JP6720624B2

JP6720624B2 - Non-combustible sheet

Info

Publication number: JP6720624B2
Application number: JP2016060264A
Authority: JP
Inventors: 小笠原　幹之; 幹之小笠原; 孝史冨永; 祐一南部; 弘樹渡邊
Original assignee: Toppan Inc
Current assignee: Toppan Inc
Priority date: 2016-03-24
Filing date: 2016-03-24
Publication date: 2020-07-08
Anticipated expiration: 2036-03-24
Also published as: JP2017170786A

Description

本発明は、不燃シートに関する。 The present invention relates to a noncombustible sheet.

近年、建築物の膜天井等に用いられるシート状部材には、火災時の安全性確保のため不燃性の要請が高まっている（特許文献１等参照）。例えば、一定の規模・用途に供する、居室や廊下・階段等の避難経路等の膜天井等には、その要求性能に応じた防火材料を用いなければならないことが、法律（建築基準法施行令第１２９条）で義務付けられている。 In recent years, sheet-like members used for membrane ceilings of buildings have been increasingly required to have nonflammability in order to ensure safety during a fire (see Patent Document 1, etc.). For example, it is necessary to use fireproof materials according to the required performance for membrane ceilings, such as living rooms, evacuation routes such as corridors, stairs, etc., that are used for a certain scale and purpose. Mandatory under Article 129).

特開２０１４−０４００３４号公報JP, 2014-040034, A

本発明は、上述したような点に着目してなされたもので、不燃性を有する不燃シートを提供することを目的としている。 The present invention has been made by paying attention to the above points, and an object thereof is to provide an incombustible sheet having incombustibility.

上記課題を解決するために、本発明の一態様は、ガラスクロスの一方の面に、エチレン−酢酸ビニル共重合樹脂を含有する第１接着剤層を介して化粧シートが貼り付けられており、化粧シートは、ポリプロピレン系樹脂とポリエチレン系樹脂との混合樹脂を含有する樹脂フィルムと、樹脂フィルムのガラスクロスと反対側の面に形成された印刷インキ層と、印刷インキ層の樹脂フィルムと反対側の面に第２接着剤層と、第２接着剤層の印刷インキ層と反対側の面に形成された表面保護層と、樹脂フィルムのガラスクロス側の面に形成された裏面プライマー層とを有し、樹脂フィルムの厚さは、０．０５４［mm］以上０．０６６［mm］以下であり、印刷インキ層の有機質量は、６．９［g/m ² ］以下であり、第２接着剤層の有機質量は、７．５［g/m ² ］以下であり、表面保護層の有機質量は、５９．５［g/m ² ］以下であり、裏面プライマー層の有機質量は、１．０５［g/m ² ］以下であり、第１接着剤層の質量は、３５．２［g/m²］以下であり、樹脂フィルム、印刷インキ層、第２接着剤層、表面保護層、裏面プライマー層及び第１接着剤層の有機質量の合計値は、１５０．５５［g/m ² ］以下であり、印刷インキ層は、塩化ビニル酢酸ビニル共重合樹脂を３０．０質量％以上含み、表面保護層は、フッ素樹脂を１９．０質量％以上、ベンゾトアゾール系の有機添加剤及びヒンダードアミン系の有機添加剤を４．０質量％以上含み、樹脂フィルムは、無機顔料を５．５５質量％以上含み、裏面プライマー層は、無機顔料を４０．０質量％以上含み、第１接着剤層は、無機顔料を１９．２質量％以上含むことを特徴とする。 In order to solve the above problems, in one embodiment of the present invention, a decorative sheet is attached to one surface of a glass cloth through a first adhesive layer containing an ethylene-vinyl acetate copolymer resin, The decorative sheet is a resin film containing a mixed resin of polypropylene resin and polyethylene resin, a printing ink layer formed on the surface of the resin film opposite to the glass cloth, and a printing ink layer opposite to the resin film. On the surface of the second adhesive layer, a surface protective layer formed on the surface of the second adhesive layer opposite to the printing ink layer, and a back surface primer layer formed on the surface of the resin film on the glass cloth side. The thickness of the resin film is 0.054 [mm] or more and 0.066 [mm] or less, the organic mass of the printing ink layer is 6.9 [g/m ² ] or less, and the second The organic mass of the adhesive layer is 7.5 [g/m ² ] or less, the organic mass of the surface protective layer is 59.5 [g/m ² ] or less, and the organic mass of the back surface primer layer is 1.05 [g / m ^2] or less, the mass of the first adhesive layer, 35.2 [g / m ^2] Ri der less, a resin film, a printing ink layer, a second adhesive layer, the surface The total organic mass of the protective layer, backside primer layer and first adhesive layer was 150.55 [g/m ² ] or less, and the printing ink layer contained 30.0 mass % of vinyl chloride-vinyl acetate copolymer resin. % Or more, the surface protective layer contains a fluororesin of 19.0 mass% or more, a benzotoazole-based organic additive and a hindered amine-based organic additive of 4.0 mass% or more, and the resin film contains an inorganic pigment. The back surface primer layer contains 40.0 mass% or more of the inorganic pigment, and the first adhesive layer contains 19.2 mass% or more of the inorganic pigment .

