JP6622347B2 - Polarizing plate manufacturing method and manufacturing apparatus - Google Patents

Description

  The present invention relates to a polarizing plate manufacturing method and a manufacturing apparatus useful as one of optical components constituting a liquid crystal display device or the like.

  Polarizing films are widely used as dichroic dyes adsorbed and oriented on polyvinyl alcohol resin films. Iodine polarizing films using iodine as a dichroic dye and dichroic direct dyes as dichroic Dye-type polarizing films used as pigments are known. These polarizing films are usually used as polarizing plates by laminating a transparent film such as a triacetyl cellulose film on one side or both sides via an adhesive.

  As a method of laminating a transparent film on one or both sides of a polarizing film, after applying an active energy ray-curable resin to the surface of the transparent film in advance, the polarizing film and the transparent film are sandwiched between a pair of nip rolls (bonding rolls). There is a method of bonding and curing by irradiation with active energy rays (Patent Document 1: Japanese Patent Laid-Open No. 2004-245925, Patent Document 2: Japanese Patent Laid-Open No. 2009-134190, Patent Document 3: Special). (Open 2011-95560).

JP 2004-245925 A JP 2009-134190 A JP 2011-95560 A

  In the above method, when the thickness of the active energy ray-curable resin applied on the surface of the transparent film is, for example, 2.0 μm or less in order to reduce the thickness of the polarizing plate, the transparent film and the polarizing film are bonded. There was a problem that air bubbles were easily mixed in.

  The present invention has been made to solve the above-described problems, and provides a polarizing plate manufacturing method and a manufacturing apparatus in which mixing of bubbles is suppressed even when the thickness of the active energy ray-curable resin is reduced. The purpose is to do.

  The present invention relates to a method for producing a polarizing plate in which a transparent film is bonded to one side or both sides of a polarizing film, the adhesive coating applying an active energy ray-curable adhesive to one side or both sides of the polarizing film. By pressing the laminated body formed by laminating the construction process and the transparent film on one side or both sides of the polarizing film via an adhesive between a pair of bonding rolls rotating in the conveying direction, It is related with the manufacturing method of a polarizing plate provided with the bonding process which bonds a polarizing film, and the active energy ray irradiation process which irradiates an active energy ray to a laminated body and hardens an adhesive agent.

  In the adhesive application step, the application thickness of the active energy ray-curable adhesive applied to one or both surfaces of the polarizing film is preferably 0.1 to 2.0 μm.

  In one embodiment of the present invention, the adhesive coating step is a step of applying an active energy ray-curable adhesive to one side or both sides of a polarizing film that is conveyed upward in the vertical direction.

  In another embodiment of the present invention, the adhesive coating step is a step of applying an active energy ray-curable adhesive to one side or both sides of a polarizing film conveyed downward in the vertical direction.

  Further, the present invention is a polarizing plate manufacturing apparatus in which a transparent film is bonded to one side or both sides of a polarizing film, the transport means transporting the polarizing film upward in the vertical direction, and transported upward in the vertical direction. An adhesive coating device for applying an active energy ray-curable adhesive on one or both sides of a polarizing film, and a laminate in which a transparent film is laminated on one or both sides of the polarizing film via an adhesive A pair of laminating rolls for laminating a transparent film and a polarizing film, and an active energy ray for irradiating an active energy ray to the laminate to cure the adhesive And an irradiation apparatus.

  Further, the present invention is a polarizing plate manufacturing apparatus in which a transparent film is bonded to one side or both sides of a polarizing film, the transporting means for transporting the polarizing film downward in the vertical direction, and transported downward in the vertical direction. An adhesive coating device for applying an active energy ray-curable adhesive on one or both sides of a polarizing film, and a laminate in which the transparent film is laminated on one or both sides of the polarizing film via an adhesive A pair of laminating rolls for laminating a transparent film and a polarizing film, and an active energy ray for irradiating an active energy ray to the laminate to cure the adhesive And an irradiation apparatus.

  ADVANTAGE OF THE INVENTION According to this invention, the thin polarizing plate with which mixing of the bubble was suppressed can be provided.

It is a schematic side view which shows 1st Embodiment of the manufacturing apparatus of the polarizing plate concerning this invention. It is a schematic side view which shows 2nd Embodiment of the manufacturing apparatus of the polarizing plate concerning this invention. It is a schematic side view which shows 3rd Embodiment of the manufacturing apparatus of the polarizing plate concerning this invention. It is a schematic side view which shows 4th Embodiment of the manufacturing apparatus of the polarizing plate concerning this invention.

[Production method of polarizing plate]
The polarizing plate produced by the present invention is a polarizing plate in which a transparent film is bonded to one side or both sides of a polarizing film. In the production method of the present invention, an adhesive coating step of applying an active energy ray-curable adhesive on one side or both sides of a polarizing film and a transparent film are laminated on one side or both sides of the polarizing film via an adhesive. The laminated body is sandwiched between a pair of laminating rolls that rotate in the conveying direction and pressed, so that the laminating body is irradiated with active energy rays, and a laminating process for laminating the transparent film and the polarizing film. And an active energy ray irradiation step for curing the adhesive. First, each material used in the production method of the present invention will be described.

(Polarizing film)
Specifically, the polarizing film used in the polarizing plate of the present invention is obtained by adsorbing and orienting a dichroic dye on a uniaxially stretched polyvinyl alcohol resin film. The polyvinyl alcohol-based resin can be obtained by saponifying a polyvinyl acetate-based resin. As the polyvinyl acetate resin, in addition to polyvinyl acetate which is a homopolymer of vinyl acetate, a copolymer of vinyl acetate and other monomers copolymerizable therewith (for example, ethylene-vinyl acetate copolymer). Polymer). Other monomers that can be copolymerized with vinyl acetate include unsaturated carboxylic acids, olefins, vinyl ethers, unsaturated sulfonic acids, acrylamides having an ammonium group, and the like. The saponification degree of the polyvinyl alcohol-based resin is 85 mol% or more, preferably 90 mol% or more, more preferably 98 to 100 mol%. The average degree of polymerization of the polyvinyl alcohol-based resin is usually 1000 to 10000, preferably 1500 to 5000. These polyvinyl alcohol resins may be modified. For example, polyvinyl formal modified with aldehydes, polyvinyl acetal, polyvinyl butyral, and the like may be used.

  A film obtained by forming such a polyvinyl alcohol resin is used as a raw film of a polarizing film. The method for forming the polyvinyl alcohol-based resin is not particularly limited, and can be formed by a conventionally known appropriate method. Although the film thickness of the raw film which consists of polyvinyl alcohol-type resin is not specifically limited, For example, it is about 10-150 micrometers. Usually, it is supplied in the form of a roll, the thickness is in the range of 20 to 100 μm, preferably in the range of 30 to 80 μm, and the industrially practical width is in the range of 1500 to 6000 mm.

  The commercially available polyvinyl alcohol film (vinylon VF-PS # 7500, manufactured by Kuraray / OPL film M-7500, manufactured by Nihon Gosei) has a thickness of 75 μm (vinylon VF-PS # 6000, manufactured by Kuraray, vinylon VF-PE #). The original fabric thickness of 6000 (manufactured by Kuraray) is 60 μm.

  The polarizing film is usually a process of dyeing a polyvinyl alcohol resin film with a dichroic dye to adsorb the dichroic dye (dyeing process), and a polyvinyl alcohol resin film adsorbed with the dichroic dye is boric acid. It is manufactured through a step of treating with an aqueous solution (boric acid treatment step) and a step of washing with water after the treatment with the boric acid aqueous solution (water washing treatment step).

  In the production of the polarizing film, the polyvinyl alcohol-based resin film is usually uniaxially stretched, but this uniaxial stretching may be performed before the dyeing treatment step or during the dyeing treatment step, It may be performed after the dyeing process. When uniaxial stretching is performed after the dyeing treatment step, the uniaxial stretching may be performed before the boric acid treatment step or during the boric acid treatment step. Of course, uniaxial stretching can be performed in these plural stages.

  Uniaxial stretching may be performed uniaxially between rolls having different peripheral speeds, or may be performed uniaxially using a hot roll. Moreover, the dry-type extending | stretching which extends | stretches in air | atmosphere may be sufficient, and the wet extending | stretching which extends | stretches in the state swollen with the solvent may be sufficient. The draw ratio is usually about 3 to 8 times.

