JP6350508B2 - Rubber composition, method for producing the same, and pneumatic tire - Google Patents

Description

  The present invention relates to a rubber composition, a method for producing the same, and a pneumatic tire.

In recent years, pneumatic tires have been desired to have high strength, performance that improves fuel consumption, and the like.
For example, Patent Document 1 describes a rubber composition comprising 1 to 50 parts by weight of a modified polymer obtained by modifying a polyolefin resin with an unsaturated carboxylic acid with respect to 100 parts by weight of a diene rubber.
Patent Document 2 contains 2 to 75 parts by weight of high-density polyethylene (including 20% by weight or more of high-density polyethylene having a crosslinkable part) with respect to 100 parts by weight of the rubber component, and the melting point of the compounded resin. A rubber composition kneaded at a higher temperature is described. Patent Document 2 describes a silane crosslinkable polymer (trade name: Linkron HF-700N, manufactured by Mitsubishi Chemical Corporation) as a high-density polyethylene having a crosslinkable portion. The above product is uncrosslinked polyethylene into which silane active groups have been introduced.

JP-A-10-87900 JP 10-67886 A

Under such circumstances, with reference to Patent Document 1, a rubber composition containing a diene rubber and acid-modified polyethylene was prepared and evaluated. As a result, such a rubber composition had a 100% elongation required recently. It has become clear that the modulus (M100) level may not be satisfied.
Further, referring to Patent Document 2, a rubber composition containing a diene rubber and high-density polyethylene was prepared and evaluated. Such a rubber composition may be inferior in elongation at break and low exothermic property. It became clear.
Accordingly, an object of the present invention is to provide a rubber composition that is excellent in modulus at 100% elongation while maintaining high low heat buildup and elongation at break. Another object of the present invention is to provide a method for producing a rubber composition and a pneumatic tire for producing the rubber composition.

As a result of intensive studies to solve the above problems, the present inventors have found that the density of the acid-modified polyethylene is 0.94 to 0.98 g / cm ³ , and the content of the acid-modified polyethylene is 100 parts by mass of the diene rubber. On the other hand, it has been found that a predetermined effect can be obtained by being 2 to 30 parts by mass, and the present invention has been achieved.
The present invention is based on the above knowledge and the like, and specifically, solves the above problems by the following configuration.

1. Contains a diene rubber, a filler, and acid-modified polyethylene,
The acid-modified polyethylene has a density of 0.94 to 0.98 g / cm ³ ;
The rubber composition whose content of the acid-modified polyethylene is 2 to 30 parts by mass with respect to 100 parts by mass of the diene rubber.
2. 2. The rubber composition according to 1 above, wherein the acid-modified polyethylene is polyethylene modified with maleic anhydride.
3. 3. The rubber composition according to 1 or 2 above, wherein the acid-modified polyethylene has a melting point of 125 to 145 ° C.
4). The rubber composition according to any one of the above 1 to 3 is produced by mixing the diene rubber, the filler, and the acid-modified polyethylene under conditions equal to or higher than the melting point of the acid-modified polyethylene. A method for producing a rubber composition.
5. The pneumatic tire formed with the rubber composition in any one of said 1-3.

The rubber composition of the present invention is excellent in modulus at 100% elongation while maintaining high low exothermic property and elongation at break.
Moreover, according to the manufacturing method of the rubber composition of this invention, the said rubber composition can be manufactured.
The pneumatic tire of the present invention is excellent in fuel efficiency and toughness.

FIG. 1 is a partial cross-sectional schematic view of a tire representing an example of an embodiment of the pneumatic tire of the present invention.

The present invention will be described in detail below.
In this specification, (meth) acryl represents acryl or methacryl.
In addition, a numerical range expressed using “to” in this specification means a range including numerical values described before and after “to” as a lower limit value and an upper limit value.
In this specification, when a component contains 2 or more types of substances, the content of the above components refers to the total content of two or more types of substances.
In the present specification, it may be said that the effect of the present invention is more excellent when at least one of modulus at 100% elongation (M100), elongation at break and low exothermic property is more excellent.

[Rubber composition]
The rubber composition of the present invention (the composition of the present invention)
Contains a diene rubber, a filler, and acid-modified polyethylene,
The acid-modified polyethylene has a density of 0.94 to 0.98 g / cm ³ ;
It is a rubber composition whose content of the acid-modified polyethylene is 2 to 30 parts by mass with respect to 100 parts by mass of the diene rubber.