本発明の不燃シートが有する不燃性は、ＩＳＯ５６６０−１に準拠したコーンカロリ燃焼試験に準拠し、不燃シートの時間に対する総発熱量及び時間に対する発熱速度を求めた際に、（i）加熱開始後２０分間の総発熱量が８［MJ/m²］以下であり、（ii）加熱開始後２０分間、最大発熱速度が１０秒以上継続して２００［kW/m²］を超えず、かつ（iii）加熱開始後２０分間、防火上有害な裏面まで貫通する亀裂及び穴がないことを満たす不燃性である。 The non-combustibility of the non-combustible sheet of the present invention is based on a corn calorie combustion test in accordance with ISO5660-1, and when the total calorific value with respect to time of the non-combustible sheet and the heat generation rate with respect to time are obtained, (i) after starting heating The total heat generation amount per minute is 8 [MJ/m ² ] or less, (ii) the maximum heat generation rate does not exceed 200 [kW/m ² ] for 10 minutes or more for 20 minutes after the start of heating, and (iii ) It is nonflammable for 20 minutes after the start of heating, satisfying no cracks and holes penetrating to the back surface which is harmful for fire protection.

本発明の一態様では、ガラスクロスを基材とすると共に、樹脂フィルムの厚さと第１接着剤層の質量とを小さくしたため、有機質料を低減することができる。それゆえ、燃焼量を低減でき、不燃性を有する不燃シートを提供することができる。 In one embodiment of the present invention, the glass cloth is used as the base material, and the thickness of the resin film and the mass of the first adhesive layer are reduced, so that the organic material can be reduced. Therefore, the amount of combustion can be reduced, and a nonflammable sheet having nonflammability can be provided.

本発明の実施形態の不燃シートを示す断面図である。It is sectional drawing which shows the noncombustible sheet of embodiment of this invention.

以下に、本発明の実施形態について図面を参照して説明する。
ここで、図面は模式的なものであり、厚みと平面寸法との関係、各層の厚みの比率等は現実のものとは異なる。また、以下に示す実施形態は、本発明の技術的思想を具体化するための構成を例示するものであって、本発明の技術的思想は、構成部品の材質、形状、構造等が下記のものに特定するものでない。本発明の技術的思想は、特許請求の範囲に記載された請求項が規定する技術的範囲内において、種々の変更を加えることができる。 Embodiments of the present invention will be described below with reference to the drawings.
Here, the drawings are schematic, and the relationship between the thickness and the plane dimension, the ratio of the thickness of each layer, and the like are different from the actual ones. Further, the embodiments described below exemplify a configuration for embodying the technical idea of the present invention, and the technical idea of the present invention is that the material, shape, structure, etc. of components are as follows. It is not specific to a thing. Various changes can be added to the technical idea of the present invention within the technical scope defined by the claims described in the claims.

（構成）
図１に示すように、本実施形態の不燃シート１０は、ガラスクロス１の一方の面に、第１接着剤層５を介して化粧シート２が貼り付けられてシート状に形成されている。
不燃シート１０の化粧シート２側の面（後述する表面保護層２Ａ）の形状は、平滑または凹凸形状とする。凹凸形状の最大深さは、例えば、０．０４４［mm］程度とする。
また、不燃シート１０の厚さは、例えば、０．１７０［mm］以上０．５７５［mm］以下とする。また、質量は、１９１［g/m²］以上４１５．７［g/m²］以下とする。 (Constitution)
As shown in FIG. 1, the non-combustible sheet 10 of the present embodiment is formed in a sheet shape by pasting a decorative sheet 2 on one surface of a glass cloth 1 with a first adhesive layer 5 interposed therebetween.
The surface of the non-combustible sheet 10 on the side of the decorative sheet 2 (the surface protective layer 2A described later) has a smooth or uneven shape. The maximum depth of the uneven shape is, for example, about 0.044 [mm].
The thickness of the non-combustible sheet 10 is, for example, 0.170 [mm] or more and 0.575 [mm] or less. The mass is 191 [g/m ² ] or more and 415.7 [g/m ² ] or less.

（ガラスクロス１）
ガラスクロス１は、ガラス繊維を織って形成したクロスである。ガラス繊維としては、例えば、Ｅガラス、表面処理剤（接着性を向上させる集束剤、シラン化合物等）を含むものを使用できる。ガラスクロス１の組成（ガラス繊維の組成）は、例えば、Ｅガラスを９７質量以上９９質量％以下、表面処理剤を１質量％以上３質量％以下含むものとする。
また、織り方は、例えば、平織りとする。さらに、糸番手は、例えば、縦糸を６８．５［tex］、横糸を６８．５［tex］とし、織密度は、例えば、縦糸を４２［本/25mm］以上４６［本/25mm］以下、横糸を３１［本/25mm］以上３５［本/25mm］以下とする。
また、ガラスクロス１の厚さは、例えば、０．１７［mm］以上０．２１［mm］以下とする。さらに、ガラスクロス１の質量は、例えば、１９０．８［g/m²］以上２３３．２［g/m²］以下（有機質量２．０［g/m²］以上６．４［g/m²］以下）とする。 (Glass cloth 1)
The glass cloth 1 is a cloth formed by weaving glass fibers. As the glass fiber, for example, one containing E glass and a surface treatment agent (a sizing agent for improving adhesiveness, a silane compound, etc.) can be used. The composition of the glass cloth 1 (the composition of the glass fiber) is, for example, 97 mass% or more and 99 mass% or less of E glass and 1 mass% or more and 3 mass% or less of the surface treatment agent.
The weaving method is, for example, plain weave. Furthermore, the yarn count is, for example, 68.5 [tex] for the warp yarn and 68.5 [tex] for the weft yarn, and the weaving density is, for example, 42 [threads/25 mm] or more and 46 [threads/25 mm] or less for the warp threads. The weft thread is 31 [threads/25 mm] or more and 35 [threads/25 mm] or less.
The thickness of the glass cloth 1 is, for example, 0.17 [mm] or more and 0.21 [mm] or less. Further, the mass of the glass cloth 1 is, for example, 190.8 [g/m ² ] or more and 233.2 [g/m ² ] or less (organic mass 2.0 [g/m ² ] or more and 6.4 [g/m ² ]. m ² ] or less).

