JP6484571B2 - Processing method of polarizing plate - Google Patents
Processing method of polarizing plate Download PDFInfo
- Publication number
- JP6484571B2 JP6484571B2 JP2016026756A JP2016026756A JP6484571B2 JP 6484571 B2 JP6484571 B2 JP 6484571B2 JP 2016026756 A JP2016026756 A JP 2016026756A JP 2016026756 A JP2016026756 A JP 2016026756A JP 6484571 B2 JP6484571 B2 JP 6484571B2
- Authority
- JP
- Japan
- Prior art keywords
- polarizing plate
- shape
- elliptical
- adhesive layer
- weak adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、入射光を偏光方向に応じて透過光と反射光とに分離する偏光板の加工方法に関する。 The present invention relates to a method of processing a polarizing plate that separates incident light into transmitted light and reflected light according to the polarization direction.
近年、液晶表示装置等では、薄型の偏光板としてポリビニルアルコール(PVA)フィルムにヨウ素化合物を吸着しこれを延伸配向させて可視光の吸収二色性を発現させた偏光フィルムが多く用いられている(例えば、特許文献1)。 In recent years, in a liquid crystal display device or the like, as a thin polarizing plate, a polarizing film in which an iodine compound is adsorbed on a polyvinyl alcohol (PVA) film and stretched and oriented to develop visible light dichroism is often used. (For example, patent document 1).
しかしながら、上記のような偏光板は、延伸性を有するため、当該偏光板(特に、内側部分)を、切断刃等を用いて所定形状に加工しようとすると、その偏光板が延伸方向に延び、もって、偏光板の延伸方向にクラックが発生してしまう可能性があるという問題があった。 However, since the polarizing plate as described above has stretchability, when the polarizing plate (particularly the inner portion) is processed into a predetermined shape using a cutting blade or the like, the polarizing plate extends in the stretching direction, Accordingly, there is a problem that cracks may occur in the stretching direction of the polarizing plate.
そこで、本発明は、上記問題に鑑み、偏光板を加工するにあたって、クラックの発生を低減させることができる偏光板の加工方法を提供することを目的としている。 In view of the above problems, an object of the present invention is to provide a method for processing a polarizing plate that can reduce the occurrence of cracks when processing the polarizing plate.
上記本発明の目的は、以下の手段によって達成される。なお、括弧内は、後述する実施形態の参照符号を付したものであるが、本発明はこれに限定されるものではない。 The object of the present invention is achieved by the following means. In addition, although the code | symbol in a parenthesis attaches the referential mark of embodiment mentioned later, this invention is not limited to this.
請求項1の偏光板の加工方法によれば、粘着力を有すると共に、内側部分が所定形状に加工され第1形状部(楕円形状部2a)を有する支持部材(弱粘着層2)に偏光板(1)を載置する工程(図2(b)参照)と、
前記支持部材(弱粘着層2)に載置された偏光板(1)の内側部分が第2形状部(楕円形状部1a)を有するように該偏光板(1)の内側部分を所定形状に加工する工程(図2(c)参照)と、
前記支持部材(弱粘着層2)の第1形状部(楕円形状部2a)及び前記偏光板(1)の第2形状部(楕円形状部1a)を、突き落とし部材(突き落とし棒TB)を用いて鉛直下向きに突き落とす工程(図3(b)参照)と、を含んでなることを特徴としている。
According to the processing method of the polarizing plate of
The inner part of the polarizing plate (1) is shaped into a predetermined shape so that the inner part of the polarizing plate (1) placed on the support member (weak adhesive layer 2) has a second shape part (elliptical part 1a). A processing step (see FIG. 2C);
The first shape portion (elliptical shape portion 2a) of the support member (weak adhesive layer 2) and the second shape portion (elliptical shape portion 1a) of the polarizing plate (1) are dropped using a drop-off member (drop-off rod TB). And a step of pushing down vertically (see FIG. 3B).
