior art, the present inventors have conducted studies for the purpose of providing a toilet roll composed of toilet paper having good touch. Further, the present inventors have conducted investigations for the purpose of providing a toilet roll without core collapse.

上記の課題を解決するために鋭意検討を行った結果、本発明者らは、１プライのトイレットロールにおいて、トイレットロールを構成するトイレットペーパーの坪量を所定の範囲とし、かつトイレットペーパーにエンボスを形成することで、巻長の長いトイレットロールを構成するトイレットペーパーにおいてもその肌触りを高め得ることを見出した。さらに、本発明者らは、このようなトイレットロールにおいては、コア芯潰れの発生がないことを発見し、本発明を完成するに至った。
具体的に、本発明は、以下の構成を有する。 As a result of earnest studies to solve the above problems, the present inventors have determined that in a 1-ply toilet roll, the basis weight of the toilet paper that constitutes the toilet roll is within a predetermined range, and the toilet paper is embossed. It has been found that, by forming the toilet roll, the touch can be improved even in the toilet paper that constitutes a long roll. Furthermore, the present inventors have found that core crushing does not occur in such a toilet roll, and have completed the present invention.
Specifically, the present invention has the following configurations.

［１］１プライのトイレットペーパーを巻き取ってロール状としたトイレットロールであって、トイレットロールの巻長が９５ｍ以上１５０ｍ以下であり、巻径が１１０ｍｍ以上１２０ｍｍ以下であり、トイレットペーパーの１プライ当たりの坪量が１０ｇ／ｍ²以上１６ｇ／ｍ²以下であり、トイレットペーパーにはエンボス加工が施されたものであるトイレットロール。
［２］トイレットペーパーの表面及び裏面のハンドフィール値の平均が６５．０以上である［１］に記載のトイレットロール。
［３］トイレットペーパーに５０ｇｆ／ｃｍ²の圧力をかけた際の厚みが７５μｍ以上１１０μｍ以下である［１］又は［２］に記載のトイレットロール。
［４］トイレットペーパーに０．５ｇｆ／ｃｍ²の圧力をかけた際の厚みが１８０μｍ以上３００μｍ以下である［１］〜［３］のいずれかに記載のトイレットロール。 [1] A toilet roll in which 1-ply toilet paper is wound into a roll shape, the toilet roll has a winding length of 95 m or more and 150 m or less, and a winding diameter of 110 mm or more and 120 mm or less. The toilet roll has a basis weight of 10 g/m ² or more and 16 g/m ² or less, and the toilet paper is embossed.
[2] The toilet roll according to [1], wherein the average of handfeel values on the front surface and the back surface of the toilet paper is 65.0 or more.
[3] The toilet roll according to [1] or [2], which has a thickness of 75 μm or more and 110 μm or less when a pressure of 50 gf/cm ² is applied to the toilet paper.
[4] The toilet roll according to any one of [1] to [3], which has a thickness of 180 μm or more and 300 μm or less when a pressure of 0.5 gf/cm ² is applied to the toilet paper.

本発明によれば、巻長の長い１プライのトイレットロールを、肌触りが良好なトイレットペーパーで構成することができる。また、本発明によれば、コア芯潰れのないトイレットロールを得ることができる。 According to the present invention, a 1-ply toilet roll having a long winding length can be formed of toilet paper having a good touch. Further, according to the present invention, a toilet roll without core core collapse can be obtained.

図１は、本発明のトイレットロールの構成を説明する概略図である。FIG. 1 is a schematic diagram illustrating the configuration of the toilet roll of the present invention. 図２は、本発明のトイレットロールの構成を説明する概略図である。FIG. 2 is a schematic diagram illustrating the configuration of the toilet roll of the present invention.

以下において、本発明について詳細に説明する。以下に記載する構成要件の説明は、代表的な実施形態や具体例に基づいてなされることがあるが、本発明はそのような実施形態に限定されるものではない。 Hereinafter, the present invention will be described in detail. The description of the constituent elements described below may be made based on typical embodiments or specific examples, but the present invention is not limited to such embodiments.

（トイレットロール）
本発明は、１プライのトイレットペーパーを巻き取ってロール状としたトイレットロールに関する。ここで、本発明のトイレットロールの巻長は９５ｍ以上１５０ｍ以下であり、巻径は１１０ｍｍ以上１２０ｍｍ以下である。また、本発明のトイレットロールを構成するトイレットペーパーの１プライ当たりの坪量は１０ｇ／ｍ²以上１６ｇ／ｍ²以下である。そして、本発明のトイレットロールを構成する１プライのトイレットペーパーにはエンボス加工が施されている。 (Toilet roll)
The present invention relates to a toilet roll in which a 1-ply toilet paper is wound into a roll shape. Here, the roll length of the toilet roll of the present invention is 95 m or more and 150 m or less, and the roll diameter is 110 mm or more and 120 mm or less. The basis weight of the toilet paper constituting the toilet roll of the present invention is 10 g/m ² or more and 16 g/m ² or less. The 1-ply toilet paper constituting the toilet roll of the present invention is embossed.

本発明のトイレットロールは上記構成を有するものであるため、巻長の長いトイレットロールであるにも関わらず、肌触りが良好なトイレットペーパーで構成されている。また、トイレットペーパーには、エンボス加工が施されているため、トイレットペーパー自体の嵩高さや厚み感が損なわれることがない。このため、１プライ品であり、かつ巻長の長いトイレットロールであるにも関わらず、トイレットペーパーの使用感が低下することがない。さらに本発明においては、巻長の長いトイレットロールを構成する際の所定の幅に断裁する時にコア芯が潰れることが抑制されている。 Since the toilet roll of the present invention has the above-mentioned configuration, it is made of a toilet paper having a good feel to the touch, even though the toilet roll has a long winding length. Moreover, since the toilet paper is embossed, the bulkiness and thickness of the toilet paper itself are not impaired. Therefore, even though the toilet roll is a one-ply product and has a long winding length, the usability of the toilet paper does not deteriorate. Further, in the present invention, the core of the core is prevented from being crushed when the toilet roll having a long winding length is cut into a predetermined width.

図１は、本発明のトイレットペーパーの構成を説明する概略図である。図１では、２プライのトイレットペーパー２０から構成されるトイレットロール１００を図示している。トイレットロール１００においては、トイレットペーパー２０のうち、巻外側に配される面を表面（ａ）といい、巻内側に配される面を裏面（ｂ）という。 FIG. 1 is a schematic diagram illustrating the configuration of the toilet paper of the present invention. FIG. 1 illustrates a toilet roll 100 including a two-ply toilet paper 20. In the toilet roll 100, the surface of the toilet paper 20 arranged on the outer side of the roll is called the front surface (a), and the surface arranged on the inner side of the roll is called the rear surface (b).

本発明のトイレットロールの巻長（巻き長さ）は９５ｍ以上１５０ｍ以下である。このような巻長を有するトイレットロールは、いわゆる長巻トイレットロールと呼ばれることもある。また、２倍巻トイレットロールもしくは３倍巻トイレットロールと称されることもある。 The roll length (roll length) of the toilet roll of the present invention is 95 m or more and 150 m or less. The toilet roll having such a roll length is sometimes called a so-called long roll toilet roll. It may also be referred to as a double roll or triple roll toilet roll.

本発明のトイレットロールの巻径（外径）は、１１０ｍｍ以上１２０ｍｍ以下であることが好ましい。ここで、トイレットロールの巻径は、図２においてＲで表される長さである。トイレットロールの巻径を上記範囲内とすることにより、あらゆるトイレットロールホルダーにトイレットロールを設置することができ、使用場面が制限されることはない。 The roll diameter (outer diameter) of the toilet roll of the present invention is preferably 110 mm or more and 120 mm or less. Here, the roll diameter of the toilet roll is a length represented by R in FIG. By setting the winding diameter of the toilet roll within the above range, the toilet roll can be installed in any toilet roll holder, and the usage scene is not limited.

