JP6326730B2 - Nonwoven fabric and method for producing the same - Google Patents
Nonwoven fabric and method for producing the same Download PDFInfo
- Publication number
- JP6326730B2 JP6326730B2 JP2013129182A JP2013129182A JP6326730B2 JP 6326730 B2 JP6326730 B2 JP 6326730B2 JP 2013129182 A JP2013129182 A JP 2013129182A JP 2013129182 A JP2013129182 A JP 2013129182A JP 6326730 B2 JP6326730 B2 JP 6326730B2
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- nonwoven fabric
- fibers
- cellulose
- number average
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、数平均繊維幅が異なる2種類の繊維を含み、高い引張強度と高い比引裂強度とを有する不織布、及びその製造方法に関する。 The present invention relates to a nonwoven fabric including two types of fibers having different number average fiber widths and having high tensile strength and high specific tear strength, and a method for producing the same.
近年、石油資源の代替および環境意識の高まりから再生産可能な天然繊維の応用に注目が集まっている。天然繊維の中でもセルロース繊維、とりわけ木材由来のセルロース繊維(パルプ)は主に紙製品として幅広く使用されている。紙に使用されるセルロース繊維の幅は10〜50μmのものがほとんどである。このようなセルロース繊維から得られる紙(シート)は不透明であり、印刷用紙として幅広く利用されている。一方、セルロース繊維をレファイナーやニーダー、サンドグラインダーなどで処理(叩解、粉砕)し、セルロース繊維を微細化(ミクロフィブリル化)すると透明紙(グラシン紙等)が得られる。また、従来からセルロース繊維で構成された不織布は、サイズ剤や紙力増強剤などを添加し、紙として印刷用紙や書籍などに利用されてきたが、気体や液体などに対する透過性を利用して、フィルター、蓄電素子、電池又はキャパシタのセパレータなどへの利用が検討されている。 In recent years, attention has been focused on the application of reproducible natural fibers due to the substitution of petroleum resources and the growing environmental awareness. Among natural fibers, cellulose fibers, particularly wood-derived cellulose fibers (pulp) are widely used mainly as paper products. Most cellulose fibers used for paper have a width of 10 to 50 μm. Paper (sheet) obtained from such cellulose fibers is opaque and is widely used as printing paper. On the other hand, when the cellulose fiber is treated (beating, pulverizing) with a refiner, kneader, sand grinder or the like, and the cellulose fiber is refined (microfibril), a transparent paper (glassine paper or the like) is obtained. Conventionally, nonwoven fabrics composed of cellulose fibers have been used for printing paper and books as paper, with the addition of sizing agents, paper strength enhancers, etc., but using permeability to gases and liquids. Application to separators for filters, power storage elements, batteries, or capacitors is under study.
特許文献1には、ミクロンオーダー以下の微小な繊維径を有するセルロース繊維で構成され、かつ機械的強度及び耐熱性が高いセルロース繊維不織布を提供することを目的として、平均繊維径0.1〜20μmのセルロース繊維と平均繊維径100nm未満のセルロースナノファイバーとを抄紙した不織布が記載されている。 In Patent Document 1, an average fiber diameter of 0.1 to 20 μm is provided for the purpose of providing a cellulose fiber nonwoven fabric composed of cellulose fibers having a fine fiber diameter of micron order or less and having high mechanical strength and heat resistance. A nonwoven fabric made by papermaking of cellulose fibers and cellulose nanofibers having an average fiber diameter of less than 100 nm is described.
また特許文献2には、薄肉であっても、透気性と機械的強度とを両立できる不織布を提供することを目的として、平均繊維径0.1〜50μmのセルロース繊維と平均繊維径1.5μm以下のポリオレフィン繊維とを含み、かつ厚みが20μm以下である不織布が記載されている。 Patent Document 2 discloses cellulose fibers having an average fiber diameter of 0.1 to 50 μm and an average fiber diameter of 1.5 μm for the purpose of providing a nonwoven fabric that can achieve both air permeability and mechanical strength even if it is thin. A nonwoven fabric containing the following polyolefin fibers and having a thickness of 20 μm or less is described.
一方、特許文献3には、短繊維、補強材及び弾性重合体からなる不織布シートであって、短繊維がアクリロニトリル50〜95重量%と少なくとも1種の他のモノマーからなるアクリロニトリル系共重合ポリマーから構成され、少なくとも2種の異なる繊維直径を有するアクリル繊維A及びBが使用され、該アクリル繊維A及びBの繊維直径が、それぞれAが0.1μm以上7μm未満、Bが10μm以上18μm未満であり、その混率が、A/B=40/60〜80/20であることを特徴とする不織布シートが記載されている。特許文献2は、繊度の異なる繊維の使用、または異なる種類の繊維を使用することにより、獣毛調あるいは杢調様風合いを与える合成皮革用不織布シートを提供することを目的としている。 On the other hand, Patent Document 3 discloses a non-woven sheet made of short fibers, a reinforcing material, and an elastic polymer, and the short fibers are made of acrylonitrile-based copolymer composed of 50 to 95% by weight of acrylonitrile and at least one other monomer. Acrylic fibers A and B having at least two different fiber diameters are used, and the fiber diameters of the acrylic fibers A and B are respectively A is 0.1 μm or more and less than 7 μm, and B is 10 μm or more and less than 18 μm. The nonwoven fabric sheet characterized by the mixing ratio being A / B = 40 / 60-80 / 20 is described. Patent document 2 aims at providing the nonwoven fabric sheet for synthetic leather which gives an animal hair tone or a tone-like texture by using the fiber from which fineness differs, or using a different kind of fiber.
本発明は、高い引張強度と高い比引裂強度とを併有する不織布、及びその製造方法を提供することを解決すべき課題とした。 This invention made it the subject which should be solved to provide the nonwoven fabric which has both high tensile strength and high specific tear strength, and its manufacturing method.
本発明者らは上記の課題を解決するために鋭意検討した結果、数平均繊維幅2nm以上1000nm未満の第1の繊維と、数平均繊維幅1000nm以上100000nm以下であり、かつ数平均繊維長が0.1〜20mmである第2の繊維とを含有する分散液をろ過し、ろ過後の湿紙状態の不織布を乾燥することによって、高い引張強度と高い比引裂強度とを併有する不織布を製造できることを見出し、本発明を完成するに至った。 As a result of intensive studies to solve the above problems, the inventors of the present invention have a first fiber having a number average fiber width of 2 nm or more and less than 1000 nm, a number average fiber width of 1000 nm or more and 100000 nm or less, and a number average fiber length. A non-woven fabric having both high tensile strength and high specific tear strength is produced by filtering the dispersion containing the second fibers of 0.1 to 20 mm and drying the non-woven fabric in the wet paper state after filtration. The present inventors have found that this can be done and have completed the present invention.