  Dyeing of the polyvinyl alcohol resin film with the dichroic dye in the dyeing process is performed, for example, by immersing the polyvinyl alcohol resin film in an aqueous solution containing the dichroic dye. As the dichroic dye, for example, iodine, a dichroic dye or the like is used. Examples of dichroic dyes include C.I. I. Dichroic direct dyes composed of disazo compounds such as DIRECT RED 39 and dichroic direct dyes composed of compounds such as trisazo and tetrakisazo are included. In addition, it is preferable that the polyvinyl alcohol-type resin film performs the immersion process to water before a dyeing process.

  When iodine is used as the dichroic dye, a method of dyeing a polyvinyl alcohol resin film by dipping it in an aqueous solution usually containing iodine and potassium iodide is employed. The content of iodine in this aqueous solution is usually 0.01 to 1 part by weight per 100 parts by weight of water, and the content of potassium iodide is usually 0.5 to 20 parts by weight per 100 parts by weight of water. When iodine is used as the dichroic dye, the temperature of the aqueous solution used for dyeing is usually 20 to 40 ° C., and the immersion time (dyeing time) in this aqueous solution is usually 20 to 1800 seconds.

On the other hand, when a dichroic dye is used as the dichroic dye, a method of immersing and dyeing a polyvinyl alcohol-based resin film in an aqueous solution containing an aqueous dichroic dye is usually employed. The content of the dichroic dye in this aqueous solution, usually, 1 × 10 ^-4 to 10 parts by weight per 100 parts by weight of water, preferably 1 × 10 ^-3 to 1 parts by weight, particularly preferably 1 × 10 ^{- 3} to 1 × 10 ⁻² parts by weight. This aqueous solution may contain an inorganic salt such as sodium sulfate as a dyeing assistant. When a dichroic dye is used as the dichroic dye, the temperature of the dye aqueous solution used for dyeing is usually 20 to 80 ° C., and the immersion time (dyeing time) in this aqueous solution is usually 10 to 1800 seconds. is there.

  The boric acid treatment step is performed by immersing a polyvinyl alcohol-based resin film dyed with a dichroic dye in a boric acid-containing aqueous solution. The amount of boric acid in the boric acid-containing aqueous solution is usually 2 to 15 parts by weight, preferably 5 to 12 parts by weight per 100 parts by weight of water. When iodine is used as the dichroic dye in the dyeing process described above, the boric acid-containing aqueous solution used in this boric acid treatment process preferably contains potassium iodide. In this case, the amount of potassium iodide in the boric acid-containing aqueous solution is usually 0.1 to 15 parts by weight, preferably 5 to 12 parts by weight per 100 parts by weight of water. The immersion time in the boric acid-containing aqueous solution is usually 60 to 1200 seconds, preferably 150 to 600 seconds, and more preferably 200 to 400 seconds. The temperature of the boric acid-containing aqueous solution is usually 40 ° C. or higher, preferably 50 to 85 ° C., more preferably 55 to 75 ° C.

  In the subsequent washing process, the polyvinyl alcohol-based resin film after the boric acid treatment described above is washed with water, for example, by immersing it in water. The water temperature in the water washing treatment is usually 4 to 40 ° C., and the immersion time is usually 1 to 120 seconds. After the water washing treatment, a drying treatment is usually performed to obtain a polarizing film. The drying process is preferably performed using, for example, a hot air dryer or a far infrared heater. The temperature of the drying treatment is usually 30 to 100 ° C, preferably 50 to 80 ° C. The time for the drying treatment is usually 60 to 600 seconds, preferably 120 to 600 seconds.

  In this way, the polyvinyl alcohol resin film is uniaxially stretched, dyed with a dichroic dye, treated with boric acid and washed with water to obtain a polarizing film. The thickness of this polarizing film is usually in the range of 5 to 50 μm.

(Transparent film)
In the present invention, a transparent film is bonded to one side or both sides of the polarizing film described above. When a transparent film is bonded on both surfaces of a polarizing film, each transparent film may be the same or a different type of film.

  Examples of the material constituting the transparent film include cycloolefin resins, cellulose acetate resins, polyethylene terephthalate, polyethylene naphthalate, polyester resins such as polybutylene terephthalate, polycarbonate resins, acrylic resins, and polypropylene. Examples thereof include film materials that have been widely used in the field.

  The cycloolefin-based resin is a thermoplastic resin (also referred to as a thermoplastic cycloolefin-based resin) having a monomer unit made of a cyclic olefin (cycloolefin), such as norbornene or a polycyclic norbornene-based monomer. The cycloolefin-based resin may be a hydrogenated product of the above-mentioned cycloolefin ring-opening polymer or a ring-opening copolymer using two or more cycloolefins, and has a cycloolefin, a chain olefin, and a vinyl group. An addition polymer with an aromatic compound or the like may be used. Those having a polar group introduced are also effective.

  In the case of using a copolymer of a cycloolefin and a chain olefin and / or an aromatic compound having a vinyl group, examples of the chain olefin include ethylene and propylene. As the aromatic compound having a vinyl group, Examples include styrene, α-methylstyrene, and nuclear alkyl-substituted styrene. In such a copolymer, the monomer unit composed of cycloolefin may be 50 mol% or less (preferably 15 to 50 mol%). In particular, when a terpolymer of a cycloolefin, a chain olefin, and an aromatic compound having a vinyl group is used, the amount of the monomer unit composed of cycloolefin can be made relatively small as described above. In such a terpolymer, the monomer unit composed of a chain olefin is usually 5 to 80 mol%, and the monomer unit composed of an aromatic compound having a vinyl group is usually 5 to 80 mol%.

  Cycloolefin-based resins may be commercially available products such as Topas (manufactured by Ticona), Arton (manufactured by JSR), ZEONOR (manufactured by Nippon Zeon), ZEONEX (manufactured by Nippon Zeon ( Co., Ltd.), Apel (manufactured by Mitsui Chemicals, Inc.), Oxis (OXIS) (manufactured by Okura Kogyo Co., Ltd.) and the like can be suitably used. When such a cycloolefin-based resin is formed into a film, a known method such as a solvent casting method or a melt extrusion method is appropriately used. In addition, for example, commercially available cycloolefin resin films such as Essina (manufactured by Sekisui Chemical Co., Ltd.), SCA40 (manufactured by Sekisui Chemical Co., Ltd.), Zeonoa Film (manufactured by Optes Co., Ltd.), etc. You may use goods.

  The cycloolefin resin film may be uniaxially stretched or biaxially stretched. By stretching, an arbitrary retardation value can be given to the cycloolefin-based resin film. Stretching is usually performed continuously while unwinding a film roll, and in a heating furnace, the roll traveling direction (film longitudinal direction), the direction perpendicular to the traveling direction (film width direction), or both Stretched. As the temperature of the heating furnace, a range from the vicinity of the glass transition temperature of the cycloolefin resin to the glass transition temperature + 100 ° C. is usually employed. The draw ratio is usually 1.1 to 6 times, preferably 1.1 to 3.5 times.

  When the cycloolefin-based resin film is in a roll-wound state, the films tend to adhere to each other and easily cause blocking. Therefore, the cycloolefin-based resin film is usually rolled after the protective film is bonded. In addition, since the cycloolefin resin film generally has poor surface activity, the surface to be bonded to the polarizing film is subjected to surface treatment such as plasma treatment, corona treatment, ultraviolet irradiation treatment, flame (flame) treatment, and saponification treatment. Is preferred. Among these, plasma treatment that can be carried out relatively easily, particularly atmospheric pressure plasma treatment, and corona treatment are preferable.

  The cellulose acetate-based resin is a cellulose partial or completely esterified product, and examples thereof include a film made of cellulose acetate ester, propionate ester, butyrate ester, and mixed ester thereof. More specifically, a triacetyl cellulose film, a diacetyl cellulose film, a cellulose acetate propionate film, a cellulose acetate butyrate film, and the like can be given. As such a cellulose ester resin film, an appropriate commercially available product, for example, Fujitac TD80 (Fuji Film Co., Ltd.), Fujitac TD80UF (Fuji Film Co., Ltd.), Fujitac TD80UZ (Fuji Film Co., Ltd.) KC8UX2M (manufactured by Konica Minolta Opto), KC8UY (manufactured by Konica Minolta Opto) Fujitac TD60UL (manufactured by Fuji Film), KC4UYW (manufactured by Konica Minolta Opto), KC6UAW (Konica Minolta Opto) Etc.) can be used preferably.

