JP6067604B2 - Beauty pack base sheet, beauty pack material using the same, and method of manufacturing beauty pack material - Google Patents
Beauty pack base sheet, beauty pack material using the same, and method of manufacturing beauty pack material Download PDFInfo
- Publication number
- JP6067604B2 JP6067604B2 JP2014034948A JP2014034948A JP6067604B2 JP 6067604 B2 JP6067604 B2 JP 6067604B2 JP 2014034948 A JP2014034948 A JP 2014034948A JP 2014034948 A JP2014034948 A JP 2014034948A JP 6067604 B2 JP6067604 B2 JP 6067604B2
- Authority
- JP
- Japan
- Prior art keywords
- beauty pack
- beauty
- nonwoven fabric
- oil
- pack material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、美容液の浸潤した顔を覆う美容パック材に関する。 The present invention relates to a beauty pack material covering a face infiltrated with a beauty serum.
従来より、顔皮膚の美容のため、栄養分や水分の補給等を目的として美容パックが行われている。 Conventionally, beauty packs have been used for the purpose of replenishing nutrients and moisture for facial skin beauty.
美容パックは、有効成分を含む液体やゾル及びそれらを泡状にしたもの（以下、纏めて「美容液等」という）を顔皮膚に塗布した後、一定時間経過してから顔に塗布していた美容液等を除去し、洗顔等をすることで完了する。 The beauty pack is applied to the face after a certain time has elapsed after applying a liquid or sol containing active ingredients and a foamed product (hereinafter collectively referred to as “beauty liquid etc.”) to the face skin. Remove the essence and wash your face.
通常、美容液等による美容効果を発揮させるためには、顔皮膚上に美容液等を一定時間保持しておかなければならない。従って、美容パックの際には、美容液等を顔面全体に均一になるように塗布したり、美容液等が乾燥したり垂れたりしてしまわないようにラッピング材で覆うような手間が必要となり、粘性が高いあるいは泡状の美容液等であれば前者の手間が大きく、粘性の低い美容液等であれば後者に関する手間が大きくなる。 In general, in order to exert the beauty effect of a beauty serum or the like, the beauty fluid or the like must be kept on the face skin for a certain period of time. Therefore, in the case of a beauty pack, it is necessary to apply the cosmetic liquid etc. evenly over the entire face, and to cover it with a wrapping material so that the cosmetic liquid etc. will not dry or sag. If the viscosity of the liquid is high or foamy, the former takes a lot of work, and if the liquid has a low viscosity, the work related to the latter is large.
そのため、粘性の低い美容液等については、それらををある程度保持することのできるシート材を基材として、該基材に予め美容液等を含浸させておいたものを美容パック材とし、この美容パック材で顔を覆う美容パック法が提案されており、更に近年では、美容パック材に含まれる有効成分そのものによる美容効果だけでなく、美容効果を向上させたりする等の付加価値を備えた美容パック材が開発されるようになっている。 Therefore, for cosmetic liquids with low viscosity, a sheet material that can hold them to some extent is used as a base material, and a cosmetic pack material is prepared by impregnating the base material in advance with a cosmetic liquid. A beauty pack method that covers the face with a pack material has been proposed, and more recently, beauty with added value such as improving the beauty effect as well as the beauty effect by the active ingredient itself contained in the beauty pack material. Pack materials are being developed.
例えば、下記特許文献１には、美肌効果の向上のためのマッサージを美容パック中に行い易くすることを目的として、マッサージの手順等が鏡文字によって記された美容パック材が開示されている。 For example, Patent Document 1 below discloses a beauty pack material in which massage procedures and the like are written in mirror letters for the purpose of facilitating a massage for improving the skin beautifying effect in a beauty pack.
また、下記特許文献２には、マイナスイオン電子作用で美肌効果を齎すことを目的として、ゲルマニウム金属片が柔軟質樹脂シートに埋め込まれた美容パックシートが開示されている。 Patent Document 2 below discloses a beauty pack sheet in which a germanium metal piece is embedded in a flexible resin sheet for the purpose of enhancing the skin beautifying effect by negative ion electronic action.
一般的に美容パック材は顔面を覆うため、その基材は顔の大きさ程度の円・楕円形状に形成され、更に、パック中に、呼吸・会話・視認が可能となるよう、口・鼻・目に相当する箇所に孔や切り込みが設けられているが、美容パック中は特定の色調・質感を有する基材が顔面全体に張り付いている状態となるため、美容パック中の顔面は美観に優れず、また、他者が見た場合の個人識別性が著しく低下し、場合によっては周囲に不要な恐怖心を生じさせてしまうこともあった。 In general, beauty pack materials cover the face, so the base material is formed into a circle or ellipse that is about the size of the face, and the mouth and nose can be breathed, conversed, and visually recognized in the pack. -Although holes and cuts are provided in the area corresponding to the eyes, the base material with a specific color tone and texture is stuck to the entire face in the beauty pack, so the face in the beauty pack is beautiful In addition, the personal identification when viewed by others is significantly reduced, and in some cases, unnecessary fear may be generated in the surroundings.
そのため、美容パックは人目を憚って行うことが当然とされ、従来の美容パック材は実質的に利用できる場所や状況（主に他人の存在に関する）について、制限の大きいものでえあった。 For this reason, it is natural that the beauty pack should be carried out with eyes, and the conventional beauty pack material has a large limitation on the places and situations (mainly related to the presence of others) that can be practically used.
本発明は、美容パック中であっても個人識別性の高い美容パック材及びその製造方法の提供を目的とする。 An object of the present invention is to provide a beauty pack material with high personal identification even in a beauty pack and a method for manufacturing the same.
上記課題を解決するため、本発明の美容パック用基材シートは、再生セルロース連続長繊維不織布に油性グラビアインキからなる隈取模様がグラビア印刷によって印刷されていることを特徴とする。 In order to solve the above-mentioned problems, the base sheet for a beauty pack of the present invention is characterized in that a reed cellulose continuous long fiber nonwoven fabric is printed with a gravel pattern made of an oil-based gravure ink by gravure printing.
本発明の美容パック用基材シートによれば、液体や乳液状の美容液が浸潤した状態における透明度が高く他者に見られた際の個人識別性が高いため、予期しない対面者が現れた場合のトラブルが従来よりも軽減できることが期待される共に、隈取模様により伝統芸能である歌舞伎の演者を模したポージング等と組み合わせることで、他者と共に楽しむことのできる美容パックとなることから、従来の美容パック用基材シートよりも美容パックを実施できる場所や状況が広くなる。 According to the base sheet for a beauty pack of the present invention, an unexpected face-to-face appears because the transparency in a state in which a liquid or milky serum is infiltrated is high and the personal identification is high when seen by others. It is expected that the troubles in the case can be reduced than before, and it becomes a beauty pack that can be enjoyed with others by combining it with posing that imitates the performer of Kabuki who is a traditional performing art with a take-off pattern, The place and the situation where a beauty pack can be implemented become wider than a conventional base sheet for a beauty pack.
加えて、本発明の美容パック用基材シートの隈取模様は、再生セルロース連続長繊維不織布に対してグラビア印刷によって油性グラビアインキが印刷されたものであるので、本発明の美容パック用基材シートは、美容液が浸潤してもインキの溶出が抑制された優れた美容パック用基材シートとなる。 In addition, the trimming pattern of the base sheet for the beauty pack of the present invention is obtained by printing oil-based gravure ink on the regenerated cellulose continuous long-fiber nonwoven fabric by gravure printing. Becomes an excellent base sheet for a beauty pack in which elution of ink is suppressed even when the cosmetic liquid is infiltrated.
なお、本発明の美容パック用基材シートにおいては、前記油性グラビアインキをウレタン系二液硬化型のものすると、再生セルロース連続長繊維不織布に対する展着性がより向上し、美容液が浸潤した場合のインキの溶出し難さや耐摩耗性がより向上するため好ましい。 In addition, in the base sheet for the beauty pack of the present invention, when the oil-based gravure ink is of a urethane two-component curable type, the spreadability to the regenerated cellulose continuous long-fiber nonwoven fabric is further improved, and the beauty liquid is infiltrated. This is preferred because the elution of the ink and the abrasion resistance are further improved.
また、本発明の美容パック用基材シートは、基材シートである再生セルロース連続長繊維不織布の目付が小さ過ぎると、美容液を浸潤させても美容パックの効果を得るために充分な量の美容液を保持できなくなる。一方、基材シートの目付が大き過ぎると、余剰の美容液を保持することにもなり、得られる美容パックの効果に対して不要なコスト増が生じることになる。従って、本発明の美容パック用基材シートにおいては、目付は８０〜１００ｇ／ｍ２程度とすることが好ましい。 In addition, when the basis weight of the regenerated cellulose continuous long-fiber nonwoven fabric that is the base material sheet is too small, the base sheet for the beauty pack of the present invention has a sufficient amount to obtain the effect of the beauty pack even if the cosmetic liquid is infiltrated. The serum cannot be retained. On the other hand, if the basis weight of the base material sheet is too large, excess cosmetic liquid is also retained, and an unnecessary cost increase is generated with respect to the effect of the obtained beauty pack. Therefore, in the base sheet for beauty packs of the present invention, the basis weight is preferably about 80 to 100 g / m 2 .
また、上記課題を解決するため、本発明の美容パック材の製造方法は、再生セルロース連続長繊維不織布に、油性グラビアインキをグラビア印刷する工程と、前記油性グラビアインキが印刷された再生セルロース連続長繊維不織布に美容液を含浸させる工程と、を含むことを特徴とする。 In addition, in order to solve the above-mentioned problems, the method for producing a beauty pack material of the present invention includes a step of gravure printing an oil-based gravure ink on a regenerated cellulose continuous long-fiber nonwoven fabric, and a regenerated cellulose continuous length printed with the oil-based gravure ink. And a step of impregnating the fiber nonwoven fabric with a cosmetic liquid.
そのため、本発明の美容パック材の製造方法によれば、美容パック時の透明度が高く、かつ、色落ちのし難い任意の模様を備えた美容パック材を、容易に得ることが可能となる。 Therefore, according to the method for manufacturing a beauty pack material of the present invention, it is possible to easily obtain a beauty pack material having an arbitrary pattern that has high transparency at the time of the beauty pack and is difficult to lose color.
なお、本発明の美容パック材の製造方法においては、前記油性グラビアインキをウレタン系二液硬化型のものとすると、より色落ちのし難い美容パック材が得られるため、より好ましい。 In the method for producing a beauty pack material of the present invention, it is more preferable that the oil-based gravure ink is of a urethane two-component curable type because a beauty pack material that is more difficult to discolor is obtained.
また、本発明の美容パック材の製造方法においては、より安全性の高い美容パック材を得るために、前記油性グラビアインキをＮＬ規制をクリアした原料からなるインキとしたり、皮膚パッチテストを行って皮膚刺激性を確認しておくことが、より好ましい。 In addition, in the method of manufacturing the beauty pack material of the present invention, in order to obtain a safer beauty pack material, the oil-based gravure ink is used as an ink made of a raw material that satisfies the NL regulations, or a skin patch test is performed. It is more preferable to confirm skin irritation.
以下、本発明の製造方法の実施例を詳細に説明する。但し、以下に示す実施例は、本発明の技術思想を具体化するための美容パック材の製造方法の一例を示すものであって、本発明をこの実施例に限定することを意図するものではなく、本発明は特許請求の範囲に示した技術思想を逸脱することなく種々の変更を行ったものにも均しく適用し得るものである。 Hereinafter, examples of the production method of the present invention will be described in detail. However, the following embodiment shows an example of a method for manufacturing a beauty pack material for embodying the technical idea of the present invention, and is not intended to limit the present invention to this embodiment. The present invention can be equally applied to various modifications without departing from the technical idea shown in the claims.
［実施例１］
［基材シート］
基材としては目付け８０ｇ／ｍ２の再生セルロース連続長繊維不織布を用いた。
銅アンモニア溶液にコットンリンターを溶解させた銅アンモニアレーヨン原液を流下緊張紡糸法により連続で紡糸することで、繊維が網状になりながら相互接着するように為し、その後、高圧水流処理で３次元的に交絡させることで、本実施例で用いる再生セルロース連続長繊維不織布原反を得た。
[Example 1]
[Base material sheet]
As the substrate, a regenerated cellulose continuous long-fiber nonwoven fabric with a basis weight of 80 g / m 2 was used.
A copper ammonia rayon stock solution in which cotton linters are dissolved in a copper ammonia solution is continuously spun by the falling tension spinning method so that the fibers are bonded to each other while forming a network, and then three-dimensionally by high-pressure water treatment. The regenerated cellulose continuous long fiber nonwoven fabric raw material used in this example was obtained by entanglement with the material.
次いで、上記で得られた再生セルロース連続長繊維不織布原反を、図１に示すように裁断及び切り込みを入れること、本実施例で用いる基材シートとした。 Subsequently, the regenerated cellulose continuous long-fiber nonwoven fabric obtained as described above was cut and cut as shown in FIG. 1 to obtain a base sheet used in this example.
［美容液］
グリセリン、１，３−ブチレングリコール、ヒアルロン酸ナトリウム、加水分解コラーゲン、水溶性コラーゲン、リン酸アスコルビルマグネシウム、椿種子エキス、茶葉エキス、里桜花エキス、リンゴ酸、アスコルビン酸、α−アルブチン、ポリクオタニウム−５１、ヒトオリゴペプチド−１、マンニトール、フラーレン、ポリビニルピロリドン（ＰＶＰ）、ベタイン、ｄｌ−ピロリドンカルボン酸ナトリウム、ソルビトール、セリン、グリシン、グルタミン酸、アラニン、リシン、アルギニン、トレオニン、プロリン、アミノカプロン酸、アルニカエキス、胡瓜エキス、西洋木蔦エキス、西洋接骨木エキス、銭葵エキス、パリエタリアエキス、ラベンダー油、ゼラニウム油、グリチルリチン酸ジカリウム、（アクリレーツ／アクリル酸アルキル（Ｃ１０−３０））クロスポリマー、ポリエチレングリコール−６０水添ヒマシ油、水酸化カリウム、キサンタンガム、メチルパラベン、フェノキシエタノールからなる分散質と、分散媒としての水からなる乳液状のゾルを本実施例で用いる美容液とした。
[Serum]
Glycerin, 1,3-butylene glycol, sodium hyaluronate, hydrolyzed collagen, water-soluble collagen, ascorbyl magnesium phosphate, persimmon seed extract, tea leaf extract, sato cherry blossom extract, malic acid, ascorbic acid, α-arbutin, polyquaternium-51 , Human oligopeptide-1, mannitol, fullerene, polyvinylpyrrolidone (PVP), betaine, sodium dl-pyrrolidonecarboxylate, sorbitol, serine, glycine, glutamic acid, alanine, lysine, arginine, threonine, proline, aminocaproic acid, arnica extract, Pepper extract, Western koji extract, Western bone extract, Zeni extract, Parietalia extract, Lavender oil, Geranium oil, Dipotassium glycyrrhizinate, (Acrylates / Alcrylate (C10-30)) Cross polymer, polyethylene glycol-60 hydrogenated castor oil, potassium hydroxide, xanthan gum, methyl paraben, phenoxyethanol, and an emulsion sol composed of water as a dispersion medium. The serum used was used.
［インキ及び印刷方法］
上記得られた基材シート及び不織布原反に対してウレタン二液硬化型の油性グラビアインキを用いて、油性グラビア印刷（印刷後のエイジングは４０℃、２４時間とした）を行った。基材シートに対しては図２に示したような図柄で印刷することで、本実施例の美容パック用基材シートを得た。
[Ink and printing method]
Oil-based gravure printing (aging after printing was performed at 40 ° C. for 24 hours) was performed on the obtained base sheet and nonwoven fabric using a urethane two-component curable oil-based gravure ink. The base material sheet for beauty packs of this example was obtained by printing the base material sheet with a pattern as shown in FIG.
不織布原反に対しては赤色及び黒色の顔料インクを、最終的に３ｃｍ×５ｃｍのべた塗り印刷片がそれぞれ得られるように印刷した後、３ｃｍ×５ｃｍ片に裁断することで本実施例の試験片とした。なお、インキに含まれる顔料にはＮＬ規制をクリアした顔料から選び、黒色：カーボンブラック、赤色：アゾ色素、青色：銅フタロシアニンとした。 For the non-woven fabric, red and black pigment inks were printed so that a final printed piece of 3 cm × 5 cm was obtained respectively, and then cut into 3 cm × 5 cm pieces to test this example. It was a piece. The pigment contained in the ink was selected from pigments that cleared the NL regulations, and black: carbon black, red: azo dye, blue: copper phthalocyanine.
［実施例２］
目付が１００ｇ／ｍ２である再生セルロース連続長繊維不織布を不織布原反として用いた以外は、実施例１と同様にして試験片を得た。
[Example 2]
A test piece was obtained in the same manner as in Example 1 except that a regenerated cellulose continuous long-fiber nonwoven fabric having a basis weight of 100 g / m 2 was used as the nonwoven fabric raw fabric.
［比較例１］
水性グラビアインキ（顔料は実施例１と同様の、黒色：カーボンブラック、赤色：アゾ色素）を用いて水性グラビア印刷を行うことで試験片にインキを印刷した以外は、実施例１と同様にして試験片を得た。
[Comparative Example 1]
Except that the ink was printed on the test piece by performing aqueous gravure printing using the aqueous gravure ink (pigment is the same as in Example 1, black: carbon black, red: azo dye), the same as in Example 1 A specimen was obtained.
［比較例２］
水性フレキソインキ（顔料は実施例１と同様の、黒色：カーボンブラック、赤色：アゾ色素）を用いてフレキソ印刷を行うことで、試験片にインキを印刷した以外は、実施例１と同様にして試験片を得た。
[Comparative Example 2]
Except that the ink was printed on the test piece by performing flexographic printing using water-based flexographic ink (pigment is the same as in Example 1, black: carbon black, red: azo dye), the same as in Example 1. A specimen was obtained.
上記の様にして得られた各試験片については、以下のようにインキの色落ち・色移りがないかの確認試験を行った。試験の結果は纏めて表１に示した。 Each test piece obtained as described above was subjected to a confirmation test for ink discoloration and color transfer as follows. The test results are summarized in Table 1.
［インキ溶出性試験］
各試験片を同じ大きさ（３ｃｍ×５ｃｍ）の濾紙と、印刷面が接するように合わせた状態で、上記美容液に含浸させる。それをバリア性のある袋に密閉した状態で４０℃、９日間静置し、濾紙への色移りがないかを目視で確認することで、インキが美容液によって溶け出さないかどうかを判定した。
[Ink dissolution test]
Each test piece is impregnated with the above-mentioned cosmetic liquid in a state where the same size (3 cm × 5 cm) filter paper and the printing surface are in contact with each other. It was left to stand at 40 ° C. for 9 days in a sealed state with a barrier bag, and it was judged whether or not the ink was not dissolved by the cosmetic liquid by visually checking whether there was any color transfer to the filter paper. .
［湿潤状態における耐摩擦性試験］
美容液に９日間含浸された状態の上記インキ溶出試験実施後の試験片の印刷面を、乾いた布で軽く５回拭き、色落ちが見られないかどうかを目視で確認することで、湿潤状態における耐摩擦性（以下、「耐湿摩性」ともいう）を判定した。
[Abrasion resistance test in wet condition]
Lightly wipe the printed surface of the test piece after the above ink elution test, which has been impregnated with a cosmetic liquid for 9 days, with a dry cloth and check visually that no discoloration is observed. Friction resistance in the state (hereinafter also referred to as “wet abrasion resistance”) was determined.
実施例１、２及び比較例１、２の全ての試験片において濾紙への色移りは見られず、インキの非溶出性は良好であった。 In all the test pieces of Examples 1 and 2 and Comparative Examples 1 and 2, no color transfer to the filter paper was observed, and the non-elution property of the ink was good.
また、実施例１及び２においては、湿潤状態でも色落ちは見られず、耐湿摩性についても良好であった。一方、比較例１については、赤色及び黒色インクの双方に湿潤状態における色落ちが見られ、また、比較例２においては湿潤状態における赤色インクに関して色落ちが見られた。 Further, in Examples 1 and 2, no color fading was observed even in a wet state, and the wet abrasion resistance was good. On the other hand, for Comparative Example 1, color loss in the wet state was observed for both the red and black inks, and in Comparative Example 2, color loss was observed for the red ink in the wet state.
［パッチ試験］
実施例１の美容パック材については、白色ワセリン及び生理食塩水を対照として以下のように２４時間連続貼付の閉鎖式パッチ試験を実施した。
[Patch test]
The cosmetic pack material of Example 1 was subjected to a 24-hour continuous patch test with white petrolatum and physiological saline as controls as follows.
（対象被験者）
選択基準：同意取得時の年齢が２０歳以上６０歳以下の日本人男性及び女性
除外基準：皮膚過敏症の者、接触性アレルギーのある者またはアレルギー症状を示す恐れのある者、検査結果に影響する可能性のあると思われる薬を服用または塗布している者、皮膚科に通っている者、妊娠中または妊娠している可能性のある者および授乳中の者、被験品貼付箇所にニキビ・吹き出物（広範囲）・シミ（広範囲）・傷・刺青・イボ・火傷痕等があることによってパッチテストの被験者として適さない者、本パッチテストに不適当と思われる既往症および現病症を有する者。
被験者数：２０名
被験者管理事項：貼付期間中の入浴は禁止した（ただし、観察部位に水をかけなければシャワー入浴は可）。剥離後観察期間中の入浴およびシャワーに関しては、観察部位に強い刺激を与えないように注意した。試験期間中（初回観察前日から最終観察当日）は、不規則な生活（睡眠不足、暴飲暴食など）を禁止した。試験期間中（初回観察前日から最終観察当日）は、発汗を伴う激しい運動を禁止した。剥離後24時間の観察まで、観察部位に触れることを禁止した。
(Subject)
Selection criteria: Japanese men and women aged 20 to 60 years at the time of obtaining consent Exclusion criteria: Persons with skin hypersensitivity, persons with contact allergies, or those who may have allergic symptoms, affecting test results Those who are taking or applying medicines that are likely to be, those who are attending dermatology, those who are pregnant or may be pregnant and breastfeeding, acne at the place where the test product is applied・ People who are unsuitable for patch testing due to pimples (wide area), stains (wide area), wounds, tattoos, warts, burn marks, etc., or who have a past or present disease that seems inappropriate for this patch test.
Number of subjects: 20 Subject management matters: Bathing during the pasting period was prohibited (however, shower bathing is possible unless water is applied to the observation site). With regard to bathing and showering during the observation period after peeling, care was taken not to give strong stimulation to the observation site. During the study period (from the day before the first observation to the day of the final observation), irregular lifestyles (lack of sleep, heavy drinking and eating away) were prohibited. During the test period (from the day before the first observation to the day of the final observation), intense exercise with sweating was prohibited. It was prohibited to touch the observation site until observation for 24 hours after peeling.
（試験デザイン）
閉鎖法パッチテスト：「皮膚刺激性・感作性試験の実施方法と皮膚性状計測および評価」第１章 皮膚刺激性試験 第３節 ヒトパッチテスト（ｐ２９）に準拠。
判定基準：「皮膚刺激性・感作性試験の実施方法と皮膚性状計測および評価」第１章 皮膚刺激性試験 第３節 ヒトパッチテスト（ｐ２９）に準拠し、以下のような基準で判定した。
(Examination design)
Closed patch test: “Skin irritation / sensitization test implementation method and skin property measurement and evaluation” Chapter 1 Skin irritation test Section 3 Human patch test (p29) compliant.
Judgment criteria: “Implementation method of skin irritation / sensitization test and measurement and evaluation of skin properties” Chapter 1 Skin irritation test Section 3 Human patch test (p29) .
（パッチテスト実施手順）
貼付部位・観察部位：背部
貼付方法：被験品が充填された皮膚テスト用パッチテープ（パッチテスター「トリイ」鳥居薬品株式会社製）を、貼付部位に貼付する。
貼付時間：２４時間
観察タイミング：剥離後６０分経過後、及び、剥離後２４時間経過後
試験実施機関：芝パレスクリニック、ＳＯＵＫＥＮ臨床試験室
(Patch test execution procedure)
Application site / observation site: Back Application method: A patch tape for skin testing (patch tester “Torii” manufactured by Torii Pharmaceutical Co., Ltd.) filled with the test product is applied to the application site.
Pasting time: 24 hours Observation timing: 60 minutes after peeling and 24 hours after peeling Testing organization: Shiba Palace Clinic, SOUKEN Clinical Laboratory
（試験結果）
パッチテストの試験結果を、表４及び表５に示す。
(Test results)
The test results of the patch test are shown in Table 4 and Table 5.
表４に示される通り、実施例１の美容パック材は、剥離６０分後で１名が弱陽性、１９名が陰性であり、剥離２４時間後で２０名が陰性であった。その結果、２４時間連続貼付による閉鎖法パッチテストにおける皮膚刺激指数は、２．５であり安全品と判定されるものであることが確認された。 As shown in Table 4, in the cosmetic pack material of Example 1, one person was slightly positive 60 minutes after peeling, 19 were negative, and 20 were negative 24 hours after peeling. As a result, it was confirmed that the skin irritation index in the closed patch test by continuous application for 24 hours was 2.5, which was judged as a safe product.
Claims (4)
前記美容パック用基材シートは、
不織布と、
前記不織布に形成され、目を露出させるための目用孔と、
前記不織布に形成され、口を露出させるための口用孔と、
前記目用孔の縁及び／又は前記口用孔の縁に沿った図柄と
を有し、
前記不織布に油性グラビアインキからなる前記図柄がグラビア印刷によって印刷されており、
前記油性グラビアインキが二液硬化型である、美容パック材。 It has a base sheet for beauty packs infiltrated with serum,
The base sheet for the beauty pack is
Non-woven fabric,
An eye hole formed in the nonwoven fabric to expose the eye;
Mouth holes for exposing the mouth, formed in the nonwoven fabric,
A pattern along the edge of the eye hole and / or the edge of the mouth hole;
Wherein the symbols consisting of oil-based gravure ink are printed by gravure printing on the nonwoven fabric,
A beauty pack material in which the oil-based gravure ink is a two-component curable type .
前記油性グラビアインキからなる前記図柄が印刷された前記不織布に美容液を含浸させる工程と
を含み、
前記不織布には、目を露出させるための目用孔と口を露出させるための口用孔とが形成され、前記目用孔の縁及び／又は前記口用孔の縁に沿うように、前記図柄が形成され、
前記油性グラビアインキが二液硬化型である、美容パック材の製造方法。 A process of gravure printing a pattern made of oil-based gravure ink on a nonwoven fabric;
Impregnating the non-woven fabric printed with the design made of the oil-based gravure ink with a cosmetic liquid,
The non-woven fabric is formed with an eye hole for exposing the eye and a mouth hole for exposing the mouth, and along the edge of the eye hole and / or the edge of the mouth hole, A pattern is formed,
The manufacturing method of the beauty pack material whose said oil-based gravure ink is a two-component curable type .
The manufacturing method of the beauty pack material of Claim 3 whose fabric weight of the said nonwoven fabric is 80-100 g / m < 2 >.