即ち、本発明によれば、以下の発明が提供される。
(1) 数平均繊維幅2nm以上1000nm未満の第1の繊維と、数平均繊維幅1000nm以上100000nm以下であり、かつ数平均繊維長が0.1〜20mmである第2の繊維とを含有し、比引裂強度が3.0mN・m2/g以上であり、かつ引張強度が10MPa以上である不織布。
(2) 第1の繊維と第2の繊維の質量比が99.9/0.1〜50/50である、(1)に記載の不織布。
(3) 第1の繊維と第2の繊維の質量比が90/10〜60/40である、(1)又は(2)に記載の不織布。
(4) 第1の繊維の数平均繊維幅が100nm以上1000nm未満である、(1)から(3)の何れかに記載の不織布。
That is, according to the present invention, the following inventions are provided.
(1) containing a first fiber having a number average fiber width of 2 nm or more and less than 1000 nm, and a second fiber having a number average fiber width of 1000 nm or more and 100,000 nm or less and a number average fiber length of 0.1 to 20 mm. A non-woven fabric having a specific tear strength of 3.0 mN · m 2 / g or more and a tensile strength of 10 MPa or more.
(2) The nonwoven fabric as described in (1) whose mass ratio of a 1st fiber and a 2nd fiber is 99.9 / 0.1-50 / 50.
(3) The nonwoven fabric as described in (1) or (2) whose mass ratio of a 1st fiber and a 2nd fiber is 90 / 10-60 / 40.
(4) The nonwoven fabric according to any one of (1) to (3), wherein the number average fiber width of the first fibers is 100 nm or more and less than 1000 nm.
(5) 坪量が3〜200g/m2である、(1)から(4)の何れかに記載の不織布。
(6) 第1の繊維がセルロース繊維であり、第2の繊維がポリエステル繊維である、(1)から(5)の何れかに記載の不織布。
(7) 数平均繊維幅2nm以上1000nm未満の第1の繊維と、数平均繊維幅1000nm以上100000nm以下であり、かつ数平均繊維長が0.1〜20mmである第2の繊維とを含有する分散液をろ過し、ろ過後の湿紙状態の不織布を乾燥する工程を含む、(1)から(6)の何れかに記載の不織布の製造方法。
(5) The nonwoven fabric according to any one of (1) to (4), wherein the basis weight is 3 to 200 g / m 2 .
(6) The nonwoven fabric according to any one of (1) to (5), wherein the first fiber is a cellulose fiber and the second fiber is a polyester fiber.
(7) containing a first fiber having a number average fiber width of 2 nm or more and less than 1000 nm, and a second fiber having a number average fiber width of 1000 nm or more and 100,000 nm or less and a number average fiber length of 0.1 to 20 mm. The manufacturing method of the nonwoven fabric in any one of (1) to (6) including the process of filtering a dispersion liquid and drying the nonwoven fabric of the wet paper state after filtration.
本発明によれば、高い引張強度と高い比引裂強度とを併有する不織布が提供される。 According to the present invention, a nonwoven fabric having both high tensile strength and high specific tear strength is provided.
以下、本発明について更に詳細に説明する。
本発明の不織布は、数平均繊維幅2nm以上1000nm未満の第1の繊維と、数平均繊維幅1000nm以上100000nm以下であり、かつ数平均繊維長が0.1〜20mmである第2の繊維とを含有し、比引裂強度が3.0mN・m2/g以上であり、かつ引張強度が10MPa以上であることを特徴とする。
Hereinafter, the present invention will be described in more detail.
The nonwoven fabric of the present invention includes a first fiber having a number average fiber width of 2 nm to less than 1000 nm, a second fiber having a number average fiber width of 1000 nm to 100,000 nm, and a number average fiber length of 0.1 to 20 mm. The specific tear strength is 3.0 mN · m 2 / g or more, and the tensile strength is 10 MPa or more.
[第1の繊維]
本発明で用いる第1の繊維は、数平均繊維幅が2nm以上1000nm未満の微細繊維であればその種類は特に限定されず、例えば、微細セルロース繊維でもよいし、微細セルロース繊維以外の微細繊維でもよく、また微細セルロース繊維と、微細セルロース繊維以外の微細繊維との混合物でもよい。特に好ましくは、第1の繊維はセルロース繊維である。
[First fiber]
The first fiber used in the present invention is not particularly limited as long as the number average fiber width is a fine fiber having a number average fiber width of 2 nm or more and less than 1000 nm. For example, the first fiber may be a fine cellulose fiber or a fine fiber other than a fine cellulose fiber. Moreover, a mixture of fine cellulose fibers and fine fibers other than fine cellulose fibers may be used. Particularly preferably, the first fiber is a cellulose fiber.
微細セルロース繊維の詳細については後記する。微細セルロース繊維以外の繊維としては、例えば、無機繊維、有機繊維、合成繊維等、半合成繊維、再生繊維が挙げられるが特に限定されない。無機繊維としては、例えば、ガラス繊維、岩石繊維、金属繊維等が挙げられるがこれらに限定されない。有機繊維としては、例えば、炭素繊維、キチン、キトサン等の天然物由来の繊維等が挙げられるがこれらに限定されない。合成繊維としては、例えば、ナイロン、ピニロン、ビニリデン、ポリエステル、ポリオレフィン(例えばポリエチレン、ポリプロピレンなど)、ポリウレタン、アクリル、ポリ塩化ビニル、アラミド等が挙げられるがこれらに限定されない。半合成繊維としては、アセテート、トリアセテート、プロミックス等が挙げられるがこれらに限定されない。再生繊維としては、例えば、レーヨン、キュプラ、ポリノジックレーヨン、リヨセル、テンセル等が挙げられるがこれらに限定されない。微細セルロース繊維と微細セルロース繊維以外の微細繊維を混合して用いる場合、微細セルロース繊維以外の微細繊維は、必要に応じて化学的処理、解繊処理等の処理を施すことができる。微細セルロース繊維以外の微細繊維に化学的処理、解繊処理等の処理を施す場合、微細セルロース繊維以外の微細繊維は、微細セルロース繊維と混合してから化学的処理、解繊処理等の処理を施すこともできるし、微細セルロース繊維以外の微細繊維に化学的処理、解繊処理等の処理を施してから微細セルロース繊維と混合することもできる。微細セルロース繊維以外の微細繊維を混合する場合、微細セルロース繊維と微細セルロース繊維以外の微細繊維の合計量における微細セルロース繊維以外の微細繊維の添加量は特に限定されないが、好ましくは50質量%以下であり、より好ましくは40質量%以下であり、さらに好ましくは30質量%以下である。特に好ましくは20質量%以下である。 Details of the fine cellulose fibers will be described later. Examples of fibers other than fine cellulose fibers include, but are not limited to, semi-synthetic fibers and regenerated fibers such as inorganic fibers, organic fibers, and synthetic fibers. Examples of inorganic fibers include, but are not limited to, glass fibers, rock fibers, and metal fibers. Examples of organic fibers include, but are not limited to, fibers derived from natural products such as carbon fibers, chitin, and chitosan. Examples of synthetic fibers include, but are not limited to, nylon, pinilone, vinylidene, polyester, polyolefin (eg, polyethylene, polypropylene, etc.), polyurethane, acrylic, polyvinyl chloride, aramid, and the like. Semi-synthetic fibers include but are not limited to acetate, triacetate, promix and the like. Examples of the regenerated fiber include, but are not limited to, rayon, cupra, polynosic rayon, lyocell, and tencel. When the fine cellulose fibers and fine fibers other than the fine cellulose fibers are mixed and used, the fine fibers other than the fine cellulose fibers can be subjected to treatments such as chemical treatment and defibration treatment as necessary. When fine fibers other than fine cellulose fibers are subjected to treatment such as chemical treatment and defibration treatment, fine fibers other than fine cellulose fibers are mixed with fine cellulose fibers and then subjected to treatment such as chemical treatment and defibration treatment. It can also be applied, and fine fibers other than fine cellulose fibers can be subjected to treatment such as chemical treatment and defibration treatment and then mixed with fine cellulose fibers. When mixing fine fibers other than fine cellulose fibers, the amount of fine fibers other than fine cellulose fibers in the total amount of fine cellulose fibers and fine cellulose fibers other than fine cellulose fibers is not particularly limited, but is preferably 50% by mass or less. Yes, more preferably 40% by mass or less, still more preferably 30% by mass or less. Especially preferably, it is 20 mass% or less.