本発明のトイレットロールを構成するトイレットペーパーの１プライ当たりの坪量は、１０ｇ／ｍ²以上１６ｇ／ｍ²以下である。トイレットペーパーの１プライ当たりの坪量は、１０ｇ／ｍ²以上であればよく、１１ｇ／ｍ²以上であることが好ましく、１２ｇ／ｍ²以上であることがより好ましい。また、トイレットペーパーの１プライ当たりの坪量は、１６ｇ／ｍ²以下であればよく、１５．５ｇ／ｍ²以下であることが好ましい。
本発明においては、トイレットペーパーの坪量を上記範囲内とすることにより、所望の巻径を有するトイレットロールを製造しやすくなる。通常、巻長の長いトイレットロールを製造する際には、ロール状に巻き取る際の巻き締め力を強くすることによって巻径をコントロールしている。しかし、本発明においては、ロール状に巻き取る際の巻き締め力を従来法における強さまで強くしなくても所望の巻径を有するトイレットロールを製造することができる。また、巻取の固さを抑えることで所定の幅に断裁する際にコア芯（紙管）潰れの発生をより効果的に抑制することができる。 The basis weight of the toilet paper constituting the toilet roll of the present invention per ply is 10 g/m ² or more and 16 g/m ² or less. The basis weight per ply of the toilet paper may be 10 g/m ² or more, preferably 11 g/m ² or more, and more preferably 12 g/m ² or more. The basis weight of the toilet paper per ply may be 16 g/m ² or less, preferably 15.5 g/m ² or less.
In the present invention, by setting the basis weight of the toilet paper within the above range, it becomes easy to manufacture a toilet roll having a desired winding diameter. Usually, when manufacturing a toilet roll having a long winding length, the winding diameter is controlled by increasing the winding tightening force when winding the roll into a roll shape. However, according to the present invention, it is possible to manufacture a toilet roll having a desired winding diameter without increasing the winding tightening force at the time of winding into a roll to the strength of the conventional method. Further, by suppressing the winding hardness, it is possible to more effectively suppress the occurrence of core core (paper tube) crushing when cutting to a predetermined width.

本発明のトイレットロールを構成する１プライのトイレットペーパーにはエンボス加工が施されている。本発明においては、１プライのトイレットペーパーの幅方向に略均一にエンボスが形成される。ここで、幅方向に略均一にエンボスが形成された場合、長さ方向の任意点から±０．５ｃｍ（長さ１ｃｍ）の長さを有する領域において、幅方向に略均一密度のエンボスが観測される。また、本発明においては、エンボスは長さ方向にも略均一にエンボスが形成されることが好ましい。すなわち、１プライのトイレットペーパーの全領域にわたって、略均一にエンボスが形成される。図１に示されたトイレットロールにおいて、巻きとかれたトイレットペーパーに施されているエンボスの様子は黒点で図示されている。図１のトイレットペーパーのエンボス加工の様子からもわかるように、本発明においては、トイレットペーパーの全領域にわたって、略均一にエンボスが形成されている。 The 1-ply toilet paper constituting the toilet roll of the present invention is embossed. In the present invention, the emboss is formed substantially uniformly in the width direction of the 1-ply toilet paper. Here, when the embossing is formed substantially uniformly in the width direction, an embossing of a substantially uniform density is observed in the width direction in a region having a length of ±0.5 cm (length 1 cm) from an arbitrary point in the length direction. To be done. Further, in the present invention, it is preferable that the emboss is formed substantially uniformly in the length direction. That is, the emboss is formed substantially uniformly over the entire area of the 1-ply toilet paper. In the toilet roll shown in FIG. 1, the embossed state applied to the rolled toilet paper is shown by a black dot. As can be seen from the state of embossing the toilet paper in FIG. 1, in the present invention, the embossing is formed substantially uniformly over the entire area of the toilet paper.

ここで、トイレットペーパーを幅方向に３分割した際に、隣り合う領域のエンボス密度の差は、それぞれ１０％以下であることが好ましい。具体的には、長さ方向の任意点から±０．５ｃｍ（長さ１ｃｍ）の長さを有する領域をサンプルとして切り出し、このサンプルを幅方向に３分割する。この場合、端縁から順に第１領域、第２領域、第３領域とに分割される。本発明においては、第１領域と第２領域のエンボス密度の差が１０％以下であることが好ましく、第２領域と第３領域のエンボス密度の差も１０％以下であることが好ましい。なお、第１領域と第３領域のエンボス密度の差も１０％以下であることが好ましい。 Here, when the toilet paper is divided into three in the width direction, it is preferable that the difference between the embossing densities of the adjacent regions is 10% or less. Specifically, a region having a length of ±0.5 cm (length 1 cm) is cut out as a sample from an arbitrary point in the length direction, and this sample is divided into three in the width direction. In this case, it is divided into a first area, a second area, and a third area in order from the edge. In the present invention, the difference in embossing density between the first region and the second region is preferably 10% or less, and the difference in embossing density between the second region and the third region is also preferably 10% or less. The difference in embossing density between the first region and the third region is also preferably 10% or less.

トイレットペーパーのエンボスパターンでは、１個のエンボス直径は０．５ｍｍ以上２ｍｍ以下が好ましく、０．７ｍｍ以上１．３ｍｍ以下がより好ましい。またエンボス密度は１０個／ｃｍ²以上３０個／ｃｍ²以下が好ましく、１５個／ｃｍ²以上２５個／ｃｍ²以下がより好ましい。 In the embossing pattern of toilet paper, one embossing diameter is preferably 0.5 mm or more and 2 mm or less, and more preferably 0.7 mm or more and 1.3 mm or less. The embossing density is preferably 10 pieces/cm ² or more and 30 pieces/cm ² or less, and more preferably 15 pieces/cm ² or more and 25 pieces/cm ² or less.

エンボス加工は、エンボスの付与されたエンボスロールを幅方向の全域に当てて、加圧することで行う。エンボスロールの押し込み量は、トイレットペーパーの厚みが後述する条件を満たすように調整することが好ましい。 The embossing is performed by applying an embossing roll with embossing to the entire area in the width direction and applying pressure. The pushing amount of the embossing roll is preferably adjusted so that the thickness of the toilet paper satisfies the condition described below.

本発明のトイレットロールを構成する１プライのトイレットペーパーに５０ｇｆ／ｃｍ²の圧力をかけた際の厚み（Ｔ_m）は７５μｍ以上であることが好ましく、８０μｍ以上であることがより好ましい。また、厚み（Ｔ_m）は１１０μｍ以下であることが好ましく、１００μｍ以下であることがより好ましい。厚み（Ｔ_m）を上記範囲内とすることにより、トイレットペーパーの厚み感をしっかりと感じとることができ、肌触りや使用感に優れたトイレットペーパーを得ることができる。 The thickness (T _m ) when a pressure of 50 gf/cm ² is applied to the 1-ply toilet paper that constitutes the toilet roll of the present invention is preferably 75 μm or more, and more preferably 80 μm or more. Further, the thickness (T _m ) is preferably 110 μm or less, and more preferably 100 μm or less. By setting the thickness (T _m ) within the above range, the thickness of the toilet paper can be firmly felt, and the toilet paper excellent in touch and feel can be obtained.

また、本発明のトイレットロールを構成する１プライのトイレットペーパーに０．５ｇｆ／ｃｍ²の圧力をかけた際の厚み（Ｔ₀）は１８０μｍ以上であることが好ましく、１９０μｍ以上であることがより好ましく、２００μｍ以上であることがさらに好ましく、２１０μｍ以上であることが特に好ましい。また、厚み（Ｔ₀）は３００μｍ以下であることが好ましく、２８０μｍ以下であることがより好ましく、２６０μｍ以下であることがさらに好ましく、２４０μｍ以下であることが特に好ましい。厚み（Ｔ₀）を上記範囲内とすることによっても、トイレットペーパーの肌触りを高めることができる。 The thickness (T ₀ ) when a pressure of 0.5 gf/cm ² is applied to the 1-ply toilet paper constituting the toilet roll of the present invention is preferably 180 μm or more, and more preferably 190 μm or more. The thickness is preferably 200 μm or more, more preferably 210 μm or more. The thickness (T ₀ ) is preferably 300 μm or less, more preferably 280 μm or less, further preferably 260 μm or less, and particularly preferably 240 μm or less. By setting the thickness (T ₀ ) within the above range, the touch of the toilet paper can be improved.

ここで、上述した厚み（Ｔ₀）及び厚み（Ｔ_m）の値はＫＥＳＦＢ３−ＡＵＴＯ−Ａ自動化圧縮試験機（カトーテック株式会社製）を用いて測定することができる。具体的には、ＫＥＳＦＢ３−ＡＵＴＯ−Ａ自動化圧縮試験機の２ｃｍ²の加圧板と受圧板間に１０ｃｍ×２０ｃｍの大きさにカットしたサンプルを設置し、５０秒／ｍｍの速さで加圧板を下降させ、その際に変化する圧力とその時のサンプルの厚みを測定する。Ｔ₀は圧力が０．５ｇｆ／ｃｍ²におけるサンプルの厚み（ｍｍ）であり、Ｔ_mは圧力が５０ｇｆ／ｃｍ²におけるサンプルの厚み（ｍｍ）である。Ｔ₀及びＴ_mの値はエンボスの凹面（エンボスロールを押し当てた面）を加圧板側として１０回の測定を行い、得られた測定データからＨａｍｐｅｌｉｄｅｎｔｉｆｉｅｒの方法で異常値を除外し、平均値として算出した値である。なお、上記サンプルの測定はＩＳＯ１８７に準拠した環境（温度２３±１℃、相対湿度５０±２％）で行う。 Here, the values of the thickness (T ₀ ) and the thickness (T _m ) described above can be measured using a KES FB3-AUTO-A automated compression tester (manufactured by Kato Tech Co., Ltd.). Specifically, a sample cut into a size of 10 cm×20 cm is installed between the pressure plate of 2 cm ² and the pressure plate of the KES FB3-AUTO-A automated compression tester, and the pressure plate is pressed at a speed of 50 seconds/mm. Is lowered, and the pressure that changes at that time and the thickness of the sample at that time are measured. T ₀ is the thickness (mm) of the sample at a pressure of 0.5 gf/cm ² , and T _m is the thickness (mm) of the sample at a pressure of 50 gf/cm ² . The values of T ₀ and T _m were measured 10 times with the embossed concave surface (the surface against which the embossing roll was pressed) as the pressure plate side, and abnormal values were excluded from the obtained measurement data by the method of Hampel identifier, and the average It is the value calculated as the value. In addition, the measurement of the sample is performed in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%).

本発明のトイレットロールは、コア芯（紙管）にトイレットペーパーを巻いてなるものである。コア芯径は３０ｍｍ以上４０ｍｍ以下であることが好ましい。トイレットロールのコア芯径はコア芯（紙管）の直径であり、図２においてＳで表されている長さである。 The toilet roll of the present invention is obtained by winding toilet paper around a core (paper tube). The core diameter is preferably 30 mm or more and 40 mm or less. The core diameter of the toilet roll is the diameter of the core (paper tube), and is the length represented by S in FIG.

本発明のトイレットロールの巻き密度は、巻長が９５ｍの場合は、０．９５ｍ／ｃｍ²以上であることが好ましく、１．０３ｍ／ｃｍ²以上であることがより好ましい。また、１．１５ｍ／ｃｍ²以下であることが好ましく、１．１２ｍ／ｃｍ²以下であることがより好ましい。
トイレットロールの巻き密度は、巻長が１２０ｍの場合は、１．１５ｍ／ｃｍ²以上であることが好ましく、１．３１ｍ／ｃｍ²以上であることがより好ましい。また、１．４５ｍ／ｃｍ²以下であることが好ましく、１．４１ｍ／ｃｍ²以下であることがより好ましい。
トイレットロールの巻き密度は、巻長が１５０ｍの場合は、１．４５ｍ／ｃｍ²以上であることが好ましく、１．６３ｍ／ｃｍ²以上であることがより好ましい。また、１．８５ｍ／ｃｍ²以下であることが好ましく、１．７７ｍ／ｃｍ²以下であることがより好ましい。
なお、上記巻き密度は、コア芯径を３９ｍｍとした場合の値である。 Winding density of toilet rolls of the present invention, when the winding length is 95 m, is preferably 0.95 m / cm ² or more, and more preferably 1.03 m / cm ² or more. Further, it is preferably 1.15 m/cm ² or less, and more preferably 1.12 m/cm ² or less.
Winding density of toilet rolls, if the winding length of 120 m, is preferably 1.15 m / cm ² or more, and more preferably 1.31m / cm ² or more. Further, it is preferably 1.45 m/cm ² or less, and more preferably 1.41 m/cm ² or less.
Winding density of toilet rolls, if the winding length of 150 meters, is preferably 1.45 m / cm ² or more, and more preferably 1.63 m / cm ² or more. Further, it is preferably 1.85 m / cm ² or less, and more preferably 1.77 m / cm ² or less.
The winding density is a value when the core diameter is 39 mm.

トイレットロールの巻き密度は、２プライのトイレットロールの巻長の長さを紙管の断面積を除いたロールの断面積（図２におけるＰ（ドット状模様部分））で除すことにより算出した値である。すなわち、巻き密度は下記の式で算出することができる。
巻き密度（ｍ／ｃｍ²）＝巻長／トイレットロール断面積 The roll density of the toilet roll was calculated by dividing the roll length of the 2-ply toilet roll by the roll cross-sectional area (P (dot-shaped pattern portion) in FIG. 2) excluding the cross-sectional area of the paper tube. It is a value. That is, the winding density can be calculated by the following formula.
Winding density (m / cm ²⁾ = winding length / toilet rolls sectional area

本発明のトイレットペーパーの表面及び裏面のハンドフィール値の平均は６５．０以上であることが好ましく、６６．０以上であることがより好ましい。なお、ＨＦ値の上限は特に限定されるものではないが、一般的に９５．０以下であることが好ましい。 The average handfeel value of the front and back surfaces of the toilet paper of the present invention is preferably 65.0 or more, more preferably 66.0 or more. Although the upper limit of the HF value is not particularly limited, it is generally preferably 95.0 or less.

ここで、ハンドフィール値（ＨＦ値）は、ティシューソフトネスアナライザー（ＥｍｔｅｃＥｌｅｃｔｒｏｎｉｃＧｍｂＨ社製）を用いて、以下の測定方法によって測定することができる。
まず、ティシューソフトネスアナライザーのサンプル台に、直径１１２．８ｍｍの円形にカットしたサンプルを設置する。このサンプルに対し、ブレード付きローターを１００ｍＮの押し込み圧力をかけて上方から押し込む。その後、ブレード付きローターを回転数が２．０回転／秒となるように回転させ、その時の振動周波数を測定する。
また、直径１１２．８ｍｍの円形にカットした別のサンプルに対し、ブレード付きローターを１００ｍＮと、６０ｍＮの圧力で押し込んだ際の上下方向の変形変位量を算出する。ＨＦ値は、振動周波数と変形変位量から算出される値であり、計算のアルゴリズムはＴＰＩＩを用いることができる。
ＨＦ値を算出する際は、表裏面について測定をそれぞれ１０回ずつ行い、得られた測定データからＨａｍｐｅｌｉｄｅｎｔｉｆｉｅｒの方法で異常値を除外する。そして、各表面のＨＦ値の平均値から、トイレットペーパーのＨＦ値の平均値を算出する。
なお、上記サンプルの測定はＩＳＯ１８７に準拠した環境（温度２３±１℃、相対湿度５０±２％）で行う。また、測定の際には、付属の説明書に従い標準サンプル（ｅｍｅｔｅｃｒｅｆ．２Ｘ（ｎｎ．ｎ））で校正し、アルゴリズムをＴＰＩＩに設定する。計算ソフトウェアとしてはｅｍｅｔｅｃｍｅａｓｕｒｅｍｅｎｔｓｙｓｔｅｍｖｅｒ．３．２２を使用する。 Here, the hand feel value (HF value) can be measured by the following measurement method using a tissue softness analyzer (manufactured by Emtec Electronic GmbH).
First, a circularly cut sample having a diameter of 112.8 mm is set on a sample table of a tissue softness analyzer. A rotor with a blade is pressed into this sample from above by applying a pressing pressure of 100 mN. Then, the rotor with blades is rotated so that the rotation speed is 2.0 rotations/second, and the vibration frequency at that time is measured.
In addition, the amount of deformation displacement in the vertical direction when the rotor with blades was pushed in at a pressure of 100 mN and 60 mN for another sample cut into a circle having a diameter of 112.8 mm was calculated. The HF value is a value calculated from the vibration frequency and the amount of deformation displacement, and the calculation algorithm can use TP II.
When calculating the HF value, the measurement is performed 10 times for each of the front and back surfaces, and the abnormal value is excluded from the obtained measurement data by the method of the Hampel identifier. Then, the average HF value of the toilet paper is calculated from the average HF value of each surface.
In addition, the measurement of the sample is performed in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%). In addition, at the time of measurement, a standard sample (emetec ref.2X (nn.n)) is calibrated according to the attached instruction, and the algorithm is set to TP II. As the calculation software, emetec measurement system ver. Use 3.22.

トイレットペーパーの長さ方向の引張強度は、１．００Ｎ／１５ｍｍ以上であることが好ましく、１．３０Ｎ／１５ｍｍ以上であることがより好ましい。また、トイレットペーパーの長さ方向の引張強度は、３．００Ｎ／１５ｍｍ以下であることが好ましく、２．６０Ｎ／１５ｍｍ以下であることがより好ましい。
トイレットペーパーの幅方向の引張強度は０．３０Ｎ／１５ｍｍ以上であることが好ましく、０．４０Ｎ／１５ｍｍ以上であることがより好ましい。また、トイレットペーパーの幅方向の引張強度は２．００Ｎ／１５ｍｍ以下であることが好ましく、１．５０Ｎ／１５ｍｍ以下であることがより好ましく、１．２０Ｎ／１５ｍｍ以下であることがさらに好ましい。 The lengthwise tensile strength of the toilet paper is preferably 1.00 N/15 mm or more, and more preferably 1.30 N/15 mm or more. The tensile strength of the toilet paper in the length direction is preferably 3.00 N/15 mm or less, more preferably 2.60 N/15 mm or less.
The tensile strength of the toilet paper in the width direction is preferably 0.30 N/15 mm or more, and more preferably 0.40 N/15 mm or more. The tensile strength in the width direction of the toilet paper is preferably 2.00 N/15 mm or less, more preferably 1.50 N/15 mm or less, and further preferably 1.20 N/15 mm or less.

トイレットペーパーの引張強度の測定は、横型引張試験機（熊谷理器社製）を用いて行うことができる。この場合、幅が１５ｍｍのサンプルを用い、引張速度５０ｍｍ／分、スパン長１００ｍｍの条件で測定を行う。本願明細書における引張強度は１プライのトイレットペーパーの引張強度であり、６サンプルの平均値である。なお、引張強度の測定は、ＩＳＯ１８７に準拠した環境（温度２３±１℃、相対湿度５０±２％）で行う。 The tensile strength of the toilet paper can be measured using a horizontal tensile tester (manufactured by Kumagai Riki Co., Ltd.). In this case, a sample having a width of 15 mm is used, and the measurement is performed under the conditions of a tensile speed of 50 mm/min and a span length of 100 mm. The tensile strength in this specification is the tensile strength of 1-ply toilet paper, and is an average value of 6 samples. The tensile strength is measured in an environment according to ISO187 (temperature 23±1° C., relative humidity 50±2%).

（繊維原料）
トイレットペーパーは、繊維原料を含むスラリーを抄紙することによって得られる。繊維原料としては、パルプを用いることが好ましい。パルプとしては、木材パルプ、非木材パルプ、脱墨パルプを挙げることができる。木材パルプとしては例えば、広葉樹パルプ（広葉樹クラフトパルプ（ＬＫＰ））、針葉樹パルプ（針葉樹クラフトパルプ（ＮＫＰ））、サルファイトパルプ（ＳＰ）、溶解パルプ（ＤＰ）、ソーダパルプ（ＡＰ）、未晒しクラフトパルプ（ＵＫＰ）、酸素漂白クラフトパルプ（ＯＫＰ）等の化学パルプ等が挙げられる。また、セミケミカルパルプ（ＳＣＰ）、ケミグラウンドウッドパルプ（ＣＧＰ）等の半化学パルプ、砕木パルプ（ＧＰ）、サーモメカニカルパルプ（ＴＭＰ、ＢＣＴＭＰ）等の機械パルプ等が挙げられるが、特に限定されない。非木材パルプとしてはコットンリンターやコットンリント等の綿系パルプ、麻、麦わら、バガス等の非木材系パルプ、ホヤや海草等から単離されるセルロース、キチン、キトサン等が挙げられるが、特に限定されない。脱墨パルプとしては古紙を原料とする脱墨パルプが挙げられるが、特に限定されない。パルプは上記の１種を単独で用いてもよいし、２種以上混合して用いてもよい。 (Fiber raw material)
Toilet paper is obtained by making a slurry containing a fiber raw material. Pulp is preferably used as the fiber raw material. Examples of pulp include wood pulp, non-wood pulp, and deinked pulp. Examples of the wood pulp include hardwood pulp (hardwood kraft pulp (LKP)), softwood pulp (softwood kraft pulp (NKP)), sulfite pulp (SP), dissolving pulp (DP), soda pulp (AP), unbleached kraft. Examples include chemical pulp such as pulp (UKP) and oxygen bleached kraft pulp (OKP). In addition, semi-chemical pulps such as semi-chemical pulp (SCP) and chemi-groundwood pulp (CGP), mechanical pulps such as groundwood pulp (GP), thermomechanical pulp (TMP, BCTMP), etc. are mentioned, but not particularly limited. Examples of the non-wood pulp include cotton-based pulp such as cotton linter and cotton lint, non-wood-based pulp such as hemp, straw and bagasse, cellulose isolated from ascidian and seaweed, chitin, chitosan, etc., but are not particularly limited. .. Examples of the deinked pulp include deinked pulp made from waste paper, but are not particularly limited. As the pulp, one type of the above may be used alone, or two or more types may be mixed and used.

繊維原料としては、針葉樹パルプ及び広葉樹パルプから選択される少なくとも１種を用いることが好ましく、針葉樹パルプを用いることが好ましい。中でも、本発明においては、針葉樹パルプと広葉樹パルプを併用することが好ましく、針葉樹クラフトパルプ（ＮＫＰ）と広葉樹クラフトパルプ（ＬＫＰ）を併用することがより好ましい。 As the fiber raw material, it is preferable to use at least one selected from softwood pulp and hardwood pulp, and it is preferable to use softwood pulp. Among them, in the present invention, it is preferable to use the softwood pulp and the hardwood pulp together, and it is more preferable to use the softwood kraft pulp (NKP) and the hardwood kraft pulp (LKP) together.

