JP6143357B2 - Polycarbonate resin composition - Google Patents

Description

  The present invention relates to a polycarbonate resin composition, and more particularly to a polycarbonate resin composition excellent in thermal stability, impact resistance and flame retardancy.

  Polycarbonate resins are resins with excellent heat resistance, mechanical properties, and electrical characteristics, and are widely used as, for example, automobile materials, electrical and electronic equipment materials, housing materials, and other parts manufacturing materials in industrial fields. . In particular, the flame retardant polycarbonate resin composition is suitably used as a member of electrical and electronic equipment such as computers, various personal computers and various portable terminals, OA / information equipment such as printers and copying machines.

  As a means for imparting flame retardancy to a polycarbonate resin, conventionally, a halogen-based flame retardant has been added to the polycarbonate resin. However, a polycarbonate resin composition containing a halogen-based flame retardant containing chlorine or bromine may lead to a decrease in thermal stability or corrosion of a molding machine screw or molding die during molding processing. there were. As an alternative method, many polycarbonate resin compositions containing a phosphorus-based flame retardant have been adopted (see, for example, Patent Documents 1 and 2).

In recent years, particularly in the field of electrical and electronic equipment, miniaturization of products and thinning of parts have progressed, and materials with good appearance and high rigidity are required.
As a method for improving the rigidity and dimensional stability of the polycarbonate resin, it is widely performed to contain an inorganic filler such as glass fiber or talc. However, when glass fiber is contained, there is a problem that the surface appearance of the molded product is deteriorated, and the use is limited in a field where a good appearance is required. On the other hand, the resin composition containing talc provides a good surface appearance.

Therefore, various polycarbonate resin compositions containing a phosphorus-based flame retardant and talc have been proposed for the purpose of imparting impact resistance and flame retardancy. At this time, the use of specific talc is also being studied. For example, Patent Document 3 discloses an alloy of polycarbonate resin and ABS resin, a phosphoric ester oligomer flame retardant, and an average particle size of 9 μm or less. , Fe ₂ O ₃ and Al ₂ O ₃ each contain 0.5% by mass or less of talc, and Patent Document 4 proposes that a phosphorus-based flame retardant and granular talc are blended.

However, the polycarbonate resin composition containing talc has a problem that the polycarbonate resin is decomposed due to the strong basicity of talc, resulting in poor impact resistance. This problem has been found to be particularly noticeable when talc is used in combination with a phosphorus-based flame retardant.
Therefore, in the prior art in which talc is blended with a polycarbonate resin and a phosphorus-based flame retardant composition, it has been very difficult to simultaneously impart high flame retardancy, excellent impact resistance, and thermal stability.

JP 59-202240 A JP-A-62-2746 JP 2004-59898 A JP 2007-314766 A

  The present invention has been made in view of the above problems, and an object of the present invention is to provide a polycarbonate resin composition that satisfies thermal stability, flame retardancy, and impact resistance at the same time.

In order to solve the above-mentioned problems, the present inventor surprisingly has high thermal stability and impact resistance when it contains Neuburg silica, instead of talc, and contains both an organic sulfonic acid metal salt and a fluoropolymer. The present inventors have found that a polycarbonate resin composition having a high degree of flame retardancy can be obtained while having the above.
The present invention provides the following polycarbonate resin composition.

[1] 0.001 to 1 part by mass of organic sulfonic acid metal salt (B), 0.1 to 8 parts by mass of Neuburg silica (C) and fluoropolymer (D) 0 with respect to 100 parts by mass of polycarbonate resin (A) The polycarbonate resin composition characterized by containing 1-1 mass part.
[2] The polycarbonate resin according to [1], further comprising 0.5 to 5 parts by mass of the core-shell type graft copolymer (E) with respect to 100 parts by mass of the polycarbonate resin (A). Composition.

  The polycarbonate resin composition of the present invention has a high degree of flame retardancy while having high thermal stability and impact resistance.

  Hereinafter, although an embodiment, an example thing, etc. are shown and explained in detail about the present invention, the present invention is limited to an embodiment, an example, etc. shown below and is not interpreted.

[Overview]
The polycarbonate resin composition of the present invention is based on 100 parts by mass of the polycarbonate resin (A), 0.001 to 1 part by mass of the organic sulfonic acid metal salt (B), 0.1 to 8 parts by mass of Neuburg silica (C), and It contains 0.1 to 1 part by mass of the fluoropolymer (D).

[Neburg silica (C)]
First, Neuburg silica (C) will be described.
Neuburg Silice (Germany: Neuburger Kieselerde, UK: Neuburg Siliceous Earth) is a silica mineral produced in the Neuburg region of southern Germany, a natural mineral composed of spherical, amorphous silica and platy kaolinite. It is. Neuburg silica is a mineral that is deposited on top of a limestone layer from the late Jurassic period, before 95 million years, and stored in a terrain called karst funnel where the limestone collapsed.
Usually, with a transmission electron microscope, kaolinite of about 0.1 to 20 μm hexagonal plate particles and spherical quartz particles of about 0.1 to 10 μm are observed.

The average particle size of Neuburg silica (C) is preferably about 1 to 10 μm, and the chemical composition is preferably about 82 to 91 mass% for SiO _{2 and} about 5 to 11 mass% for Al ₂ O ₃ . Here, the average particle size (average aggregated particle size) is the median particle size (50% volume particle size, D ₅₀ ).

  In the present invention, Neuburg silica (C) is preferably used after being dispersed, further classified or slurried by a disperser such as a jet mill or a bead mill, and filtered to remove coarse particles completely. At that time, the maximum particle size is preferably 5.0 μm or less.

  Such Neuburg silica (C) is preferably subjected to surface treatment in order to obtain sufficient affinity for polycarbonate resin or the like. The surface treatment is preferably a treatment with a silane coupling agent or the like, for example, aminosilane, mercaptosilane, vinyl silane, methacryl silane, epoxy silane, alkyl silane, or the like.

  Moreover, it is preferable that Neuburg silica clay (C) is subjected to a firing treatment in a firing furnace. By performing the baking treatment, water of crystallization existing in the kaolinite portion is removed, the hue of Neuburg silica itself is improved, and the hue of the polycarbonate resin composition containing the same is improved.

Neuburg silica (C), for example, from Hoffmann Mineral GmbH, Germany, etc., with names such as silitin, silicolloid, actidyl, etc., with various particle sizes and those with chemical surface treatment Etc. are available.
For example, Siritin V85, Siritin V88, Siritin N82, Siritin N85, Siritin N87, Siritin Z86, Siritin Z89, Siricolin P87, Siritin N85 Puris, Siritin Z86 Puris, Siritin Z89 Puris, Siricolloid P87 Puris (all trade names, Hoffman Minerals) Manufactured).
As the Neuburg silica clay (C) subjected to the surface treatment, Actidyl VM56, Actidyl MAM, Actidyl MAM-R, Actidyl EM, Actidyl AM, Actidyl MM, Actidyl PF777 (all are trade names, Hoffman Mineral Co.).
Examples of Neuburg silica (C) subjected to the firing treatment include Sylfit Z91, Actifit AM, and Actifit VM (all trade names, manufactured by Hoffman Mineral Co., Ltd.).
These can be used alone or in combination of two or more.

Neuburg Silica (C) does not decrease impact resistance even when used in combination with the organic sulfonic acid metal salt (B), and the polycarbonate resin is hardly decomposed. It was found not to get worse.
The content of Neuburg silica (C) is 0.1 to 8 parts by mass with respect to 100 parts by mass of the polycarbonate resin (A). If the amount is less than 0.1 parts by mass, no effect of improving combustibility is observed. When the amount exceeds 8 parts by mass, the impact characteristics are greatly deteriorated, and the ductility of the material cannot be maintained. The content of Neuburg silica (C) is preferably 0.3 parts by mass or more, more preferably 0.5 parts by mass or more, preferably 7 parts by mass or less, and more preferably 6 parts by mass or less. .

[Polycarbonate resin (A)]
There is no restriction | limiting in the kind of polycarbonate resin used for the polycarbonate resin composition of this invention. In addition, one type of polycarbonate resin may be used, or two or more types may be used in any combination and in any ratio.

  The polycarbonate resin is a polymer having a basic structure having a carbonic acid bond represented by a general formula: — (— O—X—C (═O) —) —. In the formula, X is generally a hydrocarbon group, but for imparting various properties, X introduced with a hetero atom or a hetero bond may be used.

  The polycarbonate resin can be classified into an aromatic polycarbonate resin in which carbon directly bonded to a carbonic acid bond is aromatic carbon and an aliphatic polycarbonate resin in which aliphatic carbon is aliphatic carbon, either of which can be used. Of these, aromatic polycarbonate resins are preferred from the viewpoints of heat resistance, mechanical properties, electrical characteristics, and the like.

  Although there is no restriction | limiting in the specific kind of polycarbonate resin, For example, the polycarbonate polymer formed by making a dihydroxy compound and a carbonate precursor react is mentioned. At this time, in addition to the dihydroxy compound and the carbonate precursor, a polyhydroxy compound or the like may be reacted. Further, a method of reacting carbon dioxide with a cyclic ether using a carbonate precursor may be used. The polycarbonate polymer may be linear or branched. Further, the polycarbonate polymer may be a homopolymer composed of one type of repeating unit or a copolymer having two or more types of repeating units. At this time, the copolymer can be selected from various copolymerization forms such as a random copolymer and a block copolymer. In general, such a polycarbonate polymer is a thermoplastic resin.