（化粧シート２）
化粧シート２は、樹脂フィルム２Ｄと、樹脂フィルム２Ｄのガラスクロス１と反対側の面に形成された印刷インキ層２Ｃと、印刷インキ層２Ｃの樹脂フィルム２Ｄと反対側の面に形成された第２接着剤層２Ｂと、第２接着剤層２Ｂの印刷インキ層２Ｃと反対側の面に形成された表面保護層２Ａとを有している。なお、第２接着剤層２Ｂは、印刷インキ層２Ｃが形成されていない場所、つまり、インキが塗布されていない場所においては、樹脂フィルム２Ｄ上に形成されることになる。また、化粧シート２は、樹脂フィルム２Ｄのガラスクロス１側の面に形成された裏面プライマー層２Ｅを有している。 (Decorative sheet 2)
The decorative sheet 2 includes a resin film 2D, a printing ink layer 2C formed on a surface of the resin film 2D opposite to the glass cloth 1, and a printing ink layer 2C formed on a surface of the printing ink layer 2C opposite to the resin film 2D. The second adhesive layer 2B and the surface protective layer 2A formed on the surface of the second adhesive layer 2B opposite to the printing ink layer 2C. The second adhesive layer 2B is formed on the resin film 2D in the place where the printing ink layer 2C is not formed, that is, in the place where the ink is not applied. The decorative sheet 2 also has a back surface primer layer 2E formed on the surface of the resin film 2D on the glass cloth 1 side.

（樹脂フィルム２Ｄ）
樹脂フィルム２Ｄは、ポリプロピレン系樹脂とポリエチレン系樹脂との混合樹脂を含有するポリプロピレン樹脂系フィルムである。また、樹脂フィルム２Ｄには、必要に応じて、無機顔料（炭酸カルシウム、酸化鉄、酸化チタン等）、有機添加剤を添加してもよい。樹脂フィルム２Ｄの組成は、例えば、混合樹脂を６７．５７質量％以上８８．６９質量％以下、無機顔料を５．５５質量％以上１８．６２質量％以下、有機添加剤を２．７５質量％以上１３．８１質量％以下含むものとする。
また、樹脂フィルム２Ｄの厚さは、例えば、０．０６６［mm］以下とし、厚さを薄くする。これにより、燃焼量を低下させる。なお、厚さの下限値は、例えば、樹脂フィルム２Ｄの強度等を考慮して、０．０５４［mm］以上とする。また、樹脂フィルム２Ｄの質量は、例えば、６４．０２［g/m²］以下（有機質量５５．０［g/m²］以下）とする。
また、樹脂フィルム２Ｄの有機質量割合は、９４．４５質量％以下とする。なお、有機質量が４９．７［g/m²］より大きく４９．８［g/m²］以下である場合には、有機質量割合は９２．７５質量％以下とする。また、有機質料が４９．８［g/m²］より大きく５５．０［g/m²］以下の場合には、有機質量割合は９１．４４質量％以下とする。 (Resin film 2D)
The resin film 2D is a polypropylene resin film containing a mixed resin of polypropylene resin and polyethylene resin. Moreover, you may add an inorganic pigment (calcium carbonate, iron oxide, titanium oxide, etc.) and an organic additive to the resin film 2D as needed. The composition of the resin film 2D is, for example, 67.57% by mass or more and 88.69% by mass or less of mixed resin, 5.55% by mass or more and 18.62% by mass or less of inorganic pigment, and 2.75% by mass of organic additive. The above content should be 13.81 mass% or less.
Moreover, the thickness of the resin film 2D is set to, for example, 0.066 [mm] or less to reduce the thickness. This reduces the amount of combustion. The lower limit of the thickness is, for example, 0.054 [mm] or more in consideration of the strength of the resin film 2D. The mass of the resin film 2D is, for example, 64.02 [g/m ² ] or less (organic mass 55.0 [g/m ² ] or less).
Further, the organic mass ratio of the resin film 2D is set to 94.45 mass% or less. When the organic mass is greater than 49.7 [g/m ² ] and 49.8 [g/m ² ] or less, the organic mass ratio is 92.75 mass% or less. When the organic material is more than 49.8 [g/m ² ] and 55.0 [g/m ² ] or less, the organic mass ratio is 91.44 mass% or less.

（印刷インキ層２Ｃ）
印刷インキ層２Ｃは、不燃シート１０の意匠性を向上するためにウレタン樹脂系インキによる印刷で形成された層である。ウレタン樹脂系インキとしては、例えば、ウレタン樹脂、塩化ビニル酢酸ビニル共重合樹脂、無機顔料を含むものを使用できる。印刷インキ層２Ｃの組成は、例えば、ウレタン樹脂を６０．２質量％以上７０．０質量％以下、塩化ビニル酢酸ビニル共重合樹脂を２５．８質量％以上３０．０質量％以下、無機顔料を０質量％以上１４．０質量％以下含むものとする。印刷方法としては、例えば、インクジェットヘッドからインク滴を吹き付けるインクジェット印刷法、グラビア印刷法を採用できる。
また、印刷インキ層２Ｃの質量は、例えば、７．５９［g/m²］以下（固形量）（有機質量７．５９［g/m²］）以下とする。 (Printing ink layer 2C)
The printing ink layer 2C is a layer formed by printing with a urethane resin-based ink in order to improve the design of the nonflammable sheet 10. As the urethane resin-based ink, for example, one containing a urethane resin, vinyl chloride vinyl acetate copolymer resin, and an inorganic pigment can be used. The composition of the printing ink layer 2C is, for example, 60.2 mass% or more and 70.0 mass% or less of urethane resin, 25.8 mass% or more and 30.0 mass% or less of vinyl chloride/vinyl acetate copolymer resin, and an inorganic pigment. It should be contained in an amount of 0 mass% or more and 14.0 mass% or less. As a printing method, for example, an inkjet printing method in which ink droplets are ejected from an inkjet head or a gravure printing method can be adopted.
The mass of the printing ink layer 2C is, for example, 7.59 [g/m ² ] or less (solid amount) (organic mass 7.59 [g/m ² ]) or less.

（第２接着剤層２Ｂ）
第２接着剤層２Ｂは、印刷インキ層２Ｃ（インキが塗布されていない場所においては、樹脂フィルム２Ｄ）と表面保護層２Ａとを接着するための接着剤層である。第２接着剤層２Ｂは、第１ウレタン樹脂系接着剤層２Ｂｂと、第１ウレタン樹脂系接着剤層２Ｂｂの表面保護層２Ａ側の面に形成された第２ウレタン樹脂系接着剤層２Ｂａとを有している。
第１ウレタン樹脂系接着剤層２Ｂｂ及び第２ウレタン樹脂系接着剤層２Ｂａのそれぞれは、ウレタン樹脂系接着剤で形成された層である。第１ウレタン樹脂系接着剤層２Ｂｂ及び第２ウレタン樹脂系接着剤層２Ｂａの組成は、例えば、ウレタン樹脂を１００質量％含むものとする。また、第１ウレタン樹脂系接着剤層２Ｂｂの質量は、５．５８［g/m²］以上６．８２［g/m²］以下（固形量）（有機質量６．８２［g/m²］以下）とする。さらに、第２ウレタン樹脂系接着剤層２Ｂａの質量は、１．１７［g/m²］以上１．４３［g/m²］以下（固形量）（有機質量１．４３［g/m²］以下）とする。 (Second adhesive layer 2B)
The second adhesive layer 2B is an adhesive layer for adhering the printing ink layer 2C (the resin film 2D when the ink is not applied) and the surface protective layer 2A. The second adhesive layer 2B includes a first urethane resin adhesive layer 2Bb and a second urethane resin adhesive layer 2Ba formed on the surface of the first urethane resin adhesive layer 2Bb on the surface protective layer 2A side. have.
Each of the first urethane resin adhesive layer 2Bb and the second urethane resin adhesive layer 2Ba is a layer formed of a urethane resin adhesive. The composition of the first urethane resin adhesive layer 2Bb and the second urethane resin adhesive layer 2Ba is assumed to include, for example, 100% by mass of urethane resin. The mass of the first urethane resin adhesive layer 2Bb is 5.58 [g/m ² ] or more and 6.82 [g/m ² ] or less (solid amount) (organic mass 6.82 [g/m ^{2 ).} ] The following) Further, the mass of the second urethane resin adhesive layer 2Ba is 1.17 [g/m ² ] or more and 1.43 [g/m ² ] or less (solid amount) (organic mass 1.43 [g/m ^{2 ].} ] The following)