繊維原料として針葉樹パルプが用いられる場合は、針葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、２０質量％以上であることが好ましく、３０質量％以上であることがより好ましく、４０質量％以上であることがさらに好ましい。また、針葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、８０質量％以下であることが好ましい。針葉樹パルプの含有量を上記範囲内とすることにより、トイレットペーパーの坪量やＨＦ値等を所望の範囲内とすることが容易になる。 When softwood pulp is used as the fiber raw material, the content of softwood pulp is preferably 20% by mass or more, and more preferably 30% by mass or more, based on the total mass of the pulp components contained in the toilet paper. More preferably, it is more preferably 40 mass% or more. Further, the content of the softwood pulp is preferably 80% by mass or less based on the total mass of the pulp components contained in the toilet paper. By setting the content of the softwood pulp within the above range, it becomes easy to set the basis weight, HF value, etc. of the toilet paper within a desired range.

繊維原料としては、針葉樹パルプと広葉樹パルプを併用することが好ましい。すなわち、トイレットペーパーには、針葉樹パルプの他に広葉樹パルプがさらに含まれることが好ましい。広葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、１０質量％以上であることが好ましく、２０質量％以上であることがより好ましく、３０質量％以上であることがさらに好ましい。また、広葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、７０質量％以下であることが好ましい。広葉樹パルプの含有量を上記範囲内とすることにより、トイレットペーパーの坪量やＨＦ値等を所望の範囲内とすることが容易になる。 As the fiber raw material, it is preferable to use softwood pulp and hardwood pulp in combination. That is, it is preferable that the toilet paper further contains hardwood pulp in addition to softwood pulp. The content of hardwood pulp is preferably 10% by mass or more, more preferably 20% by mass or more, and more preferably 30% by mass or more with respect to the total mass of the pulp components contained in the toilet paper. More preferable. The content of hardwood pulp is preferably 70% by mass or less based on the total mass of pulp components contained in the toilet paper. By setting the content of the hardwood pulp within the above range, it becomes easy to set the basis weight and the HF value of the toilet paper within the desired range.

トイレットペーパー中に含有される繊維成分（パルプ成分）のカナディアン・フリーネス・スタンダード（Ｃ．Ｆ．Ｓ）で表されるフリーネスは４００ｍｌ以上であることが好ましく、４５０ｍｌ以上であることがより好ましく、５００ｍｌ以上であることがさらに好ましい。また、フリーネスは７００ｍｌ以下であることが好ましい。繊維成分のフリーネスを上記範囲内とすることにより、トイレットペーパーの坪量やＨＦ値等を所望の範囲内とすることが容易になり、手触り感に優れたトイレットペーパーが得られる。なお、繊維成分のフリーネスは後述するように、叩解条件を制御することにより調整することができる。 The freeness represented by the Canadian Freeness Standard (CFS) of the fiber component (pulp component) contained in the toilet paper is preferably 400 ml or more, more preferably 450 ml or more, and 500 ml. It is more preferable that the above is satisfied. The freeness is preferably 700 ml or less. By setting the freeness of the fiber component within the above range, it becomes easy to set the basis weight, the HF value, etc. of the toilet paper within a desired range, and the toilet paper excellent in touch feeling can be obtained. The freeness of the fiber component can be adjusted by controlling the beating condition, as described later.

（任意成分）
トイレットペーパーには、繊維原料の他に任意成分が含まれていてもよい。任意成分としては、例えば、乾燥紙力剤、湿潤紙力剤、柔軟剤等を挙げることができる。乾燥紙力剤としては、例えば、カチオン化澱粉、ポリアクリルアミド（ＰＡＭ）、カルボキシメチルセルロース（ＣＭＣ）等を挙げることができる。湿潤紙力剤としては、ポリアミドエピクロロヒドリン、尿素、メラミン、熱架橋性ポリアクリルアミド等を挙げることができる。柔軟剤としては、例えば、アニオン系界面活性剤、ノニオン系界面活性剤、カチオン系界面活性剤等を挙げることができる。上記の任意成分は１種単独で用いてもよく、２種以上を併用してもよい。 (Arbitrary ingredient)
The toilet paper may contain optional components in addition to the fiber raw material. Examples of the optional component include a dry strength agent, a wet strength agent, and a softening agent. Examples of the dry paper strength agent include cationized starch, polyacrylamide (PAM), carboxymethyl cellulose (CMC) and the like. Examples of the wet paper strength agent include polyamide epichlorohydrin, urea, melamine, and heat-crosslinkable polyacrylamide. Examples of the softening agent include anionic surfactants, nonionic surfactants, and cationic surfactants. The above optional components may be used alone or in combination of two or more.

トイレットペーパーに乾燥紙力剤が含まれている場合は、乾燥紙力剤の含有量は、トイレットペーパーに含まれる繊維成分の１００質量部に対して、０．０１質量部以上０．５０質量部以下であることが好ましい。
トイレットペーパーに湿潤紙力剤が含まれている場合は、湿潤紙力剤の含有量は、トイレットペーパーに含まれる繊維成分の１００質量部に対して、０．００１質量部以上０．１０質量部以下であることが好ましい。
また、トイレットペーパーに柔軟剤が含まれている場合は、柔軟剤の含有量は、トイレットペーパーに含まれる繊維成分の１００質量部に対して、０．０１質量部以上０．５０質量部以下であることが好ましい。
本発明においては、上記のような任意成分の添加量を適宜調整することによって、坪量を下げた場合であっても、トイレットペーパーの強度を維持している。 When the toilet paper contains a dry strength agent, the content of the dry strength agent is 0.01 parts by mass or more and 0.50 parts by mass with respect to 100 parts by mass of the fiber component contained in the toilet paper. The following is preferable.
When the toilet paper contains a wet strength agent, the content of the wet strength agent is 0.001 part by mass or more and 0.10 part by mass or more with respect to 100 parts by mass of the fiber component contained in the toilet paper. The following is preferable.
When the toilet paper contains a softening agent, the content of the softening agent is 0.01 parts by mass or more and 0.50 parts by mass or less with respect to 100 parts by mass of the fiber component contained in the toilet paper. It is preferable to have.
In the present invention, the strength of the toilet paper is maintained even if the basis weight is lowered by appropriately adjusting the amount of addition of the optional components as described above.

（トイレットロールの製造方法）
本発明のトイレットロールの製造方法は、１プライのトイレットペーパーウェブを得る工程と、トイレットペーパーにエンボス加工を施す工程と、エンボス加工を施したトイレットペーパーをロール状に巻き取る工程と、を含む。
なお、トイレットロールの製造方法の全工程中において、上記のエンボス加工を施す工程は１回のみ設けられる。 (Method for manufacturing toilet roll)
The method for manufacturing a toilet roll of the present invention includes a step of obtaining a one-ply toilet paper web, a step of embossing the toilet paper, and a step of winding the embossed toilet paper into a roll.
In addition, in all the steps of the manufacturing method of the toilet roll, the step of performing the embossing is provided only once.

１プライのトイレットペーパーウェブを得る工程は、繊維原料を含むスラリーを得る工程を含む。スラリーを得る工程においては、繊維原料を叩解する工程を含むことが好ましい。叩解工程においては、例えば、ダブルディスクリファイナー等を用いて叩解処理を施すことができる。この時、針葉樹パルプと広葉樹パルプをそれぞれ単独で叩解してもよいし、混合させた後に叩解してもよい。 The step of obtaining a one-ply toilet paper web includes the step of obtaining a slurry containing a fiber raw material. The step of obtaining a slurry preferably includes a step of beating the fiber raw material. In the beating step, for example, a beating process can be performed using a double disc refiner or the like. At this time, the softwood pulp and the hardwood pulp may be beaten individually, or may be beaten after being mixed.