Among monomers used as raw materials for aromatic polycarbonate resins, examples of aromatic dihydroxy compounds include:
Dihydroxybenzenes such as 1,2-dihydroxybenzene, 1,3-dihydroxybenzene (ie, resorcinol), 1,4-dihydroxybenzene;
Dihydroxybiphenyls such as 2,5-dihydroxybiphenyl, 2,2′-dihydroxybiphenyl, 4,4′-dihydroxybiphenyl;
2,2′-dihydroxy-1,1′-binaphthyl, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, , 7-dihydroxynaphthalene, dihydroxynaphthalene such as 2,7-dihydroxynaphthalene;

2,2′-dihydroxydiphenyl ether, 3,3′-dihydroxydiphenyl ether, 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy-3,3′-dimethyldiphenyl ether, 1,4-bis (3-hydroxyphenoxy) Dihydroxy diaryl ethers such as benzene and 1,3-bis (4-hydroxyphenoxy) benzene;

2,2-bis (4-hydroxyphenyl) propane (ie, bisphenol A),
1,1-bis (4-hydroxyphenyl) propane,
2,2-bis (3-methyl-4-hydroxyphenyl) propane,
2,2-bis (3-methoxy-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-methoxy-4-hydroxyphenyl) propane,
1,1-bis (3-tert-butyl-4-hydroxyphenyl) propane,
2,2-bis (3,5-dimethyl-4-hydroxyphenyl) propane,
2,2-bis (3-cyclohexyl-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-cyclohexyl-4-hydroxyphenyl) propane,
α, α′-bis (4-hydroxyphenyl) -1,4-diisopropylbenzene,
1,3-bis [2- (4-hydroxyphenyl) -2-propyl] benzene,
Bis (4-hydroxyphenyl) methane,
Bis (4-hydroxyphenyl) cyclohexylmethane,
Bis (4-hydroxyphenyl) phenylmethane,
Bis (4-hydroxyphenyl) (4-propenylphenyl) methane,
Bis (4-hydroxyphenyl) diphenylmethane,
Bis (4-hydroxyphenyl) naphthylmethane,
1,1-bis (4-hydroxyphenyl) ethane,
1,1-bis (4-hydroxyphenyl) -1-phenylethane,
1,1-bis (4-hydroxyphenyl) -1-naphthylethane,
1,1-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) pentane,
1,1-bis (4-hydroxyphenyl) hexane,
2,2-bis (4-hydroxyphenyl) hexane,
1,1-bis (4-hydroxyphenyl) octane,
2,2-bis (4-hydroxyphenyl) octane,
1,1-bis (4-hydroxyphenyl) hexane,
2,2-bis (4-hydroxyphenyl) hexane,
4,4-bis (4-hydroxyphenyl) heptane,
2,2-bis (4-hydroxyphenyl) nonane,
1,1-bis (4-hydroxyphenyl) decane,
1,1-bis (4-hydroxyphenyl) dodecane,
Bis (hydroxyaryl) alkanes such as;

1,1-bis (4-hydroxyphenyl) cyclopentane,
1,1-bis (4-hydroxyphenyl) cyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,4-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,5-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxy-3,5-dimethylphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-propyl-5-methylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -3-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -3-phenylcyclohexane,
1,1-bis (4-hydroxyphenyl) -4-phenylcyclohexane,
Bis (hydroxyaryl) cycloalkanes such as;

9,9-bis (4-hydroxyphenyl) fluorene,
Cardio structure-containing bisphenols such as 9,9-bis (4-hydroxy-3-methylphenyl) fluorene;

4,4′-dihydroxydiphenyl sulfide,
Dihydroxydiaryl sulfides such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfide;

4,4′-dihydroxydiphenyl sulfoxide,
Dihydroxydiaryl sulfoxides such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfoxide;

4,4′-dihydroxydiphenyl sulfone,
And dihydroxydiaryl sulfones such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfone;

Among these, bis (hydroxyaryl) alkanes are preferable, and bis (4-hydroxyphenyl) alkanes are preferable, and 2,2-bis (4-hydroxyphenyl) propane (ie, from the viewpoint of impact resistance and heat resistance). Bisphenol A) is preferred.
In addition, 1 type may be used for an aromatic dihydroxy compound and it may use 2 or more types together by arbitrary combinations and a ratio.

  Examples of the monomer that is a raw material for the aliphatic polycarbonate resin include ethane-1,2-diol, propane-1,2-diol, propane-1,3-diol, 2,2-dimethylpropane-1, 3-diol, 2-methyl-2-propylpropane-1,3-diol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, decane-1,10-diol Alkanediols such as

  Cyclopentane-1,2-diol, cyclohexane-1,2-diol, cyclohexane-1,4-diol, 1,4-cyclohexanedimethanol, 4- (2-hydroxyethyl) cyclohexanol, 2,2,4, Cycloalkanediols such as 4-tetramethyl-cyclobutane-1,3-diol;

  Glycols such as ethylene glycol, 2,2'-oxydiethanol (ie, diethylene glycol), triethylene glycol, propylene glycol, spiro glycol and the like;

  1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 1,4-benzenediethanol, 1,3-bis (2-hydroxyethoxy) benzene, 1,4-bis ( 2-hydroxyethoxy) benzene, 2,3-bis (hydroxymethyl) naphthalene, 1,6-bis (hydroxyethoxy) naphthalene, 4,4′-biphenyldimethanol, 4,4′-biphenyldiethanol, 1,4- Aralkyl diols such as bis (2-hydroxyethoxy) biphenyl, bisphenol A bis (2-hydroxyethyl) ether, bisphenol S bis (2-hydroxyethyl) ether;

  1,2-epoxyethane (ie ethylene oxide), 1,2-epoxypropane (ie propylene oxide), 1,2-epoxycyclopentane, 1,2-epoxycyclohexane, 1,4-epoxycyclohexane, 1-methyl And cyclic ethers such as -1,2-epoxycyclohexane, 2,3-epoxynorbornane, and 1,3-epoxypropane;

  Among the monomers used as the raw material for the polycarbonate resin, carbonyl halides, carbonate esters and the like are used as examples of the carbonate precursor. In addition, 1 type may be used for a carbonate precursor and it may use 2 or more types together by arbitrary combinations and a ratio.

  Specific examples of carbonyl halides include phosgene; haloformates such as bischloroformate of dihydroxy compounds and monochloroformate of dihydroxy compounds.

  Specific examples of the carbonate ester include diaryl carbonates such as diphenyl carbonate and ditolyl carbonate; dialkyl carbonates such as dimethyl carbonate and diethyl carbonate; biscarbonate bodies of dihydroxy compounds, monocarbonate bodies of dihydroxy compounds, and cyclic carbonates. And carbonate bodies of dihydroxy compounds such as

-Manufacturing method of polycarbonate resin The manufacturing method of polycarbonate resin is not specifically limited, Arbitrary methods are employable. Examples thereof include an interfacial polymerization method, a melt transesterification method, a pyridine method, a ring-opening polymerization method of a cyclic carbonate compound, and a solid phase transesterification method of a prepolymer. Hereinafter, a particularly preferable one of these methods will be specifically described.

.. Interfacial polymerization method First, the case where a polycarbonate resin is produced by the interfacial polymerization method will be described. In the interfacial polymerization method, a dihydroxy compound and a carbonate precursor (preferably phosgene) are reacted in the presence of an organic solvent inert to the reaction and an aqueous alkaline solution, usually at a pH of 9 or higher. Polycarbonate resin is obtained by interfacial polymerization in the presence. In the reaction system, a molecular weight adjusting agent (terminal terminator) may be present as necessary, or an antioxidant may be present to prevent the oxidation of the dihydroxy compound.

  The dihydroxy compound and the carbonate precursor are as described above. Of the carbonate precursors, phosgene is preferably used, and a method using phosgene is particularly called a phosgene method.

  Examples of the organic solvent inert to the reaction include chlorinated hydrocarbons such as dichloromethane, 1,2-dichloroethane, chloroform, monochlorobenzene and dichlorobenzene; aromatic hydrocarbons such as benzene, toluene and xylene; It is done. In addition, 1 type may be used for an organic solvent and it may use 2 or more types together by arbitrary combinations and a ratio.

  Examples of the alkali compound contained in the alkaline aqueous solution include alkali metal compounds and alkaline earth metal compounds such as sodium hydroxide, potassium hydroxide, lithium hydroxide, and sodium hydrogen carbonate, among which sodium hydroxide and water Potassium oxide is preferred. In addition, 1 type may be used for an alkali compound and it may use 2 or more types together by arbitrary combinations and a ratio.

  Although there is no restriction | limiting in the density | concentration of the alkali compound in alkaline aqueous solution, Usually, in order to control pH in the alkaline aqueous solution of reaction to 10-12, it is used at 5-10 mass%. For example, when phosgene is blown, the molar ratio of the bisphenol compound and the alkali compound is usually 1: 1.9 or more in order to control the pH of the aqueous phase to be 10 to 12, preferably 10 to 11. Among these, it is preferable that the ratio is 1: 2.0 or more, usually 1: 3.2 or less, and more preferably 1: 2.5 or less.

