JP6268575B2 - Antibacterial cosmetic brush hair material, antibacterial cosmetic brush using the hair material, and method for producing the same - Google Patents
Antibacterial cosmetic brush hair material, antibacterial cosmetic brush using the hair material, and method for producing the same Download PDFInfo
- Publication number
- JP6268575B2 JP6268575B2 JP2013207866A JP2013207866A JP6268575B2 JP 6268575 B2 JP6268575 B2 JP 6268575B2 JP 2013207866 A JP2013207866 A JP 2013207866A JP 2013207866 A JP2013207866 A JP 2013207866A JP 6268575 B2 JP6268575 B2 JP 6268575B2
- Authority
- JP
- Japan
- Prior art keywords
- cosmetic brush
- antibacterial cosmetic
- hair material
- silver
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、ポリエステル系樹脂フィラメントを用いた抗菌性化粧用ブラシ毛材、その毛材を用いた抗菌性化粧用ブラシ及びその製造方法に関し、詳細には、ポリエステル系樹脂のポリトリメチレンテレフタレート（以下、「ＰＴＴ」という。）、及び、ポリブチレンテレフタレート（以下、「ＰＢＴ」という。）を含む樹脂組成物に銀含有可溶性ガラスを含有するフィラメントを、アルカリ処理によりその表面を粗面にした抗菌性化粧用ブラシ毛材、そして、その毛材を用いた使用感に優れ、且つ化粧料の含み性（掻き取り性と保持性）、転着性に優れる抗菌性化粧用ブラシ及びその製造方法に関する。 TECHNICAL FIELD The present invention relates to an antibacterial cosmetic brush hair material using a polyester resin filament, an antibacterial cosmetic brush using the hair material, and a method for producing the same, and more specifically, polytrimethylene terephthalate (hereinafter referred to as a polyester resin). , "PTT") and polybutylene terephthalate (hereinafter referred to as "PBT") resin composition containing silver-containing soluble glass filaments, the surface of which has been roughened by alkali treatment. The present invention relates to a cosmetic brush bristle material, an antibacterial cosmetic brush excellent in the feeling of use using the bristle material, and excellent in cosmetic content (scraping and holding properties) and transferability, and a method for producing the same.
従来、化粧用ブラシの毛材には、リス毛、馬毛、山羊毛等の獣毛が使用されており、これらの獣毛は、肌当たりが良い、即ち使用感が良く、また、含み性及び転着性が良好であるといわれている。リス毛の化粧用ブラシは獣毛の化粧用ブラシの最高級品として消費者から高い評価を得ている。ところが、獣毛は上記利点を有しているが天然資源であるために、その供給量に限界がある等の欠点があり、そこで、近年では獣毛の代替品として、合成繊維から作られた化粧用ブラシ毛材が提案されている。 Conventionally, animal hairs such as squirrel hair, horse hair, goat hair, etc. have been used as hair materials for cosmetic brushes, and these animal hairs have good skin contact, that is, have a good feeling of use and containability. And transferability is said to be good. The squirrel hair brush is highly regarded by consumers as the highest quality animal hair brush. However, although animal hair has the above-mentioned advantages, it is a natural resource, so there are drawbacks such as limited supply, and in recent years, it has been made from synthetic fibers as a substitute for animal hair. Cosmetic brush hair materials have been proposed.
例えば、特許文献１には、表面に凹みを設けた化粧用ブラシ毛材が提案されている。ＰＢＴの１００重量部と、平均粒子径が０．５〜１．０μｍであるシリカ、タルク、銀ゼオライト等の無機粉体の５〜１５重量部を混合して溶融紡糸し、その得られたフィラメントを５〜６倍に延伸することにより、その表面に上記無機粉体が埋没して凹みが形成される。そのフィラメントを集束して一定長に切断して得られた繊維集束体の一方端側を、アルカリ溶液中に浸漬することで上記凹みが拡大されると共に、その一方端側を溶解減量させてテーパー状に形成した化粧用ブラシ毛材が提案されている。上記凹みが形成されたフィラメントを用いた化粧ブラシ用ブラシ毛材は、そのフィラメント表面にアルカリ処理により拡大された凹みが、獣毛のキューティクルと同様の働きをすることで、獣毛と同等の含み性及び転着性を有することが開示されている（特許文献１参照）。 For example, Patent Document 1 proposes a cosmetic brush hair material having a dent on the surface. 100 parts by weight of PBT and 5 to 15 parts by weight of inorganic powder such as silica, talc, silver zeolite having an average particle size of 0.5 to 1.0 μm are mixed and melt-spun, and the filament obtained Is stretched 5 to 6 times to bury the inorganic powder on the surface thereof to form a dent. The one end side of the fiber bundle obtained by concentrating the filament and cutting it to a certain length is immersed in an alkaline solution to enlarge the dent, and the one end side is dissolved to reduce the taper. A cosmetic brush hair material formed into a shape has been proposed. The brush bristle material for cosmetic brushes using filaments with the above-mentioned dents, the dents expanded by alkali treatment on the filament surface, which has the same function as animal hair cuticles, It has been disclosed that the material has transferability and transferability (see Patent Document 1).
特許文献２には、ＰＴＴの表面に凹凸を設けたブラシ毛材が提案されている。このＰＴＴのブラシ毛材は、ＰＢＴのブラシ毛材に比べて、アルカリ処理液に浸漬して加水分解するのに通常の加水分解の３倍以上の時間が必要であり、加水分解され難いためにテーパー形成の生産性が劣り、コスト高になる問題を有していた。そこで、上記ブラシ毛材は、その先端部をテーパー状の先細部にするために、ＰＴＴを溶融紡糸し、その得られたフィラメントを５〜６倍に延伸したフィラメントを、集束した長さ方向の一方端の１０〜２０ｍｍ程度をアミン触媒含有のアルカリ処理液に浸漬して、１１０〜１３０℃で１〜２時間処理することにより、上記フィラメントにアルカリ処理で先端部にテーパー状の先細部を形成すると共に、その表面に１〜２０μｍの凹凸を形成することができるようになった。 Patent Document 2 proposes a brush bristle material having irregularities on the surface of the PTT. This PTT brush bristle material requires more than three times the normal hydrolysis time to be immersed in an alkali treatment solution and hydrolyzed as compared to PBT brush bristle material, and is difficult to hydrolyze. The productivity of taper formation is inferior and the cost is high. Therefore, the brush bristle material is formed by melting and spinning PTT in order to make the tip of the taper tapered, and extending the filaments obtained by stretching the filament 5 to 6 times. About 10 to 20 mm at one end is immersed in an alkali treatment solution containing an amine catalyst and treated at 110 to 130 ° C. for 1 to 2 hours to form a tapered taper at the tip by alkali treatment on the filament. In addition, 1-20 μm irregularities can be formed on the surface.
そして、特許文献２における、化粧用ブラシ毛材の実施例１、２のＰＴＴフィラメントの繊度は８０ｄｔｅｘと１００ｄｔｅｘである。そして、上記アルカリ処理液として、水酸化ナトリウム、加水分解促進触媒、浸透剤及びオリゴマー溶解剤よりなる処理液の使用によって、テーパー状先細部の表面に５〜５０μｍの間隔で、且つ１〜２０μｍの微細な凹凸を有するブラシ毛材を得ることができ、そのアルカリ処理後に、ベンジルアンモニウムクロライド系化合物やナフトキノン系化合物の加熱水溶液によって後処理することによって、抗菌性を付与することができることが開示されている（特許文献２参照）。 And the fineness of the PTT filament of Examples 1 and 2 of the cosmetic brush hair material in Patent Document 2 is 80 dtex and 100 dtex. And as said alkali processing liquid, by use of the processing liquid which consists of sodium hydroxide, a hydrolysis acceleration | stimulation catalyst, a penetrant, and an oligomer solubilizer, it is 5-20 micrometers on the surface of a taper-shaped detail, and 1-20 micrometers. It is disclosed that a brush bristle material having fine irregularities can be obtained, and antibacterial properties can be imparted by post-treatment with a heated aqueous solution of a benzylammonium chloride compound or a naphthoquinone compound after the alkali treatment. (See Patent Document 2).
特許文献１、２のポリエステル系樹脂フィラメントからなる化粧用ブラシ毛材は、アルカリ処理によりフィラメントの一方端側に、テーパー状の先細部を形成するものである。
特許文献１のＰＢＴフィラメントは、ＰＢＴに５〜１５重量部の無機粉体を混合して５〜６倍で延伸するために、延伸工程において延伸速度、温度等の管理を厳格に行わなければ、フィラメントが切断する恐れがあり、また、アルカリ処理によりフィラメントの表面に凹みが形成されているために、ブラシ毛材が、そのテーパー状の先細部の途中の凹み同士が対向する領域で切断する恐れがある。
The cosmetic brush bristle material made of polyester resin filaments of Patent Documents 1 and 2 forms a tapered tapered detail on one end side of the filament by alkali treatment.
The PBT filament of Patent Document 1 is mixed with 5 to 15 parts by weight of inorganic powder in PBT and stretched 5 to 6 times. There is a possibility that the filament may be cut, and because the dent is formed on the surface of the filament by the alkali treatment, the brush bristle material may be cut in a region where the dents in the middle of the tapered taper face each other. There is.
そして、特許文献２のＰＴＴフィラメント化粧用ブラシ毛材の繊度は、８０ｄｔｅｘ（８８．５２μｍ（比重を１．３０で計算））と１００ｄｔｅｘ（９８．９７μｍ（比重を１．３０で計算））である。これらの太さのフィラメントを高温度でアミン触媒含有のアルカリ処理液に浸漬して１〜２時間処理することで、そのフィラメントの表面に５〜５０μｍ程度の間隔で１〜２０μｍの凹凸を設け、その後にベンジルアンモニウムクロライド系化合物等の加熱水溶液によって抗菌処理を行っている。そのため、上記化粧用ブラシ毛材は、リス毛の使用感が得られる最高級品として製品化されているが、テーパー状先細部の形成処理とその後の抗菌処理に時間がかかり、ＰＢＴフィラメントに比べ生産性が劣ると共に、各種の処理液を準備する必要があり、低廉な値段で製造できない問題が指摘されている。また、リス毛のように４５〜６５μｍ程度の細いものを作製すると、テーパー状の途中の凹み同士が対向する領域で切断されてブラシ毛材の作製は、困難であるとの指摘がある。 And the fineness of the brush hair material for PTT filament makeup of patent document 2 is 80 dtex (88.52 μm (specific gravity is calculated by 1.30)) and 100 dtex (98.97 μm (specific gravity is calculated by 1.30)). . By immersing these thick filaments in an amine treatment-containing alkaline treatment solution at a high temperature for 1 to 2 hours, the surface of the filament is provided with irregularities of 1 to 20 μm at intervals of about 5 to 50 μm, Thereafter, antibacterial treatment is performed with a heated aqueous solution of a benzylammonium chloride compound or the like. For this reason, the above-mentioned cosmetic brush hair material has been commercialized as the highest grade product that can provide a feeling of use of squirrel hair, but it takes time to form the tapered taper and the subsequent antibacterial treatment, compared to the PBT filament. In addition to inferior productivity, it is necessary to prepare various processing solutions, and problems that cannot be produced at low prices have been pointed out. Further, it is pointed out that when a thin hair having a thickness of about 45 to 65 μm such as a squirrel hair is produced, it is difficult to produce a brush bristle material because the taper-shaped mid-dents are cut in regions facing each other.
そこで、本発明の課題は、上記実情に鑑みなされたもので、アルカリ処理液にアミン触媒を用いることがなく、またその後にベンジルアンモニウムクロライド系化合物等の加熱水溶液によって抗菌処理を行うことがない抗菌性化粧用ブラシ毛材を製造すること。また、ポリエステル系樹脂フィラメントを用いてテーパー状先細部の表面に凹凸部が形成され、そのテーパー状先細部の途中の領域で切断されることがない抗菌性化粧用ブラシ毛材を提供することである。そして、このブラシ毛材を用いた、低廉な値段で製造でき、リス毛を含む獣毛の化粧用ブラシに類似した使用感を有し、また、パウダー等の化粧料の含み性並びに転着性が良好である抗菌性化粧用ブラシを提供することである。 Accordingly, an object of the present invention has been made in view of the above circumstances, and does not use an amine catalyst in an alkaline treatment liquid, and thereafter does not perform an antibacterial treatment with a heated aqueous solution such as a benzylammonium chloride compound. Manufacturing brush hair for cosmetics. In addition, by providing an antibacterial cosmetic brush hair material in which an uneven portion is formed on the surface of a tapered tapered detail using a polyester-based resin filament and is not cut in a region in the middle of the tapered tapered detail. is there. And it can be manufactured at a low price using this brush bristle material, has a feeling of use similar to animal hair cosmetic brushes including squirrel hairs, and contains and transfers of cosmetics such as powders. It is to provide an antibacterial cosmetic brush that is good.
本発明者等は、上記課題を解決するため鋭意検討を重ねた結果、ポリエステル系樹脂のＰＴＴとＰＢＴを含む樹脂組成物に、水に可溶性の銀含有可溶性ガラスが含有された化粧用フィラメントを、アルカリ処理液に浸漬することで、テーパー状先細部の表面全面に多数の凹凸部が形成されること、また、テーパー状先細部の途中の領域で切断しないこと、また、ＰＴＴとＰＢＴの配合割合で伸張弾性率（％）とヤング率（Ｎ／ｍｍ２）が変わることを見出し、本発明の化粧用ブラシ毛材を完成した。更に、その毛材を用いた抗菌性化粧用ブラシが、リス毛を含む獣毛の化粧用ブラシと同様に、使用感が良く、また、パウダー等の化粧料の含み性並びに転着性が良好であることを見出した。そして、本発明は、抗菌性化粧用ブラシ毛材、その毛材を用いた抗菌性化粧用ブラシ及びその製造方法を完成するに至った。
即ち本発明は、以下の通りのものである。
請求項１に係る発明の抗菌性化粧用ブラシ毛材は、太さが５０〜１５０μｍである、無機粒子を含有するポリエステル系樹脂製フィラメントからなり、テーパー状に形成された先細部を備えた抗菌性化粧用ブラシ毛材であって、ポリエステル系樹脂製フィラメントは、ポリトリメチレンテレフタレート７０．０〜９０．０重量％、及びポリブチレンテレフタレート２９．２〜９．９重量％を含む樹脂組成物であり、無機粒子が銀を含有する可溶性ガラス０．８〜０．１重量％であり、先細部は、表面全面に凹凸部を備えており、該凹凸部に銀粒子が露出していることを特徴とする。
請求項２に係る発明の抗菌性化粧用ブラシ毛材は、前記銀含有可溶性ガラスに含まれる銀濃度が１．０〜４．０重量％の範囲にあることを特徴とする。
請求項３に係る発明の抗菌性化粧用ブラシ毛材は、前記抗菌性化粧用ブラシ毛材が静菌活性値２．２〜６（ＪＩＳ Ｌ １９０２−１９９８（ＩＳＯ２０７４３））の範囲の値であることを特徴とする。
請求項４に係る発明の抗菌性化粧用ブラシ毛材は、テーパー状先細部に続く毛材の胴体部に銀含有可溶性ガラスが凸状の露出している部分が形成されていることを特徴とする。
請求項５に係る発明の抗菌性化粧用ブラシ毛材は、前記抗菌性化粧用ブラシ毛材の形状が直線状又はカール状であることを特徴とする。
請求項６に係る発明の抗菌性化粧用ブラシは、請求項１の抗菌性化粧用ブラシ毛材を用いたことを特徴とする。
請求項７に係る発明の抗菌性化粧用ブラシは、リキッドブラシ、リップブラシまたはネイルケアブラシであることを特徴とする。
請求項８に係る発明の抗菌性化粧用ブラシの製造方法は、無機粒子を含有するポリエステル系樹脂製フィラメントからなり、テーパー状に形成された先細部を備えた抗菌性化粧用ブラシ毛材であって、ポリエステル系樹脂製フィラメントは、ポリトリメチレンテレフタレート７０．０〜９０．０重量％、及びポリブチレンテレフタレート２９．２〜９．９重量％、無機粒子が銀を含有する可溶性ガラス０．８〜０．１重量％である樹脂組成であり、先端部は、表面全面に凹凸部を備えてなる抗菌性化粧用ブラシ毛材の製造方法であって、樹脂組成物を紡糸機で溶融、混練し押出して、紡糸口より加熱延伸により４〜５倍の延伸を行ってフィラメントを製造する工程と、上記フィラメントを束に集束して、所定の長さに切断する工程、切断した一端を水酸化ナトリウム水溶液でアルカリ処理を行って先端部にテーパー状先細部を形成すると共に、当該先細部の表面に凹凸部を形成する工程、その後に水洗して乾燥を行う工程と、ブラシ毛材を毛束保持部材に埋設する工程とからなることを特徴とする。
As a result of intensive studies to solve the above-mentioned problems, the present inventors have obtained a cosmetic filament containing a water-soluble silver-containing soluble glass in a resin composition containing polyester-based resin PTT and PBT. By dipping in an alkali treatment solution, a large number of irregularities are formed on the entire surface of the tapered tapered detail, and it is not cut in a region in the middle of the tapered tapered detail, and the blending ratio of PTT and PBT And the elastic modulus of elasticity (%) and Young's modulus (N / mm 2 ) were found to change, and the cosmetic brush hair material of the present invention was completed. Furthermore, the antibacterial cosmetic brush using the hair material has good usability as well as the animal hair cosmetic brush including squirrel hair, and the inclusion and transferability of cosmetics such as powder are good. I found out. And this invention came to complete the antibacterial cosmetic brush hair material, the antibacterial cosmetic brush using the hair material, and its manufacturing method.
That is, the present invention is as follows.
The antibacterial cosmetic brush hair material of the invention according to claim 1 is made of a polyester resin filament containing inorganic particles having a thickness of 50 to 150 μm, and has an antibacterial shape having a tapered shape. The polyester-based resin filament is a resin composition containing polytrimethylene terephthalate 70.0 to 90.0% by weight and polybutylene terephthalate 29.2 to 9.9% by weight. Yes, it is soluble glass containing silver containing 0.8 to 0.1% by weight of inorganic particles, and the tip is provided with uneven portions on the entire surface, and the silver particles are exposed on the uneven portions. Features.
The antibacterial cosmetic brush hair material of the invention according to claim 2 is characterized in that the silver concentration contained in the silver-containing soluble glass is in the range of 1.0 to 4.0% by weight .
請 Motomeko 3 according antimicrobial cosmetic brush bristle material of the invention, a value in the range of the antimicrobial cosmetic brush hairs bacteriostatic activity value 2.2~6 (JIS L 1902-1998 (ISO20743) ) It is characterized by being.
The antibacterial cosmetic brush hair material of the invention according to claim 4 is characterized in that a convex exposed portion of the silver-containing soluble glass is formed on the body portion of the hair material following the tapered taper. To do.
The antibacterial cosmetic brush hair material of the invention according to claim 5 is characterized in that the antibacterial cosmetic brush hair material is linear or curled.
The antibacterial cosmetic brush of the invention according to claim 6 is characterized in that the antibacterial cosmetic brush hair material of claim 1 is used.
The antibacterial cosmetic brush of the invention according to claim 7 is a liquid brush, a lip brush or a nail care brush.
The method for producing an antibacterial cosmetic brush according to an eighth aspect of the present invention is an antibacterial cosmetic brush bristle material comprising a tapered tape-shaped filament made of polyester resin filaments containing inorganic particles. The polyester resin filament is composed of 70.0 to 90.0% by weight of polytrimethylene terephthalate, 29.2 to 9.9% by weight of polybutylene terephthalate, and 0.8 to 2.5% soluble glass containing silver as inorganic particles. The antibacterial cosmetic brush hair material has a resin composition of 0.1% by weight and the tip portion is provided with uneven portions on the entire surface, and the resin composition is melted and kneaded with a spinning machine. Extruding and drawing filaments by heating 4-5 times by heating from the spinneret, concentrating the filaments into bundles and cutting them to a predetermined length A process of forming a tapered taper at the tip by performing an alkali treatment with an aqueous solution of sodium hydroxide at the end, forming a concavo-convex part on the surface of the taper, then washing and drying, and brush hair And a step of embedding the material in the hair bundle holding member.
本発明の抗菌性化粧用ブラシ毛材は、ポリエステル系樹脂であるＰＴＴ７０．０〜９０．０重量％及びＰＢＴ２９．２〜９．９重量％に、その樹脂に比べて熱伝導率が約５倍大きい銀含有可溶性ガラスを、０．８〜０．１重量％の範囲で含有させることで、アルカリ処理されたテーパー状先細部の表面全面に、銀含有可溶性ガラスの溶解促進作用を働かせて１〜２μｍの凹凸部を形成した。このため、アミン触媒及びベンジルアンモニウムクロライド系化合物等の加熱水溶液を用いることなく、従来のアルカリ処理液を用いるだけで低廉な値段で製造できる。そして、上記抗菌性化粧用ブラシ毛材は、上記ＰＴＴとＰＢＴに銀含有可溶性ガラスを上記配合にすることで、テーパー状先細部の途中の領域で切断されることがなく、リス毛のように４５〜６５μｍ程度の細いものが製造できる。 The antibacterial cosmetic brush hair material of the present invention has a polyester-based resin PTT of 70.0 to 90.0% by weight and PBT of 29.2 to 9.9% by weight, and the thermal conductivity is about 5 times that of the resin. By containing a large silver-containing soluble glass in the range of 0.8 to 0.1% by weight, the dissolution promoting action of the silver-containing soluble glass works on the entire surface of the taper-shaped tapered surface that has been subjected to alkali treatment. A 2 μm uneven portion was formed. For this reason, it can manufacture at low cost only by using the conventional alkali processing liquid, without using heating aqueous solution, such as an amine catalyst and a benzylammonium chloride type compound. And the said antibacterial cosmetic brush hair material does not cut | disconnect in the area | region in the middle of a taper-shaped fine detail by using the said PTT and PBT and the said silver-containing soluble glass as the said mixing | blending, A thin product of about 45 to 65 μm can be manufactured.
また、本発明の抗菌性化粧用ブラシは、テーパー状先細部の表面全面に１〜２μｍの凹凸部が形成されており、獣毛の表面形状に類似しているので、パウダー等の化粧料の含み性並びに転着性が良好である。そして、リス毛のように４５〜６５μｍ程度の太さの毛材を用いて製造された抗菌性化粧用ブラシは、リス毛の化粧用ブラシ毛材と同様に、使用感に大変優れている。また、従来から舞台用の化粧に用いられる板ブラシの太さは、腰の強さが必要なために約１５０μｍと太いものが使われているが、本発明の抗菌性化粧用ブラシは、ＰＢＴを２５重量％以上の配合割合にすれば約１５０μｍと太く腰の強い板ブラシが製造できる。
更に、本発明の抗菌性化粧用ブラシは、抗菌性化粧用ブラシ毛材のＰＴＴとＰＢＴの配合割合を変えることで、それを使用する顔の部位、化粧料の状態に応じて、各種の化粧用ブラシ、例えば、リキッドブラシ、リップブラシ、ネイルケアブラシ、ファンデーションブラシ、パウダーブラシ、シャドーブラシ、チークブラシ、ハイライトブラシまたはコンシーラーブラシ等が製造できる。
In addition, the antibacterial cosmetic brush of the present invention has an uneven portion of 1 to 2 μm formed on the entire surface of the tapered taper, and is similar to the surface shape of animal hair. Good containment and transferability. And the antibacterial cosmetic brush manufactured using the hair material of about 45-65 micrometers thickness like a squirrel hair is very excellent in a usability | use_condition like the brush hair material for a squirrel hair. In addition, the thickness of a plate brush conventionally used for stage makeup has been about 150 μm because of the need for waist strength, but the antibacterial cosmetic brush of the present invention is a PBT. If the blending ratio is 25% by weight or more, a thick and strong plate brush of about 150 μm can be manufactured.
Furthermore, the antibacterial cosmetic brush according to the present invention can be applied to various cosmetics according to the facial part and the condition of the cosmetics by changing the blending ratio of PTT and PBT of the antibacterial cosmetic brush hair material. For example, liquid brushes, lip brushes, nail care brushes, foundation brushes, powder brushes, shadow brushes, teak brushes, highlight brushes, concealer brushes, and the like can be manufactured.
そして、本発明の抗菌性化粧用ブラシは上記テーパー状先細部の表面に銀含有可溶性ガラスを有しているので、抗菌効果に優れている。例えばリップグロスを唇に塗布するリップブラシは、唇についていた食品などの汚れがブラシ毛材に移って容器に入り、容器の中で雑菌が繁殖して悪臭を発生させると言われているが、銀イオンが雑菌の繁殖を抑制することで優れた防臭効果が得られる。 And since the antibacterial cosmetic brush of this invention has silver containing soluble glass on the surface of the said taper-shaped taper, it is excellent in the antibacterial effect. For example, a lip brush that applies lip gloss to the lips is said to be contaminated with food such as food on the lips and transferred to the brush bristle material. An excellent deodorizing effect can be obtained by suppressing the propagation of bacteria by silver ions.
（熱可塑性樹脂）
化粧用ブラシ毛材に用いるポリエステル系樹脂としては、柔軟性、弾性回復性、耐水性の物性面から、ＰＴＴ及びＰＢＴを混合した樹脂組成が用いられる。上述したように、ＰＴＴの化粧用ブラシ毛材は、ＰＢＴの化粧用ブラシ毛材に比べて、アルカリ処理液に浸漬して加水分解するのに３倍以上の時間が必要であるから、アルカリ処理液で加水分解し易いＰＢＴを配合してフィラメントとする。そして、ＰＴＴフィラメントは、ポリエステルの形態安定性とナイロンの柔らかさを兼ね備えているが、その柔らかさが逆に欠点となり硬さを必要とする化粧用ブラシ毛材には向いていないと言われている。また、ＰＢＴフィラメントは、染色が容易であること、加工糸にした場合の伸縮特性に優れており、ＰＴＴフィラメントより硬いことから各種の化粧用ブラシが実用化されている。そこで、ＰＴＴフィラメントの柔らかさを補うためにＰＴＴにＰＢＴを配合したフィラメントを作製する。
フィラメントの全組成を１００重量％として、ＰＴＴとＰＢＴは、７０．０〜９０．０：２９．２〜９．９の配合である。
(Thermoplastic resin)
As the polyester-based resin used for the cosmetic brush hair material, a resin composition in which PTT and PBT are mixed is used from the viewpoints of flexibility, elastic recovery, and water resistance. As described above, the PTT cosmetic brush bristle material requires three times or more time to be immersed and hydrolyzed in the alkaline treatment liquid as compared with the PBT cosmetic brush bristle material. A filament is prepared by blending PBT which is easily hydrolyzed with liquid. PTT filaments have both the form stability of polyester and the softness of nylon, but it is said that the softness of the PTT filaments is not suitable for cosmetic brush hair materials that are disadvantageous and require hardness. Yes. In addition, PBT filaments are easy to dye and have excellent stretch properties when processed into yarns, and are harder than PTT filaments, so various cosmetic brushes have been put to practical use. Therefore, a filament in which PBT is blended with PTT to make up the softness of the PTT filament is produced.
When the total composition of the filament is 100% by weight, PTT and PBT are blended in the range of 70.0 to 90.0: 29.2 to 9.9.
（銀含有可溶性ガラス）
銀含有可溶性ガラスは水に可溶性である。フィラメントの全組成を１００重量％として銀含有可溶性ガラスは０．８〜０．１重量％が配合されることが望ましい。また、銀含有可溶性ガラスに含まれる銀濃度は１．０〜４．０重量％の範囲にあることが望ましい。
平均粒径が１〜１０μｍであって銀濃度が１．４、２．０、３．０重量％の３種類の銀含有可溶性ガラスが日本で市販されている。この銀含有可溶性ガラスは、一般的に「銀ガラス」と呼ばれており、表に示すときはこの銀ガラスで表示する。
銀濃度が１．４重量％の銀含有可溶性ガラスで配合率が０．１重量％未満であると、加水分解が促進されないので好ましくない。配合率が０．８重量％を超えると加水分解の工程においてフィラメントが切断される状況が発生するので、上記樹脂に銀含有可溶性ガラスを配合率０．１〜０．８重量％の範囲で配合することが好ましい。また、加水分解の工程においてフィラメントが切断するのを抑えるために、平均粒径が１μｍのものが好ましい。
なお、銀含有可溶性ガラスの熱伝導率は、配合素材により１．４０Ｗ／ｍ・Ｋを中心にした幅を持った値である。実施例で用いた銀含有可溶性ガラスでは１．４０Ｗ／ｍ・Ｋの値のものである。
(Silver-containing soluble glass)
Silver-containing soluble glass is soluble in water. It is desirable that 0.8 to 0.1% by weight of the silver-containing soluble glass is blended with the total composition of the filament being 100% by weight. Moreover, it is desirable that the silver concentration contained in the silver-containing soluble glass is in the range of 1.0 to 4.0% by weight.
Three types of silver-containing soluble glass having an average particle diameter of 1 to 10 μm and silver concentrations of 1.4, 2.0 and 3.0% by weight are commercially available in Japan. This silver-containing soluble glass is generally called “silver glass”, and is indicated by this silver glass when shown in the table.
A silver-containing soluble glass having a silver concentration of 1.4% by weight and a blending ratio of less than 0.1% by weight is not preferable because hydrolysis is not promoted. If the blending ratio exceeds 0.8% by weight, the situation where the filament is cut in the hydrolysis step occurs. Therefore, the silver-containing soluble glass is blended with the above resin in the blending ratio range of 0.1 to 0.8% by weight. It is preferable to do. Moreover, in order to suppress that a filament cut | disconnects in the process of a hydrolysis, a thing with an average particle diameter of 1 micrometer is preferable.
In addition, the heat conductivity of a silver containing soluble glass is a value with the width | variety centering on 1.40 W / m * K by the mixing | blending material. The silver-containing soluble glass used in the examples has a value of 1.40 W / m · K.
（抗菌性化粧用ブラシ毛材の製造方法）
次に、本発明の抗菌性化粧用ブラシ毛材の製造方法を説明する。
抗菌性化粧用ブラシ毛材のフィラメントは、ＰＴＴペレットとＰＢＴペレット及び銀含有可溶性ガラス粉末、ＰＴＴペレットと銀含有可溶性ガラス含有のＰＢＴペレット（その逆も可）、または、ＰＴＴ粉末、ＰＢＴ粉末及び銀含有可溶性ガラス粉末を均一に分散するように撹拌し、紡糸機のホッパーに投入して溶融、混練し押出して、紡糸口より紡糸して３段の加熱延伸により４〜５倍の延伸を行って約７６μｍのフィラメントを製造する。
そして、上記フィラメントをまとめて円柱状に集束し所定の長さに切断する。切断した一端を水酸化ナトリウム水溶液でアルカリ処理を行う。その後水洗して乾燥を行う。
または、上記フィラメントにギヤクリンプ法等によりクリンプ加工を施し、そのフィラメントを円柱状に集束し所定の長さに切断する。切断した一端を水酸化ナトリウム水溶液でアルカリ処理を行う。その後、水洗して乾燥を行う。
(Method for producing antibacterial cosmetic brush hair material)
Next, the manufacturing method of the antibacterial cosmetic brush hair material of this invention is demonstrated.
The filaments of the antibacterial cosmetic bristle include PTT pellets and PBT pellets and silver-containing soluble glass powder, PTT pellets and silver-containing soluble glass-containing PBT pellets (or vice versa), or PTT powder, PBT powder and silver Stirring so that the contained soluble glass powder is uniformly dispersed, thrown into a hopper of a spinning machine, melted, kneaded, extruded, spun from the spinneret, and stretched 4-5 times by three-stage heat stretching. A filament of about 76 μm is produced.
Then, the filaments are collectively gathered into a cylindrical shape and cut into a predetermined length. One end of the cut is subjected to alkali treatment with an aqueous sodium hydroxide solution. Thereafter, it is washed with water and dried.
Alternatively, the filament is subjected to crimping by a gear crimping method or the like, and the filament is converged into a cylindrical shape and cut into a predetermined length. One end of the cut is subjected to alkali treatment with an aqueous sodium hydroxide solution. Thereafter, it is washed with water and dried.
上記フィラメントの一端をアルカリ処理液に浸漬することにより、このフィラメント表面上にある銀含有可溶性ガラスが上記アルカリ処理液で溶解されて、このアルカリ処理液に接触する表面積が拡大することで加水分解が促進される。この銀含有可溶性ガラスの溶解による加水分解の促進作用を以下に「溶解促進作用」という。その一方端側に、先端方向にテーパー状の形状を有する凹凸部が出現した領域を「テーパー状先細部」と称し、円柱状に集束したフィラメントに上記水酸化ナトリウム水溶液を毛細管現象により吸い上げて、上記樹脂の加水分解によって被覆されている銀含有可溶性ガラスを被覆する樹脂の皮膜が溶解除去される。この毛管現象と溶解作用によって上記フィラメントの胴体の表面にも凸部が現出し、この領域を「胴体部」と称する。なお、銀含有可溶性ガラスは紡糸によって表面に樹脂被膜が形成された状態になっており、銀ガラス可溶性ガラスが粒子状に点在して、その上に樹脂被膜が形成され、ひけなど樹脂収縮作用もあって、凸状に点在している。毛管現象により吸い上げられた少量のアルカリ剤によって、樹脂皮膜部分のみが除去されて、胴体部の表面には銀ガラスが露出して凸状になる。
したがって、本発明の抗菌性化粧用ブラシ毛材は、表面全面に凹凸部が形成されているテーパー状先細部の領域と胴体部の領域には凸が形成されている。上記テーパー状先細部の先端は円錐形状であり、その円錐形状を形成する基端の太さが小さいほど肌触りが優れている。この太さは、基本的にフィラメントの胴部の太さと同じである。
そして、本発明の抗菌性化粧用ブラシは、上記銀含有可溶性ガラスの溶解促進作用による凹凸部の領域を有するテーパー状先細部でファンデーション等の化粧料を塗布する。
By immersing one end of the filament in the alkali treatment liquid, the silver-containing soluble glass on the filament surface is dissolved in the alkali treatment liquid, and the surface area in contact with the alkali treatment liquid is expanded to cause hydrolysis. Promoted. The action of promoting hydrolysis by dissolving the silver-containing soluble glass is hereinafter referred to as “dissolution promoting action”. On the one end side, the region where the uneven portion having a tapered shape in the tip direction appears is called `` tapered detail '', and the sodium hydroxide aqueous solution is sucked up by a capillary phenomenon into a filament converging in a columnar shape, The resin film covering the silver-containing soluble glass coated by hydrolysis of the resin is dissolved and removed. Due to this capillary action and dissolution action, convex portions also appear on the surface of the body of the filament, and this region is referred to as a “body part”. In addition, the silver-containing soluble glass is in a state where a resin film is formed on the surface by spinning, the silver glass-soluble glass is scattered in the form of particles, and a resin film is formed thereon, and resin shrinkage action such as sink In addition, it is scattered in a convex shape. Only a resin film portion is removed by a small amount of the alkali agent sucked up by the capillary phenomenon, and silver glass is exposed on the surface of the body portion to be convex.
Therefore, the antibacterial cosmetic brush bristle material of the present invention has convex portions formed in the tapered tapered region and the body region where the concavo-convex portions are formed on the entire surface. The tip of the tapered taper has a conical shape. The smaller the thickness of the base end forming the conical shape, the better the touch. This thickness is basically the same as the thickness of the body of the filament.
And the antibacterial cosmetic brush of this invention apply | coats cosmetics, such as a foundation, with the taper-shaped detail which has the area | region of the uneven part by the melt | dissolution acceleration | stimulation effect | action of the said silver containing soluble glass.
（抗菌性化粧用ブラシ毛材の形状）
抗菌性化粧用ブラシ毛材の形状は、直線状とカール状の２種類がある。その形状が直線状のものは、リキッドブラシ、リップブラシまたはネイルケアブラシに用いられ、リキッド状の化粧料を塗布するのに用いられる。その形状がカール状のものは、ファンデーションブラシ、パウダーブラシ、シャドーブラシ、チークブラシ、ハイライトブラシまたはコンシーラーブラシに用いられ、粉末状の化粧料を塗布するのに用いられる。上記カールを付与させる加工方法としては、ギヤクリンプ法が作業性の観点から一般的に用いられている。
(Shape of antibacterial cosmetic brush hair material)
There are two types of antibacterial cosmetic brush hair materials, linear and curled. The linear shape is used for liquid brushes, lip brushes or nail care brushes, and is used to apply liquid cosmetics. The curled shape is used for foundation brushes, powder brushes, shadow brushes, teak brushes, highlight brushes or concealer brushes, and is used for applying powdery cosmetics. As a processing method for imparting the curl, a gear crimping method is generally used from the viewpoint of workability.
（抗菌性化粧用ブラシの製造方法）
本発明の抗菌性化粧用ブラシの製造方法は、樹脂を配合、紡糸、アルカリ処理、毛材埋設の工程を経る。
ポリエステル系樹脂の配合工程は、ポリトリメチレンテレフタレート７０．０〜９０．０重量％、ポリブチレンテレフタレート２９．２〜９．９重量％を含む樹脂組成物に、銀含有可溶性ガラス０．８〜０．１重量％を配合する工程である。紡糸工程は、この配合された樹脂を紡糸機で溶融、混練し押出して、紡糸口より加熱延伸により４〜５倍の延伸を行ってフィラメントを製造する工程である。アルカリ処理工程は、紡糸されたフィラメントを円柱状に集束し所定の長さに切断し、切断した一端を水酸化ナトリウム水溶液でアルカリ処理を行い、その後に水洗して乾燥が行われる工程である。このアルカリ処理によってその先端部の先端方向にテーパー状先細部が形成されると共に、その表面に凹凸部が形成される。または、集束する際に上記フィラメントにクリンプ加工を施し、そのフィラメントを集束し所定の長さに切断することもできる。毛材の埋設工程は、上記アルカリ処理したブラシ毛材を毛束保持部材に埋設して、化粧用ブラシに形成する工程である。
(Method of manufacturing antibacterial cosmetic brush)
The method for producing an antibacterial cosmetic brush of the present invention includes steps of blending resin, spinning, alkali treatment, and bristle material embedding.
The blending step of the polyester-based resin includes a resin composition containing 70.0 to 90.0% by weight of polytrimethylene terephthalate and 29.2 to 9.9% by weight of polybutylene terephthalate, and 0.8 to 0 silver-containing soluble glass. This is a step of blending 1% by weight. The spinning process is a process for producing a filament by melting, kneading, and extruding the blended resin with a spinning machine, and stretching it 4 to 5 times by heating and stretching from the spinning port. The alkali treatment step is a step in which the spun filament is converged into a cylindrical shape and cut into a predetermined length, and one end of the cut filament is alkali treated with an aqueous sodium hydroxide solution, and then washed with water and dried. By this alkali treatment, a tapered taper is formed in the tip direction of the tip portion, and an uneven portion is formed on the surface thereof. Alternatively, the filaments can be crimped when converging, and the filaments can be converged and cut into a predetermined length. The bristle material embedding step is a step of embedding the above-mentioned alkali-treated brush bristle material in a hair bundle holding member to form a cosmetic brush.
ＰＴＴペレット（ＳＯＲＯＮＡ Ｊ２２４０ Ｓｅｍｉ−Ｄｕｌｌ；Ｄｕ Ｐｏｎｔ製品）、ＰＢＴペレット（ＴＯＲＡＹＣＯＭ １４０１Ｘ０６ 東レ製品）及び銀含有可溶性ガラス（ＰＧ７２１ＳＴ 興亜硝子製品）を混合撹拌して均一にする。または、ＰＴＴ粉末（ＳＯＲＯＮＡ Ｊ２２４０ Ｓｅｍｉ−Ｄｕｌｌ；Ｄｕ Ｐｏｎｔ製品）、ＰＢＴ粉末（ＴＯＲＡＹＣＯＭ １４０１Ｘ０６ 東レ製品）及び銀含有可溶性ガラス（ＰＧ７２１ＳＴ 興亜硝子製品）を撹拌して均一に分散する。
均一に混合された樹脂を紡糸機のホッパーに投入して、２７０℃で溶融し２５０℃で混練して押し出して、紡糸口より紡糸して３段の加熱延伸により４〜５倍の延伸を行って約７６μｍのフィラメントを製造した。このフィラメントの表面は、粒子状銀ガラスがある部分は凸状に点在し、その表面は薄い樹脂皮膜が形成されている状態である。
このフィラメントを直径５ｃｍの円柱状に集束して長さ６ｃｍに切断した。
フィラメント集束の一端を１２重量％濃度の水酸化ナトリウム水溶液に１２０℃で浸漬して、経時的にその浸漬したフィラメント集束である浸漬部を、徐々に引き上げて最高１２０分間を浸漬した。上記フィラメント集束のテーパー状先細部の先端が加水分解により５〜１０μｍの太さになるように浸漬時間の調整を行った。
上記フィラメント集束の浸漬部の上方のフィラメントは、上記水酸化ナトリウム水溶液を毛細管現象により吸い上げて、上記フィラメント表面の銀含有可溶性ガラスの凸部を被覆する樹脂を溶解除去して凸部が散在する胴体部を形成した。この胴体部はフィラメントを集束する強弱を調整することによりその幅を任意に変えることができる。次いで水洗乾燥して抗菌性化粧用ブラシ毛材を得た。
PTT pellets (SORONA J2240 Semi-Dull; Du Pont product), PBT pellets (TORAYCOM 1401X06 Toray product) and silver-containing soluble glass (PG721ST Koa glass product) are mixed and stirred to be uniform. Alternatively, PTT powder (SORONA J2240 Semi-Dull; Du Pont product), PBT powder (TORAYCOM 1401X06 Toray product) and silver-containing soluble glass (PG721ST Koa glass product) are stirred and dispersed uniformly.
The uniformly mixed resin is put into a hopper of a spinning machine, melted at 270 ° C., kneaded at 250 ° C., extruded, spun from a spinning port, and stretched 4 to 5 times by three-stage heat stretching. About 76 μm of filament was produced. On the surface of this filament, the part with the particulate silver glass is scattered in a convex shape, and the surface is in a state where a thin resin film is formed.
The filament was focused into a cylindrical shape having a diameter of 5 cm and cut to a length of 6 cm.
One end of the filament bundling was dipped in a 12 wt% sodium hydroxide aqueous solution at 120 ° C., and the dipped portion that was the filament bundling soaked with time was gradually pulled up and dipped for a maximum of 120 minutes. The dipping time was adjusted so that the tip of the tapered tapered tip of the filament converging was hydrolyzed to a thickness of 5 to 10 μm.
The filament above the filament converging immersion part is a body in which the convex part is scattered by sucking up the sodium hydroxide aqueous solution by capillary action and dissolving and removing the resin covering the convex part of the silver-containing soluble glass on the filament surface. Part was formed. The width of the body portion can be arbitrarily changed by adjusting the strength of focusing the filament. Subsequently, it was washed with water and dried to obtain an antibacterial cosmetic brush hair material.
約７６μｍのフィラメントをアルカリ処理によりテーパー状先細部を形成する際に、銀含有可溶性ガラスが不均一に配合されていると、テーパー状先細部がその不均一配合された部分から切断されることがあるので、ＰＴＴ粉末、ＰＢＴ粉末及び銀含有可溶性ガラス粉末を均一に混合撹拌して、紡糸機のホッパーに投入することが肝要である。３成分を混合撹拌するか、２つの成分を先に混合し、後に残りの成分を添加混合するかは任意である。 When forming a tapered taper by applying an alkali treatment to a filament of about 76 μm, if the silver-containing soluble glass is blended inhomogeneously, the tapered taper may be cut from the heterogeneously blended portion. Therefore, it is important to uniformly mix and stir the PTT powder, PBT powder and silver-containing soluble glass powder and put them into the hopper of the spinning machine. It is optional to mix and stir the three components, or to mix the two components first and then add and mix the remaining components.
（実施例１〜９）
上記した溶融紡糸による製造方法で以下実施例１〜９に示す銀含有可溶性ガラスの３種類の含有率の異なる抗菌性化粧用ブラシ毛材を製造した。
表１に具体的に示す。銀含有可溶性ガラス０．１重量％を配合した実施例１〜３、銀含有可溶性ガラス０．５重量％を配合した実施例４〜６、銀含有可溶性ガラス０．８重量％を配合した実施例７〜９である。上記した製造方法で３種類の銀含有可溶性ガラスを配合したフィラメントを前記の条件で４〜５倍に延伸して太さ約７６μｍのフィラメントを製造した。これらのフィラメントに上記したアルカリ処理を施して、テーパー状先細部を形成した。
Three types of antibacterial cosmetic brush hair materials of silver-containing soluble glass shown in Examples 1 to 9 below were produced by the above-described production method by melt spinning.
It shows concretely in Table 1. Examples 1 to 3 blended with 0.1% by weight of silver-containing soluble glass, Examples 4 to 6 blended with 0.5% by weight of silver-containing soluble glass, Examples blended with 0.8% by weight of silver-containing soluble glass 7-9. Filaments blended with three types of silver-containing soluble glass by the above-described production method were stretched 4 to 5 times under the above conditions to produce filaments having a thickness of about 76 μm. These filaments were subjected to the alkali treatment described above to form tapered details.
（比較例１〜４）
比較例１は、１００重量％ＰＴＴフィラメントに上記アルカリ処理を施した。比較例２は、９９重量％ＰＴＴに１重量％銀含有可溶性ガラスを配合した。比較例３は、１００重量％ＰＢＴフィラメントに上記アルカリ処理を施した。比較例４は、９９重量％ＰＢＴに１重量％銀含有可溶性ガラスを配合した。
これらのフィラメントに、上記アルカリ処理を施し、胴体部及びテーパー状先細部を形成したものである。
なお、比較例のＰＴＴ及びＰＢＴは実施例で使用した樹脂、そして比較例の銀含有可溶性ガラスも実施例で使用したものを用いている。
In Comparative Example 1, 100% by weight PTT filament was subjected to the alkali treatment. In Comparative Example 2, 1 wt% silver-containing soluble glass was blended with 99 wt% PTT. In Comparative Example 3, the alkali treatment was performed on 100 wt% PBT filament. In Comparative Example 4, 1 wt% silver-containing soluble glass was blended with 99 wt% PBT.
These filaments are subjected to the alkali treatment to form a body part and a tapered tapered detail.
The PTT and PBT of the comparative examples are the same resins used in the examples and the silver-containing soluble glass of the comparative examples is also used in the examples.
次に、リス毛の表面、上記抗菌性化粧用ブラシ毛材であるフィラメント（実施例５）の表面及び比較例２のフィラメントの表面を、レ−ザー顕微鏡（ＶＫ−８７１０ ＶＫ Ａｎａｌｙｚｅｒ（キーエンス製））で撮影した１０００倍の写真を図１〜図５に示す。
図１は、レ−ザー顕微鏡で撮影したリス毛先端部の１０００倍の表面写真である。先端部の先端の太さは７μｍであり、その表面に凹凸部が多数形成されていることが分かる。
図２は、レ−ザー顕微鏡で撮影したリス毛胴体部の１０００倍の表面写真である。胴体部の太さは２５μｍであり、その表面にリング状の凹凸部が多数形成されていることが分かる。
Next, the surface of the squirrel hair, the surface of the filament that is the antibacterial cosmetic brush hair material (Example 5), and the surface of the filament of Comparative Example 2 were subjected to laser microscopy (VK-8710 VK Analyzer (manufactured by Keyence)). 1 to 5 are taken at 1000 times.
FIG. 1 is a 1000 × surface photograph of a squirrel hair tip taken with a laser microscope. The thickness of the tip of the tip is 7 μm, and it can be seen that many irregularities are formed on the surface.
FIG. 2 is a 1000 × surface photograph of a squirrel hair body taken with a laser microscope. It can be seen that the body portion has a thickness of 25 μm, and a large number of ring-shaped uneven portions are formed on the surface thereof.
図３は、レ−ザー顕微鏡で撮影した実施例５のフィラメントの先端部の１０００倍の表面写真である。先端部の先端の太さは５μｍであり、その表面に凹凸部が無数形成されていることが分かる。
図４は、レ−ザー顕微鏡で撮影した実施例５のフィラメントの胴体部の１０００倍の表面写真である。胴体部の太さは４５μｍであり、その表面に凹凸部が多数形成されていることが分かる。
図５は、レ−ザー顕微鏡で撮影した比較例２のフィラメントの先端部の１０００倍の表面写真である。先端部の先端の太さは５３μｍであり、先端部が途中で破断していることが分かる。
図６は、レ−ザー顕微鏡で撮影した比較例２のフィラメントの胴体部の１０００倍の表面写真である。胴体部の太さは４５μｍであり、その表面に凹凸部が多数形成されていることが分かる。
FIG. 3 is a 1000 × surface photograph of the tip of the filament of Example 5 taken with a laser microscope. It can be seen that the thickness of the tip of the tip is 5 μm, and numerous irregularities are formed on the surface thereof.
FIG. 4 is a 1000 × surface photograph of the filament body of Example 5 taken with a laser microscope. It can be seen that the thickness of the body portion is 45 μm, and a large number of uneven portions are formed on the surface thereof.
FIG. 5 is a 1000 × surface photograph of the tip of the filament of Comparative Example 2 taken with a laser microscope. The thickness of the tip of the tip is 53 μm, and it can be seen that the tip is broken halfway.
FIG. 6 is a 1000 × surface photograph of the body of the filament of Comparative Example 2 taken with a laser microscope. It can be seen that the thickness of the body portion is 45 μm, and a large number of uneven portions are formed on the surface thereof.
そして、実施例１〜９の抗菌性化粧用ブラシ毛材のテーパー状先細部の表面を、レ−ザー顕微鏡（ＶＫ−８７１０ ＶＫ−Ａｎａｌｙｚｅｒ（キーエンス製））によって、その表面の凹凸部の高さ及びその分布、そして、上記テーパー状先細部の先端の太さを測定した。その高さ、分布及び太さを表３に示す。
比較例１〜４の毛材のテーパー状先細部の表面を、レ−ザー顕微鏡（ＶＫ−８７１０ ＶＫ−Ａｎａｌｙｚｅｒ（キーエンス製））によって、その表面の凹凸部の高さ及びその分布、そして、上記テーパー状先細部の先端の太さを測定した。その高さ、分布及び太さを表４に示す。
表４から、比較例２及び４では、上記先端が４０μｍの太さのものが３０％発生している。この先端の太さは通常の１０倍以上の太さであり異常なものである。フィラメントの太さは約７６μｍであり、アルカリ処理で形成される上記先端が４０μｍの太さであることは異常なことであり、化粧用ブラシにその太さのものが含まれたとすると、その毛が肌を刺激する重大な欠点となる。
この異常な太さは、銀含有可溶性ガラスを１．０重量％含有させると、アルカリ処理によりテーパー状先細部の領域で発生する。従って、銀含有可溶性ガラスをＰＴＴ及びＰＢＴに１．０重量％含有させることは困難なことが分かった。
From Table 4, in Comparative Examples 2 and 4, 30% of the tip having a thickness of 40 μm is generated. The thickness of the tip is more than 10 times the normal thickness and is abnormal. The thickness of the filament is about 76 μm, and it is abnormal that the tip formed by the alkali treatment is 40 μm thick. Is a serious drawback that irritate the skin.
This extraordinary thickness occurs in a tapered tapered region due to alkali treatment when 1.0% by weight of silver-containing soluble glass is contained. Therefore, it was found that it is difficult to contain 1.0% by weight of silver-containing soluble glass in PTT and PBT.
表３及び表４の静菌活性値は、ＪＩＳ Ｌ １９０２−１９９８（ＩＳＯ２０７４３）の基準に基づいた黄色ブドウ球菌の抗菌性試験の値である。
表３の試験結果は、黄色ブドウ球菌の測定の静菌活性値が３．８〜５．６の範囲の値を示しており、優れた抗菌性が得られていることが分かる。上記基準では静菌活性値が２．２以上の値であれば、抗菌防臭基準を超えていると定められており、上記静菌活性値が３．８〜５．６の範囲の値は、それを遥かに凌ぐものである。
The bacteriostatic activity values in Tables 3 and 4 are values of the antibacterial test of Staphylococcus aureus based on the criteria of JIS L 1902-1998 (ISO 20743).
The test results in Table 3 show that the bacteriostatic activity value of S. aureus is in the range of 3.8 to 5.6, indicating that excellent antibacterial properties are obtained. In the above criteria, if the bacteriostatic activity value is a value of 2.2 or more, it is determined that the antibacterial deodorization standard is exceeded, and the bacteriostatic activity value is in the range of 3.8 to 5.6, It is far beyond that.
化粧用ブラシにおいては、そのブラシが肌に触れることで皮膚常在菌や水棲菌がブラシに付着して、これらの細菌が増殖することにより不快な臭いを発生して、使用者にとって緊急に解決して欲しい問題となっている。細菌が９９％殺菌されると臭いは感知されなくなる。この細菌の９９％殺菌は、静菌活性値が２．２の値を示すことを意味している。ところで、実施例１〜９の抗菌性化粧用ブラシ毛材は、静菌活性値が３．８〜５．６の範囲の値を示しており、静菌活性値２．２より短時間に細菌を殺菌し、臭いの発生を早急に防止できることが分かる。実施例１〜９の抗菌性化粧用ブラシ毛材は、その先端部の表面全面に銀含有可溶性ガラスの凹凸部が２５〜３９個／μｍ２の分布密度で存在するので、皮膚常在菌や水棲菌に対して抗菌性及び防臭性が優れている。 In cosmetic brushes, when the brush touches the skin, skin resident bacteria and varicella bacteria adhere to the brush, and these bacteria grow to produce an unpleasant odor, which is urgently resolved for the user. It is a problem I want you to do. The odor is no longer perceived when 99% of the bacteria are sterilized. 99% sterilization of this bacterium means that the bacteriostatic activity value is 2.2. By the way, the antibacterial cosmetic brush hair materials of Examples 1 to 9 have a bacteriostatic activity value in the range of 3.8 to 5.6, and the bacteria are shorter than the bacteriostatic activity value 2.2. It can be seen that odor can be sterilized and the generation of odor can be prevented immediately. In the antibacterial cosmetic brush hair material of Examples 1 to 9, since the uneven portions of the silver-containing soluble glass are present at a distribution density of 25 to 39 pieces / μm 2 on the entire surface of the tip portion, Excellent antibacterial and deodorant properties against varicella.
表４の比較例１及び３の静菌活性値は、ＰＴＴ及びＰＢＴに銀含有可溶性ガラスが含有されていないために、０．１、０．２の値を示している。一方、上記銀含有可溶性ガラスを１．０重量％含有させた比較例２及び４は、静菌活性値が５．６の高い値を示し抗菌効果に優れるものの、上記したように、アルカリ処理で形成される上記先端に４０μｍの異常な太さのものが発生し、化粧用ブラシにその太さのものが含まれたとすると、その毛が肌を刺激する重大な欠点となる。 The bacteriostatic activity values of Comparative Examples 1 and 3 in Table 4 indicate values of 0.1 and 0.2 because silver-containing soluble glass is not contained in PTT and PBT. On the other hand, Comparative Examples 2 and 4 containing 1.0% by weight of the above-mentioned silver-containing soluble glass have a high bacteriostatic activity value of 5.6 and are excellent in antibacterial effect. If an abnormal thickness of 40 μm is generated at the tip formed, and the cosmetic brush includes the thickness, the hair becomes a serious defect that stimulates the skin.
（使用テスト結果）
銀含有可溶性ガラスを配合した実施例と比較例の毛材を用いて、パウダーブラシについて、５名の使用テストの結果を１〜５の５段階で評価した。パウダーブラシの評価結果を表５（実施例）及び表６（比較例）に示す。
５段階の評価は、「５」が大変優れる、「４」が優れる、「３」が普通、「２」が劣る、そして、「１」が大変劣るとして評価した。
Using the hair materials of Examples and Comparative Examples in which the silver-containing soluble glass was blended, the results of the use test of five people were evaluated in five stages of 1 to 5 for the powder brush. The evaluation results of the powder brush are shown in Table 5 (Example) and Table 6 (Comparative Example).
In the five-step evaluation, “5” is very excellent, “4” is excellent, “3” is normal, “2” is inferior, and “1” is very inferior.
次に、ＰＢＴ配合量が２９．９〜２９．２重量％の実施例１、４及び７、それが１９．９〜１９．２重量％の実施例２、５及び８、それが９．９〜９．２重量％の実施例３、６及び９の物性値である、伸張弾性率（％）とヤング率（Ｎ／ｍｍ２）を計測してその結果を表７〜９に示す。
表１０は、比較例１〜４の伸張弾性率（％）とヤング率（Ｎ／ｍｍ２）を計測した結果を示すものである。
ＰＢＴ配合量が２９．９〜２９．２重量％の実施例１、４及び７の伸張弾性率（％）は７８〜８２（％）で、ヤング率（Ｎ／ｍｍ２）は３３３４〜３４３４であり、ＰＢＴ配合量が１９．９〜１９．２重量％の実施例２、５及び８の伸張弾性率（％）は８３〜８７（％）で、ヤング率（Ｎ／ｍｍ２）は３２３３〜３３３３であり、ＰＢＴ配合量が９．９〜９．２重量％の実施例３、６及び９の伸張弾性率（％）は８８〜９２で、ヤング率（Ｎ／ｍｍ２）は３１２８〜３２３２である。
以上の結果から、伸張弾性率はＰＢＴの配合割合が減少するに従って増加していることが分かり、ヤング率はＰＢＴの配合割合が減少するに従って減少していることが分かる。また、比較例１（ＰＴＴ１００重量％）の伸張弾性率は９４で、ヤング率は３０６７であり、比較例３（ＰＢＴ１００重量％）の伸張弾性率は４０で、ヤング率は４０４７であるが、ＰＢＴを２９．２重量％配合することで、比較例１の伸張弾性率９４を７８にまで減少させることができ、また、比較例１のヤング率３０６７を３４３４にまで増加させることができる。
Examples 1, 4 and 7 having a PBT content of 29.9 to 29.2% by weight have an elastic modulus (%) of 78 to 82 (%) and a Young's modulus (N / mm 2 ) of 3334 to 3434. Yes, Examples 2, 5 and 8 having a PBT content of 19.9 to 19.2% by weight had an elastic modulus (%) of 83 to 87 (%) and a Young's modulus (N / mm 2 ) of 3233 to The tensile elastic modulus (%) of Examples 3, 6 and 9 having a PBT blending amount of 9.9 to 9.2% by weight is 88 to 92, and Young's modulus (N / mm 2 ) is 3128 to 3232. It is.
From the above results, it can be seen that the tensile elastic modulus increases as the blending ratio of PBT decreases, and the Young's modulus decreases as the blending ratio of PBT decreases. Further, Comparative Example 1 (PTT 100 wt%) has an elastic modulus of 94 and Young's modulus of 3067, and Comparative Example 3 (PBT 100 wt%) has an elastic modulus of elasticity of 40 and Young's modulus of 4047. 29.2% by weight, the tensile elastic modulus 94 of Comparative Example 1 can be decreased to 78, and the Young's modulus 3067 of Comparative Example 1 can be increased to 3434.
以上述べたＰＢＴ配合量の割合と伸張弾性率とヤング率の関係は、リキッドブラシ、リップブラシ、ネイルケアブラシ、ファンデーションブラシ、パウダーブラシ、シャドーブラシ、チークブラシ、ハイライトブラシまたはコンシーラーブラシ等のブラシに応じた物性を任意に選択することが可能であることを示している。
そして、実施例１〜９のブラシ毛材は、一方端又は両方端の先端方向にテーパー状先細部が形成されると共に、テーパー状先細部の表面全面に１〜２μｍの凹凸部が設けられており、含み性、転着性が比較例１（ＰＴＴ１００重量％）より優れていることが分かる。
The relationship between the proportion of the PBT blended amount, the elastic modulus of elasticity, and the Young's modulus is as follows for liquid brushes, lip brushes, nail care brushes, foundation brushes, powder brushes, shadow brushes, teak brushes, highlight brushes, concealer brushes, etc. It shows that the corresponding physical properties can be arbitrarily selected.
And the brush bristle material of Examples 1-9 is provided with a 1 to 2 micrometer uneven | corrugated | grooved part in the whole surface of a taper-shaped detail, while a taper-shaped detail is formed in the front-end | tip direction of one end or both ends. It can be seen that the containability and transferability are superior to those of Comparative Example 1 (PTT 100 wt%).
Claims (8)
ポリエステル系樹脂製フィラメントは、ポリトリメチレンテレフタレート７０．０〜９０．０重量％、及びポリブチレンテレフタレート２９．２〜９．９重量％を含む樹脂組成物であり、無機粒子が銀を含有する可溶性ガラス０．８〜０．１重量％であり、
先細部は、表面全面に凹凸部を備えており、該凹凸部に銀粒子が露出していることを特徴とする抗菌性化粧用ブラシ毛材。 It is a hair material for an antibacterial cosmetic brush comprising a polyester resin filament containing inorganic particles having a thickness of 50 to 150 μm and having a tapered shape, and the polyester resin filament is It is a resin composition containing 70.0 to 90.0% by weight of polytrimethylene terephthalate and 29.2 to 9.9% by weight of polybutylene terephthalate, and a soluble glass containing silver containing 0.8 to 0.00%. 1% by weight,
The antibacterial cosmetic brush hair material is characterized in that the tip has an uneven portion on the entire surface, and silver particles are exposed on the uneven portion.
樹脂組成を紡糸機で溶融、混練し押出して、紡糸口より加熱延伸により４〜５倍の延伸を行ってフィラメントを製造する工程と、
上記フィラメントを束に集束して、所定の長さに切断する工程、
切断した一端を水酸化ナトリウム水溶液でアルカリ処理を行って先端部にテーパー状先細部を形成すると共に、当該先細部の表面に凹凸部を形成する工程、
その後に水洗して乾燥を行う工程と、
ブラシ毛材を毛束保持部材に埋設する工程と、
からなることを特徴とする抗菌性化粧用ブラシの製造方法。 A hair material for an antibacterial cosmetic brush comprising a tape made of polyester resin filaments containing inorganic particles, and the polyester resin filament comprises polytrimethylene terephthalate 70.0- 90.0% by weight, polybutylene terephthalate 29.2 to 9.9% by weight, inorganic particles 0.8 to 01% by weight of soluble glass containing silver, the fine details are on the entire surface A method for producing an antibacterial cosmetic brush hair material comprising uneven portions,
A step of producing a filament by melting, kneading and extruding the resin composition with a spinning machine, and stretching by 4 to 5 times by heat stretching from the spinning port;
Focusing the filaments into bundles and cutting them to a predetermined length;
A step of forming a tapered tapered portion at the tip by performing an alkali treatment with a sodium hydroxide aqueous solution on the cut end, and forming an uneven portion on the surface of the tapered portion,
Then, washing with water and drying,
A step of embedding the brush bristle material in the hair bundle holding member;
A method for producing an antibacterial cosmetic brush, comprising: