JP6460472B2 - Lining material - Google Patents
Lining material Download PDFInfo
- Publication number
- JP6460472B2 JP6460472B2 JP2015054101A JP2015054101A JP6460472B2 JP 6460472 B2 JP6460472 B2 JP 6460472B2 JP 2015054101 A JP2015054101 A JP 2015054101A JP 2015054101 A JP2015054101 A JP 2015054101A JP 6460472 B2 JP6460472 B2 JP 6460472B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- layer
- elastomer layer
- lining material
- elastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、ライニングの対象となる搬送ライン壁面や配管部材、タンク、ホッパー等に貼付けて使用されるライニング材に関する。 The present invention relates to a lining material that is used by being attached to a conveyance line wall surface, piping member, tank, hopper, or the like to be a lining object.
従来、タンク、ホッパー等の比較的大型な対象物の内面にライニング材を貼付ける場合、ハンドローラ等にて未加硫のゴムからなるライニング材をタンク等の被処理面に圧着し、圧着されたライニング材を加硫させて、被処理面に対して接着していた（特許文献１参照）。 Conventionally, when a lining material is affixed to the inner surface of a relatively large object such as a tank or a hopper, the lining material made of unvulcanized rubber is pressed against the surface to be treated such as a tank with a hand roller. The lining material was vulcanized and adhered to the surface to be treated (see Patent Document 1).
しかし、上記のようなライニング方法では、被処理面に対して予めショットブラスト等の研磨処理や、接着力を向上させるためのプライマー処理、接着剤を塗布する接着剤処理等を行う必要があった。また、接着作業も少しずつしか行うことができなかったため、非常に手間がかかっていた。さらに、被処理面に対して貼付けられたライニング材を交換する際に、接着を剥がすことが困難であった。 However, in the lining method as described above, it is necessary to previously perform a polishing process such as shot blasting, a primer process for improving the adhesive force, an adhesive process for applying an adhesive, and the like on the surface to be processed. . Also, since the bonding work could only be performed little by little, it was very time consuming. Furthermore, when replacing the lining material affixed to the surface to be treated, it has been difficult to remove the adhesion.
そこで本発明は、被処理面に対する貼付け及び交換を容易にするライニング材の提供を目的とする。 Then, an object of this invention is to provide the lining material which makes easy the sticking and replacement | exchange with respect to a to-be-processed surface.
本発明の一観点によれば、樹脂からなる樹脂層と、エラストマーに磁性体を添加した磁性エラストマー層と、を有し、一面側に前記樹脂層を、他面側に前記磁性エラストマー層を設けたライニング材が提供される。 According to one aspect of the present invention, there is provided a resin layer made of a resin and a magnetic elastomer layer obtained by adding a magnetic material to an elastomer, and the resin layer is provided on one side and the magnetic elastomer layer is provided on the other side. Lining material is provided.
本発明に係るライニング材によれば、被処理面に対する貼付け及び交換を容易にすることが可能となる。 According to the lining material according to the present invention, it is possible to facilitate the pasting and replacement on the surface to be processed.
［第１の実施の形態］
図１を参照して、本発明の第１の実施の形態に係るライニング材１について説明する。図１は、第１の実施の形態に係るライニング材１をライニング対象２に貼付けたときの概略構造を示す断面図である。
[First Embodiment]
With reference to FIG. 1, the lining material 1 which concerns on the 1st Embodiment of this invention is demonstrated. FIG. 1 is a cross-sectional view showing a schematic structure when the lining material 1 according to the first embodiment is attached to a lining object 2.
まず、ライニング材１の全体的な構造について説明する。ライニング材１は、配管部材やタンク等のライニング対象２の被処理面２００に貼付けることにより、被処理面２００への内容物の居付きや、腐食、摩耗を防ぐものである。 First, the overall structure of the lining material 1 will be described. The lining material 1 is attached to the surface to be processed 200 of the lining object 2 such as a piping member or a tank to prevent the contents from being attached to the surface to be processed 200, corrosion, and wear.
被処理面２００は、磁性体が着磁する金属等からなる。 The surface to be processed 200 is made of a metal or the like on which a magnetic material is magnetized.
ライニング材１は、樹脂からなる樹脂層１０と、エラストマーに磁性体を添加した磁性エラストマー層１１とを含んで構成されている。一面側には樹脂層１０が、他面側には磁性エラストマー層１１が設けられ、樹脂層１０と磁性エラストマー層１１とは接着されている。ライニング材１は、磁性エラストマー層１１上に樹脂層１０が積層された構造ということもできる。 The lining material 1 includes a resin layer 10 made of a resin and a magnetic elastomer layer 11 obtained by adding a magnetic material to an elastomer. A resin layer 10 is provided on one side and a magnetic elastomer layer 11 is provided on the other side, and the resin layer 10 and the magnetic elastomer layer 11 are bonded. It can also be said that the lining material 1 has a structure in which the resin layer 10 is laminated on the magnetic elastomer layer 11.
ライニング対象２の被処理面２００は、金属からなる。ライニング材１がライニング対象物２に貼付けられる際には、磁性エラストマー層１１の他面側が貼付け面１０１として被処理面２００に対して貼付けられ、樹脂層１０の表面１００が外面となる。磁性エラストマー層１１は、磁性体が添加されているため、磁力によって被処理面２００に対して固定される。 The to-be-processed surface 200 of the lining object 2 is made of metal. When the lining material 1 is affixed to the lining object 2, the other surface side of the magnetic elastomer layer 11 is affixed to the surface to be treated 200 as the affixing surface 101, and the surface 100 of the resin layer 10 becomes the outer surface. Since the magnetic substance is added to the magnetic elastomer layer 11, the magnetic elastomer layer 11 is fixed to the surface to be processed 200 by a magnetic force.
ライニング材１の形状は、ライニング対象２の被処理面２００の形状に応じて適宜選択することができる。例えば、図１では、ライニング対象２の被処理面２００を平板状に例示しているが、被処理面２００が曲面である場合には、ライニング材１も被処理面２００の形状に沿うように変形させて用いられる。 The shape of the lining material 1 can be appropriately selected according to the shape of the processing target surface 200 of the lining object 2. For example, in FIG. 1, the processing target surface 200 of the lining object 2 is illustrated as a flat plate. However, when the processing target surface 200 is a curved surface, the lining material 1 also follows the shape of the processing target surface 200. Used by deforming.
次に、樹脂層１０及び磁性エラストマー層１１の材料等について説明する。 Next, materials for the resin layer 10 and the magnetic elastomer layer 11 will be described.
樹脂層１０の材料としては、例えば、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）、フッ素樹脂等の熱可塑性樹脂や、フェノール樹脂等の熱硬化性樹脂を用いることができる。これらをブレンドしたものを用いてもよい。また、樹脂層１０の材料として、摩擦係数が低く、耐薬品性、耐溶剤性、耐油性、耐摩耗性に優れた材料を用いることが好ましい。このような観点から樹脂層１０の材料として、特に超高分子量ポリエチレン、ふっ素樹脂、ポリプロピレンが好ましい。樹脂層１０の厚みは、例えば、１ｍｍ〜１５ｍｍである。 As a material of the resin layer 10, for example, a thermoplastic resin such as polyethylene (PE), polypropylene (PP), or a fluororesin, or a thermosetting resin such as a phenol resin can be used. You may use what blended these. Further, as the material of the resin layer 10, it is preferable to use a material having a low coefficient of friction and excellent chemical resistance, solvent resistance, oil resistance, and wear resistance. From this point of view, as the material of the resin layer 10, ultra high molecular weight polyethylene, fluorine resin, and polypropylene are particularly preferable. The thickness of the resin layer 10 is, for example, 1 mm to 15 mm.
磁性エラストマー層１１は、エラストマーに磁性体を添加したものからなる。該エラストマーの材料としては、例えば、ＥＰＤＭ（エチレン・プロピレン・ジエンゴム）等のゴム材料や、熱可塑性エラストマーが用いられる。該磁性体の材料としては、例えば、粉状のフェライト等が用いられる。エラストマー及び磁性体は、それぞれが複数の材料をブレンドしたものを用いても良い。磁性エラストマー層１１において、磁性体は、エラストマー１００質量部に対して５０質量部〜５００質量部添加される。磁性エラストマー層１１の厚みは、例えば、１ｍｍ〜１０ｍｍである。 The magnetic elastomer layer 11 is formed by adding a magnetic material to an elastomer. Examples of the elastomer material include rubber materials such as EPDM (ethylene / propylene / diene rubber), and thermoplastic elastomers. As the magnetic material, for example, powdery ferrite or the like is used. As the elastomer and the magnetic material, those obtained by blending a plurality of materials may be used. In the magnetic elastomer layer 11, 50 mass parts-500 mass parts of magnetic bodies are added with respect to 100 mass parts of elastomers. The thickness of the magnetic elastomer layer 11 is, for example, 1 mm to 10 mm.