Since the composition of this invention takes such a structure, it is thought that a desired effect is acquired. The reason is not clear, but it is presumed that it is as follows.
Since the acid-modified polyethylene contained in the rubber composition of the present invention is modified with an acid and can interact with the filler to effectively disperse the filler, the rubber composition of the present invention has a low heat generation. It is thought that it is excellent in property.
Moreover, since the density of acid-modified polyethylene is 0.94 to 0.98 g / cm ³ , the acid-modified polyethylene is a so-called high-density acid-modified polyethylene. In addition, since the acid-modified polyethylene and the diene rubber have a common main chain of hydrocarbon, the acid-modified polyethylene can be entangled with the diene rubber. By imparting toughness to the diene rubber, the rubber composition of the present invention is presumed to be excellent in modulus at 100% elongation while maintaining high elongation at break.
Hereinafter, each component contained in the composition of this invention is explained in full detail.

<Diene rubber>
The diene rubber contained in the rubber composition of the present invention is not particularly limited as long as it has a double bond in the main chain. Examples of the diene rubber include natural rubber (NR), isoprene rubber (IR), butadiene rubber (BR), aromatic vinyl-conjugated diene copolymer rubber, chloroprene rubber (CR), acrylonitrile butadiene rubber (NBR), and ethylene. -Propylene-diene copolymer rubber (EPDM), styrene-isoprene rubber, isoprene-butadiene rubber, nitrile rubber, hydrogenated nitrile rubber and the like.
The diene rubbers can be used alone or in combination of two or more.
Of these, aromatic vinyl-conjugated diene copolymer rubber, NR, and BR are preferable.
Examples of the aromatic vinyl-conjugated diene copolymer rubber include styrene butadiene rubber (SBR) and styrene isoprene rubber. Of these, SBR is preferable.

  Although the weight average molecular weight of a diene rubber is not specifically limited, From a workability viewpoint, it is preferable that it is 50,000-3,000,000, and 100,000-2,000,000 is more preferable. The weight average molecular weight (Mw) of the diene rubber is a standard polystyrene equivalent value based on a value measured by gel permeation chromatography (GPC) using tetrahydrofuran as a solvent.

  When the diene rubber contains natural rubber and at least one selected from the group consisting of aromatic vinyl-conjugated diene copolymer rubber and BR, the content of the natural rubber is diene-based from the viewpoint of excellent toughness. It is preferable that it is 15-80 mass% with respect to rubber | gum, and 20-80 mass% is more preferable.

<Filler>
The filler contained in the rubber composition of the present invention is not particularly limited. For example, it can be at least one selected from the group consisting of carbon black and white filler.

(Carbon black)
Carbon black as a filler is not particularly limited. For example, the thing similar to the carbon black which can generally be used for a rubber composition is mentioned. Specific examples include SAF, ISAF, IISAF, N339, HAF, FEF, GPE, and SRF. Of these, SAF, ISAF, IISAF, N339, HAF, and FEF are preferable.

The nitrogen adsorption specific surface area (N ₂ SA) of the carbon black is preferably 30 to 250 m ² / g, more preferably 40 to 240 m ² / g, from the viewpoint that the processability of the rubber composition is excellent.
Here, N ₂ SA is a value obtained by measuring the amount of nitrogen adsorbed on the carbon black surface in accordance with JIS K 6217-2: 2001 “Part 2: Determination of specific surface area—nitrogen adsorption method—single point method”. .
Carbon blacks can be used alone or in combination of two or more.

(White filler)
The white filler as the filler is not particularly limited. For example, the thing similar to what can generally be used for a rubber composition is mentioned. Specific examples include silica, calcium carbonate, talc, mica and the like. Of these, silica is preferable.

Silica Examples of silica include wet silica, fumed silica, calcined silica, precipitated silica, pulverized silica, fused silica, and colloidal silica.

Silica preferably has a CTAB adsorption specific surface area of 50 to 300 m ² / g, more preferably 80 to 250 m ² / g, from the viewpoint of suppressing silica aggregation.
Here, the CTAB adsorption specific surface area was determined by measuring the adsorption amount of n-hexadecyltrimethylammonium bromide on the silica surface according to JIS K6217-3: 2001 “Part 3: Determination of specific surface area—CTAB adsorption method”. Value.
The white fillers can be used alone or in combination of two or more.