１プライのトイレットペーパーウェブを得る工程は、繊維原料を含むスラリーを抄紙する工程を含む。抄紙する工程で用いられる抄紙機としては、例えば、サクションブレストフォーマー（円網タイプ、長網タイプ）、ツインワイヤーフォーマー、円網フォーマー（Ｃラップ、Ｓラップ）、クレセントフォーマー等の抄紙機を挙げることができる。 The step of obtaining a one-ply toilet paper web includes a step of papermaking a slurry containing a fiber raw material. As a paper machine used in the step of making paper, for example, a suction breast former (cylinder type, fourdrinier type), twin wire former, cylinder former (C wrap, S lap), crescent former, etc. Can be mentioned.

抄紙する工程では、網状のワイヤー上に繊維原料を含むスラリーが供給されてパルプの薄層が形成される。その後、プレスパートに向かって移送されながら、パルプの薄層の水分が網の下へ抜かれることでパルプの薄層は脱水される。このような工程を脱水工程と呼ぶこともある。一般に、ワイヤーは、金属またはプラスチック製の網を環にしたものである。 In the papermaking process, a slurry containing a fiber raw material is supplied onto a mesh wire to form a thin layer of pulp. Then, while being transported to the press part, the moisture of the thin layer of pulp is drained to the bottom of the net, whereby the thin layer of pulp is dehydrated. Such a process may be called a dehydration process. In general, the wire is a ring made of metal or plastic mesh.

抄紙する工程では、例えば、針葉樹パルプと広葉樹パルプを混合したパルプスラリーを抄紙して均一な１つの層として湿紙を形成する方法、もしくは、針葉樹パルプ層と広葉樹パルプ層を抄き合わせて１枚の湿紙を形成する方法があるが、いずれの手法を採用してもよい。 In the papermaking step, for example, a method of forming a wet paper web as a uniform layer by making a pulp slurry obtained by mixing softwood pulp and hardwood pulp, or a softwood pulp layer and a hardwood pulp layer are combined to form one sheet. Although there is a method of forming the wet paper web, any method may be adopted.

脱水工程の後、湿紙はワイヤーからフェルトへと移動する。フェルトを介してプレスロールで圧力を加えることにより、湿紙はさらに機械的に搾水される。これを、プレス工程あるいは搾水工程と呼ぶこともある。 After the dewatering process, the wet paper web moves from the wire to the felt. The wet paper web is further mechanically squeezed by applying pressure with a press roll through the felt. This may be called a pressing process or a water squeezing process.

抄紙する工程は、搾水工程の後に、さらに乾燥工程を含むことが好ましい。乾燥工程は、例えば、湿紙に向かって熱風を吹き付ける工程、もしくは、ドライヤシリンダーを外周面に圧着させる工程であることが好ましい。 It is preferable that the papermaking step further includes a drying step after the water squeezing step. The drying step is preferably, for example, a step of blowing hot air toward the wet paper, or a step of pressing the dryer cylinder onto the outer peripheral surface.

エンボス加工を施す工程では、１プライのトイレットペーパーウェブにエンボス加工が施される。エンボス加工は、エンボスパターンを構成する凸構造が設置されたエンボスロールとラバーロールとの間に１プライのトイレットペーパーウェブを通し、エンボスパターンを型押しすることによって行われる。エンボスロールのエンボス高さや、押し込み量、押し込み圧を変更することによって、所望のエンボス高さを有するエンボスを形成することができる。
ここで、エンボス加工に用いるエンボスロールには凸構造高さ０．７５ｍｍ以上０．８５ｍｍ以下の凸構造が設置されていることが好ましい。また、エンボスロールには凸構造密度（エンボス密度）が１０個／ｃｍ²以上３０個／ｃｍ²以下の略均一な凸構造が設置されていることが好ましい。そして、エンボス加工では、上記のエンボスロールを８ｋｇｆ／ｃｍ以上２０ｋｇｆ／ｃｍ以下の圧力で型押しすることが好ましい。 In the embossing step, the 1-ply toilet paper web is embossed. The embossing is performed by passing a one-ply toilet paper web between the rubber roll and the embossing roll having the convex structure forming the embossing pattern, and embossing the embossing pattern. By changing the embossing height of the embossing roll, the pushing amount, and the pushing pressure, an embossing having a desired embossing height can be formed.
Here, the embossing roll used for embossing is preferably provided with a convex structure having a convex structure height of 0.75 mm or more and 0.85 mm or less. Further, it is preferable that the embossing roll is provided with a substantially uniform convex structure having a convex structure density (embossing density) of 10 pieces/cm ² or more and 30 pieces/cm ² or less. In the embossing, it is preferable that the embossing roll is embossed with a pressure of 8 kgf/cm or more and 20 kgf/cm or less.

上記エンボス工程の後には、さらに巻き取り工程が設けられる。この巻き取り工程においては、所定の製品長を満たすように、所定の長さ分の巻き取りを行う。そして、得られた巻取ロールを所定の幅に断裁する。
巻き取り工程では、例えばマンドレルシャフトを有するワインダーを用いて、以下のように行うことができる。（１）まず巻芯となる紙管をマンドレルシャフトに挿入し、固定する。（２）紙管に接着剤を付着させ、紙管にトイレットペーパーの始端部を接着固定する。（３）マンドレルシャフトを回転させることにより、トイレットペーパーを製品長さ分だけ紙管に巻き取る。 A winding step is further provided after the embossing step. In this winding step, winding of a predetermined length is performed so as to satisfy a predetermined product length. Then, the obtained winding roll is cut into a predetermined width.
The winding step can be performed as follows using, for example, a winder having a mandrel shaft. (1) First, insert the paper tube to be the core into the mandrel shaft and fix it. (2) An adhesive is attached to the paper tube, and the starting end portion of the toilet paper is adhesively fixed to the paper tube. (3) By rotating the mandrel shaft, the toilet paper is wound around the paper tube by the length of the product.

また、巻き取り工程では、巻き取る際に外側から複数の駆動ロール（例えば、アッパーロール、ロウアーロール、ライダーロール等）でロールを支持しながら巻き取ることもでき、本発明においては、このような方法（サーフェイス方式）を用いることも好ましい。サーフェイス方式で巻き取りを行うことにより、駆動ロールの押し付け圧を調整することができ、トイレットロールの巻径をコントロールしやすくなる。また、生産速度を高めることもできる。 Further, in the winding step, it is also possible to wind while supporting the roll from the outside with a plurality of drive rolls (for example, an upper roll, a lower roll, a rider roll, etc.) at the time of winding. It is also preferable to use a method (surface method). By winding with the surface method, the pressing pressure of the drive roll can be adjusted, and the roll diameter of the toilet roll can be easily controlled. Also, the production speed can be increased.

以下に実施例と比較例を挙げて本発明の特徴をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す具体例により限定的に解釈されるべきものではない。 The features of the present invention will be described more specifically below with reference to Examples and Comparative Examples. The materials, usage amounts, ratios, processing contents, processing procedures, and the like shown in the following examples can be appropriately changed without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be limitedly interpreted by the following specific examples.

（実施例１）
針葉樹クラフトパルプ（ＮＫＰ）２３質量部、広葉樹クラフトパルプ（ＬＫＰ）７７質量部となるように混合したパルプスラリーを、ダブルディスクリファイナーを用いて叩解電力２００Ｋｗで叩解した。上記パルプスラリーに柔軟剤（星光ＰＭＣ株式会社製）０．０２質量部、湿潤紙力剤（星光ＰＭＣ株式会社製）０．０５質量部を添加して、抄紙用パルプスラリーを調製した。
調製した抄紙用パルプスラリーを、ツインワイヤーヤンキーマシンにより抄紙し、トイレットペーパーウェブ巻取を得た。なお、トイレットペーパーの坪量（１プライ）が表１に記載の通りとなるように抄紙条件を調整した。
得られた原紙巻取を加工機にかけ、巻き解いた後、エンボス加工を施した。その後、コア芯径３９ｍｍのコア芯に、サーフェイス方式で上記トイレットペーパーを巻き取った。サーフェイス方式の巻き取り工程では、表１の巻径になるようにライダーロールの押し付け圧を調整し、表１の長さになるように再度巻き取った。得られた巻取を所定の幅に断裁することで１プライのトイレットロールを得た。 (Example 1)
A pulp slurry mixed so as to be 23 parts by mass of softwood kraft pulp (NKP) and 77 parts by mass of hardwood kraft pulp (LKP) was beaten with a double disc refiner at a beating power of 200 Kw. A softening agent (manufactured by Seikou PMC Co., Ltd.) 0.02 parts by mass and a wet paper strength agent (manufactured by Seikou PMC Co., Ltd.) 0.05 parts by mass were added to the pulp slurry to prepare a papermaking pulp slurry.
The prepared pulp slurry for papermaking was paper-made by a twin wire Yankee machine to obtain a toilet paper web winding. The papermaking conditions were adjusted so that the basis weight (1 ply) of the toilet paper was as shown in Table 1.
The obtained base paper winding was applied to a processing machine, unwound, and then embossed. Then, the above-mentioned toilet paper was wound around the core having a core diameter of 39 mm by the surface method. In the surface-type winding step, the pressing pressure of the rider roll was adjusted so that the winding diameter was as shown in Table 1, and the winding was performed again so that the length was as shown in Table 1. The obtained roll was cut into a predetermined width to obtain a 1-ply toilet roll.

（実施例２）
坪量が表１に記載の通りとなるように、針葉樹クラフトパルプ（ＮＫＰ）１５質量部、広葉樹クラフトパルプ（ＬＫＰ）８５質量部となるように混合したパルプスラリーを叩解電力１５０Ｋｗで叩解した以外は、実施例１と同様にして１プライのトイレットロールを得た。 (Example 2)
Except for beating at a kneading power of 150 Kw, a pulp slurry mixed so that the basis weight is as shown in Table 1 was 15 parts by mass of softwood kraft pulp (NKP) and 85 parts by mass of hardwood kraft pulp (LKP). A 1-ply toilet roll was obtained in the same manner as in Example 1.

（実施例３）
坪量が表１に記載の通りとなるように、針葉樹クラフトパルプ（ＮＫＰ）２０質量部、広葉樹クラフトパルプ（ＬＫＰ）７５質量部となるように混合したパルプスラリーを叩解電力１５０Ｋｗで叩解した以外は実施例１と同様にして１プライのトイレットロールを得た。 (Example 3)
Except for beating with a beating power of 150 Kw, a pulp slurry mixed so that the basis weight is as shown in Table 1 was 20 parts by mass of softwood kraft pulp (NKP) and 75 parts by mass of hardwood kraft pulp (LKP). A 1-ply toilet roll was obtained in the same manner as in Example 1.

（比較例１）
坪量が表１に記載の通りとなるように、針葉樹クラフトパルプ（ＮＫＰ）２３質量部、広葉樹クラフトパルプ（ＬＫＰ）７７質量部となるように混合したパルプスラリーを叩解電力２５０Ｋｗで叩解し、柔軟剤の添加量を０．０５質量部に変更した以外は実施例１と同様にして１プライのトイレットロールを得た。
（比較例２及び３）
比較例２及び３は、市販されている既知の製品である。 (Comparative Example 1)
The pulp slurry mixed so that the basis weight is as shown in Table 1 was 23 parts by mass of softwood kraft pulp (NKP) and 77 parts by mass of hardwood kraft pulp (LKP) was beaten at a beating power of 250 Kw to give a softness. A one-ply toilet roll was obtained in the same manner as in Example 1 except that the amount of the agent added was changed to 0.05 part by mass.
(Comparative Examples 2 and 3)
Comparative Examples 2 and 3 are known products that are commercially available.

（評価）
（坪量）
実施例及び比較例で得たトイレットペーパーの坪量はＪＩＳＰ８１２４に準拠して測定した。 (Evaluation)
(Basis weight)
The basis weight of the toilet paper obtained in the examples and comparative examples was measured according to JIS P8124.

（引張強度）
実施例及び比較例で得たトイレットペーパーの引張強度は、サンプル幅１５ｍｍ、引張速度５０ｍｍ／分、スパン長１００ｍｍの条件で、横型引張試験機（熊谷理器社製）を用いて測定した。なお、引張強度は、１プライのトイレットペーパーの縦方向と横方向の両方向の強度を測定した。各々の方向について６サンプルの平均値を算出してそれぞれの引張強度とした。また、引張強度の測定は、ＩＳＯ１８７に準拠した環境（温度２３±１℃、相対湿度５０±２％）で行った。 (Tensile strength)
The tensile strength of the toilet paper obtained in Examples and Comparative Examples was measured using a horizontal tensile tester (manufactured by Kumagai Riki Co., Ltd.) under the conditions of a sample width of 15 mm, a tensile speed of 50 mm/min, and a span length of 100 mm. The tensile strength was measured in both the longitudinal and lateral directions of 1-ply toilet paper. The average value of 6 samples was calculated for each direction to obtain the respective tensile strengths. The tensile strength was measured in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%).

（ＨＦ値の測定）
実施例及び比較例で得られたトイレットペーパーのＨＦ値は、ティシューソフトネスアナライザー（ＥｍｔｅｃＥｌｅｃｔｒｏｎｉｃＧｍｂＨ社製）を用いて測定した。サンプル台に、直径１１２．８ｍｍの円形にカットしたサンプルを設置し、このサンプルに対し、ブレード付きローターを１００ｍＮの押し込み圧力をかけて上方から押し込んだ。その後、ブレード付きローターを回転数が２．０回転／秒となるように回転させ、その時の振動周波数を測定した。また、直径１１２．８ｍｍの円形にカットした別のサンプルに対し、ブレード付きローターを１００ｍＮと、６０ｍＮの圧力で押し込んだ際の上下方向の変形変位量を算出した。ＨＦ値は、振動周波数と変形変位量から、算出される値であり、計算のアルゴリズムはＴＰＩＩを用いた。なお、上記の測定は、各サンプルの表面（外面）と裏面（内面）についてそれぞれ１０回ずつ行い、得られた測定データからＨａｍｐｅｌｉｄｅｎｔｉｆｉｅｒの方法で異常値を除外し、表面及び裏面について各々平均値を算出した。さらにこのようにして算出した２つの面のＨＦ値の平均値を算出し、それをＨＦ値として評価に用いた。
なお、上記サンプルの測定はＩＳＯ１８７に準拠した環境（温度２３±１℃、相対湿度５０±２％）で行った。また、測定の際には、付属の説明書に従い標準サンプル（ｅｍｅｔｅｃｒｅｆ．２Ｘ（ｎｎ．ｎ））で校正し、アルゴリズムをＴＰＩＩに設定した。計算ソフトウェアにはｅｍｅｔｅｃｍｅａｓｕｒｅｍｅｎｔｓｙｓｔｅｍｖｅｒ．３．２２を使用した。 (Measurement of HF value)
The HF value of the toilet paper obtained in the examples and comparative examples was measured using a tissue softness analyzer (manufactured by Emtec Electronic GmbH). A circular sample having a diameter of 112.8 mm was placed on the sample table, and a rotor with a blade was pressed into the sample from above by applying a pressing pressure of 100 mN. Then, the rotor with a blade was rotated so that the rotation speed was 2.0 rotations/second, and the vibration frequency at that time was measured. Further, the deformation displacement amount in the vertical direction when the rotor with a blade was pressed at a pressure of 100 mN and a pressure of 60 mN to another sample cut into a circle having a diameter of 112.8 mm was calculated. The HF value is a value calculated from the vibration frequency and the amount of deformation displacement, and the calculation algorithm used was TP II. In addition, the above-mentioned measurement is performed 10 times for each of the front surface (outer surface) and the back surface (inner surface) of each sample, the abnormal value is excluded from the obtained measurement data by the method of Hampel identifier, and the average value for each of the front surface and the back surface Was calculated. Further, the average value of the HF values of the two surfaces thus calculated was calculated and used as the HF value for evaluation.
In addition, the measurement of the sample was performed in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%). In addition, at the time of measurement, a standard sample (emetec ref.2X (nn.n)) was calibrated according to the attached instruction, and the algorithm was set to TP II. For the calculation software, emetec measurement system ver. 3.22 was used.

（圧縮性）
実施例及び比較例で得たトイレットペーパーの圧縮性について、ＫＥＳＦＢ３−ＡＵＴＯ−Ａ自動化圧縮試験機（カトーテック株式会社製）を用いて測定した。２ｃｍ²の加圧板と受圧板間に１０ｃｍ×１０ｃｍにカットしたサンプルを設置し、５０秒／ｍｍの速さで加圧板を下降させ、その際に時々刻々と変化する圧力とその時のサンプルの厚みを測定することで、下記の項目を算出した。
Ｔ₀：圧力０．５ｇｆ／ｃｍ²下におけるサンプルの厚み
Ｔ_m：圧力５０ｇｆ／ｃｍ²下におけるサンプルの厚み
上記の項目の値は、各サンプルについて１０回の測定を行い、得られた測定データからＨａｍｐｅｌｉｄｅｎｔｉｆｉｅｒの方法で異常値を除外し、平均値として算出した値である。なお、上記サンプルの測定はＩＳＯ１８７に準拠した環境（温度２３±１℃、相対湿度５０±２％）で行った。 (Compressibility)
The compressibility of the toilet paper obtained in Examples and Comparative Examples was measured using a KES FB3-AUTO-A automated compression tester (manufactured by Kato Tech Co., Ltd.). A sample cut into 10 cm×10 cm was placed between a pressure plate of 2 cm ^{2 and} a pressure plate, and the pressure plate was moved down at a speed of 50 seconds/mm. At that time, the pressure changed momentarily and the thickness of the sample at that time. The following items were calculated by measuring.
T ₀ : Thickness of sample under pressure of 0.5 gf/cm ² T _m : Thickness of sample under pressure of 50 gf/cm ² The values of the above-mentioned items are obtained by measuring 10 times for each sample. Is a value calculated as an average value by excluding abnormal values by the method of Hampel identifier. In addition, the measurement of the sample was performed in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%).

（加工適性）
エンボス加工工程の後には、巻き取り工程が設けられる。巻き取り工程においては、所定長さ分の巻き取りを行い、その後、得られた巻取を所定の幅に断裁する。この断裁後の断面の状態を５０ロール分観察し、トイレットロールのコア芯（紙管）の状態について３段階で評価を行った。表１に示した記号は下記の意味を示す。
＜コア芯潰れ＞
○：コア芯の潰れが発生せず正常
△：コア芯の潰れが１個以上１０個未満において発生
×：コア芯の潰れが１０個以上で発生 (Processability)
A winding process is provided after the embossing process. In the winding step, winding is performed for a predetermined length, and then the obtained winding is cut into a predetermined width. The state of the cross section after the cutting was observed for 50 rolls, and the state of the core core (paper tube) of the toilet roll was evaluated in three stages. The symbols shown in Table 1 have the following meanings.
<Core crush>
◯: Normal without crushing of core core Δ: Occurrence of crushing of core core of 1 to less than 10 ×: Occurrence of crushing of core core of 10 or more

（官能評価）
実施例及び比較例で得たトイレットペーパーについて、水準を隠した状態で官能評価を実施した。５０人に製品を触ってもらい、製品の肌触りについて３段階で評価を行った。表１に示した記号は下記の意味を示す。
＜肌触り＞
○：優れている
△：やや劣る
×：劣る (sensory evaluation)
With respect to the toilet paper obtained in each of the examples and the comparative examples, a sensory evaluation was performed with the level hidden. Fifty people touched the product and evaluated the touch of the product in three levels. The symbols shown in Table 1 have the following meanings.
<Feeling>
◯: Excellent Δ: Somewhat inferior ×: Inferior

表１からわかるように実施例で得られたトイレットペーパーは、肌触りが良く、かつ加工適性にも優れていた。一方、比較例１では、トイレットロールの製造工程においてコア芯が潰れるという不具合が発生した。また、比較例２及び３で得られたトイレットペーパーは、肌触りに劣っていた。 As can be seen from Table 1, the toilet paper obtained in the examples had a good feel to the touch and excellent processability. On the other hand, in Comparative Example 1, the defect that the core core was crushed occurred in the manufacturing process of the toilet roll. The toilet paper obtained in Comparative Examples 2 and 3 was inferior in touch.

２０トイレットペーパー
１００トイレットロール
ａ表面
ｂ裏面
Ｐトイレットロールロールの断面積
Ｒトイレットロールロールの巻径
Ｓ紙管径 20 Toilet paper 100 Toilet roll a Front surface b Back surface P Toilet roll Roll cross-sectional area R Toilet roll roll winding diameter S Paper tube diameter

Claims

A toilet roll made by rolling 1-ply toilet paper into a roll shape,
The roll length of the toilet roll is 95 m or more and 150 m or less,
The toilet paper has a basis weight of 10 g/m ² or more and 16 g/m ² or less,
A toilet roll in which the toilet paper is embossed.

The toilet roll according to claim 1, wherein an average of handfeel values on the front surface and the back surface of the toilet paper is 65.0 or more.

The toilet paper has an embossed pattern formed by the embossing,
The embossing density in the embossing pattern is 10 pieces/cm ² or more and 30 pieces/cm ² or less,
The toilet roll according to claim 1 or 2, wherein one emboss diameter is 0.5 mm or more and 2.0 mm or less in the emboss pattern .

The toilet roll according to claim 3, wherein the emboss pattern has an emboss depth of 0.85 mm or less.

The toilet roll according to any one of claims 1 to 4, which has a thickness of 75 µm or more and 110 µm or less when a pressure of 50 gf/cm ² is applied to the toilet paper.

The toilet rolls of toilet paper according to any one of claims 1 to 5 the thickness at the time of applying a pressure of 0.5 gf / cm ² is 300μm or less than 180 [mu] m.

Embossing 1-ply toilet paper,
A method for manufacturing a toilet roll, which comprises a step of winding embossed toilet paper into a roll shape,
The step of performing the embossing is a step of forming embossing on a 1-ply toilet paper with an embossing roll,
In the embossing step, the embossing roll is embossed with a pressure of 8 kgf/cm or more and 20 kgf/cm or less,
The roll length of the toilet roll is 95 m or more and 150 m or less,
The basis weight per 1 ply of the toilet paper is 10 g/m ²² 16 g/m or more ²² The following is a method for manufacturing a toilet roll.

The method for manufacturing a toilet roll according to claim 7, wherein the embossing roll has a convex structure, and the height of the convex structure is 0.85 mm or less.