また、請求項2の発明によれば、上記請求項1に記載の偏光板の加工方法において、前記偏光板(1)の内側部分が第2形状部(楕円形状部1a)を有するように所定形状に加工するにあたって、前記支持部材(弱粘着層2)が切断されないように前記偏光板(1)の内側部分を切断してなることを特徴としている。
Further, according to the invention of
さらに、請求項3の発明によれば、上記請求項1又は2に記載の偏光板の加工方法において、前記偏光板(1)の第2形状部(楕円形状部1a)の径は、前記支持部材(弱粘着層2)の第1形状部(楕円形状部2a)の径よりも径小であり、
前記突き落とし部材(突き落とし棒TB)の径は、前記偏光板(1)の第2形状部(楕円形状部1a)の径よりも径小であることを特徴としている。
Furthermore, according to invention of Claim 3, in the processing method of the polarizing plate of the said
A diameter of the drop-off member (drop-off rod TB) is smaller than a diameter of the second shape portion (elliptical shape portion 1a) of the polarizing plate (1).
そして、請求項4の発明によれば、上記請求項1〜3の何れか1項に記載の偏光板の加工方法において、前記突き落とし部材(突き落とし棒TB)を用いて鉛直下向き(図3(a)の矢印Y1方向参照)に突き落とされた前記支持部材(弱粘着層2)の第1形状部(楕円形状部2a)及び前記偏光板(1)の第2形状部(楕円形状部1a)は、当該突き落とし部材(突き落とし棒TB)が挿抜可能な孔(Da)が形成された収納部材(金型D)の孔(Da)内に収納されてなることを特徴としている。 And according to invention of Claim 4, in the processing method of the polarizing plate of any one of the said Claims 1-3, it uses vertically downward (FIG. 3 (a) using the said dropping member (push-off stick TB). ) (See the direction of arrow Y1) of the support member (weak adhesive layer 2) and the second shape part (elliptical part 1a) of the polarizing plate (1) and the first shape part (elliptical part 2a) of the polarizing plate (1). The push-off member (push-off rod TB) is housed in a hole (Da) of a storage member (mold D) in which a hole (Da) into which the push-out member (push-off rod TB) can be inserted and removed is formed.
次に、本発明の効果について、図面の参照符号を付して説明する。なお、括弧内は、後述する実施形態の参照符号を付したものであるが、本発明はこれに限定されるものではない。 Next, effects of the present invention will be described with reference numerals in the drawings. In addition, although the code | symbol in a parenthesis attaches the referential mark of embodiment mentioned later, this invention is not limited to this.
請求項1の発明によれば、偏光板(1)の下面に支持部材(弱粘着層2)が配置されているから、偏光板(1)の内側部分を所定形状に加工した際、支持部材(弱粘着層2)によって、偏光板(1)の延伸方向の伸びが防止され、もって、クラックの発生を低減させることができる。そしてさらに、その状態で、突き落とし部材(突き落とし棒TB)を用いて偏光板(1)の内側部分に形成されている第2形状部(楕円形状部1a)及び支持部材(弱粘着層2)の内側部分に形成されている第1形状部(楕円形状部2a)を鉛直下向きに突き落とすことにより、偏光板(1)の内側部分に形成されている第2形状部(楕円形状部1a)にのみその力が加わり、偏光板(1)の第2形状部(楕円形状部1a)以外の偏光板(1)の部分にその力が加わることがないため、もって、偏光板(1)の第2形状部(楕円形状部1a)以外の偏光板(1)の部分の延伸方向の伸びを防止することができる。これにより、クラックの発生を低減させつつ、偏光板を加工することができる。
According to the invention of
また、請求項2の発明によれば、偏光板(1)の内側部分が第2形状部(楕円形状部1a)を有するように所定形状に加工するにあたって、支持部材(弱粘着層2)が切断されないように偏光板(1)の内側部分を切断しているため、偏光板(1)の延伸方向の伸びをより一層防止し、もって、クラックが発生する事態をさらに低減させることができる。
According to the invention of
さらに、請求項3の発明によれば、偏光板(1)の第2形状部(楕円形状部1a)の径は、支持部材(弱粘着層2)の第1形状部(楕円形状部2a)の径よりも径小であり、突き落とし部材(突き落とし棒TB)の径は、偏光板(1)の第2形状部(楕円形状部1a)の径よりも径小であるから、突き落とし部材(突き落とし棒TB)によって、偏光板(1)の内側部分に形成されている第2形状部(楕円形状部1a)を偏光板(1)より容易に分離することができ、さらに、支持部材(弱粘着層2)の内側部分に形成されている第1形状部(楕円形状部2a)を支持部材(弱粘着層2)より容易に分離することができる。 Furthermore, according to invention of Claim 3, the diameter of the 2nd shape part (elliptical shape part 1a) of a polarizing plate (1) is the 1st shape part (elliptical shape part 2a) of a supporting member (weak adhesion layer 2). Since the diameter of the drop-off member (drop-off rod TB) is smaller than the diameter of the second shape portion (elliptical portion 1a) of the polarizing plate (1), the drop-off member (drop-off) The second shape portion (elliptical shape portion 1a) formed on the inner part of the polarizing plate (1) can be easily separated from the polarizing plate (1) by the rod TB), and further, the supporting member (weak adhesion) The first shape portion (elliptical shape portion 2a) formed in the inner portion of the layer 2) can be easily separated from the support member (weak adhesion layer 2).