  Moreover, the cellulose acetate type-resin film which provided the phase difference characteristic as a transparent film is also used suitably. Commercially available cellulose acetate resin films to which such retardation characteristics are imparted include WV BZ 438 (manufactured by Fuji Film Co., Ltd.), KC4FR-1 (manufactured by Konica Minolta Opto), and KC4CR-1 (Konica Minolta). Opt Co., Ltd.), KC4AR-1 (Konica Minolta Opto Co., Ltd.) and the like. Cellulose acetate is also called acetyl cellulose or cellulose acetate.

  These cellulose acetate-based resin films are easy to absorb water, and the moisture content of the polarizing plate may affect the end talmi of the polarizing plate. The moisture content during the production of the polarizing plate is preferably closer to the equilibrium moisture content in the storage environment of the polarizing plate, for example, a clean room production line or a roll storage warehouse, and depends on the configuration of the laminated film. About 5%, more preferably 2.5% to 3.0%. The numerical value of the moisture content of this polarizing plate was measured by the dry weight method and is a change in weight after 105 ° C./120 minutes.

  The thickness of the transparent film used in the polarizing plate of the present invention is preferably thin, but if it is too thin, the strength is lowered and the processability is poor. On the other hand, when it is too thick, problems such as a decrease in transparency and a longer curing time after lamination occur. Therefore, an appropriate thickness of the transparent film is, for example, 5 to 200 μm, preferably 10 to 150 μm, and more preferably 10 to 100 μm.

  In order to improve the adhesion between the adhesive and the polarizing film and / or the transparent film, the polarizing film and / or the transparent film may be subjected to corona treatment, flame treatment, plasma treatment, ultraviolet treatment, primer coating treatment, saponification treatment, etc. A surface treatment may be applied.

  The transparent film may be subjected to surface treatments such as anti-glare treatment, anti-reflection treatment, hard coat treatment, antistatic treatment, and antifouling treatment alone or in combination of two or more. The transparent film and / or the transparent film surface protective layer may contain a UV absorber such as a benzophenone compound or a benzotriazole compound, or a plasticizer such as a phenyl phosphate compound or a phthalate compound.

  Furthermore, optical functions such as functions as a retardation film, function as a brightness enhancement film, function as a reflection film, function as a transflective film, function as a diffusion film, function as an optical compensation film, etc. Can have a function. In this case, for example, by laminating an optical functional film such as a retardation film, a brightness enhancement film, a reflection film, a transflective film, a diffusion film, and an optical compensation film on the surface of the transparent film, such a function is achieved. In addition, the transparent film itself can be given such a function. Further, the transparent film may have a plurality of functions such as a diffusion film having the function of a brightness enhancement film.

  For example, the above-mentioned transparent film is subjected to a stretching process described in Japanese Patent No. 2841377, Japanese Patent No. 3094113, or the like, or a process described in Japanese Patent No. 3168850 can be used as a retardation film. The function of can be provided. The retardation characteristics in the retardation film can be appropriately selected, for example, such that the front retardation value is 5 to 100 nm and the thickness direction retardation value is 40 to 300 nm. Further, two or more layers having different central wavelengths of selective reflection by forming fine holes in the transparent film by a method as described in JP-A No. 2002-169025 and JP-A No. 2003-29030 By superimposing these cholesteric liquid crystal layers, a function as a brightness enhancement film can be imparted.

  When a metal thin film is formed on the transparent film by vapor deposition or sputtering, a function as a reflective film or a transflective film can be imparted. By coating the transparent film described above with a resin solution containing fine particles, a function as a diffusion film can be imparted. Moreover, the function as an optical compensation film can be provided by coating and aligning liquid crystalline compounds, such as a discotic liquid crystalline compound, on said transparent film. Moreover, you may make the transparent film contain the compound which expresses retardation. Further, various optical functional films may be directly bonded to the polarizing film using an appropriate adhesive. Examples of commercially available optical functional films include brightness enhancement films such as DBEF (manufactured by 3M, available from Sumitomo 3M Co., Ltd. in Japan), and viewing angle improvements such as WV film (manufactured by Fuji Film Co., Ltd.). Film, Arton Film (manufactured by JSR Corporation), Zeonoor Film (manufactured by Optes Corporation), Essina (manufactured by Sekisui Chemical Co., Ltd.), VA-TAC (manufactured by Comic Minolta Opto Corporation), Sumikalite (Sumitomo) (Chemical Co., Ltd.) etc. can be mentioned.

(Active energy ray-curable adhesive)
The polarizing film and the transparent film are bonded via an active energy ray curable adhesive. Examples of the active energy ray-curable adhesive include an adhesive made of an epoxy resin composition containing an epoxy resin that is cured by irradiation with active energy rays from the viewpoint of weather resistance, refractive index, cationic polymerization, and the like. . However, the present invention is not limited to this, and various active energy ray-curable adhesives (organic solvent adhesives, hot melt adhesives, solventless adhesives) that have been used in the manufacture of polarizing plates. Etc.) can be adopted.

  The epoxy resin means a compound having two or more epoxy groups in the molecule. From the viewpoint of weather resistance, refractive index, cationic polymerizability, and the like, the epoxy resin contained in the curable epoxy resin composition that is an adhesive is an epoxy resin that does not contain an aromatic ring in the molecule (see, for example, Patent Document 1). It is preferable that Examples of such epoxy resins include hydrogenated epoxy resins, alicyclic epoxy resins, aliphatic epoxy resins, and the like.

  The hydrogenated epoxy resin is obtained by a method of glycidyl etherifying a nuclear hydrogenated polyhydroxy compound obtained by selectively subjecting a polyhydroxy compound, which is a raw material of an aromatic epoxy resin, to a nuclear hydrogenation reaction under pressure in the presence of a catalyst. Obtainable. Examples of aromatic epoxy resins include bisphenol-type epoxy resins such as bisphenol A diglycidyl ether, bisphenol F diglycidyl ether, and bisphenol S diglycidyl ether; phenol novolac epoxy resins, cresol novolac epoxy resins, and hydroxy Examples include novolak-type epoxy resins such as benzaldehyde phenol novolac epoxy resins; glycidyl ethers of tetrahydroxyphenylmethane, glycidyl ethers of tetrahydroxybenzophenone, and polyfunctional epoxy resins such as epoxidized polyvinylphenol. Of the hydrogenated epoxy resins, hydrogenated bisphenol A glycidyl ether is preferred.

  The alicyclic epoxy resin means an epoxy resin having one or more epoxy groups bonded to the alicyclic ring in the molecule. The “epoxy group bonded to an alicyclic ring” means a bridged oxygen atom —O— in the structure represented by the following formula. In the following formula, m is an integer of 2 to 5.

A compound in which a group in the form of removing one or more hydrogen atoms in (CH ₂ ) _m in the above formula is bonded to another chemical structure can be an alicyclic epoxy resin. One or more hydrogen atoms in (CH ₂ ) _m may be appropriately substituted with a linear alkyl group such as a methyl group or an ethyl group. Among alicyclic epoxy resins, an epoxy resin having an oxabicyclohexane ring (m = 3 in the above formula) or an oxabicycloheptane ring (m = 4 in the above formula) exhibits excellent adhesion. Therefore, it is preferably used. Although the alicyclic epoxy resin used preferably below is specifically illustrated, it is not limited to these compounds.

  (A) Epoxycyclohexylmethyl epoxycyclohexanecarboxylates represented by the following formula (I):

(In the formula, R ¹ and R ² each independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms).

  (B) Epoxycyclohexanecarboxylates of alkanediol represented by the following formula (II):

(Wherein R ³ and R ⁴ each independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms, and n represents an integer of 2 to 20).

  (C) Epoxycyclohexyl methyl esters of dicarboxylic acid represented by the following formula (III):

(In the formula, R ⁵ and R ⁶ each independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms, and p represents an integer of 2 to 20).

  (D) Epoxycyclohexyl methyl ethers of polyethylene glycol represented by the following formula (IV):

(Wherein R ⁷ and R ⁸ independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms, and q represents an integer of 2 to 10).

  (E) Epoxycyclohexyl methyl ethers of alkanediols represented by the following formula (V):

(Wherein R ⁹ and R ¹⁰ independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms, and r represents an integer of 2 to 20).

  (F) Diepoxy trispiro compound represented by the following formula (VI):

(In the formula, R ¹¹ and R ¹² each independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms).

  (G) Diepoxy monospiro compound represented by the following formula (VII):

(Wherein, R ¹³ and R ¹⁴ each independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms).

  (H) Vinylcyclohexene diepoxides represented by the following formula (VIII):

(Wherein R ¹⁵ represents a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms).
(I) Epoxycyclopentyl ethers represented by the following formula (IX):

(In the formula, R ¹⁶ and R ¹⁷ each independently represent a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms).

  (J) Diepoxytricyclodecanes represented by the following formula (X):

(In the formula, R ¹⁸ represents a hydrogen atom or a linear alkyl group having 1 to 5 carbon atoms).
Among the alicyclic epoxy resins exemplified above, the following alicyclic epoxy resins are commercially available or their analogs, and are more preferably used because they are relatively easy to obtain.

(A) Esterified product of 7-oxabicyclo [4.1.0] heptane-3-carboxylic acid and (7-oxa-bicyclo [4.1.0] hept-3-yl) methanol [formula (I) In which R ¹ = R ² = H],
(B) 4-methyl-7-oxabicyclo [4.1.0] heptane-3-carboxylic acid and (4-methyl-7-oxa-bicyclo [4.1.0] hept-3-yl) methanol Ester compound of [In the formula (I), R ¹ = 4-CH ₃ , R ² = 4-CH ₃ compound],
(C) Esterified product of 7-oxabicyclo [4.1.0] heptane-3-carboxylic acid and 1,2-ethanediol [in the formula (II), R ³ = R ⁴ = H, n = 2 Compound],
(D) (7-Oxabicyclo [4.1.0] hept-3-yl) esterified product of methanol and adipic acid [in the formula (III), R ⁵ = R ⁶ = H, p = 4 compound] ,
(E) (4-Methyl-7-oxabicyclo [4.1.0] hept-3-yl) esterified product of methanol and adipic acid [in formula (III), R ⁵ = 4-CH ₃ , R ⁶ = 4-
Compound of CH ₃ , p = 4],
(F) etherified product of (7-oxabicyclo [4.1.0] hept-3-yl) methanol and 1,2-ethanediol [in the formula (V), R ⁹ = R ¹⁰ = H, r = Compound of 2].

  Moreover, as an aliphatic epoxy resin, the polyglycidyl ether of an aliphatic polyhydric alcohol or its alkylene oxide adduct can be mentioned. More specifically, 1,4-butanediol diglycidyl ether; 1,6-hexanediol diglycidyl ether; glycerin triglycidyl ether; trimethylolpropane triglycidyl ether; polyethylene glycol diglycidyl ether; propylene Diglycidyl ether of glycol; Polyether polyol obtained by adding one or more alkylene oxides (ethylene oxide or propylene oxide) to aliphatic polyhydric alcohols such as ethylene glycol, propylene glycol, and glycerin A glycidyl ether etc. are mentioned.

  The epoxy resin which comprises the adhesive agent which consists of an epoxy-type resin composition may be used individually by 1 type, and may use 2 or more types together. The epoxy equivalent of the epoxy resin used in this composition is usually in the range of 30 to 3,000 g / equivalent, preferably 50 to 1,500 g / equivalent. When the epoxy equivalent is less than 30 g / equivalent, the flexibility of the composite polarizing plate after curing may be reduced, or the adhesive strength may be reduced. On the other hand, if it exceeds 3,000 g / equivalent, the compatibility with other components contained in the adhesive may be lowered.

  In this adhesive, cationic polymerization is preferably used as a curing reaction of the epoxy resin from the viewpoint of reactivity. Therefore, it is preferable to mix | blend a cationic polymerization initiator with the curable epoxy resin composition which is an active energy ray hardening-type adhesive agent. The cationic polymerization initiator generates a cationic species or a Lewis acid by irradiation with active energy rays such as visible light, ultraviolet rays, X-rays, and electron beams, and initiates an epoxy group polymerization reaction. Hereinafter, a cationic polymerization initiator that generates a cationic species or a Lewis acid by irradiation of active energy rays and initiates a polymerization reaction of an epoxy group is referred to as a “photo cationic polymerization initiator”.

  The method of curing the adhesive by irradiating with active energy rays using a cationic photopolymerization initiator enables curing at room temperature, reducing the need to consider the distortion due to heat resistance or expansion of the polarizing film, and between the films Is advantageous in that it can be bonded well. In addition, since the photocationic polymerization initiator acts catalytically by light, it is excellent in storage stability and workability even when mixed with an epoxy resin.

  Examples of the photocationic polymerization initiator include aromatic diazonium salts; onium salts such as aromatic iodonium salts and aromatic sulfonium salts; iron-allene complexes.

  Examples of the aromatic diazonium salt include benzenediazonium hexafluoroantimonate, benzenediazonium hexafluorophosphate, and benzenediazonium hexafluoroborate. Examples of the aromatic iodonium salt include diphenyliodonium tetrakis (pentafluorophenyl) borate, diphenyliodonium hexafluorophosphate, diphenyliodonium hexafluoroantimonate, di (4-nonylphenyl) iodonium hexafluorophosphate, and the like.

  Examples of the aromatic sulfonium salt include triphenylsulfonium hexafluorophosphate, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium tetrakis (pentafluorophenyl) borate, 4,4′-bis (diphenylsulfonio) diphenylsulfide bis ( Hexafluorophosphate), 4,4′-bis [di (β-hydroxyethoxy) phenylsulfonio] diphenyl sulfide bis (hexafluoroantimonate), 4,4′-bis [di (β-hydroxyethoxy) phenylsulfonio ] Diphenyl sulfide bis (hexafluorophosphate), 7- [di (p-toluyl) sulfonio] -2-isopropylthioxanthone hexafluoroantimonate, 7- [di p-toluyl) sulfonio] -2-isopropylthioxanthone tetrakis (pentafluorophenyl) borate, 4-phenylcarbonyl-4′-diphenylsulfonio-diphenyl sulfide hexafluorophosphate, 4- (p-tert-butylphenylcarbonyl) -4 Examples include '-diphenylsulfonio-diphenylsulfide hexafluoroantimonate, 4- (p-tert-butylphenylcarbonyl) -4'-di (p-toluyl) sulfonio-diphenylsulfide tetrakis (pentafluorophenyl) borate, and the like.

  Examples of the iron-allene complex include xylene-cyclopentadienyl iron (II) hexafluoroantimonate, cumene-cyclopentadienyl iron (II) hexafluorophosphate, xylene-cyclopentadienyl iron (II). -Tris (trifluoromethylsulfonyl) methanide etc. are mentioned.

  Commercially available products of these photocationic polymerization initiators can be easily obtained. For example, “Kayarad PCI-220” and “Kayarad PCI-620” (Nippon Kayaku Co., Ltd. )), "UVI-6990" (manufactured by Union Carbide), "Adekaoptomer SP-150" and "Adekaoptomer SP-170" (manufactured by ADEKA Corporation), "CI-5102", " "CIT-1370", "CIT-1682", "CIP-1866S", "CIP-2048S", and "CIP-2064S" (manufactured by Nippon Soda Co., Ltd.), "DPI-101", "DPI-102" , “DPI-103”, “DPI-105”, “MPI-103”, “MPI-105”, “BBI-101”, “BBI-102” , “BBI-103”, “BBI-105”, “TPS-101”, “TPS-102”, “TPS-103”, “TPS-105”, “MDS-103”, “MDS-105”, “ Examples thereof include “DTS-102” and “DTS-103” (manufactured by Midori Chemical Co., Ltd.), “PI-2074” (manufactured by Rhodia), and the like.

  Only one kind of the cationic photopolymerization initiator may be used alone, or two or more kinds thereof may be mixed and used. Among these, aromatic sulfonium salts are preferably used because they have ultraviolet absorption characteristics even in a wavelength region of 300 nm or more, and thus can provide a cured product having excellent curability and good mechanical strength and adhesive strength.

  The compounding quantity of a photocationic polymerization initiator is 0.5-20 weight part normally with respect to 100 weight part of epoxy resins, Preferably it is 1 weight part or more, Preferably it is 15 weight part or less. When the blending amount of the cationic photopolymerization initiator is less than 0.5 parts by weight with respect to 100 parts by weight of the epoxy resin, curing becomes insufficient, and mechanical strength and adhesive strength tend to decrease. Moreover, when the compounding quantity of a photocationic polymerization initiator exceeds 20 weight part with respect to 100 weight part of epoxy resins, the hygroscopic property of hardened | cured material will become high because the ionic substance in hardened | cured material will increase, and durability performance. May be reduced.

  When using a photocationic polymerization initiator, the curable epoxy resin composition may further contain a photosensitizer as necessary. By using a photosensitizer, the reactivity of cationic polymerization is improved, and the mechanical strength and adhesive strength of the cured product can be improved. Examples of the photosensitizer include carbonyl compounds, organic sulfur compounds, persulfides, redox compounds, azo and diazo compounds, halogen compounds, and photoreductive dyes.

  Specific examples of the photosensitizer include benzoin derivatives such as benzoin methyl ether, benzoin isopropyl ether, and α, α-dimethoxy-α-phenylacetophenone; benzophenone, 2,4-dichlorobenzophenone, o -Benzophenone derivatives such as methyl benzoylbenzoate, 4,4'-bis (dimethylamino) benzophenone, and 4,4'-bis (diethylamino) benzophenone; thioxanthone derivatives such as 2-chlorothioxanthone and 2-isopropylthioxanthone; 2 Anthraquinone derivatives such as chloroanthraquinone and 2-methylanthraquinone; acridone derivatives such as N-methylacridone and N-butylacridone; other α, α-diethoxyacetophenone, benzi Ru, fluorenone, xanthone, uranyl compounds, halogen compounds, and the like. A photosensitizer may be used individually by 1 type and may use 2 or more types together. The photosensitizer is preferably contained in the range of 0.1 to 20 parts by weight in 100 parts by weight of the curable epoxy resin composition.

  The epoxy resin contained in the adhesive is cured by photocationic polymerization, but may be cured by both photocationic polymerization and thermal cationic polymerization. In the latter case, it is preferable to use a photocationic polymerization initiator and a thermal cationic polymerization initiator in combination.

  Examples of the thermal cationic polymerization initiator include benzylsulfonium salt, thiophenium salt, thioranium salt, benzylammonium, pyridinium salt, hydrazinium salt, carboxylic acid ester, sulfonic acid ester, and amine imide. These thermal cationic polymerization initiators can be easily obtained as commercial products. For example, “Adeka Opton CP77” and “Adeka Opton CP66” (manufactured by ADEKA Corporation), “CI” are available under the trade names. -2639 "and" CI-2624 "(manufactured by Nippon Soda Co., Ltd.)," Sun-Aid SI-60L "," Sun-Aid SI-80L "and" Sun-Aid SI-100L "(manufactured by Sanshin Chemical Industry Co., Ltd.) Etc.

  The active energy ray-curable adhesive may further contain a compound that promotes cationic polymerization, such as oxetanes and polyols.

  Oxetanes are compounds having a 4-membered ring ether in the molecule, such as 3-ethyl-3-hydroxymethyloxetane, 1,4-bis [(3-ethyl-3-oxetanyl) methoxymethyl] benzene, 3 -Ethyl-3- (phenoxymethyl) oxetane, di [(3-ethyl-3-oxetanyl) methyl] ether, 3-ethyl-3- (2-ethylhexyloxymethyl) oxetane, phenol novolac oxetane and the like. These oxetanes can be easily obtained as commercial products. For example, all of these oxetanes are trade names such as “Aron Oxetane OXT-101”, “Aron Oxetane OXT-121”, “Aron Oxetane OXT-211”. "Aron oxetane OXT-221" and "Aron oxetane OXT-212" (manufactured by Toagosei Co., Ltd.). These oxetanes are usually contained in the curable epoxy resin composition in a proportion of 5 to 95% by weight, preferably 30 to 70% by weight.

  As the polyols, those having no acidic group other than phenolic hydroxyl groups are preferable. For example, polyol compounds having no functional groups other than hydroxyl groups, polyester polyol compounds, polycaprolactone polyol compounds, polyol compounds having phenolic hydroxyl groups, polycarbonates A polyol etc. can be mentioned. The molecular weight of these polyols is usually 48 or more, preferably 62 or more, more preferably 100 or more, and preferably 1,000 or less. These polyols are usually contained in the curable epoxy resin composition in a proportion of 50% by weight or less, preferably 30% by weight or less.

  Active energy ray-curable adhesives include ion trapping agents, antioxidants, chain transfer agents, tackifiers, thermoplastic resins, fillers, flow regulators, leveling agents, plasticizers, antifoaming agents, etc. Additives can be blended. Examples of the ion trapping agent include powdered bismuth-based, antimony-based, magnesium-based, aluminum-based, calcium-based, titanium-based, and mixed inorganic compounds. The antioxidant is a hindered phenol-based antioxidant. Etc.

  Active energy ray-curable adhesives can be used as solventless adhesives that are substantially free of solvent components, but each coating method has an optimum viscosity range, A solvent may be included. It is preferable to use a solvent that dissolves the epoxy resin composition and the like well without degrading the optical performance of the polarizing film. For example, hydrocarbons represented by toluene, esters represented by ethyl acetate, and the like. And organic solvents such as The viscosity of the active energy ray-curable adhesive used in the present invention is, for example, in the range of about 5 to 1000 mPa · s, preferably 10 to 200 mPa · s, and more preferably 20 to 100 mPa · s.

(First embodiment)
Next, the manufacturing apparatus and manufacturing method of the polarizing plate of this invention are demonstrated, referring drawings. FIG. 1 is a schematic view showing a first embodiment of a polarizing plate production apparatus of the present invention.

  In the polarizing plate manufacturing apparatus shown in FIG. 1, the adhesive coating apparatuses 11 and 12 for applying an adhesive to both surfaces of the polarizing film 1, the transparent films 2 and 3, and the polarizing film 1 are laminated and laminated. Bonding rolls (nip rolls) 51 and 52 for obtaining the body 4, a roll 13 for bringing the transparent films 2 and 3 and the polarizing film 1 into close contact with each other in the laminate 4, and a position facing the outer peripheral surface of the roll 13 The first active energy ray irradiating devices 14 and 15 installed in the first, the second and subsequent active energy ray irradiating devices 16 to 18 installed further downstream in the conveying direction, and the conveying nip roll 19 are conveyed. It is provided in order along the direction.

  First, active energy ray curing is performed by the adhesive coating apparatuses 11 and 12 on both surfaces of the polarizing film 1 that is continuously drawn out from the state wound in a roll shape and conveyed upward in the vertical direction by a conveying means (not shown). A mold adhesive is applied (adhesive application process).

  And the laminated body by which the transparent films 2 and 3 with which the adhesive agent was apply | coated are laminated | stacked through the adhesive agent on both surfaces of the transparent films 2 and 3 continuously drawn out from the state wound by roll shape. The transparent film 1 and the polarizing film 2 are pressed by pressing at least one bonding roll in the direction of the other bonding roll while being sandwiched between a pair of bonding rolls 51 and 52 rotating in the transport direction. 3 are bonded together to form a laminate 4 (bonding step).

  Next, in the process of transporting the laminate 4 in close contact with the outer peripheral surface of the roll 13, the active energy rays are irradiated from the first active energy ray irradiating devices 14, 15 toward the outer peripheral surface of the roll 13, and bonded. The agent is polymerized and cured (active energy ray irradiation step).

  Note that the second and subsequent active energy ray irradiation devices 16 to 18 arranged on the downstream side in the transport direction are devices for completely polymerizing and curing the adhesive, and can be added or omitted as necessary. Finally, the laminated body 4 passes the nip roll 19 for conveyance, and is wound up by the winding roll 20 as a polarizing plate (polarizing plate winding process). Hereinafter, each step will be described in detail.

<Adhesive coating process>
Although the coating method of the adhesive agent to the polarizing film 1 is not specifically limited, For example, various coating systems, such as a doctor blade, a wire bar, a die coater, a comma coater, a gravure coater, can be utilized. Of these, taking into consideration the thin film coating, the degree of freedom of the pass line, the wideness, etc., gravure rolls are preferable as the adhesive coating apparatuses 11 and 12.

  When applying an adhesive using a gravure roll as the adhesive application device 11 or 12, the thickness of the applied adhesive (application thickness) is preferably 0.1 to 2.0 μm, more preferably. Is 0.2 μm to 1.0 μm. In this embodiment, since the unevenness | corrugation of the surface of the polarizing film 1 can be coat | covered with an adhesive agent by apply | coating an adhesive agent directly on the surface of the polarizing film 1, the bubble of the time of bonding with the transparent films 2 and 3 is carried out. Occurrence can be suppressed. In addition, when laminating a transparent film and a polarizing film via an adhesive applied on a transparent film, bubbles that are considered to be caused by unevenness on the surface of the polarizing film are likely to be generated, and the coating thickness of the adhesive is increased. Although generation | occurrence | production of a bubble can be reduced by doing, when the application | coating thickness of an adhesive agent is 2.0 micrometers or less, it may be difficult to suppress generation | occurrence | production of a bubble. In the adhesive coating method of this embodiment, even when the thickness of the adhesive is within the above range, the generation of bubbles at the time of bonding can be suppressed.

The coating thickness of the adhesive is adjusted by the draw ratio, which is the speed ratio of the gravure roll to the line speed of the polarizing film . Generally, the coating thickness of the adhesive can be adjusted to 0.1 to 2.0 μm by adjusting the draw ratio (gravure roll speed / line speed) to 0.5 to 10. More specifically, the line speed of the polarizing film 1 is 10 to 100 m / min, the gravure roll is rotated in the direction opposite to the conveying direction of the polarizing film 1, and the speed of the gravure roll is 5 to 1000 m / min. The application thickness of the adhesive can be adjusted to 0.1 to 2.0 μm.

  In the adhesive coating process, the polarizing film 1 is conveyed in the vertical direction upward as described above, and the adhesive is applied from both sides of the polarizing film 1 by the adhesive coating apparatuses 11 and 12. Although it is possible to apply the adhesive from the lower side to the polarizing film conveyed in the horizontal direction, it is difficult to apply the adhesive continuously from the upper side with a normal coating apparatus because the adhesive drips down. Therefore, in the case of the manufacturing method of the polarizing plate which bonds a transparent film on both surfaces of the polarizing film 1, an adhesive agent is apply | coated from both sides with respect to the polarizing film 1 conveyed vertically upward like the apparatus of this embodiment. The method is useful. The term “vertically upward” in the present specification is not limited to the vertical direction as long as the adhesive can be applied from both side surfaces. For example, it is within a range of ± 5 degrees with respect to the upward in the vertical direction. Including direction.

  It is preferable that the adhesive coating apparatuses 11 and 12 disposed on both sides of the transported polarizing film 1 are disposed at positions where they do not face each other. The application thickness of the adhesive can also be adjusted by the pressure applied to the polarizing film 1 by the pressure applied by the adhesive application devices 11 and 12, but it is difficult to adjust the pressure when arranged at opposing positions. Because it becomes.

  After preparation, the adhesive is usually at a predetermined temperature within the range of 15 to 40 ° C. ± 5 ° C. (for example, when the predetermined temperature is 30 ° C., 30 ° C. ± 5 ° C.), preferably ± 3 ° C., more preferably It is applied in an environment adjusted to ± 1 ° C.

<Bonding process>
In this step, the transparent films 2 and 3 that are continuously drawn out from the state of being wound in a roll are laminated on both surfaces of the polarizing film 1 to which the adhesive has been applied in the above step via the adhesive. The transparent film 1 and the polarizing film are pressed by pressing the laminating roll 51 in the direction of the laminating roll 52, for example, in a state where the laminate is sandwiched between a pair of laminating rolls 51 and 52 rotating in the transport direction. 2 and 3 are bonded together to form a laminate 4.

  The pressure applied to the laminate by pressing is not particularly limited, but when using a metal roll and a rubber roll, the instantaneous pressure in the two-sheet type press case made of Fuji Film is 0.2 to 3.0 MPa. Is more preferable, and it is 0.5 to 2.3 MPa.

  A pair of bonding rolls may have a difference in peripheral speed between one bonding roll and the other bonding roll. For example, the peripheral speed of the bonding roll (1st bonding roll) installed in the surface side bonded to the liquid crystal panel of the laminated body 4 is the opposite side of the bonding roll (2nd bonding roll). It is preferably faster than the peripheral speed. Thereby, it is possible to give the obtained polarizing plate a curl (positive curl) in which the surface bonded to the liquid crystal panel becomes convex and the opposite surface becomes concave. When the obtained polarizing plate is curled (reverse curl) so that the surface to be bonded to the liquid crystal panel is concave and the opposite surface is convex, the polarizing plate is bonded to the liquid crystal cell. When it does, it will become easy to produce malfunctions, such as a bubble biting in a center part. In this case, it is preferable to use a metal roll as the first laminating roll and a rubber roll as the second laminating roll.

  Furthermore, when the peripheral speed of the 2nd bonding roll is set to 1, it is more preferable that the ratio of the peripheral speed of the 1st bonding roll is 1.0050-1.0200. When the peripheral speed of the first laminating roll is faster than this range, the curl amount of the positive curl becomes too large, causing problems such as entrapment of bubbles at the end when laminating the polarizing plate to the liquid crystal cell. This is because, when placed in a harsh environment, the positive curl is further promoted and the end of the polarizing plate may be peeled off from the liquid crystal cell.

<Active energy ray irradiation process>
The roll 13 constitutes a convex curved surface whose outer peripheral surface is mirror-finished, and the laminate 4 is conveyed while closely contacting the surface, and the adhesive is polymerized and cured by the active energy ray irradiation devices 14 and 15 in the process. . The diameter of the roll 13 is not particularly limited when the adhesive is polymerized and cured and the laminate 4 is sufficiently adhered. The roll 13 may be driven or rotated according to the movement of the line of the laminate 4 or may be fixed so that the laminate 4 slides on the surface. Further, the roll 13 may act as a cooling roll for dissipating heat generated in the laminate 4 at the time of polymerization and curing by irradiation with active energy rays. In that case, it is preferable that the surface temperature of a cooling roll is set to 20-30 degreeC.

  The light source used for polymerizing and curing the adhesive by irradiation with active energy rays is not particularly limited, but is preferably a light source having an emission distribution at a wavelength of 400 nm or less. Examples of such a light source include a low pressure mercury lamp, a medium pressure mercury lamp, a high pressure mercury lamp, an ultrahigh pressure mercury lamp, a chemical lamp, a black light lamp, a microwave excitation mercury lamp, and a metal halide lamp.

Although the light irradiation intensity | strength to an active energy ray hardening-type adhesive agent is determined for every composition of an adhesive agent and it does not specifically limit, It is preferable that it is 10-5000 mW / cm < ² >. When the light irradiation intensity to the resin composition is less than 10 mW / cm ² , the reaction time becomes too long, and when it exceeds 5000 mW / cm ² , adhesion occurs due to heat radiated from the lamp and heat generated during polymerization of the composition. There is a possibility that yellowing of the epoxy resin composition as a constituent material of the agent or deterioration of the polarizing film may occur. The irradiation intensity is preferably an intensity in a wavelength region effective for activation of the photocationic polymerization initiator, more preferably an intensity in a wavelength region of a wavelength of 400 nm or less, and further preferably a wavelength region of a wavelength of 280 to 320 nm. Strength.

The irradiation time of the active energy ray to the active energy ray-curable adhesive is controlled for each composition to be cured and is not particularly limited, but the integrated light amount expressed as the product of the irradiation intensity and the irradiation time is 10 mJ / cm ² or more, it is preferable to set preferably such that the 10~5,000mJ / cm ^2. When the integrated light quantity to the adhesive is less than 10 mJ / cm ² , the generation of active species derived from the initiator is not sufficient, and the adhesive is not sufficiently cured. On the other hand, when the integrated light quantity exceeds 5,000 mJ / cm ² , the irradiation time becomes very long, which is disadvantageous for improving productivity.

  In the present invention, the adhesive is polymerized and cured by irradiating the laminate with active energy rays, but polymerization curing by heating may be used in combination.

When the active energy rays are ultraviolet rays, in the step of irradiating the laminate 4 with the active energy rays, the irradiation time is 0.1 while applying a tension of 100 to 800 N / m in the longitudinal direction (conveying direction) to the laminate 4. It is preferable that the laminate 4 is conveyed at a line speed that is at least 2 seconds. Moreover, it is preferable that the irradiation intensity | strength of an ultraviolet-ray shall be 10 mW / cm < ² > or more.

Moreover, when the integrated light quantity of the active energy rays by the active energy ray irradiation devices 14 and 15 is insufficient, the active energy ray irradiation devices 16 to 18 after the second are further provided to irradiate the active energy rays, and the laminated body It is preferable to accelerate the curing of the adhesive No. 4. Integrated light intensity in these whole process is 10 mJ / cm ² or more, preferably it is preferably set so that 10~5,000mJ / cm ^2. As described above, in the step of irradiating the active energy ray, the irradiation of the active energy ray is preferably performed in a plurality of times.

  In order to surely cure the adhesive at the end of the polarizing plate (laminate), for example, a method of arranging “Light Hammer 10” made by FUSION, which is an electrodeless D bulb lamp, so as to cross the film running. Is mentioned.

  The rate at which the active energy ray-curable resin is cured, that is, the reaction rate, is preferably 90% or more, more preferably 95% or more.

<Polarizing film winding process>
The tension for winding up the laminate (polarizing plate) 4 is set to 30 N / cm ^{2 to} 150 N / cm ² . ^Preferably, a ^{30N / cm 2 ~120N / cm 2} . If it is less than 30 N / cm ^2, it is not preferable because winding deviation occurs when a long roll is transferred. When it is larger than 150 N / cm ² , the tightness of the winding is strong and the tarmi is likely to occur.

Note that the longer the winding length, the more likely it is that tightening will occur with the same tension (a phenomenon that makes it difficult to return to a flat state when unrolled), so the tension is lowered continuously or stepwise while the polarizing plate is wound around the core. You may let them. Even in such a method of reducing the tension by applying a so-called taper, the tension at that time is 150 N / cm ² or less.

  The length of the polarizing plate wound around the core is not particularly limited, but is preferably 100 m or more and 4000 m or less.

  The diameter of the cylindrical core is preferably 6 inches to 12 inches. The larger the diameter of the core is, the more preferable, and more preferable is 11 inches, 12 inches, and the like.

  The material of the cylindrical core is not particularly limited as long as it can be used in a clean room and does not easily generate dust, and can secure an appropriate strength so that a wide-width polarizing plate can be wound. FRP (glass fiber reinforced plastic) Etc. can be selected.

(Second Embodiment)
FIG. 2 is a schematic view showing a second embodiment of the polarizing plate production apparatus of the present invention. In the manufacturing apparatus of the second embodiment, the polarizing film 1 that is continuously drawn out from the state wound in a roll shape is conveyed in the vertical direction upward in that the polarizing film 1 is conveyed in the vertical direction downward by a conveyance unit (not shown). This is different from the first embodiment. Since other configurations are the same as those in the first embodiment, description thereof is omitted. In the present specification, the term “vertical downward” is not limited to the vertical direction as long as the adhesive can be applied from both sides. For example, a range of ± 5 degrees with respect to the downward downward direction. It is assumed to include the direction inside.

  Also in the manufacturing apparatus of this embodiment, since the adhesive can be applied from both sides of the polarizing film 1 as in the first embodiment, the polarizing film that bonds the transparent films 2 and 3 to both sides of the polarizing film 1. It is useful for the manufacturing method of a board. In this embodiment, since the unevenness | corrugation of the surface of the polarizing film 1 can be coat | covered with an adhesive agent by apply | coating an adhesive agent directly on the surface of the polarizing film 1, the bubble of the time of bonding with the transparent films 2 and 3 is carried out. Occurrence can be suppressed.

(Third embodiment)
FIG. 3 is a schematic view showing a third embodiment of the polarizing plate production apparatus of the present invention. In the manufacturing apparatus of the third embodiment, the active energy ray is not irradiated in a state where the laminate is in close contact with the roll, and therefore the roll 13 and the active energy ray irradiating devices 14 and 15 in FIG. 1 are not provided. Only the manufacturing apparatus of the first embodiment is different. In the manufacturing apparatus of the present embodiment, instead of the first active energy ray irradiating devices 14 and 15 in FIG. The agent is polymerized and cured. Preferable conditions such as light irradiation intensity and integrated light amount in the active energy ray irradiation step are the same as preferable conditions in the active energy ray irradiation step in the first embodiment. Other configurations and other processes are the same as those in the first embodiment, and thus description thereof is omitted.

  Also in the manufacturing apparatus of this embodiment, since the adhesive can be applied from both sides of the polarizing film 1 as in the first embodiment, the polarizing film that bonds the transparent films 2 and 3 to both sides of the polarizing film 1. It is useful for the manufacturing method of a board. In this embodiment, since the unevenness | corrugation of the surface of the polarizing film 1 can be coat | covered with an adhesive agent by apply | coating an adhesive agent directly on the surface of the polarizing film 1, the bubble of the time of bonding with the transparent films 2 and 3 is carried out. Occurrence can be suppressed.

(Fourth embodiment)
In the present embodiment, the polarizing plate is manufactured from one polarizing film and one transparent film. Then, in the adhesive coating process, an adhesive is applied to one side of one polarizing film, and in the laminating process, the polarizing film and the transparent film are brought into contact with the one side of the transparent film. In a laminated state, the polarizing film and the transparent film are bonded together by being sandwiched between a pair of bonding rolls.

  Next, the manufacturing method of this embodiment is demonstrated, referring drawings. FIG. 4 is a schematic view showing a fourth embodiment of the polarizing plate production apparatus of the present invention.

  In the polarizing plate manufacturing apparatus shown in FIG. 4, an adhesive coating device 11 for applying an adhesive to one side of the polarizing film 1, the polarizing film 1, and the transparent film 2 are bonded to obtain a laminate 4. Bonding rolls (nip rolls) 51 and 52 for the above, a roll 13 for bringing the polarizing film 1 and the transparent film 2 into close contact with each other in the laminated body 4, and a first installed at a position facing the outer peripheral surface of the roll 13. Active energy ray irradiating devices 14 and 15, further second and subsequent active energy ray irradiating devices 16 to 18 installed on the downstream side in the conveying direction, and a conveying nip roll 19 are provided in order along the conveying direction. It has been.

  First, an active energy ray-curable adhesive is applied to one side of the polarizing film 1 that is continuously drawn out from a state wound in a roll shape by the adhesive application device 11 (adhesive application process).

  And the laminated body formed by laminating | stacking the polarizing film 1 with which the adhesive agent was apply | coated on the single side | surface of the transparent film 2 continuously drawn out from the state wound by roll shape via an adhesive agent is carried out. The polarizing film 2 and the transparent film 1 are bonded by pressing at least one bonding roll in the direction of the other bonding roll while being sandwiched between a pair of rotating bonding rolls 51 and 52. And the laminated body 4 is formed (bonding process).

  Next, in the process of transporting the laminate 4 in close contact with the outer peripheral surface of the roll 13, the active energy rays are irradiated from the first active energy ray irradiating devices 14, 15 toward the outer peripheral surface of the roll 13, and bonded. The agent is polymerized and cured (active energy ray irradiation step). Note that the second and subsequent active energy ray irradiation devices 16 to 18 arranged on the downstream side in the transport direction are devices for completely polymerizing and curing the adhesive, and can be added or omitted as necessary. The details of each process are the same as those in the first embodiment, and thus are omitted.

  In the manufacturing apparatus of this embodiment, since an adhesive agent can be apply | coated from the one side of the polarizing film 1, it is useful for the manufacturing method of the polarizing plate which bonds a transparent film on the single side | surface of a polarizing film. In this embodiment, since the unevenness | corrugation on the surface of a polarizing film can be coat | covered with an adhesive agent by apply | coating an adhesive agent directly on the surface of a polarizing film, generation | occurrence | production of the bubble at the time of bonding of the transparent film 2 is suppressed. Can do.

  EXAMPLES Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.

[Example 1]
In this example, a polarizing plate formed by laminating one polarizing film and one transparent film was prepared using the apparatus shown in FIG. 4 described in the fourth embodiment.

  A 40 μm thick triacetyl cellulose film “KC4CR-1” (manufactured by Konica Minolta) and a 135 μm thick composite film laminate (polyvinyl alcohol film “Vinylon VF-PS # 7500” (Kuraray) A polarizing film consisting of a cellulose ester resin film “KC4UYW” (manufactured by Konica Minolta Opto Co., Ltd.) and a surface protective film “NBO-0424” (manufactured by Fujimori Kogyo Co., Ltd.) with an adhesive layer on the KC4UYW surface. The epoxy resin composition “KR-70T” (made by ADEKA, viscosity: 44 mPa · s), which is an ultraviolet curable adhesive, is prepared on the surface of the polarizing film of the composite film laminate. The film is transported vertically upward using an adhesive coating device as shown in FIG. While coating. Under the present circumstances, the line speed of the polarizing film laminated body in an adhesive agent coating apparatus was 25 m / min, the gravure roll was rotated in the reverse direction to the conveyance direction of a laminated material, and the thickness of the adhesive bond layer was 1.0 micrometer.

  Next, the laminated body in which the triacetyl cellulose film is laminated so as to be in contact with the adhesive applied to the polarizing film is sandwiched between a pair of nip rolls (bonding rolls) having a diameter of 250 mm and pressed with a pressure of 1.0 MPa. Thus, the triacetyl cellulose film and the polarizing film were bonded together.

The laminate on which the two kinds of films are bonded is transferred at a line speed of 25 m / min while applying a tension of 600 N / m in the longitudinal direction, and the total integrated light amount (of the light irradiation intensity in the wavelength region of 280 to 320 nm). Accumulated amount) is about 250 mJ / cm ² (measuring instrument: UV manufactured by FusionUV)
Irradiation with ultraviolet rays (UVB) measured by Power Pack II was performed.

  When the obtained polarizing plate was visually observed, no bubbles were observed between the polarizing film and the triacetyl cellulose film.

[Comparative Example 1]
An epoxy resin composition, which is an ultraviolet curable adhesive, is applied to one side of a triacetyl cellulose film using an adhesive application device so as to have a thickness of 1.0 μm. A polarizing plate was produced in the same manner as in Example 1 except that it was bonded to the polarizing film of the composite film laminate.

  When the obtained polarizing plate was visually observed, bubbles were observed between the polarizing film and the triacetyl cellulose film.

  The polarizing plate of the present invention can be effectively applied to various display devices including liquid crystal display devices.

  DESCRIPTION OF SYMBOLS 1 Polarizing film, 2, 3 Transparent film, 4 Laminate (polarizing plate), 11, 12 Adhesive coating apparatus, 13 roll (cooling roll), 14, 15, 16, 17, 18 Active energy ray irradiation apparatus, 19 Transport nip roll, 20 take-up roll, 51, 52 bonding roll.

Claims (12)

A method for producing a polarizing plate in which a transparent film is bonded to one side or both sides of a polarizing film,
An adhesive coating step of applying an active energy ray-curable adhesive using a gravure roll on one or both sides of the polarizing film configured as a continuous film;
A laminate is formed by laminating the transparent film configured as a continuous film on the surface of the polarizing film that is being transported in a state where the adhesive is applied, and the laminate is formed. A laminating step of laminating the transparent film and the polarizing film by sandwiching and pressing between a pair of laminating rolls rotating in the conveying direction;
An active energy ray irradiation step of irradiating the laminate with an active energy ray to cure the adhesive; and
In the adhesive coating process, the draw ratio, which is the speed ratio of the gravure roll to the line speed of the polarizing film, is 0.5 to 10, and the active energy ray curable type is applied to one or both sides of the polarizing film. The method for producing a polarizing plate, wherein the adhesive coating thickness is 0.1 μm or more and less than 2.0 μm. A method for producing a polarizing plate in which a transparent film is bonded to one side or both sides of a polarizing film,
An adhesive coating step of applying an active energy ray-curable adhesive using a gravure roll on one or both sides of the polarizing film continuously drawn out from a rolled state,
The transparent film continuously fed from the state wound in a roll is laminated on the surface of the polarizing film on which the adhesive is applied in the state where the adhesive is applied. Forming a body, and sandwiching and pressing the laminated body between a pair of bonding rolls rotating in the transport direction, thereby bonding the transparent film and the polarizing film; and
An active energy ray irradiating step of irradiating the laminate with active energy rays to cure the adhesive;
In the adhesive coating process, the draw ratio, which is the speed ratio of the gravure roll to the line speed of the polarizing film, is 0.5 to 10, and the active energy ray curable type is applied to one or both sides of the polarizing film. The method for producing a polarizing plate, wherein the adhesive coating thickness is 0.1 μm or more and less than 2.0 μm.   The said polarizing film is a manufacturing method of the polarizing plate of Claim 1 or 2 with which the said polarizing film is conveyed at the line speed of 10-100 m / min in the said adhesive agent coating process.   Any of Claims 1-3 except the manufacturing method which has the process of heating the said adhesive agent in the said laminated body to 40 degreeC or more after the said bonding process and before the said active energy ray irradiation process. The manufacturing method of the polarizing plate of Claim 1.   The said adhesive agent coating process is a process of apply | coating an active energy ray hardening-type adhesive agent to the single side | surface or both surfaces of the said polarizing film conveyed vertically upwards, In any one of Claims 1-4. The manufacturing method of the polarizing plate of description.   The said adhesive agent coating process is a process of apply | coating an active energy ray hardening-type adhesive agent to the single side | surface or both surfaces of the said polarizing film conveyed perpendicularly | vertically downward. The manufacturing method of the polarizing plate of description. A polarizing plate manufacturing apparatus in which a transparent film is bonded to one side or both sides of a polarizing film,
An adhesive coating device for applying an active energy ray-curable adhesive on one side or both sides of the polarizing film configured as a continuous film using a gravure roll ;
The laminated body obtained by laminating the transparent film configured as a continuous film on the surface of the polarizing film on which the adhesive is applied is transported in a state where the adhesive is applied. A pair of laminating rolls for laminating the transparent film and the polarizing film by clamping while
An active energy ray irradiation device for irradiating the laminate with active energy rays to cure the adhesive;
In the adhesive coating apparatus , a draw ratio, which is a speed ratio of the gravure roll to a line speed of the polarizing film, is set to 0.5 to 10, and the adhesive is applied to one or both sides of the polarizing film by 0.1 μm or more 2 A polarizing plate manufacturing apparatus for coating with a coating thickness of less than 0.0 μm. A polarizing plate manufacturing apparatus in which a transparent film is bonded to one side or both sides of a polarizing film,
An adhesive coating device for applying an active energy ray-curable adhesive on one or both sides of the polarizing film continuously drawn out from a state wound in a roll using a gravure roll ;
Obtained by laminating the transparent film continuously drawn from the rolled state on the surface of the polarizing film on which the adhesive is applied in the state where the adhesive is applied. A pair of laminating rolls for laminating the transparent film and the polarizing film by sandwiching the resulting laminate while transporting,
An active energy ray irradiation device for irradiating the laminate with active energy rays to cure the adhesive;
In the adhesive coating apparatus , a draw ratio, which is a speed ratio of the gravure roll to a line speed of the polarizing film, is set to 0.5 to 10, and the adhesive is applied to one or both sides of the polarizing film by 0.1 μm or more 2 A polarizing plate manufacturing apparatus for coating with a coating thickness of less than 0.0 μm. A transport means for transporting the polarizing film at a line speed of 10 to 100 m / min;
The said adhesive agent coating apparatus is a manufacturing apparatus of the polarizing plate of Claim 7 or 8 which apply | coats the said adhesive agent to the single side | surface or both surfaces of the said polarizing film currently conveyed with the line speed of 10-100 m / min.   The manufacturing apparatus which has a heating lamp which heats the said adhesive agent in the said laminated body to 40 degreeC or more in the path | route between the said bonding roll and the said active energy ray irradiation apparatus is excluded. The manufacturing apparatus of the polarizing plate of any one of these. A transport means for transporting the polarizing film vertically upward;
The said adhesive agent coating apparatus apply | coats an active energy ray hardening-type adhesive agent to the single side | surface or both surfaces of the said polarizing film currently conveyed perpendicularly | vertically upward. Polarizer manufacturing equipment. A transport means for transporting the polarizing film vertically downward;
The said adhesive agent coating apparatus apply | coats an active energy ray hardening-type adhesive agent to the single side | surface or both surfaces of the said polarizing film currently conveyed perpendicularly | vertically downward. Polarizer manufacturing equipment.