JP6405315B2 - 環境障壁コーティング及びその方法 - Google Patents
環境障壁コーティング及びその方法 Download PDFInfo
- Publication number
- JP6405315B2 JP6405315B2 JP2015546488A JP2015546488A JP6405315B2 JP 6405315 B2 JP6405315 B2 JP 6405315B2 JP 2015546488 A JP2015546488 A JP 2015546488A JP 2015546488 A JP2015546488 A JP 2015546488A JP 6405315 B2 JP6405315 B2 JP 6405315B2
- Authority
- JP
- Japan
- Prior art keywords
- bond coat
- silicon
- article according
- layer
- article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
12 基材
14 多層環境障壁コーティング(EBC)システム
16 シリコン含有ボンドコート
18 追加層
20 第1のEBC層
22 追加層
24 追加層
26 凹部(陥凹)
28 突起部(突出部)
30 構成層
32 ボンドコート16の表面
34 基材12の表面
Claims (15)
- 物品であって、
連続表面を有するセラミックマトリックス複合材料基材と、
前記基材の連続表面上に設けられたボンドコートであって、元素シリコン;1又はそれ以上のシリコン合金;炭化ケイ素;窒化ケイ素;遷移金属シリサイド;シリカ;希土類ケイ酸塩;希土類アルミノケイ酸塩;アルカリ土類 アルミノケイ酸塩;及びこれらの混合物を含有する材料から形成され、凹部、突起部又はこれらの組み合わせを含む表面特徴部を有するボンドコートと、
前記基材の連続表面及びボンドコートの表面の上にある少なくとも1つの外側層と、
前記ボンドコートの表面上で前記ボンドコートと前記少なくとも1つの外側層との間で接触する構成層と、
を備え、
前記構成層が、前記ボンドコートの成分によって形成され且つ前記ボンドコートの表面特徴部に対応する特徴を表面に有していて、
前記表面特徴部が、前記構成層を通じて前記ボンドコートと前記少なくとも1つの外側層とを物理的に相互連結しており、
前記表面特徴部が、前記ボンドコートの表面の内外に40〜160μmだけ延びており、
前記表面特徴部の厚さが、前記構成層の厚さよりも厚い、
物品。 - 前記表面特徴部が、互いに等間隔で配置される、請求項1に記載の物品。
- 前記表面特徴部が、該表面特徴部が互いに非等間隔で配置されている及び/又は同じでない寸法を有する不規則なパターンを定める、請求項1に記載の物品。
- 前記表面特徴部が、前記ボンドコートの表面方向に少なくとも10μmの寸法を有する、請求項1から3のいずれかに記載の物品。
- 前記表面特徴部が、少なくとも10μm離間して配置される、請求項1から4のいずれかに記載の物品。
- 前記表面特徴部が、直線的形状、曲線形状、及び不規則な表面粗度の群からのものである、請求項1から5のいずれかに記載の物品。
- 前記ボンドコートが、基本的に元素シリコンからなる、請求項1から6のいずれかに記載の物品。
- 前記ボンドコートが、シリコンと、炭化ケイ素及び窒化ケイ素、遷移金属シリサイド及びシリカからなる群から選択された1又はそれ以上の追加の化合物とからなる、請求項1から6のいずれかに記載の物品。
- 前記少なくとも1つの外側層が、ムライト;アルカリ土類アルミノシリケート;化学式RE2SiO5又はRE2Si2O7のREシリケート;アルカリ土類アルミノケイ酸塩;RE酸化物;REアルミノケイ酸塩;及びこれらの混合物を含有し、ここでREがSc、Y、Dy、Ho、Er、Tm、Yb、Lu、Eu、Gd、Tb又はこれらの組み合わせである、請求項1から8のいずれかに記載の物品。
- 前記基材が、強化相及び/又はマトリックス相として炭化ケイ素、窒化ケイ素、及び/又はシリコンを含有する、請求項1から9のいずれかに記載の物品。
- 前記基材が、強化相及び/又はマトリックス相として炭化ケイ素を含有する、請求項10に記載の物品。
- 前記構成層が、非晶質シリカ、シリカリッチガラス、又は少なくとも1つの非晶質シリカ又はシリカリッチガラス相を含む多相混合物を含む、請求項1から11のいずれかに記載の物品。
- 前記物品が、タービンエンジンの回転構成要素である、請求項1から12のいずれかに記載の物品。
- 前記構成層が、ホウ素、アルミニウム及び/又は窒素を溶解して含有する、請求項12または13に記載の物品。
- 前記多相混合物が、イットリウムアルミノケイ酸塩又は希土類ジシリケートをさらに含む、請求項12から14のいずれかに記載の物品。