そして、請求項4の発明によれば、突き落とし部材(突き落とし棒TB)を用いて鉛直下向き(図3(a)の矢印Y1方向参照)に突き落とされた支持部材(弱粘着層2)の第1形状部(楕円形状部2a)及び偏光板(1)の第2形状部(楕円形状部1a)は、当該突き落とし部材(突き落とし棒TB)が挿抜可能な孔(Da)が形成された収納部材(金型D)の孔(Da)内に収納されているから、廃棄物を一箇所に貯めることができ、もって、廃棄物を簡単容易に破棄することができる。 According to the invention of claim 4, the first of the support member (weakly adhesive layer 2) pushed down vertically (see the direction of arrow Y <b> 1 in FIG. 3A) using the drop-off member (drop-off rod TB). The shape part (elliptical part 2a) and the second shape part (elliptical part 1a) of the polarizing plate (1) are storage members (holes Da) into which the drop-off member (drop-off rod TB) can be inserted and removed ( Since it is stored in the hole (Da) of the mold D), the waste can be stored in one place, and the waste can be easily and easily discarded.
以下、本発明に係る偏光板の加工方法の一実施形態を、図1〜図3を参照して具体的に説明する。なお、以下の説明において、上下左右の方向を示す場合は、図示正面から見た場合の上下左右をいうものとする。 Hereinafter, an embodiment of a method for processing a polarizing plate according to the present invention will be described in detail with reference to FIGS. In addition, in the following description, when showing the direction of up, down, left and right, it means up, down, left and right when viewed from the front of the figure.
まず、本実施形態に係る偏光板について説明する。 First, the polarizing plate according to this embodiment will be described.
偏光板1は、入射光を偏光方向に応じて透過光と反射光とに分離することができるもので、図1(a)に示すように、平面視矩形状に形成されている。この偏光板1は、図2(a)に示すように、長尺状のベースセパレータ10と、このベースセパレータ10上に配置されている粘着剤11と、この粘着剤11上に配置されているトリアセチルセルロースフィルム(TACフィルム)12と、偏光子13と、TACフィルム14と、位相差フィルム15と、保護フィルム16とで構成されている。
The polarizing
ベースセパレータ10は、厚み約40μmで形成されており、フッ素系ポリマー(例えば、ポリテトラフルオロエチレン、ポリクロロトリフルオロエチレン、ポリフッ化ビニル、ポリフッ化ビニリデン、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体、クロロフルオロエチレン−フッ化ビニリデン共重合体等)からなる低接着性基材、無極性ポリマー(例えば、ポリエチレン、ポリプロピレン等のオレフィン系樹脂など)からなる低接着性基材等で形成されている。
The
一方、粘着剤11は、厚み約25μmで形成されており、例えばアクリル系重合体、シリコーン系ポリマー、ポリエステル、ポリウレタン、ポリアミド、ポリエーテル、フッ素系やゴム系等のポリマーをベースポリマーとするものを適宜に選択して用いることができるもので形成されている。
On the other hand, the pressure-
また、TACフィルム12,14は、厚み約40μmで形成されており、トリアセチルセルロース(TAC)を主成分として含有するトリアセチルセルロース系樹脂フィルムにて形成されている。
The
そして、偏光子13は、無偏光(自然光)、部分偏光、又は、偏光から特定方向にのみ振動する偏光(直線偏光)を取り出す機能を有するもので、厚み約20μmで形成されており、ポリビニルアルコールあるいはエチレン単位の含有量1〜4モル%、重合度2000〜4000、ケン化度99.0〜99.99モル%であるエチレン変性ポリビニルアルコールの如き親水性ポリマーからなるフィルムを、ヨウ素の如き二色性染料で処理して延伸したものや、塩化ビニルの如きプラスチックフィルムを処理して配向させたもので形成されている。
The