（表面保護層２Ａ）
表面保護層２Ａは、不燃シート１０の表面を保護するためにアクリル樹脂系フィルムで形成された層である。アクリル樹脂系フィルムとしては、例えば、アクリル樹脂、フッ素樹脂、有機質添加剤（ベンゾトアゾール系、ヒンダードアミン系）を含むものを使用できる。表面保護層２Ａの組成は、例えば、アクリル樹脂を６９．３質量％以上８４．７質量％以下、フッ素樹脂を１７．１質量％以上２０．９質量％以下、有機質添加剤を３．６質量％以上４．４質量％以下含むものとする。フィルム（表面保護層２Ａ）の製造方法としては、例えば、耐候性を考慮すると、キャスト法等の硬度を向上可能なものが好ましい。
また、表面保護層２Ａの厚さは、例えば、０．０５５１１［mm］以下とし、質量は、６５．４５［g/m²］以下（固形量）（有機質量６５．４５［g/m²］以下）とする。
ここで、表面保護層２Ａの表面には、意匠性を付与するために凹凸模様が形成されていてもよい。凹凸模様としては、木目板導管溝、石板表面凹凸（花崗岩劈開面等）、布表面テクスチャア、梨地、砂目、ヘアライン等が例示される。 (Surface protection layer 2A)
The surface protection layer 2A is a layer formed of an acrylic resin film to protect the surface of the nonflammable sheet 10. As the acrylic resin film, for example, a film containing an acrylic resin, a fluororesin, and an organic additive (benzotoazole type, hindered amine type) can be used. The composition of the surface protective layer 2A is, for example, 69.3% by mass or more and 84.7% by mass or less of an acrylic resin, 17.1% by mass or more and 20.9% by mass or less of a fluororesin, and 3.6% by mass of an organic additive. % Or more and 4.4 mass% or less. As a method for producing the film (surface protective layer 2A), taking weatherability into consideration, for example, a method capable of improving hardness such as a casting method is preferable.
The thickness of the surface protective layer 2A is, for example, 0.05511 [mm] or less, and the mass is 65.45 [g/m ² ] or less (solid amount) (organic mass 65.45 [g/m ^2] ] The following)
Here, an uneven pattern may be formed on the surface of the surface protective layer 2A in order to impart a design property. Examples of the concavo-convex pattern include a wood grain board conduit groove, a stone board surface irregularity (granite cleavage surface, etc.), a cloth surface texturer, a satin finish, a grain, a hairline and the like.

（裏面プライマー層２Ｅ）
裏面プライマー層２Ｅは、接着性の向上のためにウレタン樹脂系プライマーで形成された層である。ウレタン樹脂系プライマーとしては、例えば、ウレタン樹脂、無機顔料（シリカ等）を含むものを使用できる。裏面プライマー層２Ｅの組成は、例えば、ウレタン樹脂を５６．０以上６４．０以下、無機顔料を３６．０以上４４．０以下含むものとする。
また、裏面プライマー層２Ｅの質量は、１．９２５［g/m²］以下（固形量）（有機質量１．１５５［g/m²］以下）とする。 (Backside primer layer 2E)
The back surface primer layer 2E is a layer formed of a urethane resin-based primer for improving the adhesiveness. As the urethane resin-based primer, for example, one containing a urethane resin and an inorganic pigment (silica or the like) can be used. The composition of the back surface primer layer 2E includes, for example, 56.0 or more and 64.0 or less urethane resin and 36.0 or more and 44.0 or less inorganic pigment.
The mass of the back surface primer layer 2E is set to 1.925 [g/m ² ] or less (solid amount) (organic mass 1.155 [g/m ² ] or less).

（第１接着剤層５）
第１接着剤層５は、ガラスクロス１と化粧シート２（裏面プライマー層２Ｅ）とを接着するためにエチレン−酢酸ビニル共重合樹脂系接着剤で形成される層である。エチレン−酢酸ビニル共重合樹脂系接着剤としては、例えば、エチレン−酢酸ビニル共重合樹脂、無機顔料（シリカ等）を含むものを使用できる。エチレン−酢酸ビニル共重合樹脂系接着剤の組成は、例えば、エチレン−酢酸ビニル共重合樹脂を８０．３質量％以上８１．３質量％以下、無機顔料を１９．２質量％以上１９．７質量％以下含むものとする。
また、エチレン−酢酸ビニル共重合樹脂系接着剤の質量は、３５．２［g/m²］以下（固形量）（有機質量２８．４９［g/m²］以下）とする。 (First adhesive layer 5)
The first adhesive layer 5 is a layer formed of an ethylene-vinyl acetate copolymer resin adhesive for adhering the glass cloth 1 and the decorative sheet 2 (back surface primer layer 2E). As the ethylene-vinyl acetate copolymer resin adhesive, for example, an adhesive containing an ethylene-vinyl acetate copolymer resin and an inorganic pigment (such as silica) can be used. The composition of the ethylene-vinyl acetate copolymer resin-based adhesive is, for example, 80.3 mass% or more and 81.3 mass% or less of ethylene-vinyl acetate copolymer resin, and 19.2 mass% or more and 19.7 mass% of the inorganic pigment. % Or less.
Further, the mass of the ethylene-vinyl acetate copolymer resin-based adhesive is set to 35.2 [g/m ² ] or less (solid amount) (organic mass 28.49 [g/m ² ] or less).

（作用その他）
以上の構成の不燃シート１０では、ガラスクロス１を基材とすると共に、樹脂フィルム２Ｄにポリプロピレン系樹脂とポリプロピレン系樹脂との混合樹脂を含有させ、第１接着剤層５にエチレン−酢酸ビニル共重合樹脂を含有させ、更に、樹脂フィルム２Ｄの厚さを０．０４５［mm］以上０．０６６［mm］以下とし、第１接着剤層５の質量を３５．２［g/m²］以下、つまり、小さくしたため、有機質量を低減することができる。それゆえ、燃焼量を低減でき、不燃性を有する不燃シート１０を提供することができる。 (Action and others)
In the non-combustible sheet 10 having the above structure, the glass cloth 1 is used as a base material, the resin film 2D contains a mixed resin of polypropylene resin and polypropylene resin, and the first adhesive layer 5 contains ethylene-vinyl acetate. Polymerized resin is further contained, and the thickness of the resin film 2D is 0.045 [mm] or more and 0.066 [mm] or less, and the mass of the first adhesive layer 5 is 35.2 [g/m ² ] or less. That is, since it is made small, the organic mass can be reduced. Therefore, the combustion amount can be reduced, and the nonflammable sheet 10 having nonflammability can be provided.