樹脂層１０と磁性エラストマー層１１とは、互いに対向する接着面１０２において、例えば、接着剤や粘着剤によって固定される。接着剤としては、例えば、弾性接着剤が用いられる。粘着剤としては、例えば、ブチルゴム系粘着剤が用いられる。樹脂層１０と磁性エラストマー層１１とは、剥がれを防止する観点から２Ｎ／ｍｍ以上の力で接着される。 The resin layer 10 and the magnetic elastomer layer 11 are fixed by, for example, an adhesive or a pressure-sensitive adhesive on the adhesive surface 102 facing each other. For example, an elastic adhesive is used as the adhesive. As the adhesive, for example, a butyl rubber adhesive is used. The resin layer 10 and the magnetic elastomer layer 11 are bonded with a force of 2 N / mm or more from the viewpoint of preventing peeling.
従来のライニング材を被処理面に張付ける際には、予め、被処理面を清掃する工程、接着剤を塗布する工程、接着剤を乾燥させる工程が必要となっており、ライニング材を被処理面に対して貼付けた後も、数日間の養生期間が必要であり、養生期間中は、ライニング対象を使用することができなかった。本実施の形態では、ライニング材１がエラストマーに磁性体を添加した磁性エラストマー層１１を貼付け面１０１（他面）側に有する。ライニング対象２の被処理面２００が平滑な表面で汚れや異物の付着がない状態であれば、被処理面２００を予めプライマー処理、接着剤を塗布する接着剤処理等を行うことなく、ライニング材１を磁力によって貼付けることができる。よって、ライニング材１をライニング対象２に対して、工数を削減して容易に貼付けることができる。また、養生期間が必要ないため、被処理面２００に対してライニング材１を貼付けた後、間をあけることなく、ライニング対象２を使用することができる。 When pasting a conventional lining material on the surface to be processed, it is necessary to clean the surface to be processed, apply an adhesive, and dry the adhesive in advance. Even after pasting on the surface, a curing period of several days was required, and the lining object could not be used during the curing period. In this Embodiment, the lining material 1 has the magnetic elastomer layer 11 which added the magnetic body to the elastomer in the sticking surface 101 (other surface) side. If the surface to be processed 200 of the lining object 2 is a smooth surface and is free of dirt and foreign matter, the surface of the surface to be processed 200 is not subjected to primer treatment, adhesive treatment for applying an adhesive, or the like. 1 can be stuck by magnetic force. Therefore, the lining material 1 can be easily attached to the lining object 2 with reduced man-hours. Moreover, since a curing period is not required, the lining object 2 can be used without leaving a gap after the lining material 1 is attached to the surface to be treated 200.
また、従来のライニング材を交換する場合には、被処理面に対して接着されているライニング材をドライバーやバール等で剥がす必要があったため、被処理面を傷付けてしまうおそれがあった。また、ライニング材を剥がした後に、被処理面に対して残った接着剤等を除去する作業が必要であった。本実施の形態におけるライニング材１は、被処理面２００に対して磁力によって貼付けられているため、ライニング材１を交換する場合にも、被処理面２００が傷つくことを防ぎつつも容易に剥がすことができる。さらに、ライニング材１を剥がした後の被処理面２００に接着剤等が残らないため、被処理面２００を処理する工程を削減することができる。 Further, when the conventional lining material is replaced, it is necessary to peel off the lining material bonded to the surface to be processed with a screwdriver or a bar, so that the surface to be processed may be damaged. In addition, after removing the lining material, it is necessary to remove the adhesive remaining on the surface to be processed. Since the lining material 1 in this Embodiment is affixed with the magnetic force with respect to the to-be-processed surface 200, when replacing the lining material 1, it peels easily, preventing the to-be-processed surface 200 from being damaged. Can do. Furthermore, since no adhesive or the like remains on the surface to be processed 200 after the lining material 1 is peeled off, the process of processing the surface to be processed 200 can be reduced.
樹脂層１０が磁性エラストマー層１１の厚さよりも厚く形成されることにより、ライニング材１の耐摩耗性を向上することができる。 By forming the resin layer 10 to be thicker than the magnetic elastomer layer 11, the wear resistance of the lining material 1 can be improved.
磁性エラストマー層１１のエラストマーを熱可塑性エラストマーとすることにより、安価に大量に製造することができる。
［第２の実施の形態］
本発明の第２の実施の形態について、図２を参照して説明する。第２の実施の形態に係るライニング材１Ａは、第１の実施の形態にかかるライニング材１と同様、樹脂層１０と磁性エラストマー層１１とを有し、中間エラストマー層１２を新たな構成として有している点で異なる。以下、この相違点について重点的に説明する。
By making the elastomer of the magnetic elastomer layer 11 a thermoplastic elastomer, it can be manufactured in large quantities at a low cost.
[Second Embodiment]
A second embodiment of the present invention will be described with reference to FIG. Like the lining material 1 according to the first embodiment, the lining material 1A according to the second embodiment has a resin layer 10 and a magnetic elastomer layer 11, and has an intermediate elastomer layer 12 as a new configuration. It differs in that it is. Hereinafter, this difference will be mainly described.
中間エラストマー層１２は、樹脂層１０と磁性エラストマー層１１との間に配置される。中間エラストマー層１２と樹脂層１０とは、互いに対向する接着面１０３で接着される。また、中間エラストマー層１２と磁性エラストマー層１１とは、互いに対向する接着面１０４も接着される。 The intermediate elastomer layer 12 is disposed between the resin layer 10 and the magnetic elastomer layer 11. The intermediate elastomer layer 12 and the resin layer 10 are bonded to each other at the bonding surfaces 103 facing each other. The intermediate elastomer layer 12 and the magnetic elastomer layer 11 are also bonded to the adhesive surfaces 104 facing each other.
中間エラストマー層１２材料としては、例えば、天然ゴム（ＮＲ）、ブタジエンゴム（ＢＲ）、スチレンブタジエンゴム（ＳＢＲ）、ニトリルゴム（ＮＢＲ）、クロロプレンゴム（ＣＲ）、エチレンプロピレンゴム（ＥＰＭ）、エチレンプロピレンジエンゴム（ＥＰＤＭ）、ブチルゴム（ＩＩＲ）、クロロスルフォン化ゴム、塩化ゴム、シリコーンゴム、フッ素ゴム、アクリルゴム等のゴム材料を用いることができる。これらをブレンドしたものを用いてもよい。また、中間エラストマー層１２は、樹脂層１０及び磁性エラストマー層１１よりも柔らかい（硬度が低い）材料が好ましい。また、中間エラストマー層１２は、樹脂層１０及び磁性エラストマー層１１との接着性が良好な材料が好ましい。このような観点から中間エラストマー層１２の材料として、特にＮＢＲ（ニトリルゴム）やＳＢＲ（スチレン・ブタジエンゴム）が好ましい。中間エラストマー層１２の厚さは、例えば、０．５ｍｍ〜５ｍｍであり、樹脂層１０及び磁性エラストマー層１１よりも薄く形成される。 Examples of the material for the intermediate elastomer layer 12 include natural rubber (NR), butadiene rubber (BR), styrene butadiene rubber (SBR), nitrile rubber (NBR), chloroprene rubber (CR), ethylene propylene rubber (EPM), and ethylene propylene. Rubber materials such as diene rubber (EPDM), butyl rubber (IIR), chlorosulfonated rubber, chlorinated rubber, silicone rubber, fluorine rubber, and acrylic rubber can be used. You may use what blended these. The intermediate elastomer layer 12 is preferably made of a softer material (having a lower hardness) than the resin layer 10 and the magnetic elastomer layer 11. Further, the intermediate elastomer layer 12 is preferably made of a material having good adhesion to the resin layer 10 and the magnetic elastomer layer 11. From this point of view, NBR (nitrile rubber) and SBR (styrene-butadiene rubber) are particularly preferable as the material for the intermediate elastomer layer 12. The thickness of the intermediate elastomer layer 12 is, for example, 0.5 mm to 5 mm, and is formed thinner than the resin layer 10 and the magnetic elastomer layer 11.
中間エラストマー層１２を構成するエラストマーには、上述のようなエラストマーの他に、適宜、加硫剤（架橋剤）、加硫助剤（架橋助剤）、充填剤、難燃剤、可塑剤、老化防止剤（酸化防止剤）、安定剤、着色剤、加工助剤等が含まれていてもよい。 In addition to the above-described elastomer, the elastomer constituting the intermediate elastomer layer 12 is appropriately vulcanized (crosslinking agent), vulcanization aid (crosslinking aid), filler, flame retardant, plasticizer, aging. An inhibitor (antioxidant), a stabilizer, a colorant, a processing aid and the like may be contained.
樹脂層１０と中間エラストマー層１２とは、互いに対向する接着面１０３において、加硫接着される。加硫接着する際には、加硫用の接着剤を用いてもよい。加硫用の接着剤としては、例えば、ロード社のケムロック（ケムロックは登録商標）ロード社のケムロック（ケムロックは登録商標）等を用いることができる。なお、加硫接着剤としては、１種類のものを用いてもよいし、２種類以上のものを組み合わせて用いてもよい。樹脂層１０と中間エラストマー層１２とは、剥がれを防止する観点から２Ｎ／ｍｍ以上の力で接着される。 The resin layer 10 and the intermediate elastomer layer 12 are vulcanized and bonded to each other on the bonding surface 103 facing each other. When vulcanizing and bonding, an adhesive for vulcanization may be used. As an adhesive for vulcanization, for example, Chemlock manufactured by Lord (Chemlock is a registered trademark) Chemlock manufactured by Lord (Chemlock is a registered trademark) or the like can be used. In addition, as a vulcanization adhesive agent, one type may be used and two or more types may be used in combination. The resin layer 10 and the intermediate elastomer layer 12 are bonded with a force of 2 N / mm or more from the viewpoint of preventing peeling.
樹脂層１０に含まれる樹脂と、中間エラストマー層１２に含まれるエラストマーとは、加硫接着を強固とするため、同じ加硫系の材料とすることが好ましい。同じ加硫系の材料とは、同じ加硫条件にて加硫が行える材料のことである。 The resin contained in the resin layer 10 and the elastomer contained in the intermediate elastomer layer 12 are preferably made of the same vulcanized material in order to strengthen vulcanization adhesion. The same vulcanization material is a material that can be vulcanized under the same vulcanization conditions.
中間エラストマー層１２と磁性エラストマー層１１とは、互いに対向する接着面１０４において、例えば、接着剤や粘着剤によって固定される。接着剤としては、例えば、弾性接着剤が用いられる。粘着剤としては、例えば、ブチルゴム系粘着剤が用いられる。樹脂層１０と磁性エラストマー層１１とは、剥がれを防止する観点から２Ｎ以上の力で接着される。 The intermediate elastomer layer 12 and the magnetic elastomer layer 11 are fixed on the adhesive surfaces 104 facing each other, for example, with an adhesive or a pressure-sensitive adhesive. For example, an elastic adhesive is used as the adhesive. As the adhesive, for example, a butyl rubber adhesive is used. The resin layer 10 and the magnetic elastomer layer 11 are bonded with a force of 2N or more from the viewpoint of preventing peeling.
以上のように、本実施の形態によれば、第１の実施の形態について説明した作用及び効果に加え、樹脂層１０及び磁性エラストマー層１１よりも柔らかい材料からなる中間エラストマー層１２を設けることによって、ライニング材１Ａのクッション性を高めることができる。 As described above, according to the present embodiment, in addition to the functions and effects described in the first embodiment, by providing the intermediate elastomer layer 12 made of a material softer than the resin layer 10 and the magnetic elastomer layer 11. The cushioning property of the lining material 1A can be improved.
以上、実施形態に沿って本発明を説明したが、本発明はこれらに制限されるものではない。例えば、種々の変更、改良、組み合わせ等が可能なことは当業者に自明であろう。
（実施の形態のまとめ）
次に、以上説明した実施の形態から把握される技術思想について、実施の形態における符号等を援用して記載する。ただし、以下の記載における各符号は、特許請求の範囲における構成要素を実施の形態に具体的に示した部材等に限定するものではない。
［１］樹脂からなる樹脂層（１０）と、エラストマーに磁性体を添加した磁性エラストマー層（１１）と、を有し、一面側に前記樹脂層（１０）を、他面側に前記磁性エラストマー層（１１）を設けたライニング材（１、１Ａ）。
［２］前記樹脂層（１０）と前記磁性エラストマー層（１１）とが接着されている前記［１］に記載のライニング材（１、１Ａ）。
［３］前記樹脂層（１０）と前記磁性エラストマー層（１１）との間にエラストマーからなる中間エラストマー層（１２）を有する、前記［１］に記載のライニング材（１Ａ）。
［４］前記樹脂層（１０）と前記中間エラストマー層（１２）とは加硫接着され、前記磁性エラストマー層（１１）と前記中間エラストマー層（１２）とは接着された前記［３］に記載のライニング材（１Ａ）。
［５］前記中間エラストマー層（１２）は、前記樹脂層（１０）及び前記磁性エラストマー層（１１）よりも柔らかい材料からなる、前記［３］又は［４］に記載のライニング材（１Ａ）。
［６］
前記樹脂層（１０）は、前記磁性エラストマー層（１１）の厚さよりも厚い、
前記［１］乃至［５］のいずれかに記載のライニング材（１、１Ａ）。
［７］
前記磁性エラストマー層（１１）のエラストマーは、熱可塑性エラストマーである、
前記［１］乃至［６］のいずれかに記載のライニング材（１、１Ａ）。
As mentioned above, although this invention was demonstrated along embodiment, this invention is not restrict | limited to these. It will be apparent to those skilled in the art that various modifications, improvements, combinations, and the like can be made.
(Summary of embodiment)
Next, the technical idea grasped from the embodiment described above will be described with reference to the reference numerals in the embodiment. However, each reference numeral in the following description does not limit the constituent elements in the claims to members or the like specifically shown in the embodiment.
[1] A resin layer (10) made of a resin and a magnetic elastomer layer (11) obtained by adding a magnetic material to an elastomer, the resin layer (10) on one side, and the magnetic elastomer on the other side. Lining material (1, 1A) provided with a layer (11).
[2] The lining material (1, 1A) according to [1], wherein the resin layer (10) and the magnetic elastomer layer (11) are bonded.
[3] The lining material (1A) according to [1], further including an intermediate elastomer layer (12) made of an elastomer between the resin layer (10) and the magnetic elastomer layer (11).
[4] The resin layer (10) and the intermediate elastomer layer (12) are vulcanized and bonded, and the magnetic elastomer layer (11) and the intermediate elastomer layer (12) are bonded. Lining material (1A).
[5] The lining material (1A) according to [3] or [4], wherein the intermediate elastomer layer (12) is made of a material softer than the resin layer (10) and the magnetic elastomer layer (11).
[6]
The resin layer (10) is thicker than the magnetic elastomer layer (11).
The lining material (1, 1A) according to any one of [1] to [5].
[7]
The elastomer of the magnetic elastomer layer (11) is a thermoplastic elastomer.
The lining material (1, 1A) according to any one of [1] to [6].
１、１Ａ ライニング材
２ ライニング対象
１０ 樹脂層
１１ 磁性エラストマー層
１２ 中間エラストマー層
１００ 表面（一面）
１０１ 貼付け面（他面）
１０２、１０３、１０４ 接着面
２００ 被処理面
DESCRIPTION OF SYMBOLS 1, 1A Lining material 2 Lining object 10 Resin layer 11 Magnetic elastomer layer 12 Intermediate elastomer layer 100 The surface (one side)
101 Pasting surface (other surface)
102, 103, 104 Adhesive surface 200 Surface to be processed
Claims (4)
エラストマーに磁性体を添加した磁性エラストマー層と、
前記樹脂層と前記磁性エラストマー層との間にエラストマーからなる中間エラストマー層を有し、前記中間エラストマー層は、前記樹脂層及び前記磁性エラストマー層よりも柔らかい材料からなり、
一面側に前記樹脂層を、他面側に前記磁性エラストマー層を設けたライニング材。 A resin layer made of resin;
A magnetic elastomer layer obtained by adding a magnetic material to the elastomer;
It has an intermediate elastomer layer made of an elastomer between the resin layer and the magnetic elastomer layer, the intermediate elastomer layer is made of a material softer than the resin layer and the magnetic elastomer layer,
A lining material provided with the resin layer on one side and the magnetic elastomer layer on the other side.
前記磁性エラストマー層と前記中間エラストマー層とは接着された、The magnetic elastomer layer and the intermediate elastomer layer are bonded,
請求項１に記載のライニング材。The lining material according to claim 1.
請求項１または２に記載のライニング材。The lining material according to claim 1 or 2.
請求項１乃至３のいずれかに記載のライニング材。The lining material according to any one of claims 1 to 3.