他方、位相差フィルム15は、位相差調整機能を有するもので、厚み約70μmで形成されており、トリアセチルセルロース(TAC)等のセルロース系樹脂や、ポリエステル系、ポリカーボネート系、ノルボルネン系、ポリアミド系、ポリイミド系、ポリエーテルスルホン系、ポリスルホン系、ポリスチレン系、アクリル系、アセテート系、ポリオレフィン系等の樹脂等のポリマーフィルムを延伸処理した複屈折性フィルム、液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムで支持した積層体等で形成されている。なお、この位相差フィルム15は、偏光子13との接着性を上げるため、例えば、その表面が、アルカリ等によってケン化処理されてもよく、あるいは、表面に適切なプライマー処理を行ってもよい。
On the other hand, the
また、保護フィルム16は、偏光子13が収縮や膨張することを防いだり、紫外線による劣化を防いだりする機能を有するもので、厚み約60μmで形成されており、透明性、機械的強度、熱安定性、水分遮蔽性、位相差値の安定性などに優れる熱可塑性樹脂で形成されている。このような保護フィルム16を構成する熱可塑性樹脂としては、例えば、メタクリル酸メチル系樹脂を代表例とする(メタ)アクリル系樹脂、ポリプロピレン系樹脂を代表例とするポリオレフィン系樹脂、環状オレフィン系樹脂、ポリ塩化ビニル系樹脂、セルロース系樹脂、スチレン系樹脂、アクリロニトリル・ブタジエン・スチレン系樹脂、アクリロニトリル・スチレン系樹脂、ポリ酢酸ビニル系樹脂、ポリ塩化ビニリデン系樹脂、ポリアミド系樹脂、ポリアセタール系樹脂、ポリカーボネート系樹脂、変性ポリフェニレンエーテル系樹脂、ポリエチレンテレフタレート系樹脂、ポリブチレンテフタレート系樹脂、ポリスルホン系樹脂、ポリエーテルスルホン系樹脂、ポリアリレート系樹脂、ポリアミドイミド系樹脂、ポリイミド系樹脂などが挙げられる。
The
かくして、上記のように構成される偏光板1は、以下のように加工される。
Thus, the
すなわち、上記偏光板1を加工、すなわち、その偏光板1の内側部分に所望の形状を形成するにあたって、まず、図1(b),図2(b)に示すように、弱粘着層2の上面に偏光板1を載置する。この弱粘着層2は、厚み約40μmで形成され、剥離可能及び/又は再粘着可能な弱粘着剤を含んで形成されており、弱粘着剤としては、例えばゴム系粘着剤、アクリル系粘着剤、シリコーン系粘着剤、ポリビニール系粘着剤、ポリウレタン系粘着剤、及びそれらの何れかの複合材料が挙げられる。
That is, when the
かくして、上記のように構成される弱粘着層2は、偏光板1の内側部分を、後述する切断刃K(図2(c)参照)を用いて切断する際、偏光板1の延伸方向の伸びを防止するもので、図1(b),図2(b)に示すように、弱粘着層2の内側部分に予め中心線O1を基点とする楕円形状部2aが形成されている。この楕円形状部2aは、例えば、直径約2.4mmからなるもので、後述する突き落とし棒TB(図2参照)で鉛直下向きに突き落とされる、すなわち、弱粘着層2からこの楕円形状部2aの部分だけが、鉛直下向きに突き落とされるように、予め、切断刃あるいはレーザー等によって弱粘着層2の内側部分に予め加工されている。
Thus, when the weak
次いで、弱粘着層2の上面に偏光板1を載置した(図1(b),図2(b)参照)後、図2(c)に示すように、偏光板1の内側部分を、切断刃Kを用いて所望の形状に切断する。すなわち、偏光板1の内側部分に、例えば、直径約2.0mmからなる中心線O2を基点とする楕円形状部1aが形成されるように、図2(c)に示すように、切断刃Kを用いて偏光板1の内側部分を切断する。この際、偏光板1(ベースセパレータ10)の下面に弱粘着層2が配置されているから、偏光板1の内側部分を切断した際、弱粘着層2によって、偏光板1の延伸方向の伸びが防止され、もって、クラックの発生を低減させることができる。なお、切断刃Kを用いて偏光板1の内側部分を切断するにあたって、図2(c)に示すように、切断刃Kを用いて偏光板1の内側部分を完全に切断し、弱粘着層2自体は切断しないか、あるいは、僅かに切断し完全に切断しない方が好ましい。弱粘着層2自体を完全に切断してしまうと、偏光板1の延伸方向の伸びの防止が低減し、もって、クラックが発生する可能性があるためである。それゆえ、弱粘着層2自体は完全に切断しない方が好ましい。なおまた、図2(c)に示すように、偏光板1の内側部分に形成されている楕円形状部1aの基点である中心線O2と、弱粘着層2の内側部分に形成されている楕円形状部2aの基点である中心線O1とは、同一線上となっている。
Next, after placing the
次いで、偏光板1の内側部分を、切断刃Kを用いて所望の形状に切断した後、図3に示すように、突き落とし棒TBを用いて、偏光板1の内側部分に形成されている楕円形状部1a及び弱粘着層2の内側部分に形成されている楕円形状部2aを鉛直下向きに突き落とす。具体的に説明すると、この突き落とし棒TBは、直径約1.6mmからなる円柱状の棒であり、上下動(鉛直上向き、鉛直下向きへ動作)できるようになっている。そしてこのような突き落とし棒TBを、図3(a)に示すように、偏光板1の内側部分に形成されている楕円形状部1a及び弱粘着層2の内側部分に形成されている楕円形状部2aを鉛直下向きに突き落とすように、偏光板1の上側から下側(矢印Y1方向)へ移動させると、図3(b)に示すように、突き落とし棒TBによって、偏光板1の内側部分に形成されている楕円形状部1aが偏光板1より分離し、さらに、弱粘着層2の内側部分に形成されている楕円形状部2aが弱粘着層2より分離し、もって、楕円形状部1a及び楕円形状部2aが鉛直下向きに突き落とされることとなる。そしてその後、突き落とし棒TBを下側(矢印Y1方向)から上側(矢印Y1方向と反対方向)へ移動させると、図1(c)(図3(b)も参照)に示すように、偏光板1の内側部分に楕円形状からなる貫通孔1a1(弱粘着層2の内側にも楕円形状からなる貫通孔2a1)が形成され、もって、偏光板1の内側に所望の形状が形成されることとなる。この際、突き落とし棒TBによって、偏光板1の内側部分に形成されている楕円形状部1aが偏光板1より容易に分離し、さらに、弱粘着層2の内側部分に形成されている楕円形状部2aが弱粘着層2より容易に分離できるように、偏光板1の内側部分に形成されている楕円形状部1aの径を弱粘着層2の内側部分に形成されている楕円形状部2aの径よりも径小にし、さらに、突き落とし棒TBの径を偏光板1の内側部分に形成されている楕円形状部1aの径よりも径小にしている。これにより、突き落とし棒TBによって、偏光板1の内側部分に形成されている楕円形状部1aが偏光板1より容易に分離でき、さらに、弱粘着層2の内側部分に形成されている楕円形状部2aが弱粘着層2より容易に分離できることとなる。そしてさらに、偏光板1の内側部分に形成されている楕円形状部1aが偏光板1よりさらに容易に分離し、弱粘着層2の内側部分に形成されている楕円形状部2aが弱粘着層2よりさらに容易に分離できるように、図3(a)に示すように、突き落とし棒TBの軸線O3と、偏光板1の内側部分に形成されている楕円形状部1aの基点である中心線O2と、弱粘着層2の内側部分に形成されている楕円形状部2aの基点である中心線O1とが同一線上となるようにしている。このようにすれば、偏光板1の内側部分に形成されている楕円形状部1aが偏光板1よりさらに容易に分離でき、弱粘着層2の内側部分に形成されている楕円形状部2aが弱粘着層2よりさらに容易に分離できることとなる。
Next, after the inner portion of the
ところで、突き落とし棒TBによって、鉛直下向きに突き落とされた偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aは、図3(b)に示すように、直径約2.4mmの孔Daが形成された金型D内に収納される。すなわち、突き落とし棒TBによって、偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aを鉛直下向きに突き落とした際、そのまま、図3(b)に示すように、突き落とし棒TBを金型Dの孔Da内に突入させる。これにより、金型Dの孔Da内の矢印Y2方向に偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aが押し込まれることとなる。そしてその後、突き落とし棒TBを金型Dの孔Da内から抜出(下側(矢印Y1方向)から上側(矢印Y1方向と反対方向)へ移動)させると、金型Dの孔Da内に、偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aが収納されることとなる。これにより、偏光板1より分離された偏光板1の楕円形状部1a及び弱粘着層2より分離された弱粘着層2の楕円形状部2aの廃棄物を一箇所に貯めることができ、もって、廃棄物を簡単容易に破棄することができる。なお、突き落とし棒TBによって、鉛直下向きに突き落とされた偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aは、図3(b)に示すように、金型Dの孔Da内に下から上に順に積層(図3(b)に示す破線部分が前回突き落とされた偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aを示し、図3(b)に示す実線部分が今回突き落とされた偏光板1の楕円形状部1a及び弱粘着層2の楕円形状部2aを示す)されることとなる。
By the way, the elliptical part 1a of the
かくして、上記のような工程を経て、偏光板1は、所望の形状に加工されこととなる。
Thus, the
しかして、以上説明した本実施形態によれば、偏光板1(ベースセパレータ10)の下面に弱粘着層2が配置されているから、偏光板1の内側部分を切断した際、弱粘着層2によって、偏光板1の延伸方向の伸びが防止され、もって、クラックの発生を低減させることができる。そしてさらに、その状態で、突き落とし棒TBを用いて、偏光板1の内側部分に形成されている楕円形状部1a及び弱粘着層2の楕円形状部2aを鉛直下向きに突き落とすことにより、偏光板1の内側部分に形成されている楕円形状部1aにのみその力が加わり、偏光板1の楕円形状部1a以外の偏光板1の部分にその力が加わることがないため、もって、偏光板1の楕円形状部1a以外の偏光板1の部分の延伸方向の伸びを防止することができる。これにより、クラックの発生を低減させつつ、偏光板を加工することができる。
Thus, according to the present embodiment described above, the weak
なお、本実施形態にて例示した偏光板は、あくまで一例であり、どのような偏光板にも適用可能である。例えば、位相差フィルム15が存しない偏光板でも良いし、輝度向上フィルムが存する偏光板でも良い。
In addition, the polarizing plate illustrated in this embodiment is an example to the last, and can be applied to any polarizing plate. For example, a polarizing plate without the
また、本実施形態においては、弱粘着層2の楕円形状部2aは、偏光板1の内側部分に形成する所望の形状(本実施形態においては、楕円形状部1a)と同一の形状にする例を示したが、それに限らず、矩形状とする等、偏光板1の内側部分に形成する所望の形状と同一の形状にしなくとも良い。
Moreover, in this embodiment, the elliptical shape part 2a of the
さらに、本実施形態においては、突き落とし棒TBを円柱状にする例を示したが、それに限らず、どのような形状でも良い。 Furthermore, in the present embodiment, an example in which the push-off rod TB is formed in a columnar shape is shown, but the present invention is not limited thereto, and any shape may be used.
1 偏光板
1a 楕円形状部(第2形状部)
2 弱粘着層(支持部材)
2a 楕円形状部(第1形状部)
TB 突き落とし棒(突き落とし部材)
D 金型(収納部材)
Da 孔
1 Polarizing plate 1a Elliptical part (second shape part)
2 Weak adhesive layer (support member)
2a Elliptical part (first shape part)
TB Sticking stick (sticking member)
D Mold (Storage material)
Da hole
Claims (4)
前記支持部材に載置された偏光板の内側部分が第2形状部を有するように該偏光板の内側部分を所定形状に加工する工程と、
前記支持部材の第1形状部及び前記偏光板の第2形状部を、突き落とし部材を用いて鉛直下向きに突き落とす工程と、を含んでなる偏光板の加工方法。 A step of placing the polarizing plate on a support member having an adhesive force and an inner portion processed into a predetermined shape and having a first shape portion;
Processing the inner part of the polarizing plate into a predetermined shape such that the inner part of the polarizing plate placed on the support member has a second shape part; and
And a step of pushing down the first shape portion of the support member and the second shape portion of the polarizing plate vertically downward using a dropping member.
前記突き落とし部材の径は、前記偏光板の第2形状部の径よりも径小である請求項1又は2に記載の偏光板の加工方法。 The diameter of the second shape portion of the polarizing plate is smaller than the diameter of the first shape portion of the support member,
3. The method for processing a polarizing plate according to claim 1, wherein a diameter of the sticking member is smaller than a diameter of the second shape portion of the polarizing plate.
The first shape part of the support member and the second shape part of the polarizing plate, which are pushed down vertically using the push-down member, are stored in the holes of the storage member in which holes through which the drop-off member can be inserted and removed are formed. The processing method of the polarizing plate of any one of Claims 1-3 formed.