本発明の不燃シート１０が有する不燃性は、ＩＳＯ５６６０−１に準拠したコーンカロリ燃焼試験に準拠し、不燃シート１０の時間に対する総発熱量及び時間に対する発熱速度を求めた際に、（i）加熱開始後２０分間の総発熱量が８［MJ/m²］以下であり、（ii）加熱開始後２０分間、最大発熱速度が１０秒以上継続して２００［kW/m²］を超えず、かつ（iii）加熱開始後２０分間、防火上有害な裏面まで貫通する亀裂及び穴がないことを満たす不燃性である。
また、本実施形態の不燃シート１０では、表面保護層２Ａとしてアクリル樹脂系フィルムを用いたため、硬度を高めることができ、耐候性を向上できる。 The non-combustibility of the non-combustible sheet 10 of the present invention is based on the corn calorie combustion test according to ISO5660-1, and when the total calorific value of the non-combustible sheet 10 with respect to time and the heat generation rate with respect to time are obtained, (i) start heating The total heat generation amount for the next 20 minutes is 8 [MJ/m ² ] or less, and (ii) the maximum heat generation rate does not exceed 200 [kW/m ² ] for 10 minutes or more for 20 minutes after the start of heating, and (Iii) It is nonflammable for 20 minutes after the start of heating, satisfying the absence of cracks and holes penetrating to the back surface which is harmful for fire protection.
Further, in the non-combustible sheet 10 of the present embodiment, since the acrylic resin film is used as the surface protective layer 2A, the hardness can be increased and the weather resistance can be improved.

さらに、本実施形態の不燃シート１０では、樹脂成分として、塩化ビニル樹脂を含まないため、燃焼時にダイオキシン等の有害物質の発生を防止できる。
また、本実施形態の不燃シート１０では、比較的質量を軽くすることができ、２［kg/m²］以下の膜天井を実現できる。膜天井は素材が軽く、柔らかい為、大きな変形や衝撃に耐えることが出来るだけでなく、万が一落下しても軽いので、安全性が高く、さらに内天井からの落下物に対し、防止ネットのような役割もある。平成２５年８月に国土交通省より、特定天井並びに天井脱落に関する対策、措置が示された。施行は平成２６年４月である。これにより、特定天井（吊り天井で、高さ６ｍ以上、２００m²以上、単位面積質量２［kg/m²］以上、居室、廊下、その他人が日常利用する場所に設けられる）に対しては、構造耐久力上安全な構造形式が義務化された。単位面積質量２［kg/m²］以下の天井材は、特定天井対象外となり、複雑な構造設計が不要で材料代、工事代を抑制できる。 Furthermore, since the nonflammable sheet 10 of the present embodiment does not contain a vinyl chloride resin as a resin component, generation of harmful substances such as dioxins during combustion can be prevented.
Further, in the non-combustible sheet 10 of the present embodiment, it is possible to make the mass relatively light and realize a membrane ceiling of 2 [kg/m ² ] or less. The material of the membrane ceiling is light and soft, so it is not only able to withstand large deformations and shocks, but also light in case of a fall, so it is highly safe, and it is like a net to prevent objects falling from the inner ceiling. There is also a role. In August 2013, the Ministry of Land, Infrastructure, Transport and Tourism announced measures and measures for specific ceilings and ceiling drops. Enforcement is April 2014. As a result, for specific ceilings (suspended ceilings, heights of 6 m or more, 200 m ² or more, unit area mass of 2 [kg/m ² ] or more, provided in living rooms, corridors, and other places where people use everyday) , A structural form that is safe in terms of structural durability has been made mandatory. Ceiling materials with a unit area mass of 2 [kg/m ² ] or less are not subject to specific ceilings, and a complicated structural design is not required and material and construction costs can be reduced.

次に、本発明の不燃シート１０の実施例について説明する。
下記の構成で、本実施例の不燃シート１０を作成した。
本実施例では、燃焼量を考慮して、有機質量が最大となる使用を選定した。なお、樹脂フィルム２Ｄについては、有機質割合が最大となる使用を選定した。
（化粧シート２）
樹脂フィルム２Ｄの一方の面に、印刷により印刷インキ層２Ｃを形成した。樹脂フィルム２Ｄの組成は、ポリプロピレン系樹脂とポリエチレン系樹脂との混合樹脂を８６．９６質量％、有機添加剤を７．４９質量％、無機顔料を５．５５質量％含むものとした。また、樹脂フィルム２Ｄの厚さは０．０６［mm］とし、質量は５２．６［g/m²］（有機質量４９．７［g/m²］）とした。また、有機質割合は、４９．４５質量％［g/m²］とした。
また、印刷インキ層２Ｃの組成は、ウレタン樹脂を７０．０質量％、塩化ビニル酢酸ビニル共重合樹脂を３０．０質量％、無機顔料を０質量％含むものとした。また、印刷インキ層２Ｃの質量は、６．９［g/m²］（固形量）（有機質量６．９［g/m²］）とした。 Next, an example of the nonflammable sheet 10 of the present invention will be described.
The non-combustible sheet 10 of this example was formed with the following configuration.
In this example, the use that maximizes the organic mass was selected in consideration of the amount of combustion. For the resin film 2D, the use that maximizes the organic content was selected.
(Decorative sheet 2)
A printing ink layer 2C was formed on one surface of the resin film 2D by printing. The composition of the resin film 2D was such that a mixed resin of polypropylene-based resin and polyethylene-based resin was 86.96% by mass, an organic additive was 7.49% by mass, and an inorganic pigment was 5.55% by mass. The thickness of the resin film 2D was 0.06 [mm], and the mass was 52.6 [g/m ² ] (organic mass 49.7 [g/m ² ]). The organic matter content was 49.45% by mass [g/m ² ].
The composition of the printing ink layer 2C was such that the urethane resin contained 70.0% by mass, the vinyl chloride vinyl acetate copolymer resin contained 30.0% by mass, and the inorganic pigment contained 0% by mass. The mass of the printing ink layer 2C was 6.9 [g/m ² ] (solid amount) (organic mass 6.9 [g/m ² ]).

続いて、印刷インキ層２Ｃの上に、第２接着剤層２Ｂ（第１ウレタン樹脂系接着剤層２Ｂｂ、第２ウレタン樹脂系接着剤層２Ｂａ）を形成した。第１ウレタン樹脂系接着剤層２Ｂｂ及び第２ウレタン樹脂系接着剤層２Ｂａの組成は、ウレタン樹脂を１００質量％含むものとした。また、第１ウレタン樹脂系接着剤層２Ｂｂの質量は、６．２［g/m²］以下（固形量）（有機質量６．２［g/m²］以下）とした。さらに、第２ウレタン樹脂系接着剤層２Ｂａの質量は、１．３［g/m²］（固形量）（有機質量１．３［g/m²］以下）とした。
続いて、第２接着剤層２Ｂを介して、印刷インキ層２Ｃに表面保護層２Ａを貼り付けた。表面保護層２Ａの組成は、アクリル樹脂を７７．０質量％、フッ素樹脂を１９．０質量％、有機質添加剤を４．０質量％含むものとした。また、厚さは０．０５０１［mm］とし、質量は５９．５［g/m²］（固形量）（有機質量５９．５［g/m²］）とした。
続いて、樹脂フィルム２Ｄの他方の面に、裏面プライマー層２Ｅを形成した。裏面プライマー層２Ｅの組成は、ウレタン系樹脂を６０．０質量％、無機顔料を４０．０質量％含むものとし、質量は１．７５［g/m²］（固形量）（有機質量１．０５［g/m²］）とした。 Subsequently, the second adhesive layer 2B (first urethane resin adhesive layer 2Bb, second urethane resin adhesive layer 2Ba) was formed on the printing ink layer 2C. The composition of the first urethane resin-based adhesive layer 2Bb and the second urethane resin-based adhesive layer 2Ba was such that 100% by mass of the urethane resin was included. The mass of the first urethane resin adhesive layer 2Bb was 6.2 [g/m ² ] or less (solid amount) (organic mass 6.2 [g/m ² ] or less). Furthermore, the mass of the second urethane resin adhesive layer 2Ba was set to 1.3 [g/m ² ] (solid amount) (organic mass 1.3 [g/m ² ] or less).
Subsequently, the surface protection layer 2A was attached to the printing ink layer 2C via the second adhesive layer 2B. The composition of the surface protective layer 2A was such that it contained 77.0% by mass of an acrylic resin, 19.0% by mass of a fluororesin, and 4.0% by mass of an organic additive. The thickness was 0.0501 [mm], and the mass was 59.5 [g/m ² ] (solid amount) (organic mass 59.5 [g/m ² ]).
Then, the back surface primer layer 2E was formed on the other surface of the resin film 2D. The composition of the back surface primer layer 2E is such that the urethane resin is 60.0 mass% and the inorganic pigment is 40.0 mass%, and the mass is 1.75 [g/m ² ] (solid amount) (organic mass 1.05). [G/m ² ]).

（第１接着剤層５）
続いて、裏面プライマー層２Ｅの上に、第１接着剤層５を形成した。第１接着剤層５の組成は、エチレン−酢酸ビニル共重合系樹脂を８０．８質量％、無機顔料を１９．２質量％含むものとした。第１接着剤層５の質量は、３２．０［g/m²］（固形量）（有機質量２５．９［g/m²］）とした。 (First adhesive layer 5)
Subsequently, the first adhesive layer 5 was formed on the back surface primer layer 2E. The composition of the first adhesive layer 5 contained 80.8% by mass of the ethylene-vinyl acetate copolymer resin and 19.2% by mass of the inorganic pigment. The mass of the first adhesive layer 5 was 32.0 [g/m ² ] (solid amount) (organic mass 25.9 [g/m ² ]).

（ガラスクロス１）
続いて、第１接着剤層５を介して、ガラスクロス１の一方の面に化粧シート２を貼り付けた。ガラスクロス１の組成は、Ｅガラスを９８質量％、表面処理剤を２質量％含むものとした。また、織り方は、平織りとし、糸番手は、縦糸を６８．５［tex］、横糸を６８．５［tex］とした。さらに、織密度は、縦糸を４４［本/25mm］、横糸を３３［本/25mm］とした。厚さは、０．１９０［mm］とし、質量は、２１２．０［g/m²］（有機質量４．２［g/m²］）とした。 (Glass cloth 1)
Subsequently, the decorative sheet 2 was attached to one surface of the glass cloth 1 via the first adhesive layer 5. The composition of the glass cloth 1 contained 98% by mass of E glass and 2% by mass of a surface treatment agent. The weave was plain weave, and the yarn count was 68.5 [tex] for the warp and 68.5 [tex] for the weft. Furthermore, the weaving density was set to 44 [warms/25 mm] for the warp threads and 33 [hooks/25 mm] for the weft threads. The thickness was 0.190 [mm] and the mass was 212.0 [g/m ² ] (organic mass 4.2 [g/m ² ]).

（評価）
（不燃試験）
上記構成の不燃シート１０に対し、コーンカロリーメーターを用いた試験方法（ＩＳＯ５６６０−１に準拠）にて、燃焼性を確認した。試験は３つのサンプルにて実施した。
試験結果を下記表１に示す。表１より、３回のサンプルの試験とも総発熱量が４．６［MJ/m²］以下であり、またいずれも１０秒以上継続して２００［kW/m²］を超えることがなかった。また、加熱開始後２０分間、裏面に達する亀裂が発生しなかった。このように、本発明に基づく不燃シート１０は、不燃材の規格を満足していることが確認できた。 (Evaluation)
(Incombustibility test)
The flammability of the non-combustible sheet 10 having the above configuration was confirmed by a test method using a cone calorimeter (based on ISO5660-1). The test was carried out on three samples.
The test results are shown in Table 1 below. From Table 1, the total calorific value was 4.6 [MJ/m ² ] or less in the tests of three times, and none of them exceeded 200 [kW/m ² ] continuously for 10 seconds or more. .. Further, no crack reaching the back surface was generated for 20 minutes after the start of heating. As described above, it was confirmed that the non-combustible sheet 10 according to the present invention satisfied the standard of non-combustible material.

１ガラスクロス
２化粧シート
２Ａ表面保護層
２Ｂ第２接着剤層
２Ｂａ第２ウレタン樹脂系接着剤層
２Ｂｂ第１ウレタン樹脂系接着剤層
２Ｃ印刷インキ層
２Ｄ樹脂フィルム
２Ｅ裏面プライマー層
５第１接着剤層
１０不燃シート 1 Glass Cloth 2 Decorative Sheet 2A Surface Protective Layer 2B Second Adhesive Layer 2Ba Second Urethane Resin Adhesive Layer 2Bb First Urethane Resin Adhesive Layer 2C Printing Ink Layer 2D Resin Film 2E Backside Primer Layer 5 First Adhesive Layer 10 non-combustible sheet

Claims

A decorative sheet is attached to one surface of the glass cloth via a first adhesive layer containing an ethylene-vinyl acetate copolymer resin,
The decorative sheet is a resin film containing a mixed resin of polypropylene resin and polyethylene resin, a printing ink layer formed on a surface of the resin film opposite to the glass cloth, and the printing ink layer. A second adhesive layer on the surface opposite to the resin film, a surface protective layer formed on the surface of the second adhesive layer opposite to the printing ink layer, and a surface of the resin film on the glass cloth side. And a back surface primer layer formed on
The thickness of the resin film is 0.054 [mm] or more and 0.066 [mm] or less,
The organic mass of the printing ink layer is 6.9 [g/m ² ] or less,
The organic mass of the second adhesive layer is 7.5 [g/m ² ] or less,
The surface protection layer has an organic mass of 59.5 [g/m ² ] or less,
The organic mass of the back surface primer layer is 1.05 [g/m ² ] or less,
Mass of the first adhesive layer state, and are 35.2 [g / m ^2] or less,
The total organic mass of the resin film, the printing ink layer, the second adhesive layer, the surface protective layer, the back surface primer layer and the first adhesive layer is 150.55 [g/m ² ] or less. And
The printing ink layer contains 30.0% by mass or more of vinyl chloride vinyl acetate copolymer resin,
The surface protective layer contains 19.0 mass% or more of a fluororesin, 4.0 mass% or more of a benzotoazole-based organic additive and a hindered amine-based organic additive,
The resin film contains 5.55 mass% or more of an inorganic pigment,
The back surface primer layer contains 40.0 mass% or more of an inorganic pigment,
The non-combustible sheet, wherein the first adhesive layer contains an inorganic pigment in an amount of 19.2% by mass or more .

The first adhesive layer contains ethylene-vinyl acetate copolymer resin in an amount of 80.3% by mass or more and 81.3% by mass or less, and an inorganic pigment in an amount of 19.2% by mass or more and 19.7% by mass or less. The non-combustible sheet according to claim 1.