<微細セルロース繊維>
本発明においては、第1の繊維として、セルロース原料を化学的処理及び解繊処理することによって得られる微細セルロース繊維を使用してもよい。
セルロース原料としては、製紙用パルプ、コットンリンターやコットンリントなどの綿系パルプ、麻、麦わら、パガスなどの非木材系パルプ、ホヤや海草などから単離されるセルロースなどが挙げられるが、特に限定されない。これらの中でも、入手のしやすさという点で、製紙用パルプが好ましいが、特に限定されない。製紙用パルプとしては、広葉樹クラフトパルプ(晒クラフトパルプ(LBKP)、未晒クラフトパルプ(LUKP)、酸素漂白クラフトパルプ(LOKP)など)、針葉樹クラフトパルプ(晒クラフトパルプ(NBKP)、未晒クラフトパルプ(NUKP)、酸素漂白クラフトパルプ(NOKP)など)、サルファイトパルプ(SP)、ソーダパルプ(AP)等の化学パルプ、セミケミカルパルプ(SCP)、ケミグラウンドウッドパルプ(CGP)等の半化学パルプ、砕木パルプ(GP)、サーモメカニカルパルプ(TMP、BCTMP)等の機械パルプ、楮、三椏、麻、ケナフ等を原料とする非木材パルプ、古紙を原料とする脱墨パルプが挙げられるが、特に限定されない。これらの中でも、より入手しやすいことから、クラフトパルプ、脱墨パルプ、サルファイトパルプが好ましいが、特に限定されない。セルロース原料は1種を単独で用いてもよいし、2種以上混合して用いてもよい。
<Fine cellulose fiber>
In the present invention, fine cellulose fibers obtained by chemically treating and defibrating cellulose raw materials may be used as the first fibers.
Examples of the cellulose raw material include paper pulp, cotton pulp such as cotton linter and cotton lint, non-wood pulp such as hemp, straw, and pagas, cellulose isolated from sea squirts and seaweed, etc., but are not particularly limited. . Among these, paper pulp is preferable in terms of availability, but is not particularly limited. Paper pulp includes hardwood kraft pulp (bleached kraft pulp (LBKP), unbleached kraft pulp (LUKP), oxygen bleached kraft pulp (LOKP), etc.), softwood kraft pulp (bleached kraft pulp (NBKP), unbleached kraft pulp) (NUCKP, oxygen bleached kraft pulp (NOKP), etc.), sulfite pulp (SP), chemical pulp such as soda pulp (AP), semi-chemical pulp (SCP), semi-chemical pulp such as chemiground wood pulp (CGP) In addition, mechanical pulp such as groundwood pulp (GP) and thermomechanical pulp (TMP, BCTMP), non-wood pulp made from cocoons, cocoons, hemp, kenaf, etc., deinked pulp made from waste paper, It is not limited. Among these, kraft pulp, deinked pulp, and sulfite pulp are preferable because they are more easily available, but are not particularly limited. A cellulose raw material may be used individually by 1 type, and may be used in mixture of 2 or more types.
微細セルロース繊維の数平均繊維幅は、2nm以上1000nm未満であり、より好ましくは数平均繊維幅100nm以上1000nm未満である。微細セルロース繊維は、通常製紙用途で用いるパルプ繊維よりもはるかに細いセルロース繊維あるいは棒状粒子でもよい。微細セルロース繊維は結晶部分を含むセルロース分子の集合体であり、その結晶構造はI型(平行鎖)である。微細セルロース繊維の数平均繊維幅は電子顕微鏡で観察して測定することができる。微細セルロース繊維の平均繊維幅が2nm未満であると、セルロース分子として水に溶解しているため、微細セルロース繊維としての物性(強度や剛性、寸法安定性)が発現しなくなる。ここで、微細セルロース繊維がI型結晶構造をとっていることは、グラファイトで単色化したCuKα(λ=1.5418Å)を用いた広角X線回折写真より得られる回折プロファイルにおいて、2θ=14〜17°付近と2θ=22〜23°付近の2箇所の位置に典型的なピークをもつことから同定することができる。また、微細セルロース繊維の電子顕微鏡観察による繊維幅の測定は以下のようにして行う。濃度0.05〜0.1質量%の微細セルロース繊維の水系懸濁液を調製し、該懸濁液を親水化処理したカーボン膜被覆グリッド上にキャストしてTEM観察用試料とする。幅の広い繊維を含む場合には、ガラス上にキャストした表面のSEM像を観察してもよい。構成する繊維の幅に応じて1000倍、5000倍、10000倍あるいは50000倍のいずれかの倍率で電子顕微鏡画像による観察を行う。但し、試料、観察条件や倍率は下記の条件を満たすように調整する。 The number average fiber width of the fine cellulose fibers is 2 nm or more and less than 1000 nm, and more preferably the number average fiber width is 100 nm or more and less than 1000 nm. The fine cellulose fibers may be cellulose fibers or rod-like particles that are much thinner than the pulp fibers normally used in papermaking applications. The fine cellulose fiber is an aggregate of cellulose molecules including a crystal part, and its crystal structure is type I (parallel chain). The number average fiber width of the fine cellulose fibers can be measured by observing with an electron microscope. When the average fiber width of the fine cellulose fiber is less than 2 nm, the physical properties (strength, rigidity, dimensional stability) as the fine cellulose fiber are not exhibited because the cellulose molecule is dissolved in water. Here, the fact that the fine cellulose fiber has the I-type crystal structure is that in a diffraction profile obtained from a wide angle X-ray diffraction photograph using CuKα (λ = 1.54181.5) monochromatized with graphite, 2θ = 14˜ It can be identified by having typical peaks at two positions near 17 ° and 2θ = 22-23 °. Moreover, the measurement of the fiber width by electron microscope observation of a fine cellulose fiber is performed as follows. An aqueous suspension of fine cellulose fibers having a concentration of 0.05 to 0.1% by mass is prepared, and the suspension is cast on a carbon film-coated grid subjected to a hydrophilic treatment to obtain a sample for TEM observation. When a wide fiber is included, an SEM image of the surface cast on glass may be observed. Observation with an electron microscope image is performed at a magnification of 1000 times, 5000 times, 10000 times, or 50000 times depending on the width of the constituent fibers. However, the sample, observation conditions, and magnification are adjusted to satisfy the following conditions.
(1)観察画像内の任意箇所に一本の直線Xを引き、該直線Xに対し、20本以上の繊維が交差する。
(2)同じ画像内で該直線と垂直に交差する直線Yを引き、該直線Yに対し、20本以上の繊維が交差する。
(1) One straight line X is drawn at an arbitrary location in the observation image, and 20 or more fibers intersect the straight line X.
(2) A straight line Y perpendicular to the straight line is drawn in the same image, and 20 or more fibers intersect the straight line Y.
上記条件を満足する観察画像に対し、直線X、直線Yと交錯する繊維の幅を目視で読み取る。こうして少なくとも重なっていない表面部分の画像を3組以上観察し、各々の画像に対して、直線X、直線Yと交錯する繊維の幅を読み取る。このように少なくとも20本×2×3=120本の繊維幅を読み取る。微細セルロース繊維の平均繊維幅はこのように読み取った繊維幅の平均値である。 The width of the fiber that intersects with the straight line X and the straight line Y is visually read from the observation image that satisfies the above conditions. In this way, at least three sets of images of the surface portion that do not overlap each other are observed, and the width of the fiber intersecting with the straight line X and the straight line Y is read for each image. Thus, at least 20 × 2 × 3 = 120 fiber widths are read. The average fiber width of fine cellulose fibers is the average value of the fiber widths read in this way.
微細セルロース繊維の繊維長は特に限定されないが、1〜1000μmが好ましく、5〜800μmがさらに好ましく、10〜600μmが特に好ましい。繊維長が1μm未満になると、微細繊維シートを形成し難くなる。1000μmを超えると微細繊維のスラリー粘度が非常に高くなり、扱いづらくなる。繊維長は、TEM、SEM、AFMによる画像解析より求めることができる。 Although the fiber length of a fine cellulose fiber is not specifically limited, 1-1000 micrometers is preferable, 5-800 micrometers is more preferable, and 10-600 micrometers is especially preferable. When the fiber length is less than 1 μm, it is difficult to form a fine fiber sheet. If it exceeds 1000 μm, the slurry viscosity of the fine fibers becomes very high and it becomes difficult to handle. The fiber length can be obtained by image analysis using TEM, SEM, or AFM.
<化学的処理>
セルロース原料又はその他の繊維原料(無機繊維、有機繊維、合成繊維等、半合成繊維、再生繊維など)の化学的処理の方法は、微細繊維を得ることができる方法である限り特に限定されないが、例えば、オゾン処理、酵素処理、又はセルロース又は繊維原料中の官能基と共有結合を形成し得る化合物による処理などが挙げられるがこれらに限定されない。
<Chemical treatment>
The method of chemical treatment of cellulose raw material or other fiber raw material (inorganic fiber, organic fiber, synthetic fiber, semi-synthetic fiber, regenerated fiber, etc.) is not particularly limited as long as it is a method capable of obtaining fine fibers, Examples include, but are not limited to, ozone treatment, enzyme treatment, or treatment with a compound capable of forming a covalent bond with a functional group in cellulose or a fiber raw material.
オゾン処理の一例としては、特開2010−254726号公報に記載されている方法を挙げることができるが特に限定されない。具体的には、繊維をオゾン処理した後、水に分散し、得られた繊維の水系分散液を粉砕処理する。 As an example of the ozone treatment, there is a method described in JP 2010-254726 A, but it is not particularly limited. Specifically, after the fiber is treated with ozone, it is dispersed in water, and the resulting aqueous dispersion of the fiber is pulverized.
酵素処理の一例としては、特願2012−115411号(特願2012−115411号に記載の内容は全て本明細書中に引用されるものとする)に記載の方法を挙げることができるが特に限定されない。具体的には、繊維原料を、少なくとも酵素のEG活性とCBHI活性の比が0.06以上の条件下で、酵素で処理する方法である。 As an example of the enzyme treatment, the method described in Japanese Patent Application No. 2012-115411 (all the contents described in Japanese Patent Application No. 2012-115411 shall be cited in the present specification) can be mentioned, but it is particularly limited. Not. Specifically, the fiber raw material is treated with an enzyme at least under a condition where the ratio of the enzyme EG activity to the CBHI activity is 0.06 or more.
セルロース又は繊維原料中の官能基と共有結合を形成し得る化合物による処理としては、特開2011−162608号公報に記載されている四級アンモニウム基を有する化合物による処理、特願2012−24457(特願2012−24457に記載の内容は全て本明細書中に引用されるものとする)に記載されているカルボン酸系化合物を使用する方法、並びに特願2011−252649(特願2011−252649に記載の内容は全て本明細書中に引用されるものとする)に記載されている「構造中にリン原子を含有するオキソ酸、ポリオキソ酸又はそれらの塩から選ばれる少なくとも1種の化合物」を使用する方法などを挙げることができるが、特に限定されない。 As the treatment with a compound capable of forming a covalent bond with a functional group in cellulose or a fiber raw material, treatment with a compound having a quaternary ammonium group described in JP 2011-162608 A, Japanese Patent Application No. 2012-24457 The contents described in the application 2012-24457 are all cited in the present specification) and the method using the carboxylic acid compound described in the application, as well as the Japanese Patent Application No. 2011-252649 (described in the Japanese Patent Application No. 2011-252649) The contents of are all cited in the present specification) "at least one compound selected from oxo acids, polyoxo acids or salts thereof containing a phosphorus atom in the structure" The method of doing, etc. can be mentioned, However It does not specifically limit.
特開2011−162608号公報に記載されている四級アンモニウム基を有する化合物による処理は、繊維中の水酸基と四級アンモニウム基を有するカチオン化剤とを反応させて、該繊維をカチオン変性する方法である。 The treatment with a compound having a quaternary ammonium group described in JP 2011-162608 A is a method of reacting a hydroxyl group in a fiber with a cationizing agent having a quaternary ammonium group to cation-modify the fiber. It is.
特願2012−24457に記載されているカルボン酸系化合物を使用する方法とは、2つ以上のカルボキシ基を有する化合物、2つ以上のカルボキシ基を有する化合物の酸無水物、およびそれらの誘導体よりなる群から選ばれる少なくとも1種のカルボン酸系化合物により、繊維原料を処理して、繊維原料にカルボキシ基を導入するカルボキシ基導入工程と、前記カルボキシ基導入工程終了後に、カルボキシ基を導入した繊維原料をアルカリ溶液で処理するアルカリ処理工程を含む方法である。 The method using a carboxylic acid compound described in Japanese Patent Application No. 2012-24457 is a compound having two or more carboxy groups, an acid anhydride of a compound having two or more carboxy groups, and derivatives thereof. The fiber raw material is treated with at least one carboxylic acid compound selected from the group consisting of a carboxy group introducing step for introducing a carboxy group into the fiber raw material, and a fiber having a carboxy group introduced after completion of the carboxy group introducing step. It is a method including an alkali treatment step of treating a raw material with an alkali solution.
特願2011−252649に記載されている構造中にリン原子を含有するオキソ酸、ポリオキソ酸又はそれらの塩から選ばれる少なくとも1種の化合物(以下化合物Aと称す)により繊維原料を処理する方法としては、繊維原料に化合物Aの粉末や水溶液を混合する方法、繊維原料のスラリーに化合物Aの水溶液を添加する方法等が挙げられる。化合物Aはリン酸、ポリリン酸、亜リン酸、ホスホン酸、ポリホスホン酸あるいはこれらのエステルが挙げられるが特に限定されない。また、これらは塩の形を取っても構わない。リン酸基を有する化合物としては、リン酸、リン酸のナトリウム塩であるリン酸二水素ナトリウム、リン酸水素二ナトリウム、リン酸三ナトリウム、ピロリン酸ナトリウム、メタリン酸ナトリウム、更にリン酸のカリウム塩であるリン酸二水素カリウム、リン酸水素二カリウム、リン酸三カリウム、ピロリン酸カリウム、メタリン酸カリウム、更にリン酸のアンモニウム塩であるリン酸二水素アンモニウム、リン酸水素二アンモニウム、リン酸三アンモニウム、ピロリン酸アンモニウム、メタリン酸アンモニウムなどが挙げられるが特に限定されない。 As a method of treating a fiber raw material with at least one compound (hereinafter referred to as Compound A) selected from oxo acids, polyoxo acids or salts thereof containing a phosphorus atom in the structure described in Japanese Patent Application No. 2011-252649 Examples thereof include a method of mixing a powder or aqueous solution of Compound A with a fiber raw material, a method of adding an aqueous solution of Compound A to a fiber raw material slurry, and the like. Compound A includes, but is not limited to, phosphoric acid, polyphosphoric acid, phosphorous acid, phosphonic acid, polyphosphonic acid or esters thereof. Moreover, these may take the form of a salt. Examples of the compound having a phosphate group include phosphoric acid, sodium phosphate sodium phosphate, disodium hydrogen phosphate, trisodium phosphate, sodium pyrophosphate, sodium metaphosphate, and potassium phosphate. Potassium dihydrogen phosphate, dipotassium hydrogen phosphate, tripotassium phosphate, potassium pyrophosphate, potassium metaphosphate, and ammonium phosphates, ammonium dihydrogen phosphate, diammonium hydrogen phosphate, triphosphate Examples thereof include ammonium, ammonium pyrophosphate, and ammonium metaphosphate, but are not particularly limited.
<解繊処理>
セルロース原料又はその他の繊維原料(無機繊維、有機繊維、合成繊維等、半合成繊維、再生繊維など)は解繊処理に供することにより微細化して、数平均繊維幅が2nm以上1000nm未満の微細繊維を得ることができる。解繊処理工程では、解繊処理装置を用いて、前記の化学的処理で得られた原料を解繊処理して、微細繊維分散液を得ることができる。
<Defibration processing>
Cellulose raw materials or other fiber raw materials (inorganic fibers, organic fibers, synthetic fibers, semi-synthetic fibers, regenerated fibers, etc.) are refined by subjecting them to a defibrating treatment, and the number average fiber width is 2 nm or more and less than 1000 nm. Can be obtained. In the defibrating treatment step, the raw material obtained by the chemical treatment can be defibrated using a defibrating apparatus to obtain a fine fiber dispersion.
解繊処理装置としては、グラインダー(石臼型粉砕機)、高圧ホモジナイザー、超高圧ホモジナイザー、高圧衝突型粉砕機、ボールミル、ディスク型リファイナー、コニカルリファイナー、二軸混練機、振動ミル、高速回転下でのホモミキサー、超音波分散機、ビーターなど、湿式粉砕する装置等を適宜使用することができるが、特にこれらに限定されない。 Defibration treatment equipment includes grinders (stone mills), high-pressure homogenizers, ultra-high-pressure homogenizers, high-pressure collision grinders, ball mills, disk refiners, conical refiners, twin-screw kneaders, vibration mills, high-speed rotations An apparatus for wet pulverization such as a homomixer, an ultrasonic disperser, and a beater can be used as appropriate, but is not particularly limited thereto.
[第2の繊維]
本発明で用いる第2の繊維は、数平均繊維幅1000nm以上100000nm以下であり、かつ数平均繊維長が0.1〜20mmであればその種類は特に限定されず、例えば、第1の繊維に関連して上記した、セルロース繊維、無機繊維、有機繊維、合成繊維等、半合成繊維、再生繊維などが挙げられるが特に限定されない。第2の繊維としては、上記の中でも合成繊維が特に好ましく、ポリエステルが最も好ましい。
[Secondary fiber]
The type of the second fiber used in the present invention is not particularly limited as long as the number average fiber width is 1000 nm or more and 100000 nm or less, and the number average fiber length is 0.1 to 20 mm. The above-mentioned cellulose fiber, inorganic fiber, organic fiber, synthetic fiber, semi-synthetic fiber, regenerated fiber and the like can be mentioned but are not particularly limited. Of the above, the second fibers are particularly preferably synthetic fibers, and most preferably polyester.
[第1の繊維と第2の繊維の質量比]
本発明において、第1の繊維と第2の繊維の質量比は、製造される不織布が3.0mN・m2/g以上の比引裂強度と、10MPa以上の引張強度とを有する限り、特に限定
されない。即ち、第1の繊維と第2の繊維の種類に応じて、製造される不織布が3.0mN・m2/g以上の比引裂強度と、10MPa以上の引張強度とを有するような第1の繊維と第2の繊維の質量比を設定して、使用することができる。好ましくは、第1の繊維と第2の繊維の質量比は、99.9/0.1〜50/50であり、さらに好ましくは、90/10〜60/40である。第2の繊維の質量比が0.1未満になると、比引裂強度が低下し、また第2の繊維の質量比が50を超えると引張強度が低下する傾向が見られ、好ましくない。
[Mass ratio of first fiber to second fiber]
In the present invention, the mass ratio between the first fiber and the second fiber is particularly limited as long as the produced nonwoven fabric has a specific tear strength of 3.0 mN · m 2 / g or more and a tensile strength of 10 MPa or more. Not. That is, according to the type of the first fiber and the second fiber, the first nonwoven fabric to be manufactured has a specific tear strength of 3.0 mN · m 2 / g or more and a tensile strength of 10 MPa or more. The mass ratio of the fiber and the second fiber can be set and used. Preferably, the mass ratio of the first fiber to the second fiber is 99.9 / 0.1 to 50/50, and more preferably 90/10 to 60/40. When the mass ratio of the second fibers is less than 0.1, the specific tear strength is lowered, and when the mass ratio of the second fibers exceeds 50, the tensile strength tends to be lowered, which is not preferable.
[不織布]
本発明の不織布は、3.0mN・m2/g以上の比引裂強度と、10MPa以上の引張強度を有する。即ち、本発明の不織布は、高い比引裂強度と、高い引張強度とを併有することを特徴とする。比引裂強度は3.0mN・m2/g以上であればその上限は特に限定されない。比引裂強度は、例えば3.0〜50mN・m2/g、好ましくは3.0〜40mN・m2/g、より好ましくは3.0〜30mN・m2/gであり、さらに好ましくは10〜50mN・m2/gであり、さらに好ましくは10〜40mN・m2/gであり、さらに好ましくは10〜30mN・m2/gである。引張強度は10MPa以上であればその上限は特に限定されない。引張強度は、例えば10〜200MPaであり、好ましくは10〜150MPaであり、より好ましくは10〜100MPaであり、さらに好ましくは10〜80MPaであり、さらに好ましくは20〜80MPaであり、特に好ましくは20〜50MPaである。
[Nonwoven fabric]
The nonwoven fabric of the present invention has a specific tear strength of 3.0 mN · m 2 / g or more and a tensile strength of 10 MPa or more. That is, the nonwoven fabric of the present invention is characterized by having both high specific tear strength and high tensile strength. If the specific tear strength is 3.0 mN · m 2 / g or more, the upper limit is not particularly limited. The specific tear strength is, for example, 3.0 to 50 mN · m 2 / g, preferably 3.0 to 40 mN · m 2 / g, more preferably 3.0 to 30 mN · m 2 / g, and even more preferably 10 It is -50mN * m < 2 > / g, More preferably, it is 10-40mN * m < 2 > / g, More preferably, it is 10-30mN * m < 2 > / g. The upper limit is not particularly limited as long as the tensile strength is 10 MPa or more. The tensile strength is, for example, 10 to 200 MPa, preferably 10 to 150 MPa, more preferably 10 to 100 MPa, still more preferably 10 to 80 MPa, still more preferably 20 to 80 MPa, and particularly preferably 20 ~ 50 MPa.
本発明の不織布の坪量は特に限定されないが、好ましくは3〜200g/m2であり、より好ましくは10〜100g/m2であり、さらに好ましくは20〜60g/m2である。 The basis weight of the nonwoven fabric of the present invention is not particularly limited, preferably 3~200g / m 2, more preferably from 10 to 100 g / m 2, more preferably from 20 to 60 g / m 2.
本発明の不織布には、用途に応じた添加剤、例えば、サイズ剤、ワックス、無機充填剤、着色剤、安定化剤(酸化防止剤、熱安定剤、紫外線吸収剤など)、可塑剤、帯電防止剤、難燃剤などを含有させもよい。 The nonwoven fabric of the present invention has additives depending on the application, such as sizing agent, wax, inorganic filler, colorant, stabilizer (antioxidant, heat stabilizer, ultraviolet absorber, etc.), plasticizer, charging An inhibitor, a flame retardant, and the like may be included.
本発明の不織布の厚みは特に限定されず、一般的には1〜100μm程度である。不織布は、目的に応じて複数の不織布を積層してもよい。 The thickness of the nonwoven fabric of this invention is not specifically limited, Generally, it is about 1-100 micrometers. A nonwoven fabric may laminate | stack a some nonwoven fabric according to the objective.
[不織布の製造方法]
本発明の不織布の製造方法は、特に限定されず、例えば、第1の繊維と第2の繊維とを混合し、湿式抄紙又は乾式抄紙などの抄紙により製造できる。
[Method for producing nonwoven fabric]
The manufacturing method of the nonwoven fabric of this invention is not specifically limited, For example, it can manufacture by mixing 1st fiber and 2nd fiber and making paper, such as wet papermaking or dry papermaking.
湿式抄紙は、通常の方法で行うことができ、例えば、手抄き抄紙器や多孔板などを備えた湿式抄紙機などを用いて抄紙してもよい。乾式抄紙も、慣用の方法、例えば、エアレイド製法、カード製法などを用いて抄紙することができる。 The wet papermaking can be performed by a usual method, and for example, the papermaking may be performed using a wet papermaking machine equipped with a manual papermaking machine or a perforated plate. Dry papermaking can also be made using conventional methods such as airlaid and card manufacturing.
例えば、本発明では、第1の繊維と第2の繊維を含有する分散液を用いて、湿式抄紙により、不織布を製造することができる。分散液は、第1の繊維と第2の繊維と分散媒とを含有する液である。分散媒としては、水、有機溶剤を使用することができるが、取り扱い性やコストの点から、水のみが好ましいが、特には限定されない。有機溶剤を使用する場合でも水と併用することが好ましいが、特には限定されない。水と併用する有機溶剤としては、アルコール系溶剤(メタノール、エタノール、プロパノール、ブタノール等)、ケトン系溶剤(アセトン、メチルエチルケトン等)、エーテル系溶剤(ジエチルエーテル、エチレングリコールジメチルエーテル、テトラヒドロフラン等)、アセテート系溶剤(酢酸エチル等)等の極性溶剤が好ましいが、特にこれらに限定されない。分散液における固形分濃度は、特に限定されないが、0.05〜10質量%であることが好ましく、0.1〜5質量%であることがより好ましい。上記した分散液をろ過し、ろ過後の湿紙状態の不織布を乾燥することによって本発明の不織布を製造することができる。
以下の実施例により本発明を更に詳細に説明するが、本発明はこれらの実施例によって限定されるものではない。
For example, in the present invention, a non-woven fabric can be produced by wet papermaking using a dispersion containing first fibers and second fibers. The dispersion liquid is a liquid containing first fibers, second fibers, and a dispersion medium. As the dispersion medium, water or an organic solvent can be used, but from the viewpoint of handleability and cost, only water is preferable, but it is not particularly limited. Even when an organic solvent is used, it is preferably used in combination with water, but is not particularly limited. Organic solvents used in combination with water include alcohol solvents (methanol, ethanol, propanol, butanol, etc.), ketone solvents (acetone, methyl ethyl ketone, etc.), ether solvents (diethyl ether, ethylene glycol dimethyl ether, tetrahydrofuran, etc.), acetate solvents A polar solvent such as a solvent (such as ethyl acetate) is preferable, but the solvent is not particularly limited thereto. Although the solid content concentration in a dispersion liquid is not specifically limited, It is preferable that it is 0.05-10 mass%, and it is more preferable that it is 0.1-5 mass%. The nonwoven fabric of the present invention can be produced by filtering the above dispersion and drying the nonwoven fabric in the wet paper state after filtration.
The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples.
(実施例1)
針葉樹晒クラフトパルプ(NBKP)をダブルディスクリファイナーにて変則フリーネスが100mlになるまで叩解し、濃度2%のパルプ分散液(A)を得た。このときの数平均繊維長は0.30mm、数平均繊維幅は24400nmであった。これを濃度が0.2%になるようにイオン交換水で希釈し、NiroSoavi社製高圧ホモジナイザー「Panda Plus2000」により処理圧力120MPaで3回の微細化処理を行い、セルロース微細繊維含有分散液(B)を得た。このときの数平均繊維幅は130nmであった。
Example 1
Softwood bleached kraft pulp (NBKP) was beaten with a double disc refiner until the irregular freeness reached 100 ml to obtain a pulp dispersion (A) having a concentration of 2%. The number average fiber length at this time was 0.30 mm, and the number average fiber width was 24400 nm. This was diluted with ion-exchanged water so that the concentration was 0.2%, and subjected to a micronization process three times at a processing pressure of 120 MPa with a high-pressure homogenizer “Panda Plus 2000” manufactured by NiroSoavi, and a dispersion containing cellulose fine fibers (B ) The number average fiber width at this time was 130 nm.
セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」(数平均繊維幅20000nm、数平均繊維長6.0mm)を、セルロース/ポリエステル短繊維が重量比で98/2となるように混合し、スリーワンモーターにて全量が十分混合されるように5分間攪拌し、セルロース微細繊維・ポリエステル短繊維混合分散液(C)を得た。 A polyester short fiber “N801” (number average fiber width 20000 nm, number average fiber length 6.0 mm) manufactured by Nihon Ester Co., Ltd. with respect to the cellulose fine fiber-containing dispersion (B) is obtained. The mixture was mixed for 2 minutes and stirred for 5 minutes so that the whole amount was sufficiently mixed with a three-one motor, to obtain a cellulose fine fiber / polyester short fiber mixed dispersion (C).
セルロース微細繊維・ポリエステル短繊維混合分散液(C)を、不織布の仕上がり坪量が40.0g/m2になるように調整し、焼結サイズが30〜50μmのアドバンテック社製ブフナーロート型ガラスフィルター「KG−90」上にアドバンテック社製PTFEメンブレンを載せたろ過瓶上に流延し、アスピレーターで吸引しながらろ過を行った。ろ過後の湿紙状態の不織布を105℃に加熱したシリンダドライヤーで0.1MPaに加圧しながら乾燥し、不織布を得た。以上の手順を経て得られた不織布の坪量は39.6g/m2であった。 Adjusting the cellulose fine fiber / polyester short fiber mixed dispersion (C) so that the finished basis weight of the non-woven fabric is 40.0 g / m 2 and the sintered size is 30-50 μm Buchner funnel type glass filter manufactured by Advantech The solution was cast on a filter bottle in which a PTFE membrane manufactured by Advantech was placed on “KG-90”, and filtered while sucking with an aspirator. The nonwoven fabric in a wet paper state after filtration was dried while being pressurized to 0.1 MPa with a cylinder dryer heated to 105 ° C. to obtain a nonwoven fabric. The basis weight of the nonwoven fabric obtained through the above procedure was 39.6 g / m 2 .
(実施例2)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で95/5となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は39.8g/m2であった。
(Example 2)
In Example 1, an operation other than mixing the polyester fine fiber “N801” manufactured by Nihon Ester Co., Ltd. with the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 95/5. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 39.8 g / m 2 .
(実験例3)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で90/10となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は40.4g/m2であった。
(Experimental example 3)
In Example 1, the operation other than mixing the polyester short fiber “N801” manufactured by Nippon Ester Co., Ltd. with the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 90/10. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 40.4 g / m 2 .
(実施例4)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で80/20となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は40.2g/m2であった。
Example 4
In Example 1, the operation other than mixing the polyester short fiber “N801” manufactured by Nippon Ester Co., Ltd. with the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 80/20. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 40.2 g / m 2 .
(実施例5)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で70/30となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は39.8g/m2であった。
(Example 5)
In Example 1, an operation other than mixing the polyester short fiber “N801” manufactured by Nippon Ester Co., Ltd. with the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 70/30. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 39.8 g / m 2 .
(実施例6)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で60/40となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は40.2g/m2であった。
Example 6
In Example 1, an operation other than mixing the polyester fine fiber “N801” manufactured by Nippon Ester Co., Ltd. with the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 60/40. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 40.2 g / m 2 .
(実施例7)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で50/50となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は40.8g/m2であった。
(Example 7)
In Example 1, an operation other than mixing the polyester fine fiber “N801” manufactured by Nihon Ester Co., Ltd. with the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 50/50. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 40.8 g / m 2 .
(比較例1)
実施例1において、セルロース微細繊維含有分散液(B)に対し、日本エステル社製ポリエステル短繊維「N801」を、セルロース/ポリエステル短繊維が重量比で20/80となるように混合した以外の操作は同様とし、不織布を得た。得られた不織布の坪量は39.6g/m2であった。
(Comparative Example 1)
In Example 1, the operation other than mixing the polyester short fiber “N801” manufactured by Nihon Ester Co., Ltd. to the cellulose fine fiber-containing dispersion (B) so that the weight ratio of cellulose / polyester short fiber is 20/80. Was the same, and a nonwoven fabric was obtained. The basis weight of the obtained nonwoven fabric was 39.6 g / m 2 .
(比較例2)
実施例1において、セルロース微細繊維含有分散液(B)に対しその他の繊維を混合せず、不織布の仕上がり坪量が40.0g/m2になるように調整した。その後は実験例1と同様の方法で不織布を得た。得られた不織布の坪量は39.5g/m2であった。
(Comparative Example 2)
In Example 1, other fibers were not mixed into the cellulose fine fiber-containing dispersion (B), and the finished basis weight of the nonwoven fabric was adjusted to 40.0 g / m 2 . Thereafter, a nonwoven fabric was obtained in the same manner as in Experimental Example 1. The basis weight of the obtained nonwoven fabric was 39.5 g / m 2 .
(比較例3)
針葉樹晒クラフトパルプ(NBKP)を、東西精器社製ナイアガラビーターで200分間叩解し、濃度2%のパルプ分散液を得た。このときの数平均繊維長は0.45mm、数平均繊維幅は25000nmであった。
得られたパルプ分散液を脱水して濃度3%にし、0.1%硫酸でpH6に調整し、50℃になるまで水浴で温めた後、Genencor社製セルラーゼ「Optimase cx 7L」をパルプ分散液の固形分に対して3%添加し、50℃、1時間撹拌しながら反応させて、酵素処理パルプ分散液を得た。
(Comparative Example 3)
Softwood bleached kraft pulp (NBKP) was beaten with a Niagara beater manufactured by Tozai Seiki Co., Ltd. for 200 minutes to obtain a pulp dispersion having a concentration of 2%. The number average fiber length at this time was 0.45 mm, and the number average fiber width was 25000 nm.
The obtained pulp dispersion was dehydrated to a concentration of 3%, adjusted to pH 6 with 0.1% sulfuric acid, warmed to 50 ° C. in a water bath, and then cellulase “Optimase cx 7L” manufactured by Genencor was added to the pulp dispersion. 3% of the solid content was added and reacted with stirring at 50 ° C. for 1 hour to obtain an enzyme-treated pulp dispersion.
酵素処理パルプ分散液を95℃以上、20分間加熱した。次いで、この分散液をイオン交換水で1%に希釈した際の電導度が所定値(10μS/cm)以下になるまで、上記酵素処理パルプ分散液をイオン交換水で洗浄しながら減圧ろ過を行った(アドバンテック社製「No.2ろ紙」使用)。ろ紙上に濃縮された酵素処理パルプをイオン交換水に入れて攪拌し、0.5%の分散液を作製し、NiroSoavi社製高圧ホモジナイザー「Panda Plus2000」により処理圧力40MPaで10回の微細化処理を行い、セルロース微細繊維含有分散液を得た。このときの数平均繊維幅は15nmであった。 The enzyme-treated pulp dispersion was heated at 95 ° C. or higher for 20 minutes. Next, vacuum filtration is performed while washing the enzyme-treated pulp dispersion with ion-exchanged water until the electrical conductivity when the dispersion is diluted to 1% with ion-exchanged water becomes a predetermined value (10 μS / cm) or less. ("No. 2 filter paper" manufactured by Advantech) was used. Enzyme-treated pulp concentrated on filter paper is placed in ion-exchanged water and stirred to prepare a 0.5% dispersion, which is refined 10 times with a high-pressure homogenizer “Panda Plus 2000” manufactured by NiroSoavi at a processing pressure of 40 MPa. To obtain a dispersion containing fine cellulose fibers. The number average fiber width at this time was 15 nm.
上記セルロース微細繊維含有分散液を、不織布の仕上がり坪量が40.0g/m2になるように調整し、焼結サイズが30〜50μmのアドバンテック社製ブフナーロート型ガラスフィルター「KG−90」上にアドバンテック社製PTFEメンブレンを載せたろ過瓶上に流延し、アスピレーターで吸引しながらろ過を行った。ろ過後の湿紙状態の不織布を70℃に加熱したシリンダドライヤーで0.1MPaに加圧しながら乾燥し、不織布を得た。以上の手順を経て得られた不織布の坪量は40.0g/m2であった。 On the above-mentioned cellulose fine fiber-containing dispersion liquid, the finished basis weight of the nonwoven fabric is adjusted to 40.0 g / m 2, and the Advantech Buchner funnel type glass filter “KG-90” having a sintered size of 30 to 50 μm is used. The solution was cast on a filter bottle on which a PTFE membrane manufactured by Advantech Co., Ltd. was placed, and filtered while sucking with an aspirator. The wet paper web nonwoven fabric after filtration was dried while being pressurized to 0.1 MPa with a cylinder dryer heated to 70 ° C. to obtain a nonwoven fabric. The basis weight of the nonwoven fabric obtained through the above procedure was 40.0 g / m 2 .
<変則フリーネス>
実施例1におけるパルプ分散液(A)を調整するにあたり基準とした変則フリーネスは、パルプ採取量を0.3g/Lとした以外はJIS P 8121 に準じて測定したフリーネスである。
<Anomaly Freeness>
The irregular freeness used as a reference in adjusting the pulp dispersion liquid (A) in Example 1 is the freeness measured according to JIS P 8121 except that the amount of collected pulp was 0.3 g / L.
<評価方法>
(1)不織布の引裂強度
JIS P 8116に準じて測定し、得られた引裂強度(mN)を、供試した不織布の坪量(g/m2)で除し、比引裂強度(mN・m2/g)として表記した。
(2)不織布の引張強度
JIS P 8113に準じて測定し、単位面積当たりの強度(MPa)を表記した。
<Evaluation method>
(1) Tear strength of nonwoven fabric Measured according to JIS P 8116, and the obtained tear strength (mN) is divided by the basis weight (g / m 2 ) of the tested nonwoven fabric to obtain specific tear strength (mN · m 2 / g).
(2) Tensile strength of nonwoven fabric Measured according to JIS P 8113, and indicated the strength (MPa) per unit area.
上記の評価結果を表1に示す。 The evaluation results are shown in Table 1.
表1から明らかなように、実施例1〜7及び比較例1においては比引裂強度の大きい不織布が得られた。上記のうち実施例1〜7においては高い比引裂強度と高い引張強度とを両立した不織布が得られたが、比較例1においては、引裂強度は向上したものの引張強度の低下が見られた。比較例2及び3においては、不織布は数平均繊維幅の小さい繊維のみで作製されており、比引裂強度の大きいものは得られなかった。 As is clear from Table 1, in Examples 1 to 7 and Comparative Example 1, nonwoven fabrics having high specific tear strength were obtained. Among Examples 1 to 7, nonwoven fabrics having both high specific tear strength and high tensile strength were obtained. In Comparative Example 1, although the tear strength was improved, a decrease in tensile strength was observed. In Comparative Examples 2 and 3, the non-woven fabric was made only of fibers having a small number average fiber width, and a high specific tear strength was not obtained.
Claims (5)