  Examples of the polymerization catalyst include aliphatic tertiary amines such as trimethylamine, triethylamine, tributylamine, tripropylamine, and trihexylamine; alicyclic rings such as N, N′-dimethylcyclohexylamine and N, N′-diethylcyclohexylamine. Formula tertiary amines; aromatic tertiary amines such as N, N′-dimethylaniline and N, N′-diethylaniline; quaternary ammonium salts such as trimethylbenzylammonium chloride, tetramethylammonium chloride, triethylbenzylammonium chloride, etc. Pyridine; guanine; guanidine salt; and the like. In addition, 1 type may be used for a polymerization catalyst and it may use 2 or more types together by arbitrary combinations and a ratio.

  Examples of the molecular weight regulator include aromatic phenols having a monohydric phenolic hydroxyl group; aliphatic alcohols such as methanol and butanol; mercaptans; phthalimides and the like. Of these, aromatic phenols are preferred. Specific examples of such aromatic phenols include alkyl groups such as m-methylphenol, p-methylphenol, m-propylphenol, p-propylphenol, p-tert-butylphenol, and p-long chain alkyl-substituted phenol. Examples thereof include substituted phenols; vinyl group-containing phenols such as isopropanyl phenol; epoxy group-containing phenols; carboxyl group-containing phenols such as o-hydroxybenzoic acid and 2-methyl-6-hydroxyphenylacetic acid; In addition, a molecular weight regulator may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.

  The usage-amount of a molecular weight regulator is 0.5 mol or more normally with respect to 100 mol of dihydroxy compounds, Preferably it is 1 mol or more, and is 50 mol or less normally, Preferably it is 30 mol or less. By making the usage-amount of a molecular weight modifier into this range, the thermal stability and hydrolysis resistance of a polycarbonate resin composition can be improved.

In the reaction, the order of mixing the reaction substrate, reaction medium, catalyst, additive and the like is arbitrary as long as a desired polycarbonate resin is obtained, and an appropriate order may be arbitrarily set. For example, when phosgene is used as the carbonate precursor, the molecular weight regulator can be mixed at any time as long as it is between the reaction (phosgenation) of the dihydroxy compound and phosgene and the start of the polymerization reaction.
In addition, reaction temperature is 0-40 degreeC normally, and reaction time is normally several minutes (for example, 10 minutes)-several hours (for example, 6 hours).

-Melt transesterification method Next, the case where a polycarbonate resin is manufactured by the melt transesterification method is demonstrated.
In the melt transesterification method, for example, a transesterification reaction between a carbonic acid diester and a dihydroxy compound is performed.

The dihydroxy compound is as described above.
On the other hand, examples of the carbonic acid diester include dialkyl carbonate compounds such as dimethyl carbonate, diethyl carbonate, and di-tert-butyl carbonate; diphenyl carbonate; substituted diphenyl carbonate such as ditolyl carbonate, and the like. Among these, diphenyl carbonate and substituted diphenyl carbonate are preferable, and diphenyl carbonate is more preferable. In addition, carbonic acid diester may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.

  The ratio of the dihydroxy compound and the carbonic acid diester is arbitrary as long as the desired polycarbonate resin can be obtained, but it is preferable to use an equimolar amount or more of the carbonic acid diester with respect to 1 mol of the dihydroxy compound. Is more preferable. The upper limit is usually 1.30 mol or less. By setting it as such a range, the amount of terminal hydroxyl groups can be adjusted to a suitable range.

  In the polycarbonate resin, the amount of terminal hydroxyl groups tends to have a great influence on thermal stability, hydrolysis stability, color tone and the like. For this reason, you may adjust the amount of terminal hydroxyl groups as needed by a well-known arbitrary method. In the transesterification reaction, a polycarbonate resin in which the amount of terminal hydroxyl groups is adjusted can be usually obtained by adjusting the mixing ratio of the carbonic diester and the aromatic dihydroxy compound; the degree of vacuum during the transesterification reaction, and the like. In addition, the molecular weight of the polycarbonate resin usually obtained can also be adjusted by this operation.

When adjusting the amount of terminal hydroxyl groups by adjusting the mixing ratio of the carbonic acid diester and the dihydroxy compound, the mixing ratio is as described above.
Further, as a more aggressive adjustment method, there may be mentioned a method in which a terminal terminator is mixed separately during the reaction. Examples of the terminal terminator at this time include monohydric phenols, monovalent carboxylic acids, carbonic acid diesters, and the like. In addition, 1 type may be used for a terminal terminator and it may use 2 or more types together by arbitrary combinations and a ratio.

  When producing a polycarbonate resin by the melt transesterification method, a transesterification catalyst is usually used. Any transesterification catalyst can be used. Among them, it is preferable to use, for example, an alkali metal compound and / or an alkaline earth metal compound. In addition, auxiliary compounds such as basic boron compounds, basic phosphorus compounds, basic ammonium compounds, and amine compounds may be used in combination. In addition, 1 type may be used for a transesterification catalyst and it may use 2 or more types together by arbitrary combinations and a ratio.

  In the melt transesterification method, the reaction temperature is usually 100 to 320 ° C. The pressure during the reaction is usually a reduced pressure condition of 2 mmHg or less. As a specific operation, a melt polycondensation reaction may be performed under the above-mentioned conditions while removing a by-product such as an aromatic hydroxy compound.

  The melt polycondensation reaction can be performed by either a batch method or a continuous method. When performing by a batch type, the order which mixes a reaction substrate, a reaction medium, a catalyst, an additive, etc. is arbitrary as long as a desired aromatic polycarbonate resin is obtained, What is necessary is just to set an appropriate order arbitrarily. However, considering the stability of the polycarbonate resin and the polycarbonate resin composition, the melt polycondensation reaction is preferably carried out continuously.

  In the melt transesterification method, a catalyst deactivator may be used as necessary. As the catalyst deactivator, a compound that neutralizes the transesterification catalyst can be arbitrarily used. Examples thereof include sulfur-containing acidic compounds and derivatives thereof. In addition, 1 type may be used for a catalyst deactivator and it may use 2 or more types together by arbitrary combinations and a ratio.

  The amount of the catalyst deactivator used is usually 0.5 equivalents or more, preferably 1 equivalent or more, and usually 10 equivalents or less, relative to the alkali metal or alkaline earth metal contained in the transesterification catalyst. Preferably it is 5 equivalents or less. Furthermore, it is 1 ppm or more normally with respect to aromatic polycarbonate resin, and is 100 ppm or less normally, Preferably it is 20 ppm or less.

-Other matters regarding polycarbonate resin The molecular weight of the polycarbonate resin is arbitrary and may be appropriately selected and determined. The viscosity average molecular weight [Mv] converted from the solution viscosity is usually 10,000 or more, preferably 16,000. Above, more preferably 17,000 or more, and usually 40,000 or less, preferably 30,000 or less, more preferably 24,000 or less. By making a viscosity average molecular weight more than the lower limit of the said range, the mechanical strength of the polycarbonate resin composition of this invention can be improved more. On the other hand, by setting the viscosity average molecular weight to be equal to or lower than the upper limit of the above range, the polycarbonate resin composition of the present invention can be suppressed and improved in fluidity, and the molding processability can be improved and the molding process can be easily performed. Two or more types of polycarbonate resins having different viscosity average molecular weights may be mixed and used, and in this case, a polycarbonate resin having a viscosity average molecular weight outside the above-mentioned preferred range may be mixed.

The viscosity average molecular weight [Mv] is obtained by using methylene chloride as a solvent and obtaining an intrinsic viscosity [η] (unit: dl / g) at a temperature of 20 ° C. using an Ubbelohde viscometer. , Η = 1.23 × 10 ⁻⁴ Mv ^0.83 . The intrinsic viscosity [η] is a value calculated from the following equation by measuring the specific viscosity [η _sp ] at each solution concentration [C] (g / dl).

  The terminal hydroxyl group concentration of the polycarbonate resin is arbitrary and may be appropriately selected and determined, but is usually 1,000 ppm or less, preferably 800 ppm or less, more preferably 600 ppm or less. Thereby, the residence heat stability and color tone of the polycarbonate resin composition of the present invention can be further improved. In addition, the lower limit is usually 10 ppm or more, preferably 30 ppm or more, more preferably 40 ppm or more, particularly for polycarbonate resins produced by the melt transesterification method. Thereby, the fall of molecular weight can be suppressed and the mechanical characteristic of the polycarbonate resin composition of this invention can be improved more.

  In addition, the unit of a terminal hydroxyl group density | concentration represents the mass of the terminal hydroxyl group with respect to the mass of polycarbonate resin in ppm. The measurement method is colorimetric determination (method described in Macromol. Chem. 88 215 (1965)) by the titanium tetrachloride / acetic acid method.

  The polycarbonate resin is a polycarbonate resin alone (the polycarbonate resin alone is not limited to an embodiment containing only one type of polycarbonate resin, and is used in a sense including an embodiment containing a plurality of types of polycarbonate resins having different monomer compositions and molecular weights, for example. .), Or an alloy (mixture) of a polycarbonate resin and another thermoplastic resin may be used in combination. Further, for example, for the purpose of further improving flame retardancy and impact resistance, a polycarbonate resin is copolymerized with an oligomer or polymer having a siloxane structure; for the purpose of further improving thermal oxidation stability and flame retardancy A monomer, oligomer or polymer having a copolymer; a monomer, oligomer or polymer having a dihydroxyanthraquinone structure for the purpose of improving thermal oxidation stability; A copolymer with an oligomer or polymer having an olefin structure; a copolymer with a polyester resin oligomer or polymer for the purpose of improving chemical resistance; Good.

  Further, in order to improve the appearance of the molded product and improve the fluidity, the polycarbonate resin may contain a polycarbonate oligomer. The viscosity average molecular weight [Mv] of this polycarbonate oligomer is usually 1,500 or more, preferably 2,000 or more, and usually 9,500 or less, preferably 9,000 or less. Furthermore, the polycarbonate ligomer contained is preferably 30% by mass or less of the polycarbonate resin (including the polycarbonate oligomer).

Further, the polycarbonate resin may be not only a virgin raw material but also a polycarbonate resin regenerated from a used product (so-called material-recycled polycarbonate resin). Examples of the used products include: optical recording media such as optical disks; light guide plates; vehicle window glass, vehicle headlamp lenses, windshields and other vehicle transparent members; water bottles and other containers; eyeglass lenses; Examples include architectural members such as glass windows and corrugated sheets. Also, non-conforming products, pulverized products obtained from sprues, runners, etc., or pellets obtained by melting them can be used.
However, the regenerated polycarbonate resin is preferably 80% by mass or less, more preferably 50% by mass or less, among the polycarbonate resins contained in the polycarbonate resin composition of the present invention. Recycled polycarbonate resin is likely to have undergone deterioration such as heat deterioration and aging deterioration, so when such polycarbonate resin is used more than the above range, hue and mechanical properties can be reduced. It is because there is sex.

[Organic sulfonic acid metal salt (B)]
The polycarbonate resin composition of the present invention contains 0.001 to 1 part by mass of the organic sulfonic acid metal salt (B) as a flame retardant with respect to 100 parts by mass of the polycarbonate resin (A). By containing the organic sulfonic acid metal salt in such an amount together with a predetermined amount of Neuburg silica (C) and fluoropolymer (D), the flame retardancy of the polycarbonate resin composition of the present invention is improved, Thermal stability and impact resistance can be expressed.

The metal of the organic sulfonic acid metal salt (B) is not particularly limited, but is preferably an alkali metal such as sodium, lithium, potassium, rubidium or cesium, or an alkaline earth such as beryllium, magnesium, calcium, strontium or barium. A metal is mentioned.
Among these, alkali metals are preferable, sodium, potassium, cesium or lithium is more preferable, sodium, potassium and cesium are more preferable, and sodium and potassium are particularly preferable. Of these, potassium is preferred from the viewpoints of flame retardancy and hydrolysis resistance.

  Among the organic sulfonic acid metal salts (B), preferred are fluorine-containing aliphatic sulfonic acid metal salts, fluorine-containing aliphatic sulfonic acid imide metal salts, aromatic sulfonic acid metal salts, and aromatic sulfonamide. Metal salts are mentioned.

  Among them, specific examples of preferable ones include potassium nonafluorobutanesulfonate, lithium nonafluorobutanesulfonate, sodium nonafluorobutanesulfonate, cesium nonafluorobutanesulfonate, lithium trifluoromethanesulfonate, sodium trifluoromethanesulfonate, Containing at least one C—F bond in the molecule, such as potassium trifluoromethanesulfonate, potassium pentafluoroethanesulfonate, potassium heptafluoropropanesulfonate, potassium decafluoro-4- (pentafluoroethyl) cyclohexanesulfonate; Alkali metal salts of fluoroaliphatic sulfonic acids;

  At least one C—F in the molecule, such as magnesium nonafluorobutanesulfonate, calcium nonafluorobutanesulfonate, barium nonafluorobutanesulfonate, magnesium trifluoromethanesulfonate, calcium trifluoromethanesulfonate, barium trifluoromethanesulfonate, etc. An alkaline earth metal salt of a fluorine-containing aliphatic sulfonic acid having a bond;

  Disodium difluoromethane disulfonate, dipotassium difluoromethane disulfonate, disodium tetrafluoroethane disulfonate, dipotassium tetrafluoroethane disulfonate, dipotassium hexafluoropropane disulfonate, dipotassium hexafluoroisopropane disulfonate, disodium octafluorobutane disulfonate An alkali metal salt of a fluorinated aliphatic disulfonic acid having at least one C—F bond in the molecule, such as dipotassium octafluorobutanedisulfonate; a metal salt of a fluorinated aliphatic sulfonic acid, such as

  Bis (perfluoropropanesulfonyl) imide lithium, bis (perfluoropropanesulfonyl) imide sodium, bis (perfluoropropanesulfonyl) imide potassium, bis (perfluorobutanesulfonyl) imide lithium, bis (perfluorobutanesulfonyl) imide sodium, In the molecule, such as potassium bis (perfluorobutanesulfonyl) imide, potassium trifluoromethane (pentafluoroethane) sulfonylimide, sodium trifluoromethane (nonafluorobutane) sulfonylimide, potassium trifluoromethane (nonafluorobutane) sulfonylimide, trifluoromethane, etc. An alkali metal salt of a fluorine-containing aliphatic disulfonic imide having at least one C—F bond;

  Cyclo-hexafluoropropane-1,3-bis (sulfonyl) imide lithium, cyclo-hexafluoropropane-1,3-bis (sulfonyl) imide sodium, cyclo-hexafluoropropane-1,3-bis (sulfonyl) imide potassium An alkali metal salt of a cyclic fluorinated aliphatic sulfonimide having at least one C—F bond in the molecule; a metal salt of a fluorinated aliphatic sulfonic imide, such as

  Diphenylsulfone-3,3′-disulfonate dipotassium, diphenylsulfone-3-sulfonate potassium, sodium benzenesulfonate, sodium (poly) styrenesulfonate, sodium paratoluenesulfonate, sodium (branched) dodecylbenzenesulfonate, tri Sodium chlorobenzenesulfonate, potassium benzenesulfonate, potassium styrenesulfonate, potassium (poly) styrenesulfonate, potassium paratoluenesulfonate, potassium (branched) dodecylbenzenesulfonate, potassium trichlorobenzenesulfonate, cesium benzenesulfonate, ( Poly) cesium styrene sulfonate, cesium p-toluenesulfonate, cesium (branched) dodecylbenzene sulfonate, cesium trichlorobenzene sulfonate Etc., alkali metal salts of aromatic sulfonic acids having at least one aromatic group in the molecule;

  Magnesium paratoluenesulfonate, calcium paratoluenesulfonate, strontium paratoluenesulfonate, barium paratoluenesulfonate, magnesium (branched) dodecylbenzenesulfonate, calcium (branched) calcium dodecylbenzenesulfonate in the molecule An alkaline earth metal salt of an aromatic sulfonic acid having an aromatic group of: an aromatic sulfonic acid metal salt, etc.

  Sodium salt of saccharin, potassium salt of N- (p-tolylsulfonyl) -p-toluenesulfimide, potassium salt of N- (N′-benzylaminocarbonyl) sulfanilimide, potassium of N- (phenylcarboxyl) -sulfanilimide Examples thereof include metal salts of aromatic sulfonamides such as alkali metal salts of aromatic sulfonamides having at least one aromatic group in the molecule, such as salts.

Among the examples described above, fluorine-containing aliphatic sulfonic acid metal salts and aromatic sulfonic acid metal salts are more preferable, and fluorine-containing aliphatic sulfonic acid metal salts are particularly preferable.
Further, as the fluorine-containing aliphatic sulfonic acid metal salt, an alkali metal salt of fluorine-containing aliphatic sulfonic acid having at least one C—F bond in the molecule is more preferable, and an alkali metal salt of perfluoroalkanesulfonic acid is particularly preferable. Specifically, potassium nonafluorobutanesulfonate is particularly preferable.
As the aromatic sulfonic acid metal salt, an alkali metal salt of an aromatic sulfonic acid is more preferable, and an alkali of diphenyl sulfone-sulfonic acid such as dipotassium 3,3′-disulfonic acid dipotassium and diphenylsulfone-3-sulfonic acid potassium. Metal salts; sodium paratoluenesulfonate, and alkali metal salts of paratoluenesulfonic acid such as potassium paratoluenesulfonate and cesium paratoluenesulfonate are particularly preferable, and alkali metal salts of paratoluenesulfonic acid are more preferable.

  In addition, 1 type may be used for organic sulfonic acid metal salt (B), and it may use 2 or more types together by arbitrary combinations and a ratio.

  As described above, the content of the organic sulfonic acid metal salt (B) is 0.001 to 1 part by mass with respect to 100 parts by mass of the polycarbonate resin (A), preferably 0.01 parts by mass or more. Preferably it is 0.03 parts by mass or more, more preferably 0.04 parts by mass or more, particularly preferably 0.05 parts by mass or more, and preferably 0.7 parts by mass or less, more preferably 0.5 parts by mass. Hereinafter, it is more preferably 0.3 parts by mass or less, and particularly preferably 0.2 parts by mass or less. By containing the organic sulfonic acid metal salt in such an amount, the formation of a carbonized layer at the time of combustion of the polycarbonate resin can be promoted, the flame retardancy can be further enhanced, and the impact resistance and other machinery possessed by the polycarbonate resin. Good properties such as physical properties, heat resistance, and electrical characteristics can be maintained. When the content is less than 0.001 part by mass, sufficient flame retardancy cannot be obtained, and when it exceeds 1 part by mass, thermal stability and hydrolysis resistance tend to be lowered.

[Fluoropolymer (D)]
The polycarbonate resin composition of this invention contains 0.1-1 mass part of fluoropolymer (D) with respect to 100 mass parts of polycarbonate resin (A). One type of fluoropolymer (D) may be used, or two or more types may be used in any combination and in any ratio.

  Examples of the fluoropolymer (D) include a fluoroolefin resin. The fluoroolefin resin is usually a polymer or copolymer containing a fluoroethylene structure. Specific examples include difluoroethylene resin, tetrafluoroethylene resin, tetrafluoroethylene / hexafluoropropylene copolymer resin, tetrafluoroethylene / perfluoroalkyl vinyl ether copolymer resin, and the like. Of these, tetrafluoroethylene resin and the like are preferable. Examples of the fluoroethylene resin include a fluoroethylene resin having a fibril forming ability.

  The average particle size of the fluoropolymer (D) is not particularly limited, but is preferably 300 to 1000 μm. When the average particle size is less than 300 μm, the drip resistance of the polycarbonate resin composition of the present invention may be reduced. When the average particle size is more than 1000 μm, the fluoropolymer tends to agglomerate and form a molded body. This is not preferable because it may cause appearance defects such as white spots. From such a viewpoint, the average particle size of the fluoropolymer (D) is more preferably 350 to 800 μm, further preferably 380 to 750 μm, and particularly preferably 400 to 700 μm.

  As described above, the content of the fluoropolymer (D) is 0.1 parts by mass or more, preferably 0.2 parts by mass or more, more preferably 0.3 parts by mass with respect to 100 parts by mass of the polycarbonate resin (A). Part or more, and 1 part by weight or less, preferably 0.9 part by weight or less, more preferably 0.8 part by weight or less. When the content of the fluoropolymer (D) is less than the lower limit of the range, the flame retardancy effect due to the anti-dripping agent tends to be insufficient, and when the content exceeds the upper limit of the range, the polycarbonate resin composition There is a possibility that an appearance defect of a molded product obtained by molding an object or a decrease in mechanical strength may occur.

[Core-shell type graft copolymer (E)]
The polycarbonate resin composition of the present invention preferably contains a core-shell type graft copolymer (E).
The core-shell type graft copolymer (E) has a rubber component as a core layer, and is selected from a (meth) acrylic acid ester compound, a (meth) acrylic acid compound, an aromatic vinyl compound, and an unsaturated nitrile compound around it. A core-shell type graft copolymer comprising a shell layer formed by copolymerizing at least one monomer component is preferred.
Such a graft copolymer may be produced by any production method such as bulk polymerization, solution polymerization, suspension polymerization, emulsion polymerization, and the copolymerization method may be a single-stage graft or a multi-stage graft. Also good. Of these, the emulsion polymerization is the easiest and preferred method.

  Specific examples of the rubber component include polybutadiene rubber, polyisoprene rubber, polybutyl acrylate and poly (2-ethylhexyl acrylate), polyalkyl acrylate rubber such as butyl acrylate-2-ethylhexyl acrylate copolymer, and polyorganosiloxane rubber. Silicone rubber, butadiene-acrylic composite rubber, composite rubber made of polyorganosiloxane rubber and polyalkylacrylate rubber, styrene-butadiene rubber, ethylene-propylene rubber, ethylene-butene rubber, ethylene-α-olefin system such as ethylene-octene rubber Examples thereof include rubber, ethylene-acrylic rubber, and fluorine rubber. These may be used alone or in admixture of two or more.

The core-shell type graft copolymer (E) is preferably a graft copolymer obtained by graft polymerization of a monomer component copolymerizable with a diene rubber component.
The rubber component generally has a glass transition temperature of 0 ° C. or lower, preferably −20 ° C. or lower, more preferably −30 ° C. or lower. Specific examples of the rubber component include polybutadiene rubber, butadiene-acrylic composite rubber, styrene-butadiene rubber, and ethylene-propylene-butadiene rubber. These may be used alone or in admixture of two or more.

  Specific examples of monomer components that can be graft copolymerized with the rubber component include aromatic vinyl compounds, vinyl cyanide compounds, (meth) acrylic acid ester compounds, (meth) acrylic acid compounds, glycidyl (meth) acrylates, and the like. Epoxy group-containing (meth) acrylic acid ester compounds; maleimide compounds such as maleimide, N-methylmaleimide and N-phenylmaleimide; α, β-unsaturated carboxylic acid compounds such as maleic acid, phthalic acid and itaconic acid and their anhydrides (For example, maleic anhydride, etc.). These monomer components may be used alone or in combination of two or more. Among these, aromatic vinyl compounds, vinyl cyanide compounds, (meth) acrylic acid ester compounds, and (meth) acrylic acid compounds are preferable from the viewpoint of mechanical properties and surface appearance, and (meth) acrylic acid esters are more preferable. A compound. Specific examples of the (meth) acrylate compound include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, cyclohexyl (meth) acrylate, octyl (meth) acrylate, and the like. be able to. Here, “(meth) acryl” refers to one or both of “acryl” and “methacryl”. The same applies to “(meth) acrylate”.

  The core-shell type graft copolymer (E) is preferably a butadiene-based elastomer from the viewpoint of impact resistance and flame retardancy. Among them, a polybutadiene-containing rubber component is used as a core layer, and (meth) acrylic acid ester is copolymerized around it. A core-shell type graft copolymer comprising a shell layer formed in this manner is particularly preferred. The core-shell type graft copolymer preferably contains 40% by mass or more of a butadiene-based rubber component, and more preferably contains 60% by mass or more. Moreover, what contains 10 mass% or more of (meth) acrylic acid components is preferable.

  Preferable specific examples of these core-shell type graft copolymers include methyl methacrylate-butadiene-styrene copolymer (MBS), methyl methacrylate-acrylonitrile-butadiene-styrene copolymer (MABS), methyl methacrylate-butadiene copolymer ( MB), methyl methacrylate-acrylic butadiene rubber copolymer, methyl methacrylate-acrylic butadiene rubber-styrene copolymer, and the like. Such rubbery polymers may be used alone or in combination of two or more.

  Further, as the core-shell type graft copolymer (E), a core-shell type graft copolymer having an acrylic rubbery polymer as a core layer and an acrylic polymer or a copolymer component as a shell layer around it is also provided. preferable.

  The acrylic rubbery polymer constituting the core layer is composed of an acrylic component. The core of the acrylic component can be obtained by polymerizing an unsaturated nitrile compound such as a (meth) acrylic acid ester compound or acrylonitrile.

  As the acrylic rubbery polymer constituting the core layer, the glass transition temperature is usually 0 ° C. or lower, preferably −20 ° C. or lower, more preferably −30 ° C. or lower. Specific examples of the rubber component include polybutyl acrylate, poly (2-ethylhexyl acrylate), and butyl acrylate / 2-ethylhexyl acrylate copolymer. These may be used alone or in admixture of two or more.

  Aromatic polyfunctional vinyl compounds such as divinylbenzene and divinyltoluene; polyvalent compounds such as ethylene glycol dimethacrylate, 1,3-butanediol diacrylate, trimethylolethane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetramethacrylate Unsaturated carboxylic acid esters of alcohol; unsaturated carboxylic acid allyl esters such as allyl acrylate and allyl methacrylate; cross-linking monomers such as di- and triallyl compounds such as diallyl phthalate, diallyl sebacate, and triallyl triazine You can also

The shell of the acrylic component can be obtained by polymerizing a (meth) acrylic acid ester compound, a (meth) acrylic acid compound, or the like.
Examples of (meth) acrylic acid ester compounds include (meth) acrylic acid alkyl esters such as methyl methacrylate, ethyl methacrylate, n-butyl methacrylate and hexyl methacrylate; aryl (meth) acrylates such as phenyl methacrylate and naphthyl methacrylate; glycidyl acrylate and glycidyl Examples thereof include glycidyl group-containing (meth) acrylates such as methacrylate; among them, methacrylic acid alkyl esters are preferable, and methyl methacrylate is more preferable.
In addition, the said (meth) acrylic acid ester compound can use 1 type (s) or 2 or more types.

  In addition to the (meth) acrylic acid ester compound, other vinyl monomers may be contained. Other vinyl monomers include, for example, aromatic vinyls such as styrene and α-methylstyrene; unsaturated nitriles such as acrylonitrile and methacrylonitrile; vinyl ethers such as methyl vinyl ether and butyl vinyl ether; maleimide, N -Maleimide compounds such as methylmaleimide and N-phenylmaleimide; α, β-unsaturated carboxylic acid compounds such as maleic acid, phthalic acid and itaconic acid, and anhydrides thereof (for example, maleic anhydride); and the like.

  Furthermore, aromatic polyfunctional vinyl compounds such as divinylbenzene and divinyltoluene; polyvalent compounds such as ethylene glycol dimethacrylate, 1,3-butanediol diacrylate, trimethylolethane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetramethacrylate Unsaturated carboxylic acid esters of alcohol; unsaturated carboxylic acid allyl esters such as allyl acrylate and allyl methacrylate; cross-linking monomers such as di- and triallyl compounds such as diallyl phthalate, diallyl sebacate, and triallyl triazine You can also

In the present invention, such a core-shell type graft copolymer (E) is contained in combination with a polycarbonate resin (A), an organic sulfonic acid metal salt (B), Neuburg silica (C) and a fluoropolymer (D). Thus, both thermal stability and impact resistance can be achieved, and an excellent polycarbonate resin composition can be obtained.
A preferable content of the core-shell type graft copolymer (E) is 0.5 to 5 parts by mass with respect to 100 parts by mass of the polycarbonate resin (A). When the content of the core-shell type graft copolymer (E) is less than 0.5 parts by mass, the effect of improving impact resistance is insufficient, and when the content exceeds 5 parts by mass, It tends to cause deterioration of flame retardancy. The content of the core-shell type graft copolymer (E) is more preferably 0.7 parts by mass or more, further preferably 0.8 parts by mass or more, more preferably 4 parts by mass or less, still more preferably 3 It is below mass parts.

[Phosphorus stabilizer]
The polycarbonate resin composition of the present invention preferably contains a phosphorus stabilizer. Any known phosphorous stabilizer can be used. Specific examples include phosphorus oxo acids such as phosphoric acid, phosphonic acid, phosphorous acid, phosphinic acid, and polyphosphoric acid; acidic pyrophosphate metal salts such as acidic sodium pyrophosphate, acidic potassium pyrophosphate, and acidic calcium pyrophosphate; phosphoric acid Group 1 or Group 2B metal phosphates such as potassium, sodium phosphate, cesium phosphate and zinc phosphate; organic phosphate compounds, organic phosphite compounds, organic phosphonite compounds, etc. Particularly preferred.

Organic phosphite compounds include triphenyl phosphite, tris (monononylphenyl) phosphite, tris (monononyl / dinonyl phenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphite, monooctyl Diphenyl phosphite, dioctyl monophenyl phosphite, monodecyl diphenyl phosphite, didecyl monophenyl phosphite, tridecyl phosphite, trilauryl phosphite, tristearyl phosphite, 2,2-methylenebis (4,6-di- tert-butylphenyl) octyl phosphite and the like. Specific examples of such organic phosphite compounds include, for example, “ADEKA STAB 1178”, “ADEKA STAB 2112”, “ADEKA STAB HP-10” manufactured by ADEKA, “JP-351” manufactured by Johoku Chemical Industry Co., Ltd., “ JP-360 ”,“ JP-3CP ”,“ Irgaphos 168 ”manufactured by BASF, and the like.
In addition, 1 type may contain phosphorus stabilizer and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the phosphorus stabilizer is usually 0.001 parts by mass or more, preferably 0.01 parts by mass or more, more preferably 0.03 parts by mass or more, with respect to 100 parts by mass of the polycarbonate resin (A). Moreover, it is 1 mass part or less normally, Preferably it is 0.7 mass part or less, More preferably, it is 0.5 mass part or less. If the content of the phosphorus stabilizer is less than the lower limit of the range, the thermal stability effect may be insufficient, and if the content of the phosphorus stabilizer exceeds the upper limit of the range, the effect May stop and become economical.

[Phenolic stabilizer]
The polycarbonate resin composition of the present invention preferably contains a phenol-based stabilizer. As a phenol type stabilizer, a hindered phenol type antioxidant is mentioned, for example. Specific examples thereof include pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl). ) Propionate, thiodiethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], N, N′-hexane-1,6-diylbis [3- (3,5-di-) tert-butyl-4-hydroxyphenylpropionamide), 2,4-dimethyl-6- (1-methylpentadecyl) phenol, diethyl [[3,5-bis (1,1-dimethylethyl) -4-hydroxyphenyl ] Methyl] phosphoate, 3,3 ′, 3 ″, 5,5 ′, 5 ″ -hexa-tert-butyl-a, a ′, a ″-(mesi Tylene-2,4,6-triyl) tri-p-cresol, 4,6-bis (octylthiomethyl) -o-cresol, ethylenebis (oxyethylene) bis [3- (5-tert-butyl-4- Hydroxy-m-tolyl) propionate], hexamethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], 1,3,5-tris (3,5-di-tert- Butyl-4-hydroxybenzyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) -trione, 2,6-di-tert-butyl-4- (4,6-bis ( Octylthio) -1,3,5-triazin-2-ylamino) phenol, 2- [1- (2-hydroxy-3,5-di-tert-pentylphenyl) ethyl] -4,6-di-te t- pentylphenyl acrylate.

Among them, pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate preferable. Specific examples of such a phenolic antioxidant include “Irganox 1010”, “Irganox 1076” manufactured by BASF, “Adekastab AO-50”, “Adekastab AO-60” manufactured by ADEKA, and the like. Is mentioned.
In addition, 1 type may be contained for the phenol type stabilizer, and 2 or more types may be contained by arbitrary combinations and ratios.

  The content of the phenol-based stabilizer is usually 0.001 part by mass or more, preferably 0.01 part by mass or more, and usually 1 part by mass or less, preferably 100 parts by mass of the polycarbonate resin (A). 0.5 parts by mass or less. When the content of the phenol-based stabilizer is less than the lower limit of the range, the effect as the phenol-based stabilizer may be insufficient, and the content of the phenol-based stabilizer exceeds the upper limit of the range. If this is the case, the effect may reach its peak and not economical.

[Release agent]
Moreover, it is also preferable to contain a mold release agent as needed. Examples of the release agent include aliphatic carboxylic acids, esters of aliphatic carboxylic acids and alcohols, aliphatic hydrocarbon compounds having a number average molecular weight of 200 to 15000, polysiloxane silicone oils, and the like.

  Examples of the aliphatic carboxylic acid include saturated or unsaturated aliphatic monovalent, divalent or trivalent carboxylic acid. Here, the aliphatic carboxylic acid includes alicyclic carboxylic acid. Among these, preferable aliphatic carboxylic acids are monovalent or divalent carboxylic acids having 6 to 36 carbon atoms, and aliphatic saturated monovalent carboxylic acids having 6 to 36 carbon atoms are more preferable. Specific examples of such aliphatic carboxylic acids include palmitic acid, stearic acid, caproic acid, capric acid, lauric acid, arachidic acid, behenic acid, lignoceric acid, serotic acid, mellicic acid, tetrariacontanoic acid, montanic acid, adipine Examples include acids and azelaic acid.

  As aliphatic carboxylic acid in ester of aliphatic carboxylic acid and alcohol, the same thing as the said aliphatic carboxylic acid can be used, for example. On the other hand, examples of the alcohol include saturated or unsaturated monohydric or polyhydric alcohols. These alcohols may have a substituent such as a fluorine atom or an aryl group. Among these, monovalent or polyvalent saturated alcohols having 30 or less carbon atoms are preferable, and aliphatic saturated monohydric alcohols or aliphatic saturated polyhydric alcohols having 30 or less carbon atoms are more preferable. Here, the term “aliphatic” is used as a term including alicyclic compounds.

  Specific examples of such alcohols include octanol, decanol, dodecanol, stearyl alcohol, behenyl alcohol, ethylene glycol, diethylene glycol, glycerin, pentaerythritol, 2,2-dihydroxyperfluoropropanol, neopentylene glycol, ditrimethylolpropane, dipentaerythritol, and the like. Is mentioned.

  In addition, said ester may contain aliphatic carboxylic acid and / or alcohol as an impurity. Moreover, although said ester may be a pure substance, it may be a mixture of a plurality of compounds. Furthermore, the aliphatic carboxylic acid and alcohol which combine and comprise one ester may each be used 1 type, and may use 2 or more types together by arbitrary combinations and a ratio.

  Specific examples of esters of aliphatic carboxylic acids and alcohols include beeswax (a mixture based on myricyl palmitate), stearyl stearate, behenyl behenate, stearyl behenate, glycerin monopalmitate, glycerin monostearate Examples thereof include rate, glycerol distearate, glycerol tristearate, pentaerythritol monopalmitate, pentaerythritol monostearate, pentaerythritol distearate, pentaerythritol tristearate, pentaerythritol tetrastearate and the like.

  Examples of the aliphatic hydrocarbon having a number average molecular weight of 200 to 15000 include liquid paraffin, paraffin wax, microwax, polyethylene wax, Fischer-Tropsch wax, and α-olefin oligomer having 3 to 12 carbon atoms. Here, the aliphatic hydrocarbon includes alicyclic hydrocarbons. Further, these hydrocarbons may be partially oxidized.

Among these, paraffin wax, polyethylene wax, or a partial oxide of polyethylene wax is preferable, and paraffin wax and polyethylene wax are more preferable.
The number average molecular weight of the aliphatic hydrocarbon is preferably 5000 or less.
The aliphatic hydrocarbon may be a single substance, but even a mixture of various constituent components and molecular weights can be used as long as the main component is within the above range.

  Examples of the polysiloxane silicone oil include dimethyl silicone oil, methylphenyl silicone oil, diphenyl silicone oil, and fluorinated alkyl silicone.

  In addition, 1 type may contain the lubricant mentioned above, and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the release agent is usually 0.001 parts by mass or more, preferably 0.01 parts by mass or more, and usually 2 parts by mass or less, preferably 1 with respect to 100 parts by mass of the polycarbonate resin (A). It is below mass parts. When the content of the release agent is less than the lower limit of the range, the effect of releasability may not be sufficient, and when the content of the release agent exceeds the upper limit of the range, hydrolysis resistance And mold contamination during injection molding may occur.

[Other ingredients]
The polycarbonate resin composition of the present invention may contain other components in addition to those described above as necessary, as long as the desired physical properties are not significantly impaired. Examples of other components include resins other than polycarbonate resins and various resin additives. In addition, 1 type may contain other components and 2 or more types may contain them by arbitrary combinations and ratios.

Other resins Examples of the other resins include thermoplastic polyester resins such as polyethylene terephthalate resin, polytrimethylene terephthalate, and polybutylene terephthalate resin;
Polystyrene resin, high impact polystyrene resin (HIPS), acrylonitrile-butadiene-styrene copolymer (ABS resin), acrylonitrile-styrene copolymer (AS resin), acrylonitrile-styrene-acrylic rubber copolymer (ASA resin), acrylonitrile -Styrene resin such as ethylene propylene rubber-styrene copolymer (AES resin); Polyolefin resin such as polyethylene resin and polypropylene resin; Polyamide resin; Polyimide resin; Polyetherimide resin; Polyurethane resin; Polyphenylene ether resin; Resins; polysulfone resins; polymethacrylate resins and the like.
In addition, 1 type may contain other resin and 2 or more types may contain it by arbitrary combinations and a ratio.

-Resin additive Examples of the resin additive include an ultraviolet absorber, a dye / pigment, an antistatic agent, an antifogging agent, an antiblocking agent, a fluidity improver, a plasticizer, a dispersant, and an antibacterial agent. In addition, 1 type may contain resin additive and 2 or more types may contain it by arbitrary combinations and a ratio.
Hereinafter, the example of an additive suitable for the polycarbonate resin composition of this invention is demonstrated concretely.

..Ultraviolet absorbers Examples of ultraviolet absorbers include inorganic ultraviolet absorbers such as cerium oxide and zinc oxide; benzotriazole compounds, benzophenone compounds, salicylate compounds, cyanoacrylate compounds, triazine compounds, oxanilide compounds, malonic acid ester compounds, Examples include organic ultraviolet absorbers such as hindered amine compounds. In these, an organic ultraviolet absorber is preferable and a benzotriazole compound is more preferable. By selecting the organic ultraviolet absorber, the polycarbonate resin composition of the present invention has good transparency and mechanical properties.

Specific examples of the benzotriazole compound include, for example, 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2- [2′-hydroxy-3 ′, 5′-bis (α, α-dimethylbenzyl). ) Phenyl] -benzotriazole, 2- (2′-hydroxy-3 ′, 5′-di-tert-butyl-phenyl) -benzotriazole, 2- (2′-hydroxy-3′-tert-butyl-5 ′) -Methylphenyl) -5-chlorobenzotriazole, 2- (2'-hydroxy-3 ', 5'-di-tert-butyl-phenyl) -5-chlorobenzotriazole), 2- (2'-hydroxy-3 ', 5'-di-tert-amyl) -benzotriazole, 2- (2'-hydroxy-5'-tert-octylphenyl) benzotriazole, 2,2'-methylenebis [4 (1,1,3,3-tetramethylbutyl) -6- (2N-benzotriazol-2-yl) phenol], among others, 2- (2′-hydroxy-5′-tert-octylphenyl) ) Benzotriazole, 2,2′-methylenebis [4- (1,1,3,3-tetramethylbutyl) -6- (2N-benzotriazol-2-yl) phenol], particularly 2- (2 ′ -Hydroxy-5'-tert-octylphenyl) benzotriazole is preferred.
Specific examples of such a benzotriazole compound include “Seesorb 701”, “Seesorb 705”, “Seesorb 703”, “Seesorb 702”, “Seesorb 704”, and “Seesorb 709” manufactured by Sipro Kasei Co., Ltd. “Biosorb 520”, “Biosorb 582”, “Biosorb 580”, “Biosorb 583” manufactured by Yakuhin Kagaku Co., Ltd. “Chemisorb 71”, “Chemisorb 72” manufactured by Chemipro Kasei Co., Ltd. “Siasorb UV5411” manufactured by Cytec Industries, “LA-32”, “LA-38”, “LA-36”, “LA-34”, “LA-31”, “TINUVIN P”, “TINUVIN 234”, “TINUVIN 326”, “TINUVIN 327” manufactured by BASF ”,“ Tinuvin 328 ”and the like.

  Specific examples of the benzophenone compound include, for example, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid, 2-hydroxy-4-n-octoxy Benzophenone, 2-hydroxy-n-dodecyloxybenzophenone, bis (5-benzoyl-4-hydroxy-2-methoxyphenyl) methane, 2,2'-dihydroxy-4-methoxybenzophenone, 2,2'-dihydroxy-4 4,4′-dimethoxybenzophenone and the like. Specific examples of such a benzophenone compound include “Seesorb 100”, “Seesorb 101”, “Seesorb 101S”, “Seesorb 102”, and “Seesorb 102” manufactured by Cypro Kasei Co., Ltd. Seesorb 103 ", joint medicine “Biosorb 100”, “Biosorb 110”, “Biosorb 130”, manufactured by Kemipro Kasei Co., Ltd. “Chemisorb 10”, “Chemisorb 11”, “Chemisorb 11S”, “Chemisorb 12”, “Chemsorb 13”, “Chemisorb 111” BASF “Ubinur 400”, BASF “Ubinur M-40”, BASF “Ubinur MS-40”, Cytec Industries “Thiasorb UV9”, “Thiasorb UV284”, “Thiasorb UV531”, “Thiasorb” UV24 "," ADEKA STAB 1413 "manufactured by ADEKA," ADEKA STAB LA-51 "and the like.

  Specific examples of the salicylate compound include phenyl salicylate and 4-tert-butylphenyl salicylate. Specific examples of such a salicylate compound include, for example, “Seesorb 201” and “Seesorb” manufactured by Sipro Kasei Co., Ltd. 202 ”,“ Kemisorb 21 ”,“ Kemisorb 22 ”manufactured by Chemipro Kasei Co., Ltd., and the like.

  Specific examples of the cyanoacrylate compound include, for example, ethyl-2-cyano-3,3-diphenyl acrylate, 2-ethylhexyl-2-cyano-3,3-diphenyl acrylate, and the like. Specifically, for example, “Seasorb 501” manufactured by Sipro Kasei Co., Ltd., “Biosorb 910” manufactured by Kyodo Pharmaceutical Co., Ltd., “Ubisolator 300” manufactured by Daiichi Kasei Co., Ltd., “Ubinur N-35” manufactured by BASF, 539 "and the like.

  Examples of the triazine compound include a compound having a 1,3,5-triazine skeleton. Specific examples of such a triazine compound include, for example, “LA-46” manufactured by ADEKA, “Tinuvin” manufactured by BASF. 1577ED "," Tinuvin 400 "," Tinuvin 405 "," Tinuvin 460 "," Tinuvin 477-DW "," Tinuvin 479 "and the like.

  Specific examples of the oxanilide compound include, for example, 2-ethoxy-2′-ethyl oxalinic acid bis-arinide and the like. Specific examples of such an oxalinide compound include “Sanduboa” manufactured by Clariant Corporation. VSU "etc. are mentioned.

  As the malonic acid ester compound, 2- (alkylidene) malonic acid esters are preferable, and 2- (1-arylalkylidene) malonic acid esters are more preferable. Specific examples of such a malonic ester compound include “PR-25” manufactured by Clariant Japan, “B-CAP” manufactured by BASF, and the like.

  The content of the ultraviolet absorber is usually 0.01 parts by mass or more, preferably 0.1 parts by mass or more, and usually 3 parts by mass or less, preferably 1 with respect to 100 parts by mass of the polycarbonate resin (A). It is below mass parts. If the content of the ultraviolet absorber is less than the lower limit of the range, the effect of improving the weather resistance may be insufficient, and if the content of the ultraviolet absorber exceeds the upper limit of the range, the mold Debogit etc. may occur and cause mold contamination. In addition, 1 type may contain the ultraviolet absorber and 2 or more types may contain it by arbitrary combinations and a ratio.

-Dye / pigment Examples of the dye / pigment include inorganic pigments, organic pigments, and organic dyes.
Examples of inorganic pigments include sulfide pigments such as cadmium red and cadmium yellow; silicate pigments such as ultramarine blue; titanium oxide, zinc white, petal, chromium oxide, iron black, titanium yellow, zinc-iron brown , Titanium Cobalt Green, Cobalt Green, Cobalt Blue, Oxide Pigment such as Copper-Chromium Black, Copper-Iron Black, Chromic Acid Pigment such as Yellow Lead and Molybdate Orange; Ferrocyan Pigment such as Bitumen Etc.

  Examples of organic pigments and organic dyes include phthalocyanine dyes such as copper phthalocyanine blue and copper phthalocyanine green; azo dyes such as nickel azo yellow; thioindigo, perinone, perylene, quinacridone, dioxazine, iso Examples thereof include condensed polycyclic dyes such as indolinone and quinophthalone; anthraquinone, heterocyclic and methyl dyes.

Of these, titanium oxide, cyanine-based, quinoline-based, anthraquinone-based, and phthalocyanine-based compounds are preferable from the viewpoint of thermal stability.
In addition, 1 type may contain the dye / pigment, and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the dye / pigment is usually 5 parts by mass or less, preferably 3 parts by mass or less, more preferably 2 parts by mass or less with respect to 100 parts by mass of the polycarbonate resin (A). If the content of the dye / pigment is too large, the impact resistance may not be sufficient.

[Production Method of Polycarbonate Resin Composition]
There is no restriction | limiting in the manufacturing method of the polycarbonate resin composition of this invention, The manufacturing method of a well-known polycarbonate resin composition can be employ | adopted widely.
Specific examples include polycarbonate resin (A), organic sulfonic acid metal salt (B), Neuburg silica (C) and fluoropolymer (D), and other components blended as necessary, such as a tumbler. And kneading using a mixer such as a Banbury mixer, a roll, a Brabender, a single-screw kneading extruder, a twin-screw kneading extruder, or a kneader.

In addition, for example, without mixing each component in advance, or only a part of the components is mixed in advance, and fed to an extruder using a feeder and melt-kneaded to produce the polycarbonate resin composition of the present invention. You can also.
Also, for example, by mixing a part of the components in advance and supplying the resulting mixture to an extruder and melt-kneading it as a master batch, this master batch is again mixed with the remaining components and melt-kneaded. The polycarbonate resin composition of the present invention can also be produced.
In addition, for example, when mixing a component that is difficult to disperse, the component that is difficult to disperse is dissolved or dispersed in a solvent such as water or an organic solvent in advance, and kneaded with the solution or the dispersion. It can also improve sex.

[Molded body]
The polycarbonate resin composition of the present invention is usually molded into an arbitrary shape and used as a molded body. There is no restriction | limiting in the shape, pattern, color, dimension, etc. of this molded object, What is necessary is just to set arbitrarily according to the use of the molded object.

  Examples of molded products include electrical and electronic equipment, information terminal equipment, home appliances, OA equipment, machine parts, vehicle parts, building members, various containers, leisure goods and miscellaneous goods, medical equipment, lighting equipment parts and members. Is mentioned.

Electric and electronic devices, information terminal devices, home appliances, and OA devices include, for example, display devices such as personal computers, game machines, TVs, electronic paper, printers, copiers, scanners, fax machines, electronic notebooks; PDAs, mobile phones, tablets Various portable terminals such as terminals; electronic desk calculators, electronic dictionaries; cameras, video cameras and their lenses; battery packs, recording media drives and reading devices, mice, numeric keys, CD players, MD players, portable radio / audio players, etc. Parts.
Among them, the polycarbonate resin composition of the present invention is particularly suitable as a member of information / mobile devices such as computers, notebook computers, tablet terminals, smartphones, mobile phones, and OA devices such as printers and copiers. Can be used.

The manufacturing method of a molded object is not specifically limited, The molding method generally employ | adopted about the polycarbonate resin composition can be employ | adopted arbitrarily. For example, injection molding method, ultra-high speed injection molding method, injection compression molding method, two-color molding method, hollow molding method such as gas assist, molding method using heat insulating mold, rapid heating mold were used. Molding method, foam molding (including supercritical fluid), insert molding, IMC (in-mold coating molding) molding method, extrusion molding method, sheet molding method, thermoforming method, rotational molding method, laminate molding method, press molding method, Examples thereof include a blow molding method. A molding method using a hot runner method can also be used.
The obtained molded article of the present invention can be used as a practical molded article having high flame retardancy and mechanical properties without impairing the excellent properties of the polycarbonate resin as described above.

Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not construed as being limited to the following examples.
In the following description, “parts” means “parts by mass” based on mass standards unless otherwise specified.
The raw material components used in the examples and comparative examples are as shown in Table 1 below.

(Examples 1-6, Comparative Examples 1-3)
[Production of resin pellets]
Each component described in Table 1 was blended in the ratio (mass ratio) described in Table 3, mixed for 20 minutes with a tumbler, then supplied to Nippon Steel Works (TEX30HSST) equipped with 1 vent, and screw Kneaded under the conditions of a rotational speed of 200 rpm, a discharge rate of 20 kg / hour, and a barrel temperature of 280 ° C., the molten resin extruded into a strand is quenched in a water tank and pelletized using a pelletizer to obtain a pellet of a polycarbonate resin composition It was.

[Evaluation of thermal stability (Q value)]
As an evaluation of thermal stability, the outflow amount per unit time: Q value was measured. The Q value is measured by drying the pellets obtained above at 120 ° C. for 4 hours or more and then using an elevated flow tester to discharge the composition per unit time under the conditions of 280 ° C. and a load of 1.60 kgf. The quantity Q value (unit: × 10 ⁻² cm ³ / sec) was measured to evaluate the thermal stability.
An orifice having a diameter of 1 mm and a length of 10 mm was used.
In Table 3, it is expressed as “thermal stability (Q value)”.

[Flame retardance evaluation]
The obtained pellets were dried at 120 ° C. for 5 hours, and then injection molded under the conditions of a cylinder temperature of 300 ° C. and a mold temperature of 80 ° C. using a SE100DU injection molding machine manufactured by Sumitomo Heavy Industries, Ltd. A test specimen for UL test having a thickness of 125 mm, a width of 13 mm, and a thickness of 0.8 mm was molded.
The flame resistance of each polycarbonate resin composition was evaluated by conditioning the test specimen for UL test obtained by the above method for 48 hours in a temperature-controlled room at 23 ° C. and 50% humidity. The test was conducted in accordance with UL94 test (combustion test of plastic materials for equipment parts) defined by Laboratories (UL). UL94V is a method for evaluating flame retardancy from the after-flame time and drip properties after indirect flame of a burner for 10 seconds on a test piece of a predetermined size held vertically, V-0, V- In order to have flame retardancy of 1 and V-2, it is necessary to satisfy the criteria shown in Table 2 below.

ここで残炎時間とは、着火源を遠ざけた後の、試験片の有炎燃焼を続ける時間の長さである。また、ドリップによる綿着火とは、試験片の下端から約３００ｍｍ下にある標識用の綿が、試験片からの滴下（ドリップ）物によって着火されるかどうかによって決定される。なお、表３中、「ＵＬ難燃性」と表記する。

Here, the after-flame time is the length of time for which the flammable combustion of the test piece is continued after the ignition source is moved away. The cotton ignition by the drip is determined by whether or not the labeling cotton, which is about 300 mm below the lower end of the test piece, is ignited by a drip from the test piece. In Table 3, it is expressed as “UL flame retardancy”.

[Impact resistance evaluation]
The pellets obtained above were dried at 120 ° C. for 5 hours, and then injection molded under the conditions of a cylinder temperature of 280 ° C. and a mold temperature of 80 ° C. using an SG75MII type injection molding machine manufactured by Sumitomo Heavy Industries, Ltd. An ISO multipurpose specimen (3 mm thick) was molded.
Based on ISO179, the notched Charpy impact strength (unit: kJ / m ² ) was measured at a temperature of 23 ° C. In Table 3, it is expressed as “notched Charpy impact strength”.

  Comparing the results of Examples 1 to 6 and Comparative Example 1 shown in Table 3, flame retardance is improved when a predetermined amount of Neuburg Silica (C) is contained in the polycarbonate resin (A), while Examples 1 and 2 are improved. Comparing with Comparative Example 2, it can be seen that although flammability is improved with talc, impact resistance and thermal stability are deteriorated. Further, when Examples 1 to 6 and Comparative Example 3 are compared, it can be seen that if there is too much Neuburg silica (C), impact resistance and flame retardancy deteriorate.

  Since the polycarbonate resin composition of the present invention is a polycarbonate resin molding material having high thermal stability and impact resistance and high flame retardancy, particularly, electrical and electronic equipment, OA equipment, information terminal equipment, and home appliances. It can be suitably used for parts such as, and the industrial applicability is very high.

Claims (2)

  For 100 parts by mass of the polycarbonate resin (A), 0.001 to 1 part by mass of the organic sulfonic acid metal salt (B), 0.1 to 8 parts by mass of Neuburg silica (C), and 0.1 to 0.1 parts of the fluoropolymer (D). A polycarbonate resin composition comprising 1 part by mass.   Furthermore, 0.5-5 mass parts of core-shell type graft copolymers (E) are contained with respect to 100 mass parts of polycarbonate resin (A), The polycarbonate resin composition of Claim 1 characterized by the above-mentioned.