It is preferable that content of a filler is 5-200 mass parts with respect to 100 mass parts of diene rubbers, and 10-150 mass parts is more preferable.
The content of carbon black is preferably 10 to 150 parts by mass and more preferably 30 to 120 parts by mass with respect to 100 parts by mass of the diene rubber.
The content of the white filler is preferably 5 to 120 parts by mass and more preferably 30 to 120 parts by mass with respect to 100 parts by mass of the diene rubber.

  When carbon black and white filler are used in combination as the filler, the content of carbon black is preferably 1 to 100 parts by mass, more preferably 2 to 80 parts by mass with respect to 100 parts by mass of the diene rubber. . In this case, the content of the white filler is preferably 5 to 150 parts by mass, more preferably 10 to 140 parts by mass with respect to 100 parts by mass of the diene rubber.

<Acid-modified polyethylene>
The acid-modified polyethylene contained in the rubber composition of the present invention is a polymer having a carboxy group or an acid anhydride group as a modifying group and having a main chain of polyethylene. The density of the acid-modified polyethylene is 0.94 to 0.98 g / cm ³ . That is, the acid-modified polyethylene contained in the rubber composition of the present invention is a so-called high-density acid-modified polyethylene.

  Examples of the acid-modified polyethylene include polyethylene modified with an unsaturated carboxylic acid. Of these, acid-modified polyethylene is preferably polyethylene modified with maleic anhydride in that the effects of the present invention are more excellent and the dispersion of the filler is excellent.

(Main chain)
The polyethylene that the acid-modified polyethylene has as the main chain is not particularly limited as long as it has an ethylene repeating unit. One preferred embodiment is that the main chain is a homopolymer of ethylene.

(Modified group)
The modified group possessed by the acid-modified polyethylene is not particularly limited as long as it is a carboxy group or an acid anhydride group.

One preferred embodiment is that the modifying group is formed by an unsaturated carboxylic acid.
Examples of the unsaturated carboxylic acid include maleic acid, fumaric acid, (meth) acrylic acid, crotonic acid, itaconic acid, or acid anhydrides of these acids.
Of these, maleic anhydride, maleic acid, and acrylic acid are preferably used.

Examples of the modifying group include a group represented by the following formula (1).
In formula (1), * represents a bonding point.

  The modifying group can be bonded to the main chain directly or via an organic group. The organic group is not particularly limited.

  One preferred embodiment of the acid-modified polyethylene has a modifying group in the side chain.

In the present invention, the density of the acid-modified polyethylene is 0.94 to 0.98 g / cm ³ . When the density of the acid-modified polyethylene is in the above range, the rubber composition of the present invention is excellent in M100 and elongation at break.
The density of the acid-modified polyethylene is preferably 0.95 to 0.98 g / cm ^{3 in} that the effect of the present invention is more excellent.
In the present invention, the density of the acid-modified polyethylene can be measured according to ASTM D1505.

The melting point of the acid-modified polyethylene is preferably 125 to 145 ° C., more preferably 125 to 140 ° C., in that the effects of the present invention are more excellent and the processability is excellent.
In the present invention, the melting point was measured at a rate of temperature increase of 10 ° C./min by differential scanning calorimetry (DSC) according to ASTM D3418.

  The acid-modified polyethylene is not particularly limited for its production. The acid-modified polyethylene can be used alone or in combination of two or more.

In this invention, content of acid-modified polyethylene is 2-30 mass parts with respect to 100 mass parts of diene rubbers. When the content of the acid-modified polyethylene is within the above range, M100, elongation at break and low exothermic property are excellent. Moreover, it is excellent in workability.
The content of the acid-modified polyethylene is preferably 2 to 20 parts by mass with respect to 100 parts by mass of the diene rubber because the effects of the present invention are more excellent and the processability is excellent.

(Other ingredients)
The rubber composition of the present invention can further contain other components (additives) as necessary within a range not impairing the purpose and effect. Examples of additives include polymers other than diene rubbers and acid-modified polyethylene; silane coupling agents, vulcanizing agents, crosslinking agents, vulcanization accelerators, vulcanization accelerators such as zinc oxide and stearic acid, Examples thereof include those that can be generally blended in a rubber composition such as a vulcanization retarder, oil, anti-aging agent, and plasticizer. The content of the additive can be appropriately selected.

-Silane coupling agent It is preferable that the rubber composition of this invention contains a silane coupling agent from a viewpoint that the effect of this invention is more excellent.
The silane coupling agent is not particularly limited. Among these, a silane coupling agent having a sulfur atom (a sulfur-containing silane coupling agent) is mentioned as one of preferred embodiments.
The sulfur-containing silane coupling agent is not particularly limited as long as it is a silane coupling agent having a sulfur atom. For example, polysulfide silane cups such as bis (3-triethoxysilylpropyl) tetrasulfide (Si69 manufactured by Evonik Degussa), 3-trimethoxysilylpropylbenzothiazole tetrasulfide, bis (3-triethoxysilylpropyl) disulfide Ringing agent: γ-mercaptopropylmethyldimethoxysilane, γ-mercaptopropyltrimethoxysilane, 3- [ethoxybis (3,6,9,12,15-pentaoxaoctacosan-1-yloxy) silyl] -1-propanethiol Mercapto silane coupling agent such as (Evonik Degussa Si363); Thiocarboxylate silane coupling agent such as 3-octanoylthiopropyltriethoxysilane; 3-thiocyanate propyltri Examples include thiocyanate silane coupling agents such as ethoxysilane.
Of these, polysulfide silane coupling agents are preferable, and bis (3-triethoxysilylpropyl) tetrasulfide and bis (3-triethoxysilylpropyl) disulfide are more preferable.
The silane coupling agents can be used alone or in combination of two or more.
As the silane coupling agent, one obtained by condensing one or more of the above silane coupling agents in advance may be used. The method for condensing the silane coupling agent is not particularly limited. For example, a conventionally well-known thing is mentioned.

  In this invention, it is preferable that content of a silane coupling agent is 1-30 mass parts with respect to 100 mass parts of diene rubbers at the point which the effect of this invention is more excellent, and is 1-25 mass parts. More preferably.

  The rubber composition of the present invention is not particularly limited for its production. For example, it can be produced by mixing a diene rubber, a filler, acid-modified polyethylene and an additive that can be used as required. Among these, a preferable production method will be described later as a production method of the rubber composition of the present invention.

  The rubber composition of the present invention can be vulcanized or crosslinked under, for example, conventionally known vulcanization or crosslinking conditions.

  The rubber composition of the present invention can be used, for example, for a pneumatic tire.

[Method for producing rubber composition]
The method for producing the rubber composition of the present invention comprises:
In the method for producing a rubber composition, the rubber composition of the present invention is produced by mixing a diene rubber, a filler, and an acid-modified polyethylene under a condition not lower than the melting point of the acid-modified polyethylene. . In the method for producing a rubber composition of the present invention, the density of the acid-modified polyethylene is 0.94 to 0.98 g / cm ³ . The content of the acid-modified polyethylene is 2 to 30 parts by mass with respect to 100 parts by mass of the diene rubber.

The diene rubber, filler and acid-modified polyethylene used in the method for producing the rubber composition of the present invention are the same as those of the rubber composition of the present invention.
In addition to the above components, additives may be further used. The additives are the same as those of the rubber composition of the present invention.

The temperature at the time of mixing (mixing temperature) is not less than the melting point of the acid-modified polyethylene and is preferably higher than the melting point of the acid-modified polyethylene from the viewpoint of excellent processability.
The temperature at the time of mixing (mixing temperature) can be 180 degrees C or less.

In addition, components other than the vulcanizing components such as a vulcanizing agent and a vulcanization accelerator may be mixed in advance, and the vulcanizing components may be added thereto.
At this time, it is mentioned as one of the preferable aspects that the mixing temperature at the time of premixing is the same as the above mixing temperature. The mixing temperature at the time of mixing after adding said vulcanization-type component is not specifically limited. It may be less than the melting point of the acid-modified polyethylene.

The time for mixing in advance can be 1 minute or more and 20 minutes or less.
The time for mixing after adding the vulcanizing system component can be 1 minute or more and 5 minutes or less.

The apparatus used when mixing the said component is not specifically limited. For example, a conventionally well-known thing is mentioned.
In the present specification, mixing includes kneading.

[Pneumatic tire]
Next, the pneumatic tire of the present invention will be described.
The pneumatic tire of the present invention is a pneumatic tire formed from the above-described rubber composition of the present invention.
The rubber composition used for the pneumatic tire of the present invention is not particularly limited as long as it is the rubber composition of the present invention.

The rubber composition can be used for a structural member constituting a pneumatic tire.
Examples of the structural member include a tire tread portion, a sidewall portion, a bead portion, a carcass layer, and a belt layer.

  Among these, the tire tread portion is preferably formed of the rubber composition of the present invention, and at least one selected from the group consisting of a cap tread and an undertread is more preferably formed of the rubber composition of the present invention. A tread is more preferable.

In FIG. 1, the partial cross-sectional schematic of the tire showing an example of the embodiment of the pneumatic tire of this invention is shown. The present invention is not limited to the attached drawings.
In FIG. 1, the pneumatic tire has a bead portion 1, a sidewall portion 2, and a tire tread portion 3. Between the pair of left and right bead portions 1, a carcass layer 4 in which fiber cords are embedded is mounted, and an end portion of the carcass layer 4 is folded around the bead core 5 and the bead filler 6 from the inside to the outside of the tire. Rolled up. In the tire tread portion 3, a belt layer 7 is disposed over the circumference of the tire outside the carcass layer 4. In the bead portion 1, a rim cushion 8 is disposed at a portion in contact with a rim (not shown).

  The pneumatic tire of the present invention can be manufactured, for example, according to a conventionally known method. Moreover, as gas with which a tire is filled, inert gas, such as nitrogen, argon, helium other than the air which adjusted normal or oxygen partial pressure, for example, can be used.

The present invention will be specifically described below with reference to examples. However, the present invention is not limited to these. In this specification, Examples I-1 to 1-3 are to be read as Reference Examples I-1 to 1-3 for the composition of the present invention.
<Manufacture of rubber composition>
A rubber composition was produced using the components shown in Table 1 or Table 2 below in the compositions (parts by mass) shown in the same table.
Specifically, first, components other than the vulcanized components (sulfur and sulfur-containing vulcanization accelerator) among the components shown in each table are about 3 by a tangential mixer under the condition of the mixing temperature 1 shown in each table. The mixture was obtained by kneading for 30 minutes. Next, a vulcanization system component was added to the said mixture, and these were knead | mixed with the open roll on the conditions of the mixing temperature 2 shown in each table | surface, and the rubber composition was manufactured.

<Evaluation>
The following evaluation was performed using the rubber composition produced as described above. The results are shown in each table. The evaluation results are shown in Table 1 below as an index with the value of Standard Example I as 100, and in Table 2 below as an index with the value of Standard Example II as 100.

(Preparation of vulcanized rubber test piece)
The rubber composition produced as described above was press vulcanized at 160 ° C. for 15 minutes in a predetermined mold to prepare a vulcanized rubber test piece.

Predetermined elongation tensile stress (S _e ): (modulus index)
Elongation at break (E _B ): (Indicator of elongation at break)
A JIS No. 3 dumbbell-shaped test piece was punched out from the vulcanized rubber test piece prepared as described above, and a tensile test at a tensile speed of 500 mm / min was conducted in accordance with JIS K6251: 2010, and the tensile stress at 100% elongation (100 % Modulus, hereinafter abbreviated as “M100”)), and elongation at break (E _B ) [%] were measured at room temperature.
The larger the index of M100, the greater the stress and the higher the modulus.
It means that it is excellent in elongation at break, so that the index of elongation at the time of cutting is large.

・ Low exothermicity: tan δ (60 ° C)
For the vulcanized rubber test piece prepared as described above, a loss tangent tan δ (with a tensile deformation strain rate of 10 ± 2%, a frequency of 20 Hz, and a temperature of 60 ° C. using a viscoelastic spectrometer (manufactured by Iwamoto Seisakusho Co., Ltd.) 60 ° C.).
The smaller the index of tan δ (60 ° C.), the lower the exothermic property.

The detail of each component shown to the said 1st table | surface and the 2nd table | surface is as follows.
NR: natural rubber, NUSIRA SIR20
SBR: styrene butadiene rubber, Nipol 1502 (manufactured by Nippon Zeon)
-BR: Butadiene rubber, Nipol BR 1220 (manufactured by Nippon Zeon)

Acid-modified polyethylene 1: Maleic anhydride-modified high-density polyethylene (Admer HE810, manufactured by Mitsui Chemicals), density 0.96 g / cm ³ , melting point 130 ° C.

Comparative acid-modified low-density polyethylene: maleic anhydride-modified low-density polyethylene (Admer LF128, manufactured by Mitsui Chemicals), density 0.9 g / cm ³ , melting point 110 ° C.
Comparative high-density polyethylene: high-density polyethylene (Novatech HJ560, manufactured by Mitsui Chemicals), density 0.96 g / cm ³ , no acid modification, melting point 135 ° C.

Carbon black: Show black N550 (made by Showa Cabot), N ₂ SA 42 m ² / g
Silica: wet silica (nip seal AQ, CTAB adsorption specific surface area 170 m ² / g, manufactured by Nippon Silica)

・ Silane coupling agent: Si69 (Evonik Degussa)
・ Zinc oxide: 3 kinds of zinc white (made by Shodo Chemical Industry Co., Ltd.)
・ Stearic acid: Stearic acid (manufactured by NOF Corporation)
Anti-aging agent (S-13): N- (1,3-dimethylbutyl) -N′-phenyl-p-phenylenediamine (Antigen 6C, manufactured by Sumitomo Chemical Co., Ltd.)
・ Wax: Sunnock manufactured by Ouchi Shinsei Chemical Co., Ltd. ・ Oil: Extract No. 4S
・ Sulfur: Oil-treated sulfur (manufactured by Karuizawa Refinery)
-Sulfur-containing vulcanization accelerator (CZ): N-cyclohexyl-2-benzothiazole sulfenamide (Sunseller CM-PO, manufactured by Sanshin Chemical Industry Co., Ltd.)

As is apparent from the results shown in Table 1, M100 was low in Comparative Example I-1 in which the density of the acid-modified polyethylene was outside the predetermined range.
Comparative Example I-2 containing high-density polyethylene that was not acid-modified was low in elongation at break and inferior in low heat build-up.
In Comparative Example I-3 in which the content of acid-modified polyethylene was less than the predetermined range, M100 was low.
In Comparative Example I-4 in which the content of the acid-modified polyethylene was larger than the predetermined range, the processability was poor and low exothermic properties could not be evaluated.

On the other hand, in Table 1, the rubber composition of the present invention was excellent in modulus at 100% elongation while maintaining high low exothermic property and elongation at break. The rubber composition of the present invention was excellent in processability.
Comparing Examples I-1 to 1-3, the larger the amount of acid-modified polyethylene, the better the modulus at 100% elongation.

As is apparent from the results shown in Table 2, Comparative Example II-1 in which the density of the acid-modified polyethylene was outside the predetermined range had a low M100.
Comparative Example II-2 containing high-density polyethylene that was not acid-modified was low in elongation at break and inferior in low heat build-up.

  On the other hand, in Table 2, the rubber composition of the present invention was excellent in modulus at 100% elongation while maintaining high low exothermic property and elongation at break. The rubber composition of the present invention was excellent in processability.

1 Bead part 2 Side wall part 3 Tire tread part 4 Carcass layer 5 Bead core 6 Bead filler 7 Belt layer 8 Rim cushion

Claims (5)

Contains a diene rubber, a filler, and acid-modified polyethylene,
The acid-modified polyethylene has a density of 0.94 to 0.98 g / cm ³ ;
The content of the acid-modified polyethylene is 2 to 30 parts by mass with respect to 100 parts by mass of the diene rubber.
The diene rubber includes natural rubber, butadiene rubber, and aromatic vinyl-conjugated diene copolymer rubber ,
The rubber composition whose content of the said natural rubber is 15-80 mass% with respect to the said diene rubber.   The rubber composition according to claim 1, wherein the acid-modified polyethylene is polyethylene modified with maleic anhydride.   The rubber composition according to claim 1 or 2, wherein the acid-modified polyethylene has a melting point of 125 to 145 ° C. Natural rubber and butadiene rubber as a diene rubber, a filler, and acid-modified polyethylene having a density of 0.94 to 0.98 g / cm ³ ,
The acid-modified polyethylene is used in an amount of 2 to 30 parts by mass with respect to 100 parts by mass of the diene rubber.
The natural rubber is used in an amount of 15 to 80% by mass with respect to the diene rubber,
By mixing under conditions above the melting point of the acid-modified polyethylene,
Containing the diene rubber, the filler, and the acid-modified polyethylene,
The diene rubber includes the natural rubber and the butadiene rubber,
The content of the acid-modified polyethylene is 2 to 30 parts by mass with respect to 100 parts by mass of the diene rubber.
The manufacturing method of a rubber composition which manufactures a rubber composition whose content of the said natural rubber is 15-80 mass% with respect to the said diene rubber .   The pneumatic tire formed with the rubber composition of any one of